Light detection and quantification is fundamental to the functioning of a broad palette of technologies. While expensive avalanche photodiodes and superconducting bolometers are examples of detectors achieving single-photon sensitivity and time resolutions down to the picosecond range, thermoelectric-based photodetectors are much more affordable alternatives that can be used to measure substantially higher levels of light power (few kW/cm2). However, in thermoelectric detectors, achieving broadband or wavelength-selective performance with high sensitivity and good temporal resolution requires careful design of the absorbing element. Here, combining the high absorptivity and low heat capacity of a nanoengineered plasmonic thin-film absorber with the robustness and linear response of a thermoelectric sensor, we present a hybrid detector for visible and near-infrared light achieving response times of the order of 100 milliseconds, almost four times shorter than the same thermoelectric device covered with a conventional absorber. Furthermore, we show an almost two times higher light-to-electricity efficiency upon replacing the conventional absorber with a plasmonic absorber. With these improvements, which are direct results of the efficiency and ultra-small thickness of the plasmonic absorber, this hybrid detector constitutes an ideal component for various medium-intensity light sensing applications requiring spectrally tailored absorption coatings with either broadband or narrowband characteristics.
The efficient detection and measurement of light, specifically monochromatic (i.e. lasers) or broadband (i.e. white lamps) light in the visible and near-infrared (NIR) range, is a major undertaking in the engineering community and related industry. Indeed, the emission and absorption of photons are phenomena accompanying many physical processes such as broadband black body radiation1,2 from hot, macroscopic objects and wavelength-specific emission from fluorescent molecular3,4,5 or solid state single-photon sources6,7. The problem of measuring weak electromagnetic radiation across the entire visible and infrared range has been largely solved by devices such as avalanche photodiodes8 and superconducting bolometers9,10. In contrast, the measurement of medium/high-intensity light, with good temporal resolution and optional tunability of the spectral response, remains a challenge.
Thermoelectrics11,12,13,14,15,16,17,18 constitutes a class of important engineering materials that can be developed into sensors by exploiting the ability to transduce between thermal and electrical signals. By combining a thermoelectric TE element with a light absorption coating, light detection can be performed. For white light detection, a broadband absorber would be desirable. On the other hand, the use of spectrally selective coatings could enable close to monochromatic light detection, for specialty application or spectrometry. In order to develop an efficient and fast light sensor based on a thermoelectric device it is thus necessary to engineer a spectrally tailorable, high-absorption, low heat-capacity, and low radiative heat-loss material to efficiently mediate the photon-to-heat conversion step19.
Plasmonic nanostructures are ideal candidates for such an energy conversion task20,21,22,23,24,25,26. They enable effective light absorption, with absorber thicknesses in the sub-wavelength regime, 1–2 orders of magnitude thinner than conventional broadband absorber coatings27,28,29,30,31. Due to their small thickness, plasmonic absorbers have inherently small heat capacities, thus combining a high light-to-heat conversion efficiency23 with a fast response. In addition, their surface emissivity can be spectrally tuned to suppress infrared thermal radiation to minimize heat loss23. Lastly, light absorption by plasmonic structures can be designed to be either broadband or wavelength-selective32 by controlling the geometry of the nanostructures and combining different metals and dielectrics29,30,31. Together, these properties make plasmonic absorbers promising candidates for use as fast photon-to-phonon converters, which in combination with thermoelectric devices33,34 can lead to fast and efficient light detectors across a wide range of light intensities.
Indeed, in the field of infrared thermal light detection a variety of photonic and plasmonic absorbers have been realized either to overcome the poor intrinsic absorption of materials in this wavelength regime or to achieve high spectral selectivity35. Also, new materials such as graphene36 and carbon nanotubes37 have been exploited as tunable, ultra-low thermal capacity absorbers. On the other hand, much less attention has been devoted to the realization of thermoelectric-based visible/near-infrared light detectors, the reported response times being of the order of several seconds for light intensities of approximately 10−4 kW/cm2 (solar irradiation)22,25,38. Similarly, commercially-available TE-based light sensors measuring visible/NIR radiation with intensities of the order of few kW/cm2 still exhibit response times of the order of 1 second or greater39,40 due to the large heat capacity of the overall system.
Here, we explore the combination of a commercial thermoelectric detector with an ultra-thin, low heat-capacity plasmonic absorber for the rapid measurement of medium-intensity visible/NIR light. Our hybrid device exhibits linear response to light intensites up to approximately 1 kW/cm2 and response times in the range of few tens of milliseconds. In particular, we show that, while coating the device with a conventional absorber substantially increases the response time, the use of a plasmonic absorber leaves the response time of the initial thermoelectric system practically unchanged (only marginally increased), while at the same time markedly improving the radiation power-to-voltage sensitivity. Since the limiting factor in the speed of the thermoelectric-plasmonic light detector is the macroscopic thermoelectric component, further miniaturization of the basic thermoelectric voltage-generating unit would allow the realization of even shorter response times. Additionally, we show how the optical properties of plasmonic structures can be tuned to realize light absorbers with progressively broader spectral response by adjusting the geometrical parameters and material composition of the plasmonic coating.
The concept of the proposed hybrid plasmonic-thermoelectric light detection device is represented in Fig. 1, together with its actual implementation (Fig. 1a). On top of a commercial bismuth telluride thermoelectric device, gSKIN XP 26 9 C (provided by greenTEG AG, Fig. 1b), we fabricate an ultrathin plasmonic structure with tunable absorption properties and low thermal capacity (effectively a plasmonic absorber coating).
This absorber coating consists of a metal-insulator-metal (MIM) multilayer structure23,29,30,31. Silver and gold were used as the metals of choice for the fabrication of the absorbers. The thickness of the top, nanostructured layer and the bottom, uniform back reflector layer are both 100 nm. We use nanosphere lithography to pattern the top metallic layer into a hexagonal array of triangles or holes. The periodicity of the hexagonal crystal is 300 nm (holes center-to-center distance). The two metal layers are separated by a dielectric spacer consisting of either SiO2 or Al2O3. The entire multilayer structure is fabricated on top of a polished aluminum surface coupled to a commercial thermoelectric heat flux sensor (gSKIN XP 26 9 C). Details about the fabrication process are provided in Methods and Supplementary Information (SI). Figure 1b and c show two photographs of a thermoelectric sensor before and after coating with a broadband plasmonic absorber layer.
We demonstrate the tunability of the absorption spectrum of the plasmonic coating by fabricating structures with slight changes in the geometrical parameters as well as the spacer and metallic materials, while leaving unchanged the overall fabrication procedure. Three thermoelectric devices with the same metal/dielectric spacer/metal structure were fabricated. By changing the metallic material (either Au or Ag), dielectric spacer material (either SiO2 or Al2O3) and thickness and the degree of connectedness of the hexagonal patterns (Fig. 2), we achieved different absorption characteristics. The absorption measurements were performed using a home-built inverted microscope equipped with an air objective (numerical aperture, NA, 0.75) for exciting the sample and collecting the reflected light. Normal illumination was achieved by focusing the excitation light onto the center of the back-focal plane of the objective41. The reflected light was analyzed with a spectrometer (Princeton Instrument)29. The absorption spectrum, A, was calculated as A = (I − R)/I, where I and R are the incident illumination and reflected spectra, respectively.
The first absorber (sensor #1) is fabricated using Ag as metal, 34 nm of SiO2 as spacer layer and a hexagonal array of holes (Fig. 2a,b). The use of Ag and SiO2 allows the excitation of a plasmonic mode at short wavelengths. Indeed, this structure presents an absorption peak at 490 nm and its absorption drops below 75% for wavelengths longer than 610 nm and below 50% for wavelengths longer than 730 nm. The second absorber (sensor #2) is fabricated using Ag as metal, 34 nm of Al2O3 as spacer and a similar top pattern and exhibits a broader spectrum (red-shift of the plasmonic peak to 650 nm) with absorption dropping below 75% percent for wavelengths longer than 790 nm (Fig. 2c,d), due to the higher refractive index of Al2O3 compared to SiO2. Figure 2b and d show SEM images of these two triangle arrays have an average bottleneck width of 13–19 nm. The result of numerical simulations performed for these two sensors are discussed in section S3 of SI. The third absorber (sensor #3) is fabricated using Au as metal, 60 nm of SiO2 and an hexagonal array of disconnected triangles as front pattern35. It presents an ultra-broadband absorption spectrum with more than 75% absorption in the entire visible and near-infrared (NIR) range (from 400 nm up to 850 nm) (Fig. 2e,f).
A thermoelectric light sensor is characterized by two main figures of merit: sensitivity (voltage output per Watt input) and response time (characteristic time, τ). We thus tested our devices with respect to these parameters.
For the sensitivity measurements, we irradiated the sensor by modulating a green laser (CrystaLaser, λ = 532 nm) with a square wave with a period of 16 s, long enough to ensure that the voltage output reaches the steady state values within each half period (both on and off states). The laser power was varied from 32 mW to 110 mW and the irradiated area was approximately equal to ≈100 μm in diameter. The laser modulation was controlled using a shutter and the laser power was adjusted using neutral density filters. The voltage output from the sensor in response to the laser irradiation was recorded using a data logger (OM-DAQPRO-5300, as shown in Fig. 1a). More details can be found in the Methods and SI.
Figure 3 shows representative voltage (mV)- radiation power (mW) characteristics of the light sensor without/with various plasmonic-mediated configurations. All devices exhibit linear responses as a function of the laser power. In the absence of any plasmonic coating, the sensitivity of the sensor with a polished aluminum surface is as low as 13.1 mV/W. In contrast, all plasmonic devices present significantly enhanced sensitivities. In particular, the sensors #1 and #2 (with Al2O3 and SiO2 spacers) present sensitivities of 82.8 mV/W and 94.8 mV/W, respectively, corresponding to a 6.3 and 7.2 fold enhancement. The broadband plasmonic detector presents the largest sensitivity of 116.1 mV/W, nearly 9 times larger than the uncoated detector. Different thermal resistivities of the individual plasmonic absorbers are most likely playing a secondary effect responsible for the variability in sensitivities achieved with different plasmonic coatings. Further optimization of the nanoscale heat generation and concentration with plasmonic nanostructures could thus open up additional possibilities for sensitivity enhancement and can be an interesting topic for future studies42. The DC noise level of the performed measurements is about 0.023 mV. This gives, according to Fig. 3, a noise-equivalent power of about 0.2 mW for the broadband sensor. For sensors without absorption layer, the noise is about 1.5 mW.
The commercial absorber that the company greenTEG AG uses for the sensors, is an inorganic ceramic coating applied with a spray process directly onto the sensor surface. Compared to the sensor with this commercial ceramic coating (gRAY B05-SC, olive green dashed line in Fig. 3, with sensitivity of 61.6 mV/W as specified by the company), sensor #3 with the broadband plasmonic absorber coatings exhibit a 2 fold sensitivity enhancement.
We then characterized the transient response of the four devices by recording the output from the sensors under excitation with light pulses. We used a data acquisition rate of 2000 Hz, sufficient for capturing transient behaviors in the tens to hundreds of msec range. Figure 4a shows a typical time sequence, which we recorded at a given laser power (66.8 mW). From the time trace we can extract the two parameters of interests: the steady state voltage value, Vsteady, which we discussed in Fig. 3, and the transient response time, τ, of the device, defined as the time during which the output voltage reaches (1 − 1/e) times of its steady state value, Vsteady. For each case, we acquired at least 3–4 cycles of illumination in order to improve the accuracy of the time-constant (response time) determination.
Figure 4b shows that all the fabricated hybrid plasmonic-thermoelectric sensors display less than 10% increase in response time compared to the original sensor with polished aluminum surface (τ = 92±3 ms). Such marginally increased response time was verified at different laser illumination powers and is attributed to the small volume of the ultra-thin absorber coating and, therefore, its practically negligible heat capacity (). In contrast, the same measurement performed for a sensor (gRAY B05-SC) with a commercial coating (20 μm) currently used by greenTEG AG for its detectors showed up to four times increase in response time (olive green dashed line in Fig. 4b) compared to the uncoated sensor. These results show that plasmonic structures are promising absorbers even for thinner and more optimized thermoelectric transducers with response times down to few milliseconds.
In conclusion, we demonstrated a visible-NIR, medium intensity, light flux sensor concept based on the combination of a thermoelectric device with an ultra-thin plasmonic absorber coating. The sensor coated with the plasmonic absorber achieved a sensitivity of 116 mV/W, nearly 9 times and 2 times higher than the sensitivity of the uncoated sensor and the sensor with commercial coating, respectively. Furthermore, while the commercial absorber coating substantially increases the response time of the sensor, application of the plasmonic sensor increased the response time by less than 10%. The absorption spectrum of the plasmonic coating and therefore, of the sensor, can be largely modulated by tuning the geometrical parameters of the absorber and the spacer material. Our work opens up a promising pathway towards achieving low-cost and fast light flux sensors for narrow-band or broadband light detection across the entire visible and near-infrared (NIR) wavelength range.
The aluminum surfaces of the thermoelectric device (greenTEG, gSKIN XP 26 9 C) were lapped and then polished to reduce their surface roughness (see SI for details). A 100 nm-thick silver or gold back-reflector and a dielectric (SiO2 or Al2O3) layer were deposited successively on the polished aluminum surface of the sensors using electron-beam evaporation. The thermal deposition of the metal and dielectric film was conducted in a vacuum evaporator (Univex 500) at a pressure of 1 × 10−7 Pa with deposition rate of 0.1 nm/s. Successively, front hexagonal silver or gold pattern was fabricated using nano-sphere lithography and reactive ion etching. First, a closely packed monolayer of polystyrene beads (Duke Scientific, diameter 300 nm) is created using dip-coating: the sample is quickly immersed into a diluted bead solution (1 wt%, 10−3 M SDS) and then withdrawn with controlled velocity (≈2.5 μm s−1). The humidity is kept constant at ≈50%. Then, reactive ion etching is used to reduce the bead size (100 sccm Ar, 10 sccm O2, 50 W, 100 μbar). The bead size is controlled by adjusting the etching time. The final pattern is created by evaporating 100 nm of silver or gold through the bead mask and by successively removing the beads by low power ultrasonication (see SI for further details of the fabrication process).
The absorption measurements were performed using a home-built inverted microscope equipped with an air objective (Zeiss 63x, numerical aperture NA 0.75) for exciting the sample and collecting the reflected light. Normal illumination was achieved by focusing the excitation light onto the center of the back-focal plane of the objective. The reflected light was analyzed with a spectrometer (Princeton Instrument). The absorption spectrum, A, was calculated as A = (I − R)/I, where I and R are the incident illumination and reflected spectra, respectively.
A green laser light (CrystaLaser, λ = 532 nm) was used for excitation. The output power was controlled by an intensity controller. The laser modulation was controlled using a shutter and the laser power was adjusted using neutral density filters (Thorlabs). The voltage output from the sensor in response to the laser irradiation was recorded using a data logger (OM-DAQPRO-5300). We used a data acquisition rate of 2000 Hz, sufficient for capturing transient behaviors in the tens to hundreds of milisecond range. From the voltage-time trace we extract the steady-state voltage value, Vsteady, and the transient response time, τ, of the device, defined as the time during which the output voltage reaches (1 − 1/e) times of its steady state value, Vsteady. For each case, we acquired at least 3–4 cycles of illumination in order to improve the accuracy of the time-constant (response time) determination. The DC detector noise was measured as the standard deviation of a time series of measured sensor output voltages in the absence of radiation excitation. For our detector, Johnson noise was found to dominate as the dynamic resistance of the system R_D = S^2*T/G = 0.96 Ohm, where S = (20 mV/K) is the Seebeck coefficient, T = 300 K is the operating temperature and G = 0.125 W/K is the thermal conductance, is much lower than the resistance between the leads of the device R > 55 Ohm. All measurements were performed in normal ambient conditions (air at atmospheric pressure and room temperature).
How to cite this article: Pan, Y. et al. A Rapid Response Thin-Film Plasmonic-Thermoelectric Light Detector. Sci. Rep. 6, 37564; doi: 10.1038/srep37564 (2016).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
R. C. Dunbar & T. B. McMahon . Activation of unimolecular reactions by ambient blackbody radiation. Science 279, 194 –197 (1998).
A. M. Hofmeiste . Mantle values of thermal conductivity and geotherm from phonon lifetimes. Science 283, 1699–1706 (1999).
H. Peter Lu, L. Xun & X. Sunney Xie . Single-Molecule enzymatic dynamics. Science, 282, 1877–1882 (1998).
Y. Taniguchi et al. Quantifying E. coli Proteome and Transcriptome with Single-Molecule Sensitivity in Single Cells. Science 329, 533–538 (2010).
C. Zong, S. Lu, A. R. Chapman & X. S. Xie . Genome-wide detection of single-nucleotide and copy-number variations of a single human cell. Science 338, 1622–1626 (2012).
T. M. Babinec et al. A diamond nanowire single-photon source. Nat. Nanotechnol. 5, 195–199 (2010).
T. Gaebel et al. Room-temperature coherent coupling of single spins in diamond. Nat. Phys. 2, 408–413 (2006).
N. Savage . Single photon counting. Nat. Photonics 3, 738–739 (2009).
C. H. Ahn et al. Electrostatic modulation of superconductivity in ultrathin GdBa2Cu3O7-x films. Science 14, 1152–1155 (1999).
J. Yan et al. Dual-gated bilayer graphene hot-electron bolometer. Nat. Nanotechnol. 7, 472–478 (2012).
R. Venkatasubramanian, E. Siivola, T. Colpitts & B. O’Quinn . Thin-film thermoelectric devices with high room-temperature figures of merit. Nature 413, 597–602 (2001).
K. F. Hsu et al. Cubic AgPbmSbTe2+m: bulk thermoelectric materials with high figure of merit. Science, 303, 818–821 (2004).
T. C. Harman, P. J. Taylor, M. P. Walsh & B. E. LaForge . Quantum dot superlattice thermoelectric materials and devices. Science 297, 2229–2232 (2002).
M. S. Dresselhaus et al. New directions for low-dimensional thermoelectric materials. Adv. Mater. 19, 1043–1053 (2007).
A. I. Boukai et al. Silicon nanowires as efficient thermoelectric materials. Nature 451, 168–171 (2008).
J. P. Heremans et al. Enhancement of thermoelectric efficiency in PbTe by distortion of the electronic density of states. Science 321, 554–557 (2008).
B. Poudel et al. High-thermoelectric performance of nanostructured bismuth antimony telluride bulk alloys. Science 320, 634–638 (2008).
A. I. Hochbaum et al. Enhanced thermoelectric performance of rough silicon nanowires. Nature 451, 163–167 (2008).
U. Dillner, E. Kessler & H. G. Meyer . Figures of merit of thermoelectric and bolometric thermal radiation sensors. J. Sens. Sens. Syst. 2, 85–94 (2013).
S. Linic, P. Christopher & D. B. Ingram . Plasmonic-metal nanostructures for efficient conversion of solar to chemical energy. Nat. Mater. 10, 911–921 (2011).
D. Kraemer et al. High-performance flat-panel solar thermoelectric generators with high thermal concentratin. Nat. Mater. 10, 532–538 (2011).
Y. Xiong et al. Solar energy conversion with tunable plasmonic nanostructures for thermoelectric devices. Nanoscale 4, 4416–4420 (2012).
G. Tagliabue, H. Eghlidi & D. Poulikakos . Rapid-response low infrared emission broadband ultrathin plasmonic light absorber. Sci. Rep. 4, 7181 (2014).
K. Aydin, V. E. Ferry, R. M. Briggs & H. A. Atwater . Broadband polarization-independent resonant light absorption using ultrathin plasmonic super absorbers. Nat. Comm. 2, 517–528 (2011).
R. Komatsu et al. Plasmonic photo-thermoelectric energy converter with black-Si absorber. Sol. Energ. Mat. Sol. Cells. l, 72–77 (2015).
Q. Lin et al. A novel design of plasmon-induced absorption sensor. Appl. Phys. Express. 9, 062002-1–4 (2016).
H. Jiaming, Z. Lei & Q. Min . Nearly total absorption of light and heat generation by plasmonic metamaterials. Phys. Rev. B 83, 165107 (2011).
A. Aubry et al. Plasmonic light-harvesting devices over the whole visible spectrum. Nano Lett. 10, 2574–2579 (2010).
G. Tagliabue, H. Eghlidi & D. Poulikakos . Facile multifunctional plasmonic sunlight harvesting with tapered triangle nanopatterning of thin films. Nanoscale 5, 9957–9962 (2013).
G. Tagliabue, C. Höller, H. Eghlidi & D. Poulikakos . Proximal gap-plasmon nanoresonators in the limit of vanishing inter-cavity seperation. Nanoscale 6, 10274–10280 (2014).
G. Tagliabue, D. Poulikakos & H. Eghlidi . Three-dimensional concentration of light in deeply sub-wavelength, laterally tapered gap-plasmon nanocavities. Appl. Phys. Lett. 108, 221108 (2016).
Y. Nishijima, H. Nigorinuma, L. Rosa & S. Juodkazis . Selective enhancement of infrared absorption with metal hole arrays. Opt. Mater. Express 2, 1367–1377 (2012).
R. Yang, A. Narayanaswamy & G. Chen . Surface-plasmon coupled nonequilibrium thermoelectric refrigerators and power generators. J. Comput. Theor. Nanosci. 2, 75–87 (2005).
S. V. Boriskina, H. Ghasemi & G. Chen . Plasmonic materials for energy: from physics to applications. Mater. today 16, 375–386 (2013).
J. J. Talghader, A. S. Gawarikar & R. P. Shea . Spectral selectivity in infrared thermal detection. Light: Science & Applications, 1, 1–11 (2012).
Y. Zhang et al. Independently tunable dual-band perfect absorber based on graphene at mid-infrared frequencies. Sci. Rep. 5, 18463 (2015).
Z. P. Yang, L. Ci, J. A. Bur, S. Y. Lin & P. M. Ajayan . Experimental observation of an extremely dark material made by a low-density nanotube array. Nano Lett. 8, 446–451 (2008).
A. Kosuga et al. A high performance photothermal film with spherical shell-type metallic nanocomposites for solar thermoelectric conversion. Nanoscale 7, 7580–7584 (2015).
Thorlabs Catalog - Thermal power sensors (c-series). http://www.thorlabs.de/newgrouppage9.cfm?objectgroup_id=3333 (accessed on 28/10/2016).
Ophir Photonics Catalog - Laser Power Sensors. http://www.ophiropt.com/laser–measurement/laser-power-energy-meters/products/Laser-Thermal-Power-Sensors (accessed on 28/10/2016).
G. Tagliabue . On harvesting, confinement and conversion of the energy of light with facile plasmonic nanostructures. Diss., Eidgenössische Technische Hochschule Zürich Nr. 22053 (2014).
Z. J. Coppens, W. Li, D. G. Walker & J. G. Valentine . Probing and controlling photothermal heat generation in plasmonic nanostructures. Nano Lett. 13, 1023–1028 (2013).
Y. Pan acknowledges the State Scholarship Fund of the China Scholarship Council for financial support. The authors thank Dr. Kelly Mauser and Prof. Harry H. Atwater from Laboratories of Applied Physics in California Institute of Technology for the valuable discussion. This work was partially supported by a grant from the Aurel-Stodola-Fonds (ETH-25 11-2) and by a grant from Alstom (SP-ESC-A 02-14). G. Tagliabue acknowledges support from the Swiss National Science Foundation with the Early Postdoc Mobility Fellowship n. P2EZP2_159101.
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Pan, Y., Tagliabue, G., Eghlidi, H. et al. A Rapid Response Thin-Film Plasmonic-Thermoelectric Light Detector. Sci Rep 6, 37564 (2016). https://doi.org/10.1038/srep37564
This article is cited by
Enhanced electrical outputs of thin-film solar thermoelectric generator with optimized metal/dielectric multilayered solar selective absorber
Applied Physics A (2022)
Ultrasensitive electrolyte-assisted temperature sensor
npj Flexible Electronics (2020)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.