HfS2 is the novel transition metal dichalcogenide, which has not been experimentally investigated as the material for electron devices. As per the theoretical calculations, HfS2 has the potential for well-balanced mobility (1,800 cm2/V·s) and bandgap (1.2 eV) and hence it can be a good candidate for realizing low-power devices. In this paper, the fundamental properties of few-layer HfS2 flakes were experimentally evaluated. Micromechanical exfoliation using scotch tape extracted atomically thin HfS2 flakes with varying colour contrasts associated with the number of layers and resonant Raman peaks. We demonstrated the I-V characteristics of the back-gated few-layer (3.8 nm) HfS2 transistor with the robust current saturation. The on/off ratio was more than 104 and the maximum drain current of 0.2 μA/μm was observed. Moreover, using the electric double-layer gate structure with LiClO4:PEO electrolyte, the drain current of the HfS2 transistor significantly increased to 0.75 mA/μm and the mobility was estimated to be 45 cm2/V·s at least. This improved current seemed to indicate superior intrinsic properties of HfS2. These results provides the basic information for the experimental researches of electron devices based on HfS2.
To realise ultra-low power circuits, three important electrical characteristics are desirable in channel materials for field-effect transistors (FETs). They are low supply voltage, high drivability and small off-leakage current. The first two can be achieved by channel scaling in the same manner as that in previous techniques1. On the other hand, continuous scaling of channel length Lch can lead to a severe short-channel effect (SCE)2. SCE increases the off-leakage current and standby power consumption of logic circuits. One of the possible solutions to reduce SCE in ultra-scaled channel (Lch < 10 nm) is the introduction of atomically thin body channel structure. However, in an extremely thin body channel consisting of conventional semiconductors such as silicon (Si)3, InGaAs4 and germanium5, surface roughness scattering severely reduces the carrier mobility6 and ballistic coefficient. Two-dimensional (2D) materials have layered crystal structure with strong covalent/ionic bond in a plane and a weak Van der Waals interaction between layers. From this unique property, 2D materials can obtain an atomically flat surface with discrete thickness defined by its single-layer thickness, a carrier transport with minimal surface roughness scattering and a strong immunity to short channel effect. These 2D material features can be useful in achieving ultra-low power operation because of the realisation of high mobility with extremely short and thin channel design. Another critical property for low leakage current operation is the bandgap value. Graphene7,8, which is the most famous 2D material, has no bandgap without the application of additional techniques9,10 and this property is a major hindrance in reducing the drain leakage. Zero (or very small) bandgap materials such as graphene show ambipolar behaviour in field-effect current modulation. The off current could not be small enough due to reverse polarity operation. Although, this property is useful in many applications (e.g. RF applications11 and sensing12), it becomes impractical in low-power logic circuits13. Moreover, to reduce the drain leakage current due to band-to-band tunnelling such as gate-induced drain leakage14, wide bandgap is desirable for materials with finite bandgap. Therefore, 2D materials with a finite bandgap, such as transition metal dichalcogenides (TMDs) (e.g. MoS215,16 and WSe217,18) or phosphorene19,20, are required for low power consumption FETs. The mobility and bandgap should be carefully and extensively investigated for various applications and for performance improvement.
HfS2 (Hafnium disulphide) was previously considered as a semi-insulating material because the measured conductivity of HfS2 is very low compared with that of MoS221,22. However, in recent studies, some attractive properties of single-layered HfS2 have been theoretically predicted. The long-wave acoustic phonon limited mobility μAP of TMDs estimated in ref. 23 and the energy bandgap Eg in ref. 24 are shown in Fig. 1, which indicate that a substantial trade-off exists between μAP and Eg. Single-layer HfS2 is expected to have good upper limit of mobility (~1800 cm2/V∙s) and reasonable energy bandgap (~1.2 eV) for a high on/off ratio. Although several reports concerning the electron mobility of MoS216,25,26 suggested the existence of several other scattering mechanisms, we understand that comparison of the mobilities in TMDs using the uniform calculation method will aptly represent the relative trend among these mobilities. Additionally, large electron affinity of HfS2 has a possibility to achieve low contact resistance for n-type carrier transport because of basic principle of the contact formation between semiconductors and metals. Consequently, we planned to experimentally evaluate the FET performance of HfS2 and reveal its potential for transistor channel. In addition, the other properties of thin-layered HfS2 have not been thoroughly investigated and we report some basic characteristics of atomically thin-layered HfS2 essential for fabrication and characterisation.
Results and Discussion
Estimation of the ballistic current for single-layer HfS2
Prior to the experiment, the ballistic current of a single-layer HfS2 FET was calculated using a simple numerical method at the potential bottleneck27 to evaluate the potential of the HfS2 channel. The electron effective masses, which are essential for this numerical calculation, were 0.24 m0 along the M–K and 3.3 m0 along the M–Γ24. The several assumptions used in the ballistic model were as follows: (1) the electron backscattering in the channel and drain injection is negligible for the ballistic limit. Therefore, only half of the states with positive wave numbers are considered. (2) The electron distribution thickness in the HfS2 layer is not considered. In other words, all electrons exist at the interface between the oxide and HfS2. (3) Parabolic and ellipsoidal conduction bands are assumed for threefold valleys at the M points in the Brillouin zone. (4) The equivalent oxide thickness is defined to be 1 nm. Further details of calculations are described in supplementary information. Figure 2(a) shows the current distribution in the 2D first Brillouin zone by the contour plot at 300 K. The arrows in the inset denote the direction of the channel selected with high symmetry (M–Γ and M–K). Figure 2(b) shows the calculated transfer characteristics of single-layer HfS2 at room temperature (RT). The off current at a gate voltage of 0 V was defined to be 100 nA/μm. Although the electrons in the conduction band had strong anisotropy in the effective masses, the drain current did not indicate a significant difference in the channel direction because of the mixing of the threefold valleys with an angle of 120° from one another. It reached to 2 mA/μm at the gate voltage of 0.6 V.
Basic properties of HfS2 flakes micromechanically transferred on Al2O3/Si
Figure 3(a) shows a piece of single-crystal HfS2, which is commercially available with high orientation and purity. We performed mechanical exfoliation using scotch tape to obtain thin-film HfS2 on the substrate. First, a small piece of HfS2 was spread on the tape and then cleaved several times to reduce its layer thickness to an average size, as shown in Fig. 3(b). Thickness-dependent colour contrast was distinctly observable. Figure 3(c) shows the optical image of the exfoliated thin-film HfS2 on a 285-nm-thick SiO2/Si substrate. Triangular or hexagonal shape often appeared in the flakes. These cleaved edges indicate the crystal orientation of the exfoliated HfS2. Incidentally, hexamethyldisilazane (HMDS) treatment helps in peeling a large size (>10 μm) atomically thin flake. The Raman spectrum of the thin HfS2 layers (<10 nm) on the SiO2/Si substrate with the excitation wavelength of 532 nm is shown in Fig. 3(d). The primary peak appeared at the Raman shift of approximately 337 cm−1 and it was consistent with the previous experimental report of bulk HfS2 that showed a first-order A1g peak28. Satellite peaks at 260 and 321 cm−1 were also considered as Eg mode. These results indicate that single-crystal layers with well-aligned atoms remained intact during exfoliation and organic solvent cleaning. At this time, no remarkable change was observed from the bulk to the thin films. The visibility of the atomically thin HfS2 layers could be strongly dependent on the thickness and permittivity of the flake and the insulator, as reported in graphene29 and MoS230. Figure 4 shows the optical microscope and the atomic force microscope (AFM) image (inset) with cut line profiles. The steps between the different contrast layers were approximately 0.7 nm/1.4 nm and they appeared to be single/double atomic steps. On the 75-nm-thick Al2O3, the contrast in the single-layer HfS2 was too weak to form electrodes using the alignment technique. However, several layers of HfS2 were clearly observable by the optical microscope and the thicknesses could be easily identified by the colour of the flakes.
HfS2 has a CdI2-like octahedral coordinated layered structure with an atomic layer thickness of 0.59 nm31 (Fig. 5(a)). The Hf atoms (blue spheres) are sandwiched by S atoms (yellow spheres) and the Hf atoms in each plane are stacked at the same position (1T, tetragonal symmetry). This crystal structure is different from that of MoS2, which typically has a trigonal prismatic coordinate with 2H symmetry. The schematic image of a fabricated FET with proper biases is shown in Fig. 5(b). The thin-body channel contains several atomic layers that were transferred onto the atomic layer deposited 75-nm-thick Al2O3/p++-Si(100) substrate. At first, we fabricated by used plasma-enhanced chemical vapour-deposited (PECVD) SiO2 (285 nm) as back-gate insulator for the first time. However, it could not work with clear current modulation by the back gate due to the small gate capacitance, high-density charge trapping and surface roughness caused due to PECVD SiO2 (please see supplementary Information Fig. S3). Au/Ti electrodes were fabricated on thin-film HfS2 as source and drain contacts. The source electrode was connected to the ground and the drain electrode was positively biased with respect to the source (VDS). Back-gate voltage VGS was applied to the p++-Si substrate. The optical microscope measurement suggested channel width and length of 10 μm (at the source edge) and 2 μm, respectively (Fig. 5(c)). From the cross-sectional height profile measured by AFM shown in Fig. 5(d), the thickness of the HfS2 channel was approximately 3.8 nm, which was composed of 6 ± 1 atomic layers.
Back gate operation of the HfS2 FET
Figure 6(a) shows the output characteristics of fabricated few-layer HfS2 FETs at RT. Clear saturation behaviour is observed in the ID–VDS curves for all VGS biases and VDS sweep (0–5 V). The robust current saturation at high VDS (5 V) indicates that the HfS2 bandgap is sufficient for short-channel FET fabrication. ID continuously increments over the measured VGS range. Unfortunately, our measurement system was not able to apply the voltage of over 40 V. A fully n-type enhancement mode operation with a threshold voltage greater than 8 V was observed. The ID–VDS curves at the small bias regime showed linearity without offset bias. Although the instability of the I–V curves depends on the measurement cycles and sweep conditions, current modulations are constantly obtained for over a month in the atmosphere. The ID–VGS (transfer) characteristics with logarithmic (left-hand side) and linear (right-hand side) scales for VDS = 3 V are also shown in Fig. 6(b). A maximum drain current of 0.2 μA/μm was obtained at VGS = 40 V. The on/off ratio was over 10,000 when the VGS was varied from −5 V (off state) to 40 V (on state). These results were partially reported in ref. 32. The effective mobility of electrons was calculated to be around 0.1 cm2/V.s which is far smaller than the theoretical expectation. It was probably limited by many intrinsic and parasitic components such as the carrier scattering, quality of flakes, contact resistance and charge trapping. This device had a large hysteresis (~15 V) (please see supplementary Information Fig. S4), which could have been caused by the response of the traps at the interface between HfS2 and Al2O3 or border/oxide traps in the bulk Al2O3. The gate leakage current IG is also plotted in logarithmic scale, which shows that IG is comparable with ID for higher values of VGS. Therefore, the on current and other performance of the present device can be improved by efficient modulation of the surface potential using a thinner gate dielectric with good interface properties.
Electric double layer transistor with HfS2 channel
The gate-induced carrier density in the HfS2 channel was limited by the back-gate properties such as interface/bulk charge trapping. To evaluate the potential of HfS2, we introduced the electric double-layer (EDL) gate structure33 for device measurement. Schematics of the carrier density modulation by back gate and EDL are shown in Fig. 7(a). In the case of Al2O3 back gate, the gate electric fields pass through the thick insulator and are partially terminated at the immobile charges. On the other hand, in the case of EDL operation, anions and cations (ClO4− and Li+ respectively) can freely move in the electrolyte. These ions form the EDL with carriers in semiconductors and metals and the electric field is localized near the surface (~5 nm). Therefore, the large gate capacitance was expected without the charge trapping. Moreover, the surface of the TMD does not have both dangling bond and disorder of atoms. The combination of TMD and electrolyte gate can potentially realise an ideal interface between the semiconductor and dielectric and efficient carrier modulation34. Figures 7(b,c) show the schematic device structure and transfer characteristics, respectively, of a fabricated HfS2 EDL transistor. LiClO4/PEO mixture was employed as an electrolyte gel for gate modulation. This time, the gate-contact electrode was far from the channel region and its area was not sufficiently large. Therefore, the effective gate voltage was smaller than the measured value (probably half or less). The measured drain current was over 0.75 mA/μm at VDS = 2 V and VGS = 5 V at RT. The IDS significantly increased from the back-gate operation and was notably high at the TMD channel in spite of the non-scaled channel length (1 μm). The maximum current density of a conventional TMD FET with a solid gate structure is approximately 0.5 mA/μm for MoS2 and it is limited by the contact resistance between MoS2 and the metal. The high drain current observed in this study indicates the superior potential of the low contact resistivity of HfS2. The relative hysteresis against the bias range was significantly reduced by the EDL gate. It means that the density of trap charges in EDL gate was far smaller than that of Al2O3 back gate. Improvement in back gate insulator would increase the drain current and reduce the hysteresis. The remaining hysteresis of the EDL transistor appeared to be caused by the response time of the anions and cations in the electrolyte. According to the magnitude of the gate current, the drain current might not depend on the electrochemical reaction at the electrode surface. The effective mobility of EDL device was roughly estimated to be 45 cm2/Vs from the peak gm by the assumption that the permittivity of the electrolyte is 5ε0 and the EDL thickness is 1 nm. It was clearly improved from the back-gate operation. However, the mobility is still smaller than the expected value (>1,000 cm2/V·s). One of the reasons can be attributed to the gate structure not being large enough for the voltage drop in the EDL to be negligible at the gate side. Therefore, the actual gate voltage for the channel EDL is less than the applied value. The accurate estimation of the contact resistance of Ti/HfS2 contact was difficult for this device. According to the maximum value of ID and applied VDS, on resistance was 2.7 kΩ·μm at most. The on resistance is comparable to the typical contact resistance of other many materials. Further evaluations and improvements is required to verify the potential of the HfS2 as the channel material.
In conclusion, we have demonstrated the fabrication and I–V characteristics of few layer HfS2 FETs. Mechanical exfoliation using scotch tape provided an atomically thin HfS2 single-crystal layer with reasonable Raman spectrum and optical contrast with several number of layers. For a channel thickness of 3.8 nm and back gate bias, robust saturation behaviour and a drain current of 0.2 μA/μm were observed with high on/off current ratio (>104). Moreover, EDL gate operation obtained the significant increase of the drain current (~0.75 mA/μm). This improved property seemed to indicate the intrinsic performance of HfS2. These results provided basic information of HfS2 as electron devices and the attractive properties considered as significant for ultra-low power applications were experimentally demonstrated.
Materials and Methods
Initially, 75-nm-thick Al2O3 was deposited on p++-Si (ρ < 0.001 Ω∙cm) by thermal atomic layer deposition system (Ultratech/Cambridge Nanotech Savannah S100) as a back-gate insulator. Next, HfS2 flakes were mechanically exfoliated from the highly oriented crystal with high purity (99.995%, HQ Graphene) using the scotch tape method and transferred on the Al2O3 surface. The Al2O3 surface was passivated by HMDS to prepare a hydrophobic surface suitable for bonding with HfS2 (please see supplementary Information Fig. S2). In this study, the exfoliated HfS2 flakes for both the channel and contact regions were not intentionally doped. After the optical identification of the transferred flakes, the alignment exposure of the source and drain electrodes was carried out by electron beam (EB) lithography (Crestec CABL-9000) using PMMA (polymethyl methacrylate). Then, Ti(20 nm)/Au(100 nm) were EB-evaporated and lifted off. Finally, back-gate contact was formed by EB evaporation of Cr (20 nm) and Au (100 nm).
The thickness of the HfS2 thin films were evaluated by AFM (Veeco Nanoscope III). All DC characteristics reported in this letter were measured by an Agilent 4155B semiconductor parameter analyser.
How to cite this article: Kanazawa, T. et al. Few-layer HfS2 transistors. Sci. Rep. 6, 22277; doi: 10.1038/srep22277 (2016).
Dennard, R. H. et al. Design of ion-implanted MOSFET’s with very small physical dimensions. IEEE J. Solid-State Circuits SC-9, 256–268 (1974).
Fjeldly, T. A. & Shur, M. Threshold Voltage Modeling and the Subthreshold Regime of Operation of Short-Channerl MOSFETs. IEEE Trans. Electron Devices 40, 137–143 (1993).
Uchida, K. & Takagi, S. Carrier scattering induced by thickness fluctuation of silicon-on-insulator film in ultrathin-body metal–oxide–semiconductor field-effect transistor. Appl. Phys. Lett. 82, 2916–2918 (2003).
Kim, S. H. et al. Experimental study on electron mobility in InxGa1–xAs-on-insulator metal–oxide–semiconductor field-effect transistors with in content modulation and MOS interface buffer engineering. IEEE Trans. Nanotechnology 12, 621–628 (2013).
Lee, C. H. et al. Characterization of electron mobility in ultrathin body germanium-on-insulator metal-insulator-semiconductor field-effect transistors. Appl. Phys. Lett. 102, 232107 (2013).
Jin, S., Fischetti, M. V. & Tang, T.-W. Modeling of surface-roughness scattering in ultrathin-body SOI MOSFETs. IEEE Trans. Electron Devices 54, 2191–2203 (2007).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Han, M. Y., Özyilmaz, B., Zhang, Y. & Kim, P. Energy band-gap engineering of graphene nanoribbons. Phys. Rev. Lett. 98, 206805 (2007).
Zhang, Y. et al. Direct observation of a widely tunable bandgap in bilayer graphene. Nature 459, 820–823 (2009).
Wu, Y. et al. High-frequency, scaled graphene transistors on diamond-like carbon. Nature 472, 74–78 (2011).
Wang, H., Wu, Y., Cong, C., Shang, J. & Yu, T. Hysteresis of electronic transport in graphene transistors. ACS Nano 4, 7221–7228 (2010).
Xia, F., Farmer, D. B., Lin, Y. & Avouris, P. Graphene field-effect transistors with high on/off current ratio and large transport band gap at room temperature. Nano Letters 10, 715–718 (2010).
Chang, T. Y., Chen, J., Ko, P. K. & Hu, C. The impact of gate-induced drain leakage current on MOSFET scaling. IEDM Tech. Dig.1987, 718–721.
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nature Nanotech. 6, 147–150 (2011).
Kim, S. et al. High-mobility and low-power thin-film transistors based on multilayer MoS2 crystals. Nature Comm. 3, 1011 (2012).
Fang, H. et al. High-Performance Single Layer WSe2 p-FETs with Chemically Doped Contacts. Nano Lett. 12, 3788–3792 (2012).
Liu, W. et al. Role of metal contacts in designing high-performance monolayer n-type WSe2 field effect transistors. Nano Letters 13, 1983–1990 (2013).
Liu, H. et al. Phosphorene: An unexplored 2D semiconductor with a high hole mobility. ACS Nano 8, 4033–4041 (2014).
Li, L. et al. Black phosphorus field-effect transistors. Nature Nanotech. 9, 372–377 (2014).
Conroy, L. E. & Park, K. C. Electrical properties of the Group IV disulfides, titanium disulfide, zirconium disulfide, hafnium disulfide and tin disulfide. Inorg. Chem. 7, 459–463 (1968).
Wieting, T. J. Electrical conductivity of thin single crystals of the IVB–VIB dichalcogenides. J. Phys. and Chem. of Solids 31, 2148–2151 (1970).
Zhang, W., Huang, Z., Zhang, W. & Li, Y. Two-dimensional semiconductors with possible high room temperature mobility. Nano Research 7, 1731–1737 (2014).
Gong, C. et al. Band alignment of two-dimensional transition metal dichalcogenides: Application in tunnel field effect transistors. Appl. Phys. Lett. 103, 053513 (2013).
Li, X. et al. Intrinsic electrical transport properties of monolayer silicon and MoS2 from first principles. Phys. Rev. B 87, 115418 (2013).
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nature Chem. 5, 263–275 (2013).
Natori, K. Ballistic metal-oxide-semiconductor field effect transistor. J. Appl. Phys. 76, 4879–4890 (1994).
Cingolani, A., Lugarà, M. & Lévy, F. Resonance Raman scattering in HfSe2 and HfS2 . Physica Scripta 37, 389–391 (1988).
Blake, P. Making graphene visible. Appl. Phys. Lett. 91, 063124 (2007).
Castellanos-Gomez, A., Agraı``t, N. & Rubio-Bollinger, G. Optical identification of atomically thin dichalcogenide crystals. Appl. Phys. Lett. 26, 1445–1458 (1965).
Greenaway, D. L. & Nitsche, R. Preparation and optical properties of Group IV–VI2 chalcogenides having the CdI2 structure. J. Phys. Chem. Solids 96, 213116 (2010).
Kanazawa, T. et al. Fabrication of Thin-Film HfS2 FET. Proc. Device Research Conf. 217–218 (2015).
Fujimoto, T. & Awaga, K. Electric-double-layer field-effect transistors with ionic liquids. Phys. Chem. Chem. Phys. 15, 8983 (2013).
Zhang, Y., Ye, J., Matsuhashi, Y. & Iwasa, Y. Ambipolar MoS2 Thin Flake Transistors. Nano. Lett. 12, 1136 (2012).
The authors would like to thank Prof. M. Watanabe for the advice and support on AFM measurement and S. Tamura for the technical support with the electron-beam lithography. This work was supported by Strategic Information and Communications R&D Promotion Programme (SCOPE) of Ministry of Internal Affairs and Communications (MIC).
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Kanazawa, T., Amemiya, T., Ishikawa, A. et al. Few-layer HfS2 transistors. Sci Rep 6, 22277 (2016). https://doi.org/10.1038/srep22277
Nano Research (2022)
npj 2D Materials and Applications (2021)
Journal of Electronic Materials (2019)
Synthesis of 2D transition metal dichalcogenides by chemical vapor deposition with controlled layer number and morphology
Nano Convergence (2018)
High-pressure Raman scattering in bulk HfS2: comparison of density functional theory methods in layered MS2 compounds (M = Hf, Mo) under compression
Scientific Reports (2018)