Abstract
Perovskite materials host an incredible variety of functionalities. Although the lightest element, hydrogen, is rarely encountered in oxide perovskite lattices, it was recently observed as the hydride anion H−, substituting for the oxide anion in BaTiO3. Here we present a series of 30 new complex hydride perovskite-type materials, based on the non-spherical tetrahydroborate anion BH4− and new synthesis protocols involving rare-earth elements. Photophysical, electronic and hydrogen storage properties are discussed, along with counterintuitive trends in structural behaviour. The electronic structure is investigated theoretically with density functional theory solid-state calculations. BH4-specific anion dynamics are introduced to perovskites, mediating mechanisms that freeze lattice instabilities and generate supercells of up to 16 × the unit cell volume in AB(BH4)3. In this view, homopolar hydridic di-hydrogen contacts arise as a potential tool with which to tailor crystal symmetries, thus merging concepts of molecular chemistry with ceramic-like host lattices. Furthermore, anion mixing BH4−←X− (X−=Cl−, Br−, I−) provides a link to the known ABX3 halides.
Similar content being viewed by others
Introduction
Interest in new complex metal hydrides during the past few years was initially driven by the extreme hydrogen densities and the potential to develop efficient and safe on-board hydrogen storage1. Metal borohydrides have large structural flexibility and display a range of other properties such as fast-ion conduction2,3 or permanent nano-porosity4. An Na-conducting borohydride-amide has been reported as an anti-perovskite type complex hydride5. Until now, metal borohydrides have been obtained by synthesis approaches that are hard to control and the often rather complex new materials have little potential for structural engineering and optimization of useful properties. Rational structure-property design is most readily accomplished in very simple and stable structure types, which are capable of accommodating a wide range of different elemental compositions. Recently, we discovered the first perovskite-type metal borohydride, KMn(BH4)3 (ref. 6), during thermal decomposition of K2Mn(BH4)4. Indeed, metal borohydrides usually crystallize with structures closely related to isoelectronic metal oxides. For instance, the polymorphs of Ca(BH4)2 are structurally related to the different modifications of TiO2 (ref. 7).
Prompted by these analogies, we have undertaken extensive investigations on perovskite-type borohydrides, the essentials of which we summarize here. New facile and easily scalable synthesis strategies, using a combination of solvent-based methods and mechano-chemical addition reactions, are developed for the synthesis of homoleptic perovskite-type metal borohydrides, whereas mechano-chemical metathesis reactions using metal halides provide anion-substituted metal borohydride-halides. Lanthanide borohydrides are also prepared in this study and act as precursors for both bi- and tri-metallic luminescent perovskite-type borohydrides. Thus, metal borohydrides can be utilized as ABX3-type host lattices.
Results
Formability of borohydride perovskites
Extensive systematic synthetic work has allowed us to successfully incorporate: A=K+, Rb+, Cs+, NH4+, CH3NH3+, B12H122−; B=Li+, Mg2+, Ca2+, Sr2+, Sn2+, Pb2+, Mn2+, Y3+, Ce3+, Eu2+, Yb2+, Gd3+, BH4− and X=BH4−, Cl−, Br−, I−, Rb+, Cs+ into the normal and inverse ABX3 providing two new interesting perovskite-type host lattices, AB2+(BH4)3 and A2LiB3+(BH4)6. Structural dynamics on the anion site are systematically introduced to the perovskite structure type, and anion substitution, where BH4− is partially replaced by the heavier halides, Cl−, Br− or I−, readily occurs, contributing to a vast structural flexibility and compositional diversity. Unlike most reported bimetallic borohydrides, the new series of perovskite materials shows a good thermal stability, often to 800 K, which may be lowered depending on the desired applications outlined below, effectively making them highly interesting host frameworks. However, metal borohydrides are often hygroscopic and may form di-hydrogen bonded solid hydrates, which may release hydrogen and form oxides upon heating. Hydrogen elimination and formation of oxides may occur at elevated temperatures, for example, T>350 K.
The classic formability criteria for the perovskite structure type are established for the novel compound series, revealing that metal borohydride perovskites form in the range ~0.8<t<0.95, where t is the Goldschmidt tolerance factor (Fig. 1). All new materials presented here have undergone a thorough crystallographic analysis. Table 1 lists the compounds most relevant to the discussion in this article and the complete list of 30 new compounds, their lattice parameters, crystal symmetries and high-temperature polymorphs is provided in Supplementary Table 1.
Lattice instabilities and di-hydrogen contacts
Metal oxide and related perovskites usually undergo a series of temperature-induced polymorphic transformations that are of great importance for their physical properties. This sequence of structural transformations is dominated by lattice instabilities, involving phonons corresponding to both octahedral rotations and polar displacements, in addition to some degree of orbital-induced effects in most compounds. These lattice distortions are stabilized at low temperatures, when the corresponding phonons, soft modes, condense. Therefore, the perovskite structure-type evolves to higher symmetries with increasing temperature. As a consequence of the symmetry increase, inversion symmetry is usually introduced, signifying the loss of interesting polar properties, such as a simple spontaneous polarization. Hence, new ways to generate low symmetries in perovskite compounds are of interest. In the following, we show that, contrary to oxide and halide perovskites, the prototypical structural high-temperature evolution to higher symmetries does not always hold for the BH4-series and that di-hydrogen contacts between neighbouring BH4 ligands appear as potential tools to tailor the symmetry.
A rigorous structural investigation of KCa(BH4)3 was undertaken during a search for ferroelectric distortions. At room temperature (RT), KCa(BH4)3 is orthorhombic (BH4 orientationally ordered) and crystallizes with the octahedral rotation pattern a0a0c+, which is characteristic of centrosymmetric tetragonal P4/mbm perovskites (Supplementary Table 1)8. In the symbol a0a0c+, superscripts refer to the sense of rotation and letters to the axis of rotation. The space group symmetry P4/mbm, however, is lowered because of the ordering of hydrogen atoms to the polar space group Pba2. Before the temperature-induced phase transition at 340 K, KCa(BH4)3 approaches tetragonal symmetry, following the intuitive structural evolution of perovskites (Fig. 2, Supplementary Fig. 1). The transition, however, is orthorhombic–orthorhombic, hence without symmetry increase. The changes in local structure are shown in Fig. 2c (Rietveld plots in Supplementary Figs 2–4). The unit cell axis c is doubled in the HT-polymorph (space group Pbn21), introducing a further octahedral tilt (a−a−c+), characteristic of the orthorhombic Pnma perovskites. Space group symmetry is lowered to Pbn21, again due to hydrogen ordering. Solid-state density functional theory (DFT) calculations were performed in different symmetries for the experimentally observed KCa(BH4)3-polymorphs, and also on the hypothetical tetragonal model, which is approached pre-transition, to determine the structural features preventing its stability. The results are summarized in Table 2 and optimized lattice parameters can be found in Supplementary Table 2. In Fig. 2 the minimum values for the interatomic hydrogen distances are highlighted, 2.126 and 2.415 Å in the LT and HT phases. In a fixed cell DFT optimization of the tetragonal model, this H···H distance drops to 1.983 Å. This value is considerably below the lowest values observed for borohydrides, similar to the Switendick criterion for stable hydrides9, 2.1 Å, which is one of the factors imposing limits on the stability of a metal hydride. An optimization in a variable cell converges to the orthorhombic lattice metric (Table 2), allowing us to identify close di-hydrogen contacts between neighbouring BH4 groups, which destabilize the tetragonal structure approached before the phase transformation. A wide range of experimental structures as well as DFT optimizations reported in the literature evidences the tendency of borohydride compounds to maximize H···H distances. Thus, assuming a repulsive nature of the homonuclear di-hydrogen contacts, we find an explanation for the unusual distortions in the high-temperature phases. In KCa(BH4)3, the close distances are relaxed to 2.415 Å in the HT-phase by 90° flips of every second axial BH4 group (Fig. 2c). The change of the octahedral tilt pattern corresponds to a very common instability in perovskites, occurring at the R-point of the Brillouin zone. The displacement generated by this instability is pointed out by arrows in Fig. 2b. In metal oxides, it involves the condensation of an octahedral rotation mode and commonly occurs in the low-temperature polymorph as a result of mode softening. In contrast, this instability is stabilized at increasing temperatures in KCa(BH4)3, owing to a new mechanism controlled by di-hydrogen contacts and suggested by DFT calculations. This is supported by further solid-state calculations on ordered bromine-substituted variants, KCa(BH4)2Br and KCa(BH4)Br2, which result in the stabilization of the tetragonal phase (Supplementary Discussion), because of the elimination of the respective short contacts by anion-substitution BH4−←Br−. Structural dynamics play an important role for this mechanism. The bandwidths of Raman and infrared active B-H bending modes were monitored across the phase transition (Fig. 2a, Supplementary Figs 5 and 6) and change abruptly at the critical temperature. This reflects a change in molecular B-H vibrations concurring with the lattice distortion identical in symmetry to the R-point instability, which in turn alludes to a certain degree of interaction between molecular and lattice vibrations. B-H vibrations involving critically close di-hydrogen contacts may thus be used to generate lattice distortions even at high temperatures in perovskite-type metal borohydrides.
These findings outlined in detail for KCa(BH4)3 are by no means restricted to specific tolerance factors but represent rather a general feature of borohydrides crystallizing with the perovskite structure. Temperature-induced lattice distortions have been discovered in various members of the AB(BH4)3 series, generating superstructures of up to 16 × unit cell volumes compared with a primitive cubic ABX3 unit cell, of which selected examples are given in Table 1. To our knowledge, unit cells of these dimensions have not been reported for such simple compositions. The largest superstructure is found for the commensurately modulated high-temperature polymorph HT1-RbCa(BH4)3, which has been stabilized at RT by Mg substitution on the B-site, shown in Fig. 3. The structural transformation of RT-RbCa(BH4)3 into the superlattice is accompanied by a significant negative unit cell volume contraction of over ΔV/V=−1.3%, exclusively due to the modulation taking place. RbCa(BH4)3 has two other high-temperature polymorphs that evolve to higher symmetries in agreement with the common structural behaviour of perovskites (Fig. 3d).
Systematic in-situ diffraction studies at variable temperature (Supplementary Fig. 7) show that the critical temperature Tc at which H···H interaction becomes sufficiently strong to drive a polymorphic transformation depends on the size of the A-cation, that is, Tc=340, 370–410 and 515 K for KCa(BH4)3, RbCa(BH4)3 and CsCa(BH4)3, respectively. The hydrogen-specific interactions tend quite frequently to generate complex distortions leading to large supercells in the borohydride family of perovskites.
Luminescence measurements
Lanthanides form the basis of red-green-blue colours in light emitting diode (LED)-based solid-state lighting with many important applications. Eu2+ luminescence based on the intense parity allowed transitions 4f65d1-4f7 is widely investigated as it is, together with Ce3+, the dominant activator in white light-emitting devices. A quantum yield of 75% was recently reported for the molecular compound [Eu(BH4)2(THF)2] and the absence of significant concentration quenching was attributed to the spatial separation of luminescent centres by BH4− (ref. 10). We have prepared various homoleptic lanthanide borohydrides with solvent-based methods, which act as precursors for tuneable perovskite-type host lattices. The lanthanide excited states, for example, those of Eu2+ or Yb2+, are not quenched by B-H vibrations in a homoleptic BH4-environment, making the borohydride perovskites a new host family of phosphors. The results from spectroscopic measurements are summarized in Fig. 4. Already neat CsEu(BH4)3 shows intense blue luminescence centred around 485 nm, 20 nm red-shifted from the precursor Eu(BH4)2 (Supplementary Fig. 8). The emission intensity of Eu2+-activated CsCa(BH4)3 (~5 mol% Eu2+) is qualitatively the same as that of bulk CsEu(BH4)3, suggesting the effect of concentration quenching to be minimal.
Eu2+ luminescence has also very recently been investigated in the perovskite CsCaBr3:Eu2+, serving as scintillator crystal11. Indeed, our results may be most readily compared with this compound as the structures are closely related. The excitation spectra both of CsCa(BH4)3:Eu2+ and bulk CsEu(BH4)3 are very similar and compare well to the one reported for Eu2+-activated CsCaBr3. The excitation spectrum of Eu2+ in the borohydride extends further into the visible compared with the bromide compounds, because of a larger crystal field splitting of the 5d electron involved in the d→f transition. The emission spectrum is considerably broader in the borohydride than the bromide-based compound, which alludes to a somewhat larger geometry difference between the ground and excited states. The temperature dependence of the band position and intensity of the Eu2+ emission was recorded between RT and 10 K, both for the doped and bulk materials, the latter being shown in Fig. 4a. Interestingly the concentration of Eu2+ in the lattice appears to have an effect on the energy-shift with temperature. Although at RT both bulk and doped emission are centred at 485 nm, spectra obtained at 10 K (Fig. 4b) demonstrate a red shift of approximately 25 nm for bulk CsEu(BH4)3, the band position being located in the green (510 nm) at 10 K. CsCa(BH4)3:Eu2+, on the other hand, does not follow this temperature dependency of the emission significantly. The origin of this is attributed to the tetragonal site symmetry, the Eu2+ centre in CsEu(BH4)3, whereas it is cubic in the host of CsCa(BH4)3, resulting in different thermal dilatations. In Fig. 4c the lifetimes of the excited states are presented. The exponential decay curves were described with single exponentials and are identical within experimental error for both doped and bulk materials, providing life times of approximately 500 ns for the Eu2+ emission, which remain constant over the entire investigated temperature range. This observation shows that there is no additional non-radiative decay path activated in this temperature range, which is remarkable for a host lattice with a rich B-H vibrational structure.
The reducing nature of the borohydride anion may be utilized to stabilize low oxidation states that are labile with respect to oxidation. This is the case, for example, for the divalent state of ytterbium Yb2+. Yb-doped crystals have been considered as potential laser crystals12 and have attracted attention as spectral conversion materials for warm-white LEDs13,14, but limited knowledge on Yb2+ is available when, for example, compared with Eu2+ or Ce3+, because of the reducing conditions required to stabilize the divalent cation in crystals.
A new stable Yb(II)-based borohydride perovskite is presented here. KYb(BH4)3 is orthorhombic and crystallizes with a commensurately modulated eightfold superlattice (Table 1), whose metric has not been reported for a simple ABX3 composition. The Yb2+ emission is centred at 520 nm, when excited in the ultraviolet at 355 nm. The lifetime of the excited state is comparable to that of the Eu2+ emission at RT.
However, the lifetime of the Yb2+ emission increases by three orders of magnitude between 300 and 10 K (Fig. 4c). A lifetime of 500 μs was determined from the decay curves at low temperatures, similar to that reported for Yb2+ in other host materials12. For a parity allowed transition lifetimes in the micro-second range are quite long. Two possibilities may be that the lowest 4f135d1 state is a triplet state, which would render the transition spin-forbidden, or that the emitting state is not 4f135d1, but 4f136s1, which would imply Δl=3 and hence the emission would be forbidden12.
Investigation of trivalent lanthanide ions is more challenging and requires a host material other than, for example, CsCa(BH4)3, adapted for divalent lanthanides. Such hosts are provided by A3B(BH4)6 and A2LiB(BH4)6. Based on this, we have designed new B-site ordered double-perovskite materials such as Cs3Gd(BH4)6, Rb3Ce(BH4)6 and Cs2LiCe(BH4)3 (Supplementary Table 1), illustrating that the borohydride perovskite lattice readily accommodates Ln3+ provided their oxidation state is stable against reduction by the BH4− anion, which we find to be the case for Gd3+ or Ce3+, for example, but not for Eu3+ or Sm3+. Luminescence spectra for Cs3Gd(BH4)6 and Cs2LiGd(BH4)6 are shown in Fig. 4d. The weaker bands occurring on the low-energy side of the sharp forbidden 6P7/2→8S7/2 (f-f) transition are denoted phonon-sidebands, which arise from energy-transfer to the lattice and are red-shifted by 1,400 and 2,500 cm−1, in perfect agreement with the energies of deformation and stretching vibrations of the BH4 molecule. The inset of Fig. 4d compares the low-energy region probed for both compounds. A broad band is visible here, which is attributed to Eu2+ impurities contained in the reactant used in the synthesis of Gd(BH4)3. The considerably broadened and asymmetric shape of this band can have its origin in the anomalous luminescence of Eu2+ (ref. 15). Both intensity and width of this band are larger in Cs2LiGd(BH4)6, likely due to a larger degree of disorder and vacancies. It is surprising that molecular B-H vibrations have no significant impact on the emission of lanthanide-excited states. Moreover, the optical properties may be tuned by halide substitution, BH4←Halide, and deuterium-hydrogen exchange, 2H←H, within the BH4-ligand itself. Borohydride lattices are rather ‘soft’, when compared with other hosts. This makes the emission of Lnn+ in borohydrides extremely sensitive to physical pressure, which can be relevant when applied as luminescent pressure sensors, especially in the low-pressure regime, where pressure determination remains challenging. The bulk modulus was extracted from equations of state determined for the potential hosts CsCa(BH4)3 and Cs2LiY(BH4)6 (Supplementary Fig. 9). The softness of material is remarkably high for a perovskite (~ 26% compression at 10 GPa) and yields small bulk moduli K0 of 27(1) and 28.3(8) GPa, respectively, similar to the larger halides but much smaller than oxides with typical values of over 150 GPa.
Electronic structure
The electronic structure calculated for selected compounds from the metal borohydride perovskites family shows that the compounds are wide-gap insulators of predominantly ionic nature. Covalent contributions are found for the bonding interactions between boron and hydrogen within the borohydride complex anion. This is readily seen from the partial density of states (DOSs) on the s-orbitals of hydrogen and the s- and p-orbitals of B, shown in Fig. 5a for the LT-polymorph of CsCa(BH4)3. The relevant orbitals of both the Cs and Ca come to lie deep within the core band. Band edges are hence dominated by B-H contributions. The DOS of the materials containing Gd, Y and Eu preserves identical features as compared with the Ca-salt. Their projected DOS are summarized in Supplementary Fig. 10. Calculated band structures (Supplementary Fig. 11) show that the band gap is direct at the Γ-point for most compounds. In compliance with the detailed structural characterization of KCa(BH4)3, the density of states and band structures were obtained for both the high- and low-temperature polymorphs of this compound to evaluate the impact of the octahedral rotations on the nature of the band gap. Interestingly, although the transition in the LT-phase is indirect, Z-Γ, because of states at the Z-point slightly higher in energy, it becomes direct, Γ-Γ, in the HT-polymorph. We recall that this transition is triggered by structural dynamics of the BH4, group which experiences a 90° flip in the HT-phase, and results in octahedral rotations identical in symmetry to the mentioned soft mode at the R-point. The coordinates of the symmetry point at the band gap experience a change at the valence band edge, which is exclusively occupied by boron and hydrogen states, from Γ to Z (Supplementary Fig. 11). The band gap energy increases very slightly after the phase transition. In the related plumbohalide compounds, such effects have been attributed to the octahedral tilts introduced in low-symmetry polymorph16,17, whereas the tilts are not found to impact on the nature of the gap. This suggests that it is the 90° re-orientation of the borohydride anion that induces the change in band gap from indirect to direct across the transition in KCa(BH4)3. The occupation of edge states can be modified by the introduction of elements with higher lying occupied orbitals. Remarkably, a novel caesium-lead borohydride, CsPb(BH4)3, was synthesized (Supplementary Table 1), which is the first non-molecular borohydride to contain a group IV metal, furthermore with the extreme electronegativity χ(Pb)=2.33 (refs 18, 19). Lead is rare on the B-site of a perovskite, and has recently attracted considerable interest among the light-harvesting plumbohalides in modern photovoltaics20,21. Tetragonal CsPb(BH4)3 is the first semiconducting metal borohydride with an experimental band gap of ~1.5 eV determined at RT, and releases 4.3 wt% gas at ~360 K (Supplementary Figs 12 and 13). The partial DOS on the Cs, Pb, B and H atoms is shown in Fig. 5b. As compared with the above-mentioned compounds, the band edges now contain a significant amount of s(Pb)-states at the valence band-edge and p(Pb)-states at the conduction band-edge, which hybridize with the ligand orbitals, hence creating covalent interactions to some extent in the octahedral Pb(BH4)3− framework, similar to what is reported for plumbohalides17,22. Anion substitution BH4−←Cl− further modifies states in the PbX3− framework of substituted variants as was theoretically investigated on CsPb(BH4)2Cl, whose DOS and band structure are summarized together with those of other compound in Supplementary Figs 10 and 11.
Hydrogen storage properties
Crystal engineering of KCa(BH4)3 (gravimetric hydrogen density ρm=9.7 wt% H2) is tempting by replacing potassium or calcium with a lighter weight cation in order to increase the gravimetric hydrogen density. However, both NaCa(BH4)3 and NaMg(BH4)3 lie outside the determined perovskite structural stability field (Fig. 1). A previous report mentions high hydrogen densities in a long list of about 20 perovskite-type metal hydrides23, for example, NaMgH3, and suggested a future expansion to complex hydrides such as NaMg(BH4)3.
The smallest stable inorganic hydrogen-rich cation is NH4+, similar in size to K+. We have succeeded in synthesizing an ammonium borohydride perovskite NH4Ca(BH4)3 (ρm=15.7 wt% H2), containing both protic and hydridic hydrogen, with short di-hydrogen bond Hδ−···Hδ+ distances of 2.2 Å, thus creating a predisposition to eliminate the hydrogen molecule by thermolysis with the onset slightly above 370 K (Fig. 6). NH4Ca(BH4)3 contains two highly disordered tetrahedral building units and can be considered the first successful stabilization of the metastable compound NH4BH4 with a very high hydrogen content of ρm=24.5 wt% H2. The tailoring of hydrogen storage properties by ammonia or amide has become an established approach24, but ammonium NH4+ has so far not been considered. The analysis of volatile decomposition products presented in Fig. 6 shows that there is no diborane released during the decomposition of the ammonium calcium perovskite. NH4Ca(BH4)3 releases one molecule of hydrogen during thermolysis and transforms to a new ammonia-borane complex Ca(BH4)2-NH3BH3 (Table 1), which releases additional hydrogen similar to previously reported reaction mechanisms for ammonia-borane complexes25,26.
We have also prepared a hybrid organic–inorganic perovskite material, CH3NH3Ca(BH4)3, by A-site substitution. Furthermore, an anti-perovskite structured compound Cs3B12H12BH4 is discovered to form in situ during the decomposition of Cs3Y(BH4)6 and Cs2LiY(BH4)6 (Y. Sadikin, personal communication, Supplementary Fig. 14). This compound may be considered the first member of a new class of closo-borane perovskite-like materials and constitutes the first in-situ observation of a well-crystallized closo-borane during the decomposition of a borohydride. Higher boranes have been suggested as important decomposition intermediates of metal borohydrides during hydrogen release reactions and are often considered to be responsible for the poor reversible hydrogen storage properties. However, structural in-situ observations have hitherto not been possible owed to the lack of crystallinity of such intermediates.
Discussion
The new series of compounds presented herein adds numerous new properties to the vast family of existing perovskite materials, from unprecedented structural behaviours dominated by weak interactions, denoted di-hydrogen contacts, known from concepts of molecular chemistry, to a variety of physical properties all attainable on the same host lattice. The chemistry of anion-mixing is expanded by the highly dynamic complex BH4, which hosts a number of unique features.
In particular, hydride-specific effects, unattainable by crystal engineering with other anions, can enrich the spectrum of mechanisms leading to lattice distortions and instabilities via weak interactions, as manifested for instance in the generation of large superlattices of borohydride perovskites. Thus, alternative mechanisms to generate lattice distortions in perovskites independent on orbital effects are presented here. Various approaches have been explored recently to stabilize ferroelectric distortions without the need of d-p hybridization requiring empty d-orbitals or ns2 lone pairs. For instance, A-site-driven ferroelectrics, such as geometric and hybrid improper ferroelectrics, generated by ordered layering schemes27,28,29 or purely electrostatic schemes as in YMnO3 (ref. 30). Both the di-hydrogen H···H contacts between BH4-ligands as well as the non-spherical shape of the anion are expected to be novel geometric tools for complex hydride perovskites to influence not only polarity by the anion-substitution BH4−←X− but also by lattice instabilities in novel candidate ferroelectrics.
While these hosts, on a structural level, merge the lattice-type-specific characteristics with new BH4-specific anion dynamics, they also constitute the first complex hydride series that can meet the requirements for genuine structure-property design. A large diversity in properties is therefore addressed herein, which in addition to applications in hydrogen storage spans solid-state phosphors, pressure sensors and, in future, possibly new electronic devices.
Exceptionally complex superlattices may be created to increase the number of crystallographically distinct emission sites, for instance to target white luminescence. Another, potentially useful, physical property of borohydrides is the interaction of elements with ionizing radiation. For instance, both boron and hydrogen have very high neutron cross-sections, providing an excellent pre-requisite for luminescent lanthanide-based scintillators using borohydride perovskites, for instance as thermal neutron detection devices.
The discovery of CsPb(BH4)3 contrasts the widely accepted semi-empirical relationship between the electronegativity and the stability of borohydrides18,19, suggesting that further disregarded electronegative elements from the periodic table may be incorporated into borohydride lattices. Borohydrides or borohydride-halides have till now not been explored regarding their electronic properties in the solid state. Electronic states generated by BH4− molecular orbitals and introduced into the Pb-X− bands may be a new tool to manipulate the band structure of plumbohalides.
The presented series of perovskites also contains light-weight materials potentially interesting for hydrogen storage applications. The usage of ammonium NH4+ as A-site cation allows stabilizing ammonium borohydride for the first time at RT. This describes an approach that is not restricted to perovskite-type borohydrides and the incorporation of NH4+ may be generalized to search for new hydrogen-rich compounds. A major drawback of boron and nitrogen-based hydrogen storage systems24 is the possible evolution of ammonia NH3 and diborane B2H6, which both lead to the failure of fuel cells. Neither of them are observed during the hydrogen release of NH4Ca(BH4)3.
In conclusion, this communication presents a range of new perovskite-type materials along with detailed investigations of structure and properties providing progress towards rational material design in complex hydrides.
Methods
Sample preparation
All samples investigated in this study were prepared by mixing appropriate quantities of starting materials and ball milling in argon atmosphere in a planetary Fritsch Pulverisette 7. Milling was performed at 600 r.p.m. with 60 repetitions at 2 min each and a 5-min break between each repetition to avoid overheating of the sample. Starting materials were purchased from Sigma-Aldrich: (KBH4, LiBH4, Ca(BH4)2, Mg(BH4)2, KCl, KBr, KI, CaCl2, CaBr2, CaI2, NH4Cl, CH3NH3Cl, EuCl2, CeCl3), Katchem Ltd. (RbBH4, CsBH4) or, in the case of not being commercially available, produced as outlined below. Sr(BH4)2 was synthesized according to a previously reported procedure31. For the neutron powder diffraction (NPD) experiment, isotope-enriched K11BH4 was purchased at Katchem Ltd. and subsequently deuterated at 400 °C and p(D2)=100 bar. Deuteration was achieved to 90%, as estimated by Raman spectra on the product and refined later on with NPD data. Ca(11BD4)2 was synthesized in house.
Synthesis of homoleptic monometallic lanthanide-borohydrides
Mn(BH4)2 and M(BH4)3 (M=Y or Gd) were prepared from a metathesis reaction between MnCl2 or MCl3 (M=Y or Gd) and LiBH4 in appropriate ratios. The reactants were ball milled (BM) separately in a Fritsch Pulverisette 6 planetary mill under inert conditions (argon atmosphere) in 80-ml tungsten carbide containers and balls (o.d. 6 mm). The sample-to-balls mass ratio was approximately 1:30 and a speed of 400 r.p.m. was selected while 5 min BM and 2 min pauses for 70 min (total BM time of 50 min) were applied. Subsequently, the reactants were added under vigorous stirring to a 2 M solution of dimethyl sulphide borane complex (S(CH3)2BH3) in toluene. The solution was kept for 72 h at RT. S(CH3)2BH3 was filtered away leaving a solid mixture of M(BH4)3 (M=Y or Gd) and LiCl. LiCl was removed from the samples by dissolution of Mn(BH4)2 or M(BH4)3 (M=Y or Gd) in dimethyl sulphide (S(CH3)2). Samples were left in (S(CH3)2) for 24 h under vigorous stirring32. The solution was successively filtered to remove LiCl and concentrated in vacuo using a rotary evaporator at T=50 °C until all the excess dimethyl sulphide had been removed and a white/yellow solid remained. α-Y(BH4)3 and Gd(BH4)3 were obtained in an adduct-free form by applying dynamic vacuum and heating at T=140 °C for 3 h, whereas the Mn(BH4)2 was heated to 110 °C.
Synchrotron and NPD
Synchrotron radiation powder X-ray diffraction data were collected at the Swiss Norwegian Beamlines of the European Synchrotron Radiation Facility (ESRF, Grenoble, France), at beamline I11 of Diamond Light Source (Didcot, England), at the Materials Science Beamline of the Swiss Light Source (Paul Scherrer Institute, Villigen, Switzerland) and at the High Energy Materials Science Beamline of Petra III (Deutsches Elektronen-Synchrotron, Hamburg). The NPD experiment was performed at the instrument HRPT of SINQ (PSI). Wavelengths of the corresponding experiments were 0.82257, 0.82712, 0.82711, 0.2072 and 1.8857 Å, respectively. For X-ray diffraction, samples were loaded into 0.5-mm borosilicate capillaries; for neutrons, a double-walled vanadium container was used, containing 2.2 g of sample. The superstructure reflections were indexed and the corresponding structures solved in direct space using the software FOX33. After structure solution, the respective models were refined with TOPAS34.
Structure determination of KCa(BH4)3
The characteristic cubic perovskite peaks were quickly identified on temperature-ramps collected between 100 and 700 K on the two-dimensional Pilatus M2 detector of SNBL BM01A. Superstructure reflections for both low-temperature and high-temperature polymorphs show excellent statistics on 2D data. The high-temperature polymorph is better crystallized, this was indexed first to an orthorhombic cell related by (sqrt2/sqrt2/2) to a hypothetical cubic KCa(BH4)3 prototype. After detailed inspection, two choices of space group remained, related by inversion symmetry, Pnma in setting Pbnm and Pna21 in setting Pbn21. The powder X-ray diffraction data did not allow to unambiguously determine the space group, but Rietveld refinements as well as sequential refinements turned out to be more stable for the non-centrosymmetric setting, Pbn21, which agrees well with the lower DFT energies (Supplementary Table 2) for this model.
Indexing of the low-temperature polymorph was much more challenging. In order to obtain the final model Pba2 for bulk LT-KCa(BH4)3, a full mode decompositions with Amplimodes35 were performed to establish possible relations between different distortion modes in different parent symmetries. A full set of solid-state calculations on all models that made sense from a theoretical and diffraction point of view was also carried out. Supplementary Table 2 provides representative DFT optimizations showing fully relaxed converged models.
Mode analysis
Distortion modes in the different polymorphs of KCa(BH4)3 were analysed with the Amplimodes35 applet available on the Bilbao crystallographic server ( http://www.cryst.ehu.es/), allowing to identify distortions that correspond to well-known soft modes frequently occurring in the perovskite lattice. The displacements were derived from the supposed tetragonal prototype P4/mbm that is approached before the structural phase transition. In polar Pba2 and P21212, the polar mode causing displacement along the unique pseudotetragonal axis was discarded by shifting the origin so that Ca atoms come to lie on (0/0/0) in all different models. The tetragonal prototype itself of course is derived from a cubic Pm-3m cell. To discuss the transition, however, it is useful to bring both orthorombic superstructures into context with P4/mbm.
Rietveld refinements
Structural refinements were carried out on all models allowing for the given lattice metric as derived above from the cubic prototype and compliant with crystallographic extinctions. BH4 was modelled as a rigid body in TOPAS34 with one free internal parameter being the bond length B-H. The same antibump restraints were applied in all refinement to ensure consistent refinements. For the case study on KCa(BH4)3, the orientation of the BH4 tetrahedron was additionally verified by refinements against neutron data collected at 15 K. Neutron data at high temperatures were not of sufficient quality to refine the high-temperature phase of KCa(BH4)3.
Vibrational spectroscopy
Infrared spectra were collected on a Bio-Rad Excalibur instrument (Bio-Rad; spectral resolution of 1 cm−1) and Raman spectra with a 488-nm solid-state laser and a Kaiser optical Holospec monochromator equipped with a liquid-cooled CCD (charge-coupled device) camera.
Thermogravimetric analysis
Differential scanning calorimetry and thermogravimetry were performed with a Netzsch 404 F3 Pegasus apparatus (Netzsch) under nitrogen flow.
Photophysical measurement
RT emission and excitation spectra were obtained using a Fluorolog 3-22 instrument. Variable temperatures down to 10 K were achieved with a closed cycle cryosystem (Janis-Sumitomo SHI-4-5, Janis) equipped with a computer-controlled temperature controller. Photo-excitation was carried out using the third harmonics of the Nd:YAG-pulsed laser (355 nm, pulse energy around 1 mJ per pulse, 20 Hz). Luminescence spectra were measured using a 0.28 m monochromator (Spex 280 M) equipped with a CCD camera (Jobin-Yvon CCD 3500, 150 g mm−1 grating). Luminescence kinetics were measured using the home-built 0.28 m monochromator (Spex 280 M) equipped with a photo multiplier (PM) tube. Absorption spectra were collected on a Bruker 66 FT-IR setup (Bruker).
Computational details
All the solid-state calculations were performed at DFT level of theory using the Vienna Ab initio Simulation Package (VASP) code36,37,38. A hybrid PBE0 functional39 was used to optimize the structures. Plane waves formed a basis set and the calculations were performed using the projector-augmented wave method40,41 and atomic pseudo-potentials42. The energy cutoff controlling the accuracy of calculations was set to 1,000 eV. Brillouin zones were sampled during structure optimization in 4/8 (DFT/Hartree-Fock) and in 32/64 (DOS calculation) k-points, respectively43,44. The positions of all the atoms in the respective computational cells were fully relaxed with both the lattice vectors fixed and optimized. Trajectories between special points of respective Brillouin zones were sampled in 10 k-points.
Additional information
How to cite this article: Schouwink, P. et al. Structure and properties of complex hydride perovskite materials. Nat. Commun. 5:5706 doi: 10.1038/ncomms6706 (2014).
References
David, W. I. F. Effective hydrogen storage: a strategic chemistry challenge. Faraday Discuss. 151, 399–414 (2011).
Unemoto, A., Matsuo, M. & Orimo, S. Complex hydrides for electrochemical energy storage. Adv. Funct. Mater. 68, 38–44 (2014).
Ley, M. B. et al. LiCe(BH4)3Cl, a new lithium-ion conductor and hydrogen storage material with isolated tetranuclear clusters. Chem. Mater. 24, 1654–1663 (2012).
Filinchuk, Y. et al. Porous and dense Mg(BH4)2 frameworks: synthesis, stability and reversible absorption of guest species. Angew. Chem. Int. Ed. 50, 11162–11166 (2011).
Somer, M. et al. α- and β-Na2(BH4)(NH2): Two modifications of a complex hydride in the system NaNH2-NaBH4; syntheses, crystal structures, thermal analyses, mass and vibrational spectra. J. Alloy. Compd 491, 98–105 (2010).
Schouwink, P. et al. Bimetallic borohydrides in the system M(BH4)2-KBH4 (M=Mg, Mn): on the structural diversity. J. Phys. Chem. C 116, 10829–10840 (2012).
Aeberhard, P. C., Refson, K., Edwards, P. P. & David, W. I. F. High-pressure crystal structure prediction of calcium borohydride using density functional theory. Phys. Rev. B 83, 174102 (2011).
Glazer, A. M. The classification of tilted octahedra in perovskites. Acta Cryst. B 28, 3384–3392 (1972).
Switendick, A.C. Band structure calculations for metal hydrogen systems. Z. Phys. Chem. 117, 89–112 (1979).
Marks, S. et al. [Ln(BH4)2(THF)2] (Ln=Eu, Yb)—A highly luminescent material. synthesis, properties, reactivity and NMR studies. J. Am. Chem. Soc. 134, 16983–16986 (2012).
Grippa, A. Y. et al. Crystal growth and scintillation properties of CsCaBr3:Eu2+ (CsCa1−xEuxBr3, 0≤x≤0.08). J. Cryst. Growth 371, 112–116 (2013).
Kueck, S., Henke, M. & Rademaker, K. Crystal growth and spectroscopic investigation of Yb2+-doped fluoride crystals. Laser Phys. 11, 116–119 (2001).
Zhang, Z. et al. Photoluminescence properties of Yb2+ in CaAlSiN3 as a novel red-emitting phosphor for white LED. J. Mater. Chem. 22, 23871–23876 (2012).
Yoo, H. S., Vaidyanathan, S., Kim, S. W. & Jeon, D. Y. Synthesis and photoluminescence properties of Yb2+ doped Ba5(PO4)3Cl phosphor for white light-emitting diodes. Opt. Mater. 31, 1555–1558 (2009).
Dorenbos, P. Anomalous luminescence of Eu2+ and Yb2+ in inorganics compounds. J Phys. Condens. Matter 15, 2645–2665 (2003).
Baikie, T. et al. Synthesis and crystal chemistry of the hybrid perovskite (CH3NH3)PbI3 for solid-state sensitised solar cell applications. J. Mater. Chem. A 1, 5628–5641 (2013).
Borriello, I., Cantele, G. & Ninno, D. Ab initio investigation of hybrid organic-inorganic perovskites based on tin halides. Phys. Rev. B 77, 235214 (2008).
Nakamori, Y. et al. Correlation between thermodynamical stabilities of metal borohydrides and cation electronegativities: first-principles calculations and experiments. Phys. Rev. B 74, 045126 (2006).
Schrauzer, G. N. Ueber ein periodensystem der metallboranate. Naturwissenschaften 42, 438 (1955).
Kim, H-S et al. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2, 591 (2012).
Green, M. A., Ho-Baillie, A. & Snaith, H. J. The emergence of perovskite solar cells. Nat. Photonics 8, 506–514 (2014).
Chang, Y. H. & Park, C. H. First-principles study of the structural and electronic properties of the lead-halide-based inorganic-organic perovskites (CH3NH3)PbX3 and CsPbX3 (X=Cl, Br, I). J. Korean Phys. Soc. 44, 889–893 (2004).
Ikeda, K., Sato, T. & Orimo, S.-I. Perovskite-type hydrides—synthesis, structures and properties. Int. J. Mat. Res 99, 471–478 (2008).
Jepsen, L. H. et al. Boron–nitrogen based hydrides and reactive composites for hydrogen storage. Mater. Today 17, 129–135 (2014).
Xiong, Z. et al. High-capacity hydrogen storage in lithium and sodium amidoboranes. Nat. Mater. 7, 138–141 (2007).
Wu, H. et al. A new family of metal borohydride ammonia borane complexes: Synthesis, structures, and hydrogen storage properties. J. Mater. Chem. 20, 6550–6556 (2010).
Benedek, N. A. & Fennie, C. J. Why are there so few perovskite ferroelectrics? J. Phys. Chem. C 117, 13339–13349 (2013).
Benedek, N. A., Mulder, A. T. & Fennie, C. J. Polar octahedral rotations: a path to new multifunctional materials. J. Solid State Chem. 195, 11–20 (2012).
Bousquet, E. et al. Improper ferroelectricity in perovskite oxide artificial superlattices. Nature 452, 732–736 (2008).
Van Aken, B. B., Palstra, T. T. M., Filippetti, A. & Spaldin, N. A. The origin of ferroelectricity in magnetoelectric YMnO3 . Nat. Mater. 3, 164–170 (2004).
Ravnsbæk, D. B. et al. Novel alkali earth borohydride Sr(BH4)2 and borohydride-chloride Sr(BH4)Cl. Inorg. Chem. 52, 10877 (2013).
Ley, M. B. et al. Novel solvates M(BH4)3S(CH3)2 and properties of halide-free M(BH4)3 (M=Y or Gd). Dalton Trans. 43, 13333–13342 (2014).
Favre-Nicolin, V. & Černý, R. FOX, ‘free objects for crystallography’: a modular approach to ab initio structure determination from powder diffraction. J. Appl. Cryst. 35, 734–743 (2002).
Coelho, A. A. TOPAS-Academic http://www.topas-academic.net/ (2012).
Orobengoa, D., Capillas, C., Aroyo, M. I. & Perez-Mato, J. M. AMPLIMODES: symmetry-mode analysis on the bilbao crystallographic server. J. Appl. Cryst. 42, 820–833 (2009).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for open-shell transition metals. Phys. Rev. B 48, 13115–13118 (1993).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comp. Mat. Sci 6, 15–50 (1996).
Perdew, J.P., Ernzerhof, M. & Burke, K. Rationale for mixing exact exchange with density functional approximations. J. Chem. Phys. 105, 9982–9985 (1996).
Blöchl, P.E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, J. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Kresse, G. & Hafner, J. Norm-conserving and ultrasoft pseudopotentials for first-row and transition elements. J Phys. Condens. Matter. 6, 8245–8527 (1994).
Bylander, D. M., Kleinman, L. & Lee, S. Self-consistent calculations of the energy bands and bonding properties of B12C3 . Phys. Rev. B 42, 1394–1403 (1990).
Teter, M.P., Payne, M.C. & Allan, D.C. Solution of Schrödinger’s equation for large systems. Phys. Rev. B 40, 12255–12263 (1989).
Pistorius, C. W. F. T. Melting and polymorphism of LiBH4 to 45 kbar. Z. Phys. Chem. 88, 253–263 (1974).
Acknowledgements
This work was supported by the Swiss National Science Foundation. Calculations were performed in the Computing Centre of the Slovak Academy of Sciences using supercomputing infrastructure acquired within the project ITMS 26230120002 and 26210120002 (Slovak Infrastructure for High-Performance Computing) supported by the Research and Development Operational Programme funded by the ERDF. The work was supported by the Danish National Research Foundation, Center for Materials Crystallography (DNRF93), the Danish Council for Strategic Research (HyFillFast), the Danish Research Council for Nature and Universe (Danscatt), the Carlsberg Foundation and the Slovak Grant Agency VEGA (2/0131/12). We further acknowledge the Swiss-Norwegian Beamlines of ESRF, the Swiss Light Source and SINQ of PSI and Petra III of DESY for the allocation of beamtime. We acknowledge Diamond Light Source for time on I11 under proposal EE7861 and Chiu C. Tang for an excellent technical support. We thank Vincenza D’Anna for assistance in the data collection of vibrational spectra, Yolanda Sadikin for the synthesis of Yttrium-, Ytterbium- and Cerium-based compounds and Tomáš Bučko for his usefull technical comments on band calculations using VASP code.
Author information
Authors and Affiliations
Contributions
P.S. and R.C. initiated the study. M.B.L. and P.S. prepared most of the samples. P.S. conceived and performed synchrotron X-ray diffraction experiments, R.C. and P.S. performed the neutron experiment and analysed X-ray and neutron diffraction data. P.S. performed vibrational spectroscopy and interpreted the data with the assistance of H.H. A.T. and P.S. collected photo-physical data and interpreted them together with H.H. Thermo-gravimetric analysis and absorption spectroscopy was performed by P.S. First-principles calculations were carried out by Ľ.S. The manuscript was written by P.S. and T.R.J. All authors commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-14, Supplementary Tables 1-2, Supplementary Discussion and Supplementary References. (PDF 1994 kb)
Rights and permissions
About this article
Cite this article
Schouwink, P., Ley, M., Tissot, A. et al. Structure and properties of complex hydride perovskite materials. Nat Commun 5, 5706 (2014). https://doi.org/10.1038/ncomms6706
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms6706
This article is cited by
-
A route towards the fabrication of large-scale and high-quality perovskite films for optoelectronic devices
Scientific Reports (2022)
-
Argyrodite-type advanced lithium conductors and transport mechanisms beyond paddle-wheel effect
Nature Communications (2022)
-
The effect of mechanically milled lead iodide powder on perovskite film morphology
Applied Physics A (2022)
-
Incorporation of expanded organic cations in dysprosium(III) borohydrides for achieving luminescent molecular nanomagnets
Scientific Reports (2021)
-
Chemically diverse and multifunctional hybrid organic–inorganic perovskites
Nature Reviews Materials (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.