Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Metallic edge states in zig-zag vertically-oriented MoS2 nanowalls


The remarkable properties of layered materials such as MoS2 strongly depend on their dimensionality. Beyond manipulating their dimensions, it has been predicted that the electronic properties of MoS2 can also be tailored by carefully selecting the type of edge sites exposed. However, achieving full control over the type of exposed edge sites while simultaneously modifying the dimensionality of the nanostructures is highly challenging. Here we adopt a top-down approach based on focus ion beam in order to selectively pattern the exposed edge sites. This strategy allows us to select either the armchair (AC) or the zig-zag (ZZ) edges in the MoS2 nanostructures, as confirmed by high-resolution transmission electron microscopy measurements. The edge-type dependence of the local electronic properties in these MoS2 nanostructures is studied by means of electron energy-loss spectroscopy measurements. This way, we demonstrate that the ZZ-MoS2 nanostructures exhibit clear fingerprints of their predicted metallic character. Our results pave the way towards novel approaches for the design and fabrication of more complex nanostructures based on MoS2 and related layered materials for applications in fields such as electronics, optoelectronics, photovoltaics, and photocatalysts.


The ability of crafting new materials in a way that makes possible controlling and enhancing their properties is one of the main requirements of the ongoing nanotechnology revolution1,2. In this context, a family of materials that has attracted intense attention recently are 2D layered materials, such as MoS2, which belong to the group of transition metal dichalcogenides (TMDs). These materials have been extensively studied due to their promising electrical and optical properties3,4,5,6. A defining feature of TMDs is that they exhibit a lack of inversion symmetry, which leads to the appearance of a variety of different edge structures. The most common of these, consisting on dangling bounds, are the armchair (AC) and the zig-zag (ZZ) edge structures.

Of particular relevance in this context, the electronic properties of MoS2 have been predicted to be affected by the presence of the different edge structures in rather different ways. For instance, the AC edges have been predicted to be semiconducting, while the ZZ edges should exhibit instead metallic behavior7,8,9,10. Moreover, ab-initio theoretical calculations predict that these metallic states at the edges of MoS2 could lead to the formation of plasmons11. Beyond this tuning of electronic properties, other attractive applications of these active edge sites arise in photocatalysis, such as their use in hydrogen evolution reactions (HER)12,13,14,15.

With these motivations, it is clear that the design and fabrication of MoS2 nanostructures with morphologies that maximize the number of exposed active edge sites is a key aspect for further improvements in terms of applications. In this respect, significant efforts have been pursued to realize the systematic bottom-up growth of vertically-oriented standing MoS2 layers. This configuration leads to the edge sites facing upwards, therefore maximizing the number of exposed edge sites as compared with the more common horizontal configuration, where its basal plane lies parallel to the substrate16,17,18,19,20,21,22,23. However, this bottom-up approach is hampered by a lack of reproducibility due to the complexities of the growth mechanism. Another limitation within the bottom-up approach is that the specific type of edges exposed cannot be selectively grown.

Ideally, one would like to combine the best of both worlds. On the one hand, it is important to be able to controllably grow MoS2 nanostructures that exhibit the largest possible surface area of edge structures, as it is achieved by the bottom-up strategy summarized above. On the other hand, one would also like to be able to select the specific type of edge sites exposed, in particular, by selecting whether these correspond to AC or to ZZ edges. Therefore, the main goal of this work is to bridge these two requirements by realizing a novel approach to the growth of vertically-oriented standing MoS2 layers with full control on the nature of the exposed edge sites.

To achieve this goal, here we adapt a well-stablished top-down approach based on focus ion beam (FIB) in a way that allows us to selectively pattern both types of edges (AC and ZZ) within out-of-plane (vertical) MoS2 nanostructures. In the context of patterning layered materials, the usefulness of FIB has been repeatedly demonstrated24,25,26. By means of this technique, we are able to selectively maximize the density of exposed edge sites while controlling their type. Subsequently, by combining high-resolution transmission electron microscopy (TEM) with electron energy-loss spectroscopy (EELS) measurements, we are able to confirm not only the crystallographic nature of both the AC and ZZ MoS2 surfaces, but also we can demonstrate that, despite the roughness and imperfections induced during the fabrication procedure, the ZZ MoS2 nanostructures clearly exhibit a metallic character, in agreement with the theoretical predictions from ab-initio calculations11.

The results of this work will open new opportunities for nanoengineering the edge type in MoS2 nanostructures as well as in related layered materials, paving the way towards novel exciting opportunities both for fundamental physics and technological applications in electronics, optoelectronics, photovoltaics, and photocatalysts.


From crystal structure considerations, the possible angles between adjacent flat edges within MoS2 flakes should be multiples of 30°. Specifically, the expected angles between adjacent AC and ZZ edge structures in a MoS2 flake such as that of Fig. 1a should be 30°, 90°, and 120°, as illustrated in Fig. 1b. Based on this information, we have designed the orientation of the different areas of the MoS2 flake that subsequently will be patterned. In this way, we can ensure the full control over the resulting specific edge crystallographic orientation.

Figure 1
figure 1

(a) Atomic model of a MoS2 flake viewed along the [0001] direction, where we indicate the corresponding zig-zag (ZZ) and armchair (AC) edges. (b) From geometric considerations, we can determine the possible values that the angles between adjacent AC and ZZ edges should take; (c) and (d) SEM micrographs of the MoS2 flake used for patterning the nanowalls, taken before and after the milling respectively. In (d), three different set of arrays can be observed. The left-most array was fabricated without the protective metal layer, while the other arrays used instead this protective metal layer.

Figure 1c,d display a scanning electron microscopy (SEM) image of the MoS2 flake that has been used for the fabrication of the nanostructures, taken before and after the milling respectively. Before the milling is performed, a protective metallic layer of tungsten (W) with a thickness of 500 nm was deposited on top of the selected areas of the MoS2 flake. Subsequently, we performed a series of milling and cleaning processes in order to construct the vertically-aligned MoS2 nanostructures. Figure 1d displays three ordered vertically-oriented patterned arrays of MoS2 nanostructures, which in the following are denoted as nanowalls (NWs). Two of these sets of nanowalls are oriented perpendicularly with respect to each other, guaranteeing that this way one of two arrays will correspond to AC (ZZ) NWs while the other array will correspond instead to the complementary ZZ (AC) ones. These NWs are found to exhibit a uniform thickness being (89 ± 5) nm (central array in Fig. 1d) and (68 ± 5) nm (rightmost array in Fig. 1d). Note that the left-most array was fabricated without the protective metal layer. For further details about the optimization of the MoS2 nanowalls see the Supplementary Information.

To further examine the crystallographic nature of the resulting vertical MoS2 nanostructures, transmission electron microscopy (TEM) studies were carried out. For these studies, we lifted out two of the MoS2 NWs from the two different patterned NWs arrays using a micromanipulator. Subsequently, the nanostructure was mounted onto a TEM half-grid. This whole procedure takes place within the FIB chamber.

Figure 2a displays a high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) image of a selected region of the ZZ MoS2 nanowall, bracketed between the Si substrate and the metallic protective layer. Figure 2b shows the corresponding chemical compositional of this nanowall obtained by means of energy dispersive X-ray (EDS) spectroscopy measurements. From the EDS map, the different chemical components of the NWs can be clearly distinguished: the MoS2 segment, embedded within the protective metal layer tungsten (W), and the silicon (Si) substrate.

Figure 2
figure 2

(a) HAADF-STEM image of an area of the ZZ MoS2 NW, which is bracketed between the Si substrate and the metallic protective layer; (b) The corresponding EDX compositional maps (Mo in green, S in yellow, W in blue).

From the crystalline structure studies carried out by means of high-resolution TEM measurements (Fig. 3), we are able to confirm the specific edge site configuration for the two NW arrays. Figure 3a,b display the results of the TEM measurements on the AC and ZZ MoS2 surfaces respectively. By comparing the two crystallographic orientations, AC and ZZ, we can observe the differences between the atomic arrangement of each surface, which are consequently characterized by different fast Fourier transforms (FFTs) (shown in the insets of Fig. 3a,b). From these results, it is clearly noticeable the excellent agreement between the experimental FFTs obtained from the TEM measurements and the corresponding ones calculated theoretically in terms of the expected atomic configuration (shown in Fig. 3c,d). These results provide direct confirmation that these vertically-oriented MoS2 nanowalls are in fact exposing ZZ and AC edge terminations, therefore validating our fabrication strategy.

Figure 3
figure 3

(a,b) HRTEM micrographs of representative ZZ and AC MoS2 nanowalls, respectively. The insets indicate the corresponding fast Fourier transform (FFT). (c) and (b) The atomic modelling associated to the AC and ZZ orientations of the NWs, together with the theoretical calculation of the expected FFTs.

Fingerprinting the edge-type nature of MoS2 nanowalls

In order to pin down the local electronic properties of the AC and ZZ MoS2 NWs, electron energy-loss spectroscopy (EELS) measurements have been carried out in a scanning transmission electron microscope (STEM). In Fig. 4 we show the energy-loss spectra corresponding to both the AC and ZZ surfaces, taken at different points along the length of the nanowall. As it can be observed in the two sets of EELS spectra, the MoS2 bulk plasmon signal appears at 23.4 eV in both samples with similar intensities and general shape, in agreement with previous analyses27,28. Nevertheless, the MoS2 surface plasmon peak, present at 15.2 eV, turns out to appear only on a restricted subset of the spectra of the ZZ-nanowalls. Considering that the fabricated AC-nanowalls are thinner than the ZZ-terminated ones, the presence of the surface MoS2 plasmon on the ZZ-nanowalls cannot be attributed to a lower thickness of the sample. Therefore, the origin of this peak should be caused by another phenomenon.

Figure 4
figure 4

(a,b) EELS spectra taken at different positions of the AC and ZZ nanowalls, respectively, for the region of electron energy losses between 5 and 40 eV. Each curve corresponds to a different position along the NWs.

In that respect, it is important to notice that the MoS2 surface plasmon peak appears and disappears in a periodic manner, depending on the specific position along the nanowall where the EELS spectrum is collected. It is found that the positions which correspond to local maxima of the intensity associated to this surface plasmon peak are separated by around 12 nm between each other. This behavior can be attributed to the presence of metallic surface plasmon polaritons (SPP), which are planar waves appearing at the interfaces between a metal and a dielectric material under some external excitation, such as an electron beam29. That could correspond to the oscillatory character present in our EELS spectra. Therefore, from this analysis, we can conclude that the ZZ MoS2 NWs surfaces present a clear metallic character. On the contrary, the AC MoS2 NWs do not exhibit such metallic behavior. With this result, we can hereby confirm that the ZZ MoS2 NWs are dominantly enclosed by zig-zag edges structures. It is also worth mentioning here that no signal arising from neither the metal layer nor the Ga used for the FIB milling were present at any of the acquired EELS spectra, indicating that the possible contamination from Ga in the nanowalls is non-existing.


In order to further validate the onset of the metallic behavior observed in the ZZ MoS2 nanowalls (NWs), we calculated the corresponding density of states (DOS) by means of ab-initio calculations in the framework of density functional theory (DFT). The van der Waals (vdW) interactions characteristic of MoS2 were incorporated by using the nonlocal vdW functional model30 as implemented in the WIEN2k code (see Methods for further details).

We modeled the ZZ MoS2 nanowall by constructing a 1 × 3 × 1 supercell of MoS2, as shown in Fig. 5a. In order to minimize the interactions between periodic images due to the 3D boundary conditions, we introduced a vacuum layer such that the distance between periodic images is 17.170 Å.

Figure 5
figure 5

(a) The ZZ MoS2 nanowall can be modelled by constructing a 1 × 3 × 1 supercell with vacuum in the z direction. A vacuum layer with length of 17.170 Å was inserted along the ZZ edge of the nanowall, in order to to avoid spurious interactions between the repeating supercell images. This 1 × 3 × 1 supercell in the x and z directions was used to determine the density of states associated to the ZZ MoS2 nanowall, which can be treated as a two-dimensional sheet composed by ZZ nanorribons stacked along the y direction. (b) (Top panel) density of states of ZZ MoS2 nanowalls, (central and bottom panels) the individual contributions to the DOS from the Mo and S atoms located at the ZZ surface.

The resulting calculated total DOS for the ZZ MoS2 NW is displayed in Fig. 5b. A clear absence of a gap in the DOS near the Fermi energy is observed, which implies a finite probability (11.65 states/eV) for states just below and above the Fermi energy level being populated, highlighting the metallic behavior of the ZZ MoS2 NWs. Figure 5b (middle panel) also displays the individual contributions of the 4d states of Mo atoms located at the surface of the ZZ MoS2 nanowall. These 4d states of Mo are also observed to cross over the Fermi energy (1.35 states/eV), contributing therefore to the metallic character of the ZZ MoS2 nanowall. The individual contribution of the 3p states of S atoms located at the surface of the NW turns out to be much smaller from the DFT calculation, 0.08 states/eV. Therefore, the dominant contribution to the metallic character of ZZ MoS2 nanowalls can be confidently attributed to Mo-4d states of MoS2.

In this work, we have presented a novel approach for the top-down fabrication of ordered vertically-oriented MoS2 nanostructures (denoted as nanowalls) which makes possible to achieve at the same time, a large density of exposed active edge sites while also to controllably select whether these are of the AC or ZZ types. The crystallographic nature of the exposed surfaces has been validated by means of high-resolution TEM measurements. We have also studied the local electronic properties of these NW surfaces by means of EELS, finding direct evidence of the metallic character of the ZZ surfaces as indicated by the presence of MoS2 surface plasmon peak.

The metallic nature of the ZZ MoS2 nanowalls can be exploited to open new opportunities for nanoengineering the edge type in MoS2 nanostructures as well as in related layered materials. This would allow new exciting opportunities both for fundamental physics and technological applications in electronics, optoelectronics, photovoltaics, and photocatalysts.


Focus ion beam patterning for the fabrication of edge-controlled MoS2 nanowalls

MoS2 bulk crystal obtained from Alfa Aesar (99.999% purity) was mechanical exfoliated with Poly-Di-Methyl-Siloxaan (PDMS) and then transferred to a SiO2/Si substrate. The MoS2 nanostructures were milled using a FEI Helios G4 CX focus ion beam. The ion milling procedure was carried out using a very low energy electron beam of 15 kV, and an ion beam of 2 pA. Before the milling procedure was carried out, a protective metal (W) layer of 500 nm of thickness was deposited on top the selected areas.

Characterization techniques

Transmission Electron Microscopy (TEM) measurements were carried out in a Titan Cube microscope using an acceleration voltage of 300 kV. Its spatial resolution at Scherzer defocus conditions is 0.08 nm in the High-Resolution Transmission Electron Microscopy (HRTEM) mode, whilst the resolution is around 0.19 nm in the HAADF-STEM (High Angle Annular Dark Field – Scanning Transmission Electron Microscopy) mode. Electron Energy Loss Spectroscopy (EELS) experiments were carried out using a Gatan Imaging Filter (GIF) spectrometer, employing a collection semi-angle of 2.95 mrad, a convergence semi-angle of 14 mrad, and an aperture of 2 mm. The energy resolution obtained by using these parameters in EELS was 0.9 eV, with an exposure time of 0.1 s/spectrum and an energy dispersion of 0.1 eV/channel.

First-principle calculations

The density of states (DOS) calculations were performed using both linearized augmented plane wave (LAPW) and local orbitals (LO) methods implemented in the WIEN2k package31. The nonlocal van der Waals32,33 (vdW) interactions used for the DOS calculations uses optB8834 for the exchange term, the local density approximation35 (LDA) for the correlation term, and the DRSLL kernel for the non-local term36. For the non-local vdW integration the cut-off density rc was set to 0.3 bohr−3, while the plane wave expansion cut-off Gmax was set to 20 bohr−1. No spin polarization was considered. The lattice parameters were found by volume and force optimization of the supercell, such that the force on each atom was less than 1.0 mRy/bohr. The total energy convergence criteria was set to be 0.1 mRy between self-consistent field (SCF) cycles, while the charge convergence criteria was set to 0.001e, with e the elementary unit charge. The core and valence electron states were seperated by an energy gap of −6.0 Ry. Furthermore, the calculations used an R*kmax of 6.0, where R is the radius of the smallest Muffin Tin sphere, and kmax is the largest k-vector. The first Brillouin zone for the lattice parameter calculations was sampled with 100 k-points using the tetrahedon method of Blöchl et al.37, which corresponds to 21 k-points in the irreducible Brillouin zone. With the above parameters the optimized lattice parameters were a = 3.107 Å and c = 2.087 Å, which are in good agreement with the experimental values a = 3.161 Å and c = 12.295 Å38. The DOS was calculated with a denser k-point sampling of the Brillouin zone consisting of 1600 k-points, corresponding to 630 k-points in the irreducible Brillouin zone.


  1. Bhattacharyya, B. et al. Evidence of robust 2D transport and Efros-Schkovskii variable range hopping in disordered topological insulator (Bi2Se3) nanowires. Sci. Rep 7, 7825 (2017).

    ADS  Article  Google Scholar 

  2. Bhattacharyya, B. et al. Observation of quantum iscillations in FUB fabricated nanowires of topological insulator (Bi2Se3). J. Phys.: Condens. Matter 29, 115602–115609 (2017).

    ADS  Google Scholar 

  3. Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805–136809 (2010).

    ADS  Article  Google Scholar 

  4. Splendiani, A. et al. Emerging photoluminiscence in monolayer MoS2. Nano Lett. 10, 1271–1275 (2010).

    CAS  ADS  Article  Google Scholar 

  5. Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nature Nanotechnol. 6, 147–150 (2011).

    CAS  ADS  Article  Google Scholar 

  6. Mak, K. F., He, K., Shan, J. & Heinz, T. F. Control of valley polarization in monolayer MoS2 by optical helicity. Nature Nanotechnol. 7, 494–498 (2012).

    CAS  ADS  Article  Google Scholar 

  7. Li, Y., Zhou, Z., Zhang, S. & Chen, Z. MoS2 Nanoribbons: High Stability and Unusual Electronic and Magnetic Properties. J. Am. Chem. Soc. 130, 16739–16744 (2008).

    CAS  Article  Google Scholar 

  8. Pan, H. & Zhang, Y.-W. Edge-dependent structural, electronic and magnetic properties of MoS2 nanoribbons. J. Mater. Chem. 22, 7280–7290 (2012).

    CAS  Article  Google Scholar 

  9. Davelou, D., Kopidakis, G., Kioseoglou, G. & Remediakis, I. N. MoS2 nanostructures: semiconductors with metallic edges. Solid State Communications 192, 42 (2014).

    CAS  ADS  Article  Google Scholar 

  10. Lauritsen, J. V. et al. Chemistry of one-dimensional metallic edge states in MoS2 nanoclusters. Nanotechnology 14, 385 (2003).

    CAS  ADS  Article  Google Scholar 

  11. Rossi, T. P. et al. Effect of edge plasmons on the optical properties of MoS2 monolayer flakes. Phys. Rev. B 96, 155407–155417 (2017).

    ADS  Article  Google Scholar 

  12. Kibsgaard, J., Chen, Z., Rienecke, B. N. & Jaramillo, T. F. Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. Nat. Mater. 11, 963 (2012).

    CAS  ADS  Article  Google Scholar 

  13. Voiry, D. et al. Conducting MoS2 Nanosheets as Catalysts for Hydrogen Evolution Reaction. Nano Lett. 13, 6222–6227 (2013).

    CAS  ADS  Article  Google Scholar 

  14. Lukowski, M. A. et al. Enhanced Hydrogen Evolution Catalysis from Chemically Exfoliated Metallic MoS2 Nanosheets. J. Am. Chem. Soc. 135, 10274–10277 (2013).

    CAS  Article  Google Scholar 

  15. Jaramillo, T. F. et al. Identification of Active Edge Sites for Electrochemical H2 Evolution from MoS2 Nanocatalysts. Science. 317(5834), 100–102 (2007).

    CAS  ADS  Article  Google Scholar 

  16. Kang, M.-A. et al. Large scale growth of vertically standing MoS2 flakes on 2D nanosheet using organic promoter. 2D Mater. 4, 025042 (2017).

    Article  Google Scholar 

  17. Agrawal, A. V. et al. Controlled growth of MoS2 flakes in-plane to edge-enriched 3D network and their surface-energy studies. ACS Appl. Nano Mater. 1, 2356 (2018).

    CAS  Article  Google Scholar 

  18. Teng, Y. et al. MoS2 nanosheets vertically grown on graphene sheets for lithium-ion battery anodes. ACS Nano 10, 8526 (2016).

    CAS  Article  Google Scholar 

  19. Zeng, X. et al. Growth of large sized two-dimensional MoS2 flakes in aqueous solution. Nanoscale 9, 6575 (2017).

    CAS  Article  Google Scholar 

  20. Wang, X., Feng, H., Wu, Y. & Jiao, L. Controlled synthesis of highly crystalline MoS2 flakes by chemical vapor deposition. J. Am. Chem. Soc. 135, 5304 (2013).

    CAS  Article  Google Scholar 

  21. Jung, Y., Shen, J., Sun, Y. & Cha, J. J. Chemically Synthesized Heterostructures of Two-Dimensional Molybdenum/Tungsten-Based Dichalcogenides with Vertically Aligned Layers. ACS Nano 8, 9550–9557 (2014).

    CAS  Article  Google Scholar 

  22. Kong, D. et al. Synthesis of MoS2 and MoSe2 Films with Vertically Aligned Layers. Nano Lett. 13, 1341–1347 (2013).

    CAS  ADS  Article  Google Scholar 

  23. Wang, H. et al. Transition-metal doped edge sites in vertically aligned MoS2 catalysts for enhanced hydrogen evolution. Nano Res. 8, 566–575 (2015).

    CAS  Article  Google Scholar 

  24. Friedensen, S., Mlack, J. T. & Drndic, M. Materials analysis and focused ion beam nanofabrication of topological insulators. Bi2Se3 Scientific Reports 7, 13466 (2017).

    ADS  Article  Google Scholar 

  25. Sharma, P. A. et al. Ion beam modification of topological insulator bismuth selenide. Appl. Phys. Lett. 105, 242106 (2016).

    ADS  Article  Google Scholar 

  26. Fox, D. S. et al. Nanopatterning and electrical tuning of MoS2 layers with a subnanometer helium ion beam. Nano Lett. 15, 5307 (2015).

    CAS  ADS  Article  Google Scholar 

  27. Yue, B. et al. High-energy electronic excitations in a bulk MoS2 single crystal. Phys. Rev. B 96, 125118 (2017).

    ADS  Article  Google Scholar 

  28. Martin, L., Mamy, R., Couget, A. & Raisin, C. Optical Properties of Collective Excitations in MoS2 and NiSe2 in the 1.7 to 30 eV Range. Phys.Stat. Sol. 58, 623 (1973).

    CAS  ADS  Article  Google Scholar 

  29. Basov, D. N., Fogler, M. M. & García de Abajo, F. J. Polaritons in van der Waals materials. Science 354, 6309 (2016).

    Article  Google Scholar 

  30. Tran, F., Stezl, J., Koller, D., Ruh, T. & Blaha, P. Simple way to apply nonlocal van der Waals functionals within all-electron methods. Phys. Rev. B 96, 054103 (2017).

    ADS  Article  Google Scholar 

  31. Blaha, P. et al. WIEN2k, An Augmented Plane Wave + Local Orbitals Program for Calculating Crystal Properties (Karlheinz Schwarz, Techn. Universität Wien, Austria), ISBN 3-9501031-1-2 (2018).

  32. Klimeš, J., Bowler, D. R. & Michaelides, A. Chemical accuracy for the van der Waals density functional. J. Phys.: Cond. Matt. 22, 022201 (2010).

    ADS  Google Scholar 

  33. Klimeš, J., Bowler, D. R. & Michaelides, A. Van der Waals density functionals applied to solids. Phys. Rev. B 83, 195131 (2011).

    ADS  Article  Google Scholar 

  34. Becke, A. D. Density-functional exchange-energy approximation with correct asymptotic behaviour. Phys. Rev. A 38, 3098 (1988).

    CAS  ADS  Article  Google Scholar 

  35. Perdew, J. P. & Wang, Y. Accurate and simple analytic representation of the electron-gas correlation energy. Phys. Rev. B 45, 13244 (1992).

    CAS  ADS  Article  Google Scholar 

  36. Dion, M., Rydberg, H., Schröder, E., Langreth, D. C. & Lundqvist, B. I. Phys. Rev. Lett. 92, 246401 (2004).

    CAS  ADS  Article  Google Scholar 

  37. Blöchl, P. E., Jepsen, O. & Andersen, O. K. Improved tetrahedon method for brillouin-zone integrations. Phys. Rev. B 49, 16223 (1994).

    ADS  Article  Google Scholar 

  38. Schönfeld, B., Huang, J. J. & Moss, S. C. Anisotropic Mean-Square Displacements (MSD) in single crystals of 2H- and 3R-MoS2. Acta Cryst. B39, 404 (1983).

    Article  Google Scholar 

Download references


M.T., L.M. acknowledge support from the Netherlands Organizational for Scientific Research (NWO) through the Nanofront program. S.C.-B. acknowledge financial support from ERC through the Starting Grant “TESLA” grant agreement No. 805021.

Author information

Authors and Affiliations



M.T. and L.M. prepared the samples. M.T. performed the FIB milling and the TEM measurements. M.T. analyzed the TEM data. M.T. and S.C.-B. prepared the figures and the discussion of the results. L.M. performed the structure modeling and DFT calculations. S.C.-B. designed and supervised the experiments. All the authors contributed to the writing of the manuscript.

Corresponding author

Correspondence to Sonia Conesa-Boj.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Tinoco, M., Maduro, L. & Conesa-Boj, S. Metallic edge states in zig-zag vertically-oriented MoS2 nanowalls. Sci Rep 9, 15602 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing