Abstract
Herein, we report green synthesized nanoparticles based on stabilization by plant gums, loaded with citrus fruits flavonoids Hesperidin (HDN) and Naringin (NRG) as novel antimicrobial agents against brain-eating amoebae and multi-drug resistant bacteria. Nanoparticles were thoroughly characterized by using zetasizer, zeta potential, atomic force microscopy, ultravoilet-visible and Fourier transform-infrared spectroscopic techniques. The size of these spherical nanoparticles was found to be in the range of 100–225 nm. The antiamoebic effects of these green synthesized Silver and Gold nanoparticles loaded with HDN and NRG were tested against Acanthamoeba castellanii and Naegleria fowleri, while antibacterial effects were evaluated against methicillin-resistant Staphylococcus aureus (MRSA) and neuropathogenic Escherichia coli K1. Amoebicidal assays revealed that HDN loaded Silver nanoparticles stabilized by gum acacia (GA-AgNPs-HDN) quantitatively abolished amoeba viability by 100%, while NRG loaded Gold nanoparticles stabilized by gum tragacanth (GT-AuNPs-NRG) significantly reduced the viability of A. castellanii and N. fowleri at 50 µg per mL. Furthermore, these nanoparticles inhibited the encystation and excystation by more than 85%, as well as GA-AgNPs-HDN only completely obliterated amoeba-mediated host cells cytopathogenicity. Whereas, GA-AgNPs-HDN exhibited significant bactericidal effects against MRSA and E. coli K1 and reduced bacterial-mediated host cells cytotoxicity. Notably, when tested against human cells, these nanoparticles showed minimal (23%) cytotoxicity at even higher concentration of 100 µg per mL as compared to 50 µg per mL used for antimicrobial assays. Hence, these novel nanoparticles formulations hold potential as therapeutic agents against infections caused by brain-eating amoebae, as well as multi-drug resistant bacteria, and recommend a step forward in drug development.
Similar content being viewed by others
Introduction
Brain-eating amoebae are pathogenic protists and causative agents for deadly central nervous system (CNS) infections including primary amoebic encephalitis (PAM) and granulomatous amoebic encephalitis (GAE)1. Infections caused by brain-eating amoebae are rare but fatal and are of global concern due to increased exposure of public water-related activities combined with global warming2. Due to their rarity and/or lack of awareness, these diseases are challenging to diagnose and difficult to treat because of their ability to form resistant cysts3. Currently, a mixture of drugs including Amphotericin B, Chlorhexidine, Voriconazole, Miltefosine, Pentamidine and others is used in the management of infections caused by brain-eating amoebae, but the prognosis remains extremely poor and the mortality rate remains more than 90%4,5. Multi-drug resistant (MDR) bacteria such as methicillin-resistant Staphylococcus aureus (MRSA) and E. coli are more common causes of infectious diseases including urinary tract infections (UTI), meningitis, gastroenteritis, respiratory and skin diseases, etc6,7.
HDN is classified as bio-flavonoid, chemically belongs to parent compound flavones (a class of flavonoid) and contains disaccharide rutinose8. HDN is a leading compound of citrus fruits, isolated mainly from rinds of some citrus species e.g., bitter orange, sweet orange, and satsuma mandarin9. HDN possesses strong antiinflammatory, antiarthritic, antioxidant, anti-carcinogenic, antidiabetic and antihypertensive properties10,11. NRG is another flavonoid extracted from citrus fruits known for its versatile pharmacological values. It has been widely studied due to its antioxidant, anti-cancer and anti-inflammatory potentials12,13. However, the true therapeutic potency of flavonoids is generally retarded by their pH intolerance, easy oxidation, poor solubility etc.14. The shortcoming of lower water solubility of NRG has presented challenges in the drug development which leads to its poorer therapeutic efficacy15,16. Green chemistry is commonly utilized to synthesize such type of green nanoparticles for drug delivery purpose with biological safe and nontoxic materials17. For instance, natural materials which include plant extracts and by products from different plants have been used to synthesize green nanoparticles. Gum tragacanth (GT) is a complex polysaccharide obtained from the extract of genus Astragalus. It consists of a mixture of heterogeneous and branched hydrophilic polysaccharides with molecular weight in the range of 840 kDa. Hydrolysis of GT produces variety of sugars including D-galactose, D-xylose, L-fucose, L-arabinose, D-galacturonic acid, L-rhamnose etc. Gums from different plants are highly biocompatible, easily available and cost effective. Gum acacia (GA) is a biocompatible polymer obtained from trees. GA is an anionic branched polysaccharide which is widely employed in food and pharmaceutics as thickener, stabilizer, emulsifier, and it is also being used in drug delivery applications as a controlled release agent18,19. Hence, nontoxic and biocompatible properties of easily available gums made them useful for drug delivery system therefore gums stabilized/reduced nanoparticles can be an innovative nano-carrier for flavonoids delivery.
Nanoparticles based materials have recently shown tremendous in vitro potential against brain-eating amoebae. For example, Lemke et al., reported nanosuspension delivery system for Amphotericin B to brain against Balamuthia mandrillaris infection20. Previously, our research showed that Amphotericin B, Nystatin and Fluconazole conjugated AgNPs showed enhanced antiamoebic activity against brain-eating N. fowleri and A. castellanii21,22. Recently, natural compounds such as cinnamic acid23, periglaucine A, betulinic acid24, and tannic acid25 coated nanomaterials have been shown to be effective against A. castellanii. Based on these reports, we synthesized HDN and NRG loaded silver and gold nanoparticles stabilized by plant gums GA and GT respectively by utilizing green synthesis protocols. The design and synthesis of these materials is unique, robust and eco-friendly. The nanomaterials are thoroughly characterized by using various spectroscopic and microscopic techniques. These green-synthesized nanomaterials are being reported for the first time against brain-eating amoebae A. castellanii and N. fowleri, and against multi-drug resistant bacteria MRSA and neuropathogenic E. coli K1. HDN loaded GA stabilized nanoparticles showed significant amoebicidal and bactericidal efficacy, while minimal cytotoxicity against human cells. These nanoparticles hold promise for further evaluation of mechanism and in vivo studies against infectious diseases caused by free-living amoeba and multi-drug resistant bacteria.
Method and Materials
Materials
GA and GT were obtained from local market. HDN, NRG and Silver nitrate (AgNO3) purchased from Sigma-Aldrich Germany. Tetrachloroauric (III) acid trihydrate (HAuCl4-3H2O) was purchased from Merck. Deionized water was used for all formulations.
Preparation of gum solutions
Stock solutions of GA and GT were prepared by dissolving respective gums in deionized water at 4 mg/mL and 8 mg/mL concentration respectively. The solutions were stirred for 24 h at room temperature to ensure complete dissolution of gums. The gum solutions were filtered to separate the undissolved materials if any. The prepared gum solutions were used to synthesize the gum stabilized nanoparticle.
Green synthesis of GA-AgNPs and GT-AuNPs
For GA-AgNPs, silver nitrate solution (9 mg/ml) was added in equal volume (1:1 v/v) to the gum solution (3 mg/ml) which were stirred magnetically at 200 × g for 2 hr at 60 °C. GA-AgNPs formation was indicted by color change from colorless to pale yellow then converted to light brown. For GT-AuNPs, 0.1 mL of 5 mM gold aqueous solution was added to GT solution (1 mL, 5 mg/mL) and the reaction mixture was magnetically stirred at 200 × g for 4 h at 60 °C. The color change from colorless to deep purple indicated the reduction of gold and formation of GT-AuNPs. The formation of GA-AgNPs and GT-AuNPs was confirmed by determination of surface plasmon resonance using UV visible spectrophotometer (UV-240, Shimadzu).
HDN and NRG loading on gum stabilized nanoparticles
HDN and NRG loaded gum stabilized nanoparticles were synthesized as described previously17,26. Briefly, 0.5 mg/mL HDN was added to above GA-AgNPs solution, and the reaction mixture was magnetically stirred at 200 × g at room temperature for 24 h. HDN loaded GA-AgNPs-HD were obtained in the form of pellet upon centrifugation at 12,000 × g for 30 min. To load NRG on GT-AuNPs, nanoparticles were centrifuged at 10,000 × g for 25 min and the collected nanoparticles pellet was re-dispersed in deionized water with the addition of 0.5 mg/mL final concentration of NRG in GT-AuNPs. The mixture was left for stirring at room temperature at 200 × g for 24 h.
Characterization of nanoparticles size, polydispersity index (PDI), zeta potential and surface morphology
The size and PDI of nanoparticles were investigated through zetasizer (Malvern instrument UK). Nanoparticles were transferred into the plastic cuvette and read by using water as dispersant at 25 °C. Zeta potential was measured by using dip cell which was dipped into the cuvette containing diluted sample at 25 °C and read on the instrument. Morphology of the nanoparticles was determined through AFM (AFM, Agilent 5500). Colloidal samples were loaded on to the mica slide and left for air drying avoiding contamination from environment. Slides mounted on the microscope were visualized after drying, under non-contact mode.
FT-IR study
FT-IR analysis of nanoparticles in comparison to gums and flavonoids alone were carried out by diluting the samples with KBr to form a pallet. The spectra were recorded in the range of 400–4000 cm−1 using FT-IR spectrometer (Shimadzu Kyoto, Japan).
Determination of flavonoids loading efficiency
The loading of HDN/NRG on nanoparticles was determined spectrophotometrically. First the nanoparticles were centrifuged at 12,000 × g for 30 min. Supernatant (containing free drug) was discarded and pellet was collected and re-dispersed in methanol up to the final volume. HDN and NRG were detected and quantified at 285 nm17,26. The percentage of encapsulated flavonoids were calculated by using this formula:
A. castellanii cultures
A. castellanii (ATCC 50492) a clinical strain belonging to the T4 genotype, was routinely cultured in 10 mL growth medium consisting of 0.75% w/v proteose peptone, 0.75% w/v yeast extract, and 1.5% w/v glucose (PYG) in 75-cm2 tissue culture flasks at 30 °C as described previously27. Amoebicidal and encystation assays were performed with healthy A. castellanii trophozoites which are adherent to the surface of tissue culture flask. These active trophozoites were detached by putting culture flasks on ice for 15 min followed by gentle tapping for roughly 5 minutes after changing PYG medium with phosphate buffer saline (PBS) to remove any unhealthy amoeba. Finally, A. castellanii trophozoites suspension was centrifuged at 2500 × g for 10 min to obtain amoeba pellet. The pellet was resuspended in 1 mL PBS, and the population of A. castellanii was determined by cell counting using a hemocytometer. 5 × 105 A. castellanii were used for amoebicidal and encystation assays.
Henrietta lacks cervical adenocarcinoma (HeLa) cells culture
HeLa cells were cultured in Roswell Park Memorial Institute (RPMI)−1640 supplemented with 10% fetal bovine serum (FBS), 10% Nu-serum, 2 mM glutamine, 1 mM pyruvate, penicillin and streptomycin (100 units/mL and 100 μg/mL respectively), non-essential amino acids, and vitamins to obtain uniform monolayers of cells in 75-cm2 culture flasks as described previously28. Old media was aspirated, and cells were trypsinized with 2 mL trypsin. The cell suspension was centrifuged for 5 min at 2000 × g, and cell pellet was resuspended in 30 mL fresh cell growth media. 200 μL of this cell suspension was seeded in each well of a 96-well plate and the plate was incubated at 37 °C in a 5% CO2 incubator with 95% humidity for at least 24 h until formation of uniform monolayer of HeLa cells. These were used for N. fowleri cultures, cytotoxicity, and cytopathogenicity assays.
N. fowleri cultures
N. fowleri (ATCC 30174) a clinical isolate from the cerebrospinal fluid of a patient was cultured in 75-cm2 tissue culture flasks containing HeLa monolayers as feed. N. fowleri was grown at 37 °C in a 5% CO2 incubator with 95% humidity as described previously21.
Amoebicidal assay
The amoebicidal effects of gums, HDN, NRG, gum stabilized nanoparticles, and these nanoparticles loaded with HDN and NRG were tested against A. castellanii and N. fowleri. 5 × 105 amoebae per well were incubated with nanoparticles and respective controls at 50 and 25 µg per mL in 24-well plates in RPMI-1640 medium at 30 °C for 24 h as reported previously27. Next, amoebae viability was determined by Trypan blue (0.1%) exclusion assay. The number of nonstained amoebae (live) were counted using a hemocytometer to estimate the viability. Untreated amoebae were used as negative control, while A. castellanii incubated with Chlorhexidine, and N. fowleri treated with Amphotericin B were considered as positive control. The results are representatives of several experiments presented as the mean ± standard error.
Encystation assay
Encystation assay was done to test the effects of these nanoparticles to inhibit the differentiation of trophozoites of A. castellanii into cysts. 5 × 105 A. castellanii were incubated with 100 µg per mL concentrations of gums, HDN, NRG, gum stabilized nanoparticles, and these nanoparticles loaded with HDN and NRG in 1.5 mL centrifuge tubes at room temperature for 10 min. 50 mM MgCl2 and 10% glucose was added in 24-well plate as encystation medium, and test samples treated and control A. castellanii were added in above 24-well plates. The cells were incubated at 30 °C for 72 h29. After 72 h, each well was treated with 0.25% sodium dodecyl sulfate (SDS) to solubilize the trophozoites and only the SDS resistant cysts were tallied using a hemocytometer. The results are representatives of several experiments presented as the mean ± standard error.
Excystation assay
1 × 106 A. castellani trophozoites were harvested on non-nutrient agar plates (1.5% bacteriological agar dissolved in water, followed by autoclaving and then spreading on petri plates). The petri plates were kept in incubator at 30 °C for 14 days, which were routinely observed under light microscope for the formation of cysts. Following this, cysts were scraped using cells scraper with PBS, counted, and stored at 4 °C for further use. 1 × 105 cysts were treated with 100 µg per mL concentrations of HDN and NRG loaded nanoparticles and respective controls in PYG for 72 h29. Cysts transformed into trophozoites were enumerated by using hemocytometer. The results are representatives of several experiments presented as the mean ± standard error.
Bacterial cultures
The bacterial cultures used in this study include neuropathogenic Escherichia coli K1 (a cerebrospinal fluid isolate from a meningitis patient; 018:K1:H7), strain E44 {Malaysian Type Culture Collection (MTCC) 710859}, and methicillin-resistant Staphylococcus aureus (MRSA) (MTCC 381123). The MRSA strain was originally isolated from blood cultures, obtained from the Luton & Dunstable Hospital NHS Foundation Trust, Luton, England, UK.
Bactericidal assay
Antibacterial potential of nanoparticles and respective controls was determined by using bactericidal assay as described previously30. Briefly, bacterial cultures were fixed to an optical density of 0.22 at 595 nm using a spectrophotometer (OD595 = 0.22) which is equivalent to 108 colony-forming units per mL (C.F.U. mL−1). An inoculum of 10 μL of above bacteria culture (corresponding approximately 106 C.F.U.) was incubated with various concentrations of GA-AgNPs-HDN, GT-AuNPs-NRG and respective controls in 1.5 mL centrifuge tubes at 37 °C for 2 h. For negative controls untreated bacterial culture were incubated with phosphate buffer saline (PBS), while 100 μg/mL gentamicin treated bacteria were used as positive control. Next, bacteria were serially diluted and 10 µL of each dilution was plated on nutrient agar plates. These plates were incubated at 37 °C overnight, followed by counting viable bacterial C.F.U.
Pathogens-mediated host cells cytotoxicity
The cytopathogenicity assay was carried out as reported previously31. 5 × 105 A. castellanii, 106 C.F.U. of each E. coli K1 and MRSA were incubated with HDN and NRG loaded nanoparticles with respective controls at different concentrations for 2 h at 30 °C. Next, the microbial cultures were centrifuged at 2500 × g for 10 minutes, and supernatants were wasted to remove extracellular materials. The pellet obtained was resuspended in 500 µL of fresh RPMI-1640 which was put on another 24-well plated with HeLa cells monolayer. Cells were incubated at 37 °C in a 5% CO2 incubator with 95% humidity for 24 h. Finally, supernatants were collected from each well and lactate dehydrogenase (LDH) cytotoxicity assay was performed using LDH kit (Roche) as described previously23. The extent of LDH release determines cells damage. Untreated cells were considered as negative control, whereas cells incubated with 0.1% Triton X-100 for 20 min gave maximum LDH release as a result of cell lysis which was taken as positive control. The % cell cytotoxicity was calculated as follows: % cell cytotoxicity = (sample absorbance − negative control absorbance)/(positive control absorbance − negative control absorbance) × 100. The results are representatives of several experiments presented as the mean ± standard error.
Cytotoxicity assay
To evaluate the cytotoxic effects of these nanoparticles on human cell, LDH cytotoxicity assay was performed as reported previously28. Briefly, 100 µg per mL concentrations of HDN and NRG loaded nanoparticles and respective controls were treated with uniform monolayer of HeLa cells in a 24-well plate, and the cells were incubated for 24 h at 37 °C in a 5% CO2 incubator. After 24 h, supernatants were collected from each well and cytotoxicity was determined by measuring lactate dehydrogenase (LDH) released by using LDH kit (Roche). Untreated cells were considered as negative control, whereas cells incubated with 0.1% Triton X-100 for 20 min gave maximum LDH release as a result of cell lysis which was taken as positive control. The percentage cell cytotoxicity was calculated as follows: % cell cytotoxicity = (sample absorbance − negative control absorbance)/(positive control absorbance − negative control absorbance) × 100. The results are representatives of several experiments presented as the mean ± standard error.
Statistical analysis
Student T test was used to measure statistical correlation and significance. P < 0.05 was the limit for significance using two-sample T test and two-tailed distribution. *Represents P < 0.05, **represents P < 0.01, while ***represents P < 0.001.
Results
Characterization of GA-AgNPs and GA-AgNPs-HDN for determination of size, PDI, zeta potential and surface morphology
Size and shape of the nanoparticles have a key importance in the design of drug delivery systems. Smaller the size of the nanoparticles greater will be the surface to volume ratio, therefore the chances of interactions between the bioactive drug molecules and the nanoparticles increases which ultimately enhances the therapeutic efficacy of the drug32. GA-AgNPs possess 107.1 ± 2.56 nm mean size with PDI 0.270 ± 0.03. Similarly, GA-AgNPs-HDN exhibit 182.8 ± 1.02 nm and PDI 0.422 ± 0.01 results are shown in Fig. 1A,B. Larger mean size and PDI of the HDN loaded nanoparticles than that of their unloaded analogue is attributed to unequal scattering of the drug moieties over the surface of GA-AgNPs. Zeta potential of GA-AgNPs and GA-AgNPs-HDN was −18.6 ± 0.54 mV and −19.1 ± 1.34 mV respectively as shown in Fig. 1C,D. Zeta potential is another important parameter for the determination of nano-carrier stability. AFM and TEM of GA-Ag-NPs and GA-Ag-NPs-HD were investigated to find their morphology. Both nanoparticles found to be spherical in shape as shown in Fig. 2A–C. A sharp characteristic surface plasmon resonance band of GA-AgNPs-HDN was obtained at 420 nm as shown in Fig. 2D.
FT-IR analysis of GA-AgNPs and GA-AgNPs-HDN
FT-IR spectrum of GA shows characteristic peaks of a complex mixture of sugars, a stretching band at 3387.8 cm−1 assign to N-H, a band at 2931.0 due to asymmetric stretching vibration of C-H groups. Similarly, peak at 1630.7 and 1429.8 cm−1 corresponds to amide C=O stretch and C-N stretching vibration. The peak at 1068.1 cm−1 is attributed to C-O stretching vibration as shown in Fig. 2E. FT-IR spectrum of GA-AgNPs shows typical peaks at 338.16 and 2924.2 for N-H and C-H respectively. The peak at 1623.4 cm−1 corresponds to C=O group, similarly peak at 1431.3 and 1061.7 cm−1 due to stretches of C-N and C-O groups of GA. The change in absorbance from 1630.7 to 1623.4 and 1429.8 to 1431.3 and from 1068.1 to 1061.7 cm−1 indicates that C=O, C-N and C-O groups are participated in the reduction and stabilization of GA-AgNPs shown in Fig. 2E. The FT-IR spectrum of HDN revealed its distinctive peaks at 3466.1and 2925.50 cm−1 assign to OH and C-H groups of HDN. The peak for C=O, C = C and aromatic C=C appeared at 1645.27, 1515.9 and 1443.0 cm−1 respectively (Fig. 2F). The FT-IR spectrum of GA-AgNPs-HDN shows all the representative peaks at their respective places with slight changes in absorbance. FT-IR analysis confirms the chemical stability of HDN as all peaks are present on their respective positions in the spectrum shown in Fig. 2F. The drug loading % was found to be 73.66%.
Characterization of GT-AuNPs and GT-AuNPs-NRG for determination of size, PDI, zeta potential and surface morphology
GT-AuNPs and GT-AuNPs-NRG exhibit 183 ± 1.04 and 221 ± 1.08 nm mean size with PDI 0.351 ± 0.02 and 0.410 ± 0.03 respectively which are shown in Table 1. The size of the GT-AuNPs as compare to NRG loaded counterpart is relatively larger which confirms the NRG loading on the surface of GT-AuNPs. Zeta potential of GT-AuNPs is −34.1 ± 0.1 and for GT-AuNPs-NRG is −27.6 ± 0.5 mV respectively. The drug loading % was found to be 72%. Surface morphology of both GT-AuNPs and GT-AuNPs-NRG were investigated through AFM and TEM, and they were found to be spherical in shape as shown in Fig. 3A–D. shows a representative surface plasmon resonance band of GT-AuNPs-NRG with maximum absorbance at 540 nm.
FT-IR analysis of GT-AuNPs and GT-AuNPs-NRG
FT-IR spectrum of GT shows its distinguishing peaks for -OH and -CH groups at 3435.8 and 2933.6 cm−1 respectively. Similarly, typical peaks 1607.1 and 1042.3 cm−1 corresponds to -C=O and -C-O groups respectively (Fig. 3E). The FT-IR spectrum of GT-AuNPs shows characteristic vibration of -OH, -CH, stretching of -C=O and stretching of -C–O at 3499.9, 2925.0, 1649.0 and 1016.3 cm−1 respectively. The changes in the characteristic peaks of GT from 3435.8 to 3499.9 cm−1, 1607.1 to 1649.0 and 1042.3 to 1016.3 cm−1 indicate that -OH, -C=O and -C-O functional groups of GT play part in the nanoparticle synthesis. The FT-IR spectrum of NRG shows distinctive peaks at 3426.7 cm for -OH groups and -CH peak at 2925.2 cm−1. Similarly, the at 1638.0 and 1065.6 cm−1 for -C=O, -C-O groups respectively (Fig. 3F). The FT-IR spectrum of GT-AuNPs-NRG shows predominant shift in peaks from 1065.6 to 1076.4 cm−1 and 1638.0 to 1645.2 cm−1. This indicates that -C-O and -C=O groups of NRG interacts with GT-AuNPs. The involvement NRG functional groups confirm its loading in GT-AuNPs.
GA-AgNPs-HDN abolished viability of A. castellanii and N. fowleri
Amoebicidal assay revealed that GA-AgNPs-HDN killed all the A. castellanii trophozoites at 50 µg per mL, and significantly reduced the number of cells by 90% at 25 µg per mL as compared to GA alone, HDN alone, and GA-AgNPs (Fig. 4A). Notably GA-AgNPs-HDN was found to be more effective than positive control Chlorhexidine. Whereas, GT-AuNPs-NRG did not produce cidal effects when statistically compared with GT alone, NRG alone and GT-AuNPs. On the other hand, both GA-AgNPs-HDN and GT-AuNPs-NRG exhibited significant amoebicidal effects against N. fowleri as compared to gums alone, drugs alone and gums stabilized nanoparticles (Fig. 4B). GA-AgNPs-HDN caused 99% reduction in N. fowleri viability at 25 µg per mL which is also significantly more effective than Amphotericin B alone. These results suggest that GA-AgNPs-HDN is an exceptional formulation which hold potential for further studies.
GA-AgNPs-HDN and GT-AuNPs-NRG inhibited encystment and excystation of A. castellanii
As encystment of A. castellanii is responsible for the resistance against drugs, these nanoparticles were tested for inhibition of encystation. GA-AgNPs-HDN and GT-AuNPs-NRG significantly inhibited the encystation of A. castellanii at 100 µg per mL as compared to respective controls (Fig. 5A). GA-AgNPs-HDN caused 95% inhibition and GT-AuNPs-NRG inhibited the encystation by 85%. The de-differentiation of cysts into trophozoites causes recurrence of infection in most of the cases. Therefore, the effects of GA-AgNPs-HDN and GT-AuNPs-NRG were also evaluated against excystation. While treated with pre-formed mature cysts of A. castellanii, GA-AgNPs-HDN inhibited excystation by 84% at 100 µg per mL (Fig. 5B). Contrary, GT-AuNPs-NRG did not exhibit significant excystation when compared with GT-AuNPs. Since most of the lead compounds and drugs have limited effects against cysts of A. castellanii, these nanoparticles showed consistent effects against trophozoite as well as resistant cyst stage.
GA-AgNPs-HDN exhibited significant bactericidal effects
Figure 6 represents the bactericidal effects of GA-AgNPs-HDN and GT-AuNPs-NRG tested at 50 and 0.5 µg per mL against MRSA and E. coli K1. GA-AgNPs-HDN showed significant bactericidal activity at 50 µg per mL against MRSA (Fig. 6B), and 0.5 µg per mL against E. coli K1 (Fig. 6D). GT-AuNPs-NRG did not exhibit bactericidal effects at 50 µg per mL against both tested bacteria (Fig. 6C,F). Figure 7 presents the corresponding field emission scanning electron microscopic (FE-SEM) analysis of bacteria before and after treatment with GA-AgNPs-HDN.
GA-AgNPs-HDN reduced the pathogens-mediated host cell cytotoxicity
The pretreatment of A. castellanii and E. coli K1 with GA-AgNPs-HDN resulted in significant reduction of their cytopathogenicity against human cells. Figure 8A describes that untreated A. castellanii caused more than 80% cell cytotoxicity against HeLa cells, contrary, GA-AgNPs-HDN (50 µg per mL) completely obliterated the host cells cytotoxicity as compared to relative controls. Similarly, the pretreatment of 0.5 µg per mL GA-AgNPs-HDN with E. coli K1 abolished the cytotoxicity of bacterium against HeLa cells as compared to untreated E. coli K1 which exhibited 74% cytotoxicity (Fig. 8B).
GA-AgNPs-HDN and GT-AuNPs-NRG showed minimal cytotoxicity against human cells
When tested against human cells, all test samples showed minimal cytotoxic effects (Fig. 9). GA-AgNPs-HDN exhibited only 11% cytotoxicity while GT-AuNPs-NRG caused 23% cytotoxicity against HeLa at a higher concentration of 100 µg per mL as compared to amoebicidal effects which were recorded at 50 and 25 µg per mL. The cytotoxicity profile against human cells suggest that these nanoparticles are biosafe and can further be evaluated for potential in in vivo studies.
Discussion
Brain-eating amoebae are opportunistic protist pathogens associated with diseases of fatal severity. The molecular pathways to target these microbes are limited which results in challenges in development of effective therapeutics4. Current management and treatment are unspecific and ineffective due to which the CNS infections caused by brain-eating amoebae almost always proved to be deadly33. Furthermore, the clinical procedures suffer from limitations including long term use of medications (a mixture of drugs including biguanides, azoles, amidines, antibiotics) and still the chances of recurrence are high34. On the other hand, ever growing drug resistance in most commonly present bacteria, and lack of newer and improved antimicrobial agents pose serious challenges to healthcare systems35. Therefore, there is an urgent need to develop novel, sustainable, and effective modalities of chemotherapeutics against infectious diseases. Nanotechnology has proved to be a model alternative to target infectious diseases36. Due to small size of nanomaterials, these are efficient drug delivery carriers for minimizing the pharmacokinetics and pharmacodynamics limitations of compounds and drugs known to have medicinal values37. Flavonoids are important nutraceutical and biologically active class of secondary metabolites natural products. Flavonoids obtained from citrus fruit plants are rich of drug candidates against a variety of diseases such as; infectious diseases, cancer, neurodegenerative etc.38,39,40,41. However, their clinical applications have some common shortcomings, and their poor bioavailability is one of the major factors14. In this study, we synthesized silver and gold nanoparticles stabilized with plant gums and loaded them with two most common citrus fruits flavonoids HDN and NRG to utilize their antimicrobial activity against brain-eating parasites A. castellanii and N. fowleri and multi-drug resistant bacteria MRSA and neuropathogenic E. coli K1.
Green synthesis of nanoparticles involves the reduction of metal ions by using environmentally and eco-friendly materials which act as reducing and stabilizing agents. Microorganisms and plant materials have been widely used for the biosynthesis of nanoparticles42. Green synthesized nanoparticles have been extensively used against microbial diseases, however, only few results are reported against parasitic diseases43. Besides metallic nanoparticles, green polymers including cellulose and starch have also been used for clinical and biomedical applications including bones healing and substitution44,45,46. The synthesis and stabilization of nanoparticles is dependent on the reducing and capping ability of the material used. In this study, the reduction of silver and gold is accomplished by using biocompatible natural gums; GA and GT. This green approach is being exploited for the formation of nanoparticles by avoiding any toxic reducing agent and harsh temperature conditions17. These nanoparticles were thoroughly characterized by various instrumental techniques before subjected to biological evaluation against brain-eating amoebae.
The role of Toll-like receptors (TLRs) in innate immune responses to pathogens is well recognized47,48. Our previous study showed that, HDN is known to reduce the expression of mRNA in TLRs which as a result reduce inflammation17. As the TLRs can influence the immunopathogenesis of CNS parasitic infections, we proposed that using TLRs targeting compounds can decrease the activity of inflammatory cytokines which may affect the parasite clearance and host survival. However, upon loading of HDN on GA-AgNPs caused surprisingly drastic amoebicidal effects, the mechanism of which is yet unknown. On the other hand, NRG acts as inhibitor of cytochrome P45049, which is known to be a common pathway associated with antimicrobial mode of action against brain-eating amoebae50. In our previous report, we showed the antibacterial effects of GT-AuNPs-NRG against a variety of bacteria, however their IC50 values were high (in the range of 250–300 µg per mL)26. GA-AgNPs-HDN are found to be more potent which showed significant bactericidal effects at 50 and 0.5 µg per mL against MRSA and E. coli K1 respectively. Interestingly, Gram-negative E. coli K1 which have additional peptidoglycan cell wall as compared to Gram-positive bacteria is found to be more susceptible to GA-AgNPs-HDN. The mode of action of such potent antimicrobial effects of these nanoparticles however is still to be determined.
Conclusions
The green synthesis of silver and gold nanoparticles stabilized with natural glycosidic polymers of plant gums (gum acacia and gum tragacanth) was achieved. These nanoparticles were further loaded with citrus fruits flavonoids HDN and NRG to obtain GA-AgNPs-HDN and GT-AuNPs-NRG. The nanoparticles were characterized by zetasizer, zetapotential, AFM, UV-vis spectrophotometric, and FT-IR analyses. GA-AgNPs-HDN and GT-AuNPs-NRG were tested against brain-eating amoebae A. castellanii and N. fowleri, as well as multi-drug resistant bacteria MRSA and neuropathogenic E. coli K1. These nanoparticles exhibited potent amoebicidal and bactericidal effects, and also inhibited the encystation and excystation processes of A. castellanii. Furthermore, these nanoparticles significantly reduced the pathogens-mediated host cells cytotoxicity. Interestingly, these nanocarriers did not show cytotoxicity against human cells even at higher concentration as compared to their concentration used for antimicrobial effects. This study demonstrates a potential development of effective antimicrobial nano-formulations based on naturally occurring flavonoids. These results are anticipated to be a major step forward in developing efficient nanomedicine against pathogenic microbes including brain-eating amoebae and bacterial infections. The mechanism of action and in vivo studies are part of our future research.
Data Availability
Data will be provided upon request on case to case basis.
References
Visvesvara, G. S., Moura, H. & Schuster, F. L. Pathogenic and opportunistic free-living amoebae: Acanthamoeba spp., Balamuthia mandrillaris, Naegleria fowleri, and Sappinia diploidea. FEMS Immun. Med. Microbiol. 50, 1–26 (2007).
Rose, J. B. et al. Climate variability and change in the United States: potential impacts on water-and foodborne diseases caused by microbiologic agents. Environ. Health Perspect. 109(Suppl 2), 211 (2001).
Anwar, A., Khan, N. A. & Siddiqui, R. Combating Acanthamoeba spp. cysts: what are the options? Parasit. Vectors. 11(1), 26 (2018).
Siddiqui, R., Aqeel, Y. & Khan, N. A. The development of drugs against Acanthamoeba infections. Antimicrob. Agents Chemother. AAC-00686 (2016).
Lorenzo-Morales, J., Khan, N. A. & Walochnik, J. An update on Acanthamoeba keratitis: diagnosis, pathogenesis and treatment. Parasite. 22 (2015).
Pantosti, A. & Venditti, M. What is MRSA? Eur. Respir. J. 34, 1190–1196 (2009).
Ali, S. M. et al. Identification and characterization of antibacterial compound (s) of cockroaches (Periplaneta americana). Appl. Microbiol. Biotechnol. 101, 253–286 (2017).
Garg, A., Garg, S., Zaneveld, L. J. & Singla, A. K. Chemistry and pharmacology of the citrus bioflavonoid hesperidin. Phytother. Res. 15, 655–669 (2001).
Ahmadi, A. & Shadboorestan, A. Oxidative stress and cancer; the role of hesperidin, a citrus natural bioflavonoid, as a cancer chemoprotective agent. Nutr. Cancer. 68, 29–39 (2016).
Mauludin, R. A. & Müller, R. H. Physicochemical properties of hesperidin nanocrystal. Int. J. Pharm. Pharm. Sci. 5, 954–960 (2013).
Bahadoran, Z., Mirmiran, P. & Azizi, F. Dietary polyphenols as potential nutraceuticals in management of diabetes: a review. J. Diabetes Metab. Disord. 12(1), 43 (2013).
Pan, M. H., Lai, C. S. & Ho, C. T. Anti-inflammatory activity of natural dietary flavonoids. Food Funct. 1, 15–31 (2010).
Manthey, J. A., Guthrie, N. & Grohmann, K. Biological properties of citrus flavonoids pertaining to cancer and inflammation. Curr. Med. Chem. 8, 135–153 (2001).
Sansone, F., Aquino, R. P., Del Gaudio, P., Colombo, P. & Russo, P. Physical characteristics and aerosol performance of naringin dry powders for pulmonary delivery prepared by spray-drying. Eur. J. Pharm. Biopharm. 72, 206–213 (2009).
Kanaze, F. I. et al. Dissolution enhancement of flavonoids by solid dispersion in PVP and PEG matrixes: A comparative study. J. Appl. Polym. Sci. 102, 460–471 (2006).
Lauro, M. R., De Simone, F., Sansone, F., Iannelli, P. & Aquino, R. P. Preparations and release characteristics of naringin and naringenin gastro-resistant microparticles by spray-drying. J. Drug Deliv. Sci. Technol. 17, 119–124 (2007).
Rao, K. et al. Gum acacia stabilized silver nanoparticles based nano-cargo for enhanced anti-arthritic potentials of hesperidin in adjuvant induced arthritic rats. Artif. cells Nanomed. Biotechnol. 1 (2018).
Mohan, Y. M., Raju, K. M., Sambasivudu, K., Singh, S. & Sreedhar, B. Preparation of acacia‐stabilized silver nanoparticles: A green approach. J. Appl. Polym. Sci. 106, 3375–3381 (2007).
Benfattoum, K. et al. Formulation characterization and in vitro evaluation of acacia gum–calcium alginate beads for oral drug delivery systems. Polym. Adv. Technol. 29, 884–895 (2018).
Lemke, A., Kiderlen, A. F., Petri, B. & Kayser, O. Delivery of amphotericin B nanosuspensions to the brain and determination of activity against Balamuthia mandrillaris amebas. Nanomed. 6, 597–603 (2010).
Rajendran, K., Anwar, A., Khan, N. A. & Siddiqui, R. Brain-Eating Amoebae: Silver Nanoparticle Conjugation Enhanced Efficacy of Anti-Amoebic Drugs against Naegleria fowleri. ACS Chem. Neurosci. 8, 2626–2630 (2017).
Anwar, A. et al. Silver nanoparticle conjugation affects antiacanthamoebic activities of amphotericin B, nystatin, and fluconazole. Parasitol. Res. 117, 265–271 (2018).
Anwar, A., Siddiqui, R., Shah, M. R. & Khan, N. A. Gold nanoparticle conjugated Cinnamic acid exhibit Antiacanthamoebic and antibacterial properties. Antimicrob. Agents Chemother. AAC-00630 (2018).
Mahboob, T. et al. Preparation of poly (dl-lactide-co-glycolide) nanoparticles encapsulated with periglaucine A and betulinic acid for in vitro anti-Acanthamoeba and cytotoxicity activities. Pathogens. 7(3), 62 (2018).
Padzik, M. et al. Tannic acid-modified silver nanoparticles as a novel therapeutic agent against Acanthamoeba. Parasitol. Res. 15, 1–7 (2018).
Rao, K. et al. Gum tragacanth stabilized green gold nanoparticles as cargos for Naringin loading: A morphological investigation through AFM. Carbohydr. Polym. 174, 243–252 (2017).
Sissons, J. et al. Use of in vitro assays to determine effects of human serum on biological characteristics of Acanthamoeba castellanii. J. Clin. Microbiol. 44, 2595–2600 (2006).
Jeyamogan, S., Khan, N. A., Anwar, A., Shah, M. R. & Siddiqui, R. Cytotoxic effects of Benzodioxane, Naphthalene diimide, Porphyrin and Acetamol derivatives on HeLa cells. SAGE Open Med. 6, 2050312118781962 (2018).
Dudley, R., Jarroll, E. L. & Khan, N. A. Carbohydrate analysis of Acanthamoeba castellanii. Exp. Parasitol. 122, 338–343 (2009).
Khan, N. A., Osman, K. & Goldsworthy, G. J. Lysates of Locusta migratoria brain exhibit potent broad-spectrum antibacterial activity. J. Antimicrob. Chemother. 62, 634–635 (2008).
Sissons, J. et al. Acanthamoeba castellanii induces host cell death via a phosphatidylinositol 3-kinase-dependent mechanism. Infect. Immun. 73, 2704–2708 (2005).
Ahmed, D. et al. Size selectivity in antibiofilm activity of 3-(diphenylphosphino) propanoic acid coated gold nanomaterials against Gram-positive Staphylococcus aureus and Streptococcus mutans. AMB Express. 7(1), 210 (2017).
Seal, D. V. Acanthamoeba keratitis update—incidence, molecular epidemiology and new drugs for treatment. Eye. 17(8), 893 (2003).
Khan, N. A. Acanthamoeba: biology and increasing importance in human health. FEMS Microbiol. Rev. 30, 564–595 (2006).
Nikaido, H. Multidrug resistance in bacteria. Ann. Rev. Biochem. 78, 119–146 (2009).
Zazo, H., Colino, C. I. & Lanao, J. M. Current applications of nanoparticles in infectious diseases. J. Control. Release. 224, 86–102 (2016).
Blanco, E., Shen, H. & Ferrari, M. Principles of nanoparticle design for overcoming biological barriers to drug delivery. Nat. Biotechnol. 33(9), 941 (2015).
Xiao, J. Dietary flavonoid aglycones and their glycosides: Which show better biological significance? Crit. Rev. Food Sci. Nutr. 57, 1874–1905 (2017).
Ren, W., Qiao, Z., Wang, H., Zhu, L. & Zhang, L. Flavonoids: promising anticancer agents. Med. Res. Rev. 23, 519–534 (2003).
Cushnie, T. T. & Lamb, A. J. Antimicrobial activity of flavonoids. Int. J. Antimicrob. Agents. 26, 343–356 (2005).
Jones, Q. R., Warford, J., Rupasinghe, H. V. & Robertson, G. S. Target-based selection of flavonoids for neurodegenerative disorders. Trends Pharmacol. Sci. 33, 602–610 (2012).
Iravani, S. Green synthesis of metal nanoparticles using plants. Green Chem. 13, 2638–2650 (2011).
Marimuthu, S. et al. Evaluation of green synthesized silver nanoparticles against parasites. Parasitol. Res. 108, 1541–1549 (2011).
Pandele, A. M. et al. Cellulose acetate membranes functionalized with resveratrol by covalent immobilization for improved osseointegration. Appl. Surf. Sci. 438, 2–13 (2018).
Dumitriu, C. et al. Production and characterization of cellulose acetate–titanium dioxide nanotubes membrane fraxiparinized through polydopamine for clinical applications. Carbohydr. Polym. 181, 215–223 (2018).
Miculescu, F. et al. Progress in hydroxyapatite–starch based sustainable biomaterials for biomedical bone substitution applications. ACS Sustain. Chem. Eng. 5, 8491–8512 (2017).
Kropf, P. et al. Toll-like receptor 4 contributes to efficient control of infection with the protozoan parasite Leishmania major. Infect. Immun. 72, 1920–1928 (2004).
Martínez-Castillo, M., Santos-Argumedo, L., Galván-Moroyoqui, J. M., Serrano-Luna, J. & Shibayama, M. Toll-like receptors participate in Naegleria fowleri recognition. Parasitol. Res. 117, 75–87 (2018).
Yune-Fang, U. et al. In vitro and in vivo effects of naringin on cytochrome P450-dependent monooxygenase in mouse liver. Life Sci. 65, 2591–2602 (1999).
Grace, E., Asbill, S. & Virga, K. Naegleria fowleri: A Review of the Pathogenesis, Diagnosis, and Treatment Options. Antimicrob. Agents Chemother. AAC-01293 (2015).
Acknowledgements
This work is supported by Sunway University, Malaysia (University Research Award INT-2018-03).
Author information
Authors and Affiliations
Contributions
A.A. conducted the experiments on Acanthamoeba prepared Figures 4, 5, 7, and wrote the first draft of manuscript. A.M. performed bacteria related and human cells assays and prepared Figure 6 and 8. Ka.R. performed Naegleria experiments and prepared Figure 4b. Ko.R. synthesized the materials under the supervision of M.R.S., and both prepared Figures 1–3. A.A., Ko.R. and M.R.S. characterized the nanomaterials. R.S. and N.A.K. conceived the idea, obtained funding, supervised all work, and corrected the manuscript. The manuscript is submitted with the consent of all authors.
Corresponding author
Ethics declarations
Competing Interests
Authors declare no competing interests. The manuscript was submitted by approval of all authors.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Anwar, A., Masri, A., Rao, K. et al. Antimicrobial activities of green synthesized gums-stabilized nanoparticles loaded with flavonoids. Sci Rep 9, 3122 (2019). https://doi.org/10.1038/s41598-019-39528-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-39528-0
This article is cited by
-
Morinda citrifolia leaf assisted synthesis of ZnO decorated Ag bio-nanocomposites for in-vitro cytotoxicity, antimicrobial and anticancer applications
Bioprocess and Biosystems Engineering (2024)
-
Effect of embelin on inhibition of cell growth and induction of apoptosis in Acanthamoeba castellanii
Archives of Microbiology (2023)
-
Phytochemical-Based Synthesis of Silver Nanoparticle: Mechanism and Potential Applications
BioNanoScience (2023)
-
Screening of Antibacterial and Antioxidant Activity of Biogenically Synthesized Silver Nanoparticles from Alternaria alternata, Endophytic Fungus of Dendrophthoe falcata-a Parasitic Plant
BioNanoScience (2022)
-
Transcriptome analysis of Escherichia coli K1 after therapy with hesperidin conjugated with silver nanoparticles
BMC Microbiology (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.