Article | Open | Published:

3D macroporous electrode and high-performance in lithium-ion batteries using SnO2 coated on Cu foam

Scientific Reports volume 6, Article number: 18626 (2016) | Download Citation


A three-dimensional porous architecture makes an attractive electrode structure, as it has an intrinsic structural integrity and an ability to buffer stress in lithium-ion batteries caused by the large volume changes in high-capacity anode materials during cycling. Here we report the first demonstration of a SnO2-coated macroporous Cu foam anode by employing a facile and scalable combination of directional freeze-casting and sol-gel coating processes. The three-dimensional interconnected anode is composed of aligned microscale channels separated by SnO2-coated Cu walls and much finer micrometer pores, adding to surface area and providing space for volume expansion of SnO2 coating layer. With this anode, we achieve a high reversible capacity of 750 mAh g−1 at current rate of 0.5 C after 50 cycles and an excellent rate capability of 590 mAh g−1 at 2 C, which is close to the best performance of Sn-based nanoscale material so far.


Developing technologies for portable electronic devices, electric vehicles, and grid-scale energy storage applications demand for high-performance lithium-ion batteries (LIBs) with high energy and high power densities and good cycling stabilities1,2. Tin dioxide (SnO2), as a promising alternative to currently used graphitic anode for next generation LIBs, has received much attention because of its high theoretical capacity of 781 mAh g−1, which is 2 times higher than that of the conventional graphitic anode (372 mAh g−1)3,4. However, practical application of the SnO2-based anode has been hindered by the inherently severe volume changes (up to 300%) during the large amounts of Li ion insertion and extraction; this can cause a pulverization of active material and a loss of electrical contact, and eventually resulting in poor capacity retention3,4,5. To resolve this issue, several strategies have been proposed, such as nanoscale electrodes6,7,8, electrodes hybridized with carbon or polymers9,10,11,12, and electrodes designed for unique architectures13,14,15,16.

A three-dimensional (3D) porous metallic architecture should have several important benefits including the following: (i) facile access of electrolyte to the electrode surface, (ii) facilitated charge transfer across the interface between electrode and electrolyte, (iii) relieved stress on the pulverization of active material by providing void spaces to absorb the large volume changes, additionally, (iv) high electron pathways in the electrode assembly17,18,19. Various fabrications about the 3D metallic scaffold have been explored such as inverse opal structure18,20, stainless steel mesh21, foams22,23,24, long chains of particles25, and fibers26 or wires27 assembly. Furthermore, a dual pore-size and pore-shape distribution architecture, interdigitated highly porous metallic scaffold, can enhance the volume density of active material by increasing surface area of the 3D scaffold as a template for deposited active material or as an active material itself18,28. A freeze-casting process is an easy, versatile, and promising method to prepare a highly interconnected microscale pore structure29,30. In this low-cost and scalable process, a solution is frozen and the frozen solvent is then removed by freeze-drying, forming a macroporous body structure as a replica of the solidified solvent structure29,30. As it is a physical process without chemical reactions, and as it uses ice crystals obtained from water or other forms of liquid template, freeze-casting generally results in pores at the surface of structure on the order of tens of micrometers in size concurrently with channel-like pores of several tens of micrometers in the structure.

We herein report a new SnO2 anode design concept, for the first time, based on a 3D macroporous Cu foam with a dual pore-size distribution by a directional freeze-casting technique. The Cu foam is utilized as both an anode current collector and a template for a SnO2 coating layer. The 3D macroporous Cu foam provides both continuous metallic struts to act as effective electron pathways and local void spaces to alleviate stress generated from large volume changes of SnO2 coating layer during cycling. This combination of properties in the electrode demonstrates a high reversible capacity, superior rate capability, and stable cycle retention with preserving its structural integrity.


Material and structure design

3D porous scaffold architecture is regarded as a smart electrode prototype for providing efficient Li ion and electron transport17,18,19. Recently, we have shown that commercially available Cu foam exhibits good electrochemical performance when used in anode for LIBs24. In this work, a freeze-casting process is employed to enhance the volumetric density of Cu scaffold. The freeze-casting technique was initially invented for use with porous ceramics and polymers because of their lower densities and the ease of suspension of particles in slurries. Since the first report on the use of biomedical materials obtained from collagen solutions in 199831, the viability of freeze-casting for ceramic-based porous biomaterials has been widely investigated. In contrast, freeze-cast metals were not created until recently due to difficulties with particle settling in, and reactivity with, the solvent. Such foams were fabricated through the freeze-casting using titanium powder32, copper oxide powder which was reduced to copper33, and iron oxide powder34. Among the prepared (Ti, Cu, and Fe2O3) foams, the Cu foam can be regarded as the best scaffold used for a current collector because of the highest electrical conductivity. As a further step, SnO2 as an active material should be combined with the Cu scaffold current collector to react with Li ions. For advanced Sn-based materials, various synthesis methods have been developed such as sputtering, chemical vapor deposition, and electron beam deposition and so on. However, these methods have low throughput and require vacuum conditions, making economical scale-up difficult. One alternative approach is to use a sol-gel method, which has many advantages over the conventional methods using solid-state reactions. For instance, the sol-gel method can provide good stoichiometric control, homogeneous molecular mixing, an uniform particle size distribution35; in addition, it does not require a vacuum system and is thus scalable at low cost. We therefore chose to utilize a sol-gel method36 to apply a SnO2 coating to the Cu scaffold current collector. The fabrication processes of Cu foam via directional freeze-casting and SnO2 coating via sol-gel methods are schematically illustrated in Fig. 1a–d. One can thus fabricate a SnO2-coated Cu foam (hereafter, referred to as SnO2/Cu foam) anode by integrating four simple processes: freeze-casting, drying, reduction/sintering, and sol-gel coating, which can be linked into a single, continuous process that is able to scale up to very high throughput. The above processes result in the formation of a 3D continuous metallic and porous Cu foam covered with SnO2 coating layer inside, which is advantageous for both electron and Li ion transport and also volume changes of SnO2 coating layer during cycling (Fig. 1e).

Figure 1: Electrode fabrication and architecture.
Figure 1

(ad) Schematic diagram of a fabrication process for SnO2-coated Cu foam electrode. (a) During directional freezing of CuO slurry, growth of vertical ice crystal colonies occurred simultaneously with entrapment of CuO particles between the ice crystals structure. A porous body structure was formed as a replica of the ice crystals (right box). (b) After drying of the ice, a porous layer-by-layer structure resulted, consisting of lightly-bound CuO particles. (c) The CuO foam was then sintered and reduced from dark green CuO to orange Cu in a hydrogen atmosphere. (d) A SnO2 sol-gel coating method was employed to fabricate a SnO2-coated Cu foam electrode. (e) Conceptual diagram of the SnO2-coated Cu foam with continuous metallic and porous structure enabling both effective electron and Li ion pathways and also stress alleviation in volume changes of SnO2 coating layer during cycling.

Fabrication of SnO2-coated Cu foam electrode

FE-SEM images (Fig. 2a–g) show morphologies of an as-prepared Cu foam prior to application of the SnO2 coating. The Cu foam indicates various morphological characteristics upon comparing side views (Fig. 2b–d) with top views (Fig. 2e–g). Figure 2a shows a layered lamellar assembly of Cu walls or lamellae. The magnified surface morphologies on a lamella (Fig. 2c,d) as indicated by the white dotted circle in Fig. 2b show a high degree of roughness caused by dendritic-like morphologies of the ice crystals30, and confirm the presence of numerous small pores ca. 10 μm in diameter. The top images of Cu foam in Fig. 2a,b perpendicular to the ice front exhibit a randomly oriented layered structure. Although the lamella thicknesses and the intervals between lamellae vary considerably (Fig. 2e), they are estimated to be below 50 and 100 μm, respectively. Figure 2f,g display the development of dendrites in side view, which are also observed from Fig. 2c,d in front view. Moreover, the cross-sectional optical images of as-prepared Cu foam are shown in vertical and horizontal views (Supplementary Fig. S1a,b, respectively), revealing numerous, continuous, macroporous walls several tens of microns in width. It is also observed that lamellar bridges originating from overgrown dendrites eventually crossed the gaps between two adjacent lamellae30; an example is indicated by blue circles in Supplementary Fig. S1b. This observation suggests that the layer-by-layer macroporous structure can make connections continuously in the horizontal direction, resulting in a well-constructed three-dimensional Cu network structure. To evaluate the pore-size and distribution for as-prepared Cu foam, a mercury intrusion porosimetry (MIP) test was carried out. Because the MIP test could not detect the main channel-like pores of over 100 μm in diameter, those secondary pores on the order of a few tens of microns were detected. The major peak of the pore distribution is 14 μm, as seen in Supplementary Fig. S2, in qualitative agreement with the image in Fig. 2d; these pores is resulted from the secondary dendritic growth of ice crystals. In addition, the surface area of Cu foam via freeze-casting process is higher than that of commercially available Cu foam in previous our work24. The inset images of Supplementary Fig. S2 also show the cross-sectional area of Cu foam and its magnified surface morphology, confirming the existence of dendritic ice crystals.

Figure 2: Freeze-cast Cu foam of macroporous layer-by-layer assembly.
Figure 2

(a) SEM image of a freeze-cast Cu foam showing a vertically aligned Cu multilayer assembly. Scale bar, 400 μm. (b–d) Side view SEM images of the macroporous layer-by-layer Cu foam. (b) An enlarged portion of the Cu foam. Scale bar, 400 μm. (c) A porous Cu layer resulted from dendritic growth of ice crystals. Scale bar, 40 μm. (d) The Cu layer with interconnected microscale pores is also confirmed at higher magnification. Scale bar, 40 μm. (e–g) Top view SEM images of the macroporous layer-by-layer Cu foam. (e) A randomly oriented layered structure. Scale bar, 400 μm. (f) The development of dendrites in side view simultaneously observed from (c,d) in front view. Scale bar, 40 μm. (g) The dendritic-like morphology character is also confirmed at higher magnification. Scale bar, 40 μm.

Figure 3 shows the cross-sectional images of SnO2/Cu foam taken by focused ion beam (FIB) milling and EDX mapping analyses, and confirms the presence of a SnO2 coating after sol-gel process (All elements including Sn are shown in Supplementary Fig. S3). The regions of interest, which are indicated by the white dotted rectangles in Fig. 3, are randomly selected for comparison of the top and interior areas of the SnO2/Cu foam. A SnO2 layer at the top is coated onto the Cu foam and estimated to be ca. 500 nm in thickness. Moreover, the presence of an interior SnO2 coating layer is clearly illustrated, as indicated by the blue arrows, surrounding a pore in the Cu foam arising from the dendrite formation on the lamella surface. The interior SnO2 coating layer is thinner than the top SnO2 coating layer. To confirm the presence of a SnO2 coating in the middle of 300 μm thick SnO2/Cu foam, cross-sectional SEM and EDX mapping images were taken at ca. 150 μm depth position. Supplementary Fig. S4a presents an entire cross-section of the SnO2/Cu foam mounted in polymer resin and polished according to standard metallographic procedures. The magnified surface on lamella in the SnO2/Cu foam interior (Supplementary Fig. S4b) indicates the border between the Cu wall and polymer resin at ca. 150 μm depth position. The lamella in SnO2/Cu foam interior is covered with a bright thin layer, implying the presence of Sn at ca. 150 μm depth position (Supplementary Fig. S4c,d). Supplementary Fig. S5 compares XRD patterns of the as-prepared Cu foam, SnO2/Cu foam and SnO2 powder directly obtained from sol-gel process and commercial SnO2 powder slurry pasted onto copper foil as control (hereafter, referred to as SnO2 SG and SnO2 NPs, respectively). The XRD pattern of as-prepared Cu foam identifies diffraction peaks for metallic copper (JCPDS 04-0836). The diffraction peaks observed in both SnO2/Cu foam and SnO2 NPs are assigned to either tetragonal rutile-structure SnO2 (JCPDS 41-1445) or Cu (JCPDS 04-0836), with no additional peaks corresponding to other phases such as SnO and Cu2O. Moreover, the oxidation stability of 3D Cu foam was examined in detail and discussed in Supplementary Fig. S5c.

Figure 3: SnO2-coated Cu foam electrode.
Figure 3

Cross-sectional SEM images of a SnO2/Cu foam electrode in its entirety and at top and interior regions as indicated by the white dotted rectangles with Sn element mapping. The blue arrows indicate interior SnO2 coating layer surrounding a secondary pore. Scale bars, 2 μm (entirety), 500 nm (top) and 500 nm (interior), respectively.

Electrochemical properties

To understand the electrochemical properties of SnO2/Cu foam electrode, cyclic voltammetry (CV) measurement was performed in the range of 0.01–2.0 V at a scan rate of 0.1 mV s−1 (Supplementary Fig. S6a). The three CV profiles of SnO2/Cu foam obtained from different sol concentration are in accordance with the electrochemical behavior of SnO2-based anode materials37,38. The normalized CV profiles display the reactive surface area of electrode, which can imply the highest porosity development of SnO2 coating layer from the 10 M of Sn(II) solution. The pH and/or viscosity resulted from the different sol concentration can affect the gelation environment and the development of porous gel39. In addition, the effect of sol concentration on LIBs performance was measured at current rate of 1 C (1 C = 781 mA g−1). The Li ion capacity is increased by increasing the Sn(II) solution as presented in Supplementary Fig. S6b, as a result, sol concentration was controlled at 10 M for subsequent experiments.

The voltage profiles of SnO2/Cu foam, SnO2 SG, and SnO2 NPs during the first two cycles at 0.5 C are shown in Supplementary Fig. S7. All electrodes are similar in electrochemical pathway, corresponding to previous reports of the SnO2-based anode37,38. The SnO2/Cu foam delivers a capacity of 1856 mAh g−1 at the first discharge curve and a reversible capacity of 1258 mAh g−1. The discharge curve exhibits a plateau at ~0.9 V resulted from the formation of solid electrolyte interface (SEI) layer and the conversion reaction of SnO2 into Sn and Li2O. The second discharge and charge capacities of SnO2/Cu foam are 1292 mAh g−1 and 1224 mAh g−1, respectively. The enhanced capacity over the theoretical capacity of 781 mAh g−1 based on the conventional alloying reaction () can be resulted from the irreversible capacity from electrolyte decomposition and the reversibility of conversion reaction (). When the conversion reaction is totally reversible, the theoretical capacity of SnO2 increases up to 1494 mAh g−1. The second discharge curve differs from the first in that the voltage plateau disappeared, suggesting that the formation of SEI layer and Li2O occur mainly in the first cycle37,38. The cycling performance of SnO2/Cu foam, SnO2 SG, and SnO2 NPs at 0.5C was evaluated in Fig. 4a. Although the capacities of all electrodes degrade with similar decreasing rate during the first 10 cycles, the SnO2/Cu foam subsequently exhibits the superior capacity retention, in contrast to the severe capacity degradation almost 90% of both SnO2 SG and SnO2 NPs. Moreover, the capacity of SnO2/Cu foam after 50 cycles presents a relatively high capacity of 750 mAh g−1, which is better than all but one40 of Sn-based anode reported recently22,41,42,43,44,45,46,47,48,49,50,51. The coulombic efficiency of SnO2/Cu foam is ~68% at the first cycle, but is ~95% after the second cycle and maintains at ~98% after 50 cycles, showing good capacity retention. Considering the existence of CuO and Cu2O as discussed in Supplementary Fig. S5c and the possibility of their reactivity with lithium, the active material can be extended to sum of SnO2, CuO, and Cu2O. Therefore, the gravimetric performance of SnO2/Cu foam can decrease by maximum of 7.28% as shown in Supplementary Fig. S8. The electrochemical reactions of electrode during discharge and charge processes can be more clearly illustrated by the differential capacity profiles; that is the differential capacity vs. voltage plots. Fig. 4b indicates the differential capacity profiles of SnO2/Cu foam at the selected cycles. The distinct peaks between 0.7 V and 0.01 V after the second cycle correspond to the specific lithiation steps in forming LixSn52,53. The lithiation peaks of SnO2/Cu foam exhibit relatively stable behaviors after the 20th cycle, suggesting that the reversible Li ion insertion into SnO2/Cu foam can continue.

Figure 4: Electrochemical properties.
Figure 4

(a) Cycle performance of SnO2/Cu foam, SnO2 SG, and SnO2 NPs at current rate of 0.5 C during 50 cycles and their coulombic efficiencies. (b) Differential capacity profiles of the SnO2/Cu foam differentiated from the discharge voltage profile after the selected cycles. (c) Rate performance of the SnO2/Cu foam at various C-rates from 0.1 C to 2 C. (d) Voltage profiles of the SnO2/Cu foam at the final discharge/charge processes in each current rate step. (e) Comparison of capacity at different current rates for the SnO2/Cu foam with other Sn-based anode materials reported in recent years. All the specific capacity and current rate are calculated based on the mass of SnO2.

The rate capability of SnO2/Cu foam was evaluated by increasing the current rate from 0.1 C to 2 C stepwise and then decreasing back to 0.1 C, as shown in Fig. 4c. When cycled at 0.1 C, the initial charge capacity of 1330 mAh g−1 decreased gradually down to 1110 mAh g−1 by the 10th cycle. However, the capacity begins to show stable capacity retention and exhibits excellent cycling stability up to the 50th cycle, where the capacity is approximately 590 mAh g−1 at 2 C. After 50 cycles, when the current rate has been returned to 0.1 C, the capacity of SnO2/Cu foam has recovered considerably, showing a good rate capability. Figure 4d exhibits the final discharge and charge voltage profile in each current rate step, for the measurements presented in Fig. 4c. Even at the highest current rate of 2 C, lithiation is still observed as shown by a sloping voltage profile around 0.1 V, corresponding to the formation of LixSn52,53. In addition, the lithiation through forming LixSn even at 2 C is more clearly presented in Supplementary Fig. S9. Figure 4e compares the rate capabilities among a number of different Sn-based anode materials reported in recent years, which confirms that the superior rate capability of SnO2/Cu foam examined in this study is close to the best performance of Sn-based nanoscale material so far40.


There are following advantageous characteristics of such a 3D macroporous electrode design that imparts the SnO2-coated Cu foam with stable cycling performance and good rate capability: (i) intrinsic structural integrity of the 3D open network with interconnected pores and continuous metallic walls within the electrode enables faster transport of both Li ion and electron, (ii) presence of the smaller surface pores in the dual pore-size Cu scaffold creates a larger surface area and increases the contact area between active material and current collector, markedly decreasing the interfacial resistance, (iii) Cu foam with interconnected pores can relieve the stress caused by the large volume changes of coated SnO2 during cycling. In Supplementary Fig. S10a, the coin shape of SnO2/Cu foam electrode after cycling is maintained, but the side and top morphologies at high magnification are coarse and pulverized as shown in Supplementary Fig. S10b,c, respectively. To elucidate the excellent stabilizing effect of SnO2/Cu foam, the cross-section of SnO2 coating was examined using FIB milling and EDX mapping analyses after 50 cycles at 1C (Fig. 5a). All elements including Sn are shown in Supplementary Fig. S10d. The top SnO2 coating layer is significantly expanded to ~2 μm after 50 cycles compared to the initial top coating layer of 500 nm (Fig. 3). However, the interior SnO2 coating maintains a similar thin layer as indicated by the blue arrows, demonstrating that the interior coating layer is preserved without being pulverized by the significant volume changes from repeated Li ion insertion and extraction. In addition, electrochemical impedance spectroscopy (EIS) measurement of the SnO2/Cu foam and SnO2 NPs after completion of the different cycles at 1 C was conducted (Fig. 5b,c). There is no obvious impedance increase in SnO2/Cu foam, implying limited growth of the SEI layer, which is ascribed to the interior thin SnO2 coating layer in the Cu scaffold, whereas the impedance of SnO2 NPs corresponding to the SEI layer increases continuously. The stable SEI of SnO2/Cu foam until 50 cycles is confirmed in Supplementary Fig. S11. The stable SEI formation on our 3D electrode, accompanying the preservation of interior SnO2 coating layer, should be important for the stable cycling performance, as well as the highly reversible rate capacity.

Figure 5: Morphology of SnO2/Cu foam electrode after 50 cycles and cell impedance test.
Figure 5

(a) Cross-sectional SEM images of the SnO2/Cu foam electrode after 50 cycles at 1 C in its entirety and at top and interior regions as indicated by the white dotted rectangles with Sn element mapping. The blue arrows indicate a preserved interior SnO2 coating layer during cycling. Scale bars, 4 μm (entirety), 4 μm (top), and 1 μm (interior), respectively. (b) Cell impedance tests of the SnO2/Cu foam and SnO2 NPs after the selected cycles at 1 C.

To gain additional insight of the stable SnO2 coating layer, the voltage profiles of SnO2/Cu foam and SnO2 NPs were examined (Supplementary Fig. S12a,b). It is observed that the different electrochemical behavior during charge process especially at high voltages approximately over 1.0 V between the electrodes. Some portion of Li2O matrix decomposes upon delithiation above 1.0 V and oxygen resulted from the decomposition reacts with Sn for forming the SnOx44,54. From the comparison of the differential capacity profiles in charge process between the 2nd and 10th cycles of the SnO2/Cu foam and SnO2 NPs (Supplementary Fig. S12c), the area corresponding to the decomposition of Li2O and the oxidation of Sn to SnO2, obtained from the integrated charge in the differential curves at voltages higher than 1.0 V, decreases in both SnO2/Cu foam and SnO2 NPs after 10 cycles. In Supplementary Fig. S12d, the area for the partially reversible oxidation of Sn in SnO2 NPs decreases sharply after 30 cycles with a negligible amount of the decomposed Li2O, whereas that in SnO2/Cu foam is maintained considerably until the 50th cycle, suggesting that the SnO2 coating layer in Cu foam is geometrically stable.

In conclusion, we have developed a SnO2-coated 3D Cu foam by employing a facile and scalable combination of freeze-casting and sol-gel coating processes. The coated Cu scaffold with a 3D macroporous metallic network structure is fabricated and used in a lithium-ion battery anode for the first time. The unique 3D structure with a dual pore-size and pore-shape distribution enables fast transport of Li ion and electron, and accommodates the large volume changes of SnO2 coating layer during cycling. By taking these advantages of the Cu foam, we successfully achieved highly reversible capacity and superior rate capability, being close to the best performance of Sn-based nanoscale material reported to date. In addition, the foam fabrication by freeze-casting is versatile and can be extended to other metals than Cu and the foams can be applied to other high-capacity anode materials that currently experience cycling damage due to the large volume changes with repeated Li ion insertion and extraction.


Synthesis of copper layer-by-layer assembly via freeze-casting

Nano-sized cupric oxide (CuO) powder, with a particle size of 40–80 nm and 99.9% purity, was purchased from Inframat Advanced Materials (Manchester, CT., USA). Cupric oxide powder slurry was prepared through the following steps: 49.4 wt% cupric oxide powder and 2.5 wt% polyvinyl alcohol (PVA, Sigma-Aldrich Co., USA) binder were slowly suspended and dissolved in 30 mL deionized water, respectively, by using stirring and sonication. The slurry was then cooled to a few degrees above the freezing point of water and poured into a Teflon mold (54 mm in interior diameter, 77 mm in length) placed on a copper rod. The freeze-casting apparatus is shown schematically in Supplementary Fig. S13. The insulated steel container was filled with liquid nitrogen (outer) and ethyl alcohol (interior) and the temperature at the top of the copper rod was fixed at −10 °C using a heater. During directional freezing of the cupric oxide slurry, growth of vertical ice crystal colonies occurred, accompanied by entrapment of copper oxide particles between the ice crystals. Once freezing was completed, the sample underwent sublimation in a freeze dryer for 40 h at −88 °C under 0.005 torr vacuum. After sublimation of the ice, a continuous, macroporous, layered-structure resulted, consisting of elongated channels separated by interconnected, parallel walls consisting of lightly-bound copper oxide particles. The green-body foam was then reduced from copper oxide to copper in a hydrogen atmosphere. Reduction and sintering consisted of presintering at 250 °C for 4 h and primary sintering at 800 °C for 14 h; these were conducted in a tube furnace containing a 5% H2/Ar gas at a heating rate of 5 °C min−1. As shown in Supplementary Fig. S14a, the dark green CuO foam turned to a typical Cu orange after reduction in the hydrogen atmosphere and underwent a volume shrinkage of 44%. Prior to applying the SnO2 coating to the freeze-cast Cu foam, the Cu foam body was cut into thin coupons and polished to 300 μm thickness with colloidal alumina following standard metallographic procedures. The freeze-cast Cu foam with 300 μm thickness was employed to an electrode, but the thickness of Cu foam was much thicker than the conventional Cu foil current collector with 20 μm and also the previous 3D scaffold electrode with 160 μm55, 59 μm56, and 10 μm20. The large difference of the electrode height in magnitude has a chance to be more reduced by introducing a physically cutting or a compression process under high pressure55,56. Therefore, the possibility to improve the volumetric energy density by reducing the thickness of Cu foam can exist in this work. Finally, disks 11 mm in diameter were then punched out. The prepared Cu foam was heated at 500 °C for 1 h in a 5% H2/Ar mixture gas to burn off any remaining binder or leftover solution from the polishing process. Supplementary Fig. S14b indicates the development of Cu struts depending on the position of Cu foam body as indicated at top and middle positions. To obtain a dense scaffold, the layer at middle position was selected and prepared for the following cutting and polishing processes.

SnO2 coating through a sol-gel process

A SnO2-based solution was prepared by dissolving 0.338 g of SnCl2·2 H2O in a solvent mixture consisting of 0.03 mL 37% hydrochloric acid and 0.47 mL ethanol to obtain a 3 M Sn(II) solution (0.564 g and 1.128 g of SnCl2·2H2O for 5 M and 10 M, respectively), which was subsequently aged at room temperature for 24 h. Triple deionized water (0.03 mL) was then added to the solution, which was aged for another 24 h. The Cu foam electrode was immersed in the prepared gel for 24 h, followed by solvent evaporation at 80 °C in vacuum. Heat treatment at 500 °C in an Ar atmosphere for 2 h converted the tin oxide precursor gel into crystalline SnO2 (Supplementary Fig. S15). The mass of coated SnO2 before and after sol-gel coating was weighed by a microbalance with an accuracy of 0.01 mg. The average SnO2 loading mass of electrode was 1.71 mg cm−2.

Electrochemical measurements and characterization

The SnO2/Cu foam, without the addition of any binder or conductive agent, was assembled into a coin cell to be used as a working electrode, and was compared with a SnO2 powder electrode as control. For the control SnO2 powder electrode, commercial SnO2 NPs (<100 nm, purchased from Aldrich) or SnO2 powder directly obtained from sol-gel process was mixed with Ketchen Black as a conductive agent, and PVDF as a binder, in N-methyl-2-pyrrolidone (NMP) solvent. The SnO2:Ketchen Black:PVDF weight ratio was 70:15:15. The mixed slurry was uniformly pasted using a doctor blade method onto a Cu foil to serve as a conventional current collector. The electrode was dried under vacuum at 120 °C for 8 h. The average SnO2 loading mass of powder electrode was 1.82 mg cm−2. 2032-type coin cells, consisting of SnO2/Cu foam or SnO2 NPs as the working electrode and with a lithium metal foil as both the counter and the reference electrodes, were assembled in a glove box under a dry Ar atmosphere. The electrolyte used in this study was 1.0 M LiPF6 dissolved in a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) in a volume ratio of 1:1. Galvanostatic tests (WBCS3000 cycler, WonATech, Korea) were carried out on the coin cells at current rate of 1 C (781 mA g−1) in the voltage range of 2.0 V to 0.01 V (vs. Li+/Li) at 25 °C. XRD patterns were obtained with a Bruker D-5005 using Cu-Kα radiation (λ = 1.5406 Å), operating at 40 kV and 40 mA with a scan range of 20–80°. The morphologies of specimens were characterized using field emission scanning electron microscopy (FE-SEM), (Carl Zeiss, SUPRA 55VP). Pore size distribution and porosity of the Cu foam were analyzed using Mercury intrusion porosimetry (MIP), (AutoPore IV 9510, Micromeritics). X-ray photoelectron spectrometer (XPS) was operated on the surface of electrode with Ar ion beam etching during 120 s using VG Scientifics (Al Kα source). The results were calibrated by referencing C1s at 285 eV using Avantage software. Electrochemical impedance spectroscopy (EIS) was conducted at a charged state (2.0 V vs. Li+/Li) after the selected cycles in 10 mV amplitude with the frequency range from 100 kHz to 10 mHz (Zahner, Germany).

Additional Information

How to cite this article: Um, J. H. et al. 3D macroporous electrode and high-performance in lithium-ion batteries using SnO2 coated on Cu foam. Sci. Rep. 6, 18626; doi: 10.1038/srep18626 (2016).


  1. 1.

    & Issues and challenges facing rechargeable lithium batteries. Nature 414, 359−367 (2001).

  2. 2.

    , , , & Challenges in the development of advanced Li-ion batteries: a review. Energy Environ. Sci. 4, 3243−3262 (2011).

  3. 3.

    & SnO2-Based Nanomaterials: Synthesis and Application in Lithium-Ion Batteries. Small 9, 1877–1893 (2013).

  4. 4.

    , , & Li-alloy based anode materials for Li secondary batteries. Chem. Soc. Rev. 39, 3115–3141 (2011).

  5. 5.

    et al. In Situ Observation of the Electrochemical Lithiation of a Single SnO2 Nanowire Electrode. Science 330, 1515–1520 (2010).

  6. 6.

    , , , & Nanostructured materials for advanced energy conversion and storage devices. Nature Mater. 4, 366–377 (2005).

  7. 7.

    & Roles of nanosize in lithium reactive nanomaterials for lithium-ion batteries. Nano Today 6, 28–41 (2011).

  8. 8.

    , , , & Synthesis of SnO2 nano hollow spheres and their size effects in lithium ion battery anode application. J. Power Sources. 225, 108–112 (2013).

  9. 9.

    & Enhancing the performances of Li-ion batteries by carbon-coating: present and future. Chem. Commun. 48, 1201–1217 (2012).

  10. 10.

    et al. Self-healing chemistry enables the stable operation of silicon microparticle anodes for high-energy lithium-ion batteries. Nature Chem. 5, 1042–1048 (2013).

  11. 11.

    , , & Preparation of Carbon-Coated NiCo2O4@SnO2 Hetero-nanostructures and Their Reversible Lithium Storage Properties. Small 11, 432–436 (2015).

  12. 12.

    , , , & Hierarchical Tubular Structures Constructed by Carbon-Coated SnO2 Nanoplates for Highly Reversible Lithium Storage. Adv. Mater. 25, 2589–2593 (2013).

  13. 13.

    et al. Recent Advances in Metal Oxide-based Electrode Architecture Design for Electrochemical Energy Storage. Adv. Mater. 24, 5166–5180 (2012).

  14. 14.

    , , & The dimensionality of Sn anodes in Li-ion batteries. Mater. Today 15, 544–552 (2012).

  15. 15.

    et al. Bowl-like SnO2@Carbon Hollow Particles as an Advanced Anode Material for Lithium-Ion Batteries. Angew. Chem. Int. Ed. 53, 12803–12807 (2014).

  16. 16.

    , , , & Structural and electrochemical properties of three-dimensionally ordered macroporous tin(IV) oxide films. J. Mater. Chem. 14, 1616–1622 (2004).

  17. 17.

    & Spatially Resolved Modeling of Microstructurally Complex Battery Architectures. J. Electrochem. Soc. 154, A856–A864 (2007).

  18. 18.

    , & Three-dimensional bicontinuous ultrafast-charge and -discharge bulk battery electrodes. Nature Nanotechnol. 6, 277–281 (2011).

  19. 19.

    , & Porous Electrode Materials for Lithium-Ion Batteries-How to Prepare Them and What Makes Them Special. Adv. Energy Mater. 2, 1056–1085 (2012).

  20. 20.

    & Three-Dimensional Metal Scaffold Supported Bicontinuous Silicon Battery Anodes. Nano Lett. 12, 2778−2783 (2012).

  21. 21.

    , & Molten salt synthesis of LiNi0.5Mn1.5O4 spinel for 5 V class cathode material of Li-ion secondary battery. Electrochim. Acta 49, 219–227 (2004).

  22. 22.

    , , & Three-Dimensional Porous Core-Shell Sn@Carbon Composite Anodes for High-Performance Lithium-Ion Battery Applications. Adv. Energy Mater. 2, 238–244 (2012).

  23. 23.

    et al. Template-free synthesized Ni nanofoams as nanostructured current collectors for high-performance electrodes in lithium-ion batteries. J. Mater. Chem. A 1, 10002–10007 (2013).

  24. 24.

    et al. 3D interconnected SnO2-coated Cu foam as a high-performance anode for lithium-ion battery applications. RSC Adv. 4, 58059–58063 (2014).

  25. 25.

    et al. Compressed hydrogen gas-induced synthesis of Au–Pt core–shell nanoparticle chains towards high-performance catalysts for Li–O2 batteries. J. Mater. Chem. A 2, 10676–10681 (2014).

  26. 26.

    et al. Fiber-Type Ni(OH)2 Electrode for Nickel-Metal Hydride Battery: Super High-Rate Charge/Discharge and Long Cycle-Life Performances. J. Electrochem. Soc. 159, A1891–A1896 (2012).

  27. 27.

    , , , & One-Pot Synthesis of Ultra-Light Nickel Nanofoams Composed of Nanowires and Their Transformation into Various Functional Nanofoams. Small 8, 3432–3437 (2012).

  28. 28.

    , & Hierarchically porous carbon derived from polymers and biomass: effect of interconnected pores on energy applications. Energy Environ. Sci. 7, 3574–3592 (2014).

  29. 29.

    , , & Freezing as a Path to Build Complex Composites. Science 311, 515–518 (2006).

  30. 30.

    Freeze-Casting of Porous Ceramics: A Review of Current Achievements and Issues. Adv. Energy Mater. 10, 155–169 (2008).

  31. 31.

    , , , & Einfluss des Einfriervorganges auf die Porenstruktur gefriergetrockneter Kollagenschwämme. Ki—Luft und Kältetechnik 34, 247–252 (1998).

  32. 32.

    & Directionally freeze-cast titanium foam with aligned, elongated pores. Acta Mater. 56, 105–113 (2008).

  33. 33.

    & Preparation and Characterization of Directionally Freeze-cast Copper Foams. Metals 2, 265–273 (2012).

  34. 34.

    , & Microstructure of Fe2O3 scaffolds created by freeze-casting and sintering. Mater. Lett. 142, 56–59 (2015).

  35. 35.

    et al. Electrode materials for lithium secondary batteries prepared by sol–gel methods. Prog. Mater. Sci. 50, 881–928 (2005).

  36. 36.

    , & A High-Rate, High-Capacity, Nanostructured Tin Oxide Electrode. Electrochem. Solid-State Lett. 3, 316–318 (2000).

  37. 37.

    & Electrochemical and In Situ X-Ray Diffraction Studies of the Reaction of Uthium with Tin Oxide Composites. J. Electrochem. Soc. 144, 2045–2051 (1997).

  38. 38.

    , & Improved electrochemical performance of SnO2-mesoporous carbon hybrid as a negative electrode for lithium ion battery applications. Phys. Chem. Chem. Phys. 16, 6630–6640 (2014).

  39. 39.

    et al. Sol-gel strategies for controlled porosity inorganic materials. J. Membrane Sci. 94, 85–102 (1994).

  40. 40.

    et al. Graphene Networks Anchored with Sn@Graphene as Lithium-ion Battery Anode. ACS Nano 8, 1728–1738 (2014).

  41. 41.

    et al. Graphene Nanoribbon and Nanostructured SnO2 Composite Anodes for Lithium-ion Batteries. ACS Nano 7, 6001–6006 (2013).

  42. 42.

    et al. Ultrasmall Sn Nanoparticles Embedded in Nitrogen-Doped Porous Carbon As High-Performance Anode for Lithium-Ion Batteries. Nano Lett. 14, 153−157 (2014).

  43. 43.

    et al. Multilayer nanoassembly of Sn-nanopillar arrays sandwiched between graphene layers for high-capacity lithium storage. Energy Environ. Sci. 4, 3611–3616 (2011).

  44. 44.

    et al. Li Storage in 3D Nanoporous Au-Supported Nanocrystalline Tin. Adv. Mater. 23, 2443–2447 (2011).

  45. 45.

    et al. 3D tin anodes prepared by electrodeposition on a virus scaffold. J. Power Sources 211, 129–132 (2012).

  46. 46.

    et al. Reduced Graphene Oxide-Mediated Growth of Uniform Tin-Core/Carbon-Sheath Coaxial Nanocables with Enhanced Lithium Ion Storage Properties. Adv. Mater. 24, 1405–1409 (2012).

  47. 47.

    et al. Three-dimensional Sn-graphene anode for high-performance lithium-ion batteries. Nanoscale 5, 10599–10604 (2013).

  48. 48.

    et al. Hierarchical nanostructured core–shell Sn@C nanoparticles embedded in graphene nanosheets: spectroscopic view and their application in lithium ion batteries. Phys. Chem. Chem. Phys. 15, 3535–3542 (2013).

  49. 49.

    et al. Graphene-Confined Sn Nanosheets with Enhanced Lithium Storage Capability. Adv. Mater. 24, 3538–3543 (2012).

  50. 50.

    & Mesoporous TiO2-Sn/C Core-Shell Nanowire Arrays as High-Performance 3D Anodes for Li-Ion Batteries. Adv. Energy Mater. 4, 1400403−1400401 (2014).

  51. 51.

    , , & Enhanced Lithium Ion Storage Property of Sn Nanoparticles: The Confinement Effect of Few-Walled Carbon Nanotubes. J. Phys. Chem. C 116, 22774−22779 (2012).

  52. 52.

    , , , & Simple Synthesis of Hollow Tin Dioxide Microspheres and Their Application to Lithium-Ion Battery Anodes. Adv. Funct. Mater. 15, 1845–1850 (2005).

  53. 53.

    , , & One-Pot Synthesis of Carbon-Coated SnO2 Nanocolloids with Improved Reversible Lithium Storage Properties. Chem. Mater. 21, 2868–2874 (2009).

  54. 54.

    et al. New Insight into the Reaction Mechanism for Exceptional Capacity of Ordered Mesoporous SnO2 Electrodes via Synchrotron-Based X-ray Analysis. Chem. Mater. 26, 6361–6370 (2014).

  55. 55.

    et al. Ultrathin Graphite Foam: A Three-Dimensional Conductive Network for Battery Electrodes. Nano Lett. 12, 2446–2451 (2012).

  56. 56.

    et al. Graphene-encapsulated Si on ultrathin-graphite foam as anode for high capacity lithium-ion batteries. Adv. Mater. 25, 4673–4677 (2013).

Download references


Y.-E.S. acknowledges the Institute for Basic Science (IBS) in Korea. This work was supported by Project Code (IBS-R006-G1). Y.H.C. acknowledges financial support from the Priority Research Center Program (2009-0093814) and the Basic Science Research Program (2013R1A1A2061636) through the National Research Foundation of Korea (NRF), which is funded by the Ministry of Education. H.C. also acknowledges support from the Basic Science Research Program (2014R1A2A1A11052513), and Priority (2012-0006680) and Pioneer (2011-0001684) Research Centers Programs through NRF. Mr. Matthew Glazer (Northwestern University in USA) is acknowledged for useful conversations.

Author information

Author notes

    • Ji Hyun Um

    Present address: Integrated Energy Center for Fostering Global Creative Researcher, Sungkyunkwan University, Suwon 440-746, Republic of Korea.


  1. School of Chemical and Biological Engineering, Seoul National University, Seoul 151-742, Republic of Korea

    • Ji Hyun Um
    •  & Yung-Eun Sung
  2. Center for Nanoparticle Research, Institute for Basic Science (IBS), Seoul 151-742, Republic of Korea

    • Ji Hyun Um
    •  & Yung-Eun Sung
  3. School of Advanced Materials Engineering, Kookmin University, Seoul 136-702, Republic of Korea

    • Myounggeun Choi
    • , Hyeji Park
    •  & Heeman Choe
  4. Department of Chemical Engineering, Kangwon National University, Samcheok 245-711, Republic of Korea

    • Yong-Hun Cho
  5. Department of Materials Science and Engineering, Northwestern University, Evanston, IL 60208, USA

    • David C. Dunand
  6. Cellmotive Co. Ltd., #518, Eng. Bldg., Kookmin University, Seoul 136-702, Republic of Korea

    • Ji Hyun Um


  1. Search for Ji Hyun Um in:

  2. Search for Myounggeun Choi in:

  3. Search for Hyeji Park in:

  4. Search for Yong-Hun Cho in:

  5. Search for David C. Dunand in:

  6. Search for Heeman Choe in:

  7. Search for Yung-Eun Sung in:


J.H.U., Y.-H.C. and Y.-E.S. conceived the idea. J.H.U. performed the electrode fabrication and electrochemical tests. M.C. fabricated the copper foam. H.P. assisted with SEM characterizations. J.H.U. discussed the results with M.C., D.D. and H.C. and wrote the paper. Y.-H.C. and Y.-E.S. coordinated and supervised the overall project. All authors discussed the results and commented on the manuscript.

Competing interests

The authors declare no competing financial interests.

Corresponding authors

Correspondence to Yong-Hun Cho or Yung-Eun Sung.

Supplementary information

About this article

Publication history






By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.