Abstract
The indirect dumping of massive volumes of toxic dyes into water has seriously affected the ecosystem. Owing to the many applications of the designed nanomaterials in the manufacturing process, there is a lot of research interest in synthesizing nanomaterials using green processes. In this research, the byproduct of bee was employed to synthesize nanoparticles (NPs) of ZnO, CuO, and biosynthesized ZnO/CuO (BZC) nanocomposite via utilizing a green and simple approach. To validate the effective fabrication of BZC nanocomposite, various characterization measurements were applied. FTIR analysis identified the functional groups in charge of producing nanoparticles and nanocomposites. Moreover, the existence of ZnO and CuO XRD peaks suggests that the nanocomposites were successfully biosynthesized. The high-resolution XPS spectrum of the BZC nanocomposite’s Zn2p3, Cu2p3, and O1s were observed. Our findings indicate the successful engineering of the prepared nanomaterials and BZC nanocomposite. Our findings indicate the successful engineering of the prepared nanomaterials and BZC nanocomposite. For Congo red (CR) fluorescent stain azo dye elimination in water, all adsorption parameters were examined at room temperature. Moreover, the adsorption experiments revealed the removal capacity for uptake CR dye using BZC nanocomposite (90.14 mg g−1). Our results show that the BZC nanocomposite exhibited high removal capability for the adsorption of CR dye. The nanosphere adsorbent offered a simple, low-cost, and green approach for water purification and industrial wastewater control.
Similar content being viewed by others
Introduction
Dyes are natural and typically synthetic materials with complex aromatic structures, but stable to degrade organically. Congo red dye (CR) is toxic to many organisms which possibly produced cancer and genetic mutation. The CR dye usage is prohibited in various countries because of health issues. However, it is still widely utilized in the textile, paper, rubber, and plastic industries1. Different systems for removing synthetic dyes have been developed to lessen their negative environmental effects. Although there are plentiful applicable decolorization techniques, not all are effective or even appropriate for use as a result of their drawbacks. The most efficient dye removal method should be able to rapidly and essentially eliminate significant amounts of dye2,3. Adsorption is an extremely effective treatment for removing dissolved organic contaminants from industrial wastewater. Significant parameters that might affect adsorption efficiency such as temperature, surface area, contact time, and pH4,5,6. Numerous researchers have worked to enhance adsorption activities and make cost-effective new alternative adsorbents with high adsorption power. Recently, much emphasis placed on reaping the benefits of using nanoparticles or nanocomposites. Nanomaterials have lately received great attention in their use as adsorbents in the remediation of environmental pollutants7. Metal oxide nanoparticles have a higher adsorption capacity, a low diffusion resistance, a specific surface area, a faster adsorption equilibrium, and semiconducting properties. Green extract can be used to create more stable nanoparticles, can be produced in a variety of sizes and forms, and is less expensive8,9,10. The ZnO/CuO nanocomposites have garnered attention because of their outstanding controllable catalytic, optical, magnetic, and electrical characteristics, and their ecologically sound nature11,12,13. ZnO/CuO nanocomposites offer a variety of bio-uses due to their chemical, physical, and low toxicity features14,15. Compared to synthesis approaches that use physical and chemical processes, a green preparation of NPs is a significant and promising approach because of its numerous advantages, as the utilization of natural materials, safety, low cost, and eco-friendly16,17,18. The findings show that increasing the surface area of the nanoparticles and decreasing the energy gap through bio-fabrication of ZnO and CuO nanocomposites, either separately or together, improves the catalytic adsorption capabilities19,20. The biosynthesized nanocomposite demonstrated the capability to reduce dye under sunlight for removing dyes from an environment21. Propolis, a resinous material assembled by honeybees, is known due to its various characteristics and prospective uses22. It has broad-spectrum antibacterial, anti-inflammatory, and antioxidant qualities, which are useful in wound healing, dental health, skincare, and gastrointestinal health. Propolis also has noninflammatory and anticancer characteristics. Its rich bioactive content is still being explored for its different health-promoting properties, emphasizing its importance in traditional medicine and natural therapies. In this paper, ZnO, CuO, and biosynthesized ZnO/CuO (BZC) nanocomposite was biologically fabricated using propolis as bee biproduct extract. The designed nanomaterials were successfully characterized and the adsorption technique for fluorescent stain dye removal using BZC was successfully examined. The adsorption parameters were investigated, including pH, contact duration, initial concentration, and dose. The fabricated BZC nanosphere demonstrate a convenient and simple protocol for water purification and industrial wastewater management model.
Experiments
Materials
Zinc nitrate hexahydrate Zn(NO3)2·6H2O, sodium hydroxide, Sodium Carbonate Na2CO3, Ammonia(33%), copper nitrate hexahydrate Cu(NO3)2·6H2O and ethanol were gained from Merck (Darmstadt, Germany). The Bee byproduct (Propolis) was purchased from a domestic market (Giza, Egypt).
Preparation of BZC using propolis extract
A particular gram of propolis granules (500 mg) was dissolved into 100 ml of deionized water to produce an extract from propolis as shown in Fig. 1. To get a suitable extract, the mixture was agitated and heated to 60 °C for 30 min. After filtering, the extract was placed in a cool location to be used later. The BZC was fabricated chemically as reported23. Whereas for BZC nanocomposite, the same method was performed with some modification and adding propolis extract. Under continuous stirring, 50 mL of Zn(NO3)2·6H2O (0.1 M) were mixed with 50 mL of Cu(NO3)2·6H2O(0.1 M) solutions. Then, 50 mL of extract and 50 mL of 0.1 M Na2CO3 were added dropwise to the metal nitrate solutions. The obtained product was put in a stainless-steel autoclave for 11 h at 100 °C. The off-white precipitate of BZC was crushed and calcinated for 2.5 h at 600 °C (Fig. 1).
Result and discussion
Characterizations of nanocomposites
The structure features and sizes of the biologically produced BZC nanocomposites were evaluated via using TEM investigation (Fig. 2). The obtained results demonstrate that the CuO, ZnO, and BZC nanocomposites were successfully biosynthesized into nano spherical forms with different diameters ranging from 15.1 to 30 nm. The irregular shape morphology of CuO NPs with weak agglomeration was investigated Fig. 2A–C. The green synthesis of ZnO nanoparticles was nearly uniformly hexagonal shape with non-agglomerate morphology (Fig. 2D–F). An important indicator of the carefully regulated shape and molecular configurations of the dense, tight structure of BZC in necklace-like form was provided by TEM images. The condensed BZC nanocomposites appeared and related to the composition of the synthesized material Fig. 2G–I. Nanocomposite showed smaller particle sizes than pure NPs, according to TEM images. Our outcomes agreed with previous results that the produced nanocomposites varied in size from individual structures under the same manufacturing conditions24.
The BZC nanocomposite crystal assembly of nanoparticles was analyzed by XRD analysis. In Fig. 3A, the CuO NPs showed well-defined peaks at 32.48°, 35.7°, 38.9°, 49.2°, 53.9°, 61.8°,66.2°, 66.24° and 68.08° which agreed to (110), (− 111), (111), (− 202), (020), (-113), (022), (-311), and (220) planes respectively. The designed CuO NPs were assigned to all of the detected peaks using the JCPDS card number 01-111725. The ZnO NPs main peaks were detected at 31.6°, 34.5°, 36.5°, 47.45°, 56.55°, 62.8°, and 66.14° which related to (100), (002), (101), (102), (110), (103), and (112) consistent with the JCPDS card number 5-0664 26,27. The existence of ZnO and CuO peaks suggests that the BZC nanocomposites were successfully biosynthesized28.
FTIR analysis was used to identify the functional groups in charge of producing nanoparticles and nanocomposites (Fig. 3B). The effective synthesis of CuO and ZnO nanoparticles is responsible for the low-frequency peaks between 400 and 1000 cm−129,30,31. The vibrations of stretching peaks for C–H of CH2 and CH3 groups were detected at 2862 and 2926 cm−1, respectively32. Furthermore, the peak around 1638 cm−1 is related to the group of the molecules from extract33. The peaks between 1050 and 1200 cm−1 are linked to C–O stretching vibrations of the extract's carboxylic acids and alcohols34. At 530 cm−1, the Zn–O bond stretching vibration emerged35,36. Moreover, the BZC nanocomposite spectra exhibited a peak that is ascribed to the vibrations of Zn–O and Cu–O bond.
In Fig. 4, XPS was used to examine the BZC nanocomposite’s chemical composition. The Zn, O, and Cu peaks in the XPS spectra survey are the only peaks visible in Fig. 4a. The high-resolution XPS spectrum of the BZC nanocomposite's Zn2p3, Cu 2p3, and O1s were observed. The oxidation state of Zn is + 2 in the form of ZnO in the as-prepared BZC nanocomposite, according to the strong characteristic peaks centered at 1024.08 eV (Zn2p3/2) and 1047.15 eV (Zn2p1/2) from XPS spectra of Zn 2p in Fig. 4b37. According to the Cu 2p XPS spectra exhibited in Fig. 4c, the primary peaks are positioned at 935.18 eV and 955.285 eV, and the existence of their distinctive peaks at 941.554 eV indicates that the copper is in the + 2 oxidation state in the form of CuO38. The broad O1s signal (Fig. 4d), which is consisting of three smaller peaks, indicates the presence of several metal oxide states as would be predicted. A peak at 531.66 eV is attributed to the oxygen in CuO and ZnO, while peaks at 531.337 eV and 533.209 eV are assigned to oxygen adsorbed in the form of hydroxyls and carbonates. As a result, it is assumed that the O comes from oxygen adsorbed on metal oxides.
BZC nanocomposite adsorption
The optimum conditions for removing fluorescent stain dye with BZC nanocomposites were investigated. The pH variations are expected to affect CR adsorption since the solute ions' pH can affect the degree of ionization and surface charge of the BZC. The CR dye solutions ranged in pH from 2 to 12 (Fig. 5A), with the maximum adsorption efficiency occurring at pH 5. As pH elevated, the adsorption efficiency diminished. BZC surfaces seem positively charged and the solution’s positive charge on the surface interface grows at low pH, resulting in increased CR dye adsorption. Our findings revealed that the removal capacity decreased with increasing BZC dose (Fig. 5B). The initial CR dye concentrations can significantly affect adsorbent performance and the initial CR concentration was changed from 20 to 500 mg/L, and adsorption was accomplished (Fig. 5C). The dye removal percentage reduces as the original dye concentration rises, which may be because the adsorption sites on the BZC nanocomposite surface are saturated37. The BZC nanocomposite surface will initially have unoccupied active sites at low concentrations, and as the initial dye concentration rises, these active sites will become exhausted, and the adsorption process will not be as effective38. The findings of a study on the impact of contact duration on dye removal from 5 to 150 min are shown in Fig. 5D. The CR dye removal increased gradually over time until it reached equilibrium. Our findings revealed that dye elimination improved with time and reached saturation after 120 min. Our findings reveal that the CR adsorption rate is notably high within the first hour of adsorption due to the huge surface area of BZC nanocomposite and the accessibility of active centers. The CR adsorption rate then stabilized as the BZC nanocomposite pores and active sites were exhausted39.
The amount of dye adsorption (q, mg/g) onto the BZC nanocomposite decreases with increasing temperature from 25 to 55 °C (Fig. 6). Adsorption is an exothermic process, as evidenced by the reduction in adsorption capability with increasing temperature40. Increasing the temperature may diminish the adsorption forces between the dye and the adsorption sites on the BZC surface since the adsorption capacity is being reduced41.
Adsorption isotherm
The Langmuir, Freundlich, and Temkin models, as well as their parameters, were constructed at various temperatures to better examine the removal process (Fig. 7A). The Langmuir plot intercept and slope were evaluated at various temperatures to establish the maximal removal capacity and isotherm constant (Fig. 7B). The straight line confirmed the monolayer adsorption of dye on the BZC nanocomposites (Fig. 7B). The Langmuir isotherm is the optimal model for explaining CR dye adsorption, as further supported by the excellent correlation coefficient (R2 = 0.993) (Table 1). The significant adsorption and binding of the dye to the BZC cavities was further supported by the high KL values observed and BZC removal capacity (qm) at 25 °C was 90.16 mg g−1, which is significantly higher than those of other adsorbents reported in Table S1. Unfavorable deviations were found after the data were fitted to the Freundlich and Temkin isotherm models (Fig. 7C,D).
Adsorption kinetics
In Fig. 8, the CR dye adsorption rate onto the BZC nanocomposite was initially high but decreased progressively until balance was established. After 150 min, which was considered the equilibrium time, there was a significant enhancement in the adsorption rate and maximum adsorption. The removal kinetics are critical parameters for estimating adsorption dynamics. The pseudo-first order (PFO) and pseudo-second order models (PSO) were employed to match the observations and analysis of the kinetics of CR dye removal onto BZC nanocomposites. The rate constant, K1, was determined using log (qe − qt) versus t plots, and the removal capacity at equilibrium, qe, cal, was calculated using the intercept and slope of the plot (Fig. 8A,B). The correlation coefficients obtained from the PFO were lower than the correlation coefficients obtained from PSO. Furthermore, the R2 values of the PSO (0.9977) for CR dye were significantly higher than those of the PFO (0.9803), implying that the dye removal kinetics follow the PSO. The correlation coefficients and qe (calc.) values from the PSO are coherent with the observed data (Table 2).
Thermodynamic studies
The temperature effect on the removal process is critical for practical adsorbent uses at 25 °C, 40 °C, and 60 °C (Fig. 9). The BZC nanocomposite adsorption capacity for dye was reduced when the temperature was raised from 25 to 60 °C, indicating that CR adsorption onto the BZC nanocomposite is exothermic. The calculating results of the essential thermodynamic parameters were displayed (Table 3). Physisorption changes free energy between 20 and 0 kJ mol−1, whereas chemisorption changes free energy between 80 and 400 kJ mol−1. The negative value of ∆H and ∆G confirms that the adsorption process is exothermic and spontaneous. It is confirmed that the reaction is more likely to occur as temperature rises by the increase in the negative value of ∆G°. The ∆S negative value exposed the decreased randomness (orderliness) at the BZC nanocomposite42.
Intraparticle mechanism
The dye removal using BZC nanocomposites was studied from the corresponding initial linear region slope, and the intraparticle mechanism of diffusion was demonstrated (Fig. 10). Our findings suggested that the early removal stages were reliable for controlling the mass transfer resistance to CR dye particles. The electron exchange between the BZC surfaces and the dye appears to be the rate-limiting stage in the chemisorption process. The negatively charged dye and the positively charged on the BZC nanocomposite surface could spontaneously interact to demonstrate the mechanism of adsorption. The BZC nanocomposite showed a significant capacity for CR dye adsorption in an acidic solution. The enhanced performance in an extremely acidic environment was driven through the highly charged BZC. These findings suggest that BZC is a highly applicable adsorbent for the removal of anionic dyes. The removal mechanism of CR through adsorption using BZC nanocomposite involves the physical binding of the dye molecules onto the surface of the composite material. The BZC nanosphere provides abundant active sites for CR molecules. The anionic in nature CR molecules can interact with the positively charged surface sites on the BZC composite via electrostatic forces. Additionally, there might be a chemical affinity between the functional groups on the surface of the composite material and the CR molecules which enhances the adsorption capacity. Therefore, the mechanism of CR removal using BZC nanocomposite via adsorption relies on the physical binding of the dye molecules onto the composite surface through electrostatic interactions, chemical affinity, and surface morphology, leading to the effective removal of the dye from aqueous solutions.
Selectivity studies
BZC was utilized to examine the selective trapping and capture of dye in the existence of common cationic and anionic dyes. Prior to the addition of CR dye (100 ppm), the effect of several dyes introduced at high concentration ranges on the trapping (uptake) systems was separately investigated (Fig. 11). At optimal experimental circumstances (i.e., starting concentration (10 mg/L), 0.05 g of BZC, pH of solution at 5, shaking 120 min, and temperature of 298 K), the influence of co-existing anionic and cationic dyes was examined. Our results show that there was no effect from cationic or anionic dyes in our data.
Reusability of BZC
The reusability of the designed absorbent was investigated using a strong stripping agent such as HCl solution. After elution with 0.1 M HCl solution, the separation (collection) of dye trapped by BZC was studied. After successive adsorption–desorption cycles, we noticed a shift in BZC removal capacity. The examined BZC adsorbent (i.e., CR dye-loaded adsorbent) was regenerated by adding BZC (0.02 g) and carefully washing it with HCl (0.1 M) numerous times until the pH of the washing solution reached 7. The BZC was then rinsed many times with distilled water and the remaining colors were extracted using ethanol. The clean BZC was collected and baked at 60 °C for 4 h and the regenerated BZC nanocomposite was utilized in the removal experiment. The adsorbent's regeneration efficiency after each adsorption/desorption cycle was determined to be 95.6 percent as shown in Fig. S1. The BZC nanocomposite adsorption site blockage may be the cause of the little decrease in regeneration efficiency. Our finding is referred to as BZC cost-efficient when used in several cycles while maintaining its efficiency for dye removal, separation, and recovery after regeneration.
Conclusion
The indirect discharge of vast volumes of toxic dyes into water has had a significant impact on the ecosystem. In this manuscript, eco-friendly BZC nanocomposites were fabricated via using the green protocol. Our results investigate the successful fabrication of ZnO/CuO nanocomposite with chain-like morphology. Moreover, the CR dye removal was studied using BZC nanocomposite under optimal adsorption process. The worm-like structure of BZC nanocomposite were accomplished for trapping CR dye. The BZC adsorbent was generated with an active positive charged surface throughout, which was greatly influenced by the adsorption conditions, such as the solution pH. Our findings show that the high removal capacity of CR dye using BZC was observed and preserved after the regeneration process. The BZC adsorbent provided a green, low-cost, and simple procedure for the removal of fluorescent azo dye for water purification and industrial wastewater control. In conclusion, there are a number of prospective applications for the adsorption of organic dyes utilizing nanomaterials. In addition to environmental remediation, other potential research areas include industrial wastewater treatment, the creation of effective dye elimination systems for the textile industry, and the production of sophisticated filtering membranes for water purification.
Data availability
All data generated or analyzed during this study are included in this published article and its supplementary information files.
References
Hu, Z., Chen, H., Ji, F. & Yuan, S. Removal of Congo red from aqueous solution by cattail root. J. Hazard. Mater. 173(1–3), 292–297 (2010).
Katheresan, V., Kansedo, J. & Lau, S. Y. Efficiency of various recent wastewater dye removal methods: A review. J. Environ. Chem. Eng. 6(4), 4676–4697 (2018).
Bhatia, D., Sharma, N. R., Singh, J. & Kanwar, R. S. Biological methods for textile dye removal from wastewater: A review. Crit. Rev. Environ. Sci. Technol. 47(19), 1836–1876 (2017).
Dawood, S. & Sen, T. Review on dye removal from its aqueous solution into alternative cost effective and non-conventional adsorbents. J. Chem. Process Eng. 1(104), 1–11 (2014).
Kandisa, R. V., Saibaba, K. V. N., Shaik, K. B. & Gopinath, R. Dye removal by adsorption: A review. J. Bioremed. Biodegrad. 7(6), 1–4 (2016).
Yagub, M. T., Sen, T. K., Afroze, S. & Ang, H. M. Dye and its removal from aqueous solution by adsorption: A review. Adv. Colloid Interface Sci. 209, 172–184 (2014).
Sayed, M. A., Ahmed, M. A., El-Shahat, M. F. & El-Sewify, I. M. Mesoporous polyaniline/SnO2 nanospheres for enhanced photocatalytic degradation of bio-staining fluorescent dye from an aqueous environment. Inorg. Chem. Commun. 139, 109326 (2022).
Fakhar-e-Alam, M. et al. Assessment of green and chemically synthesized copper oxide nanoparticles against hepatocellular carcinoma. J. King Saud Univ. Sci. 33(8), 101669 (2021).
Raza, S. H. et al. Foliar application of nano-zinc oxide crystals improved zinc biofortification in cauliflower (Brassica oleracea L. var. botrytis). Appl. Nanosci. 12(6), 1803–1813 (2022).
Munir, T., Mahmood, A., Rasul, A., Imran, M. & Fakhar-e-Alam, M. Biocompatible polymer functionalized magnetic nanoparticles for antimicrobial and anticancer activities. Mater. Chem. Phys. 301, 27677 (2023).
Das, S. & Srivastava, V. C. An overview of the synthesis of CuO-ZnO nanocomposite for environmental and other applications. Nanotechnol. Rev. 7(3), 267–282 (2018).
Li, B. & Wang, Y. Facile synthesis and photocatalytic activity of ZnO–CuO nanocomposite. Superlattices Microstruct. 47(5), 615–623 (2010).
Ashok, C. H., Rao, K. V. & Chakra, C. H. S. Facile synthesis and characterization of ZnO/CuO nanocomposite for humidity sensor application. J. Adv. Chem. Sci. 2(2), 223–226 (2016).
Fouda, A., Salem, S. S., Wassel, A. R., Hamza, M. F. & Shaheen, T. I. Optimization of green biosynthesized visible light active CuO/ZnO nano-photocatalysts for the degradation of organic methylene blue dye. Heliyon 6(9), e04896 (2020).
Elfeky, A. S. et al. Multifunctional cellulose nanocrystal/metal oxide hybrid, photo-degradation, antibacterial and larvicidal activities. Carbohydr. Polym. 230, 115711 (2020).
Fouda, A. et al. Eco-friendly approach utilizing green synthesized nanoparticles for paper conservation against microbes involved in biodeterioration of archaeological manuscript. Int. Biodeterior. Biodegrad. 142, 160–169 (2019).
Hassan, S. E. D. et al. Endophytic actinomycetes Streptomyces Spp mediated biosynthesis of copper oxide nanoparticles as a promising tool for biotechnological applications. JBIC J. Biol. Inorg. Chem. 24(3), 377–393 (2019).
Sakib, A. A. M. et al. Synthesis of CuO/ZnO nanocomposites and their application in photodegradation of toxic textile dye. J. Compos. Sci. 3(3), 91 (2019).
Vibitha, B. V., Anitha, B., Tharayil, N. J., Green synthesis of ZnO: CuO nanocomposites by Aloe Barbadansis Leaf Extract: structure and photo catalytic properties. Proc. AIP Conference Proceedings. 2287, 20031 (2020).
Mahmood, A. et al. Analyses of structural and electrical properties of aluminium doped ZnO-NPs by experimental and mathematical approaches. J. King Saud Univ. Sci. 34(2), 101796 (2022).
Corciova, A. et al. Antioxidant, antimicrobial and photocatalytic activities of silver nanoparticles obtained by bee propolis extract assisted biosynthesis. Farmacia 67, 482–489 (2019).
Popova, M., Trusheva, B. & Bankova, V. Chemistry and Applications of Propolis. In Gums, Resins and Latexes of Plant Origin: Chemistry, Biological Activities and Uses 1–33 (Springer, 2021).
Hajji, M., Ajili, M., Jebbari, N. & Kamoun, N. T. Photocatalytic performance and solar cell applications of coupled semiconductor CuO–ZnO sprayed thin films: Coupling effect between oxides. Opt. Mater. 140, 113798 (2023).
Vo, N. T. T., You, S. J., Pham, M. T. & Van Pham, V. A green synthesis approach of pn CuO/ZnO junctions for multifunctional photocatalysis towards the degradation of contaminants. Environ. Technol. Innov. 32, 103285 (2023).
Nabila, M. I. & Kannabiran, K. Biosynthesis, characterization and antibacterial activity of copper oxide nanoparticles (CuO NPs) from actinomycetes. Biocatal. Agric. Biotechnol. 15, 56–62 (2018).
Luque, P. A. et al. Green synthesis of zinc oxide nanoparticles using Citrus sinensis extract. J. Mater. Sci. 12, 9764–9770 (2018).
Fouda, A., El-Din Hassan, S., Salem, S. S. & Shaheen, T. I. In-Vitro cytotoxicity, antibacterial, and UV protection properties of the biosynthesized Zinc oxide nanoparticles for medical textile applications. Microb. Pathog. 125, 252–261 (2018).
Widiarti, N., Sae, J. & Wahyuni, S. Synthesis CuO-ZnO nanocomposite and its application as an antibacterial agent. Mater. Sci. Eng. 172(1), 012036 (2017).
Jafarirad, S., Mehrabi, M., Divband, B. & Kosari-Nasab, M. Biofabrication of zinc oxide nanoparticles using fruit extract of Rosa canina and their toxic potential against bacteria: A mechanistic approach. Mater. Sci. Eng. C 59, 296–302 (2016).
Jayaprakash, J., Srinivasan, N., Chandrasekaran, P. & Girija, E. Synthesis and characterization of cluster of grapes like pure and Zinc-doped CuO nanoparticles by sol–gel method. Spectrochim. Acta Mol. Biomol. Spectrosc. 136, 1803–1806 (2015).
Mahmoud, B. G., Khairy, M., Rashwan, F. A., Foster, C. W. & Banks, C. E. Self-assembly of porous copper oxide hierarchical nanostructures for selective determinations of glucose and ascorbic acid. RSC Adv. 6, 14474–14482 (2016).
Bayrami, A., Parvinroo, S., Habibi-Yangjeh, A. & Rahim Pouran, S. Bio-extract-mediated ZnO nanoparticles: Microwave-assisted synthesis, characterization and antidiabetic activity evaluation. Artif. Cells Nanomed. Biotechnol. 46(4), 730–739 (2017).
Nithiyavathi, R. et al. Gum mediated synthesis and characterization of CuO nanoparticles towards infectious disease-causing antimicrobial resistance microbial pathogens. J. Infect. Public Health. 14(12), 1893–1902 (2021).
Zhou, L. et al. Natural product recovery from bilberry (Vaccinium myrtillus L.) presscake via microwave hydrolysis. ACS Sustain. Chem. Eng. 6, 3676–3685 (2018).
Pirhashemi, M. & Habibi-Yangjeh, A. Ultrasonic-assisted preparation of novel ternary ZnO/Ag3VO4/Ag2CrO4 nanocomposites and their enhanced visible-light activities in degradation of different pollutants. Solid State Sci. 55, 58–68 (2016).
Asamoah, R. B. et al. Synthesis and characterization of zinc and copper oxide nanoparticles and their antibacteria activity. Results Mater. 7, 100099 (2020).
Bilal, M., Ihsanullah, I., Shah, M. U. H., Reddy, A. V. B. & Aminabhavi, T. M. Recent advances in the removal of dyes from wastewater using low-cost adsorbents. J. Environ. Manag. 321, 115981 (2022).
Hassan, A. F. & Elhadidy, H. Production of activated carbons from waste carpets and its application in methylene blue adsorption: Kinetic and thermodynamic studies. J. Environ. Chem. Eng. 5(1), 955–963 (2017).
Parvin, S., Rahman, M. W., Saha, I., Alam, M. J. & Khan, M. M. R. Coconut tree bark as a potential low-cost adsorbent for the removal of methylene blue from wastewater. Desalin. Water Treat. 146, 385–392 (2019).
Sarma, G. K., Sen Gupta, S. & Bhattacharyya, K. G. Removal of hazardous basic dyes from aqueous solution by adsorption onto kaolinite and acid-treated kaolinite: Kinetics, isotherm and mechanistic study. SN Appl. Sci. 1, 1–15 (2019).
Idan, I. J., Abdullah, L. C., Choong, T. S. Y. & Jamil, S. N. A. B. M. Equilibrium, kinetics and thermodynamic adsorption studies of acid dyes on adsorbent developed from kenaf core fiber. Adsorpt. Sci. Technol. 36(1–2), 694–712 (2018).
Kumar, V. Adsorption kinetics and isotherms for the removal of rhodamine B dye and Pb+2 ions from aqueous solutions by a hybrid ion-exchanger. Arab. J. Chem. 12(3), 316–329 (2019).
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
S.O.M., make the experiments for the nanosphere adsorbent preparation and their application in the dye adsorption. A.R. analysis of the data, drawing the figures, writing the first draft of the manuscript. I.M.E., analysis of the data, revising the first draft of the manuscript. M.M.H.K., suggesting the research idea, supervising all steps of adsorbent preparation and their application, supervising the interpretation of research results, reviewing the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Radwan, A., Mohamed, S.O., Khalil, M.M.H. et al. Effective adsorption of fluorescent congo red azo dye from aqueous solution by green synthesized nanosphere ZnO/CuO composite using propolis as bee byproduct extract. Sci Rep 14, 9061 (2024). https://doi.org/10.1038/s41598-024-58306-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-024-58306-1
Keywords
This article is cited by
-
Efficient water purification: CuO-enhanced biochar from banana peels for removing Congo red dye
Environmental Science and Pollution Research (2024)
-
Design and research of multi-information fusion RFID sensor for fruit and vegetable quality detection
Microchimica Acta (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.