Abstract
The imaging resolution of a conventional optical microscope is limited by diffraction to ∼200 nm in the visible spectrum. Efforts to overcome such limits have stimulated the development of optical nanoscopes using metamaterial superlenses, nanoscale solid immersion lenses and molecular fluorescence microscopy. These techniques either require an illuminating laser beam to resolve to 70 nm in the visible spectrum or have limited imaging resolution above 100 nm for a white-light source. Here we report a new 50-nm-resolution nanoscope that uses optically transparent microspheres (for example, SiO2, with 2 μm<diameter<9 μm) as far-field superlenses (FSL) to overcome the white-light diffraction limit. The microsphere nanoscope operates in both transmission and reflection modes, and generates magnified virtual images with a magnification up to ×8. It may provide new opportunities to image viruses and biomolecules in real time.
Similar content being viewed by others
Introduction
Optical microscopy is one of the most important scientific achievements in the history of mankind. It has revolutionized the field of life sciences and remains indispensible in many areas of scientific research. However, because of the diffraction limit, the imaging resolution of a classical optical microscope is limited to about half of the illuminating wavelengths λ. The root of the diffraction limit stems from the loss of evanescent waves in the far-field. These evanescent waves carry high spatial frequency subwavelength information of an object and decay exponentially with distance. In 2000, Pendry1 proposed a theoretical 'superlens' that produces perfect diffraction-free images. Such superlenses are engineered from a slab of artificial negative-refraction medium in which the evanescent waves, instead of decaying, are enhanced across the slab. This offers the possibility to restore the nanoscale information in the far-field and therefore a nearly perfect image can be recovered1. The first laboratory optical superlens was made of a thin slab of silver material. Through the resonant coupling of evanescence waves to surface plasmon polaritons (SPP) in silver, objects as small as 60 nm were successfully recorded on a near-field photoresist layer in the ultraviolet spectrum (λ/6 near-field resolution at λ=365 nm)2. Soon after, a SiC superlens working at mid-infrared frequency range (λ=11 μm, λ/20 near-field resolution) was demonstrated to resolve 540 nm holes3. However, these superlenses are 'near-sighted', as the images can only be picked up in the near-field4. To project a near-field image into the far-field, a far-FSL was shortly proposed and demonstrated5,6. The FSL used a silver slab to enhance the evanescent waves and an attached line grating to convert the evanescent waves into propagating waves in the far-field. The FSL did not magnify objects. An approach to the making of a magnifying superlens is to use two-dimensional SPP confined by a concentric polymer grating placed on a gold surface. It generates a ×3 magnification and a resolution of 70 nm at 495 nm wavelength (λ/7 far-field resolution)7. Hyperlens is another type of magnifying superlens. The hyperlens uses an anisotropic medium with a hyperbolic dispersion that generates a magnification effect through cylindrical or spherically curved multilayer stacks5,8,9. The hyperlens resolution reached 130 nm for 365 nm ultraviolet wavelength (λ/3 far-field resolution) and 160 nm for 410 nm visible wavelength (λ/2.6 far-field resolution), both with less than ×3 magnification9. Because of the SPP energy loss and sophisticated nanofabrication process, the resolutions of existing SPP superlens and hyperlens are limited at about (λ/3–λ/7) within the visible spectrum. The other practical limit is that the SPP superlenses must be excited/illuminated with a specific laser source and parameter configurations (wavelength, polarization and incident angle). These superlenses would not function under a standard white-light source. Furthermore, the specific laser source required for SPP excitation could heat up, absorbing samples and damaging them. Heating due to SPP loss in superlenses could be another undesired effect that affects target materials in optical imaging10. It is therefore of significant appeal for scientists and engineers to develop a white-light optical nanoscope that works across the visible spectrum. In contrast to the SPP superlens, nanolenses (thickness<800 nm, diameter<3 μm) in plano-spherical-convex shape made of dielectric materials, for example, calix hydroquinone, are naturally loss-free and have been recently fabricated using sophisticated techniques for subwavelength imaging. These nanolenses were nanoscale solid immersion lenses (nSILs)11 that resolve 220 nm line objects at 475 nm imaging wavelength (λ/2.2 far-field resolution, ×2 magnification)12. Compared with macroscopic SILs, wavelength-scale nSILs can produce a 25% smaller focus spot, which enhances the resolution11. However, it remains practically impossible for SILs to resolve nano-objects below 100 nm with visible light sources on the basis of solid immersion mechanism due to the shortage of high-index lens materials11,12.
In this study, we present a new 50-nm-resolution optical nanoscope that uses ordinary glass microspheres (n=1.46, 2 μm<diameter<9 μm) as FSL to overcome the white-light diffraction limit, attaining a resolution between λ/8 and λ/14 (far-field resolution) and a magnification between ×4 and ×8. Such a super-resolution white-light nanoscope would open up new opportunities for imaging viruses, DNA and molecules in real time.
Results
Microsphere nanoscope and experimental imaging performance
Figure 1 illustrates the schematic of a transmission mode white-light microsphere nanoscope. The microspheres are placed on the top of the object surface by self-assembly13. A halogen lamp with a peak wavelength of 600 nm is used as the white-light illumination source. The microsphere superlenses collect the underlying near-field object information, magnify it (forming virtual images which keep the same orientation as the objects in the far-field) and pick it up by a conventional ×80 objective lens (numerical aperture NA=0.9, Olympus MDPlan). In the experiments, gratings consisting of 360-nm-wide lines, spaced 130 nm apart, were imaged using 4.74-μm-diameter microspheres (Fig. 2a). The virtual image plane was 2.5 μm beneath the substrate surface and inside substrate. As can be seen from Figure 2a, only those lines with particles on top of them have been resolved. The lines without particles on top mix together and form a bright spot, which cannot be directly resolved by the optical microscope because of the diffraction limit (for the lowest visible wavelength λ=400 nm, the best diffraction-limited resolution is estimated to be 215 nm in air using the vector theory of Richards and Wolf14, and to be 152 nm by taking the solid immersion effect of a particle into account. For the main peak of a white-light source at λ=600 nm, the limits are 333 nm in air and 228 nm with solid immersion effect, respectively. Here, one should also note that the focal planes for lines with and without particles on top are different). The magnified image in Figure 2a corresponds to a ×4.17 magnification factor. Figure 2b shows a fishnet gold-coated anodic aluminium oxide (AAO) membrane imaged with 4.74-μm-diameter microspheres. The pores are 50 nm in diameter and spaced 50 nm apart. As it can be seen, the microsphere nanoscope resolves these tiny pores that are well beyond the diffraction limit, giving a resolution of between λ/8 (λ=400 nm) and λ/14 (λ=750 nm) in the visible spectrum range. It is important to note that the magnification in this case is around ×8, which is almost two times of that in the grating samples as shown in Figure 2a. This implies that the performance of microsphere superlens is affected by the near-field interaction of the sphere and the substrate. In our experiment, we have confirmed that the gold coating layer on the AAO surface not only enhanced the resolving power but also increased the magnification factor of the microsphere superlens. As self-assembled particles are easy to spread over a large surface area and meanwhile each particle can work as a superlens, the images produced by each particle can be stitched together to form a large image. These are the cases seen in Figure 2a,b, in which a hexagonal array of particles functions as an array of superlens covering a large area.
Our previous calculations reveal the fact that the Poynting vector of the radiation reflected by the surface transfers through the particle15, which permits the formation of an image in the reflection mode as well. Figure 3a demonstrates a Blu-ray DVD disk (200-nm-wide lines separated 100 nm apart) imaged with 4.74-μm-diameter microspheres in the reflection mode using the halogen light illumination. The subdiffraction-limited lines are clearly observed. Figure 3b shows another example of reflection mode imaging of a star structure made on SbTe DVD disk. The complex shape of the star, including the 90 nm corners of the star, was clearly resolved by the microsphere superlens. Further experiments have confirmed that complex shape structures can also be well imaged in the transmission mode and that both the transmission and reflection modes can achieve 50 nm resolution. Indeed, the microsphere nanoscope has proven its practicability and versatility in nanoimaging of various samples.
Experimental comparison with SILs imaging
It is important to mention that we have also conducted comparison experiments using two SILs (Supplementary Fig. S1), and confirmed that none of them can be used to resolve our samples with feature sizes between 50 and 130 nm (Supplementary Fig. S2). Immersion of samples 'into' solids, attained by positioning the samples in close contact with the flat bottom surface of the lens, provides a means to access a shorter working wavelength in lens materials, and thus higher resolution beyond that in air. The resolution limit of the SILs used in our experiments was ∼152 nm, which makes it impossible to resolve the 100 nm objects.
The imaging mechanism of the microsphere nanoscope
In principle, the imaging resolution and magnification of the microsphere superlenses are fundamentally related to their focus properties16. It is well known that small spheres can generate 'photonic nanojets' with super-resolution foci17, less well known is that such super-resolution foci are only achievable for a narrow window of (n, q) parameters, where n is the refractive index of the sphere and q is the size parameter defined as q=2πa/λ, according to Mie theory16. Figure 4a shows the calculated super-resolution window for different n and q parameters for spheres immersed in air. The y axis was calculated as (focus spot size−Rayleigh diffraction limit)/radius, which we name as super-resolution strength. For the n=1.46 spheres used in this study, super-resolution occurs for q<70, which corresponds to smaller than 9.0-μm-diameter spheres at a wavelength of λ=400 nm. From our experiments, it was verified that 10 and 50 μm spheres are not successful in 100-nm-resolution imaging tests, whereas 3.0 μm spheres produce clear 50-nm-resolution images as achieved by the 4.74 μm spheres. We also examined the use of 1 μm spheres for imaging. It is found that because of the small-view windows of such particles, high-resolution imaging was not successful. Therefore, the limit for 1 μm sphere is a practical conclusion rather than a theoretical one. The practical size window for n=1.46 microspheres is recommended as 2 μm<diameter<9 μm for 50-nm-resolution imaging. From Figure 4a, it can also be seen that refractive index has a strong effect on super-resolution foci; with n=1.8, the size window for super-resolution extends up to q∼250, which implies that particles as big as 30 μm could be used for nanoimaging. This would facilitate the experiments because of wider view windows offered by bigger particles. Moreover, one can see that the super-resolution strength is maximized at n=1.8. When refractive index increases further to n=2.0, the super-resolution strength reduces and super-resolution window shrinks, making it undesirable to use n>1.8 high-index materials for nanoimaging in our technique. On the contrary, high-index (n>1.8) materials are important for SILs as their imaging resolution is determined by the refractive index of lens materials because of the solid immersion mechanism.
Figure 4b,c compares the |E|2 intensity distribution for SIL, sphere and particle on surface calculated with the same parameters, that is, n=1.46, diameter=4.74 μm and λ=600 nm. Here, one important difference between SIL and sphere was demonstrated: a super-resolution focus outside of sphere and a diffraction-limited focus for the same-diameter SIL. Truncating of sphere into SIL causes the loss of super-resolution focus, and diffraction-limited spot of SIL makes it impossible to resolve below 100 nm objects. Super-resolution foci are the key requirement of our technique. With the presence of a substrate, the focus at particle–substrate contact region generally becomes sharper. This is evidenced by our particle on surface calculation (Fig. 4b,c). Such effects could enhance the imaging resolution according to the reciprocity principle18.
Magnification factor of the microsphere nanoscope
In cases of macroscopic spheres and SILs, in which geometrical optics applies, the virtual image magnification factor can be calculated through ray tracing as M=f/(f−a) for an object in contact with the lens surface, where f is the focal length and a is the distance between the object and the centre of the lens. Characteristically, spheres (M≈n/(2−n)) produce a higher magnification over the SILs counterparts (M≈n2) for n<2.0 because of their shorter focal length f (Supplementary Figs S3 and S4). As sphere size reduces to the super-resolution size window (2 μm<diameter<9 μm, n=1.46), geometrical ray tracing becomes invalid as evidenced by two signs. First, it fails to predict the magnification factor for those super-resolution spheres with f=a, as M=f/(f−a) becomes infinite in these cases. Second, optical rays going through such small spheres could form optical vortices and singularities inside the sphere. (Supplementary Figs S5 and S6). A mathematical model for near-field magnification with field singularities is still not available in literature. Here, we propose a fitting formula based on maximal field enhancement with some exponent, M≈(Imax/I0)β. We found that the factor β≈0.34 yields excellent agreement (<1% deviation) with exact virtual image magnification for geometrical optics approximation (Supplementary Fig. S4). Using this simplified estimation, one can determine the magnification factor for the particle on surface to be M≈5.5, which is in reasonable agreement with experimental values between 4 and 8 for different samples. In a similar manner, we found that magnification increases with particle size within super-resolution size window from M≈4 for 2 μm spheres to M≈7 for 9 μm spheres (Fig. 4d). The magnification-increasing tendency was also confirmed by experiments using 3.0 μm and 4.74 μm spheres; the magnification of 4.74 μm is about 1.2 times that of 3.0 μm spheres.
Discussion
The microsphere nanoscope demonstrated by us has a far-field resolution between λ/8 and λ/14 and a magnification between ×4 and ×8 Such resolution and magnification have greatly surpassed those of existing visible wavelength SPP hyperlens7,8 (resolution λ/7, magnification ×2.4) and nSILs11,12 (resolution λ/2.2, magnification ×2) within the visible spectrum; note that the SiC superlens resolution of λ/20, as demonstrated in the literature3, is not far-field resolution but a near-field resolution in mid-infrared spectrum range. The microsphere superlenses operate in a virtual imaging mode, and can be easily integrated with an ordinary optical microscope in both transmission and reflection modes, and work under a standard white-light illumination. From our estimations, it follows that maximal virtual image magnification can be attained with a refractive index n≈1.8. With 5 μm particles, it should resolve arbitrary structures <20 nm, making it possible to directly observe viruses and the inside of living cells under white light without the need to excite fluorescence using proper lasers as in molecular fluorescence nanoscopy19. As a final note, particles in other shapes, such as elliptical particles, could also be considered for below 50 nm imaging as near-field foci strongly depend on particle shape. In conclusion, we have demonstrated that optically transparent microspheres are high-performance optical superlens that could resolve 50 nm objects by near-field virtual imaging under a white-light source illumination. The microsphere nanoscope is robust, economical and is also easy to accommodate different kinds of samples with potential applications for imaging biological objects such as virus, DNA and molecules.
Methods
Imaging samples fabrication and preparation
The gratings used in Figure 2a were fabricated using a focused ion beam machine (Quanta 200 3D, FEI). The sample consists of 30-nm-thick chrome film coated on fused silica substrates. The AAO used in Figure 2b was fabricated by two steps anodizing in oxalic acid (0.3 mol l−1), under a constant voltage of 40 V. A porous 20-nm-thick metallic film (gold) was then formed by using a 300-μm-thick AAO as the template. The star sample used in Figure 3b was fabricated using contact particle lens array technique, which was developed by us recently20. The diluted SiO2 sphere suspension was applied onto the substrate surface by drop coating. The colloidal silica spheres (Bangs Laboratories) form an ordered monolayer through self-assembly. An Olympus microscope (MX-850), fitted with an ×80 objective lens (numerical aperture NA=0.9, Olympus MDPlan) was used to focus through the microsphere into the substrate and virtual images were collected and reported. All scanning electron microscopic images were taken by Hitachi S-3400N.
SILs imaging
Both 2.5-mm-diameter and 0.5-mm-diameter fused silica half-ball SILs) from Edmund Optics have been used for the control experiments (Supplementary Fig. S1). The SILs were placed directly onto imaging sample surface by careful manual handling, attaining an experimental configuration similar to that for the microsphere. An ×80 objective lens was used for the 0.5-mm-diameter SIL and a ×40 lens for the 2.5-mm-diameter SIL, as limited by the available gap between lens and sample. All samples as in Figures 2 and 3 have been tested with SILs without success. Example results on Blu-ray disk imaging without SILs and particles, with 0.5 mm SIL, with 2.5 mm SIL and with 4.74 μm sphere were shown for comparison in Supplementary Figure S2.
Simulation method
The geometrical optical ray tracing analysis (Supplementary Fig. S3) was carried out using Mathematica 7.0 software, and field distributions in Figure 4 were calculated by Mie theory for sphere and finite difference in time domain technique for SIL and sphere and particle on surface, respectively.
Virtual image magnification factor
Magnification factor for virtual image can be found by ray tracing under the approximation of geometrical optics (Supplementary Fig. S3). The focal lengths of SIL and sphere are fSIL≈an2/(n2−1) and fsphere≈na/2(n−1), respectively, where a is the radius. If a small point object A is situated at the plane of SIL at yA=y0≪a, then yimage≈n2y0, that is, magnification of the virtual image is MSIL≈n2. At similar conditions, magnification of the virtual image by the sphere is presented by Msphere≈n/(2−n). Thus, the spherical particle everywhere produces a higher magnification than SIL (Supplementary Fig. S3). Following the focusing properties of the sphere under the approximation of geometrical optics21, the field enhancement in the focal area is given by
Thus, under the approximation of geometrical optics, we have a relationship between field enhancement and magnification of virtual image, Msphere=f(Imax/I0), written in a parametric form, where refractive index n has a role of parameter, see in Supplementary Figure S4. This dependence with high accuracy can be approximated by a function Msphere≈(Imax/I0)β, with β≈0.34. The difference between the exact curve and approximated formula for M(n) is <1% for the whole range of refractive index from 1 to 1.95. Note that geometrical optics approximation yields singularity at n=2; thus, it cannot be applied in the vicinity of this point. Also, note that under the approximation of geometrical optics, field enhancement does not depend on the particle size. However, one can see this dependence under the approximation of the Mie theory, see Figure 4d in the article.
Energy flow simulation
Within the framework of classical Mie theory, the time-averaged Poynting vector (energy flow) is given by and field lines are the solutions of the differential equation dx/Sx=dy/Sy. We developed a Fortran program based on Mie formulation, and in Supplementary Figure S5, we present the Poynting vector lines for the microsphere with radius a=2.37 μm and refractive index n=1.46 illuminated by a plane wave with λ=600 nm. We can construct the virtual image, using the reciprocity principle and extrapolation of the Poynting vector, on the basis of this angle of vector line on the outer edge of the particle, see in Supplementary Figure S6. This method, in fact, uses the same idea of virtual image construction as in geometrical optics. We extrapolate not the straight ray but plot tangential line to the lines with some curvature. This image construction yields a magnification of 2–4 times depending on the particular Poynting vector line.
Additional information
How to cite this article: Wang, Z. et al. Optical virtual imaging at 50 nm lateral resolution with a white-light nanoscope. Nat. Commun. 2:218 doi: 10.1038/ncomms1211 (2011).
References
Pendry, J. B. Negative refraction makes a perfect lens. Phys. Rev. Lett. 85, 3966–3969 (2000).
Fang, N., Lee, H., Sun, C. & Zhang, X. Sub-diffraction-limited optical imaging with a silver superlens. Science 308, 534–537 (2005).
Taubner, T., Korobkin, D., Urzhumov, Y., Shvets, G. & Hillenbrand, R. Near-field microscopy through a SiC superlens. Science 313, 1595 (2006).
Zhang, X. & Liu, Z.W. Superlenses to overcome the diffraction limit. Nat. Mater. 7, 435–441 (2008).
Jacob, Z., Alekseyev, L. V. & Narimanov, E. Optical hyperlens: far-field imaging beyond the diffraction limit. Opt. Express 14, 8247–8256 (2006).
Liu, Z. W. et al. Far-field optical superlens. Nano Lett. 7, 403–408 (2007).
Smolyaninov, I. I., Hung, Y. J. & Davis, C. C. Magnifying superlens in the visible frequency range. Science 315, 1699–1701 (2007).
Rho, J. et al. Spherical hyperlens for two-dimensional sub-diffractional imaging at visible frequencies. Nat. Commun. 1, 150 (2010).
Liu, Z. W., Lee, H., Xiong, Y., Sun, C. & Zhang, X. Far-field optical hyperlens magnifying sub-diffraction-limited objects. Science 315, 1686 (2007).
Huang, X. H., Jain, P. K., El-Sayed, I. H. & El-Sayed, M. A. Plasmonic photothermal therapy (PPTT) using gold nanoparticles. Lasers Med. Sci. 23, 217–228 (2008).
Mason, D. R., Jouravlev, M. V. & Kim, K. S. Enhanced resolution beyond the Abbe diffraction limit with wavelength-scale solid immersion lenses. Opt. Lett. 35, 2007–2009 (2010).
Lee, J. Y. et al. Near-field focusing and magnification through self-assembled nanoscale spherical lenses. Nature 460, 498–501 (2009).
Whitesides, G. M. & Grzybowski, B. Self-assembly at all scales. Science 295, 2418–2421 (2002).
Richards, B. & Wolf, E. Electromagnetic diffraction in optical systems. II. Structure of the image field in an aplanatic system. Proc. R. Soc. London Ser. A 253, 358 (1959).
Luk'yanchuk, B. S., Wang, Z. B., Song, W. D. & Hong, M. H. Particle on surface: 3D-effects in dry laser cleaning. Appl. Phys. A 79, 747–751 (2004).
Wang, Z. B., Joseph, N., Li, L. & Luk'yanchuk, B. S. A review of optical near-fields in particle/tip-assisted laser nanofabriction. J. Mech. Eng. Sci. 224, 1113–1127 (2010).
Chen, Z. G., Taflove, A. & Backman, V. Photonic nanojet enhancement of backscattering of light by nanoparticles: a potential novel visible-light ultramicroscopy technique. Opt. Express 12, 1214–1220 (2004).
Potton, R. J. Reciprocity in optics. Rep. Prog. Phys. 67, 717–754 (2004).
Hell, S. W. Far-field optical nanoscopy. Science 316, 1153–1158 (2007).
Guo, W. et al. Near-field laser parallel nanofabrication of arbitrary-shaped patterns. Appl. Phys. Lett. 90, 243101 (2007).
Arnold, N. Theoretical description of dry laser cleaning. Appl. Surf. Sci. 208, 15–22 (2003).
Acknowledgements
We thank Dr Guanjie Liu for assisting in the AAO sample fabrication. This work is financially supported by the ASTAR/SERC grant 0921540099.
Author information
Authors and Affiliations
Contributions
Z.W. wrote the manuscript, conducted theoretical analysis and was involved in sample design and imaging experiments. W.G. conducted most of the imaging experiments and A.K. was involved in a part of the imaging experiments. L.L. initiated the particle imaging idea and supervised the whole project. Z.L. supervised the nanoimaging experiments. B.L. has considerably improved the manuscript presentation and the virtual imaging mechanism. Z.C. and M. H. contributed to the design and fabrication of samples. All authors contributed to the scientific discussion and revision of the article.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures S1-S6 (PDF 500 kb)
Rights and permissions
About this article
Cite this article
Wang, Z., Guo, W., Li, L. et al. Optical virtual imaging at 50 nm lateral resolution with a white-light nanoscope. Nat Commun 2, 218 (2011). https://doi.org/10.1038/ncomms1211
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms1211
This article is cited by
-
Dielectric microspheres enhance microscopy resolution mainly due to increasing the effective numerical aperture
Light: Science & Applications (2023)
-
Sub-50 nm optical imaging in ambient air with 10× objective lens enabled by hyper-hemi-microsphere
Light: Science & Applications (2023)
-
Wave optics of imaging with contact ball lenses
Scientific Reports (2023)
-
Far-field super-resolution chemical microscopy
Light: Science & Applications (2023)
-
The fabrication of microlens array in PMMA material with the assistant of nickel pillars by LIGA technology and thermal reflow method
Microsystem Technologies (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.