Abstract
A wide-band and tunable Q-switched erbium-doped fiber (EDF) laser operating at 1560.5 nm with a tungsten ditelluride (WTe2) saturable absorber (SA) is demonstrated. The semi-metallic nature of WTe2 as well as its small band gap and excellent nonlinear optical properties make it an excellent SA material. The laser cavity uses an 89.5 cm long EDF, pumped by a 980 nm laser diode as the linear gain while the WTe2 based SA generates the pulsed output. The WTe2 based SA has a modulation depth, non-saturable loss and saturation intensity of about 21.4%, 78.6%, and 0.35 kW/cm2 respectively. Stable pulses with a maximum repetition rate of 55.56 kHz, narrowest pulse width of 1.77 µs and highest pulse energy of 18.09 nJ are obtained at the maximum pump power of 244.5 mW. A 56 nm tuning range is obtained in the laser cavity, and the output is observed having a signal to noise ratio (SNR) of 48.5 dB. The demonstrated laser has potential for use in a large number of photonics applications.
Similar content being viewed by others
Introduction
Pulsed lasers are highly desirable laser sources that are typically realized in the form of mode-locked1 and Q-switched lasers2 that can be further classified as either active3 or passive4 systems. Active pulsed laser is accomplished through the use of acousto-optic5 and electro-optic modulators6 among other technique to generate pulses. This approach gives significant control over the various parameters of the generated pulses, but at the cost of a bulky and expensive setup. Normally, passive pulse laser can be typically achieved through the use of saturable absorbers (SAs)7,8. This approach, while providing less control over the output parameters of the generated pulses, is advantageous in that it allows for compact and cost-effective fiber laser cavities to be designed9. Topological insulators (TIs) such as bismuth selenide (Bi2Se3)10, bismuth telluride (Bi2Te3)11, black phosphorus12,13, perovskite14, as well as carbon-based materials such as carbon nanotubes (CNTs)15 and graphene16 are amongst the various materials that have shown great potential as SAs in order to produce pulses in erbium-doped fiber (EDF) laser cavities. This is because the afore-mentioned groups of materials exhibits a larger nonlinear-optical response17 as well as exceptional optical properties that include a large absorption coefficient, low defect density and long carrier lifetimes18. Besides that, the thin 2D structure of these materials give it an advantage in terms of unique photonic, magnetic, and electronic properties that is crucial for pulsed laser generation19.
Q-switched pulse generation has long been the focus of research efforts due to its advantageous intrinsic characteristics that include long pulses with higher pulse energies and durations20, which is highly desirable for applications in material processing, remote sensing, range finding, and medicine21,22,23,24,25. Furthermore, Q-switching is easier to induce as compared to mode-locking26, which would require delicate balancing between the dispersion and nonlinearities in the laser cavity27. As such, Q-switching is generally the preferred method of obtaining pulses in a laser cavity. Recently, researchers have focused their attention towards the exploration of transition metal dichalcogenide (TMD) group of materials in generating Q-switched pulses at broadband wavelengths. As SAs, TMD have significant advantages that include strong absorption28, high nonlinear optical response, optical fiber compatibility and ease of fabrication29. Luo et al.30 demonstrated passively Q-switched Ytterbium (Yb), Erbium (Er) and Thulium (Tm) fiber lasers using a molybdenum disulfide (MoS2) film as an SA, and their findings show that few-layer MoS2 films have significant potential as broadband SAs operating at the near to mid-infrared regions. Furthermore, Zhang et al.31 demonstrated the use of tungsten disulfide (WS2) to passively Q-switch EDF and Yb-fiber laser cavities. The WS2 based SA is capable of generating Q-switched pulses with microsecond durations and kilohertz repetition rates at lasing wavelengths of 1030 and 1558 nm, demonstrating the potential for WS2 as an SA in ultrafast photonic applications.
Tungsten ditelluride (WTe2) is another member of the TMD family and is a unique material as it is associated to a rising class of Weyl semimetals. This makes them highly promising for future applications as electronic, spintronic, and optoelectronic devices32,33 and also as a potential candidate for quantum spin Hall insulator materials34. Even though WTe2 belongs to the TMD family, its uniqueness arises from the additional structural distortion caused by the W atoms forming zigzag chains in a quasi-one-dimensional arrangement35. Furthermore, the small overlap between the valence band and conduction band of WTe2 results in an almost gapless band; as small as 0.7 eV36 compared to other TMD materials which typically have band gaps of more than 1 eV37. As such, WTe2 is more suitable for applications in near-infrared systems such as photodetectors, communications devices and in the area of ultrafast optics. WTe2 was also been found to have unique characteristics such as a high unsaturated magneto-resistance (MR) as well as good superconducting behaviour while under high pressure38 which makes WTe2 quite attractive for nanoelectronic applications39. In addition to that, the very fast relaxation of photocarriers makes WTe2 suitable for generating Q-switched pulses38. In a study conducted by Wang et. al.40, an ultrafast pulse was successful generated in a mode-locked thulium-doped fiber laser through the use of magnetron-sputtering deposited WTe2 as an SA. Stable soliton pulses with pulse durations of 1.25 ps and average output powers of 39.9 mW were obtained at a central wavelength of 1915.5 nm. Similarly, Koo et. al.41, developed passively mode-locked ultrafast lasers at 1556.2 nm using defective, bulk-structured WTe2 microflakes as an SA. They discovered that the structural dimensionality does not critically influence the saturable absorption performance of WTe2.
In this work, WTe2 is demonstrated as a wideband SA in a passively Q-switched EDFL operating at the 1.5 μm region. The WTe2 SA has a modulation depth of 21.4% and saturation intensity of ~0.35 kW/cm2. Stable Q-switched pulses are obtained at a central lasing wavelength of 1560.5 nm, which can be tuned over a range of 56 nm from 1522 nm to 1578 nm. The proposed SA would have significant benefits and potential to be used in various applications.
Characterization of a Tungsten Ditelluride (WTe2) - Based SA
Figure 1(a) shows the morphology of the WTe2 layer as obtained from a Hitachi SU8220 field-emission scanning electron microscope (FESEM) under x13k magnification. From the figure, it can be seen that the WTe2 nanoparticles have a flake-like morphology, and tend to stack together to form thicker flakes. Figure 1(b) shows the energy dispersive X-ray (EDX) profile of the WTe2 sample, with signal peaks associated only with the tungsten (W) and tellurium (Te) elements observed. This shows both the formation of WTe2 sample as well as its purity. The inset of Fig. 1(b) shows the area of the WTe2 sample from which the scan was obtained, as well as the weight and atomic percentage of the two elements which are 0.91% and 42. 15%, for W and 0.87% and 57.85% for Te respectively.
An NT MDT atomic force microscope (AFM) is used to measure the thickness of the WTe2 film. The location of the WTe2 film’s surface that was chosen for the thickness measurement is denoted by the blue line. The obtained AFM image is shown in Fig. 1(c), and it can be seen that the WTe2 sample used in this work consists of about six individual layers stacked together. Figure 1(d) gives the height profile of WTe2 film projected within the blue line. Six steps can be counted on the height profile, which gives the estimated thickness of the WTe2 film to be six layers. The green line represents the position of one WTe2 layer, with the thickness of a single layer estimated to be about 35.6 nm. As such, the overall thickness of the sample is estimated to be 213.6 nm. Further characterization of the WTe2 sample is also carried out using a Renishaw inVia Raman microscope linked with a 532 nm line from a doubled Nd:YAG laser as the excitation source. As displayed in Fig. 1(e), two distinct Raman peaks are seen in the Raman spectrum of WTe2. The peaks located at 163 and 211 cm−1 can be assigned to the in-plane A17 and A19 modes of WTe2, respectively42,43.
The SA assembly is formed by sandwiching a small piece of the WTe2-PVA between two optical fiber patchcords. A small amount of index matching gel is placed on the surface of the optical fiber patchcord, on which the WTe2-PVA piece is then placed. Using a fiber adaptor, another patchcord is joined to the first, thus forming the SA assembly. A white light source is linked to the SA as to obtain the linear optical transmission characteristics of the WTe2 film. The optical spectrum is observed from 1200 nm to 1600 nm using a Yokogawa AQ6370C optical spectrum analyser (OSA) with an average transmission (T) of 92.64% observed at 1560 nm as in Fig. 2(a). The nonlinear optical absorption characteristic of the WTe2 SA are investigated using the balanced twin detector technique, with a Menlo Systems ELMO femtosecond erbium laser with a 100 MHz repetition rate and 2.88 ps pulse width at 1564 nm serving as the signal source. The obtained data is inserted into the saturation model equation44:
where αs, I, Isat, and αns is refer to the modulation depth, input intensity, saturation intensity, and non-saturable loss respectively. The relative parameters for the WTe2 SA are obtained based from the resulting fitted curve as given in Fig. 2(b), with the modulation depth, saturation intensity and non-saturable loss of the WTe2 SA being ~ 21.4%, 0.35 kW/cm2, and 78.6%, respectively. The insertion loss of the WTe2 SA is measured to be approximately 0.31 dB.
Experimental Setup
Figure 3 shows the schematic of the passively Q-switched ring cavity EDF laser. The laser cavity uses a 980 nm laser diode (LD) as the pump source with a maximum output power of 244.5 mW and injected into the cavity via the 980 nm port of a 980/1550 nm wavelength-division multiplexer (WDM). The output of the WDM is connected to a 89.5 cm long EDF which has a dopant concentration, absorption, mode field diameter, and numerical aperture of 2000 ppm, 16 dB/m at 1530 nm, 9.5 µm at 1550 nm and 0.13, respectively. The EDF serves as the gain media, and is connected to an optical isolator as well as an optical tunable bandpass filter (TBPF) with a tuning range of 80 nm and a resolution of 1 nm. The signal now reaches the WTe2 based SA, and an 80:20 optical coupler is used to obtain 20% of the signal. The 80% port of the coupler is connected to the 1550 nm port of the WDM, thereby closing the optical cavity. Polarization controllers (PCs) are not included in the design of the cavity as Q-switched pulses can be observed immediately with the incorporation of the WTe2 based SA into the laser cavity and without any further optimization of the propagating signal. Therefore, adding a PC would not improve the performance of the cavity, and will instead induce additional insertion losses to the cavity.
Results and Discussion
When operating without the WTe2 SA, no pulsed outputs can be detected, thus confirming that the generation of pulses is due solely to the SA and not arising from other optical phenomena. With the WTe2 SA in the cavity, continuous wave (CW) operation is obtained at a threshold pump power of 77.43 mW while Q-switching begins at a threshold pump power of 124.9 mW. Pulsing is observed to continue steadily until the maximum pump power of 244.5 mW is reached. The pulse characteristics of the Q-switched EDF laser at a pump power of 244.5 mW are shown in Fig. 4. The optical spectrum of the pulses is given in Fig. 4(a), where the central wavelength is determined to be 1560.5 nm with a 3-dB band width of 1.55 nm. The oscilloscope trace of the Q-switched pulses is given in Fig. 4(b), whereby the generated pulses have a peak-to-peak pulse interval of 18.86 μs that corresponds to a repetition rate of 55.56 kHz. In Fig. 4(c), the single pulse profile has a full width at half maximum (FWHM) duration of 1.77 μs. Based on the RF spectrum, a frequency of 55.56 kHz is observed in Fig. 4(d), with the pulses haveing an average signal-to-noise ratio (SNR) of about 48.5 dB. This indicates that the generated Q-switched pulses are highly stable, and comparable to that of other similar systems45,46.
Figure 5(a) shows the oscilloscope traces of the output pulses obtained at four different pump powers. It can be seen from the figure that the repetition rate increases while the spacing between pulses decreases as the pump power is increased. These trends are characteristic of Q-switching operation. The repetition rate and pulse width as a function of pump power is given in Fig. 5(b) and shows the repetition rate increasing from 38.39 kHz to 55.56 kHz when the pump power is increased from 124.9 mW to 244.5 mW. At the same time, the pulse width decreases from 3.67 μs to 1.77 μs, with a sharp decrease in the pulse width before a pump power of 236.5 mW and a slower decrease after it. The slower decrease of the pulse width at the higher pump powers is attributed to the change in the saturable-absorption property of the WTe2 SA from parasitic continuous waves that can partially bleach it47. As shown in Fig. 5(c), the variation of the output power and pulse energy against the pump power shows a generally rising trend, rising from 0.28 mW to 1.01 mW and 7.31 nJ to 18.09 nJ, respectively as the pump power is pushed to the maximum. However, as can be seen from the figure, a decrease in the average output power is observed at a pump power of 204.8 mW, before the average output power continues to rise normally against the increasing pump power. This sudden decrease in power is a result of a kink in the output power of the LD as the drive current increases. This causes the output power from the fiber laser to drop slightly, then continue to increase normally as the drive current increases. Another possibility as put forward by Adel48 is that when the drive current increased, this causes an increase in the temperature of the laser diode, and shifts the lasing wavelength away from the peak absorbing wavelength of 974 nm. This reduces the absorption occurring in the EDF, thus lowering the output power of the fiber laser. Further increasing the drive current of the LD will increase the pump power and cause the output power of the fiber laser to increase in tandem, as would be expected.
Figure 6 gives the RF spectra as captured over a span of 60 minutes at a pump power of 221 mW. No significant changes in the SNR value over the time period can be observed, with the average SNR value being ~48.5 dB. Based on the inset of Fig. 6, no frequency drifting can be observed with the frequency remaining constant at about ~53.8 kHz throughout the observation period. These results indicate the high stability of the proposed laser and also that there is no significant degradation of the WTe2 SA’s performance throughout its operation period.
Figure 7(a) shows the optical spectra of the tunable wavelength output obtained at a constant pump power of 194.2 mW. From the figure, no Q-switching operation can be observed below the wavelength of 1522 nm or beyond the wavelength of 1578 nm, giving the laser a tuning wavelength of 56 nm. Figure 7(b) shows the repetition rates against different wavelengths, and from the figure it can be seen that there is a gradual increase in the repetition rate as the wavelength is tuned from 1522 to 1532 nm. In general, the high repetition rate at the larger gain region of the cavity is due to lower cavity losses. This happens as a result of the more rapid bleaching of the SA which is due to faster population inversion/depletion rates49. Above a wavelength of the 1532 nm, the variation of repetition rate trend follows the amplified spontaneous emission (ASE) spectrum of the laser, as the inset of Fig. 7(b), from which the EDF’s gain profile is obtained50. The variation of the pulse width of the Q-switched laser output over the same wavelength tuning range is given in Fig. 7(c). From the figure, it can be seen that the pulse width increases from 1.3 μs to 2.6 μs over the increasing wavelength range. This is attributed to the different wavelength regions experiencing different gains, and as such variations in the repetition rate and pulse width that correspond to the gain curve of the cavity.
A comparison of the passively Q-switched fiber laser in this work against other similar systems using different SAs is given in Table 1. From the table, it can be seen that the proposed laser of this work using the WTe2-PVA film based SA generates Q-switched pulses with the narrowest pulse width. Furthermore, the threshold pump power for Q-switching to occur in this system is lower compared other similar systems29. Overall, the output performance of the proposed laser system is comparable and at some points is better than that in previous reports, thus confirming the applicability of WTe2 as an SA for Q-switched pulse generation at the C-band region. The excellent photoresponse behaviour possessed by tellurium (Te)51 allows for good pulsed laser performance to the realized.
Methods
Preparation of a Tungsten Ditelluride (WTe2) - Based SA
Solution casting is used to fabricate the WTe2 film with a polyvinyl alcohol (PVA) polymer thin film host. The WTe2 solution is purchased from 2D Semiconductors at 99.99% purity while the PVA at MW~31,000 powder is obtained from Sigma Aldrich. Approximately 100 mg of the PVA powder is slowly added into 10 ml of deionized water (DIW) at 60 °C and stirred continuously for 2 hours using a magnetic stirrer. A homogeneous WTe2 solution is obtained by treating the purchased WTe2 solution with a bath sonicator for a period of 30 minutes. Approximately 2 mL of the homogeneous 1 mg/mL WTe2 solution is added drop by drop into a beaker containing 8 mL of the 10 mg/mL PVA solution while stirring. The mixture is stirred continuously for another 15 minutes at 60 °C. Finally, the mixture is poured into a glass petri dish and heated in an oven for 2 hours at 60 °C, and the WTe2/PVA film is carefully removed from the petri dish after being allowed to cool down to room temperature.
Laser characterization
Analysis of the sample signal is done using the Yokogawa AQ6370C OSA as well as a Yokogawa DLM2054 oscilloscope (OSC) with a 1 GHz photodetector. An Anritsu MS2683A radio frequency spectrum analyzer (RFSA) and a Thorlabs optical power meter (OPM) are used to monitor the output spectra for further analysis.
Conclusion
In this work, a broadband WTe2 based SA is demonstrated for the passive generation of Q-switched pulses in the C-band region. A stable Q-switched output is achieved at a threshold pump power of 124.9 mW with a central wavelength of 1560.5 nm. By increasing the pumping power from 124.9 mW to 244.5 mW, the repetition rate rises from 38.39 kHz to 55.56 kHz while the pulse width decreases from 3.67 µs to 1.77 µs. The proposed laser system exhibits wide-band tunability of up to 56 nm from 1522 nm to 1578 nm, and is highly stable with no significant fluctuation in frequency observed over an operation period of 60 minutes with average SNR values of 48.5 dB. The obtained experimental results imply that WTe2 has a great potential as SA and the proposed laser system can be used as a pulse tunable laser source for various optical telecommunications and measurement applications.
References
Xing, C. et al. 2D Nonlayered selenium nanosheets: Facile synthesis, photoluminescence, and ultrafast photonics. Advanced Optical Materials 5, 1700884 (2017).
Ahmad, H., Albaqawi, H. S., Yusoff, N., Chong, W. Y. & Yasin, M. Q-Switched fiber laser at 1.5 µm region using Ti3AlC2 MAX Phase-based saturable absorber. IEEE Journal of Quantum Electronics (2019).
Wang, Y. et al. An all‐optical, actively Q‐switched fiber laser by an antimonene‐based optical modulator. Laser & Photonics Reviews 13, 1800313 (2019).
Xu, Y. et al. Solvothermal synthesis and ultrafast photonics of black phosphorus quantum dots. Advanced Optical Materials 4, 1223–1229 (2016).
Zhao, H. et al. Stable pulse-compressed acousto-optic Q-switched fiber laser. Optics Letters 32(19), 2774–2776 (2007).
El-Sherif, A. F. & King, T. A. High-energy, high-brightness Q-switched Tm3+-doped fiber laser using an electro-optic modulator. Optics Communications 218(4), 337–344 (2003).
Ahmad, H., Reduan, S., Yusoff, N., Ismail, M. & Aidit, S. Mode-locked pulse generation in erbium-doped fiber laser by evanescent field interaction with reduced graphene oxide-titanium dioxide nanohybrid. Optics & Laser Technology 118, 93–101 (2019).
Ismail, M., Ahmad, F., Harun, S. W., Arof, H. & Ahmad, H. A Q-switched erbium-doped fiber laser with a graphene saturable absorber. Laser Physics Letters 10, 025102 (2013).
Cheng, L. et al. Linear and nonlinear optical properties modulation of Sb2Te3/GeTe bilayerfilm as a promising saturable absorber. Results in Physics 13, 102282 (2019).
Ahmad, H. et al. Tunable S-band Q-switched fiber laser using Bi2Se3 as the saturable absorber. IEEE Photonics J. 7(3), 1–8 (2015).
Lee, J. et al. Linearly polarized, Q-switched, erbium-doped fiber laser incorporating a bulk-structured bismuth telluride/polyvinyl alcohol saturable absorber. Opt. Eng. 55(7), 076109 (2016).
Zhou, Y. et al. Recent advances in black phosphorus-based photonics, electronics, sensors and energy devices. Materials Horizons 4, 997–1019 (2017).
Guo, Z. et al. From black phosphorus to phosphorene: basic solvent exfoliation, evolution of Raman scattering, and applications to ultrafast photonics. Advanced Functional Materials 25, 6996–7002 (2015).
Li, P. et al. Two-dimensional CH3NH3PbI3 perovskite nanosheets for ultrafast pulsed fiber lasers. ACS Applied Materials & Interfaces 9, 12759–12765 (2017).
Zhou, D. P., Wei, L., Dong, B. & Liu, W. K. Tunable passively Q-switched erbium-doped fiber laser with carbon nanotubes as a saturable absorber. IEEE Photonics Technol. Lett. 22(1), 9–11 (2010).
Popa, D., Sun, Z., Hasan, T., Torrisi, F., Wang, F. & Ferrari, A. C. Graphene Q-switched, tunable fiber laser. Appl.Phys. Lett. 98(7), 073106 (2011).
Wu, L. et al. Few‐layer tin sulfide: A promising black‐phosphorus‐analogue 2D material with exceptionally large nonlinear optical response, high stability, and applications in all‐optical switching and wavelength conversion. Advanced Optical Materials 6, 1700985 (2018).
Zhang, Y. et al. Photonics and optoelectronics using nano-structured hybrid perovskite media and their optical cavities. Physics Reports (2019).
Tao, W. et al. Emerging two-dimensional monoelemental materials (Xenes) for biomedical applications. Chemical Society Reviews (2019).
Zhang, H. N. & Gold, J. L. nanobipyramids as saturable absorbers for passively Qswitched laser generation in the 1.1 lm region. Optics Lett. 41, 1150–1152 (2016).
Plamann, K. et al. Ultrashort pulse laser surgery of the cornea and the sclera. Journal of Optics 12(8), 084002 (2010).
Stöppler, G., Kieleck, C. & Eichhorn, M. High-pulse energy Qswitched Tm3+: YAG laser for nonlinear frequency conversion to the mid-IR. In Security+ Defence. International Society for Optics and Photonics (pp. 783609–783609) (2010).
Kölbl, J., Fröschl, M., Seedsman, A. & Sperber, P. Near-infrared laser range finder using kHz repetition rate. In SPIE Europe Security and Defence. International Society for Optics and Photonics (pp. 71150M–71150M) (2008).
Kilpela, A., Pennala, R. & Kostamovaara, J. Precise pulsed time-of-flight laser range finder for industrial distance measurements. Review of Scientific Instruments 72(4), 2197–2202 (2001).
Vicente, S. C., Gamez, M. M., Kir’yanov, A. V., Barmenkov, Y. O. & Andres, M. V. Diode-pumped self-Q-switched erbium-doped all-fibre laser. Quantum Electronics 34(4), 310 (2004).
Song, Y., Shi, X., Wu, C., Tang, D. & Zhang, H. Recent progress of study on optical solitons in fiber lasers. 6, 021313 (2019).
Nady, A. et al. Nickel oxide nanoparticles as a saturable absorber for an all-fiber passively Q-switched erbium-doped fiber laser. Laser Phys. 27, 065105 (6pp) (2017).
Woodward, R. I. & Kelleher, E. J. R. D. S. A. f. F. L. Appl. Sci. 5, 1440–1456 (2015).
Mohanraj, J., Velmurugan, V. & Sivabalan, S. Transition metal dichalcogenides based saturable absorbers for pulsed laser technology. Optical Materials 60, 601–617 (2016).
Luo, Z. et al. 1-, 1.5-, and 2-μm fiber lasers Q-switched by a broadband few-layer MoS2 saturable absorber. J. Lightwave Technol. 32, 4077–4084. (2014).
Zhang, M. et al. Yb-and Er-doped fiber laser Q-switched with an optically uniform, broadband WS2 saturable absorber. Sci. Rep. 5, 17482–17491 (2015).
Liu, Y. et al. Photoresponsivity of an all-semimetal heterostructure based on graphene and WTe2. Scientific Reports 8, 12840 (2018).
Torun, E., Sahin, H., Cahangirov, S., Rubio, A. & Peeters, F. Anisotropic electronic, mechanical, and optical properties of monolayer WTe2. Journal of Applied Physics 119, 074307 (2016).
Zheng, F. et al. On the Quantum Spin Hall Gap of Monolayer 1T′‐WTe2. Advanced Materials 28, 4845–4851 (2016).
Eftekhari, A. Tungsten dichalcogenides (WS2, WSe2, and WTe2): Materials chemistry and applications. Journal of Materials Chemistry A 5, 18299–18325 (2017).
Ghosh, B., Gupta, A. & Bishnoi, B. Effects of defects on the electronic properties of WTe2 armchair nanoribbons. Journal of Semiconductors 35, 113002 (2014).
Woodward, R. I. & Kelleher, E. J. 2D saturable absorbers for fibre lasers. Applied Sciences 5, 1440–1456 (2015).
Gao, W. et al. Broadband photocarrier dynamics and nonlinear absorption of PLD-grown WTe2 semimetal films. Applied Physics Letters 112, 171112 (2018).
Ali, M. N. et al. Large, non-saturating magnetoresistance in WTe2. Nature 514, 205 (2014).
Wang, J. et al. Magnetron-sputtering deposited WTe2 for an ultrafast thulium-doped fiber laser. Optics Letters 42, 5010–5013 (2017).
Koo, J. et al. Near‐infrared saturable absorption of defective bulk‐structured WTe2 for femtosecond laser mode‐locking. Advanced Functional Materials 26, 7454–7461 (2016).
Kim, Y. et al. Anomalous lattice dynamics of mono-, bi-, and tri-layer WTe2. arXiv preprint arXiv:1508.03244 (2015).
Lee, C.-H. et al. Tungsten ditelluride: a layered semimetal. Scientific Reports 5, 10013 (2015).
Woodward, R. et al. Tunable Q-switched fiber laser based on saturable edge-state absorption in fewlayer molybdenum disulfide MoS2. Opt. Express 22, 31113–31122 (2014).
Chen, Y. et al. Mechanically exfoliated black phosphorus as a new saturable absorber for both Q-switching and mode-locking laser operation. Optics Express 23, 12823–12833 (2015).
Luo, Z. et al. Two-dimensional material-based saturable absorbers: towards compact visible-wavelength all-fiber pulsed lasers. Nanoscale 8, 1066–1072 (2016).
Ko, S., Lee, J. & Lee, J. H. Passively Q-switched ytterbium-doped fiber laser using the evanescent field interaction with bulk-like WTe2 particles. Chin. Opt. Lett. 16, 020017 (2018).
Adel, P. Pulsed fiber lasers. (Cuvillier Verlag, 2004).
Ahmad, H., Ismail, M. & Aidit, S. Optically modulated tunable O-band Praseodymium-doped fluoride fiber laser utilizing multi-walled carbon nanotube saturable absorber. Chinese Physics Letters 36, 104202 (2019).
Ahmad, H. et al. Tunable Q-switched erbium-doped fiber laser in the C-band region using nanoparticles (TiO2). Optics Communications 435, 283–288 (2019).
Xie, Z. et al. Ultrathin 2D nonlayered tellurium nanosheets: Facile liquid‐phase exfoliation, characterization, and photoresponse with high performance and enhanced stability. Advanced Functional Materials 28, 1705833 (2018).
Chen, B. et al. Q-switched fiber laser based on transition metal dichalcogenides MoS2, MoSe2, WS2, and WSe2. Optics Express 23, 26723–26737 (2015).
Ahmad, H. et al. Ternary MoWSe2 alloy saturable absorber for passively Q-switched Yb-, Erand Tm-doped fiber laser,. Optics Communications 437, 355–362 (2019).
Huang, Y. et al. Opt. Express 22, 25258 (2014).
Ahmad, H., Aidit, S. N., Ooi, S. I. & Tiu, Z. C. Tunable passively Q-switched erbium-doped fiber laser with Chitosan/MoS2 saturable absorber,. Optics and Laser Technology 103, 199–205 (2018).
Ahmad, H., Tiu, Z. C. & Ooi, S. I. Passive Q-switching in an erbium-doped fiber laser using tungsten sulphoselenide as a saturable absorber. Chinese Optics Letters 16(2), 020009 (2018).
Ahmad, H. M. S., Z. C. Tiu, A. Zarei, and S. W. Harun. Opt. Laser Technol. 79, 20 (2016).
Liu, M., Ouyang, Y., Hou, H., Liu, W. & Wei, Z. Q-switched fiber laser operating at 1.5 μmbased on WTe2. Chinese Optics Letters 17(2), 020006 (2019).
Xie, Z. et al. Revealing of the ultrafast third-order nonlinear optical response and enabled photonic application in two-dimensional tin sulfide. Photonics Research 7, 494–502 (2019).
Chu, Z., Liu, J., Guo, Z. & Zhang, H. 2 μm passively Q-switched laser based on black phosphorus. Opt. Mater. Express 6, 2374–2379 (2016).
Acknowledgements
We would like to thank the University of Malaya for funding this research under the grants BKS002 - 2019, RK021 - 2019 and RU011 - 2019 and the Ministry of Higher Education, Malaysia for funding this research under the grant HiCoE Phase II Funding.
Author information
Authors and Affiliations
Contributions
Harith Ahmad proposed the study and designed the experiment. Hissah Saedoon Albaqawi performed the fiber laser experiments and wrote the manuscript. Norazriena Yusoff prepared the WTe2 films, performed the material characterization and contributed to writing of the manuscript. Chong Wu Yi contributed to data analysis.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ahmad, H., Albaqawi, H.S., Yusoff, N. et al. 56 nm Wide-Band Tunable Q-Switched Erbium Doped Fiber Laser with Tungsten Ditelluride (WTe2) Saturable Absorber. Sci Rep 10, 9860 (2020). https://doi.org/10.1038/s41598-020-66664-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-66664-9
This article is cited by
-
Cascaded C+L-band tunable erbium-doped fiber lasers for simultaneous generation of continuous wave and mode-locked pulses
Optical and Quantum Electronics (2023)
-
Q-switched pulse generation with lutetium oxide absorber
Optoelectronics Letters (2023)
-
8-HQCdCl2H2O as an organic Q-switcher in erbium laser cavity
Optoelectronics Letters (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.