Advancements in nanoscale engineering of oxide interfaces and heterostructures have led to discoveries of emergent phenomena and new artificial materials. Combining the strengths of reactive molecular-beam epitaxy and pulsed-laser deposition, we show here, with examples of Sr1+x Ti1-x O3+δ, Ruddlesden–Popper phase La n+1Ni n O3n+1 (n = 4), and LaAl1+y O3(1+0.5y)/SrTiO3 interfaces, that atomic layer-by-layer laser molecular-beam epitaxy significantly advances the state of the art in constructing oxide materials with atomic layer precision and control over stoichiometry. With atomic layer-by-layer laser molecular-beam epitaxy we have produced conducting LaAlO3/SrTiO3 interfaces at high oxygen pressures that show no evidence of oxygen vacancies, a capability not accessible by existing techniques. The carrier density of the interfacial two-dimensional electron gas thus obtained agrees quantitatively with the electronic reconstruction mechanism.
Technological advances in atomic-layer control during oxide film growth have enabled the discoveries of new phenomena and new functional materials, such as the two-dimensional (2D) electron gas at the LaAlO3/SrTiO3 interface,1, 2 and asymmetric three-component ferroelectric superlattices.3, 4 Reactive molecular-beam epitaxy (MBE) and pulsed-laser deposition (PLD) are the two most successful growth techniques for epitaxial heterostructures of complex oxides. PLD possesses experimental simplicity, low cost, and versatility in the materials to be deposited.5 Reactive MBE employing alternately-shuttered elemental sources (atomic layer-by-layer MBE, or ALL-MBE) can control the cation stoichiometry precisely, thus producing oxide thin films of exceptional quality.6,7,8 There are, however, limitations in both techniques. Reactive MBE can use only source elements whose vapor pressure is sufficiently high, excluding a large fraction of 4d and 5d metals. In addition, ozone is needed to create a highly oxidizing environment while maintaining low-pressure MBE conditions, which increases the system complexity. On the other hand, conventional PLD using a compound target often results in cation off-stoichiometry in the films.9, 10 In this paper we present an approach that combines the strengths of reactive MBE and PLD: atomic layer-by-layer laser MBE (ALL-Laser MBE) using separate oxide targets. Ablating alternately the targets of constituent oxides, for example SrO and TiO2, a SrTiO3 film can be grown one atomic layer at a time. Stoichiometry for both the cations and oxygen in the oxide films can be controlled. Although the idea of depositing atomic layers by PLD has been explored since the early days of laser MBE,11, 12 we show that levels of stoichiometry control and crystalline perfection rivaling those of reactive MBE can be achieved by ALL-Laser MBE. The technique is effective for both non-polar (such as SrTiO3) and polar materials, such as the Ruddlesden–Popper (RP) phase La n+1Ni n O3n+1 with n = 4. By growing LaAlO3 films on SrTiO3 substrates at an oxygen pressure of 37 mTorr, sufficiently high to alleviate oxygen deficiency in SrTiO3, we show that the properties of the 2D electron gas at the LaAlO3/SrTiO3 interface are in quantitative agreement with the electronic reconstruction mechanism.
The principle of ALL-Laser MBE is schematically illustrated in Fig. 1a. The key difference between ALL-Laser MBE and conventional PLD or laser MBE is the use of separate oxide targets—instead of using a compound target of SrTiO3, targets of SrO and TiO2 are switched back and forth as they are alternately ablated by a UV laser beam. In conventional PLD or laser MBE using a compound target, all elements are ablated at once and the film grows unit cell by unit cell. In ALL-Laser MBE using separate targets, on the other hand, the film is constructed one atomic layer at a time. The number of laser pulses on each target for one atomic layer is around 100, allowing a stoichiometry control of about 1%.
It has been a common practice to control the layer-by-layer growth of thin film by recording and analyzing in real time its reflection high-energy electron diffraction (RHEED) pattern.13, 14 The intensity of the specularly-reflected RHEED spot is commonly used, which oscillates depending on the step edge density of the film. One oscillation period corresponds to the deposition of one unit cell layer in the unit cell-by-unit cell growth.15 Haeni et al. have found that the intensity of the diffracted spot can be used to control the growth of each atomic layer of SrTiO3 films in reactive MBE with alternately shuttered growth.7 In this work, we also use the diffracted spot intensity oscillation and our results confirm that the phenomenology identified by Haeni et al. also applies to ALL-Laser MBE. Figure 1b shows the RHEED intensity oscillations as the targets of SrO and TiO2 are alternately ablated. Starting from a TiO2—terminated SrTiO3 substrate surface, the diffracted spot intensity increases to a maximum when one monolayer of SrO is deposited; it then decreases to a minimum when one monolayer of TiO2 is subsequently deposited. Furthermore, we have found that the specular spot also oscillates with the same period as the diffraction spot, albeit 180° out of phase, if the Kikuchi lines caused by the diffused scattering of electrons do not overlap the specular spot (see Supplementary Materials).
The RHEED intensity depends on both the surface step edge density and the surface chemistry. When all elements of the film are delivered at the same time in the unit cell-by-unit cell growth, the chemistry information is averaged out and only the step edge density of the film is reflected in the RHEED intensity. For ALL-MBE or ALL-Laser MBE, the surface chemistry changes when different atomic layers are deposited sequentially; consequently both the step edge density and chemistry information can be observed. A detail discussion can be found in the Supplementary Materials.
In our experiment, the RHEED diffracted intensity oscillations along the SrTiO3  azimuth were used to calibrate and control the film growth. As shown in Fig. 1b, Sr/Ti > 1 leads to an increasing peak intensity and the appearance of a “double” peak, while Sr/Ti < 1 leads to a reduced peak intensity; Sr/Ti = 1 results in oscillation peaks with a constant intensity and shape. Furthermore, insufficient or excess pulses in each cycle cause beating of the RHEED intensity (Fig. 1c) while the intensity remains constant for 100% layer coverage (Fig. 1d). Using the RHEED intensity oscillation combined with the calibration of laser pulses per atomic layer obtained from the film thickness measurement, the cation stoichiometry in the films can be controlled to within ±1%.
The results of a series of 60 nm thick Sr1+x Ti1−x O3+δ films grown on TiO2-terminated (001) SrTiO3 substrates by ALL-Laser MBE are presented in Fig. 2. The x values for the five films, determined by the Rutherford backscattering spectrometry (RBS) measurement, shown in Fig. 2a, are 0.13, 0.05, −0.01, −0.07, and −0.12, respectively, with a measurement error of ±5%. They are consistent with the intended compositions (x = 0.10, 0.05, 0.00, −0.05, −0.10) controlled by the respective numbers of laser pulses. Figure 2b shows X-ray diffraction (XRD) θ–2θ scans for the films around the SrTiO3 002 diffraction peak along with that of the SrTiO3 substrate. When the film is stoichiometric, the XRD spectrum cannot be distinguished from that of the single crystal SrTiO3 substrate. When the film is not stoichiometric, regardless of Sr rich or deficient, a diffraction peak from the film at a smaller angle than the substrate peak is seen, indicating a c-axis lattice expansion well established for homoepitaxial off-stoichiometric SrTiO3.8, 9 The c lattice constant vs. x is plotted for the films in Fig. 2c. Also plotted are data from films grown by reactive MBE for comparison. The results from the two techniques are in agreement with each other. In Fig. 2d, ultraviolet Raman spectra are presented for the five films as well as a stoichiometric film grown by reactive MBE16 and a single crystal SrTiO3 substrate. For bulk SrTiO3, the Raman spectrum shows only the second-order features,17 while the spectra of all the nonstoichiometric samples contain strong first-order Raman peaks, indicating the breakdown of the central inversion symmetry. The stoichiometric film shows spectra similar to those of the stoichiometric film grown by reactive MBE (broad and weak second-order Raman peaks). The results demonstrate that ALL-Laser MBE possesses the same excellent stoichiometry control as ALL-MBE.
The ALL-Laser MBE technique can not only grow thin films of stable phases like SrTiO3, but also fabricate layered materials that may not exist in nature. As an example, we have grown thin films of the RP phase La n+1Ni n O3n+1 with n = 4 on a LaAlO3 substrate. Figure 3a shows a schematic of the La5Ni4O13 structure, in which 4 layers of NiO6 octahedra are sandwiched between the NaCl-type LaO double layers. No successful deposition of phase-pure La n+1Ni n O3n+1 thin films with n > 3 has been reported in the literature, likely due to thermodynamic instability. To grow the film by ALL-Laser MBE, La2O3 and NiO targets were ablated alternately to deposit the LaO and NiO2 atomic layers four times before an additional LaO layer was added. This is shown in Fig. 3b by the RHEED intensity oscillations, in which the fourth LaO deposition in each period contains twice as many laser pulses as the other LaO layers. The XRD θ–2θ scan of the resultant 50 unit-cell La5Ni4O13 film is presented in Fig. 3c, showing the diffraction peaks of the n = 4 RP phase from 0010–0028 without any impurity peaks or peak splitting. Figure 3d is a cross-sectional scanning transmission electron microscope (STEM) high angle annular dark field (HAADF) image of the La5Ni4O13 film, showing an extra layer of LaO every 4 unit cells of LaNiO3. In Fig. 3e, atomic resolution elemental mapping using electron energy-loss spectroscopy (EELS) indicates a perfect match between the elemental distribution and the simultaneously taken HAADF image, verifying that the extra layer is indeed LaO. Evidently, ablating from the targets of La2O3 and NiO is able to form the polar LaO and NiO2 layers to produce the RP structure. As shown by Sreedhar et al., the Ni next to the LaO rock salt layer changes its valence to maintain the charge neutrality in the RP phase.18
The ability to grow polar materials allows us to study the 2D electron gas at the LaAlO3/SrTiO3 interface using ALL-Laser MBE. Since its discovery2 several competing mechanisms have been proposed and intensely debated to explain the origin of the interfacial 2D electron gas, including electronic reconstruction,19 oxygen vacancies in the SrTiO3 substrate,20,21,22 and intermixing between the LaAlO3 film and the SrTiO3 substrate.23, 24 According to the electronic reconstruction mechanism, because the atomic layers are charge neutral in SrTiO3 but charged in LaAlO3, a diverging electric potential is built up in a LaAlO3 film grown on a TiO2-terminated SrTiO3 substrate. This leads to the transfer of half of an electron from the LaAlO3 film surface to SrTiO3 when the LaAlO3 layer is thicker than 4 unit cells, creating a 2D electron gas at the interface with a sheet carrier density of 3.3 × 1014/cm2 for sufficiently thick LaAlO3. A serious inconsistency with this mechanism is that the carrier densities reported experimentally are invariably lower than the expected value25, 26 except under conditions where reduction of SrTiO3 substrate is suspected.20, 21 Oxygen vacancies in SrTiO3 are known to contribute to conductivity, but all reported conducting LaAlO3/SrTiO3 interfaces have been grown at low oxygen pressures (<10 mTorr), and annealing in oxygen is often required;1, 19, 27, 28 higher oxygen pressures during the PLD growth result in insulating samples27 or 3D island growth.29 Low growth pressures can not only cause oxygen vacancies in SrTiO3, but can also enhance bombardment effect due to energetic species that may lead to La–Sr intermixing at the interface.27 At present, there is no consensus on the origin of the 2D electron gas at the LaAlO3/SrTiO3 interface.
Because we grow the LaAlO3 film one atomic layer at a time, we were able to grow conducting LaAlO3/SrTiO3 interfaces at an oxygen pressure as high as 37 mTorr with ALL-Laser MBE. This high oxygen pressure helps to prevent the possible oxygen reduction in SrTiO3, ensure that the LaAlO3 films are sufficiently oxygenated, and suppress the La–Sr intermixing due to the bombardment effect. Furthermore, we grew LaAlO3 films of different cation stoichiometry, LaAll+y O3(1+0.5y), as a way to test the electronic reconstruction hypothesis. As depicted by Sato et al.,28 either Al vacancies or La vacancies in the off-stoichiometric films lead to oxygen vacancies in order to keep the charge neutrality. As a result, the charges on each layer depend on the stoichiometry: the charge on the [LaO1+y ] layer is +(1−2y) and the charge on the [Al1+y O2+0.5y ] layer is −(1−2y). A similar modification of charges in each layer has been suggested for LaAlO3 films diluted with SrTiO3.30 In the electronic reconstruction picture, instead of the charge transfer of half of an electron in the case of stoichiometric LaAlO3, (0.5−y) electrons will be transferred to resolve the polar discontinuity at the interface. The sheet carrier density depends linearly on y, i.e. n s = (1−2y) × 3.3 × 1014/cm2 for sufficiently thick LaAlO3.28 For the 10 unit-cell LaAlO3 films used in this work, the dependence becomes n s = (1−2y) × 3.3 × 1014/cm2−1.6 × 1014/cm2 = (1.7−2y × 3.3) × 1014/cm2.31
Starting from a TiO2-terminated SrTiO3 substrate, we grew 10 unit-cell-thick LaAlO3 films by alternately ablating La2O3 and Al2O3 targets under an oxygen pressure of 37 mTorr. The RHEED intensity oscillations during the growth of a stoichiometric film are shown in Fig. 4a. The RHEED intensity of the first LaO layer shows an irregular pattern, reflecting the state of surface chemistry, charge, and morphology during the transition from TiO2 to LaO. The pattern becomes more regular in the subsequent layers. The reduction in the RHEED intensity from the substrate level is small throughout the growth of the 10 unit-cell stoichiometric LaAlO3 film. The 2D growth mode was maintained as confirmed by the sharp RHEED spots in Fig. 4b for the 10 unit-cell film. The atomic force microscopy (AFM) image for the film in Fig. 4c shows an atomically flat surface. To change the cation stoichiometry of the film, the number of laser pulses on the Al2O3 target for each Al1+y O2 layer was varied.
Because of the high oxygen pressure during the LaAlO3 growth, the samples were well oxygenated. This was proven by polarization-dependent X-ray absorption spectroscopy (XAS) measurements. Figure 4d shows XAS spectra with different linear polarizations and the Ti L 2,3 X-ray linear dichroism (XLD) signals are shown in Fig. 4e for different LaAl1+y O3(1+0.5y) stoichiometry. No Ti3+ related features around 462 eV, characteristic of the oxygen deficient LaAlO3/SrTiO3 samples,32, 33 are observed. Rather, the spectra are similar to the fully oxygenated samples.32, 33 Figure 4f shows the Ti L 2,3 X-ray magnetic circular dichroism (XMCD) signals obtained from opposite circularly polarized XAS spectra. Very small XMCD signals were observed, indicating very weak ferromagnetism. This again is consistent with the fully oxygen annealed LaAlO3/SrTiO3 samples.32, 33
The temperature and stoichiometry dependences of the sheet resistance, sheet carrier density, and mobility are shown in Fig. 5a–f, respectively, for the 10 unit-cell thick LaAl1+y O3(1+0.5y) films. All of the films are conducting with sheet resistance around 104 Ω/□ at 300 K, in contrast to insulating films grown by PLD from LaAlO3 compound targets at this oxygen pressure.27, 34 Note that only the Al-rich LaAl1.08O3.12 film shows metallic behavior in the full temperature range, while all other films show low-temperature resistivity upturns, consistent with earlier reports of stoichiometry dependence.35, 36 The low temperature upturn has a -lnT dependence characteristic of the Kondo effect.37 This may be attributed to the inevitable defects at the LaAlO3/SrTiO3 interface, consistent with the weak magnetism shown by Fig. 4f. The black dashed line in Fig. 5d represents the threshold normal-state sheet resistance h/4e 2, or 6.5 kΩ/□ for a superconductor-insulator transition.38 Only the Al-rich samples have normal-state sheet resistance below the dashed line; these might thus exhibit superconductivity. The sheet carrier density is around 1014/cm2 for all the samples, close to the expected value of 1.7 × 1014/cm2. The sample with a higher sheet carrier density shows a lower mobility, in agreement with previous reports.26
Thin film growth can overcome the bulk equilibrium thermodynamic limit in stabilizing new phases via various kinetic mechanisms39 and elastic effects.40 By combining the strengths of reactive MBE and PLD, ALL-Laser MBE allows us to push the boundary further. Unlike stable phase materials SrTiO3 and LaAlO3, La5Ni4O13, the RP phase with n = 4, has never been reported in the literature. Thermodynamic calculations indicate that the stability of higher-n-value RP phases requires higher oxygen pressure at higher temperature.41 ALL-Laser MBE makes the atomic layer-by-layer growth at high oxygen pressures possible, leading to the successful stabilization of La5Ni4O13. How far ALL-Laser MBE can stretch the thermodynamic limit is a question to be explored. For example, we have not been able to grow thin film of BaMnO3, which is not a thermodynamically stable phase in the bulk form.
The versatility of ALL-Laser MBE is demonstrated here by three very different examples: non-polar film on non-polar substrate (homoepitaxy of SrTiO3), polar film on polar substrate (La5Ni4O13 on LaAlO3), and polar film on non-polar substrate (LaAlO3 on SrTiO3). Laser ablation from oxide targets in oxygen atmosphere generates various neutrals, ions, and molecules in a propagating plume.42 Understanding how these species successfully react to form neutral (e.g., SrO and TiO2) or charged [e.g., (LaO)+ and (AlO2)−] atomic layers in building up the oxide thin films and heterostructures in ALL-Laser MBE warrants theoretical investigations.
The central result of our work on the LaAlO3/SrTiO3 interface is the dependence of sheet carrier density on the stoichiometry of LaAl1+y O3(1+0.5y) shown in Fig. 5e. The black dashed line represents n s = (1.7−2y × 3.3) × 1014/cm2, which is expected by the electronic reconstruction hypothesis for the 10 unit-cell films.31 The red squares, which denote 300 K sheet carrier density, overlap with the dashed line. No additional mechanism is employed to explain our data, and we cannot produce the linear dependence on the LaAl1+y O3(1+0.5y) stoichiometry quantitatively using either oxygen vacancies or intermixing mechanisms without invoking remarkable coincidence. The quantitative agreement between our experimental result and the theoretical prediction provides a strong support to the electronic reconstruction mechanism as responsible for the 2D electron gas at the LaAlO3/SrTiO3 interface.
The key differences between our result and the previous reports are the high oxygen pressure during the film growth and the high film crystallinity as demonstrated by Fig. 4. We argue that the high oxygen pressure suppresses the likelihood of oxygen vacancies in SrTiO3. Well oxygenated samples produced during film growth can avoid possible defects when sufficient oxygen is provided only after the growth by annealing. Although ALL-Laser MBE may not prevent the possible thermodynamics-driven SrTiO3–LaAlO3 interdiffusion, the high oxygen pressure reduces the intermixing due to the bombardment effect. The c lattice constant of a stoichiometric LaAlO3 film in this work was small (3.71 Å), consistent with the expected value based on the Poisson ratio for a coherently strained film on SrTiO3, indicating a high structural perfection. Previous PLD studies on the stoichiometry dependence varied the laser energy density and oxygen pressure to change the LaAlO3 composition.28, 36 In our study the films were grown under the same conditions, therefore, the stoichiometry dependence observed is free from the effects of varying deposition conditions.
As ALL-Laser MBE combines the atomic layer-by-layer growth of reactive MBE with PLD’s versatility and compatibility with a broad range of oxygen pressures, it also inherits other characteristics of PLD such as the high kinetic energy of the ablated species, the impact of which needs to be studied. Nevertheless, ALL-Laser MBE is a significant addition to the toolbox of researchers aiming for the highest quality, new physics, new materials, and new functionalities in oxide thin films and heterostructures.
The (001) SrTiO3 substrates used in this work were treated following the receipe in ref. 43 to produce atomically flat TiO2-terminated surface with one unit-cell-high steps. The (001) LaAlO3 substrates used in this work were treated following the receipe in ref. 44 to produce atomically flat AlO2-terminated surface with one unit-cell-high steps.
A KrF excimer laser (λ = 248 nm, pulse duration 25 ns) was used with repetition rate ranging from 1 to 30 Hz. For the growth of SrTiO3, a single crystal SrO target and a ceramic TiO2 target were used. The oxygen pressure during the growth was 1 × 10−6 Torr and the substrate temperature was 760 °C. With a laser energy density of 0.9 J/cm2, the number of laser pulses was about 100 for each SrO layer and 80 for each TiO2 layer in the growth of stoichiometric SrTiO3 film. The offstoichiometric films Sr1+x Ti1−x O3 were created by supplying 100x% more SrO and 100x% less TiO2 in each layer. After the deposition, the films were cooled to room temperature in oxygen at the same pressure as during the growth. For the growth of La5Ni4O13, ceramic targets of La2O3 and NiO were used. The oxygen pressure during the growth was 37 mTorr and the substrate temperature was 600 °C. With the laser energy densities of 0.7 J/cm2 for LaO and 0.9 J/cm2 for NiO, the number of laser pulses was 75 for each LaO layer and 107 for each NiO2 layer. The sequence for the growth of each RP unit cell is LaO–NiO2–LaO–NiO2–LaO–NiO2–LaO–NiO2–LaO, i. e., four LaNiO3 layers followed by one extra LaO layer. After the deposition, the films were cooled to room temperature at a oxygen pressure of 8 × 104 Pa. For the growth of LaAlO3 film, ceramic targets of La2O3 and Al2O3 were used. The oxygen pressure during the growth was 37 mTorr and the substrate temperature was 720 °C. The laser energy density was 1.0 J/cm2 on the La2O3 target, requiring 75 laser pulses for each LaO layer, and 1.3 J/cm2 on the Al2O3 target, requiring 91 laser pulses for each AlO2 layer. The offstoichiometric LaAl1+y O3(1+0.5y) films were created by supplying 100y% more Al in each layer. After the deposition, the films were cooled to room temperature in oxygen at the same pressure as during the growth.
SrO and La2O3 are not stable at ambient atmosphere—they react with water to form hydroxides and La2O3 also absorbs CO2 from the air. The SrO and La2O3 targets were removed from the vacuum sealed packages from the manufacture in a glovebox with a dry nitrogen atmosphere, mounted on the target holders, and then transferred to the vacuum chamber via a load-lock system swiftly such that their exposure to the air was as short as possible.
The XRD and reflectivity measurements were performed using a Bruker D8 Discover system with Cu Kα radiation (λ = 1.5406 Å). The Leptos fitting software (Bruker AXS Inc.) was used to determine the out-of-plane lattice constant of the films from the θ–2θ scans (the substrate peak was used as the reference) and to determine the film thickness from the X-ray reflectivity (XRR) measurement.
Ultraviolet Raman spectroscopy measurements were performed in a backscattering geometry normal to the film surface using a Jobin Yvon T64000 triple spectrometer equipped with a liquid nitrogen cooled multichannel charge coupled device detector. Ultraviolet light (325 nm line of the He–Cd laser) was used for excitation. Maximum laser power density was ~0.5 W/mm2 at the sample surface, low enough to avoid any noticeable local heating of the sample. Spectra were recorded at 10 K using a variable temperature closed-cycle helium cryostat.
XLD and XMCD measurements were carried out at the elliptically polarized undulator beamline 4.0.2 of the Advanced Light Source, using the vector magnet end station and with an energy resolution of approximately 0.1 eV.45 Samples were cryogenically cooled to 13 K. Average probing depth in the total electron yield XAS detection mode was estimated to be approximately 5 nm, providing interface-sensitive information with minimal contribution from surface adsorbates. Measurements were carried out in near-grazing (30°) incidence geometry, enabling selective alignment of the X-ray electric field parallel to the ab-plane of the film for vertically-polarized light (E║ab), and almost parallel to the c-axis of the film for vertically polarized light (E║c). The XMCD spectra were obtained utilizing circularly polarized X-rays with and by alternating the direction of the applied magnetic field of 0.3 T between parallel and antiparallel directions with respect to the X-ray helicity vector.
The authors thank Dr. S. L. Shi and Dr. F. Q. Huang of Shanghai Institute of Ceramics, Chinese Academy of Sciences for synthesizing the ceramic SrO target which was used when developing the ALL-laser MBE technique. We thank Dr. P. S. Risborough for the helpful discussions concerning the Kondo effect. We thank Dr. Ph. Ghosez for comments on the manuscript and providing us with the first-principles calculation data on the LaAlO3 thickness dependence. This material is based upon work supported by the U.S. Department of Energy, Office of Science, under Grant No. DE-SC0004764 (Q. Y. L. and X. X. X.). Raman studies at Boise State University have been supported by NSF under Grant No. DMR-1006136 (A.K.F. and D. A. T.) TEM study was supported by CCDM, an EFRC funded by U.S. DOE-BES, under award #DE-SC0012575 (Q.Q.), by DOE-BES, Materials Science and Engineering, under Contract No. DE-SC0012704 (Y.Z.), and used resources of CFN at BNL, a U.S. DOE Office of Science Facility. A.X.G. acknowledges support from the U.S. Army Research Office, under Grant No. W911NF-15-1-0181. The Advanced Light Source is supported by the Director, Office of Science, Office of Basic Energy Sciences, of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231.Author Contributions
X. X. X. conceived and designed the research. Q. Y. L., M. G., and G. Z. L. carried out the experiment to develop the ALL-Laser MBE technique. B. A. D. was responsible for the growth calibration using the split RHEED intensity peaks. Q. Y. L. grew and characterized the Sr1+x Ti1−x O3+δ and LaAl1+y O3(1+0.5y)/SrTiO3 samples. M. G. grew and characterized the Ruddlesden-Popper phase La n+1Ni n O3n+1 (n = 4) samples. D. G. S. participated in the conceptual design of ALL-Laser MBE and was responsible for the MBE-grown comparison samples of Sr1+x Ti1−x O3+δ. Q. Q. and Y. M. Z. performed the TEM measurement. R. U. C., W. B. Y., A. X. G., and E. A. performed the XLD and XMCD measurements. A. K. F. and D. A. T. performed the UV Raman measurement. M. H. H. and J. D. G. contributed to the modeling of the RHEED intensity oscillations. R. K. S. performed the early RBS measurements. Q. Y. L., X. X. X. wrote the manuscript with significant contributions from D. G. S., A. X. G., and B. A. D. as well as contributions from all other authors.Competing interests
The authors declare no competing interests.
Electronic supplementary material
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/