Abstract
Titanium dioxide (TiO2) nanotubes are promising for a wide variety of potential applications in energy, biomedical and environmental sectors. However, their low mechanical strength and wide band gap limit their widespread technological use. This article reports our recent efforts to increase the mechanical strength of TiO2 nanotubes with lowered band gap by immobilizing a peptide of D-amino K122-4 (D) onto the nanotubes. Topographies and chemical compositions of the peptide-coated and uncoated TiO2 nanotubular arrays were characterized by scanning electron microscopy and X-ray photoelectron spectroscopy (XPS). Properties of the peptide-coated and uncoated TiO2 nanotubular arrays, including hardness, elastic modulus, electron work function and photocurrent, were evaluated using micromechanical probe, Kelvin Probe and electrochemical system. Effect of the peptide on surface conductivity was also investigated through current mapping and I–V curve analysis with conductive atomic force microscopy. It is demonstrated that the peptide coating simultaneously enhances the mechanical strength, photocatalytic and electrical properties of TiO2 nanotubes.
Similar content being viewed by others
Introduction
Titanium dioxide nanotubes (TNTs) have demonstrated great potential for applications in various technical fields, e.g., environmental purification, photocatalysts, gas and humidity sensor and solar energy conversion, etc.1,2,3,4,5,6,7,8. However, low mechanical strength and brittleness as well as wide band gap impair their feasibility for widespread technological use. Many efforts have been made to improve the photocatalytic activity of TiO2 nanotubes through element doping and utilizing different fabrication methods8,9,10,11,12,13,14,15,16. However, the work on the mechanical behavior of TiO2 nanotubes is rather limited, though some relevant studies have been reported in the literature17,18,19,20. No effective systems and methods have been developed to fabricate TiO2 nanotubes with simultaneously improved mechanical strength, photocatalytic activity and electrical properties.
Here, we demonstrate a new approach to simultaneously improve the mechanical strength, photocatalytic and electrical properties of TiO2 nanotubes by incorporating TiO2 nanotubes with a peptide of D-amino K122-4 (D)21,22, which was fabricated by solid-phase peptide synthesis and purified with reversed-phase high-performance liquid chromatography (HPLC). Previous work23,24 demonstrated that this peptide interacted with the stainless steel surface and affected its surface electron state and consequently the mechanical strength and other properties such as the antibacterial capability. It was observed that the peptide-modified 304 steel surfaces were considerably harder than untreated ones23. This synthesized peptide constitutes the self-organizing or folding PilA receptor binding domain (RBD)–(a synthetic peptide consisting of residues 128–144 from Pseudomonas aeruginosa with a formed disulfide bridge) and displayed a remarkably high apparent binding affinity for steel. The chiral form of amino acids (the D-enantiomeric form) has been used to overcome protease sensitivity of peptides such that they can be used for clinical applications. D-amino acid residues can be incorporated into the peptide at protease cleavage sites to prevent the recognition of the peptide by proteases.
Effects of the peptide immobilized on TiO2 nanotubular arrays on their properties were evaluated, including surface hardness, elastic modulus, electron work function (EWF), photocurrent and conductivity.
Results and Discussion
Surface characterization
Figure 1 illustrates the top views and cross-sectional view of TiO2 nanotubular arrays before (Fig. 1a) and after (Fig. 1b) being coated with the peptide observed by SEM. The average outer diameter of the uncoated TiO2 nanotubes is about 100 nm and the wall thickness is approximately 10 nm. The average outer diameter and wall thickness of the peptide-coated TiO2 nanotubes are similar to those of the uncoated ones but the inner diameter is slightly smaller than that of the uncoated nanotubes after the peptide was coated, indicating that the peptide coating is quite thin. These results were expected, as the peptide itself is only several Angstroms in size and previous work has shown that a concentration of 10 ug/mL of peptide saturates surfaces and analysis of coated surfaces by AUGER-SEM suggested a uniform distribution of the peptide on the surface23.
XPS analysis was carried out to analyze changes in surface composition caused by the peptide coating. From obtained XPS spectra shown in Figs 2, 3, 4, clear nitrogen, sulfur and phosphorus were detected on the peptide-coated TiO2 nanotubular arrays, in comparison with the uncoated TiO2 nanotubular arrays. Quantitative XPS analysis showed 3.03% of N, 0% of S and P (i.e. no S and P) and 96.97% of Ti (Ti 2p spectrum is not shown) in the uncoated TiO2 nanotubular arrays. In comparison, the peptide-coated ones have higher concentrations of nitrogen, sulfur and phosphorus, which are 6.14% of N, 0.86% of S, 3.32% of P, respectively. Moreover, the atomic concentration ratio of nitrogen to titanium of the peptide-coated TiO2 nanotubular arrays (N/Ti = 1:10) is much higher than that of the uncoated ones (N/Ti = 1:33), meaning that the nitrogen content was significant increased as the peptide was coated. This confirms that the peptide was immobilized on the TiO2 nanotubes, since nitrogen is one of major elemental components of the peptides. Besides, the peptide has two cysteine amino acids which contain sulfur, forming a disulphide bridge, whereas the titanium should not contain sulfur, suggesting that the detected sulfur comes from the peptide immobilized on the surface. Although the peptide does not contain any phosphorus, phosphate-buffered saline (PBS) was used to dissolve the peptide which may explain why the element P was present on the peptide-coated nanotubes. Thus, we conclude that the peptide was indeed immobilized on the TiO2 nanotubes. It needs to be indicated that, XPS spectra of other elements such as oxygen, titanium and carbon in the peptide-coated and non-coated TiO2 nanotubes were also obtained. Since little changes are observed in terms of the intensity distribution and corresponding electronic state (their XPS spectra are therefore not provided here), the peptide should be simply bound to the surface of nanotubes.
Hardness and Young’s modulus
A micromechanical probe was used to evaluate effects of the coated peptide on hardness and Young’s modulus of the nanotubular arrays under a small load of 25 mN. Values of hardness and Young’s modulus were obtained from the load-indentation depth curve, automatically calculated by the micro-indentation system with WIN-HCU® software, which used Oliver-Pharr model to analyze the obtained load-depth curve. Results of the experiment demonstrated that hardness of the peptide-coated nanotubular arrays was 2.6 times as large as that uncoated TiO2 nanotubular arrays, as shown in Fig. 5. It is obvious that the peptide effectively strengthened the TiO2 nanotubular arrays. Figure 6 illustrates load-depth curves of peptide-coated nanotubes and uncoated TiO2 nanotubes, from which their elastic moduli were determined. Young’s modulus of the peptide-coated nanotubular arrays was 1.63 times as large as that of the uncoated ones. TiO2 nanotubes are brittle in nature and have low resistance to external force. When subjected to indentation, the nanotubes collapse and cause permanent damage accompanied with a larger irreversible indentation depth, leading to not only low apparent hardness but also low apparent elastic modulus. When the nanotubes were coated with the peptide, this polymeric substance played a role as a binder, which strengthened the brittle nanotubes with elevated toughness. As evidenced by the indentation tests, the peptide coating clearly improved the mechanical behavior of the TiO2 nanotubular arrays and corresponding resistance to indentation.
Effects of the peptide on EWF and photocurrent of TiO2 nanotubular arrays
Changes in the electron work function (EWF) of peptide-coated and uncoated TiO2 nanotubular arrays under illumination were monitored (Fig. 7). The presented are values relative to that of Au as a reference (5.1 meV) rather than absolute EWF values. The work function is the minimum energy required to move electrons from inside a solid at Fermi level to its surface without kinetic energy. This parameter is a measure of the electron activity. As illustrated in Fig. 7, the EWF of the peptide-coated TiO2 nanotubes is lower than that of the uncoated nanotubes, indicating that the coated nanotubes are more electrically active than the uncoated ones. As shown, when the illumination was turned on, EWFs of both samples decreased and the peptide-coated nanotubes decreased more than the uncoated ones. This suggests that the peptide enhanced the sensitivity of the nanotubes and facilitated the photon-induced electron excitation. The excitation of electrons in TiO2 nanotubes is an electron-hole separation process; facilitation of the electron-hole separation by the peptide benefits the photocatalytic capability of the TiO2 nanotubes.
The beneficial effect of the peptide on the efficiency of photon-induced electron excitation is further confirmed by observed difference in photocurrent between the peptide-coated and unmodified TiO2 nanotubes. We measured their photocurrents under pulsed irradiation of UV-vis light. Induced photocurrents of both peptide-coated and uncoated TiO2 nanotubes well respond to the pulse UV-vis light. As shown in Fig. 8, the peptide-coated TiO2 nanotubes exhibited stronger photocurrent than the uncoated nanotubes, which is consistent with the result of EWF measurement. The peak photocurrent of the peptide-coated TiO2 nanotubes is about 15% higher than that of the uncoated ones, resulting from easier photo-induced electron excitation. In order to evaluate the stability of the photocurrent response, we performed the same tests for the samples after 5, 10, 20 and 25 days, respectively. It is interesting to observe that the ratio of photocurrent of the peptide-coated TiO2 nanotubes to that of uncoated ones increased with time from 1.15:1 to 2.2:1. The increase in the ratio is rapid initially and slows down, which should approach a saturated value as the time is prolonged. It is unclear why photocurrent ratio increased with time. The peptide is very stable. D-amino acid residue containing peptides are observed naturally in a variety of bacterial cell walls and an interesting study looked at the half-life of those peptides in ocean sediment and found that it was extremely long, in the order of 100,000 plus years in a variety of ocean sediments where the dead bacteria had sedimented. Thus, we suspect the increased current flow may reflect a conformational shift of the peptide over time of exposure to the light source. Certain 3-dimensional shapes of the peptide when bound to the substrate are present and that accumulated energy state of the metal surface due to light exposure will begin to accumulate a structure that is less abundant in lower energy states. The higher energy state of the peptide conformation then likely has a higher efficiency of electron release which is then observed as an increase in current flow but this should stabilize at a certain stage. Further studies are needed in order to understand the observed phenomenon.
Current measurements and I-V characteristics
To further investigate and understand the effects of the peptide on TiO2 nanotubes, we measured the electrical conductance of the coated and uncoated TiO2 nanotubes using a multimode AFM. Figure 9 illustrates topographical images and representative line-scanned current profiles of the peptide-coated and uncoated TiO2 nanotubular arrays, which show that the peptide-coated TiO2 nanotubes have a larger current than the untreated ones at the same applied tip bias (Fig. 9(b,d)), i.e. the peptide-coated nanotubes are more electrically conductive than the uncoated ones. The average current of the peptide-coated nanotubes is about 0.3 nA, while that of the uncoated nanotubes is about 0.1 nA.
To better understand the electric characteristics of the peptide-coated and uncoated nanotubes, their I-V curves were measured and are illustrated in Fig. 10. The I-V curves demonstrate that the peptide-coated nanotubes have a higher conductivity than the uncoated ones, which is consistent with the current profiles shown in Fig. 9(b,d). The width of the zero-current region on the I-V curve of the peptide-coated nanotubes is about 1.8 eV, which is markedly smaller than that of the uncoated nanotubes (about 2.7 eV), as shown in Fig. 10. The zero-current region corresponds to the energy band gap, which is in good agreement with values of TiO2 nanotubes obtained using other techniques such as photoemission, UV absorption spectroscopy and calculation using the ab initio method25,26,27. The band gap energy (zero-current region width) of the uncoated TiO2 nanotubes extracted from I-V curve is consistent with values reported in the literature. Thus, the reduction of band gap energy of TiO2 nanotubes down to 1.8 eV by the peptide coating can be confirmed. The lower band gap of the peptide-coated nanotubes may explain why the paptide-coated nanotubes are more electrically conductive (see Fig. 9) and easier to be exited, as shown by the larger decrease in electron work function of the peptide-coated nanotubes under illumination (Fig. 7). As for the mechanism responsible for the effect of the peptide on band gap reduction, this could be related to fact that peptides are enriched in charged amino acids28,29,30. However, further studies are needed.
Remark comments
Our original expectation is to mechanically strengthen the TiO2 nanotubes using the transparent peptide without deteriorating their photocatalytic properties. It is surprising to observe that the peptide does not only mechanically strengthen the TiO2 nanotubes but also enhances their photocatalytical activity with reduced band gap and elevated surface conductivity. The reduced band gap promotes the electron-hole separation and the higher surface conductivity facilitates charge transfer, thus reducing the chance for electron-hole recombination, leading to enhanced photocatalytic activity, which would benefit other related properties such as antimicrobial and pollutant degradation capabilities.
Conclusions
TiO2 nanotubes are not mechanically strong (brittle) for feasible applications. In order to improve their mechanical strength, a transparent peptide of D-amino K122-4 (D) was coated on fabricated TiO2 nanotubular arrays, which effectively strengthen TiO2 nanotubes with considerably increased hardness, elastic modulus and resistance to indentation. Unexpectedly, it was observed that the peptide-coated nanotubes exhibited markedly increased photocatalytic activity with higher photocurrent, lower electron work function, higher surface conductivity and smaller band gap. Such improvements would render the peptide coating as an effective modifier to TiO2 nanotubular arrays not only for enhanced mechanical durability but also improved photocatalytic and electrical properties.
Methods
TiO2 nanotubes fabrication
Highly ordered TiO2 nanotubular arrays were fabricated through potentiostatic anodization in a conventional two-electrode electrochemical cell at room temperature. A 0.2 mm thick titanium foil of 20 mm × 20 mm was used as the anode and a platinum foil of 10 mm × 10 mm served as the cathode. The distance between the anode and the cathode was about 20 mm. The anodization was carried out under 50 V using a DC power supply for 1 h. Prior to anodization, titanium foils were soaked in a solution HF, HNO3 and H2O (1:3:10) for 40 s to remove the oxide layer on the surface. The electrolyte was composed of 0.25 wt% NH4F, 2.0 vol% H2O and ethylene glycol. The as-prepared TiO2 nanotubular arrays were finally annealed at 450 °C for 2 h in a tube furnace with a heating/cooling rate of 1 °C·min−1 in the air atmosphere.
Immobilization of peptide on TiO2 nanotubes
The TiO2 nanotubular arrays were coated with the D-amino K122-4 (D) peptide. The D-peptide ACTSNADNKYLPKTCQT-amide peptide, corresponding to amino acids 128-144 of the PilA receptor binding domain of Pseudomonas aeruginosa strain K122-4 was synthesized, by solid-phase peptide synthesis and purified with reversed-phase high-performance liquid chromatography (HPLC) as previously described by Wong et al.21,22. The disulphide bridge form of the peptide used in this study was generated by air-oxidization23. Purity of the peptide was verified by HPLC analysis and mass spectroscopy. Purity of the peptide was greater than 95%. The peptide was synthesized by the Peptide and Protein Chemistry Core Facility of the University of Colorado Health Sciences Center and reconstituted in phosphate buffered saline (PBS), pH 7.4. During the peptide coating process, the TiO2 nanotubular arrays were immersed in 95% EtOH for 15 min at room temperature with gentle agitation, the samples were then cleaned with acetone and gently shaken for 1 min and finally washed with water and air dried. The cleaned samples were immersed into a 10 ug·mL−1 peptide MeOH solution for 1 h at room temperature with gentle agitation. After air drying, the samples were stored at room temperature for weeks. When necessary, the samples were rinsed with distilled water, or any concentration of MeOH or EtOH.
Surface characterization
A JEOL JSM6301FXV scanning electron microscope (SEM) with a field emission electron source running a 5 KV was used for the microstructure characterization of the TiO2 nanotubular arrays with and without the peptide coating. Chemical state analysis of the samples was carried out with X-ray photoelectron spectroscopy (XPS) using a Kratos AXIS Ultra X-ray photoelectron spectrometer. A monochromatic Al source, operating at 210 W with a pass energy of 20 eV and a step of 0.1 eV, was utilized. All XPS spectra were obtained using the C1s line at 284.6 eV.
Properties characterization
Microhardness of as-fabricated TiO2 nanotubular arrays with and without the coated peptide was determined using a micromechanical probe (Fischer Technology Ltd, Winsor, CT) under a small load of 25 mN. Each reported hardness value is an average of at least five measurements. Young’s modulus was determined from the load-unload curves recorded during the microindentation test.
Electron work function (EWF) of the samples was determined using a scanning Kelvin Probe (SKP 5050, KP Technology, UK). The suspension system produces oscillations with amplitudes in the range of 1–2 mm, permitting a standoff distance, which is regulated in the region 0.1–1.0 mm, ensuring that tip-to-sample contact does not occur.
Photocurrents of the samples were measured using a commercial electrochemical system. A standard three-electrode system with a platinum foil as the counter electrode and a saturated calomel electrode (SCE) as the reference electrode was used. The electrolyte was a 0.5 mol·L−1 Na2SO4 aqueous solution and the potential used for the electrochemical analysis was set as 0.1 V vs SCE. A lamp power supply (LPS-220B, Photon Technology International, NJ, USA) was used as the light source for the photocurrent measurement.
The conductivities of TiO2 nanotubes with and without the coated peptide were measured using Agilent 5500 AFM (Agilent Technologies, USA) operated in the current sensing mode. In addition to topography and current maps, current-voltage (I-V) curves were acquired. Both current and I-V measurements were carried out in the ambient environment with its relative humidity around 25%.
Additional Information
How to cite this article: Guo, L. Q. et al. Incorporating TiO2 nanotubes with a peptide of D-amino K122-4 (D) for enhanced mechanical and photocatalytic properties. Sci. Rep. 6, 22247; doi: 10.1038/srep22247 (2016).
References
Burnside, S. D. et al. Self-organization of TiO2 nanoparticles in thin films. Chem. Mater. 10, 2419–2423 (1998).
Kato, K. et al. TiO2 coating photocatalysts with nanostructure and preferred orientation showing excellent activity for decomposition of aqueous acetic acid. Mater. Sci. Lett. 15, 913–917 (1996).
Enright, B. & Fitzmaurice, D. Spectroscopic determination of electron and hole effective masses in a nanocrystalline semiconductor film. J. Phys. Chem. 100, 1027–1033 (1996).
Caruso, R. A. et al. Modification of TiO2 network structures using a polymer gel coating technique. Chem. Mater. 13, 1114–1119 (2001).
Kasuga, T., Hiramatsu, M., Hoson, A., Sekino, T. & Niihara, K. Formation of titanium oxide nanotube. Langmuir. 14, 3160–3166 (1998).
Imai, H., Takei, Y., Shimizu, K., Matsuda, M. & Hirashima, H. Direct preparation of anatase TiO2 nanotubes in porous alumina membranes. J. Mater. Chem. 9, 2971–2977 (1999).
Imai, H., Matsuda, M., Shimizu, K., Hirashima, H. & Negishi, N. Preparation of TiO2 fibers with well-organized structures. J. Mater. Chem. 10, 2005–2011 (2000).
Kumar, P. M., Badrinarayanan, S. & Sastry, M. Nanocrystalline TiO2 studied by optical, FTIR and X-ray photoelectron spectroscopy: correlation to presence of surface states. Thin Solid Films. 358, 122–127 (2000).
Nukumizu, K., Nunoshige, J. & Domen, H. TiNxOyFz as a stable photocatalyst for water oxidation in visible light (<570nm). Chem. Lett. 32, 196–199 (2003).
Burda, C., Lou, Y. B. & Gole, J. L. Enhanced nitrogen doping in TiO2 nanoparticles. Nano. Lett. 3, 1049–1054 (2003).
Hattori, A. & Tada, H. High photocatalytic activity of F-doped TiO2 film on glass. J. Sol-Gel Sci. Technol. 22, 47–53 (2001).
Chen, X., Zhang, X., Su, Y. & Lei, L. Preparation of visible-light responsive P-F-codoped TiO(2) nanotubes. Appl. Surf. Sci. 254, 6693–6698 (2008).
Hahn, R., Ghicov, A., Salonen, J., Lehto, V. P. & Schmuki, P. Carbon doping of self-organized TiO2 nanotube layers by thermal acetylene treatment. Nanotechnology. 18, 105604–105609 (2007).
Lu, N. et al. Fabrication of boron-doped TiO2 nanotube array electrode and investigation of its photoelectrochemical capability. J. Phys. Chem. C. 111, 11836–11842 (2007).
Hoyer, P. & Masuda, H. Electrodeposited nanoporous TiO2 film by a two-step replication process from anodic porous alumina. J. Mater. Sci. Lett. 15, 1228–1234 (1996).
Chu, S. Z. et al. Fabrication and characteristics of ordered Ni nanostructures on glass by anodization and direct current electrodeposition. Chem. Mater. 14, 4595–4602 (2002).
Chu, S. Z., Wada, K. J., Inoue, S. & Todoroki, S. I. Synthesis and characterization of titania nanostructures on glass by Al anodization and sol-gel process. Chem. Mater. 14, 266–272 (2002).
Crawforda, G. A., Chawlaa, N., Das, K., Bose, S. & Bandyopadhyay, A. Microstructure and deformation behavior of biocompatible TiO2 nanotubes on titanium substrate. Acta. Biomater. 3, 359–364 (2007).
Crawforda, G. A., Chawlaa, N. & Houstonb, J. E. Nanomechanics of biocompatible TiO2 nanotubes by Interfacial Force Microscopy (IFM). J. Mech. Behav. Biomed. 2, 580–585 (2009).
Tang, X. H. & Li, D. Y. Fabrication, Geometry and Mechanical Properties of Highly Ordered TiO2 Nanotubular Arrays. J. Phys. Chem. C. 113, 7107–7113 (2009).
Wong, W. Y. et al. Structure–function analysis of the adherence-binding domain on the pilin of Pseudomonas aeruginosa strains PAK and KB7. Biochemistry. 34, 12963–72 (1995).
Wong, W. Y., Irvin, R. T., Paranchych, W. & Hodges, R. S. Antigen–antibody interactions: elucidation of the epitope and strain-specificity of a monoclonal antibody directed against the pilin protein adherence binding domain of Pseudomonas aeruginosa strain K. Protein. Sci. 1(10), 1308–18 (1992).
Davis, E. M., Li, D. Y. & Irvin, R. T. A peptide–stainless steel reaction that yields a new bioorganic-metal state of matter. Biomaterials. 32(23), 5311–5319 (2011).
Davis, E. M. et al. Evidence of extensive diversity in bacterial adherence mechanisms that exploit unanticipated stainless steel surface structural complexity for biofilm formation. Acta Biomaterialia. 4, 6236–44 (2013).
Fu, N., Tang, X. H. & Li, D. Y. Is it effective to harvest visible light by decreasing the band gap of photocatalytic materials? Appl. Phys. Lett. 100, 093901–05 (2012).
Liu, Z. J., Zhang, Q. & Qin, L. C. Reduction in the electronic band gap of titanium oxide nanotubes. Solid. State. Commun. 141, 168–171 (2007).
Mohapatra, S. K., Misra, M., Mahajan, V. K. & Raja, K. S. A novel method for the synthesis of titania nanotubes using sonoelectrochemical method and its application for photoelectrochemical splitting of water. J. Catal. 246, 362–369 (2007).
Wang, S. et al. Peptides with selective affinity for carbon nanotubes. Nat. Mater. 2, 196–200 (2003).
Kase, D. et al. Affinity selection of peptide phage libraries against single-wall carbon nanohorns identifies a peptide aptamer with conformational variability. Langmuir. 20, 8939–8941 (2004).
Pender, M. J., Sowards, L. A., Hartgerink, J. D., Stone, M. O. & Naik, R. R. Peptide-mediated formation of single-wall carbon nanotube composites. Nano Lett. 6(1), 40–44 (2006).
Author information
Authors and Affiliations
Contributions
L.Q.G. and Y.W.H. carried out experiments to fabricate and characherize the TiO2 nanotubular arrays; E.D. and B.Y. prepared the peptide and coated it to the TiO2 nanotubular arrays; B.Y. and X.G.Y. provided assistance in mechanical testing and analysis. L.Q.G. analyzed the data and wrote the manuscript; R.I. and D.Y.L. edited and revised the manuscript and the latter conceived, planned and looked after the entire investigation. All authors reviewed the manuscript. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Guo, L., Hu, Y., Yu, B. et al. Incorporating TiO2 nanotubes with a peptide of D-amino K122-4 (D) for enhanced mechanical and photocatalytic properties. Sci Rep 6, 22247 (2016). https://doi.org/10.1038/srep22247
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep22247
This article is cited by
-
Strategies to improve photodynamic therapy efficacy by relieving the tumor hypoxia environment
NPG Asia Materials (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.