For many years, the idea of analyzing atom-atom contacts in amorphous drug-polymer systems has been of major interest, because this method has always had the potential to differentiate between amorphous systems with domains and amorphous systems which are molecular mixtures. In this study, local structure of ionic and noninonic interactions were studied by High-Energy X-ray Diffraction and Pair Distribution Function (PDF) analysis in amorphous solid dispersions of lapatinib in hypromellose phthalate (HPMCP) and hypromellose (HPMC-E3). The strategy of extracting lapatinib intermolecular drug interactions from the total PDF x-ray pattern was successfully applied allowing the detection of distinct nearest neighbor contacts for the HPMC-E3 rich preparations showing that lapatinib molecules do not cluster in the same way as observed in HPMC-P, where ionic interactions are present. Orientational correlations up to nearest neighbor molecules at about 4.3 Å were observed for polymer rich samples; both observations showed strong correlation to the stability of the systems. Finally, the superior physical stability of 1:3 LP:HPMCP was consistent with the absence of significant intermolecular interactions in (∆) in the range of 3.0 to 6.0 Å, which are attributed to C-C, C-N and C-O nearest neighbor contacts present in drug-drug interactions.
The establishment of relationships between structural packing and physico-chemical properties has become fundamental for the modern pharmaceutical development1,2,3,4,5. In order to overcome poor solubility and improve bioavailability the use of amorphous and nanocrystalline systems are growing, as is the necessity of improved methods to characterize them6. In amorphous systems the atoms are ordered primarily at short (2–5 Å) and medium-range (5–20 Å.)7 distances. This makes atomic structure determination a challenging task that cannot be properly addressed by classical crystallography8,9,10,11. The quote of Alfred North Whitehead, highlighted by Mackey8 in his work about generalized crystallography fits well to better visualize this problem: “A crystal lacks rhythm from excess of pattern, while a fog is unrhythmic in that it exhibits a patternless confusion of detail”12. Although the presence of chemical bonds between molecules within the system ensures not all ordering is lost and some degree of preferred orientation can and often does persist in an amorphous solid.
Towards finding order within the chaos of amorphous systems the combination of total X-ray diffraction and pair distribution function analysis (PDF) has been utilized in the last decades as a valuable approach and it is being used more and more in the study of great variety of glasses13,14,15,16,17. The PDF expresses the probability of finding a pair of atoms which are separated from each other by a determinate distance (r), represented by peaks generated by intramolecular and intermolecular interactions, taking into account their abundance in the system13,15. Examples of common events observed in PDF patterns and information that can be extracted from them are summarized in Table 1.
Besides its wide use in the study of inorganic glasses7,18, the pharmaceutical literature is expanding in the applications of the technique5,14,15. Several groups have used conventional X-ray diffraction patterns to generate PDF patterns19,20,21,22. Due to inherent limitations of those low energy laboratory X-ray sources11 it is possible that these patterns contain artifacts, nevertheless, these papers illustrate the type of studies that can be done with PDF. Sheth and co-workers accessed the local structure of amorphous piroxicam prepared by cryogrinding from different polymorphs using this tool22. Differences in PDF patterns during grinding indicated the existence of an intermediary nanocrystalline phase during the amorphization process of crystalline form II, not observed for crystalline form I10,22. Additionally, medium-range similarity observed in PDF amorphous and crystalline phases seems to be indicative of residual memory that can drives recrystallization towards a specific polymorph10. Newman et al. reported the use of PDF to evaluate phase miscibility in indomethacin-PVP and trehalose–dextran mixtures21. In the first system, the PDF results indicated a complete miscibility with a good agreement with the number of glass transitions found; in the second system, the PDF indicated potential phase separation not detected by differential scanning calorimetry (DSC), suggesting that the system was a solid nanosuspension with nanometer sized amorphous domains lower than 30 nm.
The introduction of high-energy x-rays produced by synchrotron radiation has allowed the use of short wavelengths and access to higher Q-values (Qmáx ≥ 20 Å−1), a prerequisite for increased real space resolution and achieving more precise and accurate data11,23. Billinge and co-workers using a Qmáx = 20 Å−1 obtained a real-space resolution of 0.31 Å in the study of amorphous indomethacin and carbamazepine samples, being able to better identify differences in the molecular packing11. Benmore and colleagues used high-energy X-ray diffraction and neutron diffraction in combination with PDF to study vitrified carbamazepine, cinnarizine, miconazole, clotrimazole and probucol prepared by acoustic levitator14. The high resolution allowed the differentiation of significant intermolecular and intramolecular interactions in the range of 5–15 Å; for e.g. a shift in a peak was observed at 3.78 Å to 3.94 Å was identified due to changes in the orientation of the phenyl ring of clotrimazole caused by the vitrification process14.
In the present work we report the potential application of PDF analysis and high-energy X-ray diffraction as a tool to study acid-base interactions and drug-excipient interactions in amorphous systems. Acid-base interactions between drug-excipient play an important role in the physical stabilization of amorphous systems24,25,26. An important small molecule tyrosine kinase inhibitor used in breast cancer therapy, lapatinib (LP), has been chosen as model. It is a weak base with a secondary amine group (pKa = 7.26) and it was recently reported to form a strong intermolecular ionic interaction with acidic polymers25,26, promoting the formation of highly stable amorphous solid dispersions.
Results and Discussion
The process of spray drying consists of the rapid evaporation of the drug solution in a hot gas stream. Spray drying is very favorable to the generation of amorphous systems because of the small droplet size and containerless environment. Exploratory studies performed using Cu K-alpha radiation indicated that all initial lapatinib-polymer powder samples were amorphous, with exception of the pure drug dispersion which immediately produced partially crystalline lapatinib. This highlights the well-recognized importance of the polymers as carrier matrices to inhibit nucleation and crystallization27. However, the high noise level, low resolution and lack of information present in the patterns obtained using a conventional copper-anode X-ray laboratory source made PDF and structural studies on a laboratory powder diffractometer not realiable or possible23,28. In this context the use of high-energy X-rays is fundamental to access the structural information present only at high Q ranges23. Figure 1 shows the comparison of measured total x-ray structure factors for LP-HPMCP and LP-HPMC-E3 mixtures, respectively. Even though all drug-polymer mixtures are XRPD amorphous, high quality x-ray structure factors and PDF curves reveal significant differences among samples. The residual crystallinity of pure phase semi-crystalline lapatinib is clearly visualized from measured X-ray structure factor for Q < 4.0 Å−1, given the Bragg peaks present have similar positions to the pure crystalline drug pattern (Fig. 1e,f). The PDF of the pure spray dried drug is in good agreement with the crystalline drug in the low-r range, as would be expected, as this primarily reflects the local intramolecular structure of the molecule (Fig. 2a). Differences appear as the peaks are broadened at higher-r in the range containing more intermolecular correlations, due to the amorphicity caused by the spray drying process. An intense peak at r = 1.4 Å is a result of significant contributions of carbon-carbon interactions, the most abundant in LP structure (Table 2), although carbon-nitrogen, carbon-oxygen, carbon-fluorine and oxygen-sulphur interactions all contribute to the total x-ray scattering pattern18.
The 3:1 LP:HPMCP structure factor (Fig. 1d) is very similar to the semicristalline LP and indicates a significant residual crystallinity that was not detected by the conventional powder diffraction. The combination of high flux of synchrotron X-rays and a 2-D area detector has been reported to be able to detect levels as low as 0.2% (w/w) of crystallinity28. In case of 3:1 LP:HPMC-E3 the Bragg peaks are not present in structure factor. The slight deformation in the peak at approximately Q = 1.7 Å−1 (arrow Fig. 1j) and PDF (Fig. 2c) shows a loss in the intermolecular order at r > 5 Å when in comparison to 3:1 LP:HPMCP, suggesting that the sample is predominantly amorphous with a possible presence of very low amount of crystalline domains. After 100 days both samples recrystallized into lapatinib free base Form 129 (as well as the pure phase semi-crystalline sample), indicating that the 3:1 drug:polymer ratio samples contained enough crystalline-like interactions to eventually trigger recrystallization. Since x-ray structure factors of the 1:3 and 1:1 LP-polymer ratios do not present Bragg peaks (Fig. 1), it can be inferred that the use of amounts HPMC-E3 and HPMCP over 50% produces truly X-ray powder amorphous solid dispersions of lapatinib which can significantly influence in physical stability. This fact is in accordance with Song and co-workers who reported that a 40% drug load was suitable to obtain a stable solid dispersion of LP and HPMCP stable for 6 months at 40 °C/75%25. However, more structural insights are revealed when intermolecular interactions are evaluated separately.
The total measured x-ray structure factor and corresponding PDF contain intra- and inter-atom-atom correlations corresponding to drug-drug, drug-polymer and polymer-polymer interactions i.e.
Where the drug-drug and polymer-polymer interactions have both intramolecular and intermolecular components and by analogy S(Q) in reciprocal space, S(Q), can be replaced by D(r) in real space. A, B and C represent the appropriately normalized x-ray weighting factors based on the number of electrons and atomic concentrations associated with each.
In order to extract correlations from the overlapping peaks in the total PDF x-ray pattern, a series of analysis steps was performed with a view to isolating the lapatinib intermolecular drug interactions, , following the methodology previously outlined by Benmore15. Firstly, the intra- and intermolecular lapatinib functions, and respectively, were extracted from the total structure factor of pure lapatinib using the XISF method previously described by Mou et al.30. Here, we assumed a molecular conformation corresponding to lapatinib in form 1 since amorphous samples generally crystallize into this polymorph and this is the stable form29. The XISF method calculates the intramolecular x-ray scattering based on the atomic x, y, z positions of the single input molecule using a zeroth order Bessel function based on a trust-region algorithim. Secondly, both the intramolecular and intermolecular polymer-polymer interactions, were approximated by the pattern obtained from the pure polymer structure factor. Subtracting the x-ray weighted contributions of the polymer and intramolecular LP structure factors leaves the drug interactions alone, namely and . Similarly, in real space we can write this in terms of the differential PDF as,
The function therefore represents the probability of finding an atom on drug or polymer molecule surrounding an atom on a LP molecule at the origin as a function of radial distance, r. Examples of the isolation of the intermolecular drug term for lapatinib alone and with 1:1 mixtures of HPCM-E3 and HPCM-P polymers are shown in Figs 3 and 4, respectively.
The curve in Fig. 5 show well defined drug-drug interactions in pure amorphous lapatinib extending out to and beyond 20 Å. For the LP:HPMC-P system the drug rich 3:1 composition shows the similar correlations of slightly reduced magnitude indicating clusters of drug molecules on the scale of 1–2 nanometers (Fig. 5b). The 1:1 LP:HPMC-P curve shows just one broad peak around ~4.3 Å indicating orientational correlations only extend out to nearest neighbor molecules (Fig. 5c). The 1:3 curve (Fig. 5d) essentially shows a flat line implying that the LP molecules randomly dispersed in the polymer at this concentration, which supports the superior stability of those samples compared to the LP 3:1 HPMCP sample. In case of the LP:HPCM-E3 system the same analysis yields a different scenario. Here, the drug rich 3:1 composition shows a distinct first correlation at ~4.4 Å and a much weaker second peak at ~8.3 Å with nothing beyond that (Fig. 5f). The 1:1 LP:HPCM-E3 curve (Fig. 5g) and 1:3 (Fig. 5h) curves are similar to the 3:1 only showing the first and second peaks, but these are reduced in magnitude as might be expected due to the diminished drug concentration. Therefore it is suggested that at high concentrations in HPMC-E3 mixtures, lapatinib molecules do not cluster in the same way as observed in HPCM-P, but LP molecules do have distinct nearest neighbor interactions. Unfortunately it is not possible to distinguish between LP-LP and LP-polymer interactions using this method and a more detailed molecular simulation is required to deconvolute these specific molecular interactions. Nonetheless, we can use chemical arguments to help explain the observed differences.
Lapatinib is well known to form ionic interactions with HPMCP through an acid-base mechanism which can be clearly observed by the differences in color of the dispersions showed in Fig. 6. Whereas HPMC-E3 dispersions exhibits a pale yellow, HPMCP samples shows as bright yellow as an evidence of salt formation25. This interaction is not expected in HPMC-E3, since there are no carboxylic groups to react with amines. On the other hand, lapatinib-lapatinib interactions are mainly driven by the N14−H–O3 hydrogen bond29 which is related to the most basic nitrogen (pka 7.26), as can be inferred from the crystal structure (Fig. 7). Also, this is the principal site for ionic pair formation with the polymer. Intermolecular differential pair distribution functions show that the first intermolecular correlation arises from a valley at 3.10 Å and reaches a peak at around 4.60 Å. This fact is consistent with the distances and the number of nearest neighbor contacts related to C-C, C-N and C-O in drug-drug interactions in the crystal, as show in Figs 7, 8 and 9. Basically, when an acid-base interaction occurs the local structure is disrupted and drug molecules are dislocated by the acidic groups of the polymer, increasing the disorder of the system. Congruently, the total D(r) for LP:HPMC-E3 closely resembles that of the pure drug (Fig. 2b; peaks are indicated by arrows) due to drug-drug contacts and shows more peaks for LP: HPMC-E3 mixtures than for LP:HPMCP, indicating a more ordered system. Conversely, the total absence of those peaks in 1:3 LP:HPMCP preparations suggest that a complete reaction with the polymer has taken place on the N4 sites. In an analogy with the percolation rigidity theory31 the higher the numbers of connections and ordering, the higher the rigidity of the network will be and the more easily the system will reach the threshold for nucleation. If so, this would suggest that 1:1 LP:HPMCP and 1:3 LP:HPMC-E3 are less stable than 1:3 LP:HPMCP. In fact, this is correct. A stress test with direct exposure was carried out under 40 °C/75% RH revealing that both samples start crystallizing after 7 and 30 days, respectively, while 1:3 LP:HPMCP remains amorphous.
Synchrotron X-Ray diffraction and Pair Distribution Function Analysis were successfully applied to access the local structure of an ionic drug-polymer interactions in amorphous systems. The presence of correlations extending out to beyond 20 Å were found in the total differential distribution function D(r) of pure amorphous lapatinib and also in 3:1 drug-polymer preparations indicated the presence of crystalline domains. Plus, the strategy of extracting lapatinib intermolecular drug interactions was fundamental to visualize the presence of distinct nearest neighbor for HPMC-E3 rich samples and identify that lapatinib molecules do not cluster in the same way as observed in HPCM-P. Finally, the superior physical stability of 1:3 LP:HPMCP was clarified from a structural point of view by combining the chemical knowledge, the absence of significant contacts in at about 3.0–6.0 Å and the pattern of nearest neighbor contacts related to C-C, C-N and C-O in drug-drug interactions. This powerful approach opens new directions in the use of structural signatures or trends at the atomic and nanometer level that could predict macroscopic behavior of amorphous solid dispersions in pharmaceutical systems.
Methods and Materials
Methanol (MeOH) and dichloromethane (DCM) were procured from Macron Fine Chemicals (Center Valley, PA). Lapatinib free base was purchased from LC Laboratories (Woburn, MA). HPMC-E3 (hydroxypropyl methylcellulose, Methocel® E3) and HPMCP (HP-55) were obtained from Colorcon (West Point, PA, USA) and Shin-Etsu Chemical Company (Tokyo, Japan), respectively.
Preparation of spray dried samples
Lapatinib free base and polymers were solubilized under stirring in a 70/30 (v/v) mixture of DCM/MeOH at 2% (w/v) solids concentration. Different proportions (w/w) of drug-polymer were used as follow: 1:0 (pure drug), 3:1, 1:1, 1:3 and 0:1 (pure polymer). The solutions were spray dried using a Büchi-B190 spray dryer (Büchi, Switzerland) in the following conditions: inlet temperature of 75 °C; outlet temperature of 45 °C; aspirator flow 400 (arbitrary units), pump feed rate 5 mL/min. The powder was stored in sealed glass vial and keep under refrigeration until X-ray powder diffraction (XRPD) and high-energy X-ray analysis were performed. After that the samples were stored under ambient conditions for 100 days and reanalyzed by X-ray powder diffraction (XRPD).
Laboratory based X-ray powder diffraction
X-Ray powder diffraction patterns were measured on a Siemens/Bruker D5000 diffractometer, using Ni filtered Cu Kα radiation (λ = 1.5418 Å). The data were collected using an acceleration voltage of 40 kV and a tube current of 40 mA, step size of 0.02, step time 5 s in the angular range of 4° < 2θ < 40°
High-Energy X-Ray Diffraction
Drug-polymer samples were mounted in polymide tubing (Cole-Parmer®, Vernon Hills, IL, USA) with an inside and outside diameters of 0.0710 and 0.0750 inches, respectively. The high-energy X-ray experiments were conducted on the Beamline 6-ID-D at the Advanced Photon Source, Argonne National Laboratory using a monochromatic beam of energy 100.315 keV (0.12360(5) Å) and 0.5 mm × 0.5 mm in size to minimize absorption and multiple scattering in the sample and attain high Q-values. Scattered x-rays were detected using a Perkin Elmer XRD1621 amorphous silicon area detector. The sample-detector distance of 332.9 mm was calibrated using a NIST standard CeO2 powder sample. The 2D scattering patterns were integrated using Fit2D32 and the x-ray structure factors S(Q) extracted using PDFgetX233. The corresponding differential pair distribution functions D(r) were obtained by a Sine Fourier transformation using the HHS formalism as described by Keen34 and Susman et al.18, where,
Structure and Distance Calculations
Closest contacts distances were calculate by using CrystalExplorer 3.1 (S.K. Wolff, D.J. Grimwood, J.J. McKinnon, M.J. Turner, D. Jayatilaka, M.A. Spackman, University of Western Australia, 2012) based on crystallographic data of polymorph I29. Structure drawing and pKa calculation were performed using a Marvin 5.11.3 (Chemaxon, Budapest, Hungary) 2016 http://www.chemaxon.com.
How to cite this article: de Araujo, G. L. B. et al. Local Structure of Ion Pair Interaction in Lapatinib Amorphous Dispersions characterized by Synchrotron X-Ray diffraction and Pair Distribution Function Analysis. Sci. Rep. 7, 46367; doi: 10.1038/srep46367 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Lawrence, X. Y. Pharmaceutical quality by design: product and process development, understanding, and control. Pharm. Res. 25, 781–791 (2008).
Lee, S. L., Raw, A. S. & Yu, L. Significance of drug substance physicochemical properties in regulatory quality by design. Drugs Pharm. Sci. 178, 571 (2008).
Byrn, S. R., Zografi, G. & Chen, X. S. Accelerating proof of concept for small molecule drugs using solid‐state chemistry. J. Pharm. Sci. 99, 3665–3675 (2010).
Lawrence, X. Y. et al. Understanding pharmaceutical quality by design. AAPS J. 16, 771–783 (2014).
Zografi, G. & Newman, A. Interrelationships Between Structure and the Properties of Amorphous Solids of Pharmaceutical Interest. J. Pharm. Sci. doi: 10.1016/j.xphs.2016.05.001.
Thakral, S., Terban, M. W., Thakral, N. K. & Suryanarayanan, R. Recent advances in the characterization of amorphous pharmaceuticals by X-ray diffractometry. Adv. Drug Deliv. Rev. 100, 183–193 (2016).
Elliott, S. R. Medium-range structural order in covalent amorphous solids. Nature 354, 445–452 (1991).
Mackay, A. L. Generalised crystallography. Comput. Math. Appl. 12, 21–37 (1986).
Kohara, S. & Suzuya, K. Intermediate-range order in vitreous SiO2 and GeO2. J. Phys. Condens. Matter 17, S77 (2005).
Bates, S. et al. Analysis of amorphous and nanocrystalline solids from their X-ray diffraction patterns. Pharm. Res. 23, 2333–2349 (2006).
Billinge, S. J. et al. Characterisation of amorphous and nanocrystalline molecular materials by total scattering. Cryst Eng Comm 12, 1366–1368 (2010).
Whitehead, A. N. The principles of natural knowledge (1920).
Billinge, S. J. & Kanatzidis, M. G. Beyond crystallography: the study of disorder, nanocrystallinity and crystallographically challenged materials with pair distribution functions. Chem. Commun. 749–760 (2004).
Benmore, C. J. et al. Structural characterization and aging of glassy pharmaceuticals made using acoustic levitation. J. Pharm. Sci. 102, 1290–1300 (2013).
Benmore, C. J. In Discovering and Developing Molecules with Optimal Drug-Like Properties 263–283 (Springer, 2015).
Rademacher, N. et al. Study of the reaction products of SF 6 and C in the laser heated diamond anvil cell by pair distribution function analysis and micro-Raman spectroscopy. J. Solid State Chem. 225, 141–148 (2015).
Kohara, S. et al. Synchrotron X-ray Scattering Measurements of Disordered Materials. Z. Für Phys. Chem. 230, 339–368 (2016).
Susman, S., Volin, K. J., Montague, D. G. & Price, D. L. The structure of vitreous and liquid GeSe2: a neutron diffraction study. J. Non-Cryst. Solids 125, 168–180 (1990).
Bates, S. et al. Assessment of defects and amorphous structure produced in raffinose pentahydrate upon dehydration. J. Pharm. Sci. 96, 1418–1433 (2007).
Nollenberger, K. et al. Pair distribution function X‐ray analysis explains dissolution characteristics of felodipine melt extrusion products. J. Pharm. Sci. 98, 1476–1486 (2009).
Newman, A. et al. Characterization of amorphous API: Polymer mixtures using X‐ray powder diffraction. J. Pharm. Sci. 97, 4840–4856 (2008).
Sheth, A. R., Bates, S., Muller, F. X. & Grant, D. J. Local structure in amorphous phases of piroxicam from powder X-ray diffractometry. Cryst. Growth Des. 5, 571–578 (2005).
Dykhne, T., Taylor, R., Florence, A. & Billinge, S. J. Data requirements for the reliable use of atomic pair distribution functions in amorphous pharmaceutical fingerprinting. Pharm. Res. 28, 1041–1048 (2011).
Weuts, I. et al. Salt formation in solid dispersions consisting of polyacrylic acid as a carrier and three basic model compounds resulting in very high glass transition temperatures and constant dissolution properties upon storage. Eur. J. Pharm. Sci. 25, 387–393 (2005).
Song, Y. et al. Investigation of drug–excipient interactions in lapatinib amorphous solid dispersions using solid-state NMR spectroscopy. Mol. Pharm. 12, 857–866 (2015).
Song, Y. et al. Acid–Base Interactions of Polystyrene Sulfonic Acid in Amorphous Solid Dispersions Using a Combined UV/FTIR/XPS/ssNMR Study. Mol. Pharm. 13, 483–492 (2015).
Baghel, S., Cathcart, H. & O’Reilly, N. J. Polymeric Amorphous Solid Dispersions: A Review of Amorphization, Crystallization, Stabilization, Solid-State Characterization, and Aqueous Solubilization of Biopharmaceutical Classification System Class II Drugs. J. Pharm. Sci (2016).
Nunes, C., Mahendrasingam, A. & Suryanarayanan, R. Quantification of crystallinity in substantially amorphous materials by synchrotron X-ray powder diffractometry. Pharm. Res. 22, 1942–1953 (2005).
Araujo, G. L. B. de, Zeller, M., Smith, D., Nie, H. & Byrn, S. R. Unexpected single crystal growth induced by a wire and new crystalline structures of lapatinib. Cryst. Growth Des (2016).
Mou, Q., Benmore, C. J. & Yarger, J. L. X-ray Intermolecular Structure Factor (XISF): separation of intra-and intermolecular interactions from total X-ray scattering data. J. Appl. Crystallogr. 48, 950–952 (2015).
Thorpe, M. Continuous deformations in random networks. J. Non-Cryst. Solids 57, 355–370 (1983).
Hammersley, A. P., Svensson, S. O., Hanfland, M., Fitch, A. N. & Hausermann, D. Two-dimensional detector software: from real detector to idealised image or two-theta scan. Int. J. High Press. Res. 14, 235–248 (1996).
Qiu, X., Thompson, J. W. & Billinge, S. J. PDFgetX2: a GUI-driven program to obtain the pair distribution function from X-ray powder diffraction data. J. Appl. Crystallogr. 37, 678–678 (2004).
Keen, D. A. A comparison of various commonly used correlation functions for describing total scattering. J. Appl. Crystallogr. 34, 172–177 (2001).
Song, X. et al. Structural heterogeneity and unique distorted hydrogen bonding in primary ammonium nitrate ionic liquids studied by high-energy X-ray diffraction experiments and MD simulations. J. Phys. Chem. B 116, 2801–2813 (2012).
Meral, C., Benmore, C. J. & Monteiro, P. J. The study of disorder and nanocrystallinity in C–S–H, supplementary cementitious materials and geopolymers using pair distribution function analysis. Cem. Concr. Res. 41, 696–710 (2011).
Skinner, L. B., Chae, S. R., Benmore, C. J., Wenk, H. R. & Monteiro, P. J. M. Nanostructure of calcium silicate hydrates in cements. Phys. Rev. Lett. 104, 195502 (2010).
Du, P., Kokhan, O., Chapman, K. W., Chupas, P. J. & Tiede, D. M. Elucidating the domain structure of the cobalt oxide water splitting catalyst by X-ray pair distribution function analysis. J. Am. Chem. Soc. 134, 11096–11099 (2012).
Dr. Q. Mou is thanked for guidance on the use of his XISF program. The Advanced Photon Source is operated for the U.S. Department of Energy (DOE) Office of Science by Argonne National Laboratory and supported by the U.S. DOE under Contract No. DE-AC02-06CH11357. The authors acknowledge the São Paulo Research Foundation (FAPESP) for financial support [grant #2015/15456-5 and grant #2015/05685-7, SP, Brazil].
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
de Araujo, G., Benmore, C. & Byrn, S. Local Structure of Ion Pair Interaction in Lapatinib Amorphous Dispersions characterized by Synchrotron X-Ray diffraction and Pair Distribution Function Analysis. Sci Rep 7, 46367 (2017). https://doi.org/10.1038/srep46367
This article is cited by
X-ray fan beam coded aperture transmission and diffraction imaging for fast material analysis
Scientific Reports (2021)
Seed Layer-Assisted Chemical Bath Deposition of Cu2O Nanoparticles on ITO-Coated Glass Substrates with Tunable Morphology, Crystallinity, and Optical Properties
Journal of Inorganic and Organometallic Polymers and Materials (2021)
Amorphous solid dispersions of enzalutamide and novel polysaccharide derivatives: investigation of relationships between polymer structure and performance
Scientific Reports (2020)
Characterization of amorphous solid dispersions
Journal of Pharmaceutical Investigation (2018)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.