The molecular organization in the smectic mesophases of a series of main-chain/side-chain block copolymers was studied by X-ray diffraction on oriented specimens. The main-chain and the side-chain blocks were phase-separated and gave rise to two coexisting smectic domains with different layer periodicities. The orientation of the smectic planes in the distinct domains with respect to the fiber axis was very different in the various samples and depended on the relative length of the blocks. In the presence of relatively short side-chain blocks, the orientation of the main-chain block dominated and the smectic planes of the side-chain block were forced to be parallel to those of the main-chain block and perpendicular to the fiber axis. In contrast, when the side-chain block was sufficiently long it imposed its own orientation to the main-chain block. In this case, the smectic planes of the main-chain block were oriented parallel to those of the side-chain block and to the fiber axis.
Similar content being viewed by others
Article PDF
References
G. Galli, E. Chiellini, M. Laus, M. C. Bignozzi, A. S. Angeloni, and O. Francescangeli, Makromol. Chem., 195, 2247 (1994).
M. Laus, M. C. Bignozzi, A. S. Angeloni, O. Francescangeli, G. Galli, and E. Chiellini, Polym. J., 27, 993 (1995).
O. Francescangeli, B. Yang, G. Albertini, A. S. Angeloni, M. Laus, E. Chiellini, and G. Galli, Liq. Cryst., 13, 353 (1993).
R. Zentel and H. Ringsdorf, Makromol. Chem., Rapid Commun., 5, 393 (1984).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Francescangeli, O., Laus, M., Bignozzi, M. et al. Hybrid Liquid-Crystalline Block Copolymers II. X-Ray Diffraction Analysis of Polyester-Polymethacrylate Block Copolymers. Polym J 28, 193–197 (1996). https://doi.org/10.1295/polymj.28.193
Issue Date:
DOI: https://doi.org/10.1295/polymj.28.193