Abstract
Thermo-Electrochemical cells (Thermocells/TECs) transform thermal energy into electricity by means of electrochemical potential disequilibrium between electrodes induced by a temperature gradient (ΔT). Heat conduction across the terminals of the cell is one of the primary reasons for device inefficiency. Herein, we embed Poly(Vinylidene Fluoride) (PVDF) membrane in thermocells to mitigate the heat transfer effects - we refer to these membrane-thermocells as MTECs. At a ΔT of 12 K, an improvement in the open circuit voltage (Voc) of the TEC from 1.3 mV to 2.8 mV is obtained by employment of the membrane. The PVDF membrane is employed at three different locations between the electrodes i.e. x = 2 mm, 5 mm, and 8 mm where ‘x’ defines the distance between the cathode and PVDF membrane. We found that the membrane position at x = 5 mm achieves the closest internal ∆T (i.e. 8.8 K) to the externally applied ΔT of 10 K and corresponding power density is 254 nWcm−2; 78% higher than the conventional TEC. Finally, a thermal resistivity model based on infrared thermography explains mass and heat transfer within the thermocells.
Similar content being viewed by others
Introduction
Thermoelectricity, a phenomenon where a temperature gradient is converted into electricity, is a topic of intense research interest primarily for energy harvesting applications. A conventional thermoelectric (TE) module consists of an array of p- and n- type semiconducting materials assembled between two electrodes maintained at different temperatures. The efficiency of a typical TE device is governed by the temperatures of the hot and cold electrodes (Th and Tc) as well as the intrinsic properties of TE materials. Thus, a dimensionless figure of merit (ZT) is defined by equation (1) as a quantitative measure of energy conversion capability of TE materials (p- and n- type materials).
where “σ” is electrical conductivity (S/m), “α” is the thermoelectric, or “Seebeck”, coefficient (V/K), “T” is the absolute temperature (K) while Kelec and Klatt are the electronic and lattice contribution of thermal conductivity (W/m·K) of the material, respectively1,2,3,4. Therefore, the overall device efficiency (η) in the literature3,4 is expressed as:
Researchers have subjected intensive efforts to attain higher ZT values through various routes1,2,5,6,7,8,9 but the highest value in bulk materials is around 1.4–1.66,7 which is still insufficient for large scale industrial applications. The foremost challenge to exceed the ZT value is to overcome the interdependency of electronic and thermal properties of the materials. Equation (1) suggests that a high ZT is dependent on high electrical conductivity (σ) and Seebeck coefficient (α), and low thermal conductivity (K). Furthermore, an increase in charge carrier concentration (n, cm−3) will have a proportional effect of increasing σ, but decreasing α. Thus, there is a significant tradeoff between the three key parameters σ, α and K, where typically a material of high electrical conductivity will also have high thermal conductivity, but consequently low ZT. Strategies such as phonon glass electron crystal (PGEC) structures, quantum dots and superlattices have been devised in order to provide both high electrical conductivity and low thermal conductivity1,2,5,6,7,8,9.
In recent times, novel thermoelectric effects apart from the semiconductor-based Seebeck effect have been introduced, such as the Spin Seebeck effect10 and the electrochemical Seebeck effect. The electrochemical Seebeck effect arises in thermo-electrochemical cells, TECs, when a solution containing a redox couple is subjected to a temperature gradient. The temperature gradient between the electrodes disturbs the electrochemical potential equilibrium between the electrolyte and electrode surface causing the current to flow when the circuit is complete11. This effect can result in significantly high Seebeck coefficients of redox electrolytes, which translate into potentially high power outputs. Furthermore, these solutions generally possess low thermal conductivity, which can contribute to a higher thermoelectric figure of merit.
TECs, traditionally known as thermo-galvanic cells, have been studied since the early 1980s12,13,14. TECs generate steady electric current by the virtue of a temperature gradient between the two electrodes placed in an electrolyte. Conventionally, characterization of the electrochemical Seebeck coefficient, Se, is conducted using a two-compartment setup, connected by a salt bridge, which allows a physical pathway for ion transfer between the two compartments. The two compartments are subjected to a temperature gradient (ΔT), and ion migration is enabled from the hotter compartment to the colder compartment through the salt bridge (Fig. 1(a)). The resulting potential difference (ΔV) is used as the basis for the calculation of Se (where Se = ΔV/ΔT)11,15.
For application of these devices, the TEC is used as a cell structure as shown in Fig. 1(b) where the electrolyte and both the electrodes are confined in a single chamber. The ion transport within the cell configuration is a complex combination of natural convection, migration, thermal and chemical diffusion. Although, cell configuration is practically more applicable but maintaining the temperature gradient between electrodes is a key challenge which limits the performance of the TEC, as the thermal conductivity of the electrolyte solution will inevitably reduce ΔT. On the contrary, the two-beaker setup (Fig. 1(a)) allows maintaining high temperature gradient as the two compartments are separated and can be easily maintained at different temperatures. Typical strategies to maintain the integrity of the temperature gradient in the “cell configuration” include an auxiliary cooling system on the cold side electrode, which adds complexity, cost and bulk to the overall system. In this work, we insert and optimize the position of a PVDF membrane within the TEC to maintain the temperature gradient without any need for an auxiliary cooling system. Hu et al.16 have utilized commercial glass-frits and NOMEX HT4848 (a nylon-based polymer separator commercially prepared by NOMEX, DuPont) in their thermocells as separators between their anode and cathode. They attributed the obtained high output power density of 1.8 W/m2, and corresponding Carnot efficiency of 1.4%, to high electron transfer rates between their novel carbon nanotube electrodes and the electrolyte. Thus, the influence of the different separators on thermal gradient and electrochemical performance were not been studied in depth.
An ideal separator should be porous in order to allow ionic transport, yet highly thermal resistive in order to maintain a large temperature gradient between the electrodes. PVDF was chosen for this study as it is an excellent thermal insulator and is also highly chemically stable polymer, in particular with respect to the redox couple. Additionally, films of PVDF can be easily fabricated through facile methods such as phase inversion and electrospinning. PVDF has also been used in energy storage and conversion applications such as batteries and fuel cells17,18,19. For example, separators of PVDF-co-hexafluoropropylene (PVDF-HFP), sandwiched poly(m-phenylene isophthalamide) (PMIA) between two PVDF layers (PVDF/PMIA/PVDF) and sandwiched PVDF layer between two poly(phthalazinone ether sulfone ketone) (PPESK) (PPESK/PVDF/PPESK) have been studied for Li-ion batteries17,18,19. Researchers have also explored PVDF membranes in fuel cells and piezoelectric devices20,21. However, to the best of our knowledge, PVDF membranes have not been studied for TEC applications.
Results
The electrochemical Seebeck coefficient (Se) for the 0.7 M I−/I3− (aq) redox couple was 0.4 mV/K when tested in the two compartment cell (Fig. 1(a)). This is 0.13 mV/K less than the reported value of 0.53 ± 0.04 mV/K for a 0.4 M solution, consistent with the expectation that for this range of concentrations, an increase in molarity results in a decrease in Se15,22,23. However, highly concentrated solutions are preferred for higher power outputs from the thermocells15,24,25. The designs of thermocells used in present work and the thermo-electrochemical performances of TECs (membrane less) and MTECs (membrane inserted TEC) are depicted in Fig. 2. The maximum open circuit voltage (Voc) generated by the conventional TEC is 1.3 mV at the temperature gradient of 12 K. However, the introduction of a PVDF membrane in the TEC significantly enhances the Voc to 2.7 mV for the case of x = 5 mm, at the same value of externally applied ΔT (Fig. 2(a)). The details of open circuit voltages from the TEC and MTECs are given in Table 1. The origin of this higher performance is enhancement of the thermal gradient between the two electrodes due to the presence of the PVDF membrane, which has the effect of decreasing convective flow between the electrodes. By creating a thermal barrier between the two halves of the cell the temperature at the working surfaces of the electrodes are able to more closely approach the externally applied temperatures, thus maximizing the internal thermal gradient and achieving the maximum Voc. An illustration of the heat flow in a TEC and MTEC are presented in Fig. 3(a,c) and the thermal barrier is quantitatively expressed as a thermal resistivity (Fig. 3(b,d)).
In this paper, we first discuss the influence of PVDF membrane on the power generation characteristics of the TEC and MTECs. Then, visualisation of the mass and heat transport within the TEC and MTEC using infrared thermography allows insight into the role of the membrane separator in these cells.
Power Generation characteristics of TEC and MTEC
Inserting the PVDF membrane into the TEC has the direct benefit of enhancing the temperature gradient, and hence the generated voltage, as illustrated in Fig. 2(a). These results are summarised in Table 1, where an improvement of 52% was achieved for the case of membrane at x = 5 mm compared to the TEC. Consequently, the overall thermo-electrochemical power generation of the MTEC is shown to be enhanced significantly compared to the TEC as expressed in Fig. 4. The maximum power density from the MTEC was 245 nWcm−2, achieved for the case of x = 5 mm, measured at temperature gradient of 10 K, which is almost four times higher than the TEC maximum power density (54 nWcm−2).
It is to be noted that each membrane configuration in MTECs results in improved cell potential as compared to the TEC. In Table 1, the calculated thermal gradient between the electrodes is presented, using ΔTcalc = ΔV/Se, where Se = 0.4 mV/K and ΔV in each case is the open-circuit voltage recorded for the cases of x = 2 mm, 5 mm, and 8 mm respectively. Table 1 shows that a TEC is only able to provide a temperature gradient of 2.7 K between the electrodes, whereas the externally applied temperature gradient is 10 K. This observation further confirms the rapid heat flow in the TEC cases. In all the MTECs the thermal gradient between the electrodes is improved as compared to the TEC, reaching an optimal temperature gradient (8.8 K) for x = 5 mm. Consequently, this MTEC provides the best power performance. Additionally, the lowest power generation of 61 nWcm−2 was achieved with the x = 2 mm MTEC, when the membrane is closer to the cold electrode, which has the smallest thermal gradient amongst the membrane inserted cases.
Mass and heat transfer characteristics of the TEC
Reduction, in the case of the (I−/I3−) redox couple, occurs at the colder electrode (i.e. the cathode). The reduced species, migrate towards the anode where they oxidize; releasing the electrons13,14. This can be visualised in the infrared thermal images of the TECs in Fig. 5(I), where the convection effects coupled with the thermal diffusion allows fast equilibration of the temperature within the cell. After 29 mins of heating the average temperature of the redox solution was 26.7 °C (±1 °C). Thus, in the case of the TEC the heat transfer through mass (fluid) flow rapidly diminishes the temperature gradient across the TEC that is critical to the its operation. The images of Fig. 5(I) indicated that after 34 and 38 mins the temperature of the solution has been increased to 28.4 °C (±1 °C) and 31.0 °C (±1 °C), and thus the temperature gradient across the vertical axis has been significantly reduced. The maximum temperature difference was achieved after 38 mins of heating, thus resulting in the maximum Voc. Figure 6 shows a quantitative representation of temperature distribution within the cell, extrapolated from Fig. 5 using thermal imaging software after 38 mins of heating. In the histogram of the TEC, the temperature of the electrolyte is concentrated around ca. 30.4–31.8 °C (±1 °C) resulting in a unimodal distribution (Fig. 6(a)). The unimodal temperature distribution supports the weaker temperature gradient maintained between the electrodes of TEC.
Mass and heat transfer characteristics of the MTECs
The effect of the insertion of a PVDF membrane on the heat flow is illustrated in Fig. 5(II,III,IV) for the cases of membrane position 2 mm, 5 mm, and 8 mm, respectively. The PVDF material is an efficient thermal insulator with thermal resistivity of ~6 mK W−1 26,27,28. The thermal resistive effects of PVDF in MTECs obstruct the heat flow between the electrodes creating distinct temperature zones, thus resulting in bimodal temperature distribution in MTECs, as shown in Fig. 6(b,c,d). In the TEC after heating for 38 mins the average temperature of the electrolyte was 31.0 °C (±1 °C), whereas after the same heating time in the MTECs temperature zones of 31 °C and 35 °C (±1 °C) in the x = 2 mm case, 34 °C and 39 °C (±1 °C) in the x = 5 mm case, and 35 °C and 40 °C (±1 °C) in the x = 8 mm case were observed (Fig. 6(b,c,d)). The details of the peak positions and breadths are given in Table 1. Therefore, in summary, the presence of the membrane acts as a thermal resistor to hinder heat flow. However, the improved open circuit voltage and maximum power density also indicate that ion transfer between the electrodes is not adversely affected by the PVDF barrier.
Thermal resistance model
To further elucidate the effect of the PVDF membrane inclusion in the TEC, a thermal resistance model is proposed in Fig. 3(b,d). A temperature gradient is key to the voltage generation in a TEC, and in an ideal case this temperature gradient is maintained throughout the experiment and is equivalent to the difference in applied temperatures at the electrodes. However, more realistically, losses occur due to a number of factors: temperature gradients in the electrodes, heat lost to the environment, and convection and conduction within the solution. For TEC the equivalent thermal resistance circuit can be represented by Fig. 3(b). For the solution, the thermal resistance may be described in terms of its thermal conductivity and thermal mass transfer (predominantly convection). In this case, the relatively high convection of the solution can be represented by a low thermal resistance. As noted previously, it results in the solution reaching thermal equilibrium relatively quickly within the TEC, which significantly diminishes the temperature gradient and the power output to 2.7 K and 54 nWcm−2, respectively. In comparison, the equivalent thermal resistance of the MTEC is represented in Fig. 3(d), where the thermal resistance of the PVDF membrane is much larger than those of the solution or the electrodes. Furthermore, the presence of the membrane also has a direct impact on the thermal resistance of the solution: whilst the thermal conductivity may be assumed as constant, the thermal mass transfer effects (i.e. convection) is diminished as the volume is now physically divided into two half cells. Consequently, the thermal resistance of the solution is also increased prompting MTEC closer to the applied temperature gradient i.e. 8.8 K. Of further note is that the optimum performance of the cell (245 nWcm−2) is achieved at a membrane position of x = 5 mm, i.e. equidistant from both electrodes, where the power output in this configuration of membrane has provided 78% improvement to the performance of the TEC. This observation can also be explained within the context of limiting the convection within the half cells, as this configuration allows the minimum electrolyte volume on either side of the membrane.
Discussion
We have demonstrated here that a separator membrane significantly affected the operation of a thermo-electrochemical cell, by reducing the effect of convective currents in the electrolyte. A thermal resistance model shows that the dominant thermal resistance of the membrane reduces temperature drops in other parts of the cell, i.e. across the two electrolyte layers and across the electrode assembly. The findings of this work suggest that the insertion of the membrane at its optimum configuration is able to improve the temperature gradient by 70% and the resulting power density by 78%. These results will be useful to optimize the future performance of TECs when used in conjunction with the optimised formulations of redox couples for waste heat conversion into electricity.
Methods
Materials
The iodide/triiodide (I−/I3−) redox solution (0.7 M) was prepared in 50 ml distilled water by dissolution of Iodine (5 g, Sigma Aldrich; ≥99.8%) and Potassium Iodide (10 g, Sigma Aldrich; ≥99.5%). The solution was heated to 50 °C for 10 mins to ensure proper solubility. A 200 μm thick PVDF membrane was prepared by phase inversion method. Commercially available Poly(Vinylidene Fluoride) (PVDF, Kynar® K-761, molecular weight of 440,000, density = 1.7 g/ml and melt temperature ~165 °C) powder was mixed with 1-Methyl-2-Pyrrolidinone (NMP) in a ratio of 18% by wt. The solution was stirred for 24 hours at 60 °C. The polymer solution was then cast on a glass plate and the resultant flat sheet membranes were immediately immersed in a coagulation bath containing deionised water. The prepared PVDF membrane is porous with pore size ranging in several microns as shown in Fig. 7.
Measurement of the Seebeck coefficient of the I−/I3− aqueous redox solution
The prepared I−/I3− aqueous redox solution was put in two compartments (Pyrex glass beakers), according to the schematic shown in Fig. 1(a). Each compartment contained a Pt electrode. The physical exchange of the solutions between the two compartments was established by providing a salt bridge containing the same solution. Pt electrodes were cleaned with concentrated HNO3 followed by methanol rinsing. The thermal gradient was created by heating one of the compartments through an electrically operated heater at 0.2 °C/min rate while maintaining the other at room temperature (Fig. 1(a)).
Morphological and Heat Transfer Characterization
The surface morphology of PVDF membrane was studied by FE-SEM (HITACHI SU8030). Infrared Thermography was carried out at the framerate of 8.5 Hz through R300SR-HB (Nippon Avionics Co. Ltd.) maintaining similar environmental conditions to comprehend the role of membranes in enhancing thermal gradient within the thermocells.
Thermo-Electrochemical Cell Fabrication and Measurements
Thermo-electrochemical performance of the redox solution with PVDF membranes was studied in a 13 mm diameter and 20 mm length cells (Fig. 2(b)). The two open ends of the thermocell were closed by rubber sealants to ensure no leakage and the redox solution was inserted through a syringe. The distance between the vertically positioned graphite electrodes were kept constant at 10 mm while the membrane positions (x) were altered between 2 mm, 5 mm and 8 mm away from the top (cold) electrode. For MTECs, a rubber O-ring (ϕout = 13 mm and ϕin = 10 mm) was used to hold the membrane in the intended positions (Fig. 2(c,d,e)). The reproducibility of the results was examined and the difference in Seebeck values, on average, was found to be ±0.02 mV/K. The electrodes were cleaned by abrasive paper followed by ultrasonic cleaning with acetone. The thermocells were heated in cold-above-hot arrangement at 0.2–0.5 °C/min and the open circuit voltage (Voc) was measured by an Agilent 34461A 61/2 digital multimeter. The electrochemical Seebeck coefficient was evaluated by the slope of the linear fit between Voc and ΔT. For power output measurements the TEC and MTECs were connected to a variable resistor box (Elenco RS-500), different resistive loads (R, Ω) were applied and the corresponding cell potentials (V, mV) were recorded. The Ohm’s law (P = V2/R) was used to calculate the power values.
Additional Information
How to cite this article: Hasan, S. W. et al. High Thermal Gradient in Thermo-electrochemical Cells by Insertion of a Poly(Vinylidene Fluoride) Membrane. Sci. Rep. 6, 29328; doi: 10.1038/srep29328 (2016).
References
Synder, G. J. & Toberer, E.S. Complex thermoelectric materials. Nature Materials 7, 105–114 (2008).
Tritt, T. M. Thermoelectric phenomena, materials and applications. Annu. Rev. Mater. Res. 41, 433–448 (2011).
Telkes, M. Efficiency of thermoelectric generator. Jour. Appl. Phys. 18, 1116–1127 (1947).
Chasmar, R. P. & Stratton, R. Thermoelectric figure of merit and its relation to thermoelectric generator. Jour. Elec. Contr. 7, 52–57 (1959).
Gonzalez, M. M-., Calero, O. C-. & Chao, P. D-. Nanoengineering thermoelectrics for 21st century: Energy harvesting and other trends in the field. Renewable and Sustainable Energy Reviews 24, 288–305 (2013).
Poudel, B. et al. High-thermoelectric performance of nanostructured Bismuth Antimony Telluride bulk alloys. Science 320, 634–638 (2008).
Xie, W. et al. High performance Bi2Te3 nanocomposites prepared by single-element-melt-spinning spark-plasma sintering. J. Mater. Sci. 48, 2745–2760 (2013).
Hicks, L. D. & Dresselhaus, M. S. Thermoelectric figure of merit of a one-dimensional conductor. Phys. Rev. B. 47, 16631–16634 (1993).
Venkatasubramanian, R., Siivola, E., Colpitts, T. & O’Quinn, B. Thin-film thermoelectric devices with high room-temperature figures of merit. Nature 413, 597–602 (2001).
Uchida, K. et al. Observation of the spin Seebeck effect. Nature 455, 778–781 (2008).
Gunawan, A. et al. Liquid thermoelectrics: Review of recent and limited new data of thermogalvanic cell experiments. Nanoscale and Microscale Thermophysical Engineering 17, 304–323 (2014).
Chum, H. L. & Osteryoung, R. A. Review of thermally regenerative electrochemical systems. Technical report. Available at: http://www.nrel.gov/docs/legosti/old/416_v1.pdf. (Accessed: 15th November, 2015) (1981).
Quickenden, T. I. & Mua, Y. The power conversion efficiencies of a thermogalvanic cell operated in three different orientations. J. Electrochem. Soc. 142, 3652–3659 (1995).
Mua, Y. & Quickenden, T. I. Power conversion efficiency, electrode separation, and overpotential in the Ferricyanide/Ferrocyanide thermogalvanic cell. J. Electrochem. Soc. 143, 2558–2564 (1996).
Abraham, T. J., MacFarlane, D. R. & Pringle, J. M. Seebeck coefficients in ionic liquids–prospects for thermo-electrochemical cells”. Chem. Commun. 47, 6260–6262 (2011).
Hu, R. et al. Harvesting waste thermal energy using a Carbon-Nanotube-Based thermo-electrochemical cell. Nano Lett. 10, 838–846 (2010).
Pu, W., He, X., Wang, L., Jiang, C. & Wan, C. Preparation of PVDF-HFP microporous membrane for Li-ion batteries by phase inversion. J. Membr. Sci. 272, 11–14 (2006).
Zhai, Y. et al. Sandwich-structured PVdF/PMIA/PVdF nanofibrous separators with robust mechanical strength and thermal stability for lithium ion batteries. J. Mater. Chem. A 2, 14511–14518 (2014).
Lu, C. et al. Electrochemical performance and thermal property of electrospun PPESK/PVDF/PPESK composite separator for lithium-ion battery. J. Appl. Electrochem. 43, 711–720 (2013).
Kumar, G. G. et al. Irradiated PVdF-HFP-tin oxide composite membranes for the applications of direct methanol fuel cells. J. Membr. Sci. 350, 92–100 (2010).
Inan, T. Y., Dogan, H. & Gungor, A. PVdF-HFP membranes for fuel cell applications: effects of doping agents and coating on the membrane’s properties. Ionics 19, 629–641 (2013).
Abraham, T. J. et al. Towards ionic liquid-based thermoelectrochemical cells for the harvesting of thermal energy. Electrochimica Acta 113, 87–93 (2013).
Abraham, T. J., MacFarlane, D. R. & Pringle, J. M. High Seebeck coefficient redox ionic liquid electrolytes for thermal energy harvesting. Energy Environ. Sci. 6, 2639–2645 (2013).
Uhl, S. et al. Development of flexible micro-thermo-electrochemical generators based on ionic liquids. J. Electronic Materials 43, 3758–3764 (2014).
Alzahrani, H. A. H., Black, J. J., Goonetilleke, D., Panchompoo, J. & Aldous, L. Combining thermogalvanic corrosion and thermogalvanic redox couples for improved electrochemical waste heat harvesting. Electrochem. Comm. 58, 76–79 (2015).
Curcio, E. & Drioli, E. Membrane distillation and related operations–A review. Sep. Pur. Rev. 34, 35–86 (2005).
Yu, J., Huang, X., Wu, C. & Jiang. P. Permittivity, thermal conductivity and thermal stability of poly(vinylidene fluoride)/graphene nanocomposites. IEEE Trans. Dielec. Elec. Insul. 18, 478–484 (2011).
Camacho, L. M. et al. Advances in membrane distillation for water desalination and purification applications. Wat. 5, 94–196 (2013).
Acknowledgements
This research is supported by the University of Malaya–Ministry of Higher Education Grant, UM.C/1/625/HR/MOHE/ENG/29, University Malaya Research Grant (UMRG) under the project RP014D-13AET, FRGS under the project FP011-2014A and Science Fund under the project SF-020-2013. The authors also gratefully acknowledge funding from the Australian Research Council through its Centre of Excellence program and fellowship support for D. R. MacFarlane (Australian Laureate Fellowship).
Author information
Authors and Affiliations
Contributions
S.W.H. designed and conducted the experiments with the assistance of M.M.I.M.H. N.A.H. supervised the membrane synthesis and characterizations. S.W.H., S.M.S., M.F.M.S., A.S.A.B., J.M.P. and D.R.M. discussed and analysed the results. All authors contributed equally towards the preparation of manuscript. The project was supervised by S.M.S., M.F.M.S. and A.S.A.B.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Hasan, S., Said, S., Sabri, M. et al. High Thermal Gradient in Thermo-electrochemical Cells by Insertion of a Poly(Vinylidene Fluoride) Membrane. Sci Rep 6, 29328 (2016). https://doi.org/10.1038/srep29328
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep29328
This article is cited by
-
Flexible nanocomposite electrodes with optimized hybrid structure for improved low-grade heat harvest via thermocells
Science China Chemistry (2023)
-
Improved Thermal Gradients in Diffuser-/Nozzle-Shaped Thermally Driven Electrochemical Cells for Enhanced Output Power Density
Arabian Journal for Science and Engineering (2023)
-
Operando magnetic resonance imaging for mapping of temperature and redox species in thermo-electrochemical cells
Nature Communications (2021)
-
Weak solutions for multiquasilinear elliptic–parabolic systems: application to thermoelectrochemical problems
Boletín de la Sociedad Matemática Mexicana (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.