Structural characterization of SnO nanoparticles synthesized by the hydrothermal and microwave routes

Abstract

SnO particles were synthesized by an alkali-assisted hydrothermal and microwave methods. The aqueous-based reactions were carried out at pH ~ 8, under inert atmosphere (Ar). The reactions were taken under different times, and a full XRD structural analysis was made to evaluate the conversion from the Sn6O4(OH)4 intermediate to SnO particles. Williamson-Hall analysis showed that the size and strain of the SnO particles were time and route treatment dependent. Microwave heating yielded a single tetragonal SnO phase after 1 h of thermal treatment, and TEM images revealed spherical-shaped SnO nanoparticles with an average size of 9(1) nm. While by the hydrothermal treatment single SnO phase was obtained only after 4 hours, yielding non-uniform and elongated particles with sub-micrometric size. A dissolution-recrystallization process was taken into account as the mechanism for SnO particles formation, in which hydroxylated complexes, Sn2(OH)6−2, then condense to form the oxide. The time-shorting reaction provided by the microwave-assisted synthesis may be attributed to better heat distribution.

Introduction

Tin monoxide (SnO - Sn+2) and tin dioxide (SnO2 - Sn+4) are well-known semiconductors with p-type and n-type electronic properties, respectively1,2,3,4. Their applications have encompassed technological areas such as optoelectronics, energy storage and sensing5,6,7,8. SnO2 is a pale-yellow solid with rutile-type structure and wide-bandgap (Eg = 3.6eV) and very used for transparent conductive electrodes7, gas sensors1,8, electrochromic devices3 and photoelectrodes3,4. While SnO is a dark solid with tetragonal structure and variable optical bandgap (Eg = 2.7–3.4 eV)9,10,11, and used for gas sensor devices12, electrodes for rechargeable Li-ion batteries13,14,15, supercapacitors16, native p-type conducting material17, as well as catalyst and photocatalyst18,19.

The preparation of the SnO phase is harder than SnO2 one, due to the favorable oxidation of the Sn+2 to the thermodynamically more stable Sn+4. Therefore, the synthetic challenge is to avoid this favorable oxidation, aside from the implementation of procedures that lead to well-controlled size and morphology. In this context, micro- and nano-crystalline SnO particles have been made by chemical/physical procedures, such as hydrothermal and solvothermal preparations, electrochemistry, ultrasound- and microwave-assisted routes, ionic liquids19,20,21,22,23,24,25,26, and thermal vapor deposition, thermal evaporation3, thermal chemical vapor deposition (CVD)4, and mechanical ball milling8. Moreover, organic additives, surfactants, inert atmosphere (Ar or N2) and reductive (H2) gases are applied with purposes of improving the yield forward the lower valence phase15,25,27,28.

Thermal vapor deposition and a long time of a hydrothermal treatment have been pointed out as the better conditions to obtain single-crystalline SnO particles26,29. Furthermore, in aqueous based-synthesis, the intermediate tin (II) oxyhydroxide, Sn6O4(OH)4, is often prepared from the hydroxylation of SnCl22H2O then condensation is taken on elevated temperatures and pressures, in alkaline solutions, or suspensions, to ensure due to speciation for SnO formation30,31.

Herein, conventional- and microwave-based hydrothermal treatments were used to form SnO nanoparticles (SnO-NPs), under inert atmosphere and relatively lower pH (pH ~ 8). The synthesis efficiency was compared in terms of reaction time, size and morphological aspects. Microwave heating yielded SnO-NPs with a spherical shape, small average size, and high uniformity upon 2 hours of thermal treatment. Conversely, hydrothermal preparation provided elongated sub-micrometric SnO-NPs with different sizes and morphologies upon 4 hours of treatment. The evaluation of the crystalline structures, from Sn6O4(OH)4 to SnO, in the different reaction times, was determined using X-ray diffraction microstructural analysis and transmission electronic microscopy (TEM) images.

Experimental

Materials

Tin chloride dihydrate (SnCl2.2H2O), ammonium hydroxide (NH4OH) and hydrochloric acid (HCl) were purchased from Synth, were used without further purification. The water used was double distilled and deionized.

Synthesis of the tin (II) oxyhydroxide (Sn6O4(OH)4) precursor (1)

As a general procedure tin chloride dihydrate (0.5 mol, SnCl2.2H2O) was dissolved in 100 mL of 0.5 M HCl solution (pH ~ 2) which was then transferred to a 300 mL three-necked round bottom flask and kept under stirring at room temperature and inert atmosphere (Ar). Then, an NH4OH solution 28–30% (~25 mL) was added dropwise into the acidic solution until pH ~ 8, producing a white cloudy suspension (~125 mL) of the precursor Sn6O4(OH)4, 1.

Microwave treatment

A Titan MPS microwave extraction and digestion system (PerkinElmer) with 2.45 GHz magnetrons that provide up to 1,500 W of power supply. The equipment was set up with a ramp at the temperature of 80 °C, which was reached after 10 min with a maximum pressure control of 35 bar and an average of 20% output power. Reactions were carried out into Teflon autoclave reactors which were loaded with 30 mL from 1, then heated and left for 45 min, 1 h, 1h30min, and 2h30min (sample names showed in Fig. 1). Previously, all loaded-autoclaves were purged with argon for 10 min to maintain an oxygen-free medium. At the end of each reaction, the vessels were left to chill until room temperature. The powders were filtered off and washed several times with deionized water and dried in a muffle oven in 60 °C before characterization.

Figure 1
figure1

Powders obtained under various reaction times; sample names and characteristics.

Hydrothermal treatment

For each reaction, 30 mL of the suspension 1 was put into hydrothermal autoclave reactor with Teflon chamber and also purged with argon to obtain an inert medium, then placed in an muffle oven already pre-heated at 100 °C, for 45 min, 1 h, 1h30 and 2h30, 4 h, and 6 h (sample names showed in Table 1). After cooling until room temperature, all samples were filtered off and washed several times with distilled water and dried in a muffle oven in 60 °C before characterization.

Nanoparticles characterization

The structural characterization was performed with X-ray diffraction (XRD) measurements of the dried powder samples using a PANalytical Empyrean equipment, with a copper tube (λ = 1.5418 Å), Ni filter, and PIXcel3D detector, operating at 40 kV and 30 mA, with 2θ from 10° to 90° with a 0.02° step and counting times of 3 to 5 s/step. To quantify phases and obtain structural parameters, the Rietveld’s powder structure refinement analysis was performed32,33,34,35 using Fullprof36,37 and X’Pert Highscore Plus (PANalytical)38 software. The peak shape was assumed as a pseudo-Voigt function with axial asymmetry, preferential direction of (00 l) planes, and the background of each pattern was fitted with a polynomial function of degree 5. Isotropic thermal vibrations were considered. Experimental parameters such as the sample’s displacement and absorption were also variables. The method takes a least-square routine to minimize the difference between the observed and simulated powder diffraction patterns with the R factors, goodness of fit (SGoF) and χ²35. The crystallite size and strain were calculated via the Williamson-Hall plot39,40.

Morphological characterization was performed with transmission electron microscopy (TEM) images, carried out in a JEOL JEM 2100 with LaB6 filament, 0.23 nm point resolution and high angular dark field detector (HAADF). Samples were suspended in ethanol and sonicated for 1 hour before measurement. Images were treated with ImageJ software41,42.

Results and Discussion

Structural and morphological characterization

The powders obtained under various reaction times for both conventional and microwave hydrothermal preparations are illustrated in Fig. 1.

Table 1 Structural paramenters from Rietveld analysis: lattice parameters (a/b, c)T,H, unit cell volume (VT,H), phase weight fraction (fT,H), where T = tin oxide (SnO), H = tin (II) oxyhydroxide (Sn6O4(OH)4).

XRD results and Rietveld analysis are presented in Figs. 2 and 3, and Tables 1 and 2 respectively. All samples were indexed with the Inorganic Crystal Structure Database (ICSD, FIZ Karlsruhe) database43,44.

Figure 2
figure2

X-ray diffractograms from conventional hydrothermal (H) SnO nanoparticles. The data for H6h00 is similar for H4h00, so it was not presented in this graph. Symbols represent experimental data, the lines are for Rietveld method calculated intensity, and dashed lines denote the difference between experimental and calculated intensities.

Figure 3
figure3

X-ray diffractograms from microwave treatment (M) SnO nanoparticles. Symbols represent experimental data, the lines are for Rietveld method calculated intensity, and dashed lines denote the difference between experimental and calculated intensities.

Table 2 Convergence factors of the Rietveld Method (RWP, REXP), Goodness of Fit (SGoF) and global χ2 of the fitting.

Tables 1 and 2 present the structural parameters and fraction of the phases, besides the factors of agreement of the adjustment. Since some samples presented more than one crystallographic phase, preferential high direction, and asymmetry of peaks, especially for samples synthesized via conventional hydrothermal thermal treatment, the convergence values such as goodness of fit (SGoF) and global χ2, are relatively higher than expected in general.

Quantification results show that for the conventional hydrothermal method, the complete formation from the tin (II) oxyhydroxide phase, Sn6O4(OH)4 (P\(\overline{4}\)21c, PDF #01-084-2157)43 to pure tetragonal phase SnO (P4/nmmS, PDF #01-085-0423)44 happens with at least 4 hours of thermal treatment. Within 2 hours of treatment, it can be observed a large intensity change for (001) and (002) planes, suggesting the formation of rods with growth in the c parameter direction. Lattice parameter and cell volume are similar to those to the standard crystallographic SnO data and a slight increase with treatment time from 4 to 6 hours (Table 1). For the microwave method, there is already ~50% formation of SnO and ~50% of Sn6O4(OH)4 phases with 45 min of treatment. The complete formation of crystalline single-phase SnO occurs after a 1-hour thermal treatment.

Figure 3 shows TEM images from SnO nanoparticles synthesized by both methods. It can be seen that microwave-assisted synthesis leads to uniformly sized spheres, Fig. 4(a–c), while in the conventional hydrothermal treatment there are agglomerated particles without definite shape, Fig. 4(d–f). The conventional hydrothermal synthesis also produces elongated particles that could be responsible for the large intensity of (00 l) peaks. The average nanoparticle size for M1h00 is 9(1) nm and, for M2h00 is 4.0(7) nm. For the H6h00 sample, the sizes vary from 10 to larger than 50 nm, the elongated particles have an average length of 30(6) nm. However, the microwave treatment leads to a more uniform formation of SnO nanoparticles instead of the conventional heating method.

Figure 4
figure4

TEM images for SnO nanoparticles. (a) M2h00; (b,c) M1h00; and (d–f) H6h00.

Microstructural analysis was performed in order to evaluate the average characteristics of the SnO powders. The Williamson-Hall plot (WHP) is shown in Fig. 5, and the results are displayed in Table 3. This analysis takes into account the crystallite size and the lattice deformations instead of the Scherrer formula that only evaluates the crystallite size40,41,45,46.

Figure 5
figure5

Williansom-Hall plot for SnO nanoparticles, where β stands for FWHM (full width half maximum) from the XRD peaks after instrumental correction, θ is the diffraction angle and, λ is the X-ray wavelength. (a) Conventional hydrothermal and, (b) microwave thermal treatment.

Figure 6
figure6

Dissolution-recrystallization steps for the formation of SnO particles from Sn6O4(OH)4 intermediate.

Table 3 Crystallite size (DWH) and strain (ε) determined via Williamson-Hall Method for the SnO crystal phase.

The crystallite size calculated is greater than TEM images mostly because of the agglomerated particles between each other (Table 1), producing an effect on the intensity distribution, since crystal sizes smaller than 100 nm are harder to analyze via XRD size-strain analysis40,45,46. These particle clusters can be seen in Fig. 3(c–f). The crystallite size grows with the conventional hydrothermal treatment time, while in the microwave treatment the crystallite and nanoparticle size decreases.

The linear behavior of data in the WHP is consistent with and regular distribution of crystallite sizes. In this case, for the conventional hydrothermal treatment, the negative strain can be related to particle inhomogeneities, since the strain decreases as de particle size increases and the lattice parameters increase (Table 2). For the microwave treatment, the negative strain is related to the shrinkage of the unit cell showed by the Rietveld results (Table 2), which can also be related to the decrease in the nanoparticle size46.

Formation of SnO-NPs

Dissolution-recrystallization and oriented-attachment (OA) have been assigned to the formation of SnO particles with different textures and sizes47. In the present case, OA is ruled out because there is no evidence of an assembled architecture. Thus, SnO particles should be build up through dissolution-recrystallization way. In this pathway, the formation of SnO crystals is derived from the decomposition of the oxo-hydroxo intermediate, Sn6O4(OH)4, and then further condensation of the tin-hydroxo complexes showed in Fig. 5, proposed for aqueous-based preparations carried out at pH ~ 8.

Firstly, Sn6O4(OH)4 is dissolved by the attack of the hydroxide anion, OH, and water molecules forming the anionic Sn2(OH)6−2 complex, where two Sn+2 and hydroxo groups are bound by bridging, then it condenses to form SnO particles delivering water and hydroxide anion47. In this mechanism, in the overall synthesis, OH is consumed.

The synthesis efficiency may also be correlated to the favorable equilibrium in aqueous solution at pH ~8. SnO’s phase diagram, relating concentration as a function of pH, shows that solubility of the ionic oxo, HSnO−2, and hydroxo, Sn(OH)2, complexes are low (<10−6 M)30,31, thus, the equilibrium is promoted to SnO solid phase. Moreover, species of higher oxidation state can be suppressed, inasmuch as the reaction is taken under an inert atmosphere. Therefore this condition seems to be optimized to grow SnO particles in spite of the consumption of base throughout the stepwise mechanism.

Microwave versus Conventional oven heating

The heat-generation from microwave irradiation has been attributed to two main physical processes, namely as dipolar polarization and ionic conduction. Both are accountable for the gains such as decreased reaction rate and selectivity to obtain metal oxides48,49,50. Their magnitudes depend on the bulk dielectric permittivity (ε), a measure of the extent to which a material can be polarised by an external electric field, that can be expressed as ε = ε’ + ε”j, where ε’ is the dielectric constant of the material, ε” is the dielectric loss and j is the imaginary number where j2 = −121; the latter term ε” is related to the gain heating. Laybourn and co-workers have considered the role of the ε on the synthesis of MOFs under microwave irradiation and elucidate the influence of the concentration, ionic strength as salts are used, temperature, and microwave cavity as well. All these factors have been showed as significant, and even anion- and cation-ligand bond or interaction may exert a fair interference on the heating and reactivity51. Herein, microwave heating speeds up the formation of SnO-NPs even at a lower temperature than that for hydrothermal preparation leading to small and spherical-shaped SnO-NPs. Conversely, long particles and sheets morphologies were obtained by the conventional-hydrothermal preparation, in which heating is distributed by convection currents. Hence, one may argue that microwave delivers uniform heat through the reaction medium, which accelerates the rate of nucleation leading to small nanoparticles. On the other hand, the inhomogeneous heat spreading, under hydrothermal reaction, leads to particles of different shapes and sizes and certainly favors the ripening processes.

XRD results (see Figs. 2 and 3) showed that different intervals exist for starting the conversion from Sn6O4(OH)4 to SnO. Under microwave, it seems to be taking place at earlier reaction time while it happens only after 1 h through the hydrothermal treatment. This delay-effect has been noticed in another study concerning reaction time dependence to form SnO crystals49. Three possible explanations are i. a previous formation of an unknown tin-based structure, after then the condensation happens; ii. this interval is needed to increase the concentration of the Sn2(OH)6−2. iii. a unique effect might occur under microwave irradiation. The former may be discarded since that XRD analyses only identified the Sn6O4(OH)4 and/or SnO phases. Likewise, the second option was dismissed toward the balance of the end up mass obtained that showed practically equal for all reaction: m = 3.50(3) g. If there was a time interval for concentrating the Sn2(OH)6−2 in solution, the final mass of solid would decrease in those periods before converting to SnO. Therefore, microwave irradiation should induce a specific effect on reactivity. In order to understand the development of the Sn6O4(OH)4 crystalline precursor phase, the average crystallite size was measured from the most intense XRD peaks for both microwave (MW) and hydrothermal (HT) synthesis, Fig. 7.

Figure 7
figure7

The development of the average crystallite size of the Sn6O4(OH)4 phase during hydrothermal and microwave treatment time.

It can be seen that a second-order event in which HT treatment induces growth of the Sn6O4(OH)4 crystallite size until ~80 min, then the size decreases accompanying the conversion of Sn6O4(OH)4 to SnO. On the other hand, in the MW treatment, there is a very quick and straight decrease along with the conversion to SnO. In addition, the WHP analysis (see Fig. 5) showed that HT crystallite tensions decrease just after 2 h whereas ones from MW crystallite get an early and straight increase. Therefore, assuming a recrystallization-dissolution mechanism in which such an Sn2(OH)6−2 anionic complex is formed, these findings allow to set down the following panorama, shown in Fig. 8: i. MW treatment speeds up the formation of the anionic complex up to its saturation, then, the condensation happens inside a uniform heat distribution, favoring faster nucleation and smaller particles; ii. as the HT treatment needs first to achieve an average work temperature, the precursor Sn6O4(OH)4 grows up in disordered directions until ~1 h, then followed by SnO particle formation. After two hours, the whole system gathers enough energy to develop the condensation step form SnO from Sn2(OH)6−2, in spite of the inhomogeneous heat flux.

Figure 8
figure8

The effect of the conventional and microwave heating in the formation mechanism of SnO-NPs from Sn6O4(OH)4 53.

Moreover, taking into account the interference that microwave assisted-synthesis can have due to the variations of the bulk dielectric permittivity (e)50,51, it is not easy to predict its action on the mechanism of condensation, but should be mainly on the steps in which water acts as attacking or living group, i.e., dissolution of Sn6O4(OH)4 and oxolation of the Sn2(OH)6−2. The oxolation happens through an addition-elimination with a proton-transfer step-mechanism that releases water as leaving group forming an oxo bond, Fig. 9. As seen in the literature previously, the enhanced maturation of hydroxyapatite under microwave irradiation has been driven by the strong excitation or stretching of the calcium-water bond. Furthermore, the proposed mechanism also provides a path to the final hydroxide, OH, formation52. In our case such an effect should take place on the stepwise in which water is withdrawn, accelerating SnO formation The tetrahedra complex Sn2(OH)6−2 has two oxo bridges that are attacked by the hydroxo nucleophilic group via a nucleophilic substitution, further opening a cycle, producing the tin-alkoxy, Sn-O, that takes off a proton from water delivering OH.

Figure 9
figure9

Mechanism proposition of condensation steps: the possible pathways of the dissolution of Sn6O4(OH)4 and oxolation of the Sn2(OH)6−2 to form SnO-NPs43,44,49,50,51,52,53,54.

Conclusion

Conventional- and microwave-hydrothermal aqueous syntheses to form SnO were carried out at pH 8 under an inert atmosphere. The efficiency of conversion from Sn6O4(OH)4 to SnO was verified in the different reaction times by XRD analysis, as well as the structural and morphological  aspects of the particles. Conventional hydrothermal treatment yielded SnO sub-micrometric particles with sizes varying from 30 to 550 nm after 4 hours. By the microwave route, uniformly and spherical-shaped ZnO-NPs with 4 nm average size were obtained after 2 hours. XRD analyses indicate that size and morphology have a treatment time dependence. The XRD results were different from those observed by TEM, which can be attributed to samples’ preparation, leading to larger agglomerates. The mechanism of the formation of SnO may be assigned to a dissolution-recrystallization process, and the acceleration provided by the microwave-assisted preparation may be attributed to a better heat distribution into the synthesis medium.

References

  1. 1.

    Allen, J. P., Scanlon, D. O., Parker, S. C. & Watson, G. W. Tin monoxide: structural prediction from first-principles calculations with van der Waals corrections. The Journal of Physical Chemistry C 115(40), 19916–19924 (2011).

    CAS  Article  Google Scholar 

  2. 2.

    Wang, H. & Rogach, A. L. Hierarchical SnO2 nanostructures: recent advances in design, synthesis, and applications. Chemistry of Materials 26(1), 123–133 (2013).

    CAS  Article  Google Scholar 

  3. 3.

    Jiang, E. et al. Size-controllable synthesis of monodispersed SnO2 nanoparticles and application in electrocatalysts. The. Journal of Physical Chemistry B 109(18), 8774–8778 (2005).

    CAS  Article  Google Scholar 

  4. 4.

    Li, F. et al. One-step synthesis of graphene/SnO2 nanocomposites and its application in electrochemical supercapacitors. Nanotechnology 20(45), 455602 (2009).

    ADS  PubMed  Article  CAS  Google Scholar 

  5. 5.

    Reddy, M. V., Subba Rao, G. V. & Chowdari, B. V. R. Metal oxides and oxysalts as anode materials for Li-ion batteries. Chemical Reviews 113(7), 5364–5457 (2013).

    CAS  PubMed  Article  Google Scholar 

  6. 6.

    Li, X. et al. Determination of some basic physical parameters of SnO based on SnO/Si PN heterojunctions. Applied Physics Letters 106(13), 132102 (2015).

    ADS  Article  CAS  Google Scholar 

  7. 7.

    Minami, T. Substitution of transparent conducting oxide thin films for indium tin oxide transparent electrode applications. Thin solid films 516(7), 1314–1321 (2008).

    ADS  CAS  Article  Google Scholar 

  8. 8.

    Martinez, C. J., B. Hockey, C. B., Montgomery, S. & Semancik Porous tin oxide nanostructured microspheres for sensor applications. Langmuir 21(17), 7937–7944 (2005).

    CAS  PubMed  Article  Google Scholar 

  9. 9.

    Saji, K. J., Subbaiah, Y. V., Tian, K. & Tiwari, A. P-type SnO thin films and SnO/ZnO heterostructures for all-oxide electronic and optoelectronic device applications. Thin Solid Films 605, 193–201 (2016).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Ogo, Y. et al. Tin monoxide as an s-orbital-based p-type oxide semiconductor: Electronic structures and TFT application. Physica status solidi (a) 206(9), 2187–2191 (2009).

    ADS  CAS  Article  Google Scholar 

  11. 11.

    Nomura, K., Kamiya, T., H. & Hosono Ambipolar oxide thin‐film transistor. Advanced Materials 23(30), 3431–3434 (2011).

    CAS  PubMed  Article  Google Scholar 

  12. 12.

    Calderer, J. et al. Synthesis and characterization of metal suboxides for gas sensors. Microelectronics Reliability 40(4-5), 807–810 (2000).

    Article  Google Scholar 

  13. 13.

    Cherian, C. T., Reddy, M. V., Haur, S. C., B.V.R. & Chowdari Facile synthesis and Li-storage performance of SnO nanoparticles and microcrystals. RSC Advances 3(9), 3118–3123 (2013).

    CAS  Article  Google Scholar 

  14. 14.

    Ortiz, G. F. et al. Nanoarchitectured TiO2/SnO: a future negative electrode for high power density Li-ion microbatteries? Chemistry of Materials 22(5), 1926–1932 (2010).

    CAS  Article  Google Scholar 

  15. 15.

    Wang, L. et al. Large-scale preparation of shape-controlled SnO and improved capacitance for supercapacitors: from nanoclusters to square microplates. Nanoscale 5(16), 7613–7621 (2013).

    ADS  CAS  PubMed  Article  Google Scholar 

  16. 16.

    Kim, A. Y. et al. Ordered SnO nanoparticles in MWCNT as a functional host material for high-rate lithium-sulfur battery cathode. Nano. Research 10(6), 2083–2095 (2017).

    CAS  Google Scholar 

  17. 17.

    Zhang, J. et al. Electrical transport properties of SnO under high pressure. The. Journal of Physical Chemistry C 115(42), 20710–20715 (2011).

    CAS  Article  Google Scholar 

  18. 18.

    Wang, J. et al. One-pot hydrothermal synthesis of highly efficient SnOx/Zn2SnO4 composite photocatalyst for the degradation of methyl orange and gaseous benzene. Applied Catalysis B: Environmental 200, 19–30 (2017).

    CAS  Article  Google Scholar 

  19. 19.

    Safaei-Ghomi, J., Shahbazi-Alavi, H., E. & Heidari-Baghbahadorani SnO nanoparticles as an efficient catalyst for the one-pot synthesis of chromeno[2,3-b]pyridines and 2-amino-3, 5-dicyano-6-sulfanyl pyridines. RSC Advances 4(92), 50668–50677 (2014).

    CAS  Article  Google Scholar 

  20. 20.

    Sun, G. et al. Hydrothermal synthesis of honeycomb-like SnO hierarchical microstructures assembled with nanosheets. Materials Letters 98, 234–237 (2013).

    CAS  Article  Google Scholar 

  21. 21.

    J. Gajendiran, V. & Rajendran. A study of the nano-structured aggregated tin oxides (SnO2/SnO) and their structural and photoluminescence properties by a hydrothermal method. Materials Letters, 139, 116–118 (2015).

  22. 22.

    Cui, Y. et al. Synthesis of novel 3D SnO flower-like hierarchical architectures self-assembled by nano-leaves and its photocatalysis. Materials Research Bulletin 70, 784–788 (2015).

    CAS  Article  Google Scholar 

  23. 23.

    Cheng, H. et al. Electrochemical fabrication and optical properties of porous tin oxide films with structural colors. Journal of Applied Physics 116(15), 153511 (2014).

    ADS  Article  CAS  Google Scholar 

  24. 24.

    Zheng, H., Gu, C. D., Wang, X. L. & Tu, J. P. Fast synthesis and optical property of SnO nanoparticles from choline chloride-based ionic liquid. Journal of nanoparticle research 16(2), 2288 (2014).

    ADS  Article  CAS  Google Scholar 

  25. 25.

    Aurbach, D. et al. Nanoparticles of SnO produced by sonochemistry as anode materials for rechargeable lithium batteries. Chemistry of Materials 14(10), 4155–4163 (2002).

    CAS  Article  Google Scholar 

  26. 26.

    Nguyen, M. T. et al. Reproducible shape control of single-crystal SnO microparticles. RSC Advances 6(32), 26725–26733 (2016).

    CAS  Article  Google Scholar 

  27. 27.

    Zima, T., I. & Bataev Morphology and phase transformations of tin oxide nanostructures synthesized by the hydrothermal method in the presence of dicarboxylic acids. Journal of Solid State Chemistry 243, 282–289 (2016).

    ADS  CAS  Article  Google Scholar 

  28. 28.

    Wang, S. et al. Solution route to single-crystalline SnO platelets with tunable shapes. Chemical Communications 4, 507–509 (2005).

    Article  CAS  Google Scholar 

  29. 29.

    Guo, Y. Q. et al. Shape-controlled growth and single-crystal XRD study of submillimeter-sized single crystals of SnO. CrystEngComm 13(19), 5677–5680 (2011).

    CAS  Article  Google Scholar 

  30. 30.

    Sakaushi, K. et al. Synthesis and applications of SnO nanosheets: parallel control of oxidation state and nanostructure through an aqueous solution route. Small 6(6), 776–781 (2010).

    CAS  PubMed  Article  Google Scholar 

  31. 31.

    Uchiyama, H., Ohgi, H., H. & Imai Selective preparation of SnO2 and SnO crystals with controlled morphologies in an aqueous solution system. Crystal growth & design 6(9), 2186–2190 (2006).

    CAS  Article  Google Scholar 

  32. 32.

    R. A. Young The Rietveld Method (International Union of Crystallography Monographs on Crystal). Oxford University Press, USA, (1995).

  33. 33.

    Rietveld, H. M. Line profiles of neutron powder-diffraction peaks for structure refinement. Acta Crystallographica 22(no. 1), 151–152 (1967).

    CAS  Article  Google Scholar 

  34. 34.

    Rietveld, H. M. A profile refinement method for nuclear and magnetic structures,. Journal of Applied Crystallography 2(no. 2), 65–71 (1969).

    CAS  Article  Google Scholar 

  35. 35.

    McCusker, L. B. et al. Rietveld refinement guidelines. Journal of Applied Crystallography 32, 36–50 (1999).

    CAS  Article  Google Scholar 

  36. 36.

    J. Rodriguez-Carbajal, Fullprof Suite; version 3.5d. Institute Laue-Langevin, Grenoble, France, 2009–2012.

  37. 37.

    J. Rodriguez-Carvajal, An introduction to the program Fullprof 2000. Laboratoire Leon Brillouin (CEA-CNRS), (2001).

  38. 38.

    T. Degen, M. Sadki, E. Bron, U. König, G. Nénert The HighScore suite, Powder Diffraction, 29 S2, S13–S18 (2014).

  39. 39.

    Williamson, G. & Hall, W. X-ray line broadening from filed aluminum and wolfram. Acta Metallurgica 1(1), 22–31 (1953).

    CAS  Article  Google Scholar 

  40. 40.

    R. Guinebretière, X-ray Diffraction by Polycrystalline Materials, ISTE, London, (2007).

  41. 41.

    Langford, J. I. & Wilson, A. J. C. Scherrer after sixty years: a survey and some new results in the determination of crystallite size. Journal of applied crystallography 11, 102–113 (1978).

    CAS  Article  Google Scholar 

  42. 42.

    C. A. Schneider, W. S. Rasband, K.W. Eliceiri. NIH Image to ImageJ: 25 years of image analysis. Nature methods 9, 671–675.

  43. 43.

    I. Abrahams, S.M. Grimes, S.R. Johnston, J.C. Knowles (1996). Acta Crystallographica, Sec. C, 52 286 (2012).

  44. 44.

    Izumi, F. J. Solid State Chem. 38 381 (1981).

  45. 45.

    Brazuna, L. P. et al. Effect of Lithium and Sodium ions on size and morphology of ZnO nanoparticles synthesized by glycerol-urea route. New J. Chem. 43, 18988–18995 (2019).

    CAS  Article  Google Scholar 

  46. 46.

    Langford, J. I., Cernik, R. J. & Louër, D. The Breadth and Shape of Instrumental Line Profiles in High-Resolution Powder. Diffraction. J. Appl. Cryst. 24, 913–919 (1991).

    Article  Google Scholar 

  47. 47.

    Zhang, R. et al. Morphology modulation of SnO photocatalyst: from microplate to hierarchical architectures self-assembled with thickness controllable nanosheets. CrystEngComm 20(32), 4651–4665 (2018).

    CAS  Article  Google Scholar 

  48. 48.

    Bilecka, I. & Niederberger, M. Microwave chemistry for inorganic nanomaterials synthesis. Nanoscale 2(8), 1358–1374 (2010).

    ADS  CAS  PubMed  Article  Google Scholar 

  49. 49.

    El-Rafei, A. M., Youssef, H. & Ahmed, N. M. Synthesis and Characterization of Nano-/Micro-Crystalline SnO using Microwave and Hydrothermal Techniques. Journal of Ceramic Science and Technology 5(3), 217–222 (2014).

    Google Scholar 

  50. 50.

    Laybourn, A. et al. Metal-organic frameworks in seconds via selective microwave heating. Journal of Materials Chemistry A 5(16), 7333–7338 (2017).

    CAS  Article  Google Scholar 

  51. 51.

    Laybourn, A. et al. Understanding the electromagnetic interaction of the metal-organic framework reactants in aqueous solution at microwave frequencies. Physical Chemistry Chemical Physics 18(7), 5419–5431 (2016).

    CAS  PubMed  Article  Google Scholar 

  52. 52.

    Lerner, E., Sarig, S. & Azoury, R. Enhanced maturation of hydroxyapatite from aqueous solutions using microwave irradiation. J Mater Sci: Mater Med 2, 138–141 (1991).

    Google Scholar 

  53. 53.

    Jolivet, J.-P., Chanéac, C. & Tronc, E. Iron oxide chemistry. From molecular clusters to extended solid networks. Chem. Commun. 5, 477–483 (2004).

    Google Scholar 

  54. 54.

    Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

We would like to thank the FAPESP funding agency (grant numbers 2016/17708-4, 2017/13839-0 and, 2013/08166-5. We also thank Prof. Mario Politi for the discussions.

Author information

Affiliations

Authors

Contributions

Juliana Silva Dias made the synthesis and characterization of all samples as part of her undergraduate science project and prepared the references. Fabio Rodolfo Miguel Batista helped with the discussion about microwave effect. Rebeca Bacani made and wrote the structural and morphological characterization, and prepared Tables (1–3) and Figs. (2–5, 7). Eduardo Rezende Triboni wrote the main manuscript text and prepared Figs. (6, 8 and 9).

Corresponding author

Correspondence to E. R. Triboni.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Dias, J.S., Batista, F.R.M., Bacani, R. et al. Structural characterization of SnO nanoparticles synthesized by the hydrothermal and microwave routes. Sci Rep 10, 9446 (2020). https://doi.org/10.1038/s41598-020-66043-4

Download citation

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing