Abstract
The recently discovered oxypnictide superconductor SmFeAs(O,F) is the most attractive material among the Fe-based superconductors due to its highest transition temperature of 56 K and potential for high-field performance. In order to exploit this new material for superconducting applications, the knowledge and understanding of its electro-magnetic properties are needed. Recent success in fabricating epitaxial SmFeAs(O,F) thin films opens a great opportunity to explore their transport properties. Here we report on a high critical current density of over 105 A/cm2 at 45 T and 4.2 K for both main field orientations, feature favourable for high-field magnet applications. Additionally, by investigating the pinning properties, we observed a dimensional crossover between the superconducting coherence length and the FeAs interlayer distance at 30–40 K, indicative of a possible intrinsic Josephson junction in SmFeAs(O,F) at low temperatures that can be employed in electronics applications such as a terahertz radiation source and a superconducting Qubit.
Similar content being viewed by others
Introduction
Among the recently discovered Fe-based superconductors1, the highest superconducting transition temperature Tc of 56 K has been reported in SmFeAs(O,F)2. This new class of material shows very high upper critical fields at low temperatures together with a moderate anisotropy ranging from 4 to 73, which is suitable for high-field magnet applications. Hence several attempts on wire fabrication using SmFeAs(O,F) by powder-in-tube technique (PIT) have already been reported4, despite the lack of information on the field and orientation dependence of intra-grain critical current density [i.e., Jc(H, Θ)]. In order to exploit this material class, the knowledge of these properties should be clarified.
Epitaxial thin films are favourable for electronics device applications and investigating transport as well as optical properties thanks to their geometry. Recent success in fabricating epitaxial Fe-based superconducting thin films opens a great opportunity for investigating their physical properties and exploring possible superconducting applications. To date, high-field transport properties of Co-doped SrFe2As2 (Sr-122) and BaFe2As2 (Ba-122) and Fe(Se,Te) epitaxial thin films have been reported by several groups5,6,7. For Co-doped Ba-122, Jc performance can be tuned by introduction of artificial pinning centers and proton irradiation8,9. Additionally, multilayer approaches that can tailor superconducting properties and their anisotropy have been reported by Lee et al10. Furthermore, epitaxial Co-doped Ba-122 and Fe(Se,Te) thin films have been realised on ion beam assisted deposition MgO coated conductor templates11,12,13 and the rolling-assisted biaxially textured substrate14, respectively. Similarly, high performance K-doped Ba-122 and Sr-122 wires by PIT have been reported by Weiss et al.15 and Gao et al16, respectively. These results are very promising for realising Fe-based superconducting high-field applications. However, transport critical current properties of high-Tc (i.e., over 50 K) oxypnictide thin films have not been reported before due to the absence of high quality films. Recently, in situ prepared LnFeAs(O,F) (Ln = Nd and Sm) epitaxial thin films with Tc exceeding 50 K have been realised by molecular beam epitaxy (MBE)17,18. These successes give many possibilities to explore electro-magnetic properties.
In this paper, we report on various in – plane (i.e., current is flowing on the crystallographical ab-plane) transport properties up to 45 T of epitaxial SmFeAs(O,F) thin films grown by MBE on CaF2 (001) single crystalline substrates and discuss their pinning properties. A high Jc of over 105 A/cm2 was recorded at 45 T and 4.2 K for both crystallographic directions, which is favourable for high-field magnet applications. By analysing pinning properties the dimensional crossover between the out-of-plane superconducting coherence length ξc and the Fe-As interlayer distance dFeAs was observed at 30–40 K. This indicates the possible intrinsic Josephson junction in SmFeAs(O,F) at low temperatures.
Results
Microstructural analyses
As verified by x-ray diffraction, the biaxially textured SmFeAs(O,F) film with a narrow full width at half maximum (FWHM) of less than 0.65° was obtained (See in Supplementary Fig. S1). As shown in Fig. 1a, trapezoid shaped Sm(O,F) cap layers, which are changed from SmF3, are aligned discontinuously. Additionally, a crystallographically disordered layer with around 20 nm thickness as indicated by the arrows is present between Sm(O,F) cap and SmFeAs(O,F) layers. Relatively dark particles are observed in the SmFeAs(O,F) matrix, which are identified as iron-fluoride, presumably FeF2, by elemental mappings shown in Figs. 1b and 1c. This is due to the excess of Fe supplied during the film growth.
Compared to Fe(Se,Te)19 and Co-doped Ba-122 films20 grown by pulsed laser deposition, a relatively sharp and clean interface is observed between SmFeAs(O,F) and CaF2 substrate, as shown in Fig. 1d. Furthermore, SmFeAs(O,F) layers contained neither correlated defects nor large angle grain boundaries (GBs).
Resistivity measurements up to 45 T
The superconducting transition temperature Tc,90 defined as 90% of the normal state resistivity is 54.2 K in zero magnetic field. Figures 2a and 2b show the Arrhenius plots of resistivity for both crystallographic directions measured in static fields up to 45 T. For both directions the Tc,90 is shifted to lower temperature with increasing H, as shown in the inset of Fig. 2b. The respective Tc,90 at 45 T for H || c and || ab are 44.9 K and 49.9 K. Significant broadening of the transition is observed for H || c, which is reminiscent of high-Tc cuprates. Such broadening of the transition originates from enhanced thermally activated vortex motion for H || c. In contrast, the in-field Tc,90 as well as its transition width for H || ab are less affected by H than that for H || c.
The activation energy U0(H) for vortex motion can be estimated by the model of thermally activated flux flow21. On the assumption that U(T, H) = U0(H)(1 − T/Tc), we obtain lnρ(T, H) = lnρ0(H) − U0(H)/T and lnρ0(H) = lnρ0f + U0(H)/Tc, where ρ0f is the prefactor. In Figs. 2a and 2b, the slope of linear fits corresponds to the U0 for vortex motion. Figure 2c shows U0 as a function of H for both major directions. It can be seen that U0(H) shows a power law [i.e., U0(H) ~ H−α] for both crystallographic directions. In the range of 1 < μ0H < 8 T, α = 0.46 is observed for H || c, whilst a similar field dependence of U0(H) reaches 20 T for H || ab. In higher fields U0 for H || ab shows a weak H dependence. On the other hand, α = 1.2 is obtained for H || c in the range of 8 < μ0H < 45 T, which is close to 1, suggesting a crossover from plastic to collective pinning at around μ0H ~ 8 T22.
Figure 2d shows the relationship between lnρ0 and U0 for H || c and || ab. The linear fitting for H || c yields Tc = 53.4 ± 0.2 K, whilst the corresponding value for H || ab is Tc = 53.5 ± 0.2 K. Both Tc values are equal within error and close to Tc,90. This perfect linear scaling is due to the correct assumption that both U(T, H) = U0(H)(1 − T/Tc) and ρ0f = const. conditions are satisfied in a wide temperature range in Figs. 2a and 2b.
In-field Jc performance
The field dependence of Jc at 4.2 K for both principal crystallographic directions measured up to 45 T is displayed in Fig. 3a. Jc for is lower than that for , which is a consequence of moderate anisotropy of SmFeAs(O,F). This tendency is observed for all temperature regions (see Supplementary Fig. S2). It is worth mentioning that a of over 105 A/cm2 was recorded even at 45 T, which is favourable for high-field magnet applications.
is observed to decrease gradually with H and it shows an almost constant value of 7.4 × 105 A/cm2 for μ0H > 28 T. This behaviour can be explained by a combination of extrinsic (i.e., normal precipitates and stacking faults) and intrinsic pinning, which is a similar observation in quasi two-dimensional (2D) system YBa2Cu3O7−δ [i.e., , where ξc(0) is the out-of-plane superconducting coherence length at zero temperature and is the interlayer distance between CuO2 planes]23. SmFeAs(O,F) is an alternating structure of SmO and FeAs layers, similarly to high-Tc cuprates. Additionally, ξc(0) is shorter than the interlayer distance between Fe-As planes dFeAs. Hence, modulation of superconducting order parameter along the crystallographic c-axis (i.e., intrinsic pinning) is highly expected in SmFeAs(O,F). In fact the extrinsic pinning is dominant up to 28 T, whereas the intrinsic pinning overcomes the extrinsic one above 28 T. The estimation of ξc(0) and dFeAs in our SmFeAs(O,F) case will be discussed later.
By analysing the E-J curves from which Jc was determined, we obtain the information on the pinning potential. On the assumption of a logarithmic current dependence of the pinning potential Up for homogeneous samples, E-J curves show a power-law relation E~Jn (n ~ Up/kBT, where kB is the Boltzmann constant)24. Hence Jc scales with n and indeed the field dependence of n has a similar behaviour to Jc(H) for H || c, as presented in Fig. 3b. For H || ab, n decreases with H up to 28 T, similarly to the Jc(H) behaviour, whereas at larger field it suddenly increases due to the dominating intrinsic pinning. Hence a failure to scale Jc with n or deviations as shown in Fig. 3c indicates the presence of intrinsic pinning.
The field dependence of the pinning force density Fp for both crystallographic directions at 4.2 K is summarised in Fig. 3d. An almost field independent Fp above 10 T for H || c is observed, whereas Fp for H || ab is still increasing up to the maximum field available.
Angular dependence of Jc
In order to gain a deeper insight into the flux pinning, the angular dependence of Jc [Jc(Θ), where Θ is the angle between H and the c-axis] was measured and summarised in Fig. 4. Figure 4a presents Jc(Θ) at 30 K in three different magnetic fields. Almost isotropic Jc(Θ, 2.5 T) of around 0.14 MA/cm2 was observed at angles Θ up to 75°. Similar isotropic behaviour is seen at 6 T. These results suggest the presence of c-axis correlated defects. However, the presence of these defects is ruled out by TEM investigation, since only relatively large FeF2 particles are observed in the SmFeAs(O,F) matrix. Recently, van der Beek et al. pointed out that defects of size larger than the out-of-plane coherence length contribute to c-axis pinning in anisotropic superconductors25. Additionally, the intrinsic pinning is active below T = 30 ~ 40 K, as shown below. Hence the combination of large particles and the intrinsic pinning may be responsible for this isotropic Jc(Θ).
For H || ab, a broad maximum of Jc is observed and this peak becomes sharper with increasing H (Fig. 4a). However, the corresponding n shows a broad minimum for H close to ab direction (Fig. 4b), which is opposite behaviour to Jc. This is due to the thermal fluctuation of Josephson vortices, which leads to flux creep. Here, the flux creep rate S = −dln(J)/dln(t) and the exponent n are related as S = 1/(n − 1)26. When the applied field is close to the ab-plane, a number of thermally fluctuated Josephson vortices are generated, leading to an increase in S. This could quantitatively explain a dip of n at around H close to ab. Similar behaviour has been observed in YBa2Cu3O7−δ thin films27,28,29 and Fe(Se,Te) thin films30. On the other hand, this dip of n disappears at 40 K, although the Jc still shows a broad maximum (Figs. 4c and 4d). Hence the activation temperature of the intrinsic pinning is between 30 and 40 K, which is in good agreement with the transition temperature between Abrikosov-and Josephson-like vortices in SmFeAs(O,F) single crystals31.
Figure 4e shows Jc(Θ) measured at 4.2 K in fields up to 40 T. A sharp peak is observed for H || ab with a Jc of around of 8 × 105 A/cm2. For 2D superconductors (e.g., Bi2Sr2CaCu2O8+x), the relation holds in the intrinsic pinning regime, whereas is field independent32,33. Thus, in this regime Jc(Θ, H) depends only on the field component along the c-axis. For our SmFeAs(O,F) thin film, the aforementioned condition is satisfied above 28 T at which the crossover field between extrinsic and intrinsic pinning is observed (see Fig. 3a). Hence, for Θ > 59° (sinΘ = 28/32.5 = 0.86, Θ = sin−1(0.86) = 59°) the ab component of the applied fields exceed 28 T, entering in the field-independent region. It means that both angular–Jc curves measured at 32.5 and 40 T rescale with H cosΘ, as shown in Fig. 4f.
Discussion
We estimate the ξc(0) by using Tcr = (1 − τcr)Tc, where Tcr is the dimensional crossover temperature and is the dimensionless ratio characterising the crossover from quasi-2D layered to continuous 3D anisotropic behaviour34. By substituting Tcr = 30–40 K and dFeAs = 0.858 nm from the x-ray diffraction shown in Supplementary Fig. S1, is calculated to 0.3~0.4 nm. The ratio ξc(0)/dFeAs = 0.35 ~ 0.47 explains the intrinsic pinning related to a quasi 2D system observed in this film. The relation yields ξab(0) = 1.7 ~ 2.2 nm, where γ is the effective-mass or resistivity anisotropy, which is about 30 at T = 0 K from measurements of the c-axis plasma frequency using infrared ellipsometry35. The evaluated superconducting coherence lengths for both crystallographic directions are in very good agreement with single-crystals values reported by Welp et al36.
The presence of a dimensional crossover indicates a possible intrinsic Josephson junction in SmFeAs(O,F), which can be used in superconducting electronics applications such as a terahertz radiation source and a superconducting Qubit37,38. Indeed, the intrinsic Josephson junction was reported for a PrFeAsO0.7 single crystal, where an s-shaped stack junction in c-direction was prepared by focused ion beam39.
For high-field magnet applications, a high Jc together with a low Jc anisotropy () in the presence of magnetic field is necessary. The present results are promising, since Jc is over 105 A/cm2 at 45 T for both crystallographic directions. Further increasing in Jc is possible, since the only appreciable defects in our SmFeAs(O,F) films are large FeF2 particles. Improved pinning performance and, as a consequence, larger Jc could be realised by incorporating artificial pinning centres similarly to Co-doped Ba-122 thin films reported by Tarantini et al8. Albeit the Jc anisotropy is increasing with H, this value is still low compared to high-Tc cuprtaes. For instance, Jc anisotropy is about 3.6 at 30 T and 4.2 K in SmFeAs(O,F), whereas the corresponding value in YBa2Cu3O7−δ is over 7, albeit the latter shows higher Jc than the former40.
PIT is a more realistic process than MBE for high-field magnet applications. High temperature heat treatment in PIT leads to a loss of F, however, this problem can be solved by employing a low temperature synthesis and ex-situ process with SmF3 containing binder as explained in refs. 41,42. Despite a high Tc of over 45 K for both SmFeAs(O,F) wires, self-field Jc shows only a few thousand A/cm2 at 4.2 K, which is presumably due to grain boundaries (GBs), poor grain connectivity and low density. Obviously these PIT processed wires contain a high density of large angle GBs. In the case of Co-doped Ba-122 GBs with misorientation angles above 9° seriously reduce the critical current43. However, PIT processed K-doped Ba-122 and Sr-122 wires showed a relatively high inter-grain Jc15,16. Clean GBs (i.e., no segregation of secondary phases around GBs), good grain connectivity and a low anisotropy may be responsible for these high performance wires. An approach similar to the one employed in K-doped Ba-122 and Sr-122 wires fabrication may be useful for improving inter-grain Jc in SmFeAs(O,F) wires as well. Nevertheless bicrystal experiments on SmFeAs(O,F) will give a valuable information on these issues.
To conclude, we have explored intrinsic electro-magnetic properties of epitaxial SmFeAs(O,F) thin films prepared by MBE on CaF2 (001) substrate by measuring field-angular dependence of transport properties up to 45 T. Our findings strongly support the presence of a competition behaviour between extrinsic pinning below 28 T and intrinsic pinning above 28 T. We also determined that the intrinsic pinning starts being effective below T = 30 ~ 40 K, at which the crossover between the out-of-plane coherence length and the interlayer distance occurs. This knowledge of SmFeAs(O,F) electro-magnetic properties could stimulate future development of superconducting applications of this class of material.
Methods
Epitaxial SmFeAs(O,F) film preparation by MBE
SmFeAs(O,F) films of 80 nm thickness have been grown in the customer-designed MBE chamber. A parent compound of SmFeAsO film was prepared on CaF2 (001) single crystalline substrate at 650°C, followed by the deposition of a SmF3 cap layer. Empirically, Fe-rich pnictide films fabricated by MBE showed high Jc values44. Hence a slight Fe excess was supplied during the growth of SmFeAsO layers. After the overlayer deposition, the sample was kept at the same temperature in the MBE chamber for 0.5 h for the purpose of F diffusion into the SmFeAsO layer. The detailed fabrication process can be found in ref. 17. SmFeAs(O,F) films are grown epitaxially with high crystalline quality confirmed by x-ray diffraction, which is summarised in Supplementary Fig. S1.
Microstructural analyses by TEM
A TEM lamella was prepared by means of focused ion beam. Microstructural analyses have been performed by using a JEOL TEM-2100F transmission electron microscope equipped with an energy-dispersive x-ray spectrometer.
In-plane transport properties measurement
A small bridge of 70 μm width and 0.7 mm length was fabricated by laser cutting. I-V characteristics on this sample were measured with four-probe configuration by a commercial physical property measurement system [(PPMS) Quantum Design] up to 12 T. Transport measurements up to 45 T were carried out in the high field dc facility at the National High Magnetic Field Laboratory (NHMFL) in Tallahassee, FL. A voltage criterion of 1 μV/cm was employed for evaluating Jc. The magnetic field H was applied in maximum Lorentz force configuration during all measurements (H ⊥ J, where J is current density).
References
Kamihara, Y., Watanabe, T., Hirano, M. & Hosono, H. Iron-Based Layered Superconductor La[O1−xFx]FeAs (x = 0.05–0.12) with Tc = 26 K. J. Am. Chem. Soc. 130, 3296–3297 (2008).
Ren, Z. A. et al. Superconductivity at 55 K in Iron-Based F-Doped Layered Quaternary Compound Sm[O1−xFx]FeAs. Chinese Phys. Lett. 25, 2215–2216 (2008).
Lee, H. et al. Effects of two gaps and paramagnetic pair breaking on the upper critical field of SmFeAsO0.85 and SmFeAsO0.8F0.2 single crystals. Phys. Rev. B 80, 144512 (2009).
Gao, Z. et al. Superconducting properties of granular SmFeAsO1−xFx wires with Tc = 52 K prepared by the powder-in-tube method. Supercond. Sci. Technol. 21, 112001 (2008).
Baily, S. A. et al. Pseudoisotropic Upper Critical Field in Cobalt-Doped SrFe2As2 Epitaxial Films. Phys. Rev. Lett. 102, 117004 (2009).
Hänisch, J. et al. Jc Scaling and Anisotropies in Co-Doped Ba-122 Thin Films. IEEE Trans. Appl. Supercond. 21, 2887–2890 (2011).
Tarantini, C. et al. Significant enhancement of upper critical fields by doping and strain in iron-based superconductors. Phys. Rev. B 84, 184522 (2011).
Tarantini, C. et al. Artificial and self-assembled vortex-pinning centers in superconducting Ba(Fe1−xCox)2As2 thin films as a route to obtaining very high critical-current densities. Phys. Rev. B 86, 214504 (2012).
Maiorov, B. et al. Competition and cooperation of pinning by extrinsic point-like defects and intrinsic strong columnar defects in BaFe2As2 thin films. Phys. Rev. B 86, 094513 (2012).
Lee, S. et al. Artificially engineered superlattices of pnictide superconductors. Nat. Mater. 12, 392–396 (2013).
Iida, K. et al. Epitaxial Growth of Superconducting Ba(Fe1−xCox)2As2 Thin Films on Technical Ion Beam Assisted Deposition MgO Substrates. Appl. Phys. Express 4, 013103 (2011).
Katase, T. et al. Biaxially textured cobalt-doped BaFe2As2 films with high critical current density over 1 MA/cm2 on MgO-buffered metal-tape flexible substrates. Appl. Phys. Lett. 98, 242510 (2011).
Si, W. et al. Iron-chalcogenide FeSe0.5Te0.5 coated superconducting tapes for high field applications. Appl. Phys. Lett. 98, 262509 (2011).
Si, W. et al. High current superconductivity in FeSe0.5Te0.5-coated conductors at 30 tesla. Nat. Commun. 4, 1347 (2013).
Weiss, J. D. et al. High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks. Nat. Mater. 11, 682–685 (2012).
Gao, Z. et al. High critical current density and low anisotropy in textured (Sr1−xKx)Fe2As2 tapes for high field applications. Sci. Rep. 2, 998 (2012).
Ueda, S., Takeda, S., Takano, S., Yamamoto, A. & Naito, M. High–Tc and high–Jc SmFeAs(O,F) films on fluoride substrates grown by molecular beam epitaxy. Appl. Phys. Lett. 99, 232505 (2011).
Uemura, H. et al. Substrate dependence of the superconducting properties of NdFeAs(O,F) thin films. Solid State Commun. 152, 735–739 (2012).
Tsukada, I. et al. Epitaxial Growth of FeSe0.5Te0.5 Thin Films on CaF2 Substrates with High Critical Current Density. Appl. Phys. Express 4, 053101 (2011).
Kurth, F. et al. Versatile fluoride substrates for Fe-based superconducting thin films. Appl. Phys. Lett. 102, 142601 (2013).
Palstra, T. T. M., Batlogg, B., Schneemeyer, L. F. & Waszczak, J. V. Thermally Activated Dissipation in Bi2.2Sr2Ca0.8Cu2O8+δ . Phys. Rev. Lett. 61, 1662–1665 (1988).
Yeshurun, Y. & Malozemoff, A. P. Giant Flux Creep and Irreversibility in an Y-Ba-Cu-O Crystal: An Alternative to the Superconducting-Glass Model. Phys. Rev. Lett. 60, 2202–2205 (1988).
Awaji, S., Watanabe, K. & Kobayashi, N. Crossover from intrinsic to extrinsic pinning for YBa2Cu3O7 . Cryogenics 39, 569–577 (1999).
Zeldov, E. et al. Flux creep characteristics in high–temperature superconductors. Appl. Phys. Lett. 56, 680–682 (1990).
van der Beek, C. J., Kończykowski, M. & Prozorov, R. Anisotropy of strong pinning in multi-band superconductors. Supercond. Sci. Technol. 25, 084010 (2012).
Yamasaki, H. & Mawatari, Y. Current-voltage characteristics and flux creep in melt-textured YBa2Cu3O7−δ . Supercond. Sci. Technol. 13, 202–208 (2000).
Civale, L. et al. Identification of Intrinsic ab-Plane Pinning in YBa2Cu3O7 Thin Films and Coated Conductors. IEEE Trans. Appl. Supercond. 15, 2808–2811 (2005).
Awaji, S. et al. Flux pinning properties of TFA-MOD (Y,Gd)Ba2Cu3Ox tapes with BaZrO3 nanoparticles. Supercond. Sci. Technol. 23, 014006 (2010).
Awaji, S. et al. Anisotropy of the Critical Current Density and Intrinsic Pinning Behaviors of YBa2Cu3Oy Coated Conductors. Appl. Phys. Express 4, 013101 (2011).
Iida, K. et al. Intrinsic pinning and the critical current scaling of clean epitaxial Fe(Se,Te) thin films. Phys. Rev. B 87, 104510 (2013).
Moll, P. J. W. et al. Transition from slow Abrikosov to fast moving Josephson vortices in iron pnictide superconductors. Nat. Mater. 12, 134–138 (2012).
Tachiki, M. & Takahashi, S. Anisotropy of critical current in layered oxide superconductors. Solid State Commun. 72, 1083–1086 (1989).
Schmitt, P., Kummeth, P., Schultz, L. & Saemann-Ischenko, G. Two-Dimensional Behavior and Critical-Current Anisotropy in Epitaxial Bi2Sr2CaCu2O8+x Thin Films. Phys. Rev. Lett. 67, 267–270 (1991).
Blatter, G., Feilgl'man, M., Geshkenbin, V. B., Larkin, A. I. & Vinokur, V. Vortices in high-temperature superconductors. Rev. Mod. Phys. 66, 1125–1388 (1994).
Dubroka, A. et al. Superconducting Energy Gap and c-Axis Plasma Frequency of (Nd,Sm)FeAsO0.82F0.18 Superconductors from Infrared Ellipsometry. Phys. Rev. Lett. 101, 097011 (2008).
Welp, U. et al. Anisotropic phase diagram and superconducting fluctuations of single-crystalline SmFeAsO0.85F0.15 . Phys. Rev. B 83, 100513(R) (2011).
Ozyuzer, L. et al. Emission of Coherent THz Radiation from Superconductors. Science 318, 1291–1293 (2007).
Kubo, Y. et al. Macroscopic Quantum Tunneling in a Bi2Sr2CaCu2O8+δ Single Crystalline Whisker. Appl. Phys. Express 3, 063104 (2010).
Kashiwaya, H. et al. C-axis critical current of a PrFeAsO0.7 single crystal. Appl. Phys. Lett. 96, 202504 (2010).
Xu, A. et al. Angular dependence of Jc for YBCO coated conductors at low temperature and very high magnetic fields. Supercond. Sci. Technol. 23, 014003 (2010).
Ma, Y. et al. Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes. IEEE Trans. Appl. Supercond. 21, 2878–2881 (2011).
Fujioka, M. et al. Effective Ex – situ Fabrication of F-Doped SmFeAsO Wire for High Transport Critical Current Density. Appl. Phys. Express 4, 063102 (2011).
Katase, T. et al. Advantageous grain boundaries in iron pnictide superconductors. Nat. Commun. 2, 409 (2011).
Sakagami, A. et al. Critical current density and grain boundary property of BaFe2(As,P)2 thin films. Physica C [Online early access], doi:10.1016/j.physc.2013.04.047 (2013).
Acknowledgements
The authors would like to thank M. Weigand and B. Maiorov of Los Alamos National Laboratory, D. C. Larbalestier of Applied Superconductivity Center, National High Magnetic Field Laboratory, Florida State University for fruitful discussions and comments, as well as M. Kühnel and U. Besold for their technical support. The research leading to these results has received funding from European Union's Seventh Framework Programme (FP7/2007-2013) under grant agreement number 283141 (IRON-SEA). A portion of this work was performed at the National High Magnetic Field Laboratory, which is supported by National Science Foundation Cooperative Agreement No. DMR-0654118, the State of Florida and the U.S. Department of Energy. This research has been also supported by Strategic International Collaborative Research Program (SICORP), Japan Science and Technology Agency. V.G. acknowledges financial support of the EU (Super Iron under project No. FP7-283204).
Author information
Authors and Affiliations
Contributions
K.I., J.H. and C.T. designed the study and wrote the manuscript together with M.N., J.J., I.T., V.G., L.S. and B.H. Thin films were prepared by S.U., K.I. and S.U. conducted x-ray experiments. C.T. and K.I. measured low field transport properties. C.T., K.I., J.H., F.K., M.N. and J.J. investigated high-field transport properties. A.I., I.T. and E.R. conducted TEM investigation. All authors discussed the results and implications and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Supplementary Information
Supplementary Information for "Oxypnictide SmFeAs(O,F) superconductor: a candidate for high-field magnet applications"
Rights and permissions
This work is licensed under a Creative Commons Attribution 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by/3.0/
About this article
Cite this article
Iida, K., Hänisch, J., Tarantini, C. et al. Oxypnictide SmFeAs(O,F) superconductor: a candidate for high–field magnet applications. Sci Rep 3, 2139 (2013). https://doi.org/10.1038/srep02139
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep02139
This article is cited by
-
High Jc and low anisotropy of hydrogen doped NdFeAsO superconducting thin film
Scientific Reports (2021)
-
Artificially engineered nanostrain in FeSexTe1-x superconductor thin films for supercurrent enhancement
NPG Asia Materials (2020)
-
Exploring Multi-Component Superconducting Compounds by a High-Pressure Method and Ceramic Combinatorial Chemistry
Journal of Superconductivity and Novel Magnetism (2017)
-
Temperature Dependence Low-Field Microwave Absorption in a Powder Sample of SmFeAs(O,F) Iron Pnictide Superconductor
Journal of Superconductivity and Novel Magnetism (2017)
-
Intrinsic and extrinsic pinning in NdFeAs(O,F): vortex trapping and lock-in by the layered structure
Scientific Reports (2016)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.