Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

High-throughput screening of inorganic compounds for the discovery of novel dielectric and optical materials


Dielectrics are an important class of materials that are ubiquitous in modern electronic applications. Even though their properties are important for the performance of devices, the number of compounds with known dielectric constant is on the order of a few hundred. Here, we use Density Functional Perturbation Theory as a way to screen for the dielectric constant and refractive index of materials in a fast and computationally efficient way. Our results constitute the largest dielectric tensors database to date, containing 1,056 compounds. Details regarding the computational methodology and technical validation are presented along with the format of our publicly available data. In addition, we integrate our dataset with the Materials Project allowing users easy access to material properties. Finally, we explain how our dataset and calculation methodology can be used in the search for novel dielectric compounds.

Design Type(s) data integration objective
Measurement Type(s) electric susceptibility
Technology Type(s) computational modeling technique
Factor Type(s)  

Machine-accessible metadata file describing the reported data (ISA-Tab format)

Background & Summary

Dielectric materials are an important component for a plethora of applications in modern electronics, such as Dynamic Random Access Memory (DRAM), flash memory, the Central Processing Unit (CPU), Light Emitting Diodes (LED) and photovoltaics. While high-k dielectrics enable more charge to be stored per unit volume, thus improving performance and driving device size down, low-k materials limit cross-communication, thus enabling devices to be packed closer together. As a result, new dielectric materials with tailored properties are essential for more efficient and better performing electronics as well as miniaturization. Furthermore, with the increasing use of electronics and electric motors in engineering applications, dielectric materials are starting to play a key role in industries such as, automotive, shipping and aerospace. Their specific requirements, however, are quite different to those of consumer electronics, typically requiring longer life as well as greater resistance to mechanical stress and temperature fluctuations.

As a result, there is a need for novel dielectric materials with properties suitable for a range of applications across different industries. However, the number of compounds with known dielectric constant is currently on the order of a few hundred, which drastically limits the options available to the design engineer. The number of inorganic compounds is on the order of 30–50,000 (refs 13) hence, there exist tens of thousands of compounds for which the dielectric response remains unknown. Given the sheer size of the chemical compound space, attempting to experimentally search for new dielectrics is not practical considering the time required for synthesis and measurement. On the other hand, Density Functional Perturbation Theory (DFPT) provides a relatively fast and inexpensive method to build a comprehensive dataset from which to derive structure/chemistry—dielectric property correlations and scan for interesting compounds.

The dielectric tensor of a material relates the electric field within the material to that applied externally and is comprised of the electronic as well as ionic contributions. In addition to its importance in defining low- and high-k materials, the dielectric tensor is also useful in the calculation of other material properties (Fig. 1). For example, as demonstrated by Petousis et al.4, it is possible to estimate the refractive index, n, of compounds at optical frequencies with ~6% deviation from experiments using static DFPT calculations. Furthermore, the ionic and electronic components of the dielectric tensor can be used to predict both the Infrared (IR) and Raman spectra of compounds. Along with the elastic5 and piezoelectric6 tensors, the dielectric tensor provides all the information necessary for the solution of the constitutive equations in applications where electric and mechanical stresses are coupled.

Figure 1: Illustration summarizing the quantities calculated in this work and their relation to other, fundamental, material properties.
figure 1

Previous studies range from single-compound investigations to high-throughput screening of polymers. More specifically, one high-throughput study7 was related to a specific system (ZrxSi1−xO2) and another reported the average dielectric constant for a few tens of inorganic compounds8. There have also been high-throughput studies on dielectrics, specific to organic polymers9. Experimental databases also exist but the total number of compounds listed is on the order of a few hundred.

In this work, we use the methodology established in Petousis et al.4 to generate the largest database of dielectric tensors to date consisting of 1,056 inorganic ordered compounds. Specifically, we report the full dielectric tensor for the total response as well as the electronic and ionic contributions. We also provide an estimate for the refractive index at optical wavelengths and far from resonance. It is worth noting that some of the listed compounds are hypothetical, created in silico by e.g., structure-prediction algorithms10 and have, to our knowledge, not been synthesized yet. As our present work focuses on compound screening, we did not deliberately single out any specific chemical compositions and/or structures for calculation. Our results are integrated in the Materials Project11 which is an open database and aims at employing high-throughput methods to predicting material properties for discovery and design.


Theory and definitions

Formally, the dielectric tensor ε relates the externally applied electric field to the field within the material and can be defined as:

(1) E i = j ε i j 1 E 0 j

where E is the electric field inside the material and E0 is the externally applied electric field. the indices i, j refer to the direction in space and take the values: {1, 2, 3}. The dielectric tensor can be split in the ionic (ϵ0) and electronic (ϵ) contributions:

(2) ε i j = ε i j 0 + ε i j

Here, we consider only the response of non-zero band gap materials to time-invariant fields. In the hypothetical case that a material does not respond at all to the external field, ε i j would be equal to the identity tensor and ε i j 0 would be zero. In fact, materials with zero ionic contribution do exist. In general, for ε i j 0 to be non-zero, compounds need to have at least 2 atoms per primitive cell, each having a different atomic charge.

The dielectric tensor is symmetric and respects all the symmetry operations of the corresponding point group. This limits the number of independent elements in the tensor to a minimum of 1 and a maximum of 6 depending on the crystal symmetry (Table 1).

Table 1 Dielectric tensors shape for different crystal symmetries.

The dielectric response calculated herein corresponds to that of a single crystal. In polycrystalline samples, grains are oriented randomly and hence, the actual response will be different. Nevertheless, the upper and lower bounds of the polycrystalline dielectric constant have proven to be12:

(3) 3 1/ λ 1 + 1/ λ 2 + 1/ λ 3 < ε p o l y < λ 1 + λ 2 + λ 3 3

where λ1, λ2, λ3 are the eigenvalues of the single crystal dielectric tensor. Of course, the above inequality takes into account only the different orientation of the grains and ignores effects due to e.g., impurities or other kinds of defects. For the sake of simplicity, here we estimate the polycrystalline dielectric constant using the simple average, i.e., we define:

(4) ε p o l y λ 1 + λ 2 + λ 3 3

Generally, the dielectric response varies with the frequency of the applied external field however here, we consider the static response (i.e., the response at constant electric fields or the long wavelength limit). Since the ionic contribution vanishes at high frequencies, our results can be used to obtain an estimate of the refractive index, n, at optical frequencies and far from resonance effects using the well known formula4:

(5) n = ε p o l y

where ε p o l y is the average of the eigenvalues of the electronic contribution to the dielectric tensor. It should be noted that equation (5) assumes the material is non-magnetic.

Computational workflow

The workflow for calculating the dielectric constant is similar to the one used and extensively benchmarked against experimental data, by Petousis et al.4 (Fig. 2). All structures were downloaded from the Materials Project database11,13,14. To ensure a good starting set of materials (e.g., well-relaxed, stable structures), we apply the following 3 selection criteria: 1) the DFT band gap should be greater than 0.1 eV, 2) the hull energy in the phase diagram should be less than 0.02 eV and 3) the interatomic forces of the starting structure should be less than 0.05 eV/Å. It should be noted here that since we are using perturbation theory, our structure should ideally be as close to the ground state as possible. However, in practice4 we found that a threshold value of 0.05 eV/Å for the interatomic forces leads to acceptable errors for our screening methodology. For computational efficiency we, at this point, limit the set of calculated compounds to those with ≤20 atoms per supercell. After the DFPT calculation, the validity of the calculation is checked by ensuring the energy of the acoustic phonon modes at the Gamma point is less than 1 meV and that the dielectric tensor respects the point group symmetry operations with an error less or equal to 10% (relative) or 2 (absolute). The latter was in practice implemented by applying the symmetry operation to the tensor and ensuring that no tensor element changed by more than 10% or 2 with respect to the mean value of the original tensor element and of the tensor element after the symmetry operation was applied.’ Furthermore, if we find imaginary optical phonon modes at the Gamma point, we tag those compounds as potentially ferroelectric.

Figure 2: The workflow for calculating the dielectric tensor.
figure 2

For the DFPT calculations we used the Vienna Ab-Initio Simulation Package1518 (VASP version 5.3.4) combined with the Generalized Gradient Approximation GGA/PBE19,20+U21,22 exchange-correlation functional and Projector Augmented Wave pseudopotentials23,24. The U values are energy corrections that address the spurious self-interaction energy introduced by GGA. Here, we used U values for d orbitals only that were fitted to experimental binary formation enthalpies using Wang et al.25 method. The full list of U values used, can be found in ref. 22. The k-point density was set at 3,000 per reciprocal atom and the plane wave energy cut-off at 600 eV (ref. 4). For detailed information on the calculation of the dielectric tensor within the DFPT framework we refer to Baroni et al.26,27 and Gonze & Lee28.

Code availability

The DFPT calculations in this work were performed using the proprietary code VASP. The pre-and post-processing of the simulations was achieved using pymatgen13 and FireWorks29. Pymatgen13 is open-source software under the Massachusetts Institute of Technology (MIT) license. The workflow in Fig. 2 was implemented in FireWorks29 which is publicly available under a modified GNU General Public License.

Data Records

The calculated dielectric tensors and refractive indices are available on the Materials Project13 website ( and can be downloaded using the Materials Project API14. On the website, it is also possible to query for compounds with a certain dielectric response and refractive index by applying the appropriate filters on the search engine. Additionally, the Materials Project website provides information about the simulation parameters, crystal structure and other properties. The results are also available in the form of a JSON file that can be downloaded directly from the Dryad repository (Data Citation 1).

File format

The data for each of the calculated compounds are stored in a list and are provided as a JSON file. For each compound, there are key values, such as ‘e_electronic’ and ‘e_ionic’, that point to the appropriate property (Table 2). The key ‘meta’ contains all the appropriate metadata and has its own keys which are one level down in hierarchy. The metadata keys are presented in Table 3.

Table 2 Description of metadata keys.
Table 3 Description of metadata keys.

Graphical representation of results

In Fig. 3, we show a violin plot of the electronic and ionic contribution components of the dielectric constant for all calculated compounds, grouped according to the crystal system. Firstly, the plot shows that, as discussed above, the ionic contribution can be zero in contrast to its electronic counterpart. Furthermore, we observe the distribution of ε p o l y 0 to be similar and relatively larger for cubic and orthorhombic crystals. However, monoclinic and triclinic crystals show lower values for the ionic component. This could be due to the lower level of symmetry and hence, the lack of phonon contributions to ε i j 0 .

Figure 3: The polycrystalline estimate of the dielectric constant for the different crystal systems.
figure 3

The violin outlines are the Gaussian kernel density estimates of the data points that appear in the middle and are calculated using f(x)= 1 n h i =1 n K ( x x i h ) where K is the Gaussian kernel and h is a smoothing parameter (estimated here using Scott's normal reference rule30). The left (blue) refers to the electronic component while the right (yellow), to the ionic. The total number of compounds in each crystal system was: 236, 132, 254, 183, 166, 11 and 74 (for cubic, hexagonal, trigonal, tetragonal, orthogonal, monoclinic and triclinic respectively).

We have also plotted the results versus the band gap predicted by DFT-GGA+U (we note that DFT-GGA+U has the tendency to systematically underestimate band gaps). Figures 4 and 5 show the variation of ε t o t a l and n with band gap, respectively. Additionally, in Fig. 4 we plotted the dielectric constant of polymers calculated by Sharma et al.9. Both figures demonstrate the inverse dependence of the dielectric constant with the band gap. In fact, the trend is more pronounced for the refractive index since n= ε p o l y and hence, phonon contributions are excluded. The inverse relationship should be expected because if one considers 1st order perturbation theory, the electronic susceptibility depends inversely on the energy difference of the transition states (the latter increases, on average, with increasing band gap). However, we also observe that for a given band gap, the dielectric constant can take a range of values hinting that other aspects of the band structure are also important. Indeed as expected, compounds with a large number of states close to or at the valence/conduction bands maxima/minima have a relatively larger number of low energy transition states and hence, a relatively higher electronic dielectric constant. This is demonstrated in Fig. 6 where PtS2 ( ε p o l y 10) has a larger dielectric constant than GaAgO2 ( ε p o l y 6) even though its band gap is also larger.

Figure 4: The polycrystalline estimate of the dielectric constant ( ε p o l y ).
figure 4

The x-axis represents the DFT-GGA+U band gap values (Eg) obtained from the Materials Project website. There is a total of 1,056 data points for inorganic compounds. The red data points refer to values for polymers calculated by Huan et al.31 Red and green lines represent the figures of merit ( ε p o l y E g ) and ( ε p o l y E g ) respectively. The formulas of promising compounds with ε p o l y E g >16 and ε p o l y E g >160, are shown on the graph. HfO2, SiO2 and polyethylene are also shown for information.

Figure 5: The polycrystalline estimate of the refractive index versus band gap for the different crystal systems.
figure 5

There appears to be no trend between the refractive index/band gap inverse relationship and the crystal system the material belongs to.

Figure 6: The density of states for PtS2 and GaAgO2.
figure 6

PtS2 has a higher electronic dielectric constant than GaAgO2, even though its band gap is larger.

High-k dielectrics

In Fig. 4 we superimposed the lines ε p o l y E g =c and ε p o l y E g =c (where Eg represents the band gap of the material and c is a constant). These quantities are proxies to the figures of merit for current leakage8 and energy storage9 of a capacitor respectively. Since for high-k dielectrics, both high ε p o l y E g and ε p o l y E g are desired in order to limit leakage and maximize energy storage in applications, we identified the best performing compounds out of the ones calculated and highlighted them in Fig. 4. Thus, the design of new and better performing dielectric materials effectively becomes a battle against the inverse relationship between Eg and ε p o l y .

Another point worth noting is that although polymers follow the general trend of inorganic compounds, they do not seem to have the high dielectric constant outliers that inorganics exhibit. We believe this is due to the fact that inorganics, being structurally more ordered than polymers, can benefit from a significant contribution to the dielectric constant from the optical phonon modes.

The discussion above provides insight on the search for new high-k dielectrics that break the inverse relationship apparent in both Figs 4 and 5. Thus, we suggest that materials with the following characteristics might have superior dielectric properties:

  1. 1

    Flat conduction and valences band (d and f orbitals might help achieve this).

  2. 2

    Crystal symmetries that have been known to have significant ionic contributions to the dielectric constant (e.g., Fm 3 ¯ m, R3c).

However, we emphasize that the ionic components tend to zero at high field frequencies and hence, the effective dielectric constant might be significantly different at THz or GHz applications.

Low-k dielectrics

Since the band gap can be thought as a proxy to how insulating a material is, good low-k dielectrics will also have large Eg. However, in this case the advantage is that high band gap materials naturally have a low dielectric constant. Additionally, suppressing the ionic contributions might be beneficial. For this, the selection of low symmetry structures and elements with small difference in electronegativity may be helpful.

Technical Validation

The high-throughput calculation methodology and workflow used in the present study were validated in Petousis et al.4. Specifically, the eigenvalues of the total dielectric tensor were compared to experimental values for a set of representative compounds. This set was made up of 88 compounds consisting of 42 different elements and belonging to 14 different point groups. In cases where larger than average deviations from experiments existed, the quality of the results was ensured by confirming agreement with other state-of-the-art and compound-bespoke DFPT calculations reported in the literature. In the same reference, the method for calculating the refractive index at optical frequencies and far from resonance was also validated by comparing against experimental data found in the literature for a subset of 87 compounds.

As described in more detail in the Methods section, each calculation was tested for validity by checking the acoustic phonons at the Gamma point and the symmetry of the dielectric tensor. Furthermore, when the information was available, our results were checked against other experimental values reported in the literature. The comparison is presented in Fig. 7 and Table 4. We observe that in most cases materials deviate less than +/−25% from experiments. There are many factors that are not included in the DFPT model and contribute to this deviation e.g., (1) temperature, (2) pressure, (3) grain boundaries, (4) defects, (5) surface effects, (6) phonon anharmonicity. It should be noted that experimental values also vary between different studies. A detailed analysis of the reasons for deviation from experiments can be found in Petousis et al.4. The Mean Absolute Deviation (MAD) and Mean Absolute Relative Deviation (MARD) were 2.0 and 19.0% respectively, which we consider acceptable for a screening methodology. Once promising candidate materials are identified, further calculations and analyses can be performed to obtain a better estimate.

Figure 7: Comparison of calculated values.
figure 7

( ε p o l y ) versus experimental values in the literature. The lines indicate the relative deviation of the calculated values with respect to experiments. The Mean Absolute Deviation (MAD) and Mean Absolute Relative Deviation (MARD) were extracted as 2.0 and 19.0% respectively. Data points are listed in Table 4.

Table 4 Comparison with experimental data.

Furthermore, Fig. 8 shows the effect of structural relaxation and remnant interatomic forces on the dielectric constant. In particular, we plot the dielectric constant for a subset of 90 compounds where on the x-axis, interatomic forces are less than 0.05 eV/Å but higher than 0.01 eV/Å and on the y-axis they are less 0.01 eV/Å for the same compounds. Figure 8 shows that although the deviation between the two cases, is on average relatively small (0.22 absolute and 2.23% relative deviations), there are cases for which this deviation can be significant (e.g., 1.92 and 16.65%).

Figure 8: Plot showing the effect of remnant interatomic forces.
figure 8

The errors where calculated by taking the dielectric constant with forces less than 0.01 eV/Å as the ‘correct’ value.

Usage Notes

We present a database of calculated dielectric constant and refractive index for 1,056 compounds. Our work should be of interest to researchers and engineers from a number of different fields, for example, electronic structure theory, photovoltaics and electronic devices. We expect this database to be used in the understanding of dielectric materials and in the search for new dielectrics with unique and tailored properties. Additionally, it can be used in the screening of replacement candidates for currently used dielectrics such as SiO2. The above use cases are facilitated by the Materials Project website interface which allows users to search for materials with target dielectric response or refractive index. Furthermore, the user can specify additional constraints such as stability, band gap and/or density. In line with the Materials Project practice, users will be able to request calculated dielectric constants for compounds that are not currently listed. The existence of a database such as the one presented here, opens opportunities in data intensive Materials Science. For example, the application of machine learning techniques, could lead to the identification of structural and chemical features that are key to the dielectric response. Such features would not only enhance the theoretical understanding but could also accelerate the discovery of novel dielectric materials.

Additional information

How to cite this article: Petousis, I. et al. High-throughput screening of inorganic compounds for the discovery of novel dielectric and optical materials. Sci. Data 4:160134 doi: 10.1038/sdata.2016.134 (2017).

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.



  1. Taylor, P. Crystallographic Databases edited by F. H. Allen, G. Gergerhoff and R. Sievers. Acta Crystallogr., Sect. C: Cryst. Struct. Commun. 44, 1153–1154 (1988).

    Article  Google Scholar 

  2. Belsky, A., Hellenbrandt, M., Karen, V. L. & Luksch, P. New developments in the inorganic crystal structure database (ICSD): accessibility in support of materials research and design. Acta Crystallogr., Sect. B: Struct. Sci. 58, 364–369 (2002).

    Article  Google Scholar 

  3. Setyawan, W., Gaume, R. M., Lam, S., Feigelson, R. S. & Curtarolo, S. High-throughput combinatorial database of electronic band structures for inorganic scintillator materials. ACS Comb. Sci. 13, 382–390 (2011).

    CAS  Article  Google Scholar 

  4. Petousis, I. et al. Benchmarking of the density functional perturbation theory to enable the high-throughput screening of materials for the dielectric constant and refractive index. Phys. Rev. B 93, 115151 (2016).

    ADS  Article  Google Scholar 

  5. de Jong, M. et al. Charting the complete elastic properties of inorganic crystalline compounds. Sci. Data 2, 150009 (2015).

    CAS  Article  Google Scholar 

  6. de Jong, M., Chen, W., Geerlings, H., Asta, M. & Persson, K. A. A database to enable discovery and design of piezoelectric materials. Sci. Data 2, 150053 (2015).

    CAS  Article  Google Scholar 

  7. Zhang, J., Zeng, Q., Oganov, A. R., Dong, D. & Liu, Y. High throughput exploration of ZrxSi1−xO2 dielectrics by evolutionary first-principles approaches. Phys. Lett. A 378, 3549–3553 (2014).

    CAS  ADS  Article  Google Scholar 

  8. Yim, K. et al. Novel high-κ dielectrics for next-generation electronic devices screened by automated ab initio calculations. NPG Asia Mater. 7, e190 (2015).

    CAS  Article  Google Scholar 

  9. Sharma, V. et al. Rational design of all organic polymer dielectrics. Nat. Commun. 5, 4845 (2014).

    CAS  ADS  Article  Google Scholar 

  10. Hautier, G., Fischer, C., Ehrlacher, V., Jain, A. & Ceder, G. Data mined ionic substitutions for the discovery of new compounds. Inorg. Chem. 50, 656–663 (2010).

    Article  Google Scholar 

  11. Jain, A. et al. The Materials Project: a materials genome approach to accelerating materials innovation. APL Mat. 1, 011002 (2013).

    ADS  Article  Google Scholar 

  12. Hashin, Z. & Shtrikman, S. Conductivity of polycrystals. Phys. Rev. 130, 129 (1963).

    CAS  ADS  Article  Google Scholar 

  13. Ong, S. P. et al. Python Materials Genomics (pymatgen): a robust, open-source python library for materials analysis. Comp. Mater. Sci. 68, 314–319 (2013).

    CAS  Article  Google Scholar 

  14. Ong, S. P. et al. The materials application programming interface (API): a simple, flexible & efficient API for materials data based on REpresentational State Transfer (REST) principles. Comp. Mater. Sci. 97, 209–215 (2015).

    Article  Google Scholar 

  15. Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).

    CAS  ADS  Article  Google Scholar 

  16. Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal-amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251 (1994).

    CAS  ADS  Article  Google Scholar 

  17. Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comp. Mater. Sci. 6, 15–50 (1996).

    CAS  Article  Google Scholar 

  18. Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).

    CAS  ADS  Article  Google Scholar 

  19. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).

    CAS  ADS  Article  Google Scholar 

  20. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple [Phys. Rev. Lett. 77, 3865 (1996)]. Phys. Rev. Lett. 78, 1396 (1997).

    CAS  ADS  Article  Google Scholar 

  21. Dudarev, S. L., Botton, G. A., Savrasov, S. Y., Humphreys, C. J. & Sutton, A. P. Electron-energy-loss spectra and the structural stability of nickel oxide: An LSDA+U study. Phys. Rev. B 57, 1505 (1998).

    CAS  ADS  Article  Google Scholar 

  22. Jain, A. et al. A high-throughput infrastructure for density functional theory calculations. Comp. Mater. Sci. 50, 8 2295 (2011).

    CAS  Article  Google Scholar 

  23. Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).

    ADS  Article  Google Scholar 

  24. Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).

    CAS  ADS  Article  Google Scholar 

  25. Wang, L., Maxisch, T. & Ceder, G. Oxidation energies of transition metal oxides within the GGA+ U framework. Phys. Rev. B 73, 195107 (2006).

    ADS  Article  Google Scholar 

  26. Baroni, S., Giannozzi, P. & Testa, A. Elastic constants of crystals from linear-response theory. Phys. Rev. Lett. 59, 2662 (1987).

    CAS  ADS  Article  Google Scholar 

  27. Baroni, S., de Gironcoli, S., Dal Corso, A. & Giannozzi, P. Phonons and related crystal properties from density-functional perturbation theory. Rev. Mod. Phys. 73, 515 (2001).

    CAS  ADS  Article  Google Scholar 

  28. Gonze, X. & Lee, C. Dynamical matrices, born effective charges, dielectric permittivity tensors, and interatomic force constants from density-functional perturbation theory. Phys. Rev. B 55, 10355 (1997).

    CAS  ADS  Article  Google Scholar 

  29. Jain, A. et al. Fireworks: a dynamic workflow system designed for high-throughput applications. Concurr. Comp.-Pract. E 27, 5037–5059 (2015).

    Article  Google Scholar 

  30. Scott, D. W. On optimal and data-based histograms. Biometrika 66, 605–610 (1979).

    MathSciNet  Article  Google Scholar 

  31. Huan, T. D. et al. A polymer dataset for accelerated property prediction and design. Sci. Data 3, 160012 (2016).

    CAS  Article  Google Scholar 

  32. Seehra, M. S. & Helmick, R. E. Anomalous changes in the dielectric constants of MnF2 near its Néel temperature. J. Appl. Phys. 55, 2330–2332 (1984).

    CAS  ADS  Article  Google Scholar 

  33. Bottger, G. L. & Geddes, A. L. Infrared Lattice Vibrational Spectra of AgCl, AgBr, and AgI. J. Chem. Phys. 46, 3000 (1967).

    CAS  ADS  Article  Google Scholar 

  34. Young, K. F. & Frederikse, H. P. R. Compilation of the static dielectric constant of inorganic solids. J. Phys. Chem. Ref. Data 2, 313–410 (1973).

    ADS  Article  Google Scholar 

  35. Chandrasekhar, H. R., Bhattacharya, G., Migoni, R. & Bilz, H. Phonon spectra and lattice dynamics of lithium nitride. Solid State Commun. 22, 681–684 (1977).

    CAS  ADS  Article  Google Scholar 

  36. Madelung, O., Rössler, U. & Schulz, M. (ed.). Boron nitride (BN), optical properties, dielectric constants, hexagonal modification 10.1007/10832182_575. Available at Accessed on 16 March 2016.

  37. Barker, A. S. Jr & Ilegems, M. Infrared lattice vibrations and free-electron dispersion in GaN. Phys. Rev. B 7, 743 (1973).

    CAS  ADS  Article  Google Scholar 

  38. Madelung, O., Rössler, U. & Schulz, M. (ed.). Boron phosphide (BP), optical properties, dielectric constant 10.1007/10832182_51. Available at Accessed on 16 March 2016.

  39. Balkanski, M., Moch, P. & Parisot, G. Infrared lattice-vibration spectra in NiF2, CoF2, and FeF2 . J. Chem. Phys. 44, 940–944 (1966).

    CAS  ADS  Article  Google Scholar 

  40. Uchida, S. & Tanaka, S. Optical phonon modes and localized effective charges of transition-metal dichalcogenides. J. Phys. Soc. Jpn 45, 153–161 (1978).

    CAS  ADS  Article  Google Scholar 

  41. Kaneko, Y., Morimoto, K. & Koda, T. Optical properties of alkaline-earth chalcogenides. I. Single crystal growth and infrared reflection spectra due to optical phonons. J. Phys. Soc. Jpn 51, 2247–2254 (1982).

    CAS  ADS  Article  Google Scholar 

  42. Evans, B. L., Yoffe, A. D. & Gray, P. Physics and chemistry of the inorganic azides. Chem. Rev. 59, 515–568 (1959).

    CAS  Article  Google Scholar 

  43. Martienssen, W. & Warlimont, H. Springer handbook of condensed matter and materials data (Springer Science & Business Media, 2006).

    Google Scholar 

  44. Patrick, L. & Choyke, W. J. Static dielectric constant of SiC. Phys. Rev. B 2, 2255 (1970).

    ADS  Article  Google Scholar 

  45. Kumar, A. & Ahluwalia, P. K. Tunable dielectric response of transition metals dichalcogenides MX2 (M=Mo,W; X=S,Se,Te): Effect of quantum confinement. Physica B 407, 4627–4634 (2012).

    CAS  ADS  Article  Google Scholar 

  46. Berlincourt, D., Jaffe, H. & Shiozawa, L. R. Electroelastic Properties of the Sulfides, Selenides, and Tellurides of Zinc and Cadmium. Phys. Rev. 129, 1009 (1963).

    CAS  ADS  Article  Google Scholar 

  47. Liu, B. et al. First-principles study of lattice dynamics and thermodynamic properties of LaCl3 and LaBr3 . Phys. Rev. B 76, 064307 (2007).

    ADS  Article  Google Scholar 

  48. Madelung, O., Rössler, U. & Schulz, M. (ed.). Arsenic selenide (As 2 Se 3 ) optical properties, dielectric constant, photoluminescence 10.1007/10681727_999. Available at Accessed on 16 March 2016.

  49. Madelung, O., Rössler, U. & Schulz, M. (ed.). Tin disulfide (SnS2) optical properties, dielectric constants 10.1007/10681727_790. Available at Accessed on 16 March 2016.

  50. Schlundt, H. The dielectric constants of some inorganic solvents. J. Phys. Chem. 8, 122–130 (1903).

    Article  Google Scholar 

  51. Riede, V., Neumann, H., Nguyen, H. X., Sobotta, H. & F Levy, F. Polarization-dependent infrared optical properties of gas. Physica 100B, 355–363 (1980).

    Google Scholar 

  52. Madelung O., Rössler U. & Schulz M. (ed.) Arsenic selenide (As2Se3) optical properties, dielectric constant, photoluminescence. in Non-Tetrahedrally Bonded Elements and Binary Compounds I, 1–19 (Springer Berlin Heidelberg, 1998).

    Chapter  Google Scholar 

  53. Willardson, R. K. & Weber, E. R. SiC materials and devices Vol. 52 (Academic Press, 1998).

    Google Scholar 

  54. Madelung, O., Rössler, U. & Schulz, M. (ed.) Indium selenide (InSe) dielectric constantIn Non-Tetrahedrally Bonded Elements and Binary Compounds I, 1–3 (Springer Berlin Heidelberg, 1998).

    Chapter  Google Scholar 

  55. Swenson, R. W. & Cole, R. H. Dielectric properties of hydrogen halides. II. hydrogen chloride. J. Chem. Phys. 22, 284 (1954).

    CAS  ADS  Article  Google Scholar 

  56. Rao, K. V. & Smakula, A. Dielectric properties of thallium halides and their mixed crystals. Mater. Res. Bull. 6, 1047–1055 (1971).

    CAS  Article  Google Scholar 

  57. Lutz, H. D., Schneider, G. & Kliche, G. Far-infrared reflection spectra, TO-and LO-phonon frequencies, coupled and decoupled plasmon-phonon modes, dielectric constants, and effective dynamical charges of manganese, iron, and platinum group pyrite type compounds. J. Phys. Chem. Solids 46, 437–443 (1985).

    CAS  ADS  Article  Google Scholar 

  58. Uchino, K., Nomura, S., Vedam, K., Newnham, R. E. & Cross, L. E. Pressure dependence of the refractive index and dielectric constant in a fluoroperovskite, KMgF3 . Phys. Rev. B 29, 6921 (1984).

    CAS  ADS  Article  Google Scholar 

  59. Madelung, O., Rössler, U. & Schulz, M. (ed.) Copper aluminum sulfide (CuAlS2) resistivity, Seebeck coefficient, dielectric constants 10.1007/10717201_43. Available at Accessed on 16 March 2016.

  60. Madelung, O. (ed.) Semiconductors—basic data (Springer Science & Business Media, 2012).

    Google Scholar 

  61. Gurzadyan, G. G. & Tzankov, P. Dielectrics and electrooptics. in Springer Handbook of Condensed Matter and Materials Data, 817–901 (Springer, 2005).

    Chapter  Google Scholar 

  62. Ravindran, P., Delin, A., Johansson, B., Eriksson, O. & Wills, J. M. Electronic structure, chemical bonding, and optical properties of ferroelectric and antiferroelectric NaNO2 . Phys. Rev. B 59, 1776 (1999).

    CAS  ADS  Article  Google Scholar 

Data Citations

  1. Petousis, I. Dryad Digital Repository (2017)

Download references


This work was supported financially by the Volkswagen Group. K.A.P., W.C., D.W., M.L. and D.M. gratefully acknowledge support from the Materials Project Center, under the Department of Energy, Basic Energy Sciences Grant No EDCBEE. The calculations were performed using the computational resources of the National Energy Research Scientific Computing Center, which is supported under the Office of Science of the U.S. Department of Energy under Contract No DE-AC02-05CH11231.

Author information

Authors and Affiliations



I.P. performed the dielectric constant and refractive index calculations, developed the algorithm and the code, performed the data verification and analysis and wrote the paper. D.M. obtained experimental data from the literature. E.B. obtained experimental data from the literature. M.L. wrote the code to upload the raw data on the Materials Project website. D.W. developed the web interface on the Materials Project website. W.C. was involved in supervising and planning the work. T.G. was involved in supervising and planning the work. T.D.S. was involved in supervising and planning the work. K.A.P. was involved in supervising and planning the work and its integration with the Materials Project effort. F.B.P. was involved in supervising and planning the work.

Corresponding author

Correspondence to Ioannis Petousis.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

ISA-Tab metadata

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit Metadata associated with this Data Descriptor is available at and is released under the CC0 waiver to maximize reuse.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Petousis, I., Mrdjenovich, D., Ballouz, E. et al. High-throughput screening of inorganic compounds for the discovery of novel dielectric and optical materials. Sci Data 4, 160134 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing