Abstract
Layer-by-layer gold nanoparticles are used to generate photocurrent in an environmentally-friendly plasmon-sensitized solar cell towing to surface plasmon resonance. The efficiency of the photoelectric conversion of gold nanoparticle layers is increased as the intensity of surface plasmon resonance increases. We also explain the experimental results by modeling the phenomenon of charge separation and photocurrent formation, and the relationship between surface plasmon resonance and photocurrent formation, which has potential application in plasmon-sensitized solar cells and plasmonic solar cells in the future.
Similar content being viewed by others
Introduction
Nobel nanoparticles have many of the usual physical and optical properties, including surface plasmon resonance.1,2,3,4,5,6 Surface plasmon resonance produces a stronger electromagnetic field on the surface of gold nanoparticles and has been applied to the enhancement of Raman scattering,7 photoluminescence,8 biolight emission devices9 and solar cells.10
Recently, surface plasmon resonance of noble metals has been used to separate charges on TiO2 films to form negative potential changes and anodic currents under visible light radiation,3,11,12,13,14 which will potentially be able to facilitate the promising application of plasmon-sensitized solar cells and plasmonic solar cells in the future. A few studies3,11,12,13,14 have reported results concerning the phenomenon of plasmon-induced charge separation at TiO2 films loaded with gold nanoparticles. In these experiments, photons resulting from incident light couple with a plasmon to serve as an exciton to separate the charge on gold nanoparticles. The electron is then ejected from the gold nanoparticle onto TiO2 films. The photocurrents of TiO2 films loaded with gold nanoparticles were measured under visible light radiation. However, surface plasmon resonance is an electromagnetic standing wave. Few studies have reported how an electromagnetic standing wave, a frequency-dependent physical parameter, is able to produce a frequency-independent photocurrent (for frequencies of visible light ranging from 1014 to 1015 Hz). By understanding the mechanism of surface plasmon resonance and optimizing the fabrication of a photocell, the efficiency of photovoltaic cells is able to be enhanced.
In this paper, we use gold nanoparticles loaded on TiO2 film to form photocurrents, as shown in Figure 1. Surface plasmon resonance is used to separate the charges on TiO2 films and form the photocurrent. We then use a theoretical model to confirm the phenomenon of charge separation and photocurrent formation and the relationship between surface plasmon resonance and photocurrent formation. This result is applicable to improve the intensity of photocurrents in the field of plasmon-sensitized solar cells.
Materials and methods
Twelve grams of P-25 TiO2 (Degussa, Shinjuku-ku, Japan) powder in 15 ml deionized water mixed with 0.2 ml Triton-X 100 (Sigma, St. Louis, MO, USA) and 0.4 ml acetaldehyde (99.5%; Fluka, Heidelberg, Germany) were vibrated ultrasonically for 3 days. Subsequently, 0.5 ml TiO2 solution was spin-coated on a fluorine-doped tin oxide (FTO) glass substrate at 1000 rad s−1 for 20 s and then sintered at 500 °C for 10 h. After calcinations at 500 °C for 10 h, the FTO had a sheet resistance of 10.3 Ω per square, and the P-25 had a higher anatase content (rutile/anatase=1:4).15
Au nanoparticles (NPs) were synthesized by chemical reduction, by adding 30 ml of 3 mM HAuCl4(aq) (AlfaAesar, Lancashire, UK) to 80 ml of 5 mM tetraoctylammonium bromide (Sigma) in hexane. To this solution was added 25 ml of 0.05 M NaBH4(aq) (Alfa Aesar). The color of the solution turned from yellow to black. Au NPs were modified by tetraoctylammonium bromide. The morphology of the Au NPs in hexane under transmission electron microscopy (TEM) observation and on TiO2 FTO substrate is presented in Figure 2.
Mercapto-propyl-tri-methoxy-silane (95%; Alfa Aesar) was used as a molecular linker connecting the substrate with the Au NPs through self-assembled monolayers. The TiO2/FTO was immersed in the solution (NH4OH/H2O2/H2O=5:5:1 in volume) for 3 h in order to get modified OH− on the surface of the substrate. The TiO2/FTO was then immersed in 1% 3-mercaptopropyltrimethoxysilane hexane for 1 day, and then in a Au NPs colloid for 1 day. Au NPs were modified on the substrate. Molecular linkers, including 2 wt-% 2-mercaptoethanol (98%; Alfa Aesar) and 2 wt-% 1,3-propanedithiol (97%; Alfa Aesar) in hexane, were then added to modify the surface of the Au NPs. The Au NPs were immersed with the molecular linkers for 1 day. The sample was immersed in the Au NPs colloid again for 1 day. By repeating the above process five times, layer-by-layer Au NPs were fabricated on the substrate as an anode electrode. Thickness and fraction of layer-by-layer Au NPs on the TiO2/FTO substance are presented in Figure 3. Pt was sputtered on the indium-doped tin oxide glass as the cathode electrode.
The electrolyte was a water-based solution (35% ethanol and 65% water), including 0.1 M Ce(NO3)3/0.05 M Ce(NO3)4 (99%; ICN Biomedicals, Inc., Aurora, OH, USA).
The morphologies of the Au NPs were observed by TEM. The as-grown product was observed by a Hitachi model HF-2000 transmission electron microscope operating at 200 kV. The absorption of Au NPs was observed by UV-visible spectrometry (Hitachi U-2001 spectrophotometer). The sample was directly injected into a quartz tube for UV-visible light analysis. The optical properties and thickness were determined by ellipsometry (h-VASE; Woollam, Lincoln, NE, USA) in the visible light range. The electric properties, current and voltages, were measured by a high voltage Source-Measure unit (Keithley 237). The power of the simulated solar energy (AM1.5) was 100 mW cm−2. The J–V curve under solar simulator radiation was recorded.
Results and discussion
Energy level of surface plasmon resonance
A metal cluster with a diameter greater than 3 nm has bulk-like physical properties and energy levels that are not discrete.16 In our case, the diameter of gold NPs is ∼6 nm as shown in Figure 2a. The Fermi-level of bulk-like gold NPs is the work function. Surface plasmon resonance induces excitons to separate the positive and negative charges. The density of states of the surface plasmon resonance range from 510 to 580 nm in the visible light region (see also Figure S1 in Supplementary Information). In a solar cell, the Fermi-level of bulk-like gold NPs contacts that of the semiconductor due to the balance of the electronic density on the surface. Energy level, E, referred by the expectation value of the surface plasmon resonance’s induced dipole, is under the work function of gold NPs. The difference in energy between E and the work function is Eg, as shown in Figure 1. The SPR of gold NPs induces a dipole, which acts as an energy level to support the transition of photoelectrons. Photoelectrons then transfer from the SPR level of the gold NP to the conduction band of the semiconductor.17 Photoelectrons are injected into the anode electrode and are inhibited from returning due to the Schottky barrier.18 The charged gold NP is renewed by the donor from the electrolyte, as shown in Figure 1.
SPR enhances photoelectric voltage
Open-circuit voltage (Voc) is determined by the difference between the chemical potential of the electrolyte and the conductive band (CB) of a semiconductor (). For a regular solution case, the Gibbs free energy of an electrolyte is presented as the following:
where μ is the Gibbs free energy of electrolyte, is the ratio of Ce4+, is the ratio of Ce3+, is the Gibbs free energy of Ce4+, is the Gibbs free energy of Ce3+, and Ω is the interaction relationship between and (Ω is constant for a regular solution.). When an external electrical field is applied to the system, the free energy is represented as G′=G−qV, where q is the charge of the system, V is the potential of the external electrical field and G is the Gibbs free energy. For the Ce4+ system, the free energy is due to the four electrons of the system. On the other hand, for the Ce3+ system, the free energy is , because of the three electrons of the system.
The open-circuit voltage (Voc) is represented as the following:
The open-circuit voltage (Voc) is proportional to the external electrical field.
The SPR of gold NPs applies a strong external electric field in the near field. As the number of gold NPs increases, the intensity of SPR rises, as shown in Figure 4. When the array of gold NPs is random, as in Figure 2b, no special peak of SPR appears due to the geometric effect. The open-circuit voltage (Voc) is proportional to the external electric field for our experimental results, as shown in Figure 5c, corresponding to the above result. SPR produces a stronger electric field that enhances the open-circuit voltage of a photovoltaic cell.
SPR enhances photoelectric current
The electron excitation process19,20 in a photovoltaic cell is shown as follows:
where g is the generation, τ is the lifetime, φn is the energy level for electrons and n is the particle number. When processing for a short time interval, g, φn and n are represented as follows:
Then this can be applied in the electron excitation process:
And and . Then
In the above equation, the chemical effective capacity is , the physical effective current is iph=eg, and the reaction effective resistance is . In the above equation, the term, eg, is the special solution for the effective current: .
SPR can produce a strong electric field that functions as the hot spot to enhance the pumping rate of the electrons between bands. During this process, the generation, g, will increase. As the generation increases, the effective current in a photovoltaic cell will rise. The short-circuit current will rise at the same time. In our experiment, the short-circuit current is proportional to the SPR intensity, as is shown in Figure 5b, which presents the relation: .
SPR enhances photoelectric properties
In a photovoltaic cell, the current–voltage curve of a solar cell yields important operational parameters,21 among which are the short-circuit current Jsc, the open-circuit voltage Voc, the current Jmp and voltage Vmp at the maximum power point Pmax. The fill factor (FF) is defined as
The solar conversion efficiency (η) is given by
where Ps is the input solar irradiance (in mW cm−2).
In a p–n junction solar cell model,22 the Vmp, Jmp and FF can be determined as:
where Js is the saturated current in a photovoltaic cell, and
When SPR is applied in a solar cell, and are put into the above equations, then Vmp′, Jmp′ and FF′ are represented in the SPR solar cell case as:
where and . (b−1)+aV/kBT and −ln(b+aV/kBT) act as the antagonism for the FF′, which makes the relationship between SPR intensity and the fill factor irregular, as shown in Table 1. The solar conversion efficiency (η′) is given by
The solar conversion efficiency (η′) is a second-order equation of the external electric SPR field. In our experiment, the solar conversion efficiency (η′) is a second-order equation of SPR intensity, as shown in Figure 5d.
By modeling the phenomenon of photoelectric conversion efficiency induced by SPR, the mechanism of solar conversion efficiency can be better understood, which could be used to enhance the efficiency of plasmon-sensitized solar cells in the future.
Conclusion
Gold nanoaprticles separate charges under visible light radiation. We fabricated gold nanoparticles using the layer-by-layer method on a TiO2 film to form multilayers in order to increase the intensity of the photocurrent. The efficiency of photoelectric conversion increased as the thickness increased. After optimization, nobel metal nanoparticles are possible candidates to replace dyes in solar cells and to act as plasmon-sensitized solar cells and plasmonic solar cells in the future.
References
Huang XQ, Tang SH, Mu XL, Dai Y, Chen GX et al. Freestanding palladium nanosheets with plasmonic and catalytic properties. Nat Nanotechnol 2011; 6: 28–32.
Kabashin AV, Evans P, Pastkovsky S, Hendren W, Wurtz GA et al. Plasmonic nanorod metamaterials for biosensing, Plasmonic-metal nanostructures for efficient conversion of solar to chemical energy. Nat Mater 2009; 8: 867–871.
Li HB, Li FY, Han CP, Cui ZM, Xie GY et al. Highly sensitive and selective tryptophan colorimetric sensor based on 4,4-bipyridine-functionalized silver nanoparticles. Sens Actuat B Chem. 2009; 145: 194.
Tian Y, Shi X, Lu CQ, Wang SL . Charge separation in solid-state gold nanoparticles-sensitized photovoltaic cell. Electrochem Commun 2009; 11: 1603–1605.
Cuevas-Muniz FM, Guerra-Balcazar M, Castaneda F, Ledesma-Garcia J, Arriaga LG . Performance of Au and AuAg nanoparticles supported on Vulcan in a glucose laminar membraneless microfuel cell. J Power Sources 2011; 196: 5853.
Lu YZ, Wang YC, Chen W . Silver nanorods for oxygen reduction: Strong effects of protecting ligand on the electrocatalytic activity. J Power Sources 2011; 196: 3033.
Zhou HQ, Qiu CY, Yu F, Yang HC, Chen MJ et al. Thickness-dependent morphologies and surface-enhanced raman scattering of Ag deposited on n-Layer graphenes. J Phys Chem C 2011; 115: 11348–11354.
Niu BJ, Wu LL, Tang W, Zhang XT, Meng QG . Enhancement of near-band edge emission of Au/ZnO composite nanobelts by surface plasmon resonance. CryStengComm 2011; 13: 3678–3681.
Su YH, Tu SL, Tseng SW, Chang YC, Chang SH et al. Influence of surface plasmon resonance on the emission intermittency of photoluminescence from gold nano-sea-urchins. Nanoscale 2010; 2: 2639–2646.
Baba A, Aoki N, Shinbo K, Kato K, Kaneko F . Grating-coupled surface plasmon enhanced short-circuit current in organic thin-film photovoltaic cells. ACS Appl Mater Interf 2011; 3: 2080–2084.
Furube A, Du L, Hara K, Katoh R, Tachiya M . Ultrafast plasmon-induced electron transfer from gold nanodots into TiO2 nanoparticles. J Am Chem Soc 2007; 129: 14852.
Linic S, Christopher P, Ingram DB . Plasmonic-metal nanostructures for efficient conversion of solar to chemical energy. Nat Mater 2011; 10: 911.
Tian Y, Tatsuma T . Plasmon-induced photoelectrochemistry at metal nanoparticles supported on nanoporous TiO2 . Chem Commun (Camb) 2004; (16): 1810–1811
Tian Y, Tatsuma T . Mechanisms and applications of plasmon-induced charge separation at TiO2 films loaded with gold nanoparticles. J Am Chem Soc 2005; 127: 7632.
Two highly dispersed metallic oxides by the aerosil process. Degussa Corp.: Akron, OH, USA, 1990. Degussa technical bulletin no. 56.
Zhu M, Aikens CM, Hollander FJ, Schatz GC, Jin R . Correlating the crystal structure of a thiol-protected Au25 cluster and optical properties. J Am Chem Soc 2008; 130: 5883.
Furube A, Du L, Hara K, Katoh R, Tachiya M . Ultrafast plasmon-induced electron transfer from gold nanodots into TiO2 nanoparticles. J Am Chem Soc 2007; 129: 14852.
McFarland EW, Tang J . A photovoltaic device structure based on internal electron emission. Nature 2003; 421: 616.
Bisquert J, Cahen D, Hodes G, Riihle S, Zaban A . Physical chemical principles of photovoltaic conversion with nanoparticulate, mesoporous dye-sensitized solar cells. J Phys Chem B 2004; 108: 8106.
Wang Q, Ito S, Gratzel M, Fabregat-Santiago F, Mora-Seró I et al. Characteristics of high efficiency dye-sensitized solar cells. J Phys Chem B 2006; 110: 25210.
Smestad GP . Optoelectronics of solar cells. Washington, DC: SPIE; 2002.
Wurfel P . Physics of Solar Cells: From Principles to New Concepts. Weinhein: Wiley-VCH Verlag GmbH & Co. KGaA; 2005.
Acknowledgements
This work was financially supported by the National Science Council of Taiwan, No. 100-2218-E-259-003-MY3, which is gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Additional information
Note: Supplementary information is available on the Light: Science & Applications' website.
Supplementary information
Rights and permissions
This work is licensed under the Creative Commons Attribution-NonCommercial-No Derivative Works 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/3.0/
About this article
Cite this article
Su, YH., Ke, YF., Cai, SL. et al. Surface plasmon resonance of layer-by-layer gold nanoparticles induced photoelectric current in environmentally-friendly plasmon-sensitized solar cell. Light Sci Appl 1, e14 (2012). https://doi.org/10.1038/lsa.2012.14
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/lsa.2012.14