Abstract
In this paper, we present the first experimental evidence of the piezoelectric nature of struvite (MgNH4PO4·6H2O). Using a single diffusion gel growth technique, we have grown struvite crystals in the form of plane parallel plates. For struvite crystals of this shape, we measured the piezoelectric coefficients d33 and d32. We have found that at room temperature the value of piezoelectric coefficient d33 is 3.5 pm/V, while that of d32 is 4.7 pm/V. These values are comparable with the values for other minerals. Struvite shows stable piezoelectric properties up to the temperature slightly above 350 K, for the heating rate of 0.4 K/min. For this heating rate, and above this temperature, the thermal decomposition of struvite begins, which, consequently, leads to its transformation into dittmarite with the same non-centrosymmetric symmetry as in case of struvite. The struvite-dittmarite transformation temperature is dependent on the heating rate. The higher the heating rate, the higher the temperature of this transformation. We have also shown that dittmarite, like struvite exhibits piezoelectric properties.
Similar content being viewed by others
Introduction
Struvite is a mineral first identified and described by Ulex in 18451. Struvite is magnesium ammonium phosphate hexahydrate, the chemical formula of which is MgNH4PO4⋅6H2O. It crystallizes in the orthorhombic system, in space group Pmn21 and has the following unit cell parameters: a = 6.9650(2) Å, b = 6.1165(2) Å, c = 11.2056(3) Å2. Struvite forms transparent crystals that can become white, which is a sign of a gradual loss of water of crystallization.
In the light of extensive research, it can be stated that struvite has been studied for several reasons. First of all, struvite is the most common mineral found in infectious urinary stones. Infectious urinary stones are the result of urinary tract infection with urease-producing bacteria, mainly of the Proteus species. Urease is a bacterial enzyme that breaks down urea, physiologically present in urine, into carbon dioxide and ammonia. This decomposition initiates a whole series of chemical reactions that lead to the crystallization of various solid phases, of which struvite is the main phase3,4,5,6. Such stones pose a serious problem, the more so as a continuous increase in the incidence of infectious stones has been observed, especially in highly developed countries.
Struvite also poses a problem in wastewater treatment plants because it easily precipitates in specific places, clogging pipes, and other devices7,8,9,10,11,12,13. Struvite formation is strongly related to the wastewater pH level; the higher the pH, the greater the crystallization potential of struvite. On the other hand, struvite is a potential source of phosphorus, nitrogen, and magnesium, therefore it is the main compound recovered from wastewater and transformed into a useful fertilizer containing these elements (e.g. Refs.14,15,16,17). Struvite recovery from wastewater is particularly important due to phosphorus10,18,19 because natural sources of phosphorus free from heavy metals are ever more rare. Phosphorus, nitrogen, and potassium are the three main elements necessary for plant life. That is why many fertilizers contain phosphates, and phosphorus recovery from wastewater, in particular from struvite, proves very important.
Recently, struvite has been found to be a ferroelectric20. Ferroelectric properties, in particular spontaneous polarization, as indicated in Ref.20, may affect the interaction of bacteria with struvite crystals in urine, as well as interaction with admixtures inhibiting or accelerating the growth of these crystals. Struvite, as a ferroelectric crystal, should also be a piezoelectric crystal. Piezoelectrics are materials in which an electric field can be generated by mechanical stress applied. Piezoelectrics also exhibit reverse piezoelectric phenomenon, consisting of the appearance of mechanical stress (change in crystal size) under the influence of an applied electric field. The piezoelectric effect was discovered in 1880 by brothers Pierre and Jacques Curie21. There are different types of materials that exhibit piezoelectric properties. Piezoelectric materials can be in the form of single crystals (the best known natural piezoelectric material is quartz, SiO2), polycrystals (usually ceramics), and non-crystalline materials (such as polymers)22. There are different mechanisms causing the piezoelectric effect. Crystalline materials exhibit a piezoelectric effect due to their unique crystal structure. Struvite is a single crystal and additionally a mineral and belongs to the mm2 point group, which is one of the 20 point groups in which the piezoelectric effect is possible.
The aim of the research presented in this paper is the experimental measurement of the piezoelectric effect of struvite depending on temperature, and its description. This phenomenon for struvite has not been described in the literature so far, although struvite is indicated as a piezoelectric material in Ref.23.
Materials and methods
Growth of struvite crystals
To measure the piezoelectric effect, it is necessary to have a crystal of a specific size in the form of a flat plate. We have grown such crystals in a metasilicate gel environment, using a single diffusion gel growth technique. We used the same crystal growth method for studies on struvite ferroelectricity. This method is described in Ref.20. Here, it can only be said briefly that all reagent-grade purity chemicals used were purchased from Sigma Aldrich. For the gel preparation we used anhydrous sodium metasilicate (Na2SiO3; SMS), ammonium dihydrogen phosphate (NH4H2PO4; ADP), and magnesium acetate tetrahydrate (Mg(CH3COO)2∙4H2O). The chemicals were dissolved in distilled water. A 0.5 M aqueous ADP solution and 1.07 specific gravity SMS solution were mixed in appropriate amounts to obtain a pH of 7.0. The mixture prepared in this way was poured into 19 cm long tubes with a diameter of 3 cm and allowed to gel for 24 h. After gelation, 25 ml of 1 M magnesium acetate tetrahydrate was gently poured onto the surface of the newly formed gel in test tubes and closed with a lid. The crystal growth usually lasted for three to four weeks. After this time, struvite crystals had the form of rectangular platelets about 1 cm long along the b axis. An example photo of such a crystal is shown in Fig. 1a. The Miller indices of the crystal faces (Fig. 1b) were determined using the X-ray diffraction method, as described in Ref.2.
Piezoelectric effect measurement
Two methods were used to determine the piezoelectric properties. For both of these methods, the struvite crystal was in the form of a plane parallel plate (as shown in Fig. 1a,b). However, to measure the piezoelectric effect, the struvite crystal with surface (001) (as in Fig. 1) was polished to a size of 5.125 × 1.25 × 0.3 mm with the longest edge parallel to the b axis. This geometry is needed for measuring the d32 coefficient (as shown for example in Ref.24 in Fig. 1). Silver electrodes were deposited on opposite faces (001) and \(\left( {00\overline{1}} \right)\). Miller indices of faces were determined on the basis of XRD data presented in Ref.2. Prior to making measurements the sample was poled in d.c. electric field at 293 K. The piezoelectric properties reached a saturation state for the poling field of strength 15 kV/cm, significantly more extensive than the value of the coercive field assumed 6 kV/cm, reported by us in Ref.20.
The first method used was related to measurements of piezoelectric resonances, in order to calculate the d32 piezoelectric coefficient. To find the piezoelectric frequencies, the complex admittance Y was measured as a function of frequency f using Hewlett-Packard 4192A impedance analyser. The measurements of the absolute Y and phase angle θ were carried out with sinusoidal voltage of 1 V. Small step frequency was used to detect the admittance changes near the resonance frequencies accurately. The forced damped harmonic oscillator model was applied to calculate the complex elastic compliances, coefficient of electromechanical coupling k32, low-frequency permittivity ε33 and finally, the piezoelectric coefficient d32 (Fig. 3).
In the second method which used the inverse piezoelectric effect, quasi-static strain was measured for the same poled sample as that used in dynamic method. Mathematically, the strain can be represented as follows:
where \(\eta_{i}\), \(d_{ij}\) and \(E_{j}\) stand for strain tensor, piezoelectric coefficient, and electric field, respectively. A quasi-static method based on capacitance sensor was used to determine the piezoelectric strain \({\eta}_{3}\) in crystals under the electric field applied. η3 denotes the strain of lattice along the [001] axis. Details of the measurement method can be found in Ref.25. Sample deformation was induced by alternating electric field E of frequency 160 Hz applied to the sample and transferred via a quartz rod with one end placed on the sample surface and the other one connected to the plate of capacitor sensor with the capacity of C0. The value of C0 was adjustable, to optimize resolution depending on the magnitude of strain being measured. The frequency of 160 Hz was chosen to avoid external noise and to minimize experimental error. The surface area of the end of quartz rod touching the crystal was of the order of 0.1 mm2. Piezoelectric deformation appeared synchronously with the applied voltage of angular frequency ω causing changes ∆Cp of sensor capacity C0. The changes in capacity C over time t can be expressed by the equation: C(t) = C0 + ΔCp · sin(ωt). ΔCp was determined through recording of the current by means of a lock-in amplifier and the piezoelectric strain amplitude \({\eta}_{3}\) was calculated from the relation
where S is the surface of sensor capacitance plates, d is the thickness of the sample, and ε0 is the vacuum permittivity. From the η3 strain, the piezoelectric coefficient d33 can be determined from the relation
Since the strain was measured on the poled crystal (surface (001)) and an electric field E3 was applied along the direction [001], the piezoelectric coefficient d33 could be determined.
Differential scanning calorimetry (DSC) measurements
The DSC measurements were made with DSC 200 F3 differential scanning calorimeter (NETZSCH). The measurements were performed under the flow of analytical grade 6.0 nitrogen (flow rate 20.0 cm3/min) in the temperature range of 293.16–413.16 K with heating rate of 0.4 and 1.2 K/min, and 293.16–433.16 K with heating rate of 2.0 K/min. The samples were sealed in crucibles with internal size fitting the size of single crystals used for measurement. Each measurement was done for one single crystal. Aluminum crucibles were used with a mass difference between them smaller than 0.005 mg. Specific heat capacity of all crucibles was tested before measurements and the difference between the reference crucible and crucible containing sample was not larger than 0.01 J/g. The temperature and enthalpy were calibrated with the use of six spectrally pure standards: adamantane, In, Sn, Bi, Zn, and CsCl. Each measurement was done in triplicate (for the same heating rate and temperature range) and the mass of samples was in the range of 3.861–17.040 mg. For all repetitions of measurements for the same conditions, the calculated enthalpies were equal within reported significant figures.
Thermogravimetry/differential thermal analysis (TG/DTA)
Thermal analysis was carried out in STA 449 F1 TG–DTA/FTIR/QMS (NETZSCH) system of thermogravimetric analyser, coupled with infrared (IR) and mass spectrometer. The samples (mass: 10.031–10.976 mg) were heated in open corundum crucibles up to the temperatures in the range of 293.16–413.16 K with heating rate of 0.4 and 1.2 K/min in analytical grade 6.0 nitrogen. The volatile products of the decomposition process were determined from simultaneously registered IR and mass spectra.
X-ray powder diffraction
The X-ray powder diffraction (XRPD) patterns were measured in reflection mode on XPert PRO X-ray powder diffraction system equipped with Bragg–Brentano PW 3050/65 high resolution goniometer and PW 3011/20 proportional point detector. The Cu Kα1 radiation was used. The patterns were measured at 291.0(2) K in the range of 5–90° with the narrowest beam attenuator. Diamond powder was used as an internal reference. The samples were sprinkled onto the sample holders using a small sieve, to avoid preferred orientation. The thicknesses of the samples were no more than 0.1 mm. During the measurements, each specimen was spun in the specimen plane to improve particle statistics. Continuous coupled ω-2θ scan mode was used during measurement. X’Pert HighScore Plus26 software was used for data collection and data processing. The reference pattern was taken from Powder Diffraction File27.
Results and discussion
For the sample prepared according to the procedure described in Sect. Piezoelectric effect measurement, the d32 piezoelectric coefficient was measured using the resonance method. Prior to measurements, the sample was polished to the thickness of 0.3 mm. Struvite has a good (001) cleavage plane28,29 perpendicular to the polar axis which greatly facilitates the preparation of thin plates. Figure 2a presents randomly oriented domains for the crystal before poling process, while Fig. 2b presents single-domain state of the crystal after poling in the d.c field. To visualise the domains, we have used the technique described in Ref.20. After poling, according to procedure mentioned in Sect. Piezoelectric effect measurement, the Y(f) dependencies were collected as a function of temperature. These dependencies are presented in Fig. 3. With temperature increase the resonance frequency shifted towards lower frequencies. Based on these data the temperature dependence of the d32 piezoelectric coefficient, estimated from the resonance frequency fr (local maximum od admittance, Y) and antiresonance frequency fa (local minimum of admittance, Y), was drawn. The method for determination of piezoelectric coefficients is described elsewhere30.
We have found that the piezoelectric properties described by d32 are not strongly dependent on temperature in the range from room temperature to 320 K. We have repeated the dependence as that in Fig. 3 a few times and no changes have been found. Since we wanted to measure the d33(T) dependence (Figs. 4 and 5) for the same poled crystal, we did not continue the measurements by resonance technique to a higher temperature to avoid the crystal decomposition.
Figure 4 shows the linear dependence of strain η3 versus electric field E3 in the range of the strengths up to 4 kV/cm. We have chosen this field strength in order not to destroy the single domain state (the coercive field for struvite, as reported in Ref.20 is of the order of 6 kV/cm). It was confirmed by a linear function of the polarization P versus E observed simultaneously throughout the quasi-static measurements. The d33 piezoelectric module has been calculated from the linear η3(E3) run (Eq. (3)) and amounts to 3.5 ± 0.2 pm/V.
However, essential changes have been found in a much broader temperature range. Namely, the piezoelectric properties are observed up to 390 K (Fig. 5). Up to the temperature of 352.5 K, the value of the d33 piezoelectric coefficient oscillates around the value of 3.5 pm/V, which is characteristic for the temperature of 293 K. As can be seen in Fig. 5, above 352.5 K, the d33 piezoelectric coefficient increases irregularly and finally the dependence d33(T) drastically goes to a minimal value for 380 K. Interestingly, above this temperature, we still observe the piezoelectric response. This sudden decrease in the value of the d33 coefficient may indicate that at 380 K we are dealing with the transformation of struvite into a different structure. The irregularity that appears above the temperature of 352.5 K may indicate that this transformation begins just from this temperature. It should also be kept in mind that the results presented in the Fig. 5 were obtained for a temperature rate equal to 0.4 K/min.
To test whether struvite undergoes any transformation with increasing temperature, struvite was heated under controlled conditions. Initially, struvite was heated in open crucibles. Such heating leads to its decomposition to magnesium hydrogen phosphate (MgHPO4). The process of decomposition starts after reaching the temperature of 333 K and from the beginning it is accompanied by releasing gaseous water and ammonia molecules (Figs. 6 and 7). Mass spectra contain two principal signals with m/z of 17 and 18 (m/z is the mass-to-charge ratio value), which also confirms the formation of NH3 and H2O as gaseous products. This finding is in agreement with the previously published results concerning the thermal decomposition of struvite31. Despite the accordance with the literature, this measurement did not answer the question of what happens to struvite at 380 K, as it is observed in the measurement of piezoelectric properties. That is why we have decided to measure the thermal decomposition of struvite under conditions as close as possible to those during the piezo-effect measurements. To get the piezoelectric response, silver electrodes were applied to faces (001) and \(\left( {00\overline{1}} \right)\). Assuming that these electrodes could influence the process of thermal decomposition of struvite, we measured the process of thermal decomposition by placing struvite in a sealed crucible matching the crystal size (see Materials and Methods). The crystals adhered to the bottom and cover of the crucible with faces (001) and \(\left( {00\overline{1}} \right)\), respectively. This procedure of the crystal faces adhering to the crucible was to imitate the existence of silver electrodes.
Changes in the environment of the crystal influence both the decomposition process and the resulting product. We have checked that single crystals of struvite heated in sealed crucibles are stable in chemical composition up to 366.5–378.5 K, depending on the heating rate (Fig. 8, Table 1).
Then, for all samples, a well distinguishable exothermic process is observed which leads to development of a thermally stable product. In other words, under experimental conditions, struvite is transformed into another stable product. The temperature for completion of this transformation varies from 386.9 to 398.8 K depending on the heating rate (Fig. 8 and Table 1). The typical effect of an increase in decomposition temperature and measured specific enthalpy with increase in heating rate is observed (Table 1), resulting from differences in energy flux for experiments with different set up.
To make sure that the final product obtained on heating is stable, we performed another experiment. After phase transformation, the samples were cooled to the initial temperature. As can be seen in Fig. 9, cooling the samples back to the starting temperature did not produce any sharp or evident energetic effect. Only a smooth change of enthalpy is observed in the whole measurement range, and this proves that the process observed on heating is irreversible and the final product is stable. There are reports in the literature (e.g. Ref.32) that dittmarite can turn into struvite in a sufficiently long time when exposed to high humidity air. We did not observe such a process under the conditions of our experiment.
For the heating rate of 0.4 K/min, in the case of piezo-effect measurements, we obtained an irregular increase in the value of d33, starting from the temperature of 352.5 K (Fig. 5). These irregularities may indicate a change in the chemical composition of the test sample. Comparing this result with the result obtained from DSC measurements for the same heating rate, we see that struvite is stable in terms of its chemical composition up to the temperature of 366.5 K (Fig. 8a). At first glance, it may seem that these temperatures do not coincide. However, it should be borne in mind that despite the fact that during the DSC measurements we tried to imitate the conditions prevailing during the piezo-effect measurement as well as possible, these conditions were not identical. This is how we explain the difference in these temperatures. From the measurements of the piezoelectric effect (Fig. 5) we can also see that at the temperature of 380 K we observe a sharp decrease in d33, but above this temperature we still observe a piezoelectric response. As suggested earlier, this may be related to the decomposition of struvite into a different structure. In the DSC tests, at the same heating rate of 0.4 K/min, the conversion of struvite into a different structure finalizes at 386.9 K (Fig. 8a and Table 1). Because the piezoelectric and DSC experiments were not performed at exactly the same conditions, these two temperatures coincide quite well.
So, the question remained concerning the structure and chemical composition of this end product. To check that, XRPD patterns were registered. In all cases, dittmarite is the sole phase observed (Fig. 10). Dittmarite is a mineral with the chemical formula of MgNH4PO4·H2O (chemical formula for struvite is MgNH4PO4⋅6H2O). It crystallizes in the orthorhombic system with the Pmn21 space group, i.e. the space group is the same as in the case of struvite. The unit cell parameters of the obtained dittmarite (determined on the basis of the XRPD pattern, Fig. 10b) are as follows: a = 5.620 Å, b = 8.745 Å, c = 4.783 Å. This means that when struvite is heated under the conditions described, it transforms from magnesium ammonium phosphate hexahydrate into magnesium ammonium phosphate monohydrate, with a simultaneous change in unit cell parameters.
To evaluate the influence of higher heating rates, as well as prolonged annealing time, on the final product, the single crystal put in the sealed crucible was inserted into the furnace, heated to 393 K and kept there for 90 min. In such experiment, dittmarite was also observed as the final product. This proves that the formation of dittmarite in sealed crucible is independent of the heating rate and annealing time. All measured dittmarite samples had a high degree of crystallinity (amorphous phase scattering was not observed in any XRPD pattern) and had a large size of crystallites (the observed broadening of reflections was the same as for microcrystalline standard and originated only from instrumental broadening). It should be noted that in all crucibles unsealed after DSC measurement the crystals retained their shape. The transformation of struvite into dittmarite has been reported many times in the literature32,33,34,35,36,37. The researchers indicated that such a transformation in air (not in solution) depends on temperature and heating rate, which is also confirmed by our research.
It must be outlined that imperfections of struvite crystals alter the smoothness of the DSC curve and cause the occurrence of additional local energy maximum. For example, the presence of visible dislocation in crystal led to the emergence of additional maxima at 384.5 K for temperature rate of 2.0 K/min (Fig. 11) and breakage of crystal into two parts, along observed dislocation. This can be explained by strain existing in the crystal after water has been released which splits the crystal exactly in the defect area, i.e. in the weakest point of the crystal lattice. In all the measured crystals with defects, the local maximum emerges from the global maximum when water loss is sufficient for strain relaxations, and it occurs before the global maximum of the struvite → dittmarite conversion process.
The observed results imply that the complete closing of the single crystal of struvite in a crucible (or any other vessel) is sufficient for crystalline dittmarite to be formed when heating above 370 K.
The FTIR, DSC and XPRD tests clearly show that struvite heated in sealed crucibles remains stable in terms of chemical composition up to the temperature of 366.5–378.5 K, depending on the heating rate. For the heating rate of 0.4 K/min, for which piezo-effect measurements were made, the temperature of 352.5 K for which irregularities in the variability of d33 are observed—which may indicate a change in the chemical composition of the sample—corresponds quite well with the results obtained from DSC tests, taking into account the fact that measurement conditions were not identical in both measurement techniques. As a consequence, the process of changing the chemical composition of struvite leads to the final product, which is dittmarite.
Based on these results, we can conclude that the piezoelectric response observed above the temperature of 380 K (Fig. 5) is a dittmarite response. Dittmarite is non-centrosymmetric, it crystallizes in the same space and point group as struvite and exhibits a piezoelectric effect either. Hence, this article presents the first experimental evidence regarding the piezo-effect in dittmarite to the best of our knowledge. However, we were unable to determine precisely the coefficient of the piezoelectric tensor.
The struvite-dittmarite transformation at 380 K was also confirmed through measurements of the permittivity as a function of temperature. Figure 12 shows dependencies of ε33(T), for four different frequencies, in the temperature range in which transformation to the dittmarite structure takes place.
As shown in Fig. 12, the fastest changes in the course of ε33(T) start above 350 K, which is approximately the temperature at which the change in the chemical composition of struvite begins. Moreover, this Figure shows a weak dielectric dispersion in the temperature range 300–380 K and frequency range 10 kHz to 1 MHz. The most important result is a clear transformation into dittmarite structure at 380 K. After exceeding this temperature, the dependence ε33(T) no longer resembles that for struvite and decreases almost twice. The fact that ε33(T) is not repeatable after two heating–cooling cycles means that to get complete transformation into dittmarite, one has to be at the temperature higher than 380 K. As results from DSC measurements (Fig. 8a and Table 1), the temperature of completion of struvite transformation into dittmarite is 386.9 K for the heating rate of 0.4 K/min.
As our results presented in this paper show, piezoelectric coefficients d33 and d32 observed for struvite crystals at room temperature are 3.5 pm/V and 4.7 pm/V, respectively. Struvite is a mineral, so it is worth comparing the piezo-response of other minerals. In the review38 piezoelectric constants d33 for various minerals are presented. One of the lowest values of d33 is exhibited by mineral boracite, for which the d33 is 0.6 pm/V at room temperature. For ice, d33 is 2 pm/V at 0 °C, and for tourmaline, d33 is 33 pm/V at room temperature. As it results from Ref.38, the highest value of d33 exhibits mineral stibiotantalite, for which d33 is 370 pm/V at room temperature. It must therefore be concluded that struvite has a d33 value which is typical for minerals, but within the range of smaller values. The d32 value obtained for struvite is much more difficult to compare with the values for other crystals because it is determined much less frequently. We have managed to find the d32 coefficient values for two minerals: magnetite38 and changbaiite (lead niobate)39. For magnetite, d32 and d33 values are given for − 269 °C as higher than 0.06 pm/V and 0.25 pm/V, respectively. For changbaiite, the coefficients d32 and d33 are equal to 24 pm/V and 60 pm/V39, respectively. Comparing the d32 and d33 values for magnetite and changbaiite may indicate that the d32 coefficients are smaller than the d33 ones. A similar relationship is often observed also for crystals, which are not minerals (e.g. Ref.40). In the case of struvite, we observe the inverse relationship. This means that this issue requires additional research. It is known that the physical properties of the crystal, including the piezoelectric properties, depend on the non-centrosymmetric structure of the crystal. The structure of struvite is known to consist of PO43- and NH4+ tetrahedra and Mg[H2O]62+ octahedra bound by hydrogen bonds41. PO4 tetrahedra are regular, while Mg[H2O]62+ octahedra are very distorted41. In addition, there are net electric dipole in struvite resulting from the existence of spontaneous polarization20. It is known that piezoelectric properties can be influenced by symmetry elements resulting from the space group, but in the case of struvite, the contribution of these elements to piezoelectric properties should be analysed from the point of view of distorted octahedra and net moment dipole. Only such an analysis can provide credible evidence for the origin of piezoelectricity in struvite as well as explain the relationship between d32 and d33. This remains a challenge for future research.
Conclusions
To the best of our knowledge, this paper presents the first experimentally confirmed piezoelectric properties of struvite. We have found that at room temperature the d33 coefficient is 3.5 pm/V, while that of d32 is 4.7 pm/V. These are typical values for minerals, within the range of lower values. These coefficients do not change significantly with increasing temperature. However, struvite reveals the piezoelectric properties up to a specific temperature that depends on the rate at which the crystal is heated. At the rate 0.4 K/min, struvite shows stable piezoelectric properties up to 352.5 K. Above this temperature, for that heating rate, struvite begins to lose ammonia and crystallization water and undergoes transformation into a monohydrate form, i.e. dittmarite. The temperature of this transformation is dependent on heating rate of the crystal. The higher the heating rate, the higher the temperature of this transformation. Dittmarite is stable and does not convert to struvite during the cooling process. Dittmarite, like struvite, is non-centrosymmetric and also exhibits piezoelectric properties that, to the best of our knowledge, have not been reported yet.
There are still many challenges to be faced regarding the crystallization of struvite, either in wastewater treatment plants or in the context of infectious urinary stones. We believe that studies concerning the piezoelectric effect reported in this paper will introduce further research into other struvite-related phenomena.
References
Ulex, G. L. On struvite, a new mineral. Mem. Proc. Chem. Soc. 3, 106–110 (1845).
Prywer, J., Sieroń, L. & Czylkowska, A. Struvite grown in gel, its crystal structure at 90 K and thermoanalytical study. Curr. Comput.-Aided Drug Des. 9, 89. https://doi.org/10.3390/cryst9020089 (2019).
McLean, R. J. C., Nickel, J. C., Cheng, K. J. & Costerton, J. W. The ecology and pathogenicity of urease-producing bacteria in the urinary tract. Crit. Rev. Microbiol. 16, 37–39 (1988).
Amtul, Z., Atta-ur-Rahman, R. A. & Siddiqui, M. I. C. Chemistry and mechanism of urease inhibition. Curr. Med. Chem. 9, 1323–1348 (2002).
Bouropoulos, NCh. & Koutsoukos, P. G. Spontaneous precipitation of struvite from aqueous solutions. J. Cryst. Growth 213, 381–388 (2000).
Stroup, S.P., Auge, B.K. Urinary Infection and Struvite stones in P.N. Rao et al (eds) Urinary Tract Stone Disease Springer-Verlag London Limited 2011, chapter 18 - Urinary infection and struvite stones.
Doyle, J. D. & Parsons, S. A. Struvite formation, control and recovery. Water Res. 36, 3925–3940 (2002).
Brett, S., Guy, J., Morse, G. K. & Lester, J. N. Phosphorous Removal and Recovery Technologies (Selper Publications, 1997).
Ye, Z. et al. Phosphorus recovery from wastewater by struvite crystallization: property of aggregates. J. Environ. Sci. 26, 991–1000 (2014).
Booker, N. A., Pristley, A. J. & Fraser, I. H. Struvite formation in wastewater treatment plants: opportunities for nutrient recovery. Environ. Technol. 20, 777–782 (1999).
Gaterell, M. R., Gay, R., Wilson, R., Gochin, R. J. & Lester, J. N. An economic and environmental evaluation of the opportunities for substituting phosphorus recovered from wastewater treatment works in existing UK fertiliser markets. Environ. Technol. 21, 1067–1084 (2000).
Jaffer, Y., Clark, T. A., Pearce, P. & Parsons, S. A. Potential phosphorous recovery by struvite formation. Water Res. 36, 1834–1842 (2002).
Maqueda, C., Perez Rodriguez, J. L. & Lebrato, J. Study of struvite precipitation in anaerobic digesters. Water Res. 28, 411–416 (1994).
Capdevielle, A., Sýkorová, E., Béline, F. & Daumer, M. L. Kinetics of struvite precipitation in synthetic biologically treated swine wastewaters. Environ. Technol. 35, 1250–1262 (2014).
Weil, M. The struvite-type compounds M[Mg(H2O)6](XO4), where M = Rb, Tl and X = P, As. Cryst. Res. Technol. 43, 1286–1291 (2008).
Fang, C., Zhang, T., Jiang, R. & Ohtake, H. Phosphate enhance recovery from wastewater by mechanism analysis and optimization of struvite settle ability in fluidized bed reactor. Sci. Rep. 6, 32215 (2016).
Strickland, J. Perspectives for phosphorous recovery offered by enhanced biological removal. Environ. Technol. 20, 721–725 (1999).
Abbona, F. Crystallization of calcium and magnesium phosphates from solution of low concentration. J. Cryst. Growth 104, 661–671 (1997).
Pradhan, S. K., Mikola, A. & Vahala, Riku. Nitrogen and phosphorus harvesting from human urine using a stripping, absorption, and precipitation process. Environ. Sci. Technol. 51(9), 5165–5171 (2017).
Prywer, J. et al. First experimental evidences of the ferroelectric nature of struvite. Cryst. Growth Des. 20, 4454–4460 (2020).
Curie, J. & Curie, P. Développement par compression de l’électricité polaire dans les cristaux hémièdres à faces inclinées. Compt. Rend. 91, 294–297 (1880).
Steinem, C. & Janshoff, A. SENSORS | Piezoelectric Resonators in Encyclopedia of Analytical Science 2nd edn, 269–276 (Springer, 2005).
Lafuente, B., Downs, R. T., Yang, H. & Stone, N. The power of databases: The RRUFF project. In Highlights in Mineralogical Crystallography (eds Armbruster, T. & Danisi, R. M.) 1–30 (W. De Gruyter, 2020).
Tylczyński, Z. & Wiesner, M. Pyroelectric, piezoelectric, elastic and dielectric properties of triglycine zinc chloride crystal. J. Alloys Compd. 588, 177–181 (2014).
Roleder, K. Measurement of the high-temperature electrostrictive properties of ferroelectrics. J. Phys. E Sci. Instrum. 16(12), 1157–1159 (1983).
X’Pert HighScore Plus v. 2.1.0, PANalytical B.V. Almelo, The Netherlands, 2004.
Powder Diffraction File, PDF-2, Release 2004, The International Centre for Diffraction Data® (ICDD®) 12 Campus Boulevard, Newtown Square, PA, U.S.A 2004.
Bland, J. & Basinski, S. Crystal Symmetry of Struvite (Guanite). Nature 183, 1385–1387 (1959).
John W. Anthony, Richard A. Bideaux, Kenneth W. Bladh, and Monte C. Nichols, Eds., Handbook of Mineralogy, Mineralogical Society of America, Chantilly, VA 20151-1110, USA. http://www.handbookofmineralogy.org/.
Roleder, K. et al. The piezoelectric effect in Na0.5Bi0.5TiO3 ceramics. J. Phys. Condens. Matter 14, 5399 (2002).
Tansel, B., Lunn, G. & Monje, O. Struvite formation and decomposition characteristics for ammonia and phosphorus recovery: a review of magnesium-ammonia-phosphate interactions. Chemosphere 194, 504–514 (2018).
Bhuiyan, M. I. H., Mavinic, D. S. & Koch, F. A. Thermal decomposition of struvite and its phase transition. Chemosphere 70, 1347e1356 (2008).
Babić-Ivančić, V., Kontrec, J., Kralj, D. & Brečević, L. Precipitation diagrams of struvite and dissolution kinetics of different struvite morphologies. Croat. Chem. Acta 75, 89e106 (2002).
Babić-Ivančić, V., Kontrec, J., Brečević, L. & Kralj, D. Kinetics of struvite to newberyite transformation in the precipitation system MgCl2–NH4H2PO4–NaOH–H2O. Water Res. 40, 3447e3455 (2006).
Frost, R. L., Weier, M. L. & Erickson, K. L. Thermal decomposition of struvite: implications for the decomposition of kidney stones. J. Therm. Anal. Calorim. 76, 1025e1033 (2004).
Huang, H., Xiao, D., Lium, J., Hou, L. & Ding, D. Recovery and removal of nutrients from swine wastewater by using a novel integrated reactor for struvite decomposition and recycling. Sci. Rep. 5, 10183 (2015).
Bayuseno, A. P. & Schmahl, W. W. Hydrothermal synthesis of struvite and its phase transition: Impacts of pH, heating and subsequent cooling methods. J. Cryst. Growth 498, 336–345 (2018).
Helman, D. S. Symmetry-based electricity in minerals and rocks: a review with examples of centrosymmetric minerals that exhibit pyro and piezoelectricity. Periodico di Mineralogia 85, 201–248 (2016).
Robert, E. Newnham, Properties of Materials: Anisotropy, Symmetry, Structure 94 (Oxford University Press Inc., New York, 2005).
Xiaoli, Du. et al. Large-sized crystal growth and piezoelectric properties of the single crystals of LiNa5Mo9O30. CrystEngComm 23, 1912–1917 (2021).
Whitaker, A. & Jeffery, J. W. The Crystal Structure of Struvite, MgNH4PO4·6H2O. Acta Crystallogr. Sect. B 42, 1429 (1970).
Acknowledgements
My (J.P.) special thanks go to Rafał Kruszyński (Ph.D., D.Sc.), a co-author of this paper and a colleague of mine who passed away in September 2020. Rafał played a key role in designing the specific conditions for measuring DSC, TG, DTA, XRPD, presented out-of-the-box thinking and showed great commitment to this research. In various ways, he has challenged my thinking. I also appreciate his willingness to devote his time so generously on this research. The cooperation with him was a pleasure.
Funding
This work was supported by the Ministry of Science and Higher Education (Poland), Grant No. I-71/501/7-71-1-1.
Author information
Authors and Affiliations
Contributions
J.P. formulated the problem raised in the article, managed a research project covering research that is the problem of the article, and has grown struvite crystals using a single diffusion gel growth technique. R.K. and M.Ś. measured DSC, TG, DTA, XRPD. A.S., D.K. and K.R. measured piezo-effect in struvite. All the authors took part in writing the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Prywer, J., Kruszyński, R., Świątkowski, M. et al. First experimental evidence of the piezoelectric nature of struvite. Sci Rep 11, 14860 (2021). https://doi.org/10.1038/s41598-021-94410-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-94410-2
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.