Abstract
The quest for multiferroic materials with ferroelectric and ferromagnetic properties at room temperature continues to be fuelled by the promise of novel devices. Moreover, being able to tune the electrical polarization and the paramagnetic-to-ferromagnetic transition temperature constitutes another current research direction of fundamental and technological importance. Here we report on the first-principles-based prediction of a specific class of materials—namely, R2NiMnO6/La2NiMnO6 superlattices where R is a rare-earth ion—that exhibit an electrical polarization and strong ferromagnetic order near room temperature, and whose electrical and ferromagnetic properties can be tuned by means of chemical pressure and/or epitaxial strain. Analysis of the first-principles results naturally explains the origins of these highly desired features.
Similar content being viewed by others
Introduction
The search for multiferroic materials combining electric and magnetic behaviours in a single phase has attracted a lot of attention from the perspective of designing new devices1,2,3,4,5,6,7 and deepening our knowledge of materials and electromagnetism. One particularly important current research direction aims at the discovery of materials that possess electrical polarization and are ferromagnetic at room temperature. Strikingly, it appears that these two desired features rarely coexist4,6,8,9. For instance, Bi2MnReO6 and Bi2NiReO6 have been predicted to exhibit an electrical polarization at room temperature, but both the Re and Ni/Mn sublattices adopt an antiferromagnetic order, therefore yielding a ‘ferrimagnetic’ rather than ferromagnetic overall ordering near 300 K (ref. 4). Similarly, ferrimagnetism (or weak magnetization) instead of ferromagnetism occurs in other compounds possessing a room-temperature electrical polarization, and that is the case for GaFeO3 (ref. 6), hexagonal LuFeO3 epitaxial thin films7 and the solid solutions formed by mixing lead zirconium titanate and lead iron tantalite perovskites10. In other words, systems exhibiting both a significant electrical polarization and a strong magnetization near room temperature are very scarce (as also consistent with refs 11, 12).
On the other hand, double perovskite Bi2NiMnO6 has been recently synthesized and found to be ferroelectric below 485 K and ferromagnetic below 140 K (ref. 13). While this latter ordering occurs below room temperature, and therefore makes Bi2NiMnO6 useless for practical applications, Azuma et al.13 have been critical in pointing out the possibility of investigating double perovskites for the search of ferromagnets having a polarization near 300 K. Double perovskite oxides R2NiMnO6 (where R is a rare-earth element)14 are thus attractive, especially since La2NiMnO6 has a ferromagnetic Curie temperature Tcm~287 K and Tcm is nearly linearly dependent on (and thus tunable with) the radius of the rare-earth ion in R2NiMnO6 (ref. 14). Unfortunately, one shortcoming of the R2NiMnO6 systems is that they are ‘not’ ferroelectric but rather possess antipolar displacements resulting15 from their oxygen octahedral tilting pattern (a−a−c+ in Glazer’s notation16). Nevertheless, the possibility of inducing a spontaneous electrical polarization at room temperature in R2NiMnO6-based double perovskite oxides may exist, for example, by mixing them with La2NiMnO6 compounds to form short-period (001)-oriented R2NiMnO6/La2NiMnO6 superlattices. As a matter of fact, recent studies2,17 have shown that (001)-oriented (ABO3)1/(A′BO3)1 superlattices can exhibit an electrical polarization if both ABO3 and A′BO3 materials adopt an a−a−c+ tilting pattern, because of the mechanism called hybrid improper ferroelectricity17. It is therefore legitimate to wonder whether (001) R2NiMnO6/La2NiMnO6 superlattices can be ferromagnetic and have an electrical polarization near room temperature.
Here we report that such features can indeed be realized in these systems. Moreover, we show that their electrical polarization and magnetic Curie temperature can be tuned (and thus adjusted to desired values) by varying the chemical pressure (that is, the size of the rare-earth ion) and/or the epitaxial strain imposed by the substrates on which the R2NiMnO6/La2NiMnO6 superlattice films can be grown. Finally, this study also allows us to better understand the mechanism of hybrid improper ferroelectricity, by providing the atomistic energy and interactions that are responsible for it in R2NiMnO6/La2NiMnO6 systems.
Results
Structure and magnetic ordering in La2NiMnO6
As detailed in the Methods section, first-principles calculations are performed on La2NiMnO6 systems and on R2NiMnO6/La2NiMnO6 superlattices for which the Ni atoms only have Mn atoms as first-nearest neighbours of the B-sublattice and vice versa.
Let us first compare our predicted lattice parameters and magnetic moments of bulk La2NiMnO6, in its P21/n ground state, to experimental data, in order to check the accuracy of our approach. Ferromagnetic order of Ni and Mn ions is assumed here. The a, b and c lattice vectors in the 20-atom P21/n unit cell of La2NiMnO6 are along the pseudo-cubic [110], [-110] and [001] directions, respectively, and their magnitudes are calculated to be 5.466, 5.425 and 7.676 Å, respectively. They therefore agree rather well (namely, within 0.73%) with the results measured at 3.5 K (ref. 18), which are 5.506, 5.456 and 7.732 Å, respectively. Our computed magnetic moments for Ni2+ and Mn4+ are 1.54 and 3.13 μB, respectively. This is in reasonable agreement with both experimental (1.9 μB for Ni2+ and 3.0 μB for Mn4+)18 and previous first-principles (1.43 μB for Ni2+ and 3.0 μB for Mn4+)19 results.
Ferroelectric ordering in the superlattices
We initially build the R2NiMnO6/La2NiMnO6 superlattices by substituting La3+ ions by R3+ ions in every other AO (001) plane of the perovskite structure, and then relax both atomic positions and lattice vectors. Let us do such substitution by starting from the relaxed P21/n ground state of La2NiMnO6 (still assuming ferromagnetic order) and replacing the second LaO layer of our 20-atom periodic supercell by RO layers (see Fig. 1a). While the R2NiMnO6 and La2NiMnO6 bulk compounds exhibit a paraelectric P21/n ground state, the R2NiMnO6/La2NiMnO6 superlattices are all found to adopt an electrical polarization (and a polar P21 space group) after the full structural relaxation is reached. This electrical polarization is found here to be antiparallel to the in-plane b axis. Interestingly, we also numerically found that it can lie parallel to that axis when the R ions occupy the first, rather than second, AO layer of the 20-atom cell of our R2NiMnO6/La2NiMnO6 superlattices. Figure 2a further shows that the magnitude of this polarization increases on decreasing the rare-earth ionic radius, rR, therefore revealing the possibility of continuously tuning of this polarization via the so-called chemical pressure associated with the different size of the rare-earth ions20,21. In fact, since the ionic radius of La in La2NiMnO6 or R2NiMnO6/La2NiMnO6 material is about 1.16 Å (ref. 22; La has a coordination number of eight in these compounds), Fig. 2a also shows that the in-plane electrical polarization is enhanced when the difference of ionic radius between R and La increases. Practically, the electrical polarization ranges between 1.4 μC cm−2 for the Ce2NiMnO6/La2NiMnO6 system and 9.2 μC cm−2 for the Er2NiMnO6/La2NiMnO6 superlattice, such values being large enough to be experimentally detected. They are also of the same order as the in-plane electrical polarization predicted to exist, via the so-called hybrid improper ferroelectricity, in the BiFeO3/LaFeO3 superlattice grown on a (001)-oriented SrTiO3 substrate2 and in some other (ABO3)1/(A′BO3)1 superlattices17 combining two pure ABO3 and A′BO3 materials that adopt the a−a−c+ tilting pattern and are paraelectric. (Note that a and c in this notation of the tilting pattern refer to rotations around the pseudo-cubic <001> axes.)
Interestingly, our superlattices also possess a similar tilting pattern, with antiphase tilting of the NiO6 and MnO6 octahedra in the (a,b) plane as well as in-phase tilting about the out-of-plane c direction. Let us therefore determine whether the mechanism of hybrid improper ferroelectricity, that technically relies on an energy of the form λQ1Q2P based on symmetry arguments (where λ is a constant, Q1 and Q2 are in-plane antiphase and out-of-plane in-phase tilting modes, respectively, and P is the in-plane polarization), also applies to our investigated systems. If it does apply, we also wish to provide a microscopic understanding for the formation of the electrical polarization in our systems. For that, it is important to first recall that Bellaiche and Íñiguez15 demonstrated, via the introduction of specific atomistic interactions giving rise to the energy that was denoted ΔE1, that any a−a−c+ tilting pattern in any perovskite material should also generate antipolar motions of the A atoms that are parallel to the b direction in one (001) AO plane and then antiparallel to the b axis in the next (001) AO plane. Such antipolar displacements of the La ions are indeed numerically found in the relaxed P21/n state of bulk La2NiMnO6. We then decided to start from this latter state of La2NiMnO6 (adopting ferromagnetism), then substitute the second LaO layer by an RO layer (in our periodic 20-atom supercell) to create the R2NiMnO6/La2NiMnO6 superlattice shown in Fig. 1a, but preventing any ionic relaxation from occurring after such substitution is done. The resulting average forces along the b direction for all types of ions are displayed in Fig. 2b as a function of the rare-earth ionic radius22. Note that there are no average forces on any kind of atom along the a and c axes and, by average force, we mean the sum of the forces on the same kind of atoms divided by the number of these forces. Three important features are revealed by this figure. First of all, the force on the R3+ ions is the dominant one among all forces felt by ions along the b direction. Second, this force on the R3+ ions is antiparallel to the b axis (interestingly, we further found that this force is parallel to the b direction if the R ions occupy the first AO layer). Third, the magnitude of this force increases as rR decreases. It is thus clear that the electrical polarization of the fully relaxed R2NiMnO6/La2NiMnO6 superlattices shown in Fig. 2a mostly originates from the fact that the opposite antipolar motions (along the b direction) of R and La ions do not have the same magnitude, as schematized in Fig. 1b and also consistent with refs 2, 23. Such an inhomogeneity of antipolar motions can be understood when realizing that the ΔE1 atomistic energy provided in ref. 15 naturally leads (because of the a−a−c+ tilting pattern) to the (001) LaO layers of Fig. 1 experiencing a ‘global, macroscopic-like’ energy of the form −K1,LaωRωMuLa where K1,La is a positive constant, ωR and ωM are scalars characterizing the in-plane antiphase and out-of-plane in-phase tiltings, respectively24, and uLa is the displacement of the La ions along the b axis with respect to their ideal positions. Similarly, the (001) RO layers of Fig. 1 have an associated energy of the form +K1,RωRωMuR, where K1,R is another positive constant (which is different from K1,La because of the different chemical nature of the AO layers) and uR is the displacement of the R ions along the b direction. By summing these two different energies and introducing the polarization P=(uLa+uR)/2 and an antiferroelectric vector A=(uLa−uR)/2 (associated with the X-point of the five-atom cubic Brillouin zone), one obtains a total energy that can be decomposed into two novel parts, namely −(K1,La+K1,R)ωRωMA and −(K1,La−K1,R)ωRωMP. The former is responsible for the existence of a homogenous in-plane antiferroelectric vector in the superlattice, while the latter precisely characterizes the so-called hybrid improper ferroelectricity17,23. Note that the effective charges of La and R ions are found to be rather similar along the b axis (namely, around 4.15), with their differences typically ranging between 2% (when R=Ce) and 7% (when R=Er). One can thus directly relate polarization with ionic displacements of La and R ions, in first approximation (we numerically found that the difference in effective charges between La and R ions typically results in a change of a polarization that is five times smaller than the polarization arising from the assumption that La and R ions have the same average effective charge in the R2NiMnO6/La2NiMnO6 superlattices). Note also that the fact that Fig. 2a shows that the magnitude of the polarization is enhanced when the difference in size between the R and La ions increases implies that the coefficient in front of the second aforementioned energy, namely K1,La−K1,R, becomes larger as the size difference between R and La ions is bigger. Interestingly, if we start again from the symmetry–invariant energy ΔE1 provided in ref. 15 and consider the same tilting pattern as above (that is, same values of ωR and ωM), but choose the alternate ordering of the (001) LaO and RO planes (that is, with respect to the example above, we exchange the locations of La and R atoms), one can show that the polarization-inducing energy term turns out to be −(K1,R−K1,La)ωRωMP, that is, the same as above but with opposite sign. The minimization of this energy, via structural relaxation of the A atoms, implies that the polarization will then switch its direction when the R ions occupy the first (rather than the second) AO layer of the used 20-atom periodic supercell. Note that, ultimately, the phase matching between the La/R ordering and the antiphase rotations ωR determines the polarization direction. Note also that, and as demonstrated in refs 2, 25, the polarization of systems possessing trilinear coupling energy (as it is the case here) is switchable, which also typically leads to a switch of oxygen octahedral tiltings. It will also be interesting to determine in future studies whether this polarization switching is homogenous or (non)inhomogenous in nature (especially when defects are present in the grown sample). Finally, let us point out that, as shown in Fig. 1b, any two first-nearest neighbouring R (respectively, La) ions in any (001) AO plane move in an antiparallel manner to each other along the a axis—that is, along the in-plane direction that is perpendicular to the polarization. Such an additional displacement originates from the ΔE2 atomistic energy of ref. 15, which induces another antiferroelectric vector (in this case associated with the R-point of the five-atom cubic Brillouin zone) as a result of the a−a−c+ tilting pattern. Such additional displacements average out to zero in any (001) AO plane, and therefore do not give rise to any component of the macroscopic spontaneous polarization along the a axis.
Magnetic ordering in the superlattices
Having understood the origin of the polarization in the R2NiMnO6/La2NiMnO6 superlattices, it is clear that this polarization should remain non-zero at room temperature since the energy −(K1,La−K1,R)ωRωMP implies that the polarization is driven by the oxygen octahedral tiltings and both the antiphase and in-phase oxygen octahedral tiltings are known to exist at ambient conditions in both La2NiMnO6 and R2NiMnO6 pure materials26. Let us now check whether these superlattices can also exhibit a significant magnetization at 300 K, which would thus make them room-temperature multiferroics. First, note that Fig. 2c shows that the computed magnetization of the R2NiMnO6/La2NiMnO6 superlattices at T=0 K is large (of the order of 2.4–2.5 Bohr magneton per five atoms) for any R ion, as consistent with a strong ferromagnetism. To determine whether this magnetization can persist up to room temperature, we calculate the paramagnetic-to-ferromagnetic Curie point of R2NiMnO6/La2NiMnO6 superlattices (see Fig. 2d). We first investigate the Curie temperature of bulk R2NiMnO6 and La2NiMnO6 double perovskites as a function of the rare-earth ionic radius, arising from the use of different Hubbard U values (see Supplementary Fig. 1 and Supplementary Discussion). The calculated Curie temperatures are systematically overestimated compared with the experimental values14. In addition, the increasing of Hubbard U enhances TC in bulk R2NiMnO6 and La2NiMnO6. Thus, we multiplied the first-principles-derived exchange constants (with Hubbard U 3.0 eV for both Ni and Mn) of all the spin Hamiltonians used in this work by a factor of 0.685, which is the correction needed so that the Heisenberg Hamiltonians reproduce all the experimental paramagnetic-to-ferromagnetic transition temperatures of the different R2NiMnO6 systems14 (see Supplementary Fig. 2 and Supplementary Discussion). The calculated Curie temperature of R2NiMnO6/La2NiMnO6 superlattices decreases from ~290 to ~165 K when going from R=Ce to R=Er. As a result, the magnetic temperature of R2NiMnO6/La2NiMnO6 is significantly tunable (that is, by >100 K) via the chemical pressure associated with the size of the R ions, and Ce2NiMnO6/La2NiMnO6 superlattice is a specifically promising candidate for designing a near room-temperature multiferroic material. These two findings are of obvious technological importance. Please note that our calculated Curie temperature of Ce2NiMnO6/La2NiMnO6 superlattice is the largest one compared with the other eight R2NiMnO6/La2NiMnO6 superlattices as well as bulk La2NiMnO6. This leads us to gain more insight into La2NiMnO6 and R2NiMnO6. Thus we investigate the correlation between Curie temperature of bulk R2NiMnO6 perovskites and antiphase as well as in-phase tilting angles (see Supplementary Figs 3 and 4 and Supplementary Discussion).
Effects of epitaxial strain on physical properties
All the aforementioned calculations concern fully relaxed R2NiMnO6/La2NiMnO6 systems. However, in some cases, some lattice vectors are imposed by external conditions and thus cannot relax to their equilibrium values. This is the case for epitaxial (001) thin films, for which the in-plane lattice parameters are those of the substrate on top of which the films are grown. It is thus relevant to investigate the effect of an epitaxial misfit strain on properties of the R2NiMnO6/La2NiMnO6 superlattices. For that purpose, the calculated electric polarization and Curie temperature of (001)-oriented films made of Ce2NiMnO6/La2NiMnO6, Pr2NiMnO6/La2NiMnO6, Sm2NiMnO6/La2NiMnO6, Er2NiMnO6/La2NiMnO6 and La2NiMnO6, are shown in Fig. 3a,b as a function of the in-plane lattice parameter (aIP). Our calculated results first show that the electric polarization of the investigated R2NiMnO6/La2NiMnO6 superlattices is basically independent of the epitaxial strain, with the exception of Er2NiMnO6/La2NiMnO6 for which the polarization slightly increases from ~9.0 to ~10.5 μC cm−2 when aIP decreases from 3.96 to 3.68 Å. This insensitivity of the polarization with strain is technologically useful since it implies that the polarization persists for a large choice of available substrates. It is also fundamentally interesting since it goes against the common knowledge that in-plane polarization of (001) films should rapidly decrease, and even disappear, when decreasing the in-plane lattice constant (that is, when the strain becomes compressive and large in magnitude)27,28,29. In fact, and as consistent with what was recently found for rare-earth orthochromates20, such a unusual and weak dependence of the in-plane polarization on the strain is due to the fact that a larger epitaxial compression tends to reduce the in-plane antiphase tilting ωR while increasing the out-of-plane in-phase tilting ωM. As a result, the product ωRωM is largely independent of the strain, and so is the in-plane polarization that depends on this ωRωM product via the aforementioned hybrid improper ferroelectricity mechanism.
Moreover, Fig. 3b shows that the paramagnetic-to-ferromagnetic Curie temperature of the superlattices (and La2NiMnO6) is rather sensitive to the epitaxial strain, as consistent with ref. 30 and magnetostriction: as aIP decreases, the Curie temperature goes up significantly at first, to eventually become weakly aIP dependent. Figure 3b therefore shows that one can also create a near room-temperature multiferroic, and tune magnetic transition temperature, by applying an appropriate epitaxial strain in the R2NiMnO6/La2NiMnO6 superlattices. In particular, (001) Ce2NiMnO6/La2NiMnO6 films are promising materials to exhibit magnetization and polarization above 290 K, when grown on any substrate having an in-plane lattice constant ranging between 3.70 and 3.80 Å (which corresponds to an average compressive epitaxial strain experienced by Ce2NiMnO6/La2NiMnO6 films varying between −3.9% and −1.3%).
Discussion
We have discovered that (and understood why) (001)-oriented R2NiMnO6/La2NiMnO6 superlattices can adopt an electrical polarization and be ferromagnetic essentially up to room temperature. Moreover, our first-principles calculations also reveal that the electric and magnetic properties can be tuned by chemical pressure and/or epitaxial strain in these systems. We thus hope that our predictions will soon be experimentally confirmed and used to design novel spintronic devices. Note that these predictions are for R2NiMnO6/La2NiMnO6 superlattice systems that are perfectly chemically ordered, and that disordering on the A- or B-sites likely will affect physical properties. It is thus important for experimentalists to fully control atomic ordering in the grown samples in order to be able to check our predictions. We are optimistic that our proposed R2NiMnO6/La2NiMnO6 superlattices will be successfully grown in a near future based on the facts that similar compounds (namely, NaRMnWO6 and, especially, Bi2NiMnO6/La2NiMnO6 superlattices) have already been synthesized31,32. Note also that polarization and magnetism are coupled in our R2NiMnO6/La2NiMnO6 superlattices since polarization is typically found to be enhanced by around 3% when going from the ferromagnetic to ferrimagnetic state (for which Mn and Ni ions being nearest neighbours to each other have opposite direction of their magnetic moment as well as different magnitudes for these moments). It is also important to realize that not all possible devices using multiferroics require a strong coupling between polarization (P) and magnetization (M). For instance, one can think of a four-state memory for which +/−P and +/−M can be accessed by using electric and magnetic fields, respectively, and for which it is desired to have a weak (rather than strong) coupling between P and M33. We also hope that other room-temperature ferromagnetic multiferroics will be discovered following the general design principles employed here—namely: to combine two paraelectric compounds that are both ferromagnetic within a superlattice, create an electrical polarization in the resulting superlattice via the so-called hybrid improper ferroelectricity mechanism, and tune electrical and magnetic properties of the superlattice by chemical pressure or epitaxial strain.
Methods
Calculation of structure and ferroelectric polarization
First-principles calculations are performed on La2NiMnO6 systems and on R2NiMnO6/La2NiMnO6 superlattices by using the Vienna ab initio Simulation Package (VASP) within the framework of the projected augmented wave method34. As consistent with ref. 14, a specific chemical ordering is assumed for all these compounds so that, within the B-sublattice, Ni atoms only have Mn atoms as first-nearest neighbours and vice versa. Practically, we investigate R=Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho and Er, and R2NiMnO6/La2NiMnO6 superlattices are built from La2NiMnO6 by replacing every other (001) LaO plane by a plane with RO composition (see Fig. 1 drawn by VESTA code35). The generalized gradient approximation GGA+U method with the parameterization of Perdew–Burke–Ernzerh revised for solids (PBEsol)36 is used in the present work. The effective on-site Coulomb interaction is selected to be 3 eV for both Ni2+ and Mn4+ ions, in line with typical choices in the literature19,37. We treat the valence electron configuration as follows: 5s25p65d16s2 for La, Ce, Pr, Nd, Sm; 5p65d16s2 for Gd, Tb, Dy, Ho, Er; 3d94s1 for Ni; 3d64s1 for Mn; and 2s22p4 for O. The 4f electrons of rare-earth ions are thus kept as core electrons owing to the fact that partially filled f orbitals are usually not well described by the current density functional theory (see, for example, ref. 34) and the properties studied in this article can be well mimicked without explicitly treating the 4f electrons. For instance, Supplementary Fig. 2 shows that the experimental Curie temperatures of bulks R2NiMnO6 of ref. 14 can be very well reproduced without the need to incorporate 4f electrons in the valence, which is consistent with the known facts that 4f electrons only contribute to magnetism at very low temperature26. Similarly, we numerically found that the inclusion of the 4f electrons has a relatively small effect on structural properties at 0 K, as demonstrated by the change of the a, b and c lattice parameters of Gd2NiMnO6 by only 0.5%, 0.08% and 0.4%, respectively, with respect to the case when these 4f electrons are kept in the core. We also use a plane wave energy cut-off of 500 eV and a 6 × 6 × 4 k-point mesh for Brillouin zone integrations. Structural optimizations were stopped when forces were <0.005 eV Å−1. The space group of the different phases encountered in the present work is determined by using the FINDSYM software38 and the electric polarization is calculated by the Berry phase approach39 (note that the electric polarization is evaluated by choosing the P21/n ground state of bulk La2NiMnO6 as reference).
Calculation of magnetic Curie temperature
The in-plane and out-of-plane magnetic exchange constants JNi-Mn determined from our first-principles calculations are taken as input for an effective Heisenberg Hamiltonian H=½ΣJNi-MnSNi·SMn, where we assume classical spins and take |SNi|=|SMn|=1 for simplicity (these exchange constants are reported in Supplementary Tables 1 and 2). To compute the magnetic ordering temperatures, we solve such Hamiltonians by means of Monte Carlo simulations40 of a 20 × 20 × 20 periodically repeated simulation supercell that contains 4,000 Ni spins and 4,000 Mn spins. We use 40,000 Monte Carlo sweeps for thermalization and 60,000 additional sweeps for computing statistical averages. Finally, note that we multiplied the first-principles-derived exchange constants of all the spin Hamiltonians used in this work by a factor of 0.685, which is the correction needed so that the Heisenberg Hamiltonians reproduce all the experimental paramagnetic-to-ferromagnetic transition temperatures of the different R2NiMnO6 systems reported in ref. 14 (see Supplementary Fig. 2).
Additional information
How to cite this article: Zhao, H. J. et al. Near room-temperature multiferroic materials with tunable ferromagnetic and electrical properties. Nat. Commun. 5:4021 doi: 10.1038/ncomms5021 (2014).
References
Ramesh, R. & Spaldin, N. A. Multiferroics: progress and prospects in thin films. Nat. Mater. 6, 21–29 (2007).
Zanolli, Z., Wojdeł, J. C., Íñiguez, J. & Ghosez, P. Electric control of the magnetization in BiFeO3/LaFeO3 superlattices. Phys. Rev. B 88, 060102 (2013).
Lee, J. H. et al. A strong ferroelectric ferromagnet created by means of spin-lattice coupling. Nature 466, 954–958 (2010).
Ležaić, M. & Spaldin, N. A. High-temperature multiferroicity and strong magnetocrystalline anisotropy in 3d-5d double perovskites. Phys. Rev. B 83, 024410 (2011).
Rocquefelte, X., Schwarz, K., Blaha, P., Kumar, S. & van den Brink, J. Room-temperature spin-spiral multiferroicity in high-pressure cupric oxide. Nat. Commun. 4, 2511 (2013).
Mukherjee, S. et al. Room temperature nanoscale ferroelectricity in magnetoelectric GaFeO3 epitaxial thin films. Phys. Rev. Lett. 111, 087601 (2013).
Wang, W. et al. Room-temperature multiferroic hexagonal LuFeO3 Films. Phys. Rev. Lett. 110, 237601 (2013).
Eerenstein, W., Mathur, N. D. & Scott, J. F. Multiferroic and magnetoelectric materials. Nature 442, 759–765 (2006).
He, Q. et al. Electrically controllable spontaneous magnetism in nanoscale mixed phase multiferroics. Nat. Commun. 2, 225 (2011).
Evans, D. M. et al. Magnetic switching of ferroelectric domains at room temperature in multiferroic PZTFT. Nat. Commun. 4, 1534 (2013).
Albrecht, D. et al. Ferromagnetism in multiferroic BiFeO3 films: a first-principles-based study. Phys. Rev. B 81, 140401(R) (2010).
Scott, J. F. Room-temperature multiferroic magnetoelectrics. NPG Asia Mater. 5, e72 (2013).
Azuma, M. et al. Designed Ferromagnetic, Ferroelectric Bi2NiMnO6 . J. Am. Chem. Soc. 127, 8889–8892 (2005).
Bull, C. L. & McMillan, P. F. Raman scattering study and electrical properties characterization of elpasolite perovskites Ln2(BB')O6 (Ln=La, Sm...Gd and B, B'=Ni, Co, Mn). J. Solid State Chem. 177, 2323–2328 (2004).
Bellaiche, L. & Íñiguez, J. Universal collaborative couplings between oxygen-octahedral rotations and antiferroelectric distortions in perovskites. Phys. Rev. B 88, 014104 (2013).
Glazer, A. The classification of tilted octahedra in perovskites. Acta Crystallogr. Sect. B 28, 3384–3392 (1972).
Rondinelli, J. M. & Fennie, C. J. Octahedral rotation-induced ferroelectricity in cation ordered perovskites. Adv. Mater. 24, 1961–1968 (2012).
Rogado, N. S., Li, J., Sleight, A. W. & Subramanian, M. A. Magnetocapacitance and magnetoresistance near room temperature in a ferromagnetic semiconductor: La2NiMnO6 . Adv. Mater. 17, 2225–2227 (2005).
Das, H., Waghmare, U. V., Saha-Dasgupta, T. & Sarma, D. D. Electronic structure, phonons, and dielectric anomaly in ferromagnetic insulating double pervoskite La2NiMnO6 . Phys. Rev. Lett. 100, 186402 (2008).
Zhao, H. J., Ren, W., Chen, X. M. & Bellaiche, L. Effect of chemical pressure, misfit strain and hydrostatic pressure on structural and magnetic behaviors of rare-earth orthochromates. J. Phys. Condens. Matter 25, 385604 (2013).
Zhao, H. J., Ren, W., Yang, Y., Chen, X. M. & Bellaiche, L. Effect of chemical and hydrostatic pressures on structural and magnetic properties of rare-earth orthoferrites: a first-principles study. J. Phys. Condens. Matter 25, 466002 (2013).
Shannon, R. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Crystallogr. Sect. A 32, 751–767 (1976).
Mulder, A. T., Benedek, N. A., Rondinelli, J. M. & Fennie, C. J. Turning ABO3 antiferroelectrics into ferroelectrics: design rules for practical rotation-driven ferroelectricity in double perovskites and A3B2O7 Ruddlesden-Popper compounds. Adv. Funct. Mater. 23, 4810–4820 (2013).
Kornev, I. A., Bellaiche, L., Janolin, P. E., Dkhil, B. & Suard, E. Phase diagram of Pb(Zr,Ti)O3 solid solutions from first principles. Phys. Rev. Lett. 97, 157601 (2006).
Yang, Y., Íñiguez, J., Mao, A.-J. & Bellaiche, L. Prediction of a novel magnetoelectric switching mechanism in multiferroics. Phys. Rev. Lett. 112, 057202 (2014).
Booth, R. J. et al. An investigation of structural, magnetic and dielectric properties of R2NiMnO6 (R=rare earth, Y). Mater. Res. Bull. 44, 1559–1564 (2009).
Pertsev, N. A., Zembilgotov, A. G. & Tagantsev, A. K. Effect of mechanical boundary conditions on phase diagrams of epitaxial ferroelectric thin films. Phys. Rev. Lett. 80, 1988–1991 (1998).
Diéguez, O. et al. Ab initio study of the phase diagram of epitaxial BaTiO3 . Phys. Rev. B 69, 212101 (2004).
Lai, B.-K., Kornev, I. A., Bellaiche, L. & Salamo, G. J. Phase diagrams of epitaxial BaTiO3 ultrathin films from first principles. Appl. Phys. Lett. 86, 132904 (2005).
Guo, H. et al. Growth of epitaxial thin films of the ordered double perovskite La2NiMnO6 on different substrates. Appl. Phys. Lett. 89, 022509 (2006).
King, G. et al. Magnetic structures of NaLMnWO6 perovskites (L=Na, Nd and Tb). Phys. Rev. B 79, 224428 (2009).
Padhan, P. et al. Magnetodielectric effect in Bi2NiMnO6-La2NiMnO6 superlattices. J. Phys. Condens. Matter 21, 306004 (2009).
Scott, J. F. Data storage: multiferroic memories. Nat. Mater. 6, 256–257 (2007).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric andmorphology data. J. Appl. Cryst. 44, 1272–1276 (2011).
Perdew, J. P. et al. Restoring the density-gradient expansion for exchange in solids and surfaces. Phys. Rev. Lett. 100, 136406 (2008).
Zhu, M. et al. Electronic and magnetic properties of La2NiMnO6 and La2CoMnO6 with cationic ordering. Appl. Phys. Lett. 100, 062406 (2012).
Stokes, H. T. & Hatch, D. M. FINDSYM: program for identifying the space-group symmetry of a crystal. J. Appl. Crystallogr. 38, 237–238 (2005).
King-Smith, R. D. & Vanderbilt, D. Theory of polarization of crystalline solids. Phys. Rev. B 47, 1651–1654 (1993).
Escorihuela-Sayalero, C., Diéguez, O. & Íñiguez, J. Strain engineering magnetic frustration in perovskite oxide thin films. Phys. Rev. Lett. 109, 247202 (2012).
Acknowledgements
This work is supported by National Science Foundation of China under Grant Nos. 51332006 (X.M.C. and H.J.Z.), 11274270 (X.M.C.) and 11274222 (W.R.), Program for Innovative Research Team in University of Ministry of Education of China (IRT13037), Shanghai Shuguang Program (12SG34) and the Eastern Scholar Program at Shanghai Institutions of Higher Education, Shanghai Municipal Education Commission. We thank the financial support of ARO Grant W911NF-12-1-0085 (W.R. and L.B.) and of the Department of Energy, Office of Basic Energy Sciences, under contract ER-46612 (Y.Y. and L.B.). J.Í. had financial support from MINECO-Spain (Grant Nos. MAT2010-18113 and CSD2007-00041). Some computations were also made possible thanks to the MRI grant 0722625, MRI-R2 grant 0959124, and grant 0918970 from NSF, Shanghai Supercomputer Center, and a Challenge grant from the Department of Defense.
Author information
Authors and Affiliations
Contributions
H.J.Z. performed the first-principles calculations presented in this article with help from W.R. Y.Y. conducted the Monte Carlo simulations with the help of J.I. X.M.C. and L.B. supervised the research work. All authors contributed to the discussion of the results and preparation of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-4, Supplementary Tables 1-2 and Supplementary Discussion (PDF 162 kb)
Rights and permissions
About this article
Cite this article
Zhao, H., Ren, W., Yang, Y. et al. Near room-temperature multiferroic materials with tunable ferromagnetic and electrical properties. Nat Commun 5, 4021 (2014). https://doi.org/10.1038/ncomms5021
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms5021
This article is cited by
-
Ferromagnetism and ferroelectricity in a superlattice of antiferromagnetic perovskite oxides without ferroelectric polarization
npj Computational Materials (2023)
-
The atlas of ferroicity in two-dimensional MGeX3 family: Room-temperature ferromagnetic half metals and unexpected ferroelectricity and ferroelasticity
Nano Research (2021)
-
Site-specific spectroscopic measurement of spin and charge in (LuFeO3)m/(LuFe2O4)1 multiferroic superlattices
Nature Communications (2020)
-
B-site ordering effect on structural and magnetic properties of ‘Y’-modified double perovskite La2NiMnO6 nanoparticles
Journal of Materials Science: Materials in Electronics (2020)
-
Tetragonal tungsten bronze/barium hexaferrite room-temperature multiferroic composite ceramics
SN Applied Sciences (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.