Abstract
The orbital two-channel Kondo effect displaying exotic non-Fermi liquid behaviour arises in the intricate scenario of two conduction electrons compensating a pseudo-spin-1/2 impurity of two-level system. Despite extensive efforts for several decades, no material system has been clearly identified to exhibit all three transport regimes characteristic of the two-channel Kondo effect in the same sample, leaving the interpretation of the experimental results a subject of debate. Here we present a transport study suggestive of a robust orbital two-channel Kondo effect in epitaxial ferromagnetic L10-MnAl films, as evidenced by a magnetic field-independent resistivity upturn with a clear transition from logarithmic- to square-root temperature dependence and deviation from it in three distinct temperature regimes. Our results also provide an experimental indication of the presence of two-channel Kondo physics in a ferromagnet, pointing to considerable robustness of the orbital two-channel Kondo effect even in the presence of spin polarization of the conduction electrons.
Similar content being viewed by others
Introduction
The overscreened two-channel Kondo (2CK) effect displaying exotic non-Fermi liquid (NFL) physics has attracted widespread interest in recent years, especially due to their potential relevance to a host of current topics including strongly correlated physics, Majorana fermions, high-Tc superconductors, topological matters, carbon nanotubes and quantum dots1,2,3,4,5,6. In spin 2CK effect, a spin-1/2 impurity couples to conduction electrons into two equal orbital channels via an exchange interaction6,7,8,9. Below Kondo temperature (TK) the 2CK model gives rise to impurity quantum criticality accompanied by exotic NFL behaviour as the consequence of two conduction electron spins attempting to compensate the spin-1/2 impurity. However, the strict requirements of zero local magnetic field and channel symmetry make a direct observation of the spin 2CK effect difficult. Intriguingly, an analogous orbital 2CK effect was proposed to arise from resonant scattering centres with orbital degrees of freedom, for example, two-level systems (TLSs)10,11,12. As depicted in Fig. 1a, in a TLS, the tunnelling entity (for example, an atom, atom group or localized electron) coherently tunnels at a rate of 108–1012 s−1 between two independent quantum wells with asymmetry energy Δz, tunnelling matrix element Δx and energy splitting Δ=(Δz2+Δx2)1/2 between the lowest two eigenstates11,12. For the noncommutative model this problem is reduced to the 2CK case, the TLS being represented by a pseudo-spin-1/2 and the spin degeneracy of the conduction electrons being the two channels10,13. The orbital 2CK effect from TLSs is manifested in electrical transport by a unique temperature (T) dependence in resistivity with three distinct T regimes (Fig. 1b): a low-T upturn characterized by Δρxx∼lnT for T>TK, followed by NFL behaviour (Δρxx∼T1/2) for TD (=Δ2/TK)<T<<TK and deviation from T1/2 dependence upon further cooling11,12. The T1/2 dependence is a hallmark of the NFL state in the orbital 2CK effect, in striking contrast to the T2 scaling of Fermi-liquid (FL) behaviour in fully screened Kondo effect14. The stability of the low-T orbital 2CK fixed point is an important issue. Theoretically, the fixed point is unstable to Δ, channel-symmetry breaking in the exchange coupling and a magnetic field changing the electron population of the two channels, but stable to exchange anisotropy in the Kondo coupling15,16. Although the TLS model with electron-assisted tunnelling10 breaks down in the weak coupling limit17,18, the 2CK effect is theoretically expected in the case of resonant scattering and strong coupling19.
Despite the intensive studies for almost 30 years, the experimental proof for the existence of the orbital 2CK effect has been far from certain. First, it remains a challenge to unambiguously demonstrate the three-regime T dependence of the resistivity expected from the orbital 2CK effect in a single material system. Although the NFL behaviour was reported in Cu point contacts (PCs) and glassy ThAsSe single crystal20,21,22,23, their small Δ prevented the observation of possible breakdown of the T1/2 behaviour at lower T. Upadhyay et al.24 observed the NFL behaviour and the low-energy restoration of the FL in conductance spectroscopy of Ti PCs, but there was no indication of a crossover to logarithmic dependence at high energies. Furthermore, the H dependence and microscopic mechanisms of the orbital 2CK effect have remained unsettled. Although present theories expect an imbalance in the channel population to produce a crossover to FL behaviour at low temperatures25, a magnetic field of up to 14 (5) T did not affect the NFL behaviour in ThAsSe (ref. 22) (Ti PCs24). Microscopically, the dynamic tunnelling centres in TLSs were interpreted as a group of nonmagnetic atoms in PCs20,21, whereas resonant tunnelling of an electron in a polar bond transformation was argued to be responsible for the enhancement of TK to a few K in ThAsSe (ref. 22). Therefore, materials with TLSs of larger TK and Δ are desirable for a thorough study of the orbital 2CK physics, including its T and H dependencies and microscopic mechanisms.
Ferromagnetic correlations are predicted to have a detrimental effect on the spin 2CK, while in the case of the orbital 2CK, a coexistence over a large T range is possible as the electron spin variable does not directly enter into the interaction process. A crossover to FL behaviour is, however, expected at a low finite temperature in the neighbourhood of the T=0 2CK fixed point due to the asymmetry in the channel population. So far, there are two reports on orbital Kondo effect in ferromagnets26,27. The ferromagnetic UAs1−xSe1+x and Mn5Si3Cx display a logarithmic low-T upturn in the resistivity. A crossover to FL behaviour was also observed in Mn5Si3Cx at low T. However, neither shows a T1/2 dependence characteristic of 2CK effect, possibly because of their low TK, large TD and partial polarization of the conduction electrons.
In this work, we report experimental evidence of TLS-induced orbital 2CK effect in a ferromagnetic system, L10-MnAl epitaxial films with strong perpendicular magnetic anisotropy (PMA). We observed a low-T resistivity upturn with a clear transition from a lnT dependence to NFL behaviour signified by a T1/2 dependence, and deviation from it upon further cooling. The T dependencies are independent of applied magnetic fields up to 8 T. This represents an observation of all three theoretically expected transport regimes from the orbital 2CK effect in the same samples. The greatly enhanced TK and Δ in this system suggest fast coherent tunnelling of the TLSs and strong coupling with the conduction electrons. Moreover, the structural disorders in L10-ordered films can be tailored by varying the growth parameters28,29,30,31,32, offering a convenient pathway of tuning the relevant 2CK parameters.
Results
Sample structure and ferromagnetism
A series of 30-nm-thick L10-MnAl single-crystalline films (Fig. 1c) were grown at substrate temperatures (Ts) of 200, 250, 300, 350 and 400 °C. The degree of structural disorder decreases with increasing Ts from 200 to 350 °C, and then increases when Ts goes up to 400 °C, which is evidenced by both the intensity and the full width at half maximum of the L10-MnAl (002) peaks of X-ray diffraction patterns33. These films are strongly strained due to the epitaxial growth as indicated by their shorter c axes than bulk (c=3.57 Å)34, which make them likely candidates to have dynamic defects24. These films exhibit strong PMA as revealed by the well-defined hysteretic anomalous Hall resistance (Fig. 1d) and perpendicular magnetization hysteresis33.
Temperature dependence of the longitudinal resistivity
Figure 1e shows the T dependence of the zero-field longitudinal resistivity (ρxx) of the L10-MnAl films. Each film shows a resistivity minimum at a characteristic temperature (Tm) (Supplementary Fig. 1a). In the high T regime (T>Tm), ρxx increases linearly with T due to increasing phonon scattering (Supplementary Fig. 1b). Here we show that the low-T resistivity upturn in our L10-MnAl films likely arises from the TLS-induced orbital 2CK effect. Figure 2a–c plots the T dependence of resistivity variation at H=0 T for the L10-MnAl films, which shows distinct signatures associated with the TLS-induced 2CK effect. In the first regime, as displayed in Fig. 2a, the resistivity increase, Δρxx (Δρxx=ρxx−ρ1, with the offset ρ1 determined from the best linear fit of ρxx−lnT, see Supplementary Fig. 1c), varies linearly with lnT below a temperature T0 for all films with different Ts, similar to the well-known single-channel Kondo (1CK) effect due to static magnetic impurities14. Δρxx deviates from the lnT dependence and transitions to a T1/2 dependence when T drops below TK (Supplementary Fig. 2). The T1/2-dependent resistivity is regarded as a distinct signature of the NFL behaviour from the 2CK effect. Here, an interpretation of localization effects can be excluded, even if a dimensional crossover is considered. Taking into account the resistivity of films (132–214 μΩ cm), which yields a mean-free-path of 2.4–5.5 nm, the film thickness of 30 nm, and the high crossover temperatures (that is, TK) of up to 23 K, a dimensional crossover seems impossible because neither the thermal length (relevant for e–e interaction) nor the inelastic scattering length (relevant for quantum interference) is likely to approach the film thickness at these temperatures.
As can be seen in Fig. 2b, Δρxx (Δρxx=ρxx−ρ2, where ρ2 was determined from the best linear fit of ρxx−T1/2; ρ1 and ρ2 track each other, see Supplementary Fig. 1c) begins to increase more slowly than T1/2 below a characteristic temperature TD, indicating deviation from the NFL behaviour. The deviation is generic, H-independent (Fig. 3a) and distinct from that induced by quantum corrections in ThAsSe that only appeared at zero field22,23. This represents an observation of the TLS theory-expected deviation from the orbital 2CK state below TD in a diffusive conductor. We emphasize that the deviation is not due to Joule heating because the resistivities measured under a.c. current of 1 μA and d.c. current of 10 μA are virtually identical. Also, such deviation is not expected from conductance corrections due to electron–electron interaction or quantum interference effects. The lower temperature limit for the T1/2 regime is given theoretically by TD=Δ2/TK, from which Δ can be determined. In fully screened 1CK systems14 and frozen slow two-state systems27,35, ρxx was observed to saturate following the FL behaviour (∼T2) at low T. The latter have large tunnelling barrier and negligibly small Δx that only allow thermally activated hopping or incoherent tunnelling at a very slow rate (<<108 s−1) (ref. 10). However, in the TLS-induced 2CK effect, it has remained unclear how the system experimentally deviates from the NFL behaviour below TD. To shed light on this important issue in L10-MnAl, we measured ρxx down to 330 mK. As shown in Fig. 2c, none of these films with different Ts shows FL-like saturation (T2) in the studied temperature range, distinctly different from the expectation of a fully screened Kondo effect14. There are three possible reasons for this discrepancy: a broad distribution of TD of the TLSs; overlapping of the screening clouds of different TLSs; and the spin polarization of the conduction electrons due to the ferromagnetism. A broad distribution of TD would severely distort the T1/2 behaviour and is not a likely scenario. The 2CK displays impurity quantum critical behaviour so that the screening would diverge at T=0 under ideal conditions (Δ=0), in contrast to the 1CK problem where the screening radius (R) is finite. For orbital 2CK with nonzero Δ, R at T=0 K limit can be estimated by kFR∼D/TD, where kF is Fermi wavevector, D is band width (of the order of Fermi Energy EF). Using kF ∼1.7 Å−1 (EF∼11 eV)36, D∼10 eV, TD∼1 K for MnAl, one can estimate R to be on the order of ∼104 Å at T=0 K, which is much larger than the average distance between TLSs (see below). Hence, with decreasing T the screening clouds will eventually overlap, although this problem has yet to be quantitatively studied. The spin polarization, if homogeneous, should produce a crossover to a T2 dependence.
Figure 2d plots the slopes α=−dρxx/d(lnT) for TK<T<T0 and β=−dρxx/d(T1/2) for TD<T<TK as a function of Ts. It is evident that α and β have a similar Ts dependence, that is, α (β) first drops quickly from their maximum of 2.5 μΩ cm/lnK (1.0 μΩ cm K−1/2) at 200 °C to the minimum of 0.2 μΩ cm/lnK−1 (0.15 μΩ cm K−1/2) at 300–350 °C, and finally goes up to 0.25 μΩ cm/lnK−1 (0.18 μΩ cm K−1/2) at 400 °C. As is revealed in the metallic PC experiments, thermal annealing can significantly change the number of TLSs20,21. Here, the non-monotonic dependence of α and β on Ts could be ascribed mainly to the thermal tailoring of the density of active TLSs (NTLS). For the strong coupling TLS centres11, NTLS can be estimated by in the diffusive transport regime, where Δρxxm, τe and N(EF) are the maximum resistivity upturn due to the TLSs, electron scattering time and density of states at Fermi level, respectively. τe can be determined to be ∼10−15 s by ρxx=m*/ne2τe, where m*, n and e are effective mass, density (∼1022 cm−3) and charge of conduction electrons, respectively. Using a typical N(EF) (ref. 36) of ∼4 × 1022 eV−1cm−3 and experimental values of Δρxxm (≈Δρxx at 330 mK), NTLS was calculated and shown in Fig. 1d. The fast TLSs were annealed away20,21 and its density was reduced quickly as Ts increases to 300 °C; however, the overall population of TLSs increases beyond 350 °C due to the structural deterioration and strain relaxation of the L10-MnAl films33. The large NTLS (∼1020 cm−3) yields an average distance of ∼20 Å for the TLSs in these films.
The T1/2 and lnT dependencies of the resistivity upturns in different samples can be visualized more directly by collapsing the T-dependent Δρxx data of different samples onto single scaling curves of −Δρxx/βTK1/2=(T/TK)1/2 and −Δρxx/α−lnTK=ln(T/TK) for TD/TK<T/TK<1 and 1<T/TK<T0/TK, respectively. Figure 2e shows the log–log plot of −Δρxx/βTK1/2 against T/TK for the L10-MnAl samples with different Ts, from which log(−Δρxx/βTK1/2) is shown to scale linearly with log(T/TK) with a slope of 1/2 in TD/TK<T/TK<1 for all the samples. Similarly, the data for all the samples in the T range 1<T/TK<T0/TK can be scaled onto a single curve of −Δρxx/α−lnTK=ln(T/TK), as demonstrated by the semilog plot of −Δρxx/α−lnTK against T/TK (Fig. 2f).
Magnetic field effects
To establish more rigorously the orbital 2CK effect in our L10-MnAl films, we examined the effect of applied perpendicular magnetic fields, H, on the T-dependent resistivity. Here, in these films with strong PMA, anisotropic magnetoresistance (MR) and MR from spin disorder scattering under perpendicular H should be negligible due to the orthogonal magnetization-current relation and the large energy gap in spin wave excitation spectrum. This is highly amenable to study the H dependence of a 2CK effect. As an example, we show ρxx (T) of the L10-MnAl film grown at 200 °C under various H from 0 to 8 T in Fig. 3a,b. The magnetic fields have no measurable effects on the T dependence: ρxx scales linearly with lnT and T1/2 at TK<T<T0 and TD<T<TK (T0∼82.5 K, TK∼23 K and TD∼8.8 K), respectively. The same features hold for other films with different Ts. Figure 3c,d summarizes the values of α and β as a function of H for the L10-MnAl films with different Ts. It is clear that both α and β for all films are independent of H, strongly suggesting a nonmagnetic origin of the resistivity upturn scaling in the L10-MnAl. Specifically, there is no measurable change in T0, TK and TD under different H (Fig. 3a,b), suggesting a negligible effect of H on the coupling strength, the tunnelling symmetry and barrier height of the TLSs. These observations provide strong evidence for the orbital 2CK effect being induced by TLSs of nonmagnetic impurities. Here, it also should be pointed out that the Zeeman energy (∼0.9 meV at H=8 T) is negligibly small in comparison with EF and ferromagnetic exchange splitting (Eexchange∼2 eV) in L10-MnAl (ref. 36), hence should not have any measurable effect on the channel asymmetry (ΔN=N↑−N↓, where N↑ and N↓ are the numbers of majority and minority spins in the conduction band, respectively) and the three-regime resistivity upturn16,24,25. A small negative MR (<0.5%) is observed in the L10-MnAl at high H in a broad T range from 2 to 300 K, see Supplementary Fig. 3. The MR does not saturate even at 7 T and shows a linear scaling with H1/2, which is similar to that in ThAsSe (ref. 20). The MR shows a T dependence, which appears to have no correlation with any characteristic temperatures of the 2CK effect (Fig. 4). Though not yet well understood, such a MR behaviour in materials showing orbital 2CK effect due to TLSs is unlikely to be related to the T1/2 dependence of ρxx at TD<T<TK.
Characteristic temperatures of orbital 2CK effect
Figure 4 summarizes the relevant characteristic temperatures T0, TK and TD, and Δ of the L10-MnAl films as a function of Ts. As Ts increases, T0 drops markedly from 82.5 to 11.4 K, and goes up to 20.0 K as a consequence of the non-monotonic dependence of the TLS population on Ts (Fig. 2d). TK represents the temperature below which conduction electrons can overscreen the pseudo-spin of the impurity in an orbital 2CK system. Since there is an overlap between the two T regimes of lnT and T1/2 dependencies, the values of TK are defined as the centre of the T overlap. In striking contrast to the small experimental values in Cu PCs (0.1–5 K) and theoretical calculations on amorphous systems (<<1 K), TK ranges from 23.0 to 5.4 K in the L10-MnAl. The significant enhancement of TK in this system could be understood in terms of resonant scattering due to strong coupling of conduction electrons to the scattering centres19. Within this scenario, the decrease of TK at higher Ts may come from a reduced strength of the resonant scattering. Another intriguing observation is that Δ is tuned by as much as a factor of ∼5.6 when Ts varies between 200 and 400 °C, which is difficult to achieve in previously studied systems of metallic PCs or glasses using a voltage or magnetic field20,21,22,23,24. As Ts goes up, the fastest TLSs are annealed away, leaving the slower ones to dominate the scattering of conduction electrons. Therefore, with Ts increasing from 200 to 350 °C, the value of Δ for active TLSs decreases, leading to a reduction of TD. The upturn of T0, TK and TD, and Δ at Ts of 400 °C may be attributed to the increased population of fast TLSs and enhanced resonant scattering of conduction electrons due to the structural degradation31. Here, it is worth mentioning that the values of Δ observed in L10-MnAl films are much larger than those reported in Cu PCs (∼1 K)20,21 and ThAsSe (<0.01 K)22,23. Besides the small tunnelling barriers and fast scattering rates (that is, intrinsic TLS energy splitting), the adjacent Kondo cloud overlaps suggested by the non-T2 deviation and the ferromagnetic exchange splitting could also be responsible for the great enhancement in the effective values of Δ in these L10-MnAl ferromagnetic films. As suggested by the close correlation between the Ts dependence of the characteristic parameters of the TLS-induced 2CK effect, that is, α, β, T0 and TK, and Δ with those of structural imperfections and the magnetic properties (for example, magnetization and PMA)33, electrons as the tunnelling centres of the TLSs in the L10-MnAl films can be excluded. Similarly, the magnetic Mn atoms can also be ruled out because of the nonmagnetic nature of the orbital Kondo effect. Therefore, we surmise that the nonmagnetic small Al atoms have the role of TLS centres in the present films. In nanoscale tunnelling systems (for example, 3–10 nm-wide Cu PCs37), it has been possible to observe individual constituent of the 1/f noise, for example, that results from the motion of atomic defects or electrons. However, such constituent is much more difficult to resolve in metallic films37, for example, our L10-MnAl epitaxial films. New spectroscopic probe techniques need developing for definitely identifying the microscopic nature of the TLSs in these diffusive metal films.
Coexistence of orbital 2CK with ferromagnetism
Now, we discuss the apparent coexistence of orbital 2CK with ferromagnetism. In a conventional ferromagnet, although the Kondo coupling between the TLS and itinerant electrons is irrelevant to the electron spins, the symmetry of the two spin channels is broken due to ferromagnetic exchange splitting of the d-band. The channel asymmetry should lead to different tunnelling rates of a TLS for two spin channels and thus weaken the NFL behaviours in comparison with its nonmagnetic counterpart (ΔN=0). If the degree of channel asymmetry (P=ΔN/(N↑+N↓)) is large enough, this should be manifested as a decreased magnitude (β) and an enhanced effective breakdown temperature (TD) of the 2CK effect as a result of the enhanced decoupling of TLS from one spin channel. On the basis of a simple assumption in the Stoner model for itinerant ferromagnetism38, the saturation magnetization (Ms) can be an index of the channel asymmetry, that is, Ms∝ΔN. However, this effect is difficult to quantify experimentally as one cannot vary Ms while keeping other parameters (for example, NTLS, coupling strength, Kondo cloud overlap, barrier height and tunnelling rate) of the TLSs constant in a set of samples. For our L10-MnAl films, the Ts dependence of the measured β and TD is dominated by the variation of the other parameters, respectively, rather than that of ΔN, as suggested by the quite different Ts dependence of the 2CK parameters (β and TD) and Ms. The fully ordered L10-MnAl is theoretically an itinerant magnet with a spin polarization of 23.8% at the Fermi surface39 and a magnetization Ms of ∼800 e.m.u. cm−3 (that is, 2.37 μB f.u.−1)28,36. In our disordered L10-MnAl samples, the measured Ms is much smaller (157–306 e.m.u. cm−3, see Fig. 5), suggesting a very low ΔN (<<N↓) and P (<<1). This could be a reason why it is still difficult to establish a definitive quantitative correlation between ΔN and the 2CK parameters (β and TD).
Discussion
We have observed transport behaviour highly suggestive of a robust orbital 2CK effect from TLSs in epitaxial L10-MnAl films with strong PMA. The H-independent resistivity upturn scaling with lnT and T1/2 in the two T regimes below the resistance minimum, and deviation from the NFL behaviour at the lowest temperatures are consistent with the TLS model. The molecular beam epitaxy growth method afforded unprecedented tunability of the TLS density, TK and Δ in this material system, leading to the insight on the origin of the 2CK effect. The greatly enhanced TK and Δ suggest resonant tunnelling of TLSs due to the strong coupling with conduction electrons. The orbital 2CK effect in a material with significant ferromagnetism and conduction spin polarization is an intriguing observation that warrants further theoretical and experimental studies.
Methods
Sample growth and characterization
L10-MnAl films were grown on 150 nm GaAs-buffered semi-insulating GaAs (001) by molecular beam epitaxy and capped with a ∼4 nm-thick Al2O3 layer. The thickness and Mn/Al atomic ratio of L10-MnAl layer is calibrated to be 30 nm and 1.1 by cross-sectional high-resolution transmission microscopy with energy dispersive X-ray spectroscopy31, respectively. Synchrotron X-ray diffraction and Quantum Design SQUID were used to characterize the structures and magnetization properties of these films.
Device fabrication and transport measurement
These films were patterned into 60 μm wide Hall bars with adjacent electrode distance of 200 μm using photolithography and ion-beam etching for transport measurements (Fig. 1c). The longitudinal resistivity was measured as a function of temperature (T) and magnetic field (H) in a Quantum Design PPMS for T=2–300 K (DC, I=10 μA) and in an Oxford 3He cryostat for T=0.33–5 K (a.c, I=1 μA).
Additional information
How to cite this article: Zhu, L. J. et al. Orbital two-channel Kondo effect in epitaxial ferromagnetic L10-MnAl films. Nat. Commun. 7:10817 doi: 10.1038/ncomms10817 (2016).
References
Béri, B. & Cooper, N. R. Topological Kondo effect with Majorana Fermions. Phys. Rev. Lett. 109, 156803 (2012).
Kashuba, O. & Timm, C. Topological Kondo effect in transport through a superconducting wire with multiple Majorana end states. Phys. Rev. Lett. 114, 116801 (2015).
Jarillo-Herrero, P. et al. Orbital Kondo effect in carbon nanotubes. Nature 434, 484–488 (2005).
Mitchell, A. K., Sela, E. & Logan, D. E. Two-channel Kondo physics in two-Impurity Kondo models. Phys. Rev. Lett. 108, 086405 (2012).
Delattre, T. et al. Noisy Kondo impurities. Nat. Phys 5, 208–212 (2009).
Potok, R. M., Rau, I. G., Shtrikman, H., Oreg, Y. & Goldhaber-Gordon, D. Observation of the two-channel Kondo effect. Nature 446, 167–171 (2007).
Yeh, S. & Lin, J. Two-channel Kondo effects in Al/AlOx/Sc planar tunnel junctions. Phys. Rev. B 79, 012411 (2009).
Nozières, P. & Blandin, A. Kondo effect in real metals. J. Phys. France 41, 193–211 (1980).
Schlottmann, P. & Sacramento, P. D. Multichannel Kondo problem and some applications. Adv. Phys. 42, 641–682 (1993).
Zawadowski, A. Kondo-like state in a simple model for metallic glasses. Phys. Rev. Lett. 45, 211–214 (1980).
Cox, D. L. & Zawadowki, A. Exotic Kondo effects in metals: Magnetic ions in a crystalline electric field and tunneling centres. Adv. Phys. 47, 599–942 (1998).
Delft, J. von et al. The 2-channel Kondo model: I. Review of experimental evidence for its realization in metal nanoconstrictions. Annals. Phys. 263, 1–55 (1998).
Muramatsu, A. & Guinea, F. Low-temperature behavior of a tunneling atom interacting with a degenerate electron gas. Phys. Rev. Lett. 57, 2337 (1986).
Hewson, A. C. The Kondo Problem to Heavy Fermions Cambridge Univ. Press (1993).
Pang, H. B. & Cox, D. L. Stability of the fixed point of the two-channel Kondo Hamiltonian. Phys. Rev. B 44, 9454 (1991).
Affleck, I. et al. Relevance of anisotropy in the multichannel Kondo effect: comparison of conformal field theory and numerical renormalization-group results. Phys. Rev. B 45, 7918 (1992).
Aleiner, I. L. et al. Kondo temperature for the two-channel Kondo models of tunneling centers. Phys. Rev. Lett. 86, 2629 (2001).
Aleiner, I. L. et al. Experimental tests for the relevance of two-level systems for electron dephasing. Phys. Rev. B 63, 201401 (R) (2001).
Zaránd, G. Existence of a two-channel Kondo regime for tunneling impurities with resonant scattering. Phys. Rev. B 72, 245103 (2005).
Ralph, D. C. & Buhrman, R. A. Observations of Kondo scattering without magnetic impurities: a point contact study of two-level tunneling systems in metals. Phys. Rev. Lett. 69, 2118 (1992).
Ralph, D. C., Ludwig, A. W. W., Delft, J. v. & Buhrman, R. A. 2-channel Kondo scaling in conductance signals from 2 level tunneling systems. Phys. Rev. Lett. 72, 1064 (1994).
Cichorek, T. et al. Two-channel Kondo effect in glasslike ThAsSe. Phys. Rev. Lett. 94, 236603 (2005).
Cichorek, T. et al. TLS Kondo effect in structurally disordered ThAsSe. J. Mag. Mag. Mater 272, 66–67 (2004).
Upadhyay, S. H. et al. Low-energy restoration of Fermi-liquid behavior for two-channel Kondo scattering. Phys. Rev. B 56, 12033 (1997).
Schlottmann, P. & Lee, K. J. B. Quenching of overcompensated Kondo impurities via channel asymmetry. Physica B 223–224, 458–463 (1996).
Henkie, Z., Fabrowski, R. & Wojakowski, A. Anisotropies of the electrical resistivity and Hall effect in UAsSe. J. Alloys Compd. 219, 248–251 (1995).
Gopalakrishnan, B. et al. Electronic transport in magnetically ordered Mn5Si3Cx films. Phys. Rev. B 77, 104414 (2008).
Zhu, L. J., Nie, S. H. & Zhao, J. H. Recent progress in perpendicularly magnetized Mn-based binary alloy films. Chin. Phys. B 22, 118505 (2013).
Zhu, L. J. et al. Multifunctional L10-Mn1.5Ga films with ultrahigh coercivity, giant perpendicular magnetocrystalline anisotropy and large magnetic energy product. Adv. Mater. 24, 4547 (2012).
Zhu, L. J., Pan, D., Nie, S. H., Lu, J. & Zhao, J. H. Tailoring magnetism of multifunctional MnxGa films with giant perpendicular anisotropy. Appl. Phys. Lett. 102, 132403 (2013).
Nie, S. H. et al. Perpendicularly magnetized τ-MnAl (001) thin films epitaxied on GaAs. Appl. Phys. Lett. 102, 152405 (2013).
Zhu, L. J., Pan, D. & Zhao, J. H. Anomalous Hall effect in epitaxial L10-Mn1.5Ga films with variable chemical ordering. Phys. Rev. B 89, 220406 (R) (2014).
Nie, S. H., Zhu, L. J., Pan, D., Lu, J. & Zhao, J. H. Structural characterization and magnetic properties of perpendicularly magnetized MnAl films grown by molecular-beam epitaxy. Acta. Phys. Sin 62, 178103 (2013).
Koch, A. J. J. et al. New Material for Permanent Magnets on a Base of Mn and Al. J. Appl. Phys. 31, 75 (1960).
Zimmerman, N. M., Golding, B. & Haemmerle, W. H. Magnetic field tuned energy of a single two-level system in a mesoscopic metal. Phys. Rev. Lett. 67, 1322 (1991).
Sukuma, A. Electronic structure and magnetocrystalline anisotropy Energy of MnAl. J. Phys. Soc. Jpn 63, 1422 (1994).
Ralls, K. S. & Burman, R. A. Microscopic study of 1/f noise in metal nanobridges. Phys. Rev. B 44, 5800 (1991).
Stoner, E. C. Collective electron ferromagnetism. Proc. R. Soc. Lond. Ser. A 165, 372–414 (1938).
Park, J. H. et al. Saturation magnetization and crystalline anisotropy calculations for MnAl permanent magnet. J. Appl. Phys. 109, 09A731 (2010).
Acknowledgements
We thank Y.Q. Li and J. Liao for their help on the ultralow temperature measurements. We also thank S. von. Molnár and G. Woltersdorf for discussions. L.J.Z., S.H.N. and J.H.Z. were supported partly by MOST of China (grant no. 2015CB921503), NSFC (grant no. 61334006) and the CAS/SAFEA International Partnership Program for Creative Research Teams. P.X. acknowledges support from NSF grant DMR-1308613. P.S. was supported by the US Department of Energy under grant DE-FG02-98ER45707.
Author information
Authors and Affiliations
Contributions
L.J.Z. and J.H.Z. designed the experiment. L.J.Z. and S.H.N. grew the samples and performed the structural and magnetic characterizations. L.J.Z. fabricated the Hall bar devices and performed transport measurements. L.J.Z., P.X., P.S. and J.H.Z. analysed the data and wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-3 and Supplementary Reference (PDF 525 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zhu, L., Nie, S., Xiong, P. et al. Orbital two-channel Kondo effect in epitaxial ferromagnetic L10-MnAl films. Nat Commun 7, 10817 (2016). https://doi.org/10.1038/ncomms10817
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms10817
This article is cited by
-
Transport signatures of the topological surface state induced by the size effect in superconductor β-PdBi2
Science China Physics, Mechanics & Astronomy (2023)
-
Iron phthalocyanine on Au(111) is a “non-Landau” Fermi liquid
Nature Communications (2021)
-
Anomalous resistivity upturn in epitaxial L21-Co2MnAl films
Scientific Reports (2017)
-
Observation of orbital two-channel Kondo effect in a ferromagnetic L10-MnGa film
Scientific Reports (2016)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.