Original Article

Polymer Journal (2017) 49, 133–139; doi:10.1038/pj.2016.66; published online 27 July 2016

Twisting poly(3-substituted thiophene)s: cyclopolymerization of gemini thiophene monomers through catalyst-transfer polycondensation

Chunhui Zhao1,2, Kazuhiko Nagura3, Masayuki Takeuchi1,2 and Kazunori Sugiyasu1

  1. 1Molecular Design & Function Group, National Institute for Materials Science (NIMS), Ibaraki, Japan
  2. 2Department of Materials Science and Engineering, Graduate School of Pure and Applied Sciences, University of Tsukuba, Ibaraki, Japan
  3. 3International Center for Young Scientists, National Institute for Materials Science (NIMS), Ibaraki, Japan

Correspondence: Dr M Takeuchi or Dr K Sugiyasu, Molecular Design & Function Group, National Institute for Materials Science (NIMS), 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan. E-mail: TAKEUCHI.Masayuki@nims.go.jp or SUGIYASU.Kazunori@nims.go.jp

Received 13 May 2016; Revised 1 June 2016; Accepted 2 June 2016
Advance online publication 27 July 2016

Top

Abstract

Polythiophenes are an important class of materials in the field of organic electronics. The molecular structures of polythiophenes have a critical role in determining device performance; therefore, substantial efforts have been devoted to controlling their regioregularity, molecular weight and polydispersity. Herein, we demonstrate a new approach for controlling another structural parameter, the dihedral angle. We exploited the unique polymerization mechanism of cyclopolymerization: an alternating intramolecular–intermolecular chain propagation that produces a series of cyclic molecules along the polythiophene chain. We designed gemini thiophene monomers in which two thiophene monomers are tethered by an alkylene strap and we processed the monomers by using the catalyst-transfer polycondensation method. We found that the dihedral angle in the polythiophene is dictated by the size of the macrocycle formed.

Top

Introduction

In general, the polymerization of a monomer that has two polymerizable moieties results in insoluble cross-linked polymer networks. However, with an appropriate monomer design and optimized polymerization conditions, a soluble polymer can be obtained through a process called cyclopolymerization in which an alternating intramolecular–intermolecular chain propagation produces a series of cyclic molecules along the polymer chain.1, 2 To achieve this, monomers are generally designed such that thermodynamically favored five-or six-membered rings are formed. However, with an elaborate monomer design, large macrocycles can be produced, thus resulting in polymeric materials with the capacity of molecular recognition.3, 4, 5, 6, 7, 8 In addition, the alternating propagation process can be exploited for sequence control in a polymer main chain.9, 10 As such, cyclopolymerization is an intriguing polymerization methodology that allows access to novel polymer structures. The aim of the present study was to apply cyclopolymerization to the synthesis of poly(3-substituted thiophene)s (P3XT).

P3XT, in which ‘X’ represents the substituents, are semiconducting polymers that are widely used in various organic electronic devices.11, 12 Synthetic methodologies that produce well-defined P3XT structures have been developed in the past two decades and have contributed to the understanding of structure–property relationships.13, 14 The structural parameters regarding P3XT include regioregularity (head-to-tail selectivity), molecular weight and polydispersity, which are currently controllable because of recent advances in nickel catalyst-transfer polycondensation (CTP).15, 16, 17, 18, 19, 20 In this study, we focus our attention on another structural parameter, specifically the dihedral angle of the conjugated backbone, because it governs the effective conjugation length along the polymer chain.21, 22 Indeed, the dihedral angle has an important role in device performance. For instance, Bao and colleagues23 have reported that a twisted polythiophene backbone, compared with a planar polymer, achieves larger open-circuit voltages in bulk heterojunction solar cells. Given the nature of chain growth, the CTP method would enable cyclopolymerization of thiophenes (Scheme 1a). We can then deduce that the dihedral angle of P3XT is dictated by the size of the macrocycles formed (Scheme 1b). To date, cyclopolymerization that produces π-conjugated polymers has been limited to the synthesis of polyacetylene by ring-closing metathesis;24, 25, 26 to the best of our knowledge, this study is the first report of polythiophene synthesis through cyclopolymerization.

Scheme 1.
Scheme 1 - Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

(a) Proposed cyclopolymerization mechanism based on catalyst-transfer polycondensation. (b) Cyclopolymerization of GMms. (c and d) Synthetic scheme of the gemini thiophene monomer, GMm, 7, M8 and reference polymer P8: (i) 3-methoxyphenylmagnesium bromide, Ni(dppp)Cl2, THF, reflux; (ii) BBr3, DCM, 0°C; (iii) (AcO)2O, NaOH, THF; (iv) NBS, CHCl3, AcOH; (v) I2, PhI(OAc)2, DCM; (vi) NaOH aq.; (vii) Br(CmH2m)Br, Cs2CO3, DMF; (viii) octylbromide, Cs2CO3, DMF; (ix) iso-propylmagnesium chloride and lithium chloride, then the external catalyst; and (x) iso-propylmagnesium chloride and lithium chloride, then quenched with methanol. A full color version of this scheme is available at Polymer Journal online.

Full scheme and legend (139K)

Top

Experimental procedure

General

Reagents and solvents were purchased from commercial suppliers and used without further purification. Air- and/or water-sensitive reactions were conducted under argon by using dry solvents. Nuclear magnetic resonance (NMR) spectra were recorded on a JEOL ECS-400 (Tokyo, Japan, 400MHz) spectrometer. Matrix-assisted laser desorption ionization time-of-flight mass spectra were measured by using a Shimadzu AXIMA-CFR Plus station (Kyoto, Japan). Melting points were determined with a Yanako NP-500P micro melting point apparatus (Tokyo, Japan). Ultraviolet–visible absorption and fluorescence spectra were recorded on a JASCO V-630 spectrophotometer (Tokyo, Japan) and JASCO FP-8500 spectrofluorometer, respectively. The molecular weight distribution Mn and Mw/Mn (polydispersity index, PDI) values of the polymers were determined in tetrahydrofuran (THF) at 40°C (polystyrene standard for CPms and P8, and poly(methyl methacrylate) standard for P6′, where CP stands for cyclopolymer) using a TOSOH GPC system (Tokyo, Japan, HLC-8320GPC EcoSEC) equipped with two TSK gel super-multipore HZ-M columns and an ultraviolet detector (254nm).

Polymerization of gemini thiophene monomers

A typical procedure for cyclopolymerization of gemini thiophene monomers is as follows.27, 28 A round-bottomed flask was heated with a heat gun under reduced pressure. After the flask was cooled to room temperature, the gemini thiophene monomer GM4 (113mg, 0.138mmol) was placed in the flask. The flask was then evacuated and re-filled with argon three times. After the addition of a solution of LiCl (0.5moll−1 in THF, 1.108mmol, 2.22ml) and dry THF (20ml), a solution of iso-propylmagnesium chloride (2moll−1 in THF, 0.277mmol, 0.138ml) was added under 0°C. The resulting mixture was stirred at room temperature for 1h. Then, an external-initiator (o-tolyl)(1,2-bis(diphenylphosphino)ethane)nickel bromide (1.7mg, 5%) was added and the mixture was stirred again at room temperature overnight. The reaction mixture was quenched with 5M HCl aqueous solution, washed with water and extracted with CHCl3 three times. The combined organic layer was washed with brine and dried over MgSO4. After the solvent was evaporated, the product was purified by reprecipitation two times (THF/MeOH=1ml/30ml and then THF/acetone=1ml/30ml).

Ring-opening cross metathesis of CP6′ with butyl acrylate

A flask was charged with CP6′ (17.4mg, 40μmol), evacuated and re-filled with argon three times.29 CP6′ was dissolved in dichloromethane (DCM, 0.5ml), into which butyl acrylate (11.3mg, 89μmol) and Grubbs catalyst, second generation (1.7mg, 5%), were added in sequence. The resultant mixture was stirred at 40°C for 8h and then washed with water and extracted with CHCl3 three times. The combined organic layer was washed with brine and dried over MgSO4. After the solvent was evaporated, the product was purified by reprecipitation (THF/MeOH=1ml/30ml).

Top

Results and Discussion

Synthesis of monomers

We designed and synthesized gemini thiophene monomers in which 2-bromo-5-iodo-thiophenes, which are able to be processed by CTP,17, 18, 19 are tethered by alkylene straps (Scheme 1b: GMm, where GM stands for ‘gemini monomer’ and m represents the strap length). These monomers were synthesized in seven steps, as shown in Scheme 1c. Kumada–Tamao–Corriu cross-coupling between 3-methoxyphenylmagnesium bromide and 3-bromothiophene produced compound 1. We first conducted bromination of thiophene in 1 using N-bromosuccinimide; however, the reaction was not selective and the anisole moiety was also brominated. We therefore replaced the methoxy group with acetoxy group to alter the reactivity. With 3, bromination and subsequent iodination resulted in good yield, thereby producing the 2-bromo-5-iodo-thiophene skeleton, 5. Deprotection of the acetoxy group followed by Williamson ether synthesis produced gemini thiophene monomers, GMm. M8 and 7 were also synthesized as a reference monomer and a model compound for a ‘pendant’ defect, respectively (Scheme 1d). All the compounds were ambiguously characterized, as discussed in the Supplementary Information.

Cyclopolymerization of gemini thiophene monomers

CTP of GMms under common conditions ([GMm]=100mM, Ni(dppp)Cl2, THF, room temperature) resulted in insoluble orange precipitates, whereas M8 yielded a soluble regioregular polythiophene (P8), thus suggesting that the gemini monomers underwent cross-linking. We further optimized the concentrations and catalyst systems. Under diluted concentration conditions (6mM) and using an external catalyst ((o-tolyl)(1,2-bis(diphenylphosphino)ethane)nickel bromide30, 31), we obtained polythiophenes that were soluble in common organic solvents, briefly implying successful cyclopolymerization. We performed matrix-assisted laser desorption ionization time-of-flight mass spectral measurements using several matrices and additives (such as sodium trifluoroacetate); however, we did not observe the peaks of polymeric species. Size-exclusion chromatography revealed that the average molecular weights (Mns) of the obtained polymers were in the range of 6 to 9K with PDI values of 1.4 to 1.6 (Table 1). These values are not strong indicators of controlled polymerization, yet it is known that cyclopolymerization often results in a relatively large PDI value, in particular when a large macrocycle is designed.


1H-NMR spectra of CP4, CP6 and CP8 together with those of P8 and 7 are shown in Figure 1. Although the spectra are somewhat complicated to interpret, all the CPm spectra were similar. The integral ratios of the aromatic peaks (6.5–7.5 p.p.m.) to the OCH2 peak in the straps (~3.9 p.p.m.) were in agreement with the expected ratio (10H:4H). Compared with P8, CPms showed broad peaks, most probably because of slow molecular motion restricted by the strap. In addition, sharp peaks representing compound 7 were not clearly observed in CPms, thus suggesting that the pendant defect, which would be formed by the failure of cyclization, is negligible.

Figure 1.
Figure 1 - Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

1H-NMR spectra of (a)P8, (b) CP4, (c) CP6, (d) CP8 and (e) 7. The asterisks indicate the solvent peaks: deuterated DCM for polymers and chloroform for 7.

Full figure and legend (74K)

13C-NMR spectra were simpler than the 1H-NMR spectra and allowed for further characterization. Although the 13C-NMR spectra of the M8 and GM8 monomers were virtually the same (Supplementary Figure S2), the spectra of P8 and CP8 did not overlap (Figures 2b and c), thus indicating that these two polymers have distinct structures. 13C-NMR distortionless enhancement by polarization transfer experiments distinguish tertiary and quaternary carbons in the aromatic moiety. In P8 (as well as in M8 and GM8, as shown in Supplementary Figure S3), as anticipated, five tertiary carbons were observed (Figure 2d), whereas CP8 showed one additional tertiary carbon at 126.24 p.p.m. (as indicated by the arrow in Figure 2e). It is noteworthy that the two equivalent thiophenes in the gemini monomer become dissimilar after the cyclopolymerization in the linear sequence along the polymer chain (Scheme 1b). Taking the ring-current effect by the anisole moiety into account,32 we attribute the new peak to the tertiary carbon of thiophene located inside the macrocycle.

Figure 2.
Figure 2 - Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

(a) Structures of P8 and CP8. 13C-NMR spectra of (b) P8 and (c) CP8, and 13C-NMR distortionless enhancement by polarization transfer (DEPT) spectra of (d) P8 and (e) CP8. A full color version of this figure is available at Polymer Journal online.

Full figure and legend (98K)

To further corroborate the cyclic structure, we synthesized GM6′ in which the strap contains an olefin. GM6′ was polymerized under the optimized conditions and we obtained a cyclopolymer CP6′ (Mn=6.4K, PDI=1.4). Except for the olefin moiety, CP6′ showed similar 1H- and 13C-NMR spectra to those of CP6. However, treating CP6′ with butyl acrylate in the presence of a second-generation Grubbs catalyst significantly changed the spectra; as shown in Figure 3c, the 1H-NMR spectrum became sharper, thus suggesting that the conformational restriction was released. The peak of tertiary carbon at 126 p.p.m., which is characteristic of the cyclic structure (see above), disappeared after the metathesis reaction (Figures 3c and d). In addition, the 1H- and 13C-NMR spectra of CP6′ after the cross-metathesis reaction resembled those of P8. These results indicate that the cross-metathesis reaction opened the macrocycles, thus producing P6′ (Figure 3e). Importantly, the molecular weight did not change significantly after the metathesis reaction (Mn=5.3K, PDI=1.9), thus suggesting that the cross-link defect, if any, in CP6′ was insignificant. These results provide further indirect evidence of the proposed structure of the cyclopolymers.

Figure 3.
Figure 3 - Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

(a) Ring-opening cross-metathesis reaction of CP6′ with butyl acrylate. (b and c) 1H- and (d and e) 13C-NMR of CP6′ (a and d) before and (c and e) after the metathesis reaction. The peak indicated by the arrow in d disappears after the metathesis reaction. The asterisks indicate the solvent and residual water peaks in deuterated THF. A full color version of this figure is available at Polymer Journal online.

Full figure and legend (104K)

Structure–property relationship of cyclopolymers

Figure 4a compares the absorption spectra of CP4, CP6, CP8 and P8. Interestingly, the absorption maxima gradually blue-shifted as the strap length increased. Although the peak shift was not significant, we also observed a similar tendency in the fluorescence spectra (Figures 4b and c). The absorption spectra of CPms measured in the film state were similar to those measured in solution, a result that we believe corroborates the cyclic structure, because it should prohibit conformational changes on film formation. To gain insight into the structure–property relationship, we performed density functional theory calculations (B3LYP/6-31+G(d,p)) for the repeating units of CPm: cyclized bithiophenes (Figure 5). As the strap length increased, the dihedral angle became larger. By using the energy-minimized structures of cyclized bithiophenes (Figure 5 and Supplementary Figure S4), we conducted additional time-dependent density functional theory calculations for their trimers (that is, sexithiophene conjugation) (B3LYP/6-31G(d)//B3LYP/6-31(d)). Although the excitation energies were slightly overestimated, the highest occupied molecular orbital–lowest unoccupied molecular orbital gap increased as the strap length increased, a tendency that agrees well with the experimental results (Supplementary Figure S5).33

Figure 4.
Figure 4 - Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

(a) Absorption and (b) fluorescence spectra of CP4 (i), CP6 (ii), CP8 (iii) and P8 (iv). (c) Plots of (triangle) absorption maxima and (circle) fluorescence maxima as a function of the strap length. A full color version of this figure is available at Polymer Journal online.

Full figure and legend (101K)

Figure 5.
Figure 5 - Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

(a) Top and side views of the optimized structures of cyclic bithiophenes at the B3LYP/6-31+G(d,p) level. (b) Plot of the dihedral angle of the bithiophene unit as a function of the strap length. A full color version of this figure is available at Polymer Journal online.

Full figure and legend (70K)

A previous study by our group, conceptually related to the present study, has demonstrated that the dihedral angle of bithiophene is affected by cyclic side chains.34, 35, 36, 37 In STBm/n (Scheme 2), the movable range of the dihedral angle of the bithiophene backbone was defined by the length of the strap. The longer the strap, the larger the fluctuation of the dihedral angle (Scheme 2c). However, the change in absorption spectra induced by this approach was not significant.36 The present study adds another example of ‘strapped’ polythiophenes, which appear to be more effective than our previous molecular design concept in terms of controlling the dihedral angle.

Scheme 2.
Scheme 2 - Unfortunately we are unable to provide accessible alternative text for this. If you require assistance to access this image, please contact help@nature.com or the author

(a) Structure of STBm/n. (b) X-ray crystallographic structure of STB6/6. (c) Schematic illustration of the side views of STB6/6 and STB10/10, representing the control of the dihedral angle of the bithiophene backbone by changing the strap length. A full color version of this scheme is available at Polymer Journal online.

Full scheme and legend (61K)

Top

Conclusions

In conclusion, we present a proof-of-concept example of the synthesis of polythiophene through cyclopolymerization. To date, structural parameters, such as regioregularity, molecular weight and polydispersity, have been controlled using the CTP method. We demonstrate that another important structural parameter, the dihedral angle, can also be controlled by the monomer design. Therefore, the photophysical properties of polythiophene can be modulated.

The present study expands the scope of the CTP method in terms of the intramonomer condensation process; such an acrobatic CTP is expected to lead to the production of novel conjugated polymer structures.38, 39 Although the concept is still preliminary, optimization of the monomer structure as well as the polymerization conditions (for example, catalyst systems) should improve the controllability of quasi-living CTP and provide the ability to synthesize block and gradient polymers.30, 40, 41, 42 We are also interested in controlling the axial chirality of the bithiophene dihedral angle by using a chiral ligand; this research is now in progress in our laboratory.

Top

Conflict of interest

The authors declare no conflict of interest.

Top

References

  1. Butler, G. B. Cyclopolymerization and cyclocopolymerization. Acc. Chem. Res. 15, 370–378 (1982). | Article |
  2. Butler, G. B. Cyclopolymerization. J. Polym. Sci. A Polym. Chem. 38, 3451–3461 (2000). | Article |
  3. Ochiai, B., Ootani, Y. & Endo, T. Controlled cyclopolymerization through quantitative 19-membered ring formation. J. Am. Chem. Soc. 130, 10832–10833 (2008). | Article | PubMed | CAS |
  4. Edizer, S., Veronesi, B., Karahan, O., Aviyente, V., Degirmenci, I., Galbiati, A. & Pasini, D. Efficient free-radical cyclopolymerization of oriented styrenic difunctional monomers. Macromolecules 42, 1860–1866 (2009). | Article |
  5. Zhu, L., Lin, N.-T., Xie, Z.-Y., Lee, S.-L., Huang, S.-L., Yang, J.-H., Lee, Y.-D., Chen, C.-h., Chen, C.-H. & Luh, T.-Y. Ruthenium-catalyzed cascade metathetical cyclopolymerization of bisnorbornenes with flexible linkers. Macromolecules 46, 656–663 (2013). | Article |
  6. Narumi, A., Sakai, R., Ishido, S., Sone, M., Satoh, T., Kaga, H., Nakade, H. & Kakuchi, T. Enantiomer-selective radical polymerization of bis(4-vinylbenzoate)s with chiral atom transfer radical polymerization initiating systems. Macromolecules 40, 9272–9278 (2007). | Article | CAS |
  7. Sakai, R., Satoh, T., Kakuchi, R., Kaga, H. & Kakuchi, T. Helicity induction of polyisocyanate with a crown cavity on the main chain synthesized by cyclopolymerization of α, ω—diisocyanate. Macromolecules 37, 3996–4003 (2004). | Article | ISI | CAS |
  8. Terashima, T., Kawabe, M., Miyabara, Y., Yoda, H. & Sawamoto, M. Polymeric pseudo-crown ether for cation recognition via cation template-assisted cyclopolymerization. Nat. Commun. 4, 2321 (2013). | Article | PubMed |
  9. Hibi, Y., Tokuoka, S., Terashima, T., Ouchi, M. & Sawamoto, M. Design of AB divinyl ‘template monomers’ toward alternating sequence control in metal-catalyzed living radical polymerization. Polym. Chem. 2, 341–347 (2011). | Article | CAS |
  10. Hibi, Y., Ouchi, M. & Sawamoto, M. Sequence-regulated radical polymerization with a metal-templated monomer: repetitive ABA sequence by double cyclopolymerization. Angew. Chem. Int. Ed. 50, 7434–7437 (2011). | Article | CAS |
  11. Perepichka, I. G. & Perepichka, D. F. Handbook of Thiophene-Based Materials: Applications in Organic Electronics and Photonics, (John Wiley & Sons, Ltd., 2009).
  12. Roncali, J. Conjugated poly(thiophenes): synthesis, functionalization, and applications. Chem. Rev. 92, 711–738 (1992). | Article | ISI | CAS |
  13. McCullough, R. D. The chemistry of conducting polthiophenes. Adv. Mater. 10, 93–116 (1998). | Article | ISI | CAS |
  14. Mishra, A., Ma, C. Q. & Bauerle, P. Functional oligothiophenes: molecular design for multidimensional nanoarchitectures and their applications. Chem. Rev. 109, 1141–1276 (2009). | Article | PubMed | ISI | CAS |
  15. Yokoyama, A., Miyakoshi, R. & Yokozawa, T. Chain-growth polymerization for poly(3-hexylthiophene) with a defined molecular weight and a low polydispersity. Macromolecules 37, 1169–1171 (2004). | Article | CAS |
  16. Sheina, E. E., Liu, J. S., Iovu, M. C., Laird, W. & McCullough, R. D. Chain growth mechanism for regioregular nickel-initiated cross-coupling polymerizations. Macromolecules 37, 3526–3528 (2004). | Article |
  17. Bryan, Z. J. & McNeil, A. J. Conjugated polymer synthesis via catalyst-transfer polycondensation (CTP): mechansim, scope, and applications. Macromolecules 46, 8395–8405 (2013). | Article |
  18. Yokozawa, T. & Yokoyama, A. Chain-growth condensation polymerization for the synthesis of well-defined condensation polymers and π-conjugated polymers. Chem. Rev. 109, 5595–5619 (2009). | Article | PubMed | ISI | CAS |
  19. Yokozawa, T. & Ohta, Y. Transformation of step-growth polymerization into living chain-growth polymerization. Chem. Rev. 116, 1950–1968 (2016). | Article | PubMed |
  20. Kiriy, A., Senkovskyy, V. & Sommer, M. Kumada catalyst-transfer polycondensation: mechanism, opportunities, and challenges. Macromol. Rapid Commun. 32, 1503–1517 (2011). | Article |
  21. Ahn, T. K., Kim, K. S., Kim, D. Y., Noh, S. B., Aratani, N., Ikeda, C., Osuka, A. & Kim, D. Relationship between two-photo absorption and the π-conjuagtion pathway in porphyrin arrays through dihedral angle control. J. Am. Chem. Soc. 128, 1700–1704 (2006). | Article | PubMed |
  22. Mishchenko, A., Vonlanthen, D., Meded, V., Burkle, M., Li, C., Pobelov, I. V., Bagrets, A., Viljas, J. K., Pauly, F., Evers, F., Mayor, M. & Wandlowski, T. Influence of conformation on conductance of biphenyl-dithiol single-molecule contacts. Nano Lett. 10, 156–163 (2010). | Article | PubMed | ISI | CAS |
  23. Ko, S., Hoke, E. T., Pandey, L., Hong, S., Mondal, R., Risko, C., Yi, Y., Noriega, R., McGehee, M. D., Brédas, J.-L., Salleo, A. & Bao, Z. Controlled conjugated backbone twisting for an increased open circuit voltage while having short-circuit current in poly(hexylthiophene) derivatives. J. Am. Chem. Soc. 134, 5222–5232 (2012). | Article | PubMed | CAS |
  24. Schattenmann, F. J. & Schrock, R. R. Solube, highly conjugated polyenes via the molybdenum-catalyzed copolymerization of acetylene and diethyl dipropargylmalonate. Macromolecules 29, 8990–8991 (1996). | Article |
  25. Anders, U., Nuyken, O., Buchmeiser, M. R. & Wurst, K. Stereoselective cyclopolymerization of 1,6-heptadiynes: access to alternating cis-trans-1,2-(cyclopent-1-enylene)vinylenes by fine-tuning of molybdenum imidoalkylidenes. Angew. Chem. Int. Ed. 41, 4044–4047 (2002). | Article |
  26. Kang, E.-H., Lee, I. S. & Choi, T.-L. Ultrafast cyclopolymerization for polylene synthesis: living polymerization to dendronized polymers. J. Am. Chem. Soc. 133, 11904–11907 (2011). | Article | PubMed |
  27. Ohshimizu, K., Takahashi, A., Rho, Y., Higashihara, T., Ree, M. & Ueda, M. Synthesis and characterization of polythiophenes bearing aromatic groups at the 3-position. Macromolecules 44, 719–727 (2011). | Article |
  28. Lamps, J.-P. & Catala, J.-M. Kinetic study, by UV vis spectroscopy, on the strong effect of LiCl on the controlled polymerization of 2-bromo-3-hexyl-5-iodothiophene and 2-iodo-3-hexyl-5-bromothiophene: determination of the propagation rate constants, application to the synthesis of high molecular weight polydodecylthiophene. Macromolecules 44, 7962–7968 (2011). | Article |
  29. Randl, S., Connon, S. J. & Blechert, S. Ring opening-cross metathesis of unstrained cycloalkenes. Chem. Commun. 1796–1797 (2001).
  30. Palermo, E. F. & McNeil, A. J. Impact of copolymer sequence on solid-state properties for random, gradient and block copolymers containing thiophene and selenophene. Macromolecules 45, 5948–5955 (2012). | Article |
  31. Bronstein, H. A. & Luscombe, C. K. Externally initiated regioregular P3HT with controlled molecular weight and narrow polydispersity. J. Am. Chem. Soc. 131, 12894–12895 (2009). | Article | PubMed |
  32. Vernet, R. D. & Boekelheide, V. Nuclear magnetic resonance spectroscopy. ring-current effects on carbon-13 chemical shifts. Proc. Natl Acad. Sci. USA 71, 2961–2964 (1974). | Article | PubMed |
  33. Marsella, M. J. & Swager, T. M. Designing conducting polymer-based sensors: selective ionochromic response in crown ether containing polythiophene. J. Am. Chem. Soc. 115, 12214–12215 (1993). | Article |
  34. Pan, C. J., Zhao, C. H., Takeuchi, M. & Sugiyasu, K. Conjugated oligomers and polymers sheathed with designer side chains. Chem. Asian J. 10, 1820–1835 (2015). | Article | PubMed |
  35. Sugiyasu, K., Honsho, Y., Harrison, R. M., Sato, A., Yasuda, T., Seki, S. & Takeuchi, M. A self-threading polythiophene: defect-free insulated molecular wires endowed with long effective conjugation length. J. Am. Chem. Soc. 132, 14754–14756 (2010). | Article | PubMed | ISI | CAS |
  36. Ouchi, Y., Sugiyasu, K., Ogi, S., Sato, A. & Takeuchi, M. Synthesis of self-threading bithiophenes and their structure-property relationships regarding cyclic side-chains with atomic precision. Chem. Asian J. 7, 75–84 (2012). | Article | PubMed |
  37. Shomura, R., Sugiyasu, K., Yasuda, T., Sato, A. & Takeuchi, M. Electrochemical generation and spectroscopic characterization of charge carriers within isolated planar polythiophene. Macromolecules 45, 3759–3771 (2012). | Article |
  38. Pan, C. J., Sugiyasu, K., Aimi, J., Sato, A. & Takeuchi, M. Picket-fence polythiophene and its diblock copolymers that afford microphase separations comprising a stacked and an isolated polythiophene ensemble. Angew. Chem. Int. Ed. 53, 8870–8875 (2014). | Article |
  39. Wu, S., Sun, Y., Huang, L., Wang, J., Zhou, Y., Geng, Y. & Wang, F. Grignard metathesis chain-growth polymerization for poly(bithienylmethylene)s: ni catalyst can transfer across the nonconjugated monomer. Macromolecules 43, 4438–4440 (2010). | Article |
  40. Zhang, Y., Tajima, K., Hirota, K. & Hashimoto, K. Synthesis of all-conjugated diblock copolymers by quasi-living polymerization and observation of their microphase separation. J. Am. Chem. Soc. 130, 7812–7813 (2008). | Article | PubMed | CAS |
  41. Yokoyama, A., Kato, R., Miyakoshi, T. & Yokozawa, T. Precision synthesis of poly(N-hexylpyrrole) and Its diblock copolymer with poly(p-phenylene) via catalyst-transfer polycondensation. Macromolecules 41, 7271–7273 (2008). | Article |
  42. Hollinger, J., Jahnke, A. A., Coombs, N. & Seferos, D. S. Controlling phase separation and optical properties in conjugated polymers through selenophene−thiophene copolymerization. J. Am. Chem. Soc. 132, 8546–8547 (2010). | Article | PubMed |
Top

Acknowledgements

This work was supported by KAKENHI (Grant Numbers 23655108 and 25620101), Scientific Research on Innovative Aria ‘π-System figuration: control of electron and structural dynamism for innovative functions’ (26102009), and the Nanotechnology Network Project from the Ministry of Education, Culture, Sports, Science and Technology, Japan. We thank Dr Takashi Nakanishi (NIMS) for access to the workstation for theoretical calculation, and Dr Chengjun Pan (Shenzhen University) and Dr Fengniu Lu (NIMS) for fruitful discussions.

Supplementary Information accompanies the paper on Polymer Journal website