Molybdenum disulfide (MoS2) has recently received much attention for nanoscale electronic and photonic applications. To explore the intrinsic properties and enhance the performance of MoS2-based field-effect transistors, thorough understanding of extrinsic effects such as environmental gas and contact resistance of the electrodes is required. Here, we report the effects of environmental gases on the transport properties of back-gated multilayered MoS2 field-effect transistors. Comparisons between different gases (oxygen, nitrogen and air and nitrogen with varying relative humidities) revealed that water molecules acting as charge-trapping centers are the main cause of hysteresis in the transfer characteristics. While the hysteresis persisted even after pumping out the environmental gas for longer than 10 h at room temperature, it disappeared when the device was cooled to 240 K, suggesting a considerable increase in the time constant of the charge trapping/detrapping at these modestly low temperatures. The suppression of the hysteresis or instability in the easily attainable temperature range without surface passivation is highly advantageous for the device application of this system. The humidity dependence of the threshold voltages in the transfer curves indicates that the water molecules dominantly act as hole-trapping centers. A strong dependence of the on-state current on oxygen pressure was also observed.
Molybdenum disulfide (MoS2) has attracted much attention as a novel two-dimensional material for electronic and optical devices1,2,3,4. Unlike graphene5, MoS2 has a sizable energy gap, 1.2 eV for bulk and 1.8 eV for a monolayer6,7. This energy gap is highly advantageous for semiconducting device applications, including field-effect transistors (FETs)8,9,10,11,12,13,14,15,16,17,18. Owing to their ultrathin layered structure (0.6 nm for a monolayer), FETs with a channel made of a monolayer or few layers of MoS2 are immune to short-channel effects19. This opens the possibility of achieving a significantly high number density of FETs fabricated on a substrate, as compared to conventional Si metal-oxide-semiconductor field-effect transistors19.
One of the limitations of MoS2-based FETs is their high sensitivity to extrinsic effects such as environmental gas9,15,17,18 and contact resistance of the electrodes20,21,22,23. The environmental gas leads to instability of transport properties in the FETs. Protective passivation or encapsulation of the devices against the environment has been intensively studied9,24,25. On the other hand, intrinsic mobility cannot be estimated simply from the transfer characteristics acquired with two-point measurement because the contact resistance related to the Schottky barrier at the contact is typically not negligible. To explore the intrinsic properties and enhance the performance of MoS2-based FETs, thorough understanding of such extrinsic effects is required. In the present paper, we focus on the environmental gas effect on the transport properties of the MoS2-based FET. It is known that the channel surface adsorbs gases such as water vapor and oxygen, causing fluctuations in its transport properties9,15,17,18. The interaction between these molecules and the MoS2 surface is characterized as physisorption26,27. In particular, the hysteresis in the transfer characteristics is due to the charge trapping associated with the atoms and molecules adsorbed on the surface for MoS2 as well as for carbon nanotubes28,29, graphene30,31 and pentacene32. However, the mechanisms behind the influence of various gases have not been fully understood. In this study, we quantitatively examine the influence of various gases on the hysteresis in the transfer characteristics, such as oxygen, nitrogen and air with varying humidities. Our results indicate that water is the main cause of the hysteresis. We observed a remarkable temperature dependence in the hysteresis, that is, the hysteresis disappeared at a modestly low temperature of ~240 K, suggesting a convenient way of suppressing the hysteresis. The dominance of hole trapping by water molecules over electron trapping is also observed.
Figure 1a shows an optical image of the back-gated FET device with a 6-nm-thick MoS2 flake that was used to produce all the data except the results shown in Fig. 2a. The channel length and width of the sample are L = 4.3 μm and W = 4.1 μm, respectively. The devices with the Ti/Au contacts exhibited Ohmic Ids–Vds behavior at room temperature, where Ids and Vds are the drain–source current and drain–source voltage, respectively (see Supplementary Fig. S1). Figure 1b shows the transfer characteristics (Ids–Vg curves, where Vg is the gate voltage) in vacuum and air at varying pressures. The increase in the hysteresis with increasing pressure indicates that the hysteresis is attributed to the adsorbed molecules in air that act as charge-trapping centers. The transfer curves in the different sweep directions are separately affected by the trapped charges. As the air pressure increases, the threshold voltages shift away in both the positive and negative directions, thereby increasing the hysteresis. This indicates that hole (electron) trapping is responsible for the negative (positive) shift of the transfer curve in the forward (backward) sweep and that the time constant for charge trapping/detrapping is comparable to the measurement time of the order of 1 min. Similar results for the conductance hysteresis were obtained using fabricated FET devices with multilayer MoS2 channels. The transfer characteristics in dry nitrogen with varying values of pressure are compared in sFig. S2, which indicates that the main cause of the increase in the hysteresis shown in Fig. 1b is not increased nitrogen pressure.
In Fig. 1c, the transfer characteristics in different environmental gases are compared, such as dry nitrogen, dry oxygen, air (relative humidity RH = 18%) and humid nitrogen (RH = 80%). The total pressure of the gases was approximately 740 Torr for the displayed data. Table 1 summarizes the magnitudes of the hysteresis in terms of the difference in the threshold voltages ΔVth = Vth2 − Vth1 in different sweep directions, where Vth1 and Vth2 are defined as the voltages at which the drain–source current is Ids = 1 nA. The molecules, in decreasing order of contribution to the hysteresis, are water, oxygen and nitrogen. It is remarkable that the influence of water (RH = 80%) on the hysteresis is more than thrice that of dry oxygen.
We note that the environmental effect on the hysteresis was reversible, that is, the hysteresis decreased again when the environmental gas was pumped out for a few minutes without annealing the devices. The small residual hysteresis in the data taken in vacuum shown in Fig. 1b is attributed to the small number of adsorbed gas molecules that remain adsorbed even in vacuum. Figure 1d shows the transfer characteristics after the humid nitrogen was evacuated using a turbo-molecular pump for various periods of time. A gradual decrease in the hysteresis is observed for a period longer than 10 h, indicating the slow desorption of water molecules in vacuum at room temperature. This is ascribed to the strong hydrogen bonds between the water molecules and sulfur surface of MoS2 that has a considerable polarity and hydrophilicity9, which is in clear contrast to the hydrophobicity of graphene and nanotubes28. We note that the calculated adsorption energies of water and oxygen molecules on the monolayer MoS2 are considerably higher than the thermal energy at room temperature26,27. The residual hysteresis in vacuum may partly be of intrinsic origin, as proposed in ref. 33.
We observe a remarkable temperature dependence of the hysteresis, as shown in Fig. 2a, using a device different from the one used for acquiring the other data. The devices had similar thicknesses but different channel lengths and widths, as specified in the figure caption. Cooling the sample below 273 K drastically reduced the hysteresis. At 240 K, the hysteresis ascribed to the charge trapping was completely suppressed. Similar temperature dependence was observed for the multiple devices we fabricated. The disappearance of the hysteresis at low temperatures is attributed to the prolonged time constant for charge trapping/detrapping. The analysis of the temperature dependence of this time constant will be a subject of future study. The suppression of the hysteresis or instability in the easily attainable temperature range without surface passivation is highly advantageous for the device application of this system.
The dependence of the magnitude of the hysteresis ΔVth on the relative humidity is shown in Fig. 2b. A positive dependence is clearly observed up to RH = 80%. Because the measuring range of the humidity sensor used in the present study is from 20% to 85%, the saturating behavior with decreasing humidity is ascribed to the limitation of the humidity sensor. Considering ΔVth = 2.4 V in vacuum (Table 1), ΔVth should be approximately proportional to the relative humidity. Humidity sensors could be developed using this humidity dependence of the transfer characteristics2,9,34,35. The linearity between ΔVth and humidity indicates the physisorption of water molecules, because the sheet density of physisorbed molecules is proportional to the gas pressure26.
In Fig. 2b, the threshold voltages Vth1 and Vth2 are also shown. With an increase in the humidity, Vth2 is nearly constant; however, Vth1 decreases significantly. Therefore, the increasing hysteresis is caused by the variation in Vth1. Because the decrease in Vth1 is caused by hole trapping in the forward sweep, this result indicates that the water molecules dominantly act as hole-trapping centers. This is also implied from the transfer curves shown in Fig. 1c. A comparison between the transfer curves in air (RH = 18%) and humid nitrogen (RH = 80%) reveals that the curve swept in the positive direction (off-to-on sweep) considerably shifts to the negative Vg direction with an increase in the RH, while the curves swept in the negative direction (on-to-off sweep) nearly coincide with each other. This observation is consistent with the results shown in Fig. 2b. We note that similar shifts in the threshold voltages, suggesting the dominance of hole trapping in the environmental effect on the MoS2-based FET, were indicated in several papers9,15,18, although this asymmetry between the electron and hole trappings was not mentioned. While it has been indicated that water and oxygen molecules act as charge acceptors in equilibrium26,27, the slow dynamics of the trapped charges on these molecules under varying gate voltage, which should explain the mechanism of the hysteresis, is still to be investigated.
Upon comparing the influences of various gases on the transport properties, we observed that the on-state current (Ids at Vds = 0.1 V and Vg = 40 V) decreased by approximately 40% with increasing oxygen pressure, as shown in Fig. 3. We note that an even stronger dependence of the on-state current on oxygen pressure was reported for a bi-layer MoS2 FET18. In contrast, the dependence of the on-state current on the RH was small (<10%) and not monotonic from RH = 10% to 80%, as shown in Supplementary Fig. S3. This small RH dependence of the on-state current may be due to the changes in temperature during measurement. The temperature dependence of conductivity is explained in terms of the Schottky barriers at the contacts and phonon scattering17,18. The small increase (14%) in the on-state current with increasing nitrogen pressure, as shown in Supplementary Fig. S4, is also assumed to be due to temperature variations. These results indicate that the adsorbed oxygen molecules on the channel surface are effective charge scatterers, while the charge scattering due to the adsorbed water molecules is not pronounced, irrespective of the fact that the charges trapped by the adsorbed water molecules are the main cause of the hysteresis in the transfer characteristics. The suppression of the scattering by the charges trapped by the adsorbed water molecules may be explained in terms of the short-range charge screening induced by the dielectric properties of the multilayer of water on the MoS2 surfaces, which could exist in ambient air because of hydrogen bonding among the water molecules28. Another possible explanation for the O2-pressure dependence of the on-state current is the reduction in the sheet carrier density due to the charge transfer from MoS2 to the oxygen molecules, which was the mechanism behind the increase in photoluminescence with increasing O2 pressure for the monolayer MoS226. We assume that the reduction in the carrier density due to the charge transfer to the oxygen molecules is unlikely to be the main cause of the decreasing on-state current. This is because the MoS2 flakes of our devices exist in multilayers (approximately 10 layers) and the calculated values of the charge transfer to water and oxygen are not significantly different from each other (within a factor of four)26,27, while the humidity dependence of the on-state current was not observed.
We investigated the influence of various environmental gases, such as nitrogen, oxygen and water, on the hysteresis of the transfer characteristics of the multilayer MoS2-based FETs. Water molecules are most influential on the magnitude of the hysteresis, while oxygen is less so. The dependencies on the pressure and relative humidity of the environmental gases of the hysteresis were clearly observed. While the hysteresis persisted after evacuating the device at room temperature for longer than 10 h, it was completely suppressed by cooling down to ~240 K. This suppression is attributed to the temperature dependence of the time constant for charge trapping/detrapping. The suppression of the hysteresis by modest cooling without protective passivation or encapsulation is very promising for device applications by reducing the instability in MoS2 devices caused by the environmental effects. The variation of the transfer curves at different levels of humidity indicates that the water molecules dominantly act as hole-trapping centers. The decrease in the on-state current with increasing oxygen pressure suggests that the adsorbed oxygen molecules become effective scattering centers for the charge carriers. These results provide a solid basis for understanding the environmental effects in the MoS2-based FETs. The applicability of this system to sensors for humidity and oxygen is also suggested.
Thin MoS2 flakes were exfoliated from a bulk crystal (SPI Supplies) using adhesive tape36. The flakes on the tape were then transferred onto a gel sheet (Gel-Pak, PF-20-X4)37. Subsequently, the flakes on the gel sheet were deposited on a Si substrate with a 270-nm-thick SiO2 layer. The intermediate gel sheet step was very effective in obtaining clean flakes with very little glue on the adhesive tape37. After locating a suitable MoS2 flake using an optical microscope, the source and drain electrodes made of Ti(12 nm)/Au(75 nm) were fabricated using photolithography and electron-beam deposition. The highly n-doped Si substrate was used as a back gate. An atomic force microscope was used to measure the thicknesses of the MoS2 flakes and the transfer and output characteristics of the devices were measured using a source measure unit Keithley 236 and a gate-voltage source with a homemade voltage amplifier within a ±100 V range. To examine the environmental effects, the devices were housed in a vacuum chamber with a base pressure of 10−4 Pa. The transport properties in different gases with various pressures were then measured. To study the influence of water molecules, water was bubbled with dry nitrogen gas. Relative humidity (RH) was monitored using a humidity sensor (TDK CHS-GSS). All the measurements were performed at room temperature except the data shown in Fig. 2a. The low-temperature data shown in Fig. 2a were taken using a cryostat with a cryogen-free refrigerator. The sample cell of the cryostat was filled with helium gas at 2000 Torr for heat exchange.
How to cite this article: Shimazu, Y. et al. Environmental Effects on Hysteresis of Transfer Characteristics in Molybdenum Disulfide Field-Effect Transistors. Sci. Rep. 6, 30084; doi: 10.1038/srep30084 (2016).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Ganatra, R. & Zhang Q. Few-layer MoS2: A promising layered semiconductor. ACS Nano 8, 4074–4099 (2014).
Tong, X., Ashalley, E., Lin, F., Li, H. & Wang, Z. M. Advances in MoS2-based field effect transistors (FETs). Nano-Micro Letters 7, 203–218 (2015).
Wang, H., Yuan, H., Hong, S. S., Li, Y. & Cui, Y. Physical and chemical tuning of two-dimensional transition metal dichalcogenides. Chem. Soc. Rev. 44, 2664–2680 (2015).
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).
Kuc, A., Zibouche, N. & Heine, T. Influence of quantum confinement on the electronic structure of the transition metal sulfide TS2 . Phys. Rev. B 83, 245213 (2011).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011).
Late, D. J., Liu, B., Ramakrishna Matte, H. S. S., Dravid, V. P. & Rao, C. N. R. Hysteresis in single-layer MoS2 field effect transistors. ACS Nano 6, 5635–5641 (2012).
Fontana, M. et al. Electron-hole transport and photovoltaic effect in gated MoS2 Schottky junctions. Sci. Rep. 3, 1634 (2013).
Liu, H. et al. Switching mechanism in single-layer molybdenum disulfide transistors: An insight into current flow across Schottky barriers. ACS Nano 8, 1031–1038 (2014).
Park, W. et al. Photoelectron spectroscopic imaging and device applications of large-area patteranble single-layer MoS2 synthesized by chemical vapor deposition. ACS Nano 8, 4961–4968 (2014).
Perera, M. M. et al. Improved carrier mobility in few-layer MoS2 field-effect transistors with ionic-liquid gating. ACS Nano 7, 4449–4458 (2013).
Pu, J. et al. Highly flexible MoS2 thin-film transistors with ion gel dielectrics. Nano Lett. 12, 4013–4017 (2012).
Cho, K. et al. Electric stress-induced threshold voltage instability of multilayer MoS2 field effect transistors. ACS Nano 7, 7751–7758 (2013).
Liu, H., Neal, A. T. & Ye, P. D. Channel length scaling of MoS2 MOSFETs. ACS Nano, 6, 8563–8569 (2012).
Kwon, H.-J., Jang, J., Kim, S., Subramanian, V. & Grigoropoulos, C. P. Electrical characteristics of multilayer MoS2 transistors at real operating temperatures with different ambient conditions. Appl. Phys. Lett. 105, 152105 (2014).
Qiu, H. et al. Electrical characterization of back-gated bi-layer MoS2 field-effect transistors and the effect of ambient on their performances. Appl. Phys. Lett. 100, 123104 (2012).
Taur, Y. & Ning, T. H. Fundamentals of Modern VLSI Devices (Cambridge University Press, Cambridge, 1998).
Popov, I., Seifert, G. & Tomanek, D. Designing electrical contacts to MoS2 monolayers: A computational study. Phys. Rev. Lett. 108, 156802 (2012).
Das, S., Chen, H. Y., Penumatcha, A. V. & Appenzeller, J. High performance multilayer MoS2 transistors with scandium contacts. Nano Lett. 13, 100–105 (2013).
Fang, H. et al. Degenerate n-doping of few-layer transition metal dichalcogenides by potassium. Nano Lett. 13, 1991–1995 (2013).
Gong, C., Colombo, L., Wallace, R. M. & Cho, K. The unusual mechanism of partial fermi level pinning at metal-MoS2 Interfaces. Nano Lett. 14, 1714–1720 (2014).
Cho, K. et al. Electrical and optical characterization of MoS2 with sulfur vacancy passivation by treatment with alkanethiol molecules. ACS Nano 9, 8044–8053 (2015).
Park, W. et al. Oxygen environmental and passivation effects on molybdenum disulfide field effect transistors. Nanotechnology 24, 095202 (2013).
Tongay, S. et al. Broad-range modulation of light emission in two-dimensional semiconductors by molecular physisorption gating. Nano Lett. 13, 2831–2836 (2013).
Yue, Q., Shao, Z., Chang, S. & Li, J. Adsorption of gas molecules on monolayer MoS2 and effect of applied electric field. Nanoscale Res. Lett. 8, 425 (2013).
Kim, W. et al. Hysteresis caused by water molecules in carbon nanotube field-effect transistors. Nano Lett. 3, 193–198 (2003).
Ong, H. G. et al. Origin of hysteresis in the transfer characteristic of carbon nanotube field effect transistor. J. Phys. D: Appl. Phys. 44, 285301 (2011).
Wang, H., Wu, Y., Cong, C., Shang, J. & Yu, T. Hysteresis of electronic transport in graphene transistors. ACS Nano 4, 7221–7228 (2010).
Lee, Y. G. et al. Fast transient charging at the graphene/SiO2 interface causing hysteretic device characteristics. Appl. Phys. Lett. 98, 183508 (2011).
Gu, G. & Kane, M. G. Moisture induced electron traps and hysteresis in pentacene-based organic thin-film transistors. Appl. Phys. Lett. 92, 053305 (2008).
Shu, J. et al. The intrinsic origin of hysteresis in MoS2 field effect transistors. Nanoscale 8, 3049–3056 (2016).
Late, D. J. et al. Sensing behavior of atomically thin-layered MoS2 transistors. ACS Nano, 7, 4879–4891 (2013).
Zhang, S. L., Jung, H., Huh, J. S., Yu, J. B. & Yang, W. C. Efficient exfoliation of MoS2 with volatile solvents and their application for humidity sensor. J. Nanosci. Nanotechnol. 14, 8518–8522 (2014).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Castellanos-Gomez, A. et al. Deterministic transfer of two-dimensional materials by all-dry viscoelastic stamping. 2D Materials 1, 011002 (2014).
This work was supported by JSPS KAKENHI Grant Number 15K13497.
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Shimazu, Y., Tashiro, M., Sonobe, S. et al. Environmental Effects on Hysteresis of Transfer Characteristics in Molybdenum Disulfide Field-Effect Transistors. Sci Rep 6, 30084 (2016). https://doi.org/10.1038/srep30084
Kinetics and Thermodynamics of Adsorption–Desorption of Water Vapors on Microsized Powders of Layered Molybdenum Disulfide
Powder Metallurgy and Metal Ceramics (2020)
npj 2D Materials and Applications (2018)
Scientific Reports (2017)