Earth-abundant metal catalysts are critically needed for sustainable chemical synthesis. Here we report a simple, cheap and effective strategy of producing novel earth-abundant metal catalysts at metal–organic framework (MOF) nodes for broad-scope organic transformations. The straightforward metalation of MOF secondary building units (SBUs) with cobalt and iron salts affords highly active and reusable single-site solid catalysts for a range of organic reactions, including chemoselective borylation, silylation and amination of benzylic C–H bonds, as well as hydrogenation and hydroboration of alkenes and ketones. Our structural, spectroscopic and kinetic studies suggest that chemoselective organic transformations occur on site-isolated, electron-deficient and coordinatively unsaturated metal centres at the SBUs via σ-bond metathesis pathways and as a result of the steric environment around the catalytic site. MOFs thus provide a novel platform for the development of highly active and affordable base metal catalysts for the sustainable synthesis of fine chemicals.
Metal oxides, metal alloys and metal nanoparticles dispersed on oxide supports form the cornerstone of heterogeneous catalysts used in chemical and petrochemical industries1,2. However, the presence of multiple active sites makes selectivity difficult to achieve in traditional heterogeneous catalysis. Significant effort has thus been devoted to developing single-site heterogeneous catalysts3,4. The simplest and most common method of producing single-site heterogeneous catalysts is to anchor catalytically active atoms, ions or molecular complexes to high surface area solid supports, such as silica or other robust metal oxides. However, this approach often leads to non-uniform distribution of catalysts throughout the solid supports, which can be complicated by intermolecular interactions between catalytic sites and the interactions of active sites with surface functionalities. Preventing intermolecular deactivation has been a challenge in the development of novel base metal catalysts, since homogeneous base metal catalysts generally need to be stabilized with bulky, elaborately designed ligands that can impede their catalytic activity. In this work, we attempt to use inorganic oxide clusters that are well positioned and separated in porous metal–organic frameworks (MOFs) to design highly active earth-abundant metal-based single-site solid catalysts.
Built out of metal cluster secondary building units (SBUs) and organic linkers, MOFs have been explored as useful molecular materials for many potential applications, including gas storage5,6, separation7,8, catalysis9,10, sensing11,12,13, biomedical imaging14, drug delivery15, solar energy harvesting16 and conductivity17,18. By utilizing pre-metalated organic struts or via postsynthetic metalation of the functionalized bridging linkers, MOFs provide a highly tunable platform to engineer single-site solid catalysts for many organic transformations that cannot be performed by traditional porous inorganic materials19,20,21,22,23. The diversity of metal cluster SBUs offers an alternative strategy for generating MOF catalysts. Although MOF SBUs have been used as acid catalysts24,25, their application in more challenging catalytic reactions or as potential supports for catalysis has been far less explored26,27.
Herein, we report a simple strategy for discovering highly active base metal catalysts functionalized at metal–organic framework nodes (M@SBU). The straightforward and cost-effective metalation of SBUs of UiO-MOFs with readily available cobalt and iron precursors affords highly electron-deficient and coordinatively unsaturated metal centres that can catalyse interesting organic reactions. We believe this occurs via σ-bond metathesis reaction pathways. The Co@SBU and Fe@SBU MOF materials are highly active and reusable single-site solid catalysts for site-selective sp3 C–H functionalization reactions, such as undirected benzylic C–H borylation, silylation and amination. In addition, we have also discovered the first example of catalytic undirected sp3 C–H silylation with alkoxysilane using the Co@SBU catalyst.
Synthesis and characterization of M@UiO Materials
UiO-68 was synthesized via a solvothermal reaction between ZrCl4 and triphenyldicarboxylic acid (H2TPDC) in the presence of DMF (N,N-dimethylformamide) and trifluoroacetic acid in 95% yield (Supplementary Figs 1–3)28. The deprotonation of Zr3(μ3-OH) sites in SBUs of UiO-68 with nBuLi followed by reaction with CoCl2 or FeBr2·2THF in THF afforded the Co- or Fe-functionalized UiO materials (UiO-CoCl and UiO-FeBr) as a deep blue or brown solid, respectively (Fig. 1a and Supplementary Figs 4–15). Crystallinity of UiO-68 was maintained upon metalation, as suggested by similarities in the powder X-ray diffraction patterns of UiO-68, UiO-CoCl and UiO-FeBr (Fig. 1b,e). Inductively coupled plasma-mass spectrometry (ICP-MS) analysis of the digested UiO-CoCl and UiO-FeBr revealed 100% metalation at the Zr3(μ3-OH) sites, corresponding to four Co/Fe centres per Zr6 node. Infrared spectrum of UiO-CoCl showed the disappearance of νμ3O–H band (∼3,640 cm−1, KBr), consistent with metalation of Zr3(μ3-OH) sites (Supplementary Fig. 9). In addition, the TEM-EDX analysis indicated that cobalt and iron are uniformly distributed throughout the particles (Fig. 1d, Supplementary Figs 10 and 12). UiO-66 and UiO-67 were functionalized with CoCl2 in a similar fashion as UiO-68 (Supplementary Figs 16–17).
A single-crystal X-ray diffraction study revealed that UiO-CoCl crystallizes in the Fm m space group, with the Zr6(μ3-O)4(μ3-OH)4 SBUs connected by the TPDC bridging linkers to afford the 12-connected fcu topology. The void space was calculated to be 79.6% by PLATON (Supplementary Fig. 19 and Supplementary Table 1). However, due to the crystallographic disorder of the CoCl moiety, the Co coordination environments in UiO-CoCl could not be established by X-ray crystallography (Supplementary Fig. 20). Instead, we used X-ray absorption spectroscopy to investigate the coordination environments of Co and Fe. The oxidation states of UiO-CoCl and UiO-FeBr are +2, as determined by comparing the energies of the pre-edge peaks to the Co(II) and Fe(II) reference compounds (Supplementary Figs 21–29). Fitting the extended X-ray absorption fine structure (EXAFS) regions of UiO-CoCl and UiO-FeBr confirmed that the Co and Fe centres were coordinated to three SBU oxygen atoms (one oxide moiety that is triply bridged to three Zr centres and two TPDC carboxylate oxygen atoms that are doubly bridge the Zr centres) and one halogen atom as shown in the model complexes (Fig. 1c,f; Supplementary Tables 2–4).
UiO-Co-catalysed undirected benzylic C−H borylation
Upon treatment with NaEt3BH, UiO-Co became an active catalyst in undirected dehydrogenative borylation of benzylic C−H bonds using B2(pin)2 (pin=pinacolate) or HBpin as the borylating agents. Borylation of alkyl C−H bonds provides alkyl boronates, which are versatile reagents in organic synthesis29,30. Although selective borylation of benzylic C−H bonds has been achieved with a few homogeneous catalysts based on precious metals such as Pd31, Rh32 or Ir33, the earth-abundant metal-catalysed undirected and chemoselective benzylic C−H borylation is rare34. Recently, α-di-imine cobalt catalysts were reported for benzylic C–H borylation at high catalyst loadings (5–30 mol%) and with long reaction times35. The UiO-Co catalysed borylation reactions were first screened by varying temperatures and solvents, which revealed high catalytic activities and selectivities when the borylation reactions were performed using B2(pin)2 in neat alkylarenes at 103 °C (Supplementary Tables 5 and 6). Under optimized reaction conditions, primary benzylic boronate esters were afforded in excellent yields from a range of methylarenes with UiO-Co (0.2 mol% Co) (Table 1). The borylation reactions of m-xylene and toluene afforded corresponding boronate esters in good yields with excellent selectivities for the benzylic boronates over the aryl boronates (entries 1–2, Table 1). The powder X-ray diffraction patterns of UiO-Co recovered from the borylation reaction of m-xylene remained the same as that of freshly prepared UiO-Co (Fig. 1b), indicating that the MOF frameworks are stable under the catalytic conditions. Only benzylic boronates were obtained in good yields from mesitylene, p-xylene and 4-tert-butyl-toluene, presumably because the steric hindrance at the aryl C−H bonds was greater than that of benzylic positions (entries 3–9, Table 1). TONs as high as 2,300 were obtained for the borylation of mesitylene. However, reactions with electron-deficient methylarenes such as m-chlorobenzene were slow. Notably, UiO-Co-catalysed borylation occurred not only at primary benzylic C−H bonds, but also at secondary and tertiary benzylic C−H bonds. At 0.2 mol% Co loading, UiO-Co afforded secondary and tertiary benzylic boronate esters from ethylbenzene and isopropryl benzene, respectively, in 100% conversion, and the selectivities for the benzylic products over the aryl products were ∼4:1 (entries 12–13, Table 1). These results contrast with analogous reactions reported with a chemoselective homogeneous iridium catalyst that is active for borylation of only primary benzylic C−H bonds33.
Unlike homogeneous catalysts, which cannot be easily reused, we found that, at a 1.0 mol% Co loading, the UiO-Co catalyst could be used at least five times in the borylation of p-xylene (Supplementary Fig. 30). Furthermore, the boronate ester was obtained in high purity simply by removing the solid catalyst and the organic volatiles. The heterogeneity of UiO-Co was confirmed by several experiments. The leaching of Co and Zr into the supernatant was very low—0.14 and 0.056%, respectively—during the course of the borylation reaction, as shown by ICP-MS analysis. Moreover, no further conversion was detected after removal of UiO-Co from the reaction mixture (Supplementary Discussion). Our control experiment ruled out the contribution of catalytic activity of any trapped Co nanoparticles within the MOFs (Supplementary Discussion). In addition, the rate of the borylation reaction of p-xylene was significantly higher than that of analogous bulkier alkenes 4-tert-butyl-toluene and 3,5-di-tert-butyl-toluene under identical conditions, which demonstrates that catalysis is facilitated by Co@SBU sites both inside the pores and on the surface of the MOFs (Supplementary Table 8 and Supplementary Discussion).
Having shown the highly selective benzylic C−H borylation of alkylarenes with the UiO-Co catalyst, we sought to investigate the nature of the catalytic species and to reveal their mechanism using structural, kinetic and spectroscopic techniques. The treatment of UiO-CoCl with NaEt3BH in THF likely affords the ‘Zr3-(μ4-O)-Co-H’ (UiO-CoH) species. The reaction of UiO-CoH with HBpin readily generates UiO-Co-Bpin and an equivalent amount of H2 (Supplementary Fig. 32). UiO-Co-Bpin can also be prepared by the reaction of UiO-CoCl with B2pin2 at 100 °C for 12 h. X-ray absorption near edge structure analysis indicated that the Co centres in both UiO-CoH and UiO-Co-Bpin are in +2 oxidation states (Supplementary Fig. 21). EXAFS fitting of UiO-CoH or UiO-Co(Bpin) revealed a Co local coordination environment similar to UiO-CoCl, where Co is coordinated to three SBU oxygen atoms and one hydride or one Bpin, respectively (Fig. 2a and Supplementary Figs 25–27).
We also prepared the Co-functionalized oxozirconium methacrylate cluster Zr6(OCoCl)4O4(OMc)12 (Mc, methacrylate, Fig. 2b, Supplementary Fig. 18 and Supplementary Methods)36 as a homogeneous control to test whether Co@SBU is a competent catalyst for the borylation reactions. EXAFS analysis indicated that the Co coordination environment of Zr6(OCoCl)4O4(OMc)12 is similar to that of UiO-CoCl (Fig. 2c, Supplementary Fig. 28, and Supplementary Table 3). Interestingly, on activation with NaEt3BH, this homogeneous Zr6-based Co-cluster was also active in catalysing C−H borylation of p- and m-xylenes with selectivities for the benzylic boronates over the aryl boronates (Supplementary Table 7), similar to those observed for UiO-Co, suggesting that the SBUs were the sites of catalysis. However, the reaction rate and the chemoselectivity in the borylation of m-xylene were lower for the homogeneous catalyst than those of UiO-Co. Furthermore, UiO-Co was more active and chemoselective than analogous UiO-MOFs with smaller pore sizes, such as UiO-67-Co and UiO-66-Co (entries 1–3, Supplementary Table 5). These results demonstrate that the porous frameworks and the pore sizes of UiO-Co are crucial in controlling the chemoselectivity and the rate of the reaction.
To further explore the mechanism, the empirical rate law was determined by the method of initial rates (<10% conversion), which showed that the C−H borylation of p-xylene catalysed by UiO-Co has a first-order dependence on the catalyst and p-xylene concentrations (Fig. 2d) and a zeroth-order dependence on the B2pin2 concentration (Supplementary Fig. 33). In addition, the conversion of the deuterated p-xylene was slower than the proteo-p-xylene. Primary kinetic isotope effects from initial substrate conversion measurements [k′obs(H)/k′obs(D)=1.73(9)] indicated that the C−H bond cleavage of p-xylene is likely the turnover-limiting step (Supplementary Fig. 34). Furthermore, we did not observe any deuterium incorporation into the benzyl boronate, which suggests that the C–H bond activation is irreversible. The oxidative addition of C–H bond to the Co-centre is unlikely to occur in the turnover-limiting step because the Co2+ centre was electron poor and the borylation of the benzylic C−H bonds was faster than that of the more electron-rich aryl C−H bonds of alkylarenes. Instead, UiO-Co-catalysed benzylic borylation likely proceeds via σ-bond metathesis pathways. On the basis of our experimental observations, we propose the following mechanism (Fig. 2e): The reaction of ‘Zr3-μ4-O-Co-Cl’ moiety in UiO-CoCl with NaEt3BH generates the active species UiO-CoH in the cycle. The σ-bond metathesis between Co-H and B2pin2 produces Zr3-μ4-O-Co-Bpin species, which then reacts with the alkylarene via a four-centred turnover-limiting step involving [2σ+2σ] cycloaddition of a ‘Co–Bpin’ bond with the ‘H–CH2Ar’ bond of alkylarene to furnish the benzyl boronates and regenerate UiO-CoH. Although the electron-deficient Co catalyst should favour the electron-rich aryl C-H bonds, the steric hindrance from the three phenyl rings surrounding the Co centre directs selective binding of less-hindered benzylic C–H bonds (Fig. 2f and Supplementary Fig. 31).
UiO-Co-catalysed undirected benzylic C−H silylation
Inspired by the discovery of UiO-Co catalysed selective borylation of the benzylic C−H bonds, we attempted to develop undirected benzylic C−H silylation reactions using alkyl- and alkoxysilanes. Although significant progress has been made in developing catalysts for aryl C−H silylation, the silylation of alkyl C−H bonds has been far less explored37,38. In particular, examples of undirected intermolecular alkyl C−H silylation are few39,40,41, and there is no report of such transformation with trialkoxysilanes. Direct installation of a trialkoxysilyl group via alkyl C−H bond activation generates alkyltrialkoxysilanes, which are not only useful precursors to commercial polymers but also widely used as silylating agents for surface functionalization and as nontoxic transmetalation agents in cross-coupling reactions. We used UiO-Co as the active catalyst in the silylation of benzylic C−H bonds with Et3SiH or (OEt)3SiH (Table 2 and Supplementary Figs 35–38). Heating the mixture of UiO-Co (0.2–0.4 mol% Co) and silane in neat alkylarene at 98 °C gave the corresponding alkylsilanes. Owing to the difficulty of isolating some silylated products, the crude products were directly oxidized via Tamao–Fleming oxidation, and the final products were isolated as the corresponding benzyl alcohols42,43. In the case of silylation of m-xylene and ethylbenzene with Et3SiH, we observed good selectivities of silylation in favour of benzylic C−H bonds over aryl C−H bonds, resulting in high yields of benzyl alcohols. Interestingly, reactions of (OEt)3SiH occurred exclusively with benzylic C−H bonds of the alkylarenes, as shown by GC-MS and 1H NMR spectroscopy, providing corresponding benzylic alcohols after oxidation in 62–89% yield.
UiO-Co-catalysed hydrogenation and hydroboration reactions
UiO-Co is also highly active for catalytic hydrogenation of a range of olefins at room temperature (Table 3). Mono-substituted alkenes such as 1-octene and styrene were readily hydrogenated in quantitative yields with TONs>1.0 × 105 (entries 1–4, Table 3). At 0.1–0.01 mol% Co-loading, UiO-Co catalysed hydrogenation of 1,1-, cis-1,2-disubstituted alkenes, α-isopropylstyrene and cyclohexene in quantitative yields (entries 5–9, Table 3 and Supplementary Fig. 39). In addition, dialkenes (allyl ether), tri-substituted alkenes (trans-α-methylstilbene) and carbonyl-functionalized alkenes (dimethyl itaconate) were quantitatively hydrogenated in excellent yields (entries 10–13, Table 3). Within only 66 h, UiO-Co displayed an exceptional TON of 3.54 × 106 in hydrogenation of 1-octene, the highest TON ever reported for an earth-abundant metal-catalysed olefin hydrogenation (entry 2, Table 3). Furthermore, only 3.7 p.p.m. Co and 1.7 p.p.m. Zr remained in the n-octane product after simple filtration. UiO-Co showed impressive recyclability: it could be recovered and reused without any loss of catalytic activity at least 16 times for the hydrogenation of 1-octene at a 0.01 mol% Co loading (Supplementary Fig. 40). The powder X-ray diffraction patterns of UiO-Co after hydrogenation were the same as those of the pristine MOF catalysts, which verified the stability of the framework under catalytic conditions (Fig. 2b). Hardly any metal was leached after the first run, according to ICP-MS analyses of the organic product, with leachings of only 0.9% for Co and 1.0% for Zr. Furthermore, no conversion of alkene was observed after the removal of the solid catalyst, demonstrating that the leached Co was not responsible for the catalytic activity (Supplementary Discussion).
We also evaluated the UiO-Co for catalytic hydroboration of alkenes and carbonyl compounds (Table 4 and Supplementary Figs 41–42). We examined hydroboration reactions by treating alkenes, ketones or aldehydes with HBpin and 0.01–0.4 mol% UiO-Co at 60–100 °C. UiO-Co resulted in borate ester products from several carbonyl substrates, including alkyl and alkoxy-functionalized aryl ketones and aldehydes in 81–98% yields with TONs up to 5.4 × 104 (Table 4). Alkenes such as 1-octene, styrene and α-methylstyrene were hydroborated selectively with 0.1–0.4 mol% UiO-Co in anti-Markovnikov manner to give corresponding alkylboronates in extremely high yields (Table 4). We obtained pure hydroboration products through a simple process of removing the catalyst by centrifuge, then removing the organic volatiles.
UiO-FeBr catalysed sp3 C–H amination
We next examined the use of UiO-68 in other base metal-catalysed organic transformations. We studied the catalytic activity of UiO-FeBr in C–H amination reactions because the conversion of C–H bonds to C–N bonds provides a valuable method for introducing nitrogen functionalities directly into a molecule44,45,46,47. Developing iron catalysts for sp3 C–H amination is of particular interest due to the high abundance and low toxicity of iron48,49,50. Although most Fe-catalysed C–H amination reactions use sulfamides or azides as a nitrogen source45,46,48,50,51, we report here the first example of using aniline as a nitrogen source. Heating aniline with neat substrates such as indane, tetraline and cyclohexene gave a C–H aminated product in 41–53% yield with UiO-FeBr (2–10 mol% Fe, Table 4 and Supplementary Fig. 43). We propose a catalytic process involving a one-electron Fe(II)–Fe(III) cycle, which is analogous to the well-studied copper-catalysed C–H amination reactions that are believed to proceed through a Cu(I)–Cu(II) cycle (Supplementary Fig. 44)47. The inverse dependence of conversions on the substrate sizes (Table 5, entries 1–3) is consistent with the notion that the sp3 C–H amination occurs at the UiO-FeBr site inside the MOF owing to the sluggish diffusion of large substrates through MOF channels.
The deprotonation of μ3–OH sites of MOFs SBUs followed by reactions with iron- and cobalt-halides afforded Fe- and Co-functionalized MOF-materials for a broad scope of organic transformations (Fig. 3). The treatment of UiO-CoCl with NaEt3BH generated highly robust μ4–O–Co(H) species at MOF nodes due to the prevention of intermolecular decomposition pathways. All the functionalized MOF materials were characterized by powder X-ray diffraction, ICP-MS, TEM-EDX, X-ray absorption spectroscopy, TGA and BET analysis. The UiO carboxylate groups did not react with nBuLi during lithiation and metalation as evident by the observation of only H2TPDC in the 1H NMR spectrum of the digested metalated UiO-68 (Supplementary Fig. 8 and Supplementary Discussion) and by the retention of strong carboxylate carbonyl stretching peaks at 1,605 and 1,591 cm−1 in the infrared (KBr) spectrum (Supplementary Fig. 9a). EXAFS of UiO-CoCl and UiO-FeBr suggested that the Co(II) and Fe(II) centres in the MOFs were coordinated to three SBU oxygen atoms: one oxide moiety that is triply bridged to three Zr centres and two TPDC carboxylate oxygen atoms that doubly bridge the Zr centres and one halogen atom. The very-weak-field coordination environment consisting of O-atoms that the UiO-M (M=Co, Fe) framework provides is very different than those accessible to molecular catalysts that typically consist of stronger field N- or P-donor atoms. Indeed, bipyridine and phenathroline-based MOF-Co catalysts were recently reported to be active in borylation of arene C–H bonds instead of benzylic C–H bonds52. Beyond the low coordination number, weak-field catalyst sites that lead to high electrophilicity are possible in these MOFs but are simply not available to small molecule homogeneous catalyst systems because ligands based on weakly binding O-donors would readily dissociate from first row transition metals.
Our spectroscopic and kinetic studies suggest that the SBU-supported Co–H species can chemoselectively catalyse sp3 C–H functionalization reactions via σ-bond metathesis pathways and as a result of the steric environment around the catalytic site. However, the nature of the active species has not been unambiguously established and will be the subject of future studies. The role of the MOF-framework and the strategy of using a specific pore size are also very important for chemoselective reactions. As discussed previously, UiO-Co was more active and chemoselective than homogeneous cluster control, Zr6(OCoCl)4O4(OMc)12 (Supplementary Tables 9–12), and also analogous UiO-MOFs with smaller pore sizes, such as UiO-67-Co and UiO-66-Co. These results suggest that the chemoselective C–H activation reactions occurred within the pore and were dependent on the open channel sizes because of competition between the reactions occurring at SBUs within the pore and the non-selective background reactions occurring on the surface, as well as on the different diffusion rates of the organic substrates through the open channels of varied sizes.
In summary, we developed a simple strategy of treating metal–organic framework nodes with readily available and cheap earth-abundant metal precursors to afford highly active and selective single-site solid catalysts for a broad scope of organic transformations, including novel site-selective borylation and silylation of sp3 C−H bonds. The unique coordination environment of Co/Fe centres of the secondary building units as well as the porous frameworks and pore structures of UiO-MOF play important roles in controlling the rate and chemoselectivity of these organic reactions. Owing to the high stability of UiO-MOFs and the ease of functionalizing SBUs with metal ions, we anticipate that MOFs may offer a versatile platform for discovering new catalytic transformations and developing earth-abundant metal and other metal catalysts for sustainable synthesis of fine and commodity chemicals. The cost effective nature of the present M@SBU approach has the potential to move MOF catalysts from novel discoveries to practical applications.
All of the catalytic reactions were carried out under nitrogen in a standard inert atmosphere with Schlenk techniques or inside a nitrogen-filled glovebox. Detailed procedures for the syntheses of ligands and MOFs are reported in the Supplementary Methods.
Synthesis of UiO-68 and UiO-CoCl
ZrCl4 (1.30 mg, 5.03 μmol) and 1,4-bis(4-carboxyphenyl)benzene (1.6 mg, 5.53 μmol) were dissolved in 0.8 ml of DMF in a 1 dram vial, and 15.4 μl of trifluoroacetic acid was then added. The vial was capped and heated at 120 °C for 3 days to afford UiO-68 as a white solid (2.0 mg, 95% yield). In the glovebox, UiO-68 (20.0 mg) in 3 ml THF was cooled to −30 °C for 30 min and 33 μl of nBuLi (2.5 M in hexane) was added dropwise to the cold suspension. The resulting light yellow mixture was stirred slowly overnight, collected and washed with THF. Then the lithiated UiO-68 was transferred to a vial containing 5 ml THF solution of CoCl2 (6.0 mg). The mixture was stirred overnight, collected and washed with THF to afford UiO-CoCl as a deep blue solid.
Procedure for UiO-Co catalysed benzylic C–H borylation of methylarenes
In a glovebox, UiO-CoCl (1.0 mg, 0.2 mol% Co) was charged into a small vial, to which 0.5 ml THF was added. Then, 15 μl NaBEt3H (1.0 M in THF) was added to the vial, and the mixture was stirred slowly for 1 h in the glovebox. The solid was centrifuged out of suspension and washed twice with THF and then once with p-xylene. B2pin2 (43.0 mg, 0.169 mmol) in 2.0 ml p-xylene was added to the vial and the resulting mixture was transferred to a Schlenk tube. The tube was heated under nitrogen at 103 °C for 3 days. The reaction mixture was cooled to room temperature and the solid was centrifuged out of suspension. The extract was passed through a short plug of Celite and then concentrated in vacuo to give the pure boronate ester in 96% yield (75 mg, 0.324 mmol).
Procedure for UiO-Co-catalysed benzylic C–H silylation
In a glovebox, UiO-CoCl (1.0 mg, 0.2 mol% Co) was charged into a small vial, and 0.5 ml THF was added. Then, 15 μl NaBEt3H (1.0 M in THF) was added to the vial, and the mixture was stirred slowly for 1 h in the glovebox. The solid was centrifuged out of suspension and washed twice with THF and then once with p-xylene. The solid suspended in 2 ml toluene was transferred to a Schlenk tube and (EtO)3SiH (62.6 μl, 0.34 mmol) was added to the mixture. The tube was heated under nitrogen at 98 °C for 3 days. The reaction mixture was cooled to room temperature, and the solid was centrifuged out of suspension. The extract was concentrated in vacuo and then the residue was heated at 60 °C in vacuum for 3 h to give benzyltriethoxysilane as a colourless liquid in 89% yield (38 mg, 0.151 mmol).
Procedure for UiO-Fe-catalysed C–H amination
In a glovebox, UiO-FeBr (16 μmol Fe) was centrifuged off THF, washed twice with heptane and transferred into a Schlenk tube with indane (0.587 ml, 4.8 mmol). Aniline (0.0146, ml, 0.16 mmol) and di-tert-butylperoxide (0.0882, ml, 0.48 mmol) were directly added to the Schlenk tube, which was stirred at 100 °C for 3 days. The solid was then centrifuged out of suspension and washed twice with THF and the extract was concentrated under rotavap. The residue was purified by column chromatography on silica gel with 1% Et3N and 5% EtOAc in Hexanes to afford the aminated product (16 mg, 0.076 mmol, 45%).
The crystal structures reported are deposited at the Cambridge Crystallographic Data Centre (CCDC) under deposition numbers 1439497 and 1440158. The crystallographic files can be obtained free of charge from the Cambridge Crystallographic Data Centre via http://www.ccdc.cam.ac.uk/data_request/cif. All other data are available from the authors upon reasonable request.
How to cite this article: Manna, K. et al. Chemoselective single-site Earth-abundant metal catalysts at metal–organic framework nodes. Nat. Commun. 7:12610 doi: 10.1038/ncomms12610 (2016).
Brown, S. H. in Handbook of Green Chemistry Wiley-VCH (2010).
Boudart, M., Davis, B. H. & Heinemann, H. in Handbook of Heterogeneous Catalysis 1–48Wiley-VCH (2008).
Hlatky, G. G. Heterogeneous single-site catalysts for olefin polymerization. Chem. Rev. 100, 1347–1376 (2000).
Thomas, J. M., Raja, R. & Lewis, D. W. Single-site heterogeneous catalysts. Angew. Chem. Int. Ed. 44, 6456–6482 (2005).
Rosi, N. L. et al. Hydrogen storage in microporous metal-organic frameworks. Science 300, 1127–1129 (2003).
Sumida, K. et al. Carbon dioxide capture in metal–organic frameworks. Chem. Rev. 112, 724–781 (2011).
Chen, B. et al. A microporous metal–organic framework for gas-chromatographic separation of alkanes. Angew. Chem. Int. Ed. 45, 1390–1393 (2006).
Li, J.-R., Sculley, J. & Zhou, H.-C. Metal–organic frameworks for separations. Chem. Rev. 112, 869–932 (2011).
Ma, L., Abney, C. & Lin, W. Enantioselective catalysis with homochiral metal-organic frameworks. Chem. Soc. Rev. 38, 1248–1256 (2009).
Yoon, M., Srirambalaji, R. & Kim, K. Homochiral Metal–organic frameworks for asymmetric heterogeneous catalysis. Chem. Rev. 112, 1196–1231 (2012).
Allendorf, M. D. et al. Stress-induced chemical detection using flexible metal−organic frameworks. J. Am. Chem. Soc. 130, 14404–14405 (2008).
Lan, A. et al. A luminescent microporous metal–organic framework for the fast and reversible detection of high explosives. Angew. Chem. Int. Ed. 48, 2334–2338 (2009).
Kreno, L. E. et al. Metal–organic framework materials as chemical sensors. Chem. Rev. 112, 1105–1125 (2011).
Della Rocca, J., Liu, D. & Lin, W. Nanoscale metal–organic frameworks for biomedical imaging and drug delivery. Acc. Chem. Res. 44, 957–968 (2011).
Horcajada, P. et al. Porous metal-organic-framework nanoscale carriers as a potential platform for drug delivery and imaging. Nat. Mater. 9, 172–178 (2010).
Kent, C. A. et al. Energy transfer dynamics in metal−organic frameworks. J. Am. Chem. Soc. 132, 12767–12769 (2010).
Givaja, G., Amo-Ochoa, P., Gomez-Garcia, C. J. & Zamora, F. Electrical conductive coordination polymers. Chem. Soc. Rev. 41, 115–147 (2012).
Narayan, T. C., Miyakai, T., Seki, S. & Dincă, M. High charge mobility in a tetrathiafulvalene-based microporous metal–organic framework. J. Am. Chem. Soc. 134, 12932–12935 (2012).
Ma, L., Falkowski, J. M., Abney, C. & Lin, W. A series of isoreticular chiral metal–organic frameworks as a tunable platform for asymmetric catalysis. Nat. Chem. 2, 838–846 (2010).
Manna, K., Zhang, T., Greene, F. X. & Lin, W. Bipyridine- and phenanthroline-based metal–organic frameworks for highly efficient and tandem catalytic organic transformations via directed C–H activation. J. Am. Chem. Soc. 137, 2665–2673 (2015).
Fei, H. et al. Reusable oxidation catalysis using metal-monocatecholato species in a robust metal–organic framework. J. Am. Chem. Soc. 136, 4965–4973 (2014).
Sawano, T., Thacker, N. C., Lin, Z., McIsaac, A. R. & Lin, W. Robust, chiral, and porous BINAP-based metal–organic frameworks for highly enantioselective cyclization reactions. J. Am. Chem. Soc. 137, 12241–12248 (2015).
Manna, K., Zhang, T., Carboni, M., Abney, C. W. & Lin, W. Salicylaldimine-based metal-organic framework enabling highly active olefin hydrogenation with iron and cobalt catalysts. J. Am. Chem. Soc. 136, 13182–13185 (2014).
Jiang, J. et al. Superacidity in sulfated metal–organic framework-808. J. Am. Chem. Soc. 136, 12844–12847 (2014).
Jiang, J. & Yaghi, O. M. Brønsted acidity in metal–organic frameworks. Chem. Rev. 115, 6966–6997 (2015).
Yang, D. et al. Metal–organic framework nodes as nearly ideal supports for molecular catalysts: NU-1000- and UiO-66-supported iridium complexes. J. Am. Chem. Soc. 137, 7391–7396 (2015).
Nguyen, H. G. T. et al. Vanadium-node-functionalized UiO-66: a thermally stable MOF-supported catalyst for the gas-phase oxidative dehydrogenation of cyclohexene. ACS Catal. 4, 2496–2500 (2014).
Cavka, J. H. et al. A new zirconium inorganic building brick forming metal organic frameworks with exceptional stability. J. Am. Chem. Soc. 130, 13850–13851 (2008).
Jana, R., Pathak, T. P. & Sigman, M. S. Advances in transition metal (Pd,Ni,Fe)-catalyzed cross-coupling reactions using alkyl-organometallics as reaction partners. Chem. Rev. 111, 1417–1492 (2011).
Chemler, S. R., Trauner, D. & Danishefsky, S. J. The B-alkyl Suzuki–Miyaura cross-coupling reaction: development, mechanistic study, and applications in natural product synthesis. Angew. Chem. Int. Ed. 40, 4544–4568 (2001).
Ishiyama, T., Ishida, K., Takagi, J. & Miyaura, N. Palladium-catalyzed benzylic C–H borylation of alkylbenzenes with bis(pinacolato)diboron or pinacolborane. Chem. Lett. 30, 1082–1083 (2001).
Mertins, K., Zapf, A. & Beller, M. Catalytic borylation of o-xylene and heteroarenes via C–H activation. J. Mol. Catal. A Chem. 207, 21–25 (2004).
Larsen, M. A., Wilson, C. V. & Hartwig, J. F. Iridium-catalyzed borylation of primary benzylic C–H bonds without a directing group: scope, mechanism, and origins of selectivity. J. Am. Chem. Soc. 137, 8633–8643 (2015).
Furukawa, T., Tobisu, M. & Chatani, N. Nickel-catalyzed borylation of arenes and indoles via C-H bond cleavage. Chem. Commun. 51, 6508–6511 (2015).
Palmer, W. N., Obligacion, J. V., Pappas, I. & Chirik, P. J. Cobalt-catalyzed benzylic borylation: enabling polyborylation and functionalization of remote, unactivated C (sp3)-H bonds. J. Am. Chem. Soc. 138, 766–769 (2016).
Kickelbick, G., Wiede, P. & Schubert, U. Variations in capping the Zr6O4(OH)4 cluster core: X-ray structure analyses of [Zr6(OH)4O4(OOC-CH=CH2)10]2(μ–OOC-CH=CH2)4 and Zr6(OH)4O4(OOCR)12(PrOH) (R=Ph, CMe=CH2). Inorg. Chim. Acta 284, 1–7 (1999).
Cheng, C. & Hartwig, J. F. Catalytic silylation of unactivated C–H Bonds. Chem. Rev. 115, 8946–8975 (2015).
Yang, Y. & Wang, C. Direct silylation reactions of inert C-H bonds via transition metal catalysis. Sci. China Chem. 58, 1266–1279 (2015).
Toutov, A. A. et al. Silylation of C-H bonds in aromatic heterocycles by an Earth-abundant metal catalyst. Nature 518, 80–84 (2015).
Sadow, A. D. & Tilley, T. D. Catalytic functionalization of hydrocarbons by σ-bond-metathesis chemistry: dehydrosilylation of methane with a scandium catalyst. Angew. Chem. Int. Ed. 42, 803–805 (2003).
Ishikawa, M., Okazaki, S., Naka, A. & Sakamoto, H. Nickel-catalyzed reactions of 3,4-benzo-1,1,2,2-tetraethyl-1,2-disilacyclobutene with aromatic compounds. Organometallics 11, 4135–4139 (1992).
Tamao, K., Ishida, N., Tanaka, T. & Kumada, M. Silafunctional compounds in organic synthesis. Part 20. Hydrogen peroxide oxidation of the silicon-carbon bond in organoalkoxysilanes. Organometallics 2, 1694–1696 (1983).
Fleming, I., Henning, R. & Plaut, H. The phenyldimethylsilyl group as a masked form of the hydroxy group. J. Chem. Soc., Chem. Commun. 29–31 (1984).
Gephart, R. T. & Warren, T. H. Copper-catalyzed sp3 C–H amination. Organometallics 31, 7728–7752 (2012).
Paradine, S. M. et al. A manganese catalyst for highly reactive yet chemoselective intramolecular C(sp3)–H amination. Nat. Chem 7, 987–994 (2015).
Lu, H., Jiang, H., Wojtas, L. & Zhang, X. P. Selective intramolecular C–H amination through the metalloradical activation of azides: synthesis of 1,3-diamines under neutral and nonoxidative conditions. Angew. Chem. Int. Ed. 49, 10192–10196 (2010).
Gephart, R. T. et al. Catalytic C–H amination with aromatic amines. Angew. Chem. Int. Ed. 51, 6488–6492 (2012).
Paradine, S. M. & White, M. C. Iron-catalyzed intramolecular allylic C–H amination. J. Am. Chem. Soc. 134, 2036–2039 (2012).
Hennessy, E. T. & Betley, T. A. Complex N-heterocycle synthesis via iron-catalyzed, direct C–H bond amination. Science 340, 591–595 (2013).
McIntosh, J. A. et al. Enantioselective intramolecular C–H amination catalyzed by engineered cytochrome P450 enzymes in vitro and in vivo. Angew. Chem. Int. Ed. 52, 9309–9312 (2013).
Hennessy, E. T. & Betley, T. A. Complex N-heterocycle synthesis via iron-catalyzed, direct C-H bond amination. Science 340, 591–595 (2013).
Zhang, T., Manna, K. & Lin, W. Metal–organic frameworks stabilize solution-inaccessible cobalt catalysts for highly efficient broad-scope organic transformations. J. Am. Chem. Soc. 138, 3241–3249 (2016).
This work was supported by the NSF (CHE-1464941) and startup funds from the University of Chicago. We thank C. Poon and Dr A. Filatov for experimental help and Dr I. C. Hsiao for editing the manuscript. X-ray absorption spectroscopy analysis was performed at Beamline 9-BM, Advanced Photon Source (APS), Argonne National Laboratory (ANL). Use of the 9-BM beamline at the Advanced Photon Source, an Office of Science User Facility operated for the U.S. Department of Energy (DOE) Office of Science by Argonne National Laboratory, was supported by the U.S. DOE under Contract No. DE-AC02-06CH11357. Single-crystal diffraction studies were performed at ChemMatCARS, APS, ANL. ChemMatCARS is principally supported by the Divisions of Chemistry (CHE) and Materials Research (DMR), NSF, under grant number NSF/CHE-1346572. Use of the Advanced Photon Source, an Office of Science User Facility operated for the U.S. DOE Office of Science by ANL, was supported by the U.S. DOE under Contract No. DE-AC02-06CH11357.
The authors declare no competing financial interests.
Supplementary Figures 1-44, Supplementary Tables 1-12, Supplementary Discussion, Supplementary Methods and Supplementary References (PDF 4244 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Manna, K., Ji, P., Lin, Z. et al. Chemoselective single-site Earth-abundant metal catalysts at metal–organic framework nodes. Nat Commun 7, 12610 (2016). https://doi.org/10.1038/ncomms12610
This article is cited by
Construction of isolated Ni sites on nitrogen-doped hollow carbon spheres with Ni–N3 configuration for enhanced reduction of nitroarenes
Nano Research (2022)
Heterogeneous catalysts with programmable topologies generated by reticulation of organocatalysts into metal-organic frameworks: The case of squaramide
Nano Research (2021)
Recent Advances in the Engineering of Single-Atom Catalysts Through Metal–Organic Frameworks
Topics in Current Chemistry (2021)
Anisotropic reticular chemistry
Nature Reviews Materials (2020)
Study of CoCu Alloy Nanoparticles Supported on MOF-Derived Carbon for Hydrosilylation of Ketones
Catalysis Letters (2020)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.