Transferred via contacts as a platform for ideal two-dimensional transistors

Abstract

Two-dimensional semiconductors have a number of valuable properties that could be used to create novel electronic devices. However, creating 2D devices with good contacts and stable performance has proved challenging. Here we show that transferred via contacts, made from metal embedded in insulating hexagonal boron nitride and dry transferred onto 2D semiconductors, can be used to create high-quality 2D transistors. The approach prevents damage induced by direct metallization and allows full glovebox processing, providing a clean, stable and damage-free platform for 2D device fabrication. Using the approach, we create field-effect transistors (FETs) from bilayer p-type tungsten diselenide (WSe2) that exhibit high hole mobility and low contact resistance. The fabricated devices also exhibit high current and stability for over two months of measurements. Furthermore, the low contact resistance and clean channel allow us to create a nearly ideal top-gated p-FET with a subthreshold swing of 64 mV per decade at 290 K.

Access options

Rent or Buy article

Get time limited or full article access on ReadCube.

from$8.99

All prices are NET prices.

Fig. 1: Fabrication process for TVCs and conventional contacts.
Fig. 2: Electrical properties of bilayer WSe2 with TVCs at 295 K.
Fig. 3: Contact properties of bilayer WSe2 p-FETs with TVCs.
Fig. 4: Low-temperature measurements for a back-gated bilayer WSe2 p-FET with TVCs.
Fig. 5: Effects of direct metallization and glovebox processing.
Fig. 6: Double-gated bilayer WSe2 with TVCs as a nearly ideal 2D p-FET.

Data availability

The data that support the findings within this paper are available from the corresponding authors on reasonable request.

References

  1. 1.

    Allain, A., Kang, J., Banerjee, K. & Kis, A. Electrical contacts to two-dimensional semiconductors. Nat. Mater. 14, 1195–1205 (2015).

    Article  Google Scholar 

  2. 2.

    Kerelsky, A. et al. Absence of a band gap at the interface of a metal and highly doped monolayer MoS2. Nano Lett. 17, 5962–5968 (2017).

    Article  Google Scholar 

  3. 3.

    English, C. D., Shine, G., Dorgan, V. E., Saraswat, K. C. & Pop, E. Improved contacts to MoS2 transistors by ultra-high vacuum metal deposition. Nano Lett. 16, 3824–3830 (2016).

    Article  Google Scholar 

  4. 4.

    Xu, S. et al. Universal low-temperature ohmic contacts for quantum transport in transition metal dichalcogenides. 2D Mater. 3, 021007 (2016).

    Article  Google Scholar 

  5. 5.

    Yamamoto, M., Nakaharai, S., Ueno, K. & Tsukagoshi, K. Self-limiting oxides on WSe2 as controlled surface acceptors and low-resistance hole contacts. Nano Lett. 16, 2720–2727 (2016).

    Article  Google Scholar 

  6. 6.

    Kim, D. et al. The enhanced low resistance contacts and boosted mobility in two-dimensional p-type WSe2 transistors through Ar+ ion-beam generated surface defects. AIP Adv. 6, 105307 (2016).

    Article  Google Scholar 

  7. 7.

    Chuang, H.-J. et al. Low-resistance 2D/2D ohmic contacts: a universal approach to high-performance WSe2, MoS2 and MoSe2 transistors. Nano Lett. 16, 1896–1902 (2016).

    Article  Google Scholar 

  8. 8.

    Kaushik, N., Karmakar, D., Nipane, A., Karande, S. & Lodha, S. Interfacial n-doping using an ultrathin TiO2 layer for contact resistance reduction in MoS2. ACS Appl. Mater. Interfaces 8, 256–263 (2016).

    Article  Google Scholar 

  9. 9.

    Kim, C. et al. Fermi level pinning at electrical metal contacts of monolayer molybdenum dichalcogenides. ACS Nano 11, 1588–1596 (2017).

    Article  Google Scholar 

  10. 10.

    Kaushik, N. et al. Schottky barrier heights for Au and Pd contacts to MoS2. Appl. Phys. Lett. 105, 113505 (2014).

    Article  Google Scholar 

  11. 11.

    Lee, G.-H. et al. Highly stable, dual-gated MoS2 transistors encapsulated by hexagonal boron nitride with gate-controllable contact, resistance and threshold voltage. ACS Nano 9, 7019–7026 (2015).

    Article  Google Scholar 

  12. 12.

    Movva, H. C. P. et al. Density-dependent quantum Hall states and Zeeman splitting in monolayer and bilayer WSe2. Phys. Rev. Lett. 118, 247701 (2017).

    Article  Google Scholar 

  13. 13.

    Wang, G. et al. Exciton dynamics in WSe2 bilayers. Appl. Phys. Lett. 105, 182105 (2014).

    Article  Google Scholar 

  14. 14.

    Jones, A. M. et al. Spin-layer locking effects in optical orientation of exciton spin in bilayer WSe2. Nat. Phys. 10, 130–134 (2014).

    Article  Google Scholar 

  15. 15.

    Lee, J.-H. et al. Reliable piezoelectricity in bilayer WSe2 for piezoelectric nanogenerators. Adv. Mater. 29, 1606667 (2017).

    Article  Google Scholar 

  16. 16.

    Liu, Y. et al. Approaching the Schottky–Mott limit in van der Waals metal–semiconductor junctions. Nature 557, 696–700 (2018).

    Article  Google Scholar 

  17. 17.

    Telford, E. J. et al. Via method for lithography free contact and preservation of 2D materials. Nano Lett. 18, 1416–1420 (2018).

    Article  Google Scholar 

  18. 18.

    Wang, Y. et al. Does p-type ohmic contact exist in WSe2–metal interfaces? Nanoscale 8, 1179–1191 (2015).

    Article  Google Scholar 

  19. 19.

    Choi, H. H. et al. Accurate extraction of charge carrier mobility in 4-probe field-effect transistors. Adv. Funct. Mater. 28, 1707105 (2018).

    Article  Google Scholar 

  20. 20.

    Allain, A. & Kis, A. Electron and hole mobilities in single-layer WSe2. ACS Nano 8, 7180–7185 (2014).

    Article  Google Scholar 

  21. 21.

    Movva, H. C. P. et al. High-mobility holes in dual-gated WSe2 field-effect transistors. ACS Nano 9, 10402–10410 (2015).

    Article  Google Scholar 

  22. 22.

    Zhang, R., Drysdale, D., Koutsos, V. & Cheung, R. Controlled layer thinning and p-type doping of WSe2 by vapor XeF2. Adv. Funct. Mater. 27, 1702455 (2017).

    Article  Google Scholar 

  23. 23.

    Chen, C.-H. et al. Hole mobility enhancement and p-doping in monolayer WSe2 by gold decoration. 2D Mater. 1, 034001 (2014).

    Article  Google Scholar 

  24. 24.

    Fang, H. et al. High-performance single layered WSe2 p-FETs with chemically doped contacts. Nano Lett. 12, 3788–3792 (2012).

    Article  Google Scholar 

  25. 25.

    Shokouh, S. H. H. et al. High-performance, air-stable, top-gate, p-channel WSe2 field-effect transistor with fluoropolymer buffer layer. Adv. Funct. Mater. 25, 7208–7214 (2015).

    Article  Google Scholar 

  26. 26.

    Chuang, H.-J. et al. High mobility WSe2 p- and n-type field-effect transistors contacted by highly doped graphene for low-resistance contacts. Nano Lett. 14, 3594–3601 (2014).

    Article  Google Scholar 

  27. 27.

    Tosun, M. et al. High-gain inverters based on WSe2 complementary field-effect transistors. ACS Nano 8, 4948–4953 (2014).

    Article  Google Scholar 

  28. 28.

    Appenzeller, J., Lin, Y.-M., Knoch, J. & Avouris, P. Band-to-band tunneling in carbon nanotube field-effect transistors. Phys. Rev. Lett. 93, 196805 (2004).

    Article  Google Scholar 

  29. 29.

    Yoon, Y. & Salahuddin, S. Inverse temperature dependence of subthreshold slope in graphene nanoribbon tunneling transistors. Appl. Phys. Lett. 96, 013510 (2010).

    Article  Google Scholar 

  30. 30.

    Nipane, A., Jayanti, S., Borah, A. & Teherani, J. T. Electrostatics of lateral p–n junctions in atomically thin materials. J. Appl. Phys. 122, 194501 (2017).

    Article  Google Scholar 

  31. 31.

    Ma, N. & Jena, D. Charge scattering and mobility in atomically thin semiconductors. Phys. Rev. X 4, 011043 (2014).

    Google Scholar 

Download references

Acknowledgements

This work was supported by the National Science Foundation through a CAREER Award (ECCS-1752401) and by the Center for Precision Assembly of Superstratic and Superatomic Solids (DMR-1420634). This work is also supported by the National Research Foundation of Korea through the Global Research Laboratory (GRL) program (2016K1A1A2912707) and Research Fellow program (2018R1A6A3A11045864).

Author information

Affiliations

Authors

Contributions

Y.J., M.S.C., J.H. and J.T.T. conceived the research and designed the experiments. Y.J. and M.S.C. fabricated and measured the devices under J.T.T.’s supervision. A.N. and A.B. contributed to the data analysis and manuscript revision. B.K. contributed to the Hall measurements. A.Z. performed TEM measurements. T.T. and K.W. contributed h-BN material. W.J.Y., J.H. and J.T.T. contributed to discussions of the results. Y.J., M.S.C. and J.T.T. wrote the manuscript.

Corresponding author

Correspondence to James T. Teherani.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–11.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Jung, Y., Choi, M.S., Nipane, A. et al. Transferred via contacts as a platform for ideal two-dimensional transistors. Nat Electron 2, 187–194 (2019). https://doi.org/10.1038/s41928-019-0245-y

Download citation

Further reading

Search

Quick links

Sign up for the Nature Briefing newsletter for a daily update on COVID-19 science.
Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing