Abstract
Spin Hall oscillators (SHO) are promising candidates for the generation, detection and amplification of high frequency signals, that are tunable through a wide range of operating frequencies. They offer to be read out electrically, magnetically and optically in combination with a simple bilayer design. Here, we experimentally study the spatial dependence and spectral properties of auto-oscillations in SHO devices based on Pt(7 nm)/Ni80Fe20(5 nm) tapered nanowires. Using Brillouin light scattering microscopy, we observe two individual self-localized spin-wave bullets that oscillate at two distinct frequencies (5.2 GHz and 5.45 GHz) and are localized at different positions separated by about 750 nm within the SHO. This state of a tapered SHO has been predicted by a Ginzburg-Landau auto-oscillator model, but not yet been directly confirmed experimentally. We demonstrate that the observed bullets can be individually synchronized to external microwave signals, leading to a frequency entrainment, linewidth reduction and increase in oscillation amplitude for the bullet that is selected by the microwave frequency. At the same time, the amplitude of other parasitic modes decreases, which promotes the single-mode operation of the SHO. Finally, the synchronization of the spin-wave bullets is studied as a function of the microwave power. We believe that our findings promote the realization of extended spin Hall oscillators accomodating several distinct spin-wave bullets, that jointly cover an extended range of tunability.
Similar content being viewed by others
Introduction
Spin current-driven magnetization dynamics has a great potential for advancing nano-sized magnetic devices towards practical applications1,2,3,4,5,6. As a prominent example, spin Hall oscillators (SHO) could serve as the next generation of oscillators that can be read out electrically, optically and magnetically. They unite a simple device design based on a bilayer of a heavy metal and ferromagnet with exceptionally high tuneability. Not only can this be utilized to generate versatile, yet controllable, electrical microwave signals, but is also promising for the realization of highly flexible spin-wave sources7.
The active element of a SHO is a ferromagnetic layer, whose magnetization is driven by a spin current into a steady-state precession. The spin current is generated from a charge current in the adjacent heavy metal via the spin Hall effect8. Owing to the magnetic nature, the SHO’s frequency is directly tunable via external or internal magnetic fields spanning a broad regime from MHz up to GHz frequencies, with the prospect of reaching hundreds of GHz9,10,11,12.
Due to nonlinearities in the magnetic system, an intrinsic connection of the frequency to the oscillation amplitude occurs13. This allows to tune SHOs directly by the strength of the driving spin current and additionally provides an exceptional wide-ranged synchronization to external signals by frequency entrainment14,15,16.
However, these nonlinearities also decrease the phase stability of SHOs17,18,19. They promote scattering processes among the different eigenmodes and increase sensitivity to ambient noise16,20. As a consequence, SHOs are limited in their phase stability and output power18. To suppress the nonlinear scattering processes, the active region of the ferromagnetic layer is typically restricted to the nanoscale. This reduces the amount of eigenmodes and results in extended single-mode operation on the expense of absolute output power. Therefore, current research aims at synchronizing either several SHO to each other21,22 or increasing the active area of SHOs23.
Recent works show, that the active area of SHOs can be expanded to one-dimensional wires up to the micrometer range24. Moreover, it has been demonstrated that slight tapering of the nanowire extends the single-mode operation and reduces their phase noise25. Nevertheless, for higher spin current densities, these SHO switch from a single-mode operation to a spectrally broader and polychromatic output25. For this regime, the simultaneous excitation of multiple bullet-modes has been suggested based on electrical measurements and modeled by a nonlinear Ginzburg-Landau equation25, but has not yet been directly observed. Such spin-wave bullets are stabilized by spatiotemporal self-focusing into a two-dimensional dynamically confined soliton. Importantly, in the tapered geometry, the driving torques and demagnetizing fields change continuously along the SHO. This is predicted to result in the stabilization of spin-wave bullets at distinct positions with different frequencies. In this paper we confirm the proposed formation of two bullets by Brillouin light scattering (BLS) microscopy26 and measure their localization and frequency. We demonstrate synchronization of the auto-oscillation modes to external signals and investigate the corresponding manipulation of the individual spin-wave bullets. By imprinting an external microwave modulation on the driving current, injection locking of the SHO, amplitude enhancement and linewidth reduction of the individual bullet modes is demonstrated. Moreover, single-mode operation of the SHO is facilitated by suppression of modes different from the selected bullet, while the frequency of the enhanced bullet can be defined by the chosen microwave frequency. In the final step the increase in the amplitude of the spin-wave bullets by an external signal is studied as a function of the microwave power. We find a steep initial increase in auto-oscillation intensity promising for the use of these SHO as microwave detectors or amplifiers.
Results
The first section presents the studied SHO geometry and its magnetic configuration. In the next section, the linear spin-wave eigenmodes as a basis of the auto-oscillations are assessed by BLS microscopy measurements and micromagnetic simulations. Subsequently, the formation of spin-wave bullets is confirmed experimentally, providing a description of their characteristics. Finally, injection locking of the SHO and its effect on the individual spin-wave bullets are discussed. All measurements were performed at ambient temperatures.
Sample description and magnetic configuration
Tapered nanowire spin Hall oscillators (SHO) were fabricated by sputter deposition and electron beam lithography. Following the design of previous studies24,25, the layer-stack consists of Pt(7 nm)/Ni80Fe20(5 nm)/Al2O3 (2 nm). A scanning electron microscopy (SEM) image of the studied nanowire SHO along with the coordinate system is shown in Fig. 1a. It has a total length of 6 µm and is tapered by an angle of 1.45°. Its active region is limited to a length of 1.9 μm by Au(35 nm)/Cr(7 nm) electrodes, that allow to apply dc and rf currents to the SHO. Due to the tapering, the width increases linearly from 171 nm up to 268 nm along the active region. More detailed information on the fabrication of the device is given in the methods section.
To set the magnetic state of the nanowire SHO as studied in previous works25, a saturating magnetic field of 300 mT is applied at an in-plane angle of ϕ = 80° with respect to its long axis. The external field is then gradually decreased in strength to 70 mT. This configuration allows for injection locking of the SHO to a microwave modulation of the bias current as will be discussed later. The resulting magnetization and effective field are shown in Fig. 1b as calculated by micromagnetic simulations (see methods). For an external magnetic field applied at ϕ = 80°, almost perpendicular to the long axis of the nanowire, effective field wells are created at the top and bottom edges of the SHO. These wells and the magnetic orientation are shown in Fig. 1d for the outmost positions at the dc leads. Due to the tapering, the effective field and magnetization changes gradually along the SHO. This spatial dependency of the maximum amplitude of the effective field along the SHO is plotted in Fig. 1c. As expected, the demagnetizing field in the center of the SHO (y = 0) decreases with increasing width of the nanowire, so that the effective field is found to increase almost linearly along the SHO by about 9 mT.
Linear spin-wave dynamics
Before addressing the nonlinear auto-oscillations, we investigate the linear spin-wave eigenmodes of the SHO as a basis for its operating characteristics. Therefore, we perform micromagnetic simulations for small excitation amplitudes. Three spin-wave modes of discrete frequencies and different localization across the SHO (y-direction) are found. Their frequencies and amplitude profiles are plotted in Fig. 2a,b. The two lower frequency modes of 5.24 GHz (E1) and 5.6 GHz (E2) are localized at the bottom and top edge of the SHO, respectively. Such modes are well known from transversally magnetized nanowires27,28 and referred to as “edge” modes. Since the top and bottom edge of the SHO enclose different angles with the external field, the two edge modes are split in frequency by about 360 MHz. The third linear mode (B1) is localized to the widths center (y = 0) of the wire (bulk mode) and decreases slightly in frequency along the SHO from 6.75 GHz at the narrow end to 6.55 GHz at the wide end.
We then utilize BLS microscopy26 to measure thermally excited spin waves at several positions along the SHO experimentally in Fig. 2c. Each vertical line comprises a spin-wave spectrum with the color code displaying the detected intensity. In each spectrum, the signal maximum closely corresponds to the lowest frequency of the spin-wave band29. For analysis of this maximum, each spectrum was fitted by a Lorentzian function to the low-frequency side. An exemplary fit is shown in Fig. 2d for the position at x = 623 nm yielding an onset frequency of 5.63 GHz. The estimated spin-wave band gap along the SHO is plotted in the BLS intensity graph in Fig. 2c (black dots). Moving along the SHO within the active region from its narrow to its wide end, it increases by ~300 MHz from about 5.6 to 5.9 GHz, which we attribute to the increase of the effective field of about 9 mT (see Fig. 1c) combined with an increase in the spin-wave quantization width.
The experimental observation of one single spin-wave band is in contrast to the three distinct spin-wave resonances found in the simulations. We believe this is attributed to the finite spin-wave coherence length in the real device, which does not permit the simulated quantization into distinct modes. As discussed in the following section, the spin-wave coherence length increases when driving the SHO by a dc current Idc, due to the compensation of the dissipative losses. Consequently, we observe discretized spin-wave eigenmodes for this case in the same device.
Bullet formation in the free running SHO
To determine the current range for dc-driven auto-oscillations, constant currents Idc between −0.5 and 2.5 mA were applied to the nanowire SHO. This regime without any rf modulation on the driving current is referred to as the free running regime of the SHO. The dynamic response was then detected via BLS microscopy at four equidistant positions along the SHO. The black dots in Fig. 3a show the auto-oscillation signal, integrated for all four positions, as a function of Idc, while blue triangles represent the inverse of the integrated intensity. When calculating the output power of the SHO (equation 84b in15), we obtain best agreement to the measured data assuming a critical current ζ = IC = 2.28 mA, a nonlinear damping coefficient Q = 0.8 and a noise background η = 1 (black and blue lines). The critical current IC corresponds to an averaged current density in the Pt layer of 95 MA/cm2 and agrees well with typical values for Pt/Ni80Fe20 systems found in literature30,31.
For the highest applied current of Idc = 2.5 mA we record the spatial characteristic of the auto-oscillations as shown in Fig. 3b. Each vertical line represents a BLS spectrum with the intensity color coded on a logarithmic scale. For this driving current we observe multiple auto-oscillation signals at different frequencies and distinct spatial dependence as predicted for the formation of separate spin-wave bullets. As discussed in the following, we identify two points of main auto-oscillation intensity as bullet A and bullet B. In addition, two modes are observed for higher frequencies with decreasing signal intensities referred to as “standing spin-wave”, SSW mode, and B1 mode. To assess the validity of this classification into two spin-wave bullets and additional modes B1 and SSW, we analyze the spectra in more detail. As exemplarily presented in Fig. 3c, three auto-oscillation peaks occur simultaneously. For each x-position we fit these signal peaks by three separate Lorentzian (solid lines) and distinguish between a low-frequency (LF), middle-frequency (MF) and high-frequency (HF) signal. The extracted spatial dependency of the individual peak amplitudes is presented in Fig. 3d. The corresponding center frequencies are shown together with the simulated spin-wave eigenmodes in Fig. 3e.
Discussing first the auto-oscillation amplitude, the LF and MF peaks contribute strongest to the auto-oscillations. Both of these modes show higher intensities at the positions about x = 500 nm and x = 1250 nm. The localization to these two distinct positions indicates the formation of two bullet modes. The calculation of this state according to the nonlinear Ginzburg-Landau model25 is shown as a black line in Fig. 3d for a given moment in time. As a guide to the eye, the modeled bullet positions are schematically indicated by grey boxes in the background of the data. We obtain best agreement between the calculated amplitude distribution and its smaller value for the bullet mode localized in the wider part of the wire at x = 1250 nm with the experimental data for the LF signal. However, for the experimentally recorded amplitude of the LF signal the extrema are less pronounced, which very likely results from the convolution of the measured intensities with the finite spatial resolution of the BLS microscope of about 340 nm. Extracting the frequency of the LF signal at these two positions (Fig. 3e) yields bullet frequencies of 5.2 and 5.45 GHz, respectively. Hence, the spectral separation due to the tapered geometry is determined to be 250 MHz. This is in good agreement with the modeled value of 190 MHz25. Therefore, we identify two spin-wave bullets corresponding to the LF signal.
In addition to these two bullet modes, a standing spin wave, the SSW mode, that is quantized along the length of the SHO (x-direction) is observed corresponding to the MF signal. The assumption of a standing spin wave is substantiated by the constant mode frequency of about 5.6 GHz along the entire SHO and high degree of spatial symmetry of its amplitude. This mode is also in accordance with an expected increase in the coherence length by the spin-transfer torque, promoting quantization effects. Therefore, we conclude that this auto-oscillation originates from a linear spin-wave eigenmode quantized along the active region of the SHO by the abrupt change in effective field and damping at the dc leads. Qualitative comparison of the mode frequency with the simulated spin-wave eigenmodes indicates, that this standing wave is likely localized to the bottom or top edge of the SHO (E1 or E2).
The third HF signal is only about 10% in amplitude compared to the aforementioned signals. The corresponding mode exhibits a higher frequency and similar frequency dependence along the SHO as the bulk mode B1 that is observed in the simulations. Therefore, we attribute this mode to the linear spin-wave mode localized across the SHO nanowires center (y = 0). Due to its low intensity, this mode is expected to be negligible for our discussion of the auto-oscillations in the tapered SHO. In the following, we focus on the manipulation of the dominant spin-wave bullets and SSW mode during synchronization of the SHO by injection locking.
Injection locking of the SHO
We now discuss synchronization of the SHO to an external signal in form of a well defined microwave modulation of the dc current. For nano-contact SHOs, this approach has been shown to lead to frequency entrainment and an increase in coherence within a certain frequency range, which we here refer to as the locking window32,33,34,35. In this work, we investigate this synchronization for the micrometer long tapered nanowire SHO. These experiments demonstrate the SHOs general ability to synchronize to other oscillators or external sources, but are particularly interesting for maintaining its single-mode operation as well as improving its spectral purity, despite the multitude of available eigenmodes. In addition, the bullets amplitude, localization and frequency can be manipulated via the injection of external signals.
For the experiment, we combine a microwave signal with a constant current source via a common bias Tee. This allows the simultaneous application of both an ac current Iac and a dc current Idc to the SHO. To exclude pronounced excitation of spin waves by the microwave current itself, we measure the spin-wave spectra for a microwave power of nominally 0.06 mW for the inactive SHO, Idc = 0 mA. As expected, only a slight increase in the detected intensities well below 10% is observed compared to the thermal spectra. Hence, direct excitation of magnetization dynamics by the ac currents can be neglected for these small microwave powers.
Subsequently, the injection locking of the SHO, driven at Idc = 2.5 mA, to this small amplitude rf signal is analyzed by recording the auto-oscillations at the position of bullet A (x = 500 nm). In the experiments, the microwave frequency is swept over the spectral range of auto-oscillations covering the bullet and SSW mode. In order to determine their frequency, amplitude and linewidth, each spectrum is fitted by two Lorentzian. The obtained data is summarized in Fig. 4 presenting the extracted frequencies (a and b), linewidths (c) and amplitudes (d) for the bullet mode (blue squares) and the SSW mode (black dots).
We observe synchronization of the SHO to the external rf signal within two separate locking windows centered around the free-running auto-oscillation frequencies of 5.2 and 5.57 GHz. This is seen by the frequency entrainment of the modes and the external signal within the locking windows highlighted by light-blue and grey boxes in the background of the data in Fig. 4a,b. These approximately 100 MHz-wide locking windows are estimated by the points of inflection in the measured frequency dependencies as well as simultaneous linewidth reduction presented in Fig. 4c. The free-running linewidth of the bullet mode has been shown to be smaller than 100 MHz by electrical measurements25. However, our recorded values are limited by the spectral resolution of the experimental set up of about 190 MHz (red line in Fig. 4c). Nevertheless, the Full width at half maximum (FWHM) linewidth of the SSW mode is found to be on the order of 300 MHz and reduces significantly within the locking windows. This reduction clearly shows the improved coherence and stabilization of the auto-oscillations by the external signal. Additionally, it may also be attributed to reduced mode hopping and smaller spatial fluctuations of the bullet modes for the injection-locked SHO.
Analyzing the mode amplitudes in the locked regime (Fig. 4d), reveals a pronounced amplification of the locked mode, whereas the other mode is simultaneously suppressed in amplitude. This suppression excludes a sole enhancement of the auto-oscillations by direct excitation via the microwave signal and substantiates a redirection of energy towards the single-mode operation in the synchronized state.
For deeper analysis, we now discuss the spatial and spectral characteristic of the locked auto-oscillations, which we image via spatially-resolved BLS measurements along the SHO for different frequencies of the injected microwave current. Figure 5 summarizes the results for microwave frequencies of 5.255 GHz (a–c), 5.3 GHz (d–f) 5.35 GHz (g–i), 5.4 GHz (j–l), and 5.625 GHz (m–o). All measurements were performed at an increased nominal ac output power of 1 mW and a direct current of Idc = 2.5 mA to enhance the frequency entrainment and amplification. They are normalized to an identical optical reference signal and shown on the same logarithmic color scale to achieve comparable amplitudes. Grey boxes in the background of the data indicate the synchronized areas as derived from the reduction in linewidth and enhanced amplitude. We observe different regimes in which either only bullet A or B (single bullet state “SB A” and “SB B”) or both bullet modes (double bullet state “DBS”) couple to the microwave signal.
We first focus on the synchronization of one single individual bullet, when applying microwave frequencies of 5.255 or 5.4 GHz. These two frequencies are close to the free-running frequencies of bullet A and B, which oscillate at 5.2 and 5.45 GHz, respectively. The amplitude analysis in Fig. 5b,n show the amplification of the individual bullets. As a guide to the eye, the maximum amplitude of the free-running auto-oscillation outside of the locking regime is indicated by green dashed lines. Both bullets remain at their initial position around x = 500 nm (Fig. 5a) and x = 1250 nm (Fig. 5j), but exhibit amplitudes that are by a factor of 8 to 10 larger compared to the free running values and a linewidth reduced to the detection limit (Fig. 5c,l). When the microwave frequency is slightly increased from 5.255 GHz to 5.3 GHz the amplitude of bullet A reduces and the spatial extent of the locked-regime decreases accompanied by a slight shift in the bullet position to about x = 400 nm. Further incrementing the external frequency by another 50 MHz to 5.35 GHz leads to a transition in the locking characteristic. The auto-oscillatory state clearly shows two maxima with equal intensities at distinct positions along the nanowire (Fig. 5g–i). We attribute this observation to a partial locking of both bullets to the external signal with increased hopping between the aforementioned two single-bullet operations. This is substantiated by the increased linewidth and reduced amplitudes compared to the single-bullet states.
Surprisingly, for an external frequency of 5.625 GHz, higher than the one of the bullets, a state of similar amplitude and linewidth dependence is observed (Fig. 5m–o). On first glance, this could be attributed to synchronization of the SSW mode spanning along the SHO at a free-running frequency about 5.6 GHz, very close to the external one. However, the linewidth of a standing spin-wave resonance is expected to stay constant spatially. In contrast to this, we observe an increase in linewidth at about x = 700 nm between the amplitude maxima. This observations seems to indicate partial locking of the individual bullets. We do not discuss the nature of this state in this work in greater detail, but focus on the amplification of bullet A with increasing microwave power.
The measurement position is fixed again on the bullet A, x = 500 nm, and different external signal strengths, that cover a power range between 0.008 mW and 1 mW at a frequency of 5.2 GHz, are applied to the SHO for Idc = 2.5 mA. Figure 6 presents the recorded intensities of bullet A (red dots) as a function of the microwave power. A linear fit of the amplified signal (red line) results in a power exponent of 0.67 close to 2/3. To discuss the enhancement of the auto-oscillations by injection locking, the green line shows the measured intensity when only applying the dc current in the free running regime. As expected, this base intensity is identical to the signal strength for very low microwave powers within the noise of the measurements. The difference of the intensity during injection locking (red dots) and the base intensity (green line) is plotted as red crosses in the same graph. According to analytical calculations36, this difference is expected to follow a square root dependence on the microwave power. Interestingly, the data show a much steeper increase, in particular for microwave powers below 0.04 mW.
We believe this can be attributed to thermal effects on the phase stability of the auto-oscillations. In the abscence of an external signal, the ambient noise decreases the coherence of the auto-oscillations resulting in increased linewidth and reduced output power. When increasing the microwave signals above the thermal noise floor, the phase is defined by the external signal leading to injection locking. This results in a steep increase in the auto-oscillation signal with increasing microwave power due to the higher degree of coherence. For microwave powers above 0.04 mW, a less pronounced linear increase in amplification with applied power of the microwave signal is observed as indicated by the linear fit of slope 0.95 ± 0.08 (dashed black line) as guide to the eye. This indicates the transition to simple additional direct excitation of spin-wave dynamics with further increasing the microwave power, which is connected to an increase in the precession cone angle, after phase coherence is established. To estimate the influence of the direct excitation of dynamics by the microwave current, we additionally perform measurements when the SHO is turned off (Idc = 0 mA) and detect the intensities for the frequency of bullet A (blue triangles), as well as the frequency of maximum excitation efficiency of 5.6 GHz (black dots). As can be clearly seen, the strength of the directly excited dynamics is well below the amplification values and follows a linear power dependence confirmed by the slopes of 0.98 ± 0.06 and 0.97 ± 0.08. Hence, we conclude that two regimes of amplification of the auto-oscillations are observed. Up to microwave powers of about 0.04 mW the coherence is improved by overcoming the fluctuations stemming from the thermal noise floor via injection locking of the SHO to the external microwave signal. For higher microwave powers further amplification of the auto-oscillation signal is observed with a less pronounced increase. This is promising for utilizing such SHO as sensitive microwave detectors.
Discussion and Conclusion
In this work, the auto-oscillations in SHOs of tapered nanowire geometry are studied experimentally. Spatially resolved BLS microscopy is used to decompose the oscillations into their spectral contributions and reveal their individual localization. Our experimental study confirms that higher driving currents excite two separate auto-oscillatory modes, which oscillate at different frequencies and are localized at separate positions spaced by about 750 nm. These modes are identified as nonlinear self-localized spin-wave bullets, stabilized by the tapered geometry, in agreement with previous electrical characterization and a nonlinear Ginzburg-Landau model25. We control the state of auto-oscillation utilizing externally injected microwave signals with various frequencies and signal powers.
In particular, it is demonstrated that the auto-oscillations can be tuned by the rf signal so that either one or both bullets are synchronized to the external source and enhanced in amplitude. Simultaneously, all other modes are suppressed promoting single mode operation. This allows the manipulation of the tapered SHO simply by small changes in the injected microwave frequency or power. Within the entire investigated regime of externally imprinted microwave powers up to 1 mW, signal amplification is observed with an initial steep increase in output power attributed to overcoming the thermal noise and increase in coherence of the oscillations. This grants an additional possibility of configuring the SHO output with the prospect of utilization in microwave amplifiers or detectors. As an important advantage over straight nanowire geometries, the tapered nanowire design offers reduced phase noise, extended single-mode operation and is promising for the realization of several spin-wave bullets with distinct frequencies and position when increasing the oscillator length. Their coherence, mutual interaction and individual reaction to external signals can be targeted in future time-resolved studies in these SHO. In particular, combining various bullets with distinct frequencies and localization in one device is promising for the realization of wide locking windows and a high degree of tunabilty.
Methods
BLS microscopy
The spin-wave intensity was measured locally by means of Brillouin light scattering microscopy (BLS microscopy) at room temperature26. Light from a continuous-wave, single-frequency 532 nm solid-state laser is focused to a laser spot and scanned over the sample-surface. The back-scattered light is then analyzed using a six-pass Fabry-Perot interferometer TFP-2 (JRS Scientific Instruments), where the BLS intensity is proportional to the square of the amplitude of the magnetization dynamics at the laser spot position. For the conditions of the presented measurements the spectral and spatial resolution was experimentally determined to be 190 ± 30 MHz and 340 ± 50 nm, respectively (Full Width Half Maximum values).
Sample fabrication
Thin films are grown by magnetron sputter deposition. A 5 nm thick Pt film is deposited on an Al2O3 (0001) substrate at 585 °C and subsequently annealed in-situ for 1 hour at the same temperature. The tapered nanowire SHO is defined on the 5 nm Pt film by means of e-beam lithography, sputter deposition, and lift-off. For the sputter deposition, the sample is briefly treated to an Ar plasma cleaning etch and then the remaining stack structure Pt(2 nm)/Ni80Fe20(5 nm)/Al(2 nm) is immediately deposited in-situ at room temperature. The Al(2 nm) capping layer is naturally oxidized and serves to protect the Ni80Fe20 layer from oxidation. The Cr(7 nm)/Au(35 nm) leads are defined by means of e-beam lithography, e-beam evaporation, and subsequent lift-off. Finally, Ar plasma etching is used to remove the remaining exposed 5 nm Pt layer (everywhere but under the tapered nanowire and leads).
Micromagnetic simulations
Micromagnetic simulations are performed using the software package MuMax337. A 2.9 µm long tapered magnetic wire of 220 nm average width, 5 nm thickness and a tapering angle of 1.45° is modeled. The geometry is then represented on a 1024 × 256 × 1 grid, resulting in approximate cell sizes of 2.9 × 1.2 × 5 nm 3, below the exchange length of Py. The saturation magnetization MS = 530 kA/m and exchange stiffness A = 5 pJ/m are set according to the experimentally determined values for this type of nanowire24. To excite and study the spin-wave dynamics, a homogeneous out-of-plane pulse with a time dependency of sinc(40 GHz·2π·t) and a damping parameter αG = 0.007 are used. The magnetic dynamics is saved every 20 ps over a duration of 25 ns in the simulation. Subsequently, the time trajectory of the magnetization of each cell is Fourier transformed to yield its power spectrum. The mode profiles are then calculated by windowed Fourier backtransformation for the mode frequency.
References
Locatelli, N., Cros, V. & Grollier, J. Spin-torque building blocks. Nat. Publ. Group 13, 11–20 (2014).
Miwa, S. et al. Highly sensitive nanoscale spin-torque diode. Nat. Mater. 13, 50–56 (2014).
Choi, H. S. et al. Spin nano–oscillator–based wireless communication. Sci. Reports 4, 1488 (2014).
Urazhdin, S. et al. Nanomagnonic devices based on the spin-transfer torque. Nat. Nanotechnol. 9, 509–513 (2014).
Slavin, A. Microwave sources: Spin-torque oscillators get in phase. Nat. Nanotechnol. 4, 479–480 (2009).
Liu, R. H., Lim, W. L. & Urazhdin, S. Dynamical Skyrmion State in a Spin Current Nano-Oscillator with Perpendicular Magnetic Anisotropy. Phys. Rev. Lett. 114, 1259 (2015).
Urazhdin, S. et al. Excitation of coherent propagating spin waves by pure spin currents. Nat. Commun. 7, 1–6 (2016).
Hoffmann, A. Spin Hall Effects in Metals. IEEE Transactions on Magn. 49, 5172–5193 (2013).
Bonetti, S., Muduli, P., Mancoff, F. & Åkerman, J. Spin torque oscillator frequency versus magnetic field angle: The prospect of operation beyond 65 GHz. Appl. Phys. Lett. 94, 102507 (2009).
Maehara, H. et al. High Q factor over 3000 due to out-of-plane precession in nano-contact spin-torque oscillator based on magnetic tunnel junctions. Appl. Phys. Express 7, 023003 (2014).
Naganuma, H. et al. Electrical Detection of Millimeter-Waves by Magnetic Tunnel Junctions Using Perpendicular Magnetized L1 0-FePd Free Layer. Nano Lett. 15, 623–628 (2014).
Rippard, W., Pufall, M., Kaka, S., Russek, S. & Silva, T. Direct-Current Induced Dynamics in Co90Fe10/Ni80Fe20Point Contacts. Phys. Rev. Lett. 92, 3775 (2004).
Consolo, G. et al. Combined Frequency-Amplitude Nonlinear Modulation: Theory and Applications. IEEE Transactions on Magn. 46, 3629–3634 (2010).
Wang, C., Xiao, D., Zhou, Y., Åkerman, J. & Liu, Y. Phase-locking of multiple magnetic droplets by a microwave magnetic field. AIP Adv. 7, 056019 (2017).
Slavin, A. & Tiberkevich, V. Nonlinear Auto-Oscillator Theory of Microwave Generation by Spin-Polarized Current. IEEE Transactions on Magn. 45, 1875–1918 (2009).
Tiberkevich, V. S., Khymyn, R. S., Tang, H. X. & Slavin, A. N. Sensitivity to external signals and synchronization properties of a non-isochronous auto-oscillator with delayed feedback. Sci. Reports 4 (2014).
Sankey, J. C. et al. Mechanisms limiting the coherence time of spontaneous magnetic oscillations driven by dc spin-polarized currents. Phys. Rev. B 72 (2005).
Chen, T. et al. Spin-Torque and Spin-Hall Nano-Oscillators. Proc. IEEE 104, 1919–1945 (2016).
Keller, M. W., Kos, A. B., Silva, T. J., Rippard, W. H. & Pufall, M. R. Time domain measurement of phase noise in a spin torque oscillator. Appl. Phys. Lett. 94, 193105 (2009).
Sharma, R. et al. Mode-hopping mechanism generating colored noise in a magnetic tunnel junction based spin torque oscillator. Appl. Phys. Lett. 105, 132404 (2014).
Kaka, S. et al. Mutual phase-locking of microwave spin torque nano-oscillators. Nat. 437, 389–392 (2005).
Awad, A. A. et al. Long-range mutual synchronization of spin Hall nano-oscillators. Nat. Phys. 13, 292–299 (2016).
Luo, L. et al. Spin-torque oscillation in large size nano-magnet with perpendicular magnetic fields. J. Magn. Magn. Mater. 432, 356–361 (2017).
Duan, Z. et al. Nanowire spin torque oscillator driven by spin orbit torques. Nat. Commun. 5, 5616 (2014).
Yang, L. et al. Reduction of phase noise in nanowire spin orbit torque oscillators. Sci. Reports 5, 16942 (2015).
Sebastian, T., Schultheiss, K., Obry, B., Hillebrands, B. & Schultheiß, H. Micro-focused Brillouin light scattering: imaging spin waves at the nanoscale. Front. Phys. 3, 1589 (2015).
Topp, J., Podbielski, J., Heitmann, D. & Grundler, D. Internal spin-wave confinement in magnetic nanowires due to zig-zag shaped magnetization. Phys. Rev. B 78, 024431 (2008).
Duan, Z. et al. Spin-wave modes in permalloy/platinum wires and tuning of the mode damping by spin Hall current. Phys. Rev. B 90, 024427 (2014).
Cottam, M. G. & Lockwood, D. J. One-magnon and two-magnon Raman scattering in MnF2. J. Magn. Magn. Mater. 54–57, 1143–1144 (1986).
Demidov, V. E. et al. Control of Magnetic Fluctuations by Spin Current. Phys. Rev. Lett. 107, 107204 (2011).
Demidov, V. E., Urazhdin, S., Zholud, A., Sadovnikov, A. V. & Demokritov, S. O. Nanoconstriction-based spin-Hall nano-oscillator. Appl. Phys. Lett. 105, 172410 (2014).
Rippard, W., Pufall, M. & Kos, A. Time required to injection-lock spin torque nanoscale oscillators. Appl. Phys. Lett. 103, 182403 (2013).
Lebrun, R. et al. Understanding of Phase Noise Squeezing Under Fractional Synchronization of a Nonlinear Spin Transfer Vortex Oscillator. Phys. Rev. Lett. 115, 017201 (2015).
Ulrichs, H. et al. Synchronization of spin Hall nano-oscillators to external microwave signals. Nat. Commun. 5, 1–6 (2014).
Tsunegi, S. et al. Self-Injection Locking of a Vortex Spin Torque Oscillator by Delayed Feedback. Sci. Reports 6, 11 (2016).
Slavin, A. N. & Tiberkevich, V. S. Nonlinear self-phase-locking effect in an array of current-driven magnetic nanocontacts. Phys. Rev. B 72, 092407–4 (2005).
Vansteenkiste, A. & Van de Wiele, B. MuMax: A new high-performance micromagnetic simulation tool. J. Magn. Magn. Mater. 323, 2585–2591 (2011).
Acknowledgements
The authors acknowledge financial support from the Deutsche Forschungsgemeinschaft within programme SCHU 2922/1-1. The work at UCI was supported by the National Science Foundation through Awards No. DMR-1610146, No. EFMA-1641989 and No. ECCS-1708885. We also acknowledge support by the Army Research Office through Award No. W911NF-16-1-0472 and Defense Threat Reduction Agency through Award No. HDTRA1-16-1-0025. K.S. acknowledges funding within the Helmholtz Postdoc Programme. K.W. thanks A. Kákay for discussion on the experimental results and providing computational infrastructure together with T. Schneider.
Author information
Authors and Affiliations
Contributions
A.S. and L.Y. fabricated the samples. K.W. and T.H. conducted the experiment(s) and analyzed the experimental data. All authors interpreted and discussed the results. K.W., K.S. and H.S. co-wrote the manuscript. All authors discussed and reviewed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wagner, K., Smith, A., Hache, T. et al. Injection locking of multiple auto-oscillation modes in a tapered nanowire spin Hall oscillator. Sci Rep 8, 16040 (2018). https://doi.org/10.1038/s41598-018-34271-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-34271-4
Keywords
This article is cited by
-
Probing spin dynamics of ultra-thin van der Waals magnets via photon-magnon coupling
Nature Communications (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.