High-quality, 25 nm octahedral-shaped Fe3O4 magnetite nanocrystals are epitaxially grown on 9 nm Au seed nanoparticles using a modified wet-chemical synthesis. These Fe3O4-Au Janus nanoparticles exhibit bulk-like magnetic properties. Due to their high magnetization and octahedral shape, the hybrids show superior in vitro and in vivo T2 relaxivity for magnetic resonance imaging as compared to other types of Fe3O4-Au hybrids and commercial contrast agents. The nanoparticles provide two functional surfaces for theranostic applications. For the first time, Fe3O4-Au hybrids are conjugated with two fluorescent dyes or the combination of drug and dye allowing the simultaneous tracking of the nanoparticle vehicle and the drug cargo in vitro and in vivo. The delivery to tumors and payload release are demonstrated in real time by intravital microscopy. Replacing the dyes by cell-specific molecules and drugs makes the Fe3O4-Au hybrids a unique all-in-one platform for theranostics.
Recent advances in nanotechnology suggested new platforms for cancer diagnostics and treatment1,2,3,4,5. Different from traditional imaging with contrast agents and subsequent administration of therapeutics, the new concept of cancer-fighting nanomedicine aims at integrated designs to explore multiple functions via so called «all-in-one» systems6,7,8,9. Multifunctional nanoparticles (NPs) can enable theranostics for simultaneous imaging and therapy as well as multimodal imaging with the combination of two or more visualization modalities10,11,12. Currently, the theranostics paradigm evolves from a simple combination of therapy with a diagnostic test towards nanotherapeutic systems with imaging function, e.g. allowing for the simultaneous monitoring of drug delivery and release13,14. Therefore, multifunctional theranostic NPs enable noninvasive in vivo pharmacokinetic and biodistributional analyses in order to improve drug targeting to pathological sites and therapeutic effectiveness at an early stage of a disease15,16. Important prerequisites for a working all-in-one platform using hybrid NPs as drug carriers are the circulation time in blood and the effectiveness of accumulation in tumor tissue17,18. Consequently, it is of utmost importance to understand how multifunctional NPs interact with biological environment in vivo.
Nowadays, these processes can be visualized via various imaging techniques including magnetic resonance imaging (MRI) due to its exquisite soft tissue contrast, high spatial resolution, and wide clinical applicability19,20. A vast amount of research has been devoted to complement MRI by optical imaging leading to so-called dual-mode techniques21,22. A key focus in nanomedicine involves the use of nanomaterials as contrast agents for improved anatomical and functional imaging15,23. Using hybrid NPs, the anatomic information provided by MRI can be supplemented by functional details of a molecular event by dual-mode imaging. A relatively new imaging technique is intravital microscopy (IVM) enabling real time studies of the pharmacodynamics and pharmacokinetics at cellular level in live systems. IVM has been used to investigate the accumulation of fluorescently labeled NPs in tumors24,25,26, interactions with the tumor microenvironment (macrophages, monocytes, neutrophils) and the physiological and mechanistic barriers to therapeutic NPs accumulation in target cells27,28. Hybrid magnetic NPs conjugated or doped with fluorescent agents have thereby confirmed an improved image quality29,30,31. The contrast enhancement mediated by magnetic NPs strongly depends on their perturbation of nearby protons and can be tuned by their size, shape and intrinsic magnetism like the saturation magnetization and the magnetocrystalline anisotropy32,33,34. Understanding the interplay of these parameters is critical for effective imaging35,36. Considerable efforts have been made for the rational design and manufacture of magnetic NPs with high relaxivity37,38. However, the complexity of this aim is much greater than initially expected, calling for a broad multidisciplinary expertise in chemistry, physics, biology, and engineering19,39.
Hybrid materials for theranostics are increasingly attracting attention since they enable the combination of different properties and functions in one multipurpose hybrid material15,40,41,42. In particular, high adaptability is achieved by controlling the surface chemistry43,44. Due to biocompatibility, Fe3O4 and Au are the materials of choice for therapeutic and diagnostic dual use45,46,47,48. Over the last years a vast variety of fluorescent markers, vector molecules, and drugs has been developed for Au NPs decoration49,50. While the Fe3O4 part is the MRI contrast agent, it can also be used as a second binding site for functional molecules. Further, its ability for steered guidance along strong field gradients, hyperthermia applications and magneto-mechanical actuation are outstanding and may lead to even more enhanced therapies7,51,52,53,54,55,56,57. Due to these properties, targeted delivery based on magnetic NPs to malignant tissues is a promising concept in cancer biology28,57,58,59.
Several highlights have been demonstrated in this field using Fe3O4-Au hybrid structures60,61,62,63,64,65, including the combination of therapeutic species and targeting molecules for drug delivery66, the synergistic effect of magnetic hyperthermia and photo-thermal/photodynamic therapy67,68 as well as dual-mode contrast agents for magnetic resonance imaging and computer tomography69,70. In addition, Fe3O4-Au Janus NPs exhibit two binding sites and can serve as a unique tool for studying NPs drug delivery in vivo, although not much attention has been spent to this, yet. Due to the overall complexity of the hybrid systems it is extremely important to show the full «journey» of Fe3O4-Au NPs from the first steps of synthesis, subsequent characterization and primary functionalization to the final in vivo application.
In this work, we present a unique combination of novel Fe3O4-Au hybrids synthesis and their full physical-chemical characterization revealing unusual fundamental properties. Subsequently, we show that these hybrids are operational in vitro and in vivo. The overall concept of this work is schematically presented in Fig. 1.
Detailed studies of the structure by transmission electron microscopy and X-Ray diffraction discover octahedral-like, single-crystalline Fe3O4 NPs with bulk-like lattice parameters, epitaxially grown on top of Au seeds, providing two surfaces for the functionalization chemistry. Further characterization reveals large saturation magnetization values and the presence of the Verwey transition in the temperature dependence of the magnetization, pointing to bulk-like ferrimagnetic properties. High quality and stoichiometry of our Fe3O4 NPs is additionally proven by Mössbauer spectroscopy data. Fe3O4-Au NPs are subsequently covered with a biocompatible polymeric shell. We show for the first time a path to multifunctionality of such Fe3O4-Au hybrids by simultaneous conjugation of two fluorescent dyes or alternatively the combination of drug and dye, selectively binding to Fe3O4 and Au. Fe3O4-Au NPs are functionalized with covalently attached Sulfo-Cyanine5 NHS ester derivative (Cy5) fluorescent dye via thiol-Au bonds allowing NP tracking. In addition, the anticancer therapeutics doxorubicin (DOX) or Nile Red dye is loaded into the polymeric shell at the Fe3O4 surface as a model for a hydrophobic drug. Further, functionalized Fe3O4-Au hybrids are thoroughly tested in the 4T1 murine breast cancer cell line for stability, in vitro toxicity, cell internalization, drug carrier capabilities and release. After this comprehensive in vitro study, subsequent targeting of fluorescently labeled Fe3O4-Au hybrids to 4T1 tumors reveals high values of passive accumulation. Further IVM experiments with Fe3O4-Au hybrids labeled with Cy5 and loaded with Nile Red dye successfully prove the payload delivery to tumors with its subsequent release.
Finally, we demonstrate the high potential of our Fe3O4-Au hybrids for MRI diagnostics. The R2 relaxivity in water and 4T1 cells is at least doubled as compared to the maximum values obtained for Fe3O4-Au hybrids71,72 and 3–5 times higher as compared to commercial T2 contrast agents in medical use36,73,74 opening new avenues for in vivo contrast enhancement. Therefore, such NPs represent a unique platform for modern theranostics, comprising the diagnostics function together with the ability for studying the cargo and vehicle functions separately and in conjugation, both in vitro and in vivo, for targeted drug delivery.
Results and Discussion
Preparation of Fe3O4-Au hybrid NPs
We start the synthesis of Fe3O4-Au hybrid NPs with oleylamine-stabilized Au NPs as described elsewhere75. After that Fe3O4 is grown on the Au seed particles along the synthesis established before76,77. We replace 1-octadecene by phenyl ether and increase the reaction time from 45 min to 3 h allowing for a full crystallization process. Here, the NPs exhibit a strongly improved crystallinity and a highly facetted growth mode based on an octahedral motif as we show in the following section.
Fe3O4-Au hybrid NPs have high-quality crystalline structure and octahedral morphology
The structure and morphology of the Fe3O4-Au NPs are investigated by X-Ray Diffraction (XRD) and transmission electron microscopy (TEM). Figure 2a presents the experimental data and a Rietveld refinement combining powder diffraction reference data of Fe3O4 (ICDD PDF-2 № 00-019-0629) and Au (ICDD PDF-2 № 03-065-8601). All expected powder diffraction peaks of magnetite are clearly observed, and the fit resembles the relative intensities convincingly. The extracted lattice constants, crystallite sizes and phase volume fractions are collected in Supplementary Table S1. Since magnetite Fe3O4 and maghemite γ-Fe2O3 are structurally similar, XRD only gives a first hint which phase has been prepared. The XRD result a = 0.8394 nm points towards Fe3O4 (a = 0.8397 nm) rather than γ-Fe2O3 (a = 0.8346 nm)78. Further evidence for Fe3O4 is given by Mössbauer spectroscopy below. XRD suggests bulk-like Fe3O4 and Au NPs with crystallite sizes of 26 nm and 5 nm, respectively. The volume fractions of the Fe3O4 and Au phases are 96.2% and 3.8%, which corresponds to 84.6 and 15.4 mass-% assuming Fe3O4 and Au bulk density, respectively (see Supplementary Table S2).
Figure 2b presents a TEM image of Fe3O4-Au NPs. The seeded growth of the highly facetted Fe3O4 on almost spherical Au NPs forming Janus NPs is clearly observed. The Fe3O4 NPs have the tendency to form octahedra, which are mainly found in two morphologies, truncated or elongated. The Fe3O4 median diagonal length is 25 ± 5 nm and the spherical Au NPs exhibit an average diameter of 9 ± 2 nm. The size histograms of both components are provided in Supplementary Fig. S1. The Fe3O4 TEM size and the XRD crystallite size fit very well indicating single crystalline Fe3O4 while the XRD Au crystallite size of 5 nm suggests polycrystalline Au in the hybrid NPs. In Supplementary Fig. S2a, the elemental mapping by energy-dispersive X-ray (EDX) spectroscopy in high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) proves the presence of both Fe3O4 and Au in the hybrid NPs and the integrated EDX spectrum in Supplementary Fig. S2b delivers mass fractions of 86.7% Fe3O4 and 13.3% Au. Further, atomic emission spectrometry (AES) yields 85.3 and 14.7 mass % Fe3O4 and Au, respectively (see Supplementary Table S2). Thus, all 3 techniques deliver similar Fe3O4 and Au mass content within 2%.
Next, we evaluate the crystallographic interface of Fe3O4 and Au in the hybrids using atomically resolved HAADF-STEM imaging (Fig. 2c). It is directly visible that the Au NPs, acting as seeds in the synthesis, allow for epitaxial growth of Fe3O4 on Au forming the Janus structure with Au(200) || Fe3O4(200) and Au || Fe3O4 similar to electrodeposited epitaxial films79. The interplanar distances calculated from HAADF images are found very close to Fe3O4 and Au bulk values (Supplementary Table S3). We ascribe the growth mode of a single Fe3O4 NP per Au seed to the long crystallization process. This, however, cannot be unambiguously clarified based on the present experiments. The bright field high-resolution TEM (HRTEM) images presented in Supplementary Fig. S3 further prove the Janus character of the NPs. The spherical Au NPs are clearly located at the Fe3O4 surface. Since HRTEM and HAADF imaging only yield 2D projections of 3D objects, we analyze the three-dimensional (3D) morphology of the Fe3O4-Au NPs by electron tomography. Supplementary Fig. S4 presents a rendered reconstruction with clearly separated Fe3O4 and Au entities. The Supplementary Video S1 (3D tomography) further yields that the Au NPs are located at the Fe3O4 surface enabling functionalization as discussed below. Note, that the stability of the NPs under the electron beam is limited and some deterioration cannot be avoided in 3D tomography. To the best of our knowledge such an octahedral-spherical morphology of a Fe3O4-Au hybrid has not been described in literature before. We note for completeness that Fe3O4-Au NPs with non-spherical magnetite morphology for sensors and supercatalysts80,81, Fe3O4-Co or Fe3O4-Cu82, and FePt-PbS NPs83 have been investigated. However, the latter three systems do not meet the requirements for biomedical applications due to their inherent toxicity. In fact, the morphology of Fe3O4-Au hybrid NPs is usually not discussed in detail and mostly spherical or cubic Fe3O4 NPs are obtained. Interestingly, it has been shown for pure Fe3O4 NPs that size and morphology strongly affect the properties of the final product82.
Fe3O4-Au hybrid NPs exhibit bulk-like magnetic properties
Further proof of the high quality Fe3O4 can be gained inspecting the magnetic properties. Figure 3a presents magnetization loops at 5 K and 300 K confirming the expected ferrimagnetic response. Hysteresis loops are measured up to ±9 T at 5 K and 300 K and up to ± 1 T at intermediate temperatures (Supplementary Fig. S5). From high field measurements the saturation magnetization MS of 96.0 ± 3.0 (86.0 ± 3.0) Am2/kg at 5 K (300 K) for Fe3O4 has been evaluated subtracting the Au content (EDX analysis in Supplementary Table S2). These values are very close to the bulk ones of 96.4 (92.0) Am2/kg at 5 K (300 K) reflecting the high quality of the Fe3O4 crystals84,85. The coercive field µ0HC decreases from 57 mT at 5 K to 9 mT at 300 K (Supplementary Table S4). Sharrock’s equation derived for the temperature dependence of the coercive field of single domain, randomly oriented, non-interacting NPs,
allows to estimate the volume averaged blocking temperature TB = 278 K as shown by the linear fit in Fig. 3b86,87. The non-vanishing coercive field above TB is related to NPs with larger volumes. In the approximation of spherical particles with a diameter of 22 nm (cf. Supplementary Fig. S1) we extract an effective anisotropy constant Keff = (1.4 ± 0.2) · 104 Jm−3 from 21kBT ≈ Keff V with kB the Boltzmann constant and V the NP volume. The prefactor 21 accounts for an attempt frequency of 109 Hz and the VSM measurement time of 1 s32,88. This value is in good agreement with the first order anisotropy constant of bulk Fe3O4 K1 = 1.3 ·104 Jm−389.
Figure 3c presents zero field cooled and field cooled (ZFC/FC) magnetization curves measured in 5 mT from 5 K to 350 K. After ZFC the magnetization rises monotonously to the highest temperature reflecting the broad Fe3O4 volume distribution in the sample and the gradual transition to the superparamagnetic state. The ZFC/FC curves split directly at the highest temperature, and the FC curve gives a rather constant value. The most important features in these curves are the kinks at TV = 123 K. We identify this with the Verwey transition from monoclinic to the cubic inverse spinel structure90. This feature is rarely observed in NPs and if at all, only at significantly reduced temperatures. Furthermore, slightly off-stoichiometric Fe3(1−x)O4 single crystals show a decreasing TV from 123 K for x = 0 to TV = 110 K for x = 0.00389. Similar behavior has been observed in Ag@Fe3O4 core-shell NPs with TV = 120 K91.
Further insight into the NP magnetic structure is obtained by Mössbauer spectroscopy. Figure 3d presents the spectrum and its simulation. All extracted parameters are listed and explained in Supplementary Table S5 and accompanying text. For off-stoichiometric Fe3(1−x)O4 crystals, the data deliver a vacancy parameter x = 0.01, which in turn gives 31% of Fe2+ ions close to the 33% Fe2+ in a stoichiometric Fe3O4 crystal. Considering further that a 25 nm-sized Fe3O4 NP has about 6% Fe atoms at the surface, the total amount of over-oxidized Fe ions should be in the range of one atomic layer or less. Details on the estimation are given in the Supplementary Information.
In other words, both magnetometry and Mössbauer spectrometry prove high-quality, stoichiometric Fe3O4 in the NPs. Moreover, from the structural and magnetic data it can be concluded that the Fe3O4-Au Janus NPs exhibit bulk-like properties. Further, the NPs are highly stable as MS decreases only by 5% after 6 months of powder storage in ambient conditions.
Fe3O4-Au hybrid NPs enable various modes of surface functionalization
Along with a fundamental understanding of the physical properties of Fe3O4-Au NPs for theranostics, the preparation of water-stable NPs is required for their use in biomedicine. For that purpose Fe3O4-Au NPs are transferred to water (NP-PEG) by means of phospholipid-polyethylene glycol block-copolymer (DSPE-PEG-COOH), which is widely used in drug delivery applications72,92. As a result, the surface of NP-PEG is decorated with polymeric chains and carboxylic groups, imparting negative ζ–potential of −19.1 ± 3.3 mV to the NPs. Dynamic light scattering (DLS) gives a final hydrodynamic diameter of DHD = 121 ± 5 nm. This size is suitable for cell uptake and tumor targeting21. NP-PEG solutions in both DI H2O and PBS are stable in external magnetic fields (Supplementary Fig. S6). No deterioration of their saturation magnetization is observed. Note that the particles are free to rotate when the magnetic field is released. Thus the field-dependent magnetization has zero remanence for both low and high field sweeping rates (Supplementary Fig. S6, inset).
Subsequently, NP-PEG are used for two modes of surface functionalization, so called «single» and «double» functions (see Fig. 1). Single functionalization (NP-Cy5) is solely based on the attachment of a Cy5 fluorescent dye derivative, containing an S-S fragment, to the Au surface forming strong covalent Au-S bonds, while the Fe3O4 part is still decorated with polyethylene glycol and serves for the overall stabilization. Both, the NP-Cy5 hydrodynamic diameter and the ζ–potential do not change significantly in comparison with the corresponding NP-PEG values (125 ± 7 nm and −20.2 ± 4.7 mV, respectively), which can be explained by the relatively low amount of Cy5 attached (33 µg of Cy5 per 1000 µg of Fe3O4/154 µg of Au).
Besides the Cy5 labelling, double functionalization includes non-covalent loading of the second fluorescent dye Nile Red (NRed-NP-Cy5) or antitumor drug doxorubicin (DOX-NP-Cy5) into the polymeric shell on Fe3O4 NPs. Both doxorubicin and Nile Red can be loaded in the phospholipid part of DSPE-PEG-COOH at 86 µg of Nile Red and 285 µg of doxorubicin per 1000 µg of Fe3O4. In both cases the hydrodynamic diameter increases but still remains below 200 nm (172 ± 15 nm for NRed-NP-Cy5, 198 ± 19 nm for DOX-NP-Cy5). The ζ–potential is still negative for NRed-NP-Cy5 (−24.9 ± 5.1 mV) due to the strong hydrophobic properties of Nile Red “hidden” in the polymer shell. On the contrary, the ζ–potential of DOX-NP-Cy5 changes sign (+22.4 ± 5.3 mV) due to the positive charge of the doxorubicin base.
The efficiency of the conjugation of dyes and drug to NP-Cy5, NRed-NP-Cy5 and DOX-NP-Cy5 is estimated by absorption spectroscopy in the visible range. Supplementary Fig. S7a,b reveals the characteristic peak of Cy5 (≈640 nm) for all labeled NPs with the appearance of a Nile Red peak (≈539 nm) and a doxorubicin (≈480 nm) for NRed-NP-Cy5 and DOX-NP-Cy5, respectively. The absence of unbound dyes after washing steps (centrifugation combined with filtration and dialysis) is proven by measuring the supernatant absorbance. The selective functionalization of Au NPs with Cy5 and the loading of doxorubicin into the polymeric shell covering Fe3O4 NPs in hybrid Fe3O4-Au NPs is demonstrated by separate experiments with Fe3O4-PEG NPs (20 nm diameter magnetic core) and Au-PEG NPs (9 nm diameter) according to the identical protocol. As a result, an enhanced signal at 450–500 nm corresponding to doxorubicin absorption is observed only for DOX-NP-Cy5 and Fe3O4-PEG NPs, while the peak at 635–650 nm corresponding to Cy5 absorption is revealed only for DOX-NP-Cy5 and Au-PEG NPs (Supplementary Fig. S7c).
Fe3O4-Au hybrid NPs are stable, non-toxic and internalized by cancer cells in vitro
To ensure the Fe3O4-Au hybrid NPs biocompatibility, we study their stability in physiological buffers and their in vitro toxicity. Figure 4a,b demonstrates that NP-PEG (333 μg·ml−1 Fe3O4 and 51 μg·ml−1 Au concentration) preserve their initial hydrodynamic diameter and polydispersity index for at least 2 weeks at 25 °C in deionized water and 1× PBS. Further, in RPMI cell media, both in presence and in absence of serum (FBS), stability is achieved for at least 2 days at 37 °C, which is sufficient for subsequent in vitro/in vivo studies. Similar stability is observed for NP-Cy5 (Supplementary Fig. S8a,b).
Both NP-PEG and NP-Cy5 are found to be non-toxic in a wide concentration range in a MTS assay (Fig. 4c and Supplementary Fig. 8c) and in a hemolytic ex vivo test (Supplementary Fig. S9). Cytotoxicity and hemolytic activity are revealed only for highest NPs concentration (0.333 mg·ml−1). Oxidative stress has been proposed as the main cytotoxic mechanism of magnetic NPs93,94,95. Reactive oxygen species (ROS) detection after 4 h and 24 h of 4T1 cells incubation with NP-PEG confirms that only the highest NPs concentration results in increased ROS production 24 h after co-cultivation (Supplementary Fig. S9).
For deeper studies of the NPs interaction with cells, we investigate the dynamics of NP-Cy5 accumulation in 4T1 cells for 24 h (Fig. 4d). Accumulation of NPs in 4T1 cytoplasm is detected as early as 30 min after NPs inoculation on cells (193 μg·ml−1 Fe3O4, 30 μg·ml−1 Au, 6 μg·ml−1 Cy5) further increasing after 6 h. After 30 min of incubation, a NP-Cy5 diffuse distribution in the cytoplasm is observed with profound perinuclear area accumulation. After 6 h of co-incubation, NP-Cy5 are detected as aggregates and localize near the cells nuclei as well as in cell lamellae presumably due to accumulation in late endosomes and/or multivesicular bodies96. Free Cy5 (used as control) does not accumulate in the cells. To prove the internalization of NPs, laser scanning confocal microscopy has been performed. 3D optical sections clearly demonstrate that NPs accumulate inside cancer cells rather than on cell membranes (Fig. 4e). Quantification of Fe3O4 and Au by AES in cells incubated with NP-PEG (100 μg·ml−1 Fe3O4, 15 μg·ml−1 Au) during 48 h and thoroughly washed with PBS also suggests NPs internalization (Fig. 4f). It should be emphasized that the ratio of accumulated to the delivered amount is identical for Fe3O4 and Au. Thus, the Fe3O4-Au hybrid NPs most probably remain intact during in vitro experiments.
Fe3O4-Au hybrid NPs deliver therapeutic payload to cancer cells
The Fe3O4-Au hybrid NPs can be used as a vehicle for drug delivery. Here, we use NP-Cy5, loaded with doxorubicin (DOX-NP-Cy5). Experiments with its release kinetics from DOX-NP-Cy5 solutions (NP concentration 1000 μg·ml−1 Fe3O4, 154 μg·ml−1 Au, 33 μg·ml−1 Cy5, 285 μg·ml−1 doxorubicin, Fig. 5a) show that this process is rather slow in RPMI cell medium (pH = 7.2), since only 13% of the loaded drug is released during 48 h, while in 0.1 M acetate buffer (pH = 4.7) almost 20% of doxorubicin is released in the first 2 h and doubled after 48 h. The accelerated release of doxorubicin at a lower pH is due to the drug’s high solubility in these conditions97,98. Therefore, it can be expected that in cell medium DOX-NP-Cy5 keep the loaded doxorubicin before internalization by cells with subsequent drug release after pH change, taking place in acidic cell compartments (e.g. endolysosomes) upon DOX-NP-Cy5 internalization.
To investigate the efficiency of doxorubicin delivery by Fe3O4-Au hybrid NPs, we incubate 4T1 cells with DOX-NP-Cy5 (63 μg·ml−1 Fe3O4; 2 μg·ml−1 Cy5; 18 μg·ml−1 doxorubicin) and compare the dynamics of drug accumulation at different time points with free doxorubicin of the same concentration. In both cases, gradual increase of doxorubicin fluorescence intensity in cells nuclei is detected (Fig. 5b and Supplementary Fig. S10). Although at early stages (15 min–1 h) free doxorubicin tends to accumulate faster than doxorubicin delivered by DOX-NP-Cy5 (Fig. 5c), the difference decreases after 2–4 h and balances within the error bar after 6 h of co-cultivation. Consistent with this data, DOX-NP-Cy5 are able to kill 4T1 cells after 48 h co-cultivation, although not as effective as the free drug (IC50 = 4 µM and 1.2 µM DOX, respectively; Fig. 5d). This difference is probably due to the fact that free doxorubicin continuously penetrates the cells by passive diffusion through the plasma membrane99. DOX-NP-Cy5 internalization (by endocytosis)96,100 and doxorubicin release from NPs take more time: NPs are required to bind to the cell plasma membrane, penetrate inside the cell by active endocytosis and get into endolysosome with low pH (4.5–5.0) to release the drug (Fig. 5a)101. These experiments indicate that Fe3O4-Au hybrid NPs can be used for therapeutic cargo delivery to cancer cells.
Fe3O4-Au hybrid NPs accumulate in tumors via enhanced permeability and retention effect (EPR effect)
Upon intravenous injection, liver and spleen sequester up to 99% of NPs enormously decreasing their delivery to the target tissues102. The NPs clearance rate depends on their size, surface chemistry and charge, thus larger cationic NPs are retained in liver and spleen to greater extent than its smaller counterparts with neutral surface charge103,104 NPs stability in blood flow and decreased blood clearance (prolonged circulation time) are prerequisites for their efficient delivery to the tumor bed. Many studies have shown the power of the NPs for specific targeting and killing cells in vitro, however, less than 1% of the administered NP dose is delivered in vivo to a solid tumor42,102. Low percentage of the injected dose (ID) accumulating in malignant tissues is a main issue for the NPs clinical translation, so increasing the delivery efficiency is a central strategy in the field. Enhanced permeability and retention effect (EPR effect) is a major factor of NPs passive delivery to malignant tissues105.
We study NPs delivery to malignant tissues in vivo by intravenous injection of NP-Cy5 (6.6 mg·kg−1 Fe3O4) to mice while imaging 4T1-GFP tumor microenvironment by IVM (Fig. 6a, Supplementary Video S2). In 1–3 minutes after systemic administration, tumor vessels are counterstained with floating NPs with no signs of aggregation. Notably, the fluorescence intensity inside vessels rapidly increases within the first minutes and remains stable for at least 30 min (Fig. 6a, Supplementary Fig. S11a) suggesting delayed clearance of circulating NPs. Starting from 15 min after injection, NP-Cy5 are detected outside tumor vessels (Fig. 6a). Extravascular Cy5 fluorescence intensity corresponding to the local concentration of NPs keeps growing during the observation time (60 min). NPs diffusion into tumor tissues is mostly limited to the 100 μm perivascular region. It has been suggested that tumor macrophages play an essential role in NPs accumulation and drug release in malignant tissues106. Consistent with these reports, we have found adsorption of NPs on perivascular stromal cells, most likely macrophages.
To investigate the dynamics of NP-Cy5 accumulation in tumors, the entire body is examined by in vivo fluorescence imaging (IVIS). As expected, 1 h after i.v. administration, NPs are mainly found in liver, but 6 h upon injection NPs accumulation in tumors is clearly detectable (Fig. 6b,c). Although the fluorescence intensity in tumors slightly decreases after 24 h, the tumor/liver intensity ratio constantly increases from 1 h to 24 h (Fig. 6b). We quantify the NPs biodistribution in 4T1 tumor-bearing mice by measuring the Fe and Au concentrations by AES. Tumors, kidneys, lungs, heart, spleen and liver are collected 24 h after NP-Cy5 injection and dissolved in aqua regia. Consistent with IVIS data, Au accumulation is detected mostly in liver and tumor (Fig. 6e). A similar biodistribution profile is obtained for Fe (Supplementary Fig. S11b). Au and Fe concentrations in liver are higher than in tumors opposite to IVIS data. Presumably, IVIS underestimates NPs accumulation in inner organs due to light scattering from deeper tissues.
Nonetheless, based on AES data, up to 3% of the injected dose reaches the tumor 24 h upon i.v. injection that is higher than the median NPs delivery efficiency recently reviewed by Wilhelm et al.102 Overall, the data suggest that upon systemic administration, Fe3O4-Au hybrid NPs accumulate in tumor tissue due to the EPR effect.
Fe3O4-Au hybrid NPs deliver payload to tumors
NPs-based drug delivery to the tumor site is essential but not sufficient for an efficient treatment. Drug release from the carrier is required in order to exert its effect. Two different binding sites make the Fe3O4-Au Janus NPs a unique tool for simultaneous studying of the vehicle biodistribution and cargo release. We demonstrate this using NRed-NP-Cy5. While the Cy5 label is covalently bound to Au in Fe3O4-Au NPs and enables NPs tracking, Nile Red is non-covalently loaded into the polymeric shell on Fe3O4 NP, mimicking a hydrophobic drug (e.g. paclitaxel) and enabling in vivo imaging of the payload release due to its fluorescent properties. Interestingly, recent studies suggest that Nile Red can also be used as a photosensitizer107,108.
NRed-NP-Cy5 delivery and distribution have been studied by IVM in 4T1-GFP-bearing animals. Due to its higher fluorescence intensity, Cy5 is detected on single NPs resulting in vasculature counterstaining immediately after i.v. injection. In contrast, Nile Red fluorescence in tissues is lower as compared to Cy5, thus only NP aggregates in the vessels are found to be Nile Red and Cy5 double positive (Fig. 7a and Supplementary Video S3). Real-time imaging reveals Nile Red release in the tumor microenvironment. Within 2 min after NPs attachment to the vessel wall, Nile Red diffuses into the surrounding malignant tissue (Fig. 7b and Supplementary Video S4).
Next, we investigate the vehicle and payload accumulation in tumors 6 h after NRed-NP-Cy5 i.v. injection. The Cy5 signal is detected throughout the tumor tissue after NPs injection (Fig. 7c,d) as compared to the untreated tumor (Fig. 7e). Although Nile Red accumulates at the same spots, no co-localization with Cy5 is found at microscopic level, presumably due to the drug release in tumor tissue. Consistent with its lipophilic properties, Nile Red is also found in perivascular lipocytes. The above experiments suggest that Fe3O4-Au Janus NPs are suitable carriers for hydrophobic drug delivery to tumor microenvironment. The promising perspective here is the combination of drug species and low-weight ligands to cell receptors (for instance, PSMA-ligands109,110) allowing the attachment of the final bio-conjugate to specific cells for targeted drug delivery66.
Fe3O4-Au hybrid NPs as MRI contrast agent
The hybrid NPs show all important features of a platform for therapy (cf. Fig. 1). The double functionality allows for NPs tracking and payload release as shown above. Moreover, the outstanding magnetic properties may also lead to enhanced functionality in MRI. We are judging the potential of Fe3O4-Au hybrid NPs for diagnostics by the evaluation of the T2 contrast enhancement in MRI measuring the R2 relaxivity values as function of Fe concentration in water and in 4T1 cells. Figure 8a presents the proton T2−1 relaxation time, and Fig. 8b phantom images as function of Fe concentration for NP-PEG in water and 4T1 cells. A linear relationship is found for both specimens for all concentrations. In the respective regimes we do not observe agglomeration effects nor precipitation during 40 min of measurement in B = 7 T.
The transverse relaxivity coefficient R2 is the slope in Fig. 8a; and we obtain R2 = 498.1 mM−1s−1 for NP-PEG in water. This value is more than 3 times larger as compared to commercial T2 contrast agents with R2 ≈ 160 mM−1s−1 proving the superior MR contrast of the hybrid NPs as compared to commercial agents73. Further, the diagnostic capabilities of the hybrid NPs are tested in vitro. After incubation of 4T1 cells with NP-PEG for 24 h, the obtained R2 = 276.9 mM−1s−1 decreases, however, remains reasonably high for imaging in line with other experiments in cell cultures111. Note that MRI is conducted in a 7 T (298.06 MHz) animal scanner, which has the advantages of high signal-to-noise ratio and high spatial resolution for in vivo animal imaging. However, the induction of B = 7 T is much higher than those of most clinical scanners in use (1.5–3 T, 63.87–127.74 MHz). Smolensky et al. have shown that the transverse relaxivity R2 of iron oxide NPs is independent of the magnetic field strength in the frequency range of 20–500 MHz112. This means that the MRI results obtained in this study are also valid for clinical scanners at lower fields. As compared to the recent literature the present hybrid Fe3O4-Au NPs are more efficient than other Janus NPs (R2 = 125.5–381.4 mM−1s−1)71,111,113,114. The most probable reasons for this extraordinary high performance are the perfect crystallinity and the resulting bulk-like MS leading to a stronger local magnetic field in the vicinity of NPs. This is in agreement with the suggestion of Lee et al.115 that the R2 value solely depends on the MS value. In addition to the stray field strength, the facets of NPs produce strong stray field gradients ΔB in their vicinity, especially near the 6 corners and 8 edges of the magnetic octahedrons. According to MRI theory116 an additional gradient ΔB leads to an acceleration of the transverse relaxation of spins, expressed by 1/T2* = 1/T2 + γΔВ/2, where T2* denotes the shortened transverse relaxation time, T2 is the transverse relaxation time in a homogeneous field, and γ = 2.67·108 rad s−1 T−1 the gyromagnetic ratio of water protons. These findings correlate with the highest R2 values ever reported (761 mM−1s−1 for 22 nm cubic Fe3O4 NPs115 and 679 mM−1s−1 for Fe3O4 octopods117). The experiments clearly point to a highly improved R2 relaxivity of Fe3O4-Au hybrid NPs due to their angular structure as compared to commercial spherical contrast agents.
Next, we test NPs potential in in vivo MRI. Developing new contrast agents for MRI imaging is crucial for tumor lesions detection118 and personalized MRI-guided therapy24. Although a variety of iron oxide-based NPs has been developed for contrast-enhanced MRI, poor delivery efficiency remains a major challenge in tumor-detecting imaging. In our experiment, 4T1-bearing mice or B16-F10-bearing mice are i.v. treated with NP-PEG (6.6 mg·kg−1 Fe3O4), and T2-weighthed images are captured before, 30 min, 6 h and 24 h after NPs injection (Fig. 8c, Supplementary Figs S12 and S14). Although 30 min after injection NPs accumulation is detected mainly in liver, at later time points (6 h and 24 h) enhanced tumor contrasting is clearly seen. Consistent with IVIS data, NPs accumulation peak in malignant tissues is around 6 h after injection. High accumulation efficiency of our NPs in malignant lesions (up to 3%) coupled with MRI data makes Fe3O4-Au hybrid NPs an attractive platform for tumor theranostics.
The investigated Fe3O4-Au hybrid NPs have multifunctional properties forming an all-in-one platform for theranostics. We presented a comprehensive study starting with the chemical preparation, via careful physical characterization and biomedical functionalization to in vitro and in vivo testing of the NPs functionalities for diagnostics and therapy.
Due to rigorous design we achieved 25 nm octahedral-shaped Fe3O4-Au hybrid NPs with bulk-like structural and magnetic properties. The large magnetization of stoichiometric Fe3O4 and the faceted growth mode yield a superior in vitro and in vivo T2 contrast in MRI as compared to other hybrids or commercial materials. We ascribe this finding to the large magnetization of the crystals and the huge field gradients in the vicinity of the corners and edges of the octahedra.
The two functional surfaces (Au and Fe3O4) allow for the selective loading with fluorescence dyes or drugs for fluorescence tracking and payload delivery after transfer of the non-toxic hybrids to water. Multimodal fluorescence imaging and intravital microscopy of the uptake of the hybrids in vitro in the 4T1 cancer cell line and the corresponding in vivo breast cancer model prove that the NPs are passively accumulated in the tumor at a reasonable dose and the payload can be released in the tumor cells. These innovative multifunctional hybrid NPs combine therapeutic and visualization capabilities for the future use in simultaneous magnetic resonance imaging and therapy strategies based on targeted drug delivery, magnetic hyperthermia or magneto-mechanical actuation.
Synthesis of Fe3O4-Au NPs
Fe3O4-Au NPs were synthesized according to a modified protocol76,77. 0.28 ml of Fe(CO)5 were injected in the pre-heated (120 °C) mixture of phenyl ether and oleic acid under the argon atmosphere. Afterwards, 0.5 ml of oleylamine and 2 ml of pre-synthesized 9 nm Au NPs (20 mg ml−1 in hexane, synthesized along the procedure established by Liu et al.75) were added. The final solution was boiled at 260°С for 3 h and cooled to room temperature, followed by 1 h of room-temperature oxidation in ambient air. The NPs were isolated via centrifugation, washed with isopropanol and dispersed in toluene or chloroform.
Synthesis of NP-PEG
Fe3O4-Au NPs were transferred into water medium with 1,2-distearoyl-sn-glycero-3-phosphoethanolamine-N-[carboxy(polyethylene glycol)−5000] ammonium salt (DSPE-PEG-COOH)119. Briefly, equal volumes of Fe3O4-Au NPs and DSPE-PEG-COOH solutions (both 1 mg ml−1 in chloroform) were mixed by sonication for 5 minutes. Then the obtained mixture was left under weak N2 flow overnight. After the solvent evaporated, 1 ml of DI H2O was added to the precipitate and then it was resuspended in water aided by ultrasound for 5–10 minutes. Unbound polymer was removed by centrifugation. Finally, the sample was passed through a 0.45 μm syringe filter.
Synthesis of NP-Cy5
NP-Cy5 were obtained by conjugation of NP-PEG with Sulfo-Cyanine5 NHS ester derivative (Cy5) fluorescent dye. 0.1 mg of Cy5 in 100 µl of DI H2O was added to 5 mg of cystamine dihydrochloride in 900 µl of PBS (pH = 8.3–8.5), shaken on a vortex well and kept on ice overnight. The resulting conjugate of Cy5 was mixed with 1 ml of NP-PEG solution overnight at room temperature. After that, unbound dye was firstly removed by multiple centrifugations, and then the resulting NP-Cy5 solution was dialyzed against water (MWCO = 12 kDa) for 24 h. To confirm that washing steps effectively remove unbound dye, an aliquot of NP-Cy5 was passed through Amicon Ultra-4 Centrifugal Filter Units (100 kDa). The quantity of conjugated dye in NP-Cy5 (33 µg of Cy5 per 1000 µg of Fe3O4/154 µg of Au) was estimated with a calibration graph.
Synthesis of NRed-NP-Cy5
NRed-NP-Cy5 were synthesized by conjugation of Fe3O4-Au NPs with two fluorescent dyes, Nile Red (NRed) and Sulfo-Cyanine5 NHS ester derivative (Cy5). 100 μl of NRed (1 mg ml−1 in chloroform) was added to the mixture of 1 ml of Fe3O4-Au NPs and 1 ml of DSPE-PEG-COOH solutions (both 1 mg ml−1 in chloroform), further procedure was performed by the same protocol as for NP-PEG synthesis, resulting in the stabilization of NRed-NP in water solution (0.5 mg ml−1). In parallel with this, 0.1 mg of Cy5 in 100 µl of DI H2O was added to 5 mg of cystamine dihydrochloride in 900 µl of PBS (pH = 8.3–8.5), shaken on a vortex well and kept on ice overnight. The resulting conjugate of Cy5 was mixed with 1 ml of NRed-NP solution overnight at room temperature. The process of purification used was the same as for NP-Cy5. The quantity of conjugated dyes in NRed-NP-Cy5 (86 µg of Nile Red and 33 µg of Cy5 per 1000 µg of Fe3O4/154 µg of Au) was estimated with a calibration graph.
Synthesis of DOX-NP-Cy5
DOX-NP-Cy5 were obtained by doxorubicin loading to NP-Cy5. 100 μl of doxorubicin hydrochloride solution (DOX, 5 mg ml−1 in DI H2O) was added to 1 ml of NP-Cy5 (1 mg ml−1 in 1×PBS), and the mixture was shaken overnight at room temperature. Non-bound DOX was removed by centrifugation. The quantity of loaded drug (285 µg of DOX per 1000 µg of Fe3O4) was estimated with a calibration graph.
Patterns were measured from 2θ = 30° to 120° at a scan rate 0,1° per step and 3 s per point using the X-ray powder diffractometer Rigaku Ultima IV with Co-Kα radiation and graphite monochromator on the diffracted beam. Quantitative XRD analysis (including crystal size evaluation by determination of the coherent scattering region, OCD) was performed using PHAN% and SPECTRUM programs developed by Physical Materials Science Department of NUST «MISiS» (modification of Rietveld method), based on the minimization of the difference between the experimental spectrum, taken from the points, and model (calculated) one. For fitting the spectra, the lattice parameters, the amount of each phase and their crystallite diameter are optimized.
Experiments were conducted using a FEI Tecnai F20 and a probe-side Cs-corrected JEOL JEM 2200FS microscopes, both operated at 200 kV acceleration voltage. Overview images were taken in conventional bright-field TEM mode while the high-angle annular dark-field STEM mode was used for the high-resolution micrographs. Samples were prepared by casting and evaporating a droplet of solution onto a carbon-coated copper grid (300 mesh). The average diameter of NPs was calculated from TEM images by analysis of about 1000 NPs for each sample using ImageJ software. EDX elemental mapping was carried out in the scanning mode utilizing an Oxford X-max detector.
Dried powder of Fe3O4-Au NPs or NP-PEG solution (1 mg ml−1 in DI H2O/ 1× PBS) was compressed in synthetic capsules and the hysteresis loops and temperature dependent magnetization were measured in a Quantum Design PPMS DynaCool system.
Mössbauer spectra of 57Fe nuclei at room temperature were recorded with a MS-1104Em spectrometer in transmission geometry with a 57Co(Rh) radiation source. Spectra analysis was performed by Univem MS program, the relative intensities (area) of elementary spectra were determined.
The hydrodynamic size and ζ–potential of NP-PEG, NP-Cy5, NRed-NP-Cy5, DOX-NP-Cy5 were measured by dynamic light scattering (DLS) using a Nano ZS Zetasizer (Malvern Instruments). The average NPs sizes with error ranges were obtained from three measurements of each sample. Recording of optical spectra of NPs in the visible range (400–800 nm) was performed using Thermo Scientific Multiscan GO instrument.
2.5 ml of DOX-NP-Cy5 were suspended in RPMI cell medium (pH = 7.2) or 0.1 M acetate buffer, (pH = 4.7) to a final 1000 μg·ml−1 Fe3O4, 154 μg·ml−1 Au, 33 μg·ml−1 Cy5, 285 μg·ml−1 DOX concentration and incubated at 37 °C. 30 min, 2 h, 6 h, 24 h or 48 h after the incubation start, 500 µl of solution were centrifuged (10 min, 14100 g) for complete DOX-NP-Cy5 precipitation and supplemented with 3–5 min of magnetic decantation. Afterwards the supernatant absorbance at 480 nm wavelength, corresponding to released DOX, was measured. NP-Cy5 sample of the same concentration after the same centrifugation/decantation procedure was used as a negative control (0%). 100% release was achieved by 30 s treatment of DOX-NP-Cy5 with ultrasonic band (positive control). After background subtraction, the absorbance was normalized to the total absorbance of initially loaded drug.
BV421-conjugated rat anti-mouse Ly6g (clone 1A8) were purchased from BD Biosciences Pharmingen (San Diego, CA). PE-conjugated Armenian hamster anti-mouse CD49b (clone HMα2) were purchased from Biolegend (San Diego, CA).
4T1 (mouse breast cancer) and B16-F10 (mouse melanoma) cells were purchased from the American Type Culture Collection (ATCC, Manassas, VA, USA). Cells were cultured in RPMI-1640 (for 4T1) and DMEM (for B16-F10) medium (Gibco) supplemented with 10% fetal bovine serum (FBS) (Gibco) and 2 mM L-glutamine (Gibco) at 37 °C in a humidified incubator supplied with 5% CO2. GFP expressing cell line was obtained by 4T1 lentivirus transduction (MOI = 50) using LVT-TagGFP (Eurogen, Russia). All cell lines were routinely tested negative for mycoplasma.
Animals and tumor models
All animal experiments were reviewed at the bioethical commission by the Federal State Budgetary Educational Institution of Higher Education “The Russian National Research Medical University named after N.I. Pirogov” of the Ministry of Health of the Russian Federation and approved for conducting (conclusion of the bioethical commission No. 25/2017 and 26/2017). All methods were performed in accordance with Directive 2010/63/EU of the European Parliament and of the Council of 22 September 2010 on the protection of animals used for scientific purposes (Annex VIII). Six to eight-week-old female BALB/c and C57/bl6 mice were obtained from Andreevka Animal Center (Andreevka, Russia) and maintained in specific-pathogen free facility. At the time of investigations, animals were between 7 and 11 weeks old and weighed 20–25 g. 4T1 or 4T1-GFP tumours were established by injecting 1 × 106 cells and B16-F10-6 × 106 cells (in 50 µl PBS) subcutaneously into the right/left hind flanks. When tumours reached about 25 mm2 (after 7–10 days) NPs were injected through a tail vein.
Standard MTS test was performed as described elsewhere120. Briefly, 4T1 cells were seeded in 96-well plates (104 cells/well). 24 h after, serial dilutions of NP-PEG, NP-Cy5, DOX-NP-Cy5 or free doxorubicin (each point in 50 μl of 1×PBS, pH = 7.4, Gibco) were added to cells. When comparing the cytotoxicity of NP-PEG to NP-Cy5, the equal concentrations of Fe3O4 were used (Supplementary Fig. S8,c). When comparing the cytotoxicity of DOX-NP-Cy5 to free doxorubicin (DOX), the same concentrations of DOX were used (Fig. 5d). Cell culture medium with addition of 50 μl 1× PBS was used as a negative control. DMSO (25%) was added in culture medium as a positive control. Afterwards cells were incubated during 48 h at 37 °C and 5% CO2, then the medium with NPs was carefully removed, cells were washed with PBS, and 20 μl of 3-(4,5-dimethylthiazol-2-yl)-5-(3-carboxymethoxyphenyl)-2-(4-sulfophenyl)-2H-tetrazolium (MTS reagent, CellTiter 96 AQueous Non-Radioactive Cell Proliferation Assay, Promega, USA) was added to each well with 100 μl of culture medium according to manufacturer’s instructions. After 4 h of incubation at 37 °C in darkness, plates were placed on a permanent magnet for 3–5 min to remove the NPs from solution, and 100 μl of culture medium with MTS from each well were carefully replaced in new plates. The absorbance of the solution was measured at 490 nm wavelength using Thermo Scientific Multiskan GO spectrometer. Survival was calculated as percent compared to cells treated with PBS. MTS assay revealed 100% cell death after incubation with DMSO, data not shown. The absorbance of MTS-reagent in culture medium without cells was taken as zero.
ROS detection by 2′,7′-dichlorodihydrofluorescein diacetate (H2DCFDA)
Cells were seeded in 24-well plates at a concentration 105 cells ml−1 and cultured at 37 °C in a humidified incubator supplied with 5% CO2. 24 h after, NP-PEG, dispersed in 1×PBS (pH = 7.4), were added to cells for 4 h and 24 h with final concentrations 16; 49; 91; 193 and 333 µg ml−1 of cell medium in the well. Cells, incubated with addition of 1× PBS and 1 mM H2O2, were used as negative and positive controls, correspondingly. To detect ROS in cells after incubation with NPs, the culture medium was removed and HBSS (pH = 7.4, Gibco) with 2 mM L-glutamine and 10 mM HEPES was added to cells. Then unfixed cells were stained with 2 µM H2DCFDA (life technologies) for 30 min at 37 °C in a humidified incubator. After this cells were carefully washed with new portions of HBSS 3 × 5 min and investigated in the fourth portion. The obtained preparations were analysed at fluorescence microscope EVOS (life technologies), objective PlanFluor 20×/0.45, GFP channel (470/22 nm Excitation; 510/42 nm Emission).
Determination of the hemolysis
NPs hemolytic activity was assessed ex vivo, as previously described with modifications121. In brief, 0.5 ml of mouse blood was obtained by cardiac puncture and centrifuged (10 min, 900 g). Supernatants were ruled out and the red blood cells (RBC) were resuspended in PBS to remove traces of plasma. This washing step was repeated twice and then RBC were dispersed in PBS, at a concentration of 4 x 109 cells ml−1. 0.5 ml of NP-PEG in serial dilutions in 1× PBS (3–330 µg ml−1 Fe3O4) were mixed with 25 µl of RBC. The mixtures were incubated at 25 °C, under continuous agitation for the required time (10 min or 24 h) and then centrifuged (5 min, 900 g). The absorbance of the solution was measured at 540 nm wavelength, and the percentage of hemolysis was assessed by comparing with the positive (0.5 ml of distilled water) and negative (0.5 ml of 1×PBS) controls. The results were expressed as the percentage of hemolysis caused.
Dynamic of NP-Cy5 and doxorubicin accumulation in cells
4T1 cells were seeded on the coverslip glasses in Petri dishes at concentration 105 cells ml−1. After 24 h, NP-Cy5 (136 μg ml−1 Fe3O4; 8 μg ml−1 Cy5) or free Cy5 (8 μg ml−1 Cy5) dye were added to cells and incubated for 15; 30; 45 min; 1; 2; 4; 6 and 24 h. Alternatively, DOX-NP-Cy5 (63 μg·ml−1 Fe3O4; 2 μg·ml−1 Cy5; 18 μg·ml−1 (31 μM) DOX) or free DOX (31 μM) were added to cells. At required time points, cells were fixed in 4% formaldehyde (Sigma) for 15 min and imaged using EVOS (life technologies, objective PlanFluor 60×/0,75) in Cy5 channel (628/40 nm Excitation; 692/40 nm Emission). DOX accumulation was quantified by measuring its fluorescence intensity in RFP channel (531/40 nm Excitation; 593/40 nm Emission) in cells nuclei (60–70 cells/time point) in ImageJ software. Fluorescence intensity in untreated cells was taken for zero. The absence of NP-PEG (136 μg ml−1 Fe3O4) instrinsic fluorescence in Cy5/RFP/GFP channels and the absence of NP-Cy5 (136 μg ml−1 Fe3O4; 8 μg ml−1 Cy5) fluorescence in RFP/GFP channels after the identical incubation with cells were also checked (Supplementary Fig. S13). The exposure was adjusted separately for each channel and kept constant during all measurements.
4T1 cells were seeded 105 cells·ml−1 in 30 mm SPL coverglass bottom dish (Biolab, Korea) and 24 h later treated with NP-Cy5 (33 μg·ml−1 Fe3O4). Z-stacks (8 steps, 500 nm each) were captured after 30 min of co-incubation using a Nikon A1r MP inverted microscope (Nikon, Japan; oil immersion objective x60/1,49). Maximum projections along X, Y and Z-axis were made using NIS elements AR software.
Atomic emission spectrometry
For in vitro studies 4T1 cells were seeded in 75 cm2 flasks and cultivated for 24 h. Subsequently, cells were treated with NP-PEG in 1×PBS (final concentration 100 μg·ml−1 Fe3O4, and 15 μg·ml−1 Au) and incubated for 48 h at 37 °C and 5% CO2. After three PBS washing steps, cells were detached with TrypLE (Gibco), resuspended in culture medium and counted. Untreated cells were used as control. Later, cells were dissolved in aqua regia, and the concentrations of Fe and Au were measured by microwave coupled plasma-atomic emission spectrometry (Agilent 4200 MP-AES, USA) using the calibration curve for the standard samples in 0.1–1 mg·ml−1 concentration range.
For in vivo studies 24 h after NPs i.v. injection (6.6 mg kg−1 Fe3O4, 1 mg kg−1 Au) mice (n = 3) were sacrificed after injection by cardiac perfusion with 30 mL PBS under anesthesia, and the liver, spleen, kidney, lung, heart and tumor were collected. The organs were weighed and digested in aqua regia during 24 h. Quantification of the iron and gold concentration was carried out by atomic emission spectrometry as described above. Untreated animals were used as control (n = 3) for measuring endogenous gold and iron levels. Mean gold and iron levels in control organs were subtracted from corresponding gold/iron levels in NPs-treated group to get NPs-associated gold/iron concentration (µg/g tissue). NPs delivery efficiency calculations were based on iron/gold concentration in the tumor tissues, tumor mass and injected dose.
Mice were anesthetized by intraperitoneal injection of 200 mg kg−1 ketamine (Moscow Endocrine Plant, Russia) and 10 mg kg−1 xylazine (Nita-Farm, Russia) and the tail vein was cannulated with polyethylene tubing (0.28 × 0.60 mm, InStech Laboratories, Inc., Plymouth Meeting PA, USA) for delivering fluorescently labeled antibodies (5–10 μg) and maintaining the anaesthetics. Body temperature was maintained using a heated stage. NP-Cy5 or NRed-NP-Cy5 (3 mg kg−1 Fe3O4) were injected through a tail vein. Skin and tumor preparations were made as described122. Briefly, a midline incision along the spine was made and the skin reflected. The thin connective tissue membrane overlaying the inside surface of the skin was removed and edges of this skin flap were secured using sutures to expose and stabilize the tumor/vessels for imaging. Intravital imaging was performed using a Nikon A1r MP inverted microscope (Nikon, Japan). For kinetic studies fluorescence intensity was measured in intravascular and interstitial ROI using NIS-Elements AR software (Nikon, Japan).
In vivo fluorescent imaging
Animals with both flanks grafted 4T1-tumors (n = 3) were anesthetized with isoflurane and imaged using IVIS Spectrum CT (Perkin Elmer) on 640/680 nm excitation/emission wavelengths before and 1–24 h after NP i.v. injection (6.6 mg kg−1 Fe3O4). For autofluorescense correction spectral unmixing protocol was applied. Average fluorescence intensities were measured in selected ROI in Living Image 4.3 (Perkin Elmer) and tumor/liver ratios were calculated.
In vitro and in vivo MRI
For in vitro studies the T2 relaxation rate of water protons in the presence of NP-PEG was measured in 500 μl test tubes at 18 °С in a ClinScan 7 T MRI system (Bruker BioSpin). Image acquisition was performed in the Spin Echo mode with following parameters: MRI system TR = 10 s, TE = 16, 24, …, 256 ms, flip angle = 180°, resolution 640 × 448 pixel, field of view 120 × 82.5 mm2. Signal intensities from regions of interest were determined using ImageJ and the T2 relaxation time was calculated by linear fitting as function of TE. The T2 relaxivity values were calculated from linear fitting of T2−1 relaxation times as function of Fe concentration. The slopes represent the R2 values for NP-PEG in water and 4T1 cell culture used for MR imaging. Cells were incubated with NP-PEG (100 μg·ml−1 Fe3O4, 15 μg·ml−1 Au) during 48 h. Cells, cultivated in free medium, were used as control. Non-bound NPs were removed by cell washing with PBS as described above for AES sample preparation. Cells with attached NPs were suspended in 2% agarose gel.
For in vivo studies, images were obtained using a 20-cm volumetric coil as a transmitter and a 4-segment surface coil as a receiver of the RF signal. BALB/c mice with both flanks grafted 4T1-tumors (n = 3) and C57/bl6 mice with right flanks grafted B16-F10 tumors (n = 2) were anesthetized with isoflurane and scanned before and 0.5–24 h after NPs i.v. injection (6.6 mg kg−1 Fe3O4) using the following settings: 1) fat-suppressed T2-weighted turbo spin–echo (TSE) images were made in transversal planes (TR = 3000 ms, TE = 38 ms, FOV = 21 × 30 mm, base resolution (136 × 192); 2) T2* weighted gradient echo (GRE) images were made in transversal planes (TR = 400 ms, TE = 10 ms, FOV = 27 × 35 mm, base resolution (200 × 256). Images were processed in RadiAnt DICOM Viewer.
Plotting and calculation of the standard deviation (SD) and standard error of mean (SEM) values were made using Origin 8.0 and Prism 6 – GraphPad software. Data were analysed using the Analysis of Variance (ANOVA) test. P values < 0.05 were considered significant.
The data supporting the plots and other findings of this study are available from the corresponding authors upon reasonable request.
Ferrari, M. Cancer nanotechnology: Opportunities and challenges. Nature Reviews Cancer 5, 161–171, https://doi.org/10.1038/nrc1566 (2005).
Cho, K. J., Wang, X., Nie, S. M., Chen, Z. & Shin, D. M. Therapeutic nanoparticles for drug delivery in cancer. Clinical Cancer Research 14, 1310–1316, https://doi.org/10.1158/1078-0432.ccr-07-1441 (2008).
Ma, Y. F., Huang, J., Song, S. J., Chen, H. B. & Zhang, Z. J. Cancer-Targeted Nanotheranostics: Recent Advances and Perspectives. Small 12, 4936–4954, https://doi.org/10.1002/smll.201600635 (2016).
Peer, D. et al. Nanocarriers as an emerging platform for cancer therapy. Nature Nanotechnology 2, 751–760, https://doi.org/10.1038/nnano.2007.387 (2007).
Sanna, V., Pala, N. & Sechi, M. Targeted therapy using nanotechnology: focus on cancer. International Journal of Nanomedicine 9, 467–483, https://doi.org/10.2147/ijn.s36654 (2014).
Chen, G. Y., Roy, I., Yang, C. H. & Prasad, P. N. Nanochemistry and Nanomedicine for Nanoparticle-based Diagnostics and Therapy. Chemical Reviews 116, 2826–2885, https://doi.org/10.1021/acs.chemrev.5b00148 (2016).
Golovin, Y. I., Klyachko, N. L., Majouga, A. G., Sokolsky, M. & Kabanov, A. V. Theranostic multimodal potential of magnetic nanoparticles actuated by non-heating low frequency magnetic field in the new-generation nanomedicine. Journal of Nanoparticle Research 19, https://doi.org/10.1007/s11051-017-3746-5 (2017).
Sumer, B. & Gao, J. M. Theranostic nanomedicine for cancer. Nanomedicine 3, 137–140, https://doi.org/10.2217/174358126.96.36.199 (2008).
Cardoso, V. F. et al. Advances in Magnetic Nanoparticles for Biomedical Applications. Advanced Healthcare Materials 7, https://doi.org/10.1002/adhm.201700845 (2018).
Fang, S. et al. Dual-Stimuli Responsive Nanotheranostics for Multimodal Imaging Guided Trimodal Synergistic Therapy. Small 13, 1602580–n/a, https://doi.org/10.1002/smll.201602580 (2017).
Lee, D. E. et al. Multifunctional nanoparticles for multimodal imaging and theragnosis. Chemical Society Reviews 41, 2656–2672, https://doi.org/10.1039/c2cs15261d (2012).
Hung, C. C. et al. Active Tumor Permeation and Uptake of Surface Charge-Switchable Theranostic Nanoparticles for Imaging-Guided Photothermal/Chemo Combinatorial Therapy (vol 6, pg 302, 2016). Theranostics 7, 559–560, https://doi.org/10.7150/thno.18728 (2017).
Lammers, T., Aime, S., Hennink, W. E., Storm, G. & Kiessling, F. Theranostic Nanomedicine. Accounts of Chemical Research 44, 1029–1038, https://doi.org/10.1021/ar200019c (2011).
De Crozals, G., Bonnet, R., Farre, C. & Chaix, C. Nanoparticles with multiple properties for biomedical applications: A strategic guide. Nano Today 11, 435–463, https://doi.org/10.1016/j.nantod.2016.07.002 (2016).
Pelaz, B. et al. Diverse Applications of Nanomedicine. Acs Nano 11, 2313–2381, https://doi.org/10.1021/acsnano.6b06040 (2017).
Gao, N. et al. Tumor Penetrating Theranostic Nanoparticles for Enhancement of Targeted and Image-guided Drug Delivery into Peritoneal Tumors following Intraperitoneal Delivery. Theranostics 7, 1689–1704, https://doi.org/10.7150/thno.18125 (2017).
Overchuk, M. & Zheng, G. Overcoming obstacles in the tumor microenvironment: Recent advancements in nanoparticle delivery for cancer theranostics. Biomaterials 156, 217–237, https://doi.org/10.1016/j.biomaterials.2017.10.024 (2018).
Blanco, E., Shen, H. & Ferrari, M. Principles of nanoparticle design for overcoming biological barriers to drug delivery. Nat Biotech 33, 941–951, https://doi.org/10.1038/nbt.3330 (2015).
Ni, D. L., Bu, W. B., Ehlerding, E. B., Cai, W. B. & Shi, J. L. Engineering of inorganic nanoparticles as magnetic resonance imaging contrast agents. Chemical Society Reviews 46, 7438–7468, https://doi.org/10.1039/c7cs00316a (2017).
Kim, S. L. I. C. K. K. In Nanoplatform‐Based Molecular Imaging (ed. Xiaoyuan Chen) Ch. 22, 541–563 (John Wiley & Sons, Inc., 2011).
Gobbo, O. L., Sjaastad, K., Radomski, M. W., Volkov, Y. & Prina-Mello, A. Magnetic Nanoparticles in Cancer Theranostics. Theranostics 5, 1249–1263, https://doi.org/10.7150/thno.11544 (2015).
Mosayebi, J., Kiyasatfar, M. & Laurent, S. Synthesis, Functionalization, and Design of Magnetic Nanoparticles for Theranostic Applications. Advanced Healthcare Materials 6, https://doi.org/10.1002/adhm.201700306 (2017).
Cristina Tudisco, M. T. C., Guglielmo G. Condorelli. In Biomedical Applications of Functionalized Nanomaterials: Concepts, Development and Clinical Translation Ch. 12, 335–370 (2018).
Miller, M. A. et al. Predicting therapeutic nanomedicine efficacy using a companion magnetic resonance imaging nanoparticle. Science Translational Medicine 7, https://doi.org/10.1126/scitranslmed.aac6522 (2015).
Ramanathan, R. K. et al. Correlation between Ferumoxytol Uptake in Tumor Lesions by MRI and Response to Nanoliposomal Irinotecan in Patients with Advanced Solid Tumors: A Pilot Study. Clinical cancer research: an official journal of the American Association for Cancer Research, https://doi.org/10.1158/1078-0432.ccr-16-1990 (2017).
Jiang, W., Huang, Y., An, Y. & Kim, B. Y. S. Remodeling Tumor Vasculature to Enhance Delivery of Intermediate-Sized Nanoparticles. Acs Nano 9, 8689–8696, https://doi.org/10.1021/acsnano.5b02028 (2015).
Liang, X. et al. Intravital Multiphoton Imaging of the Selective Uptake of Water-Dispersible Quantum Dots into Sinusoidal Liver Cells. Small 11, 1711–1720, https://doi.org/10.1002/smll.201402698 (2015).
Miller, M. A. & Weissleder, R. Imaging the pharmacology of nanomaterials by intravital microscopy: Toward understanding their biological behavior. Advanced drug delivery reviews, https://doi.org/10.1016/j.addr.2016.05.023 (2016).
Biju, S. et al. Multifunctional beta-NaGdF4:Ln(3+) (Ln = Yb, Er, Dy) nanoparticles with NIR to visible upconversion and high transverse relaxivity: a potential bimodal contrast agent for high-field MRI and optical imaging. Rsc Advances 6, 61443–61448, https://doi.org/10.1039/c6ra09450c (2016).
Cha, E. J. et al. Development of MRI/NIRF ‘activatable’ multimodal imaging probe based on iron oxide nanoparticles. Journal of Controlled Release 155, 152–158, https://doi.org/10.1016/j.jconrel.2011.07.019 (2011).
Sheng, Y., Li, S., Duan, Z. Q., Zhang, R. & Xue, J. M. Fluorescent magnetic nanoparticles as minimally-invasive multi-functional theranostic platform for fluorescence imaging, MRI and magnetic hyperthermia. Materials Chemistry and Physics 204, 388–396, https://doi.org/10.1016/j.matchemphys.2017.10.076 (2018).
Massner, C. et al. Genetically Controlled Lysosomal Entrapment of Superparamagnetic Ferritin for Multimodal and Multiscale Imaging and Actuation with Low Tissue Attenuation. Advanced Functional Materials, 1706793, https://doi.org/10.1002/adfm.201706793 (2018).
Krishnan, K. M. Fundamentals and Applications of Magnetic Materials. (Oxford University Press, 2016).
Thanh, N. T. Clinical Applications of Magnetic Nanoparticles. (CRC Press, 2018).
Yoo, D., Lee, J. H., Shin, T. H. & Cheon, J. Theranostic Magnetic Nanoparticles. Accounts of Chemical Research 44, 863–874, https://doi.org/10.1021/ar200085c (2011).
Zhu, L., Zhou, Z. Y., Mao, H. & Yang, L. L. Magnetic nanoparticles for precision oncology: theranostic magnetic iron oxide nanoparticles for image-guided and targeted cancer therapy. Nanomedicine 12, 73–87, https://doi.org/10.2217/nnm-2016-0316 (2017).
Huang, J., Zhong, X. D., Wang, L. Y., Yang, L. L. & Mao, H. Improving the Magnetic Resonance Imaging Contrast and Detection Methods with Engineered Magnetic Nanoparticles. Theranostics 2, 86–102, https://doi.org/10.7150/thno.4006 (2012).
Revia, R. A. & Zhang, M. Q. Magnetite nanoparticles for cancer diagnosis, treatment, and treatment monitoring: recent advances. Materials Today 19, 157–168, https://doi.org/10.1016/j.mattod.2015.08.022 (2016).
Huang, H. Y. & Lovell, J. F. Advanced Functional Nanomaterials for Theranostics. Advanced Functional Materials 27, https://doi.org/10.1002/adfm.201603524 (2017).
Pankhurst, D. O. A. Q. A. In Nanoscience: Nanostructures through Chemistry Vol. 1 (ed P. O’Brien) 60–88 (Royal Society of Chemistry, 2013).
Nan, X. Y. et al. Dual-Targeted Multifunctional Nanoparticles for Magnetic Resonance Imaging Guided Cancer Diagnosis and Therapy. Acs Applied Materials & Interfaces 9, 9986–9995, https://doi.org/10.1021/acsami.6b16486 (2017).
Zhang, R. X. et al. Design of nanocarriers for nanoscale drug delivery to enhance cancer treatment using hybrid polymer and lipid building blocks. Nanoscale 9, 1334–1355, https://doi.org/10.1039/c6nr08486a (2017).
Yu, M. K., Park, J. & Jon, S. Targeting Strategies for Multifunctional Nanoparticles in Cancer Imaging and Therapy. Theranostics 2, 3–44, https://doi.org/10.7150/thno.3463 (2012).
Angelakeris, M. Magnetic nanoparticles: A multifunctional vehicle for modern theranostics. Biochimica Et Biophysica Acta-General Subjects 1861, 1642–1651, https://doi.org/10.1016/j.bbagen.2017.02.022 (2017).
Wang, H. et al. Magnetic/NIR-responsive drug carrier, multicolor cell imaging, and enhanced photothermal therapy of gold capped magnetite-fluorescent carbon hybrid nanoparticles. Nanoscale 7, 7885–7895, https://doi.org/10.1039/c4nr07335e (2015).
Sanavio, B. & Stellacci, F. Recent Advances in the Synthesis and Applications of Multimodal Gold-Iron Nanoparticles. Current Medicinal Chemistry 24, 497–511, https://doi.org/10.2174/0929867323666160829111531 (2017).
Kim, D.-H. et al. Biofunctionalized magnetic-vortex microdiscs for targeted cancer-cell destruction. Nat Mater 9, 165–171, https://doi.org/10.1038/nmat2591 (2010).
Li, L. L. et al. Microenvironment-Driven Bioelimination of Magnetoplasmonic Nanoassemblies and Their Multimodal Imaging-Guided Tumor Photothermal Therapy. ACS Nano 10, 7094–7105, https://doi.org/10.1021/acsnano.6b03238 (2016).
Cao-Milán, R. & Liz-Marzán, L. M. Gold nanoparticle conjugates: recent advances toward clinical applications. Expert Opinion on Drug Delivery 11, 741–752, https://doi.org/10.1517/17425247.2014.891582 (2014).
Giljohann, D. A. et al. Gold Nanoparticles for Biology and Medicine. Angewandte Chemie International Edition 49, 3280–3294, https://doi.org/10.1002/anie.200904359 (2010).
Myrovali, E. et al. Arrangement at the nanoscale: Effect on magnetic particle hyperthermia. Scientific Reports 6, https://doi.org/10.1038/srep37934 (2016).
Liebana Vinas, S. et al. Tuning the magnetism of ferrite nanoparticlese. Journal of Magnetism and Magnetic Materials 415, 20–23, https://doi.org/10.1016/j.jmmm.2016.02.098 (2016).
Klyachko, N. L. et al. Changing the Enzyme Reaction Rate in Magnetic Nanosuspensions by a Non-Heating Magnetic Field. Angewandte Chemie-International Edition 51, 12016–12019, https://doi.org/10.1002/anie.201205905 (2012).
Golovin, Y. I. et al. Towards nanomedicines of the future: Remote magneto-mechanical actuation of nanomedicines by alternating magnetic fields. Journal of Controlled Release 219, 43–60, https://doi.org/10.1016/j.jconrel.2015.09.038 (2015).
Hayashi, K. et al. Superparamagnetic Nanoparticle Clusters for Cancer Theranostics Combining Magnetic Resonance Imaging and Hyperthermia Treatment. Theranostics 3, 366–376, https://doi.org/10.7150/thno.5860 (2013).
Liebana-Vinas, S. et al. Optimum nanoscale design in ferrite based nanoparticles for magnetic particle hyperthermia. Rsc Advances 6, 72918–72925, https://doi.org/10.1039/c6ra17892h (2016).
Efremova, M. V. et al. In situ Observation of Chymotrypsin Catalytic Activity Change Actuated by Non-Heating Low-Frequency Magnetic Field. ACS Nano. https://doi.org/10.1021/acsnano.7b06439 (2018).
Steichen, S. D., Caldorera-Moore, M. & Peppas, N. A. A review of current nanoparticle and targeting moieties for the delivery of cancer therapeutics. European Journal of Pharmaceutical Sciences 48, 416–427, https://doi.org/10.1016/j.ejps.2012.12.006 (2013).
Semkina, A. et al. Core-shell-corona doxorubicin-loaded superparamagnetic Fe3O4 nanoparticles for cancer theranostics. Colloids and Surfaces B-Biointerfaces 136, 1073–1080, https://doi.org/10.1016/j.colsurfb.2015.11.009 (2015).
Xu, C. J. & Sun, S. H. New forms of superparamagnetic nanoparticles for biomedical applications. Advanced Drug Delivery Reviews 65, 732–743, https://doi.org/10.1016/j.addr.2012.10.008 (2013).
Liu, Y. J. et al. Magneto-Plasmonic Janus Vesicles for Magnetic Field-Enhanced Photoacoustic and Magnetic Resonance Imaging of Tumors. Angewandte Chemie-International Edition 55, 15297–15300, https://doi.org/10.1002/anie.201608338 (2016).
Zhao, C. Q. et al. Biosynthesized Gold Nanoclusters and Iron Complexes as Scaffolds for Multimodal Cancer Bioimaging. Small 12, 6255–6265, https://doi.org/10.1002/smll.201602526 (2016).
Stafford, S., Garcia, R. S. & Gun’ko, Y. K. Multimodal Magnetic-Plasmonic Nanoparticles for Biomedical Applications. Applied Sciences-Basel 8, https://doi.org/10.3390/app8010097 (2018).
Belyanina, I. V. et al. In Vivo Cancer Cells Elimination Guided by Aptamer-Functionalized Gold-Coated Magnetic Nanoparticles and Controlled with Low Frequency Alternating Magnetic Field. Theranostics 7, 3326–3337, https://doi.org/10.7150/thno.17089 (2017).
Majouga, A. et al. Enzyme-functionalized gold-coated magnetite nanoparticles as novel hybrid nanomaterials: Synthesis, purification and control of enzyme function by low-frequency magnetic field. Colloids and Surfaces B-Biointerfaces 125, 104–109, https://doi.org/10.1016/j.colsurfb.2014.11.012 (2015).
Xu, C. J., Wang, B. D. & Sun, S. H. Dumbbell-like Au-Fe3O4 Nanoparticles for Target-Specific Platin Delivery. Journal of the American Chemical Society 131, 4216-+, https://doi.org/10.1021/ja900790v (2009).
Leung, K. C. F. et al. Gold and iron oxide hybrid nanocomposite materials. Chemical Society Reviews 41, 1911–1928, https://doi.org/10.1039/c1cs15213k (2012).
Rajkumar, S. & Prabaharan, M. Theranostics Based on Iron Oxide and Gold Nanoparticles for Imaging-Guided Photothermal and Photodynamic Therapy of Cancer. Current Topics in Medicinal Chemistry 17, 1858–1871, https://doi.org/10.2174/1568026617666161122120537 (2017).
Tomitaka, A. et al. Development of magneto-plasmonic nanoparticles for multimodal image-guided therapy to the brain. Nanoscale 9, 764–773, https://doi.org/10.1039/C6NR07520G (2017).
Cai, H. et al. Dendrimer-Assisted Formation of Fe3O4/Au Nanocomposite Particles for Targeted Dual Mode CT/MR Imaging of Tumors. Small 11, 4584–4593, https://doi.org/10.1002/smll.201500856 (2015).
Kim, D. et al. Amphiphilic polymer-coated hybrid nanoparticles as CT/MRI dual contrast agents. Nanotechnology 22, https://doi.org/10.1088/0957-4484/22/15/155101 (2011).
Kharisov, B. I. et al. Solubilization, dispersion and stabilization of magnetic nanoparticles in water and non-aqueous solvents: recent trends. RSC Advances 4, 45354–45381, https://doi.org/10.1039/C4RA06902A (2014).
Qin, J. et al. A high-performance magnetic resonance imaging T-2 contrast agent. Advanced Materials 19, 1874-+, https://doi.org/10.1002/adma.200602326 (2007).
Choi, D. et al. Fabrication of MnxFe1-xO Colloidal Solid Solution as a Dual Magnetic-Resonance-Contrast Agent. Small 5, 571–573, https://doi.org/10.1002/smll.200801258 (2009).
Liu, X. O., Atwater, M., Wang, J. H. & Huo, Q. Extinction coefficient of gold nanoparticles with different sizes and different capping ligands. Colloids and Surfaces B-Biointerfaces 58, 3–7, https://doi.org/10.1016/j.colsurfb.2006.08.005 (2007).
Yu, H. et al. Dumbbell-like bifunctional Au-Fe3O4 nanoparticles. Nano Letters 5, 379–382, https://doi.org/10.1021/nl047955q (2005).
Wei, Y. H., Klajn, R., Pinchuk, A. O. & Grzybowski, B. A. Synthesis, Shape Control, and Optical Properties of Hybrid Au/Fe3O4 “Nanoflowers”. Small 4, 1635–1639, https://doi.org/10.1002/smll.200800511 (2008).
David, B. et al. Atmospheric-pressure Microwave Torch Discharge Generated γ-Fe2O3 Nanopowder. Physics Procedia 44, 206–212, https://doi.org/10.1016/j.phpro.2013.04.025 (2013).
Sorenson, T. A., Morton, S. A., Waddill, G. D. & Switzer, J. A. Epitaxial electrodeposition of Fe3O4 thin films on the low-index planes of gold. Journal of the American Chemical Society 124, 7604–7609, https://doi.org/10.1021/ja0201101 (2002).
Liu, S., Guo, S. J., Sun, S. & You, X. Z. Dumbbell-like Au-Fe3O4 nanoparticles: a new nanostructure for supercapacitors. Nanoscale 7, 4890–4893, https://doi.org/10.1039/c5nr00135h (2015).
Zhai, Y. M., Jin, L. H., Wang, P. & Dong, S. J. Dual-functional Au-Fe3O4 dumbbell nanoparticles for sensitive and selective turn-on fluorescent detection of cyanide based on the inner filter effect. Chemical Communications 47, 8268–8270, https://doi.org/10.1039/c1cc13149d (2011).
Schick, I. et al. Inorganic Janus particles for biomedical applications. Beilstein Journal of Nanotechnology 5, 2346–2362, https://doi.org/10.3762/bjnano.5.244 (2014).
Nguyen, T. D. Portraits of colloidal hybrid nanostructures: Controlled synthesis and potential applications. Colloids and Surfaces B-Biointerfaces 103, 326–344, https://doi.org/10.1016/j.colsurfb.2012.10.049 (2013).
Topfer, J. & Angermann, A. Nanocrystalline magnetite and Mn-Zn ferrite particles via the polyol process: Synthesis and magnetic properties. Materials Chemistry and Physics 129, 337–342, https://doi.org/10.1016/j.matchemphys.2011.04.025 (2011).
Wang, J., Peng, Z. M., Huang, Y. J. & Chen, Q. W. Growth of magnetite nanorods along its easy-magnetization axis of 110. Journal of Crystal Growth 263, 616–619, https://doi.org/10.1016/j.jcrysgro.2003.11.012 (2004).
Sharrock, M. P. Time-Dependence oF Switching Fields in Magnetic Recording Media (Invited). Journal of Applied Physics 76, 6413–6418, https://doi.org/10.1063/1.358282 (1994).
Kuerbanjiang, B. et al. Exchange bias of Ni nanoparticles embedded in an antiferromagnetic IrMn matrix. Nanotechnology 24, https://doi.org/10.1088/0957-4484/24/45/455702 (2013).
Franken, L. et al. Splenic red pulp macrophages are intrinsically superparamagnetic and contaminate magnetic cell isolates. Scientific Reports 5, https://doi.org/10.1038/srep12940 (2015).
Aragon, R. Magnetization and Exchange in Nonstoichiometric Magnetite. Physical Review B 46, 5328–5333, https://doi.org/10.1103/PhysRevB.46.5328 (1992).
Verwey, E. J. W. Electronic conduction of magnetite (Fe3O4) and its transition point at low temperatures. Nature 144, 327–328, https://doi.org/10.1038/144327b0 (1939).
Brollo, M. E. F. et al. Compact Ag@Fe3O4 Core-shell Nanoparticles by Means of Single-step Thermal Decomposition Reaction. Scientific Reports 4, https://doi.org/10.1038/srep06839 (2014).
Nicolas, J., Mura, S., Brambilla, D., Mackiewicz, N. & Couvreur, P. Design, functionalization strategies and biomedical applications of targeted biodegradable/biocompatible polymer-based nanocarriers for drug delivery. Chemical Society Reviews 42, 1147–1235, https://doi.org/10.1039/c2cs35265f (2013).
Nel, A., Xia, T., Madler, L. & Li, N. Toxic potential of materials at the nanolevel. Science 311, 622–627, https://doi.org/10.1126/science.1114397 (2006).
Li, N., Xia, T. & Nel, A. E. The role of oxidative stress in ambient particulate matter-induced lung diseases and its implications in the toxicity of engineered nanoparticles. Free Radical Biology and Medicine 44, 1689–1699, https://doi.org/10.1016/j.freeradbiomed.2008.01.028 (2008).
Patil, U. S. et al. In Vitro/In Vivo Toxicity Evaluation and Quantification of Iron Oxide Nanoparticles. International Journal of Molecular Sciences 16, 24417–24450, https://doi.org/10.3390/ijms161024417 (2015).
Oh, N. & Park, J. H. Endocytosis and exocytosis of nanoparticles in mammalian cells. International Journal of Nanomedicine 9, 51–63, https://doi.org/10.2147/ijn.s26592 (2014).
Nguyen, D. H., Bae, J. W., Choi, J. H., Lee, J. S. & Park, K. D. Bioreducible cross-linked Pluronic micelles: pH-triggered release of doxorubicin and folate-mediated cellular uptake. Journal of Bioactive and Compatible Polymers 28, 341–354, https://doi.org/10.1177/0883911513491642 (2013).
Nizamov, T. R. et al. Effect of Iron Oxide Nanoparticle Shape on Doxorubicin Drug Delivery Toward LNCaP and PC-3 Cell Lines. BioNanoScience, https://doi.org/10.1007/s12668-018-0502-y (2018).
Speelmans, G., Staffhorst, R., Steenbergen, H. G. & deKruijff, B. Transport of the anti-cancer drug doxorubicin across cytoplasmic membranes and membranes composed of phospholipids derived from Escherichia coli occurs via a similar mechanism. Biochimica Et Biophysica Acta-Biomembranes 1284, 240–246, https://doi.org/10.1016/s0005-2736(96)00137-x (1996).
Kou, L., Sun, J., Zhai, Y. & He, Z. The endocytosis and intracellular fate of nanomedicines: Implication for rational design. Asian Journal of Pharmaceutical Sciences 8, 1–10, https://doi.org/10.1016/j.ajps.2013.07.001 (2013).
Mindell, J. A. In Annual Review of Physiology, Vol 74 (eds D. Julius & D. E. Clapham) 69–86 (2012).
Wilhelm, S. et al. Analysis of nanoparticle delivery to tumours. Nature Reviews Materials 1, https://doi.org/10.1038/natrevmats.2016.14 (2016).
Walkey, C. D. & Chan, W. C. W. Understanding and controlling the interaction of nanomaterials with proteins in a physiological environment. Chemical Society Reviews 41, 2780–2799, https://doi.org/10.1039/c1cs15233e (2012).
Walkey, C. D., Olsen, J. B., Guo, H. B. & Emili, A. & Chan, W. C. W. Nanoparticle Size and Surface Chemistry Determine Serum Protein Adsorption and Macrophage Uptake. Journal of the American Chemical Society 134, 2139–2147, https://doi.org/10.1021/ja2084338 (2012).
Nakamura, Y., Mochida, A., Choyke, P. L. & Kobayashi, H. Nanodrug Delivery: Is the Enhanced Permeability and Retention Effect Sufficient for Curing Cancer? Bioconjugate Chemistry 27, 2225–2238, https://doi.org/10.1021/acs.bioconjchem.6b00437 (2016).
Miller, M. A. et al. Tumour-associated macrophages act as a slow-release reservoir of nano-therapeutic Pt(IV) pro-drug. Nature Communications 6, https://doi.org/10.1038/ncomms9692 (2015).
Bouchaala, R. et al. Light-triggered release from dye-loaded fluorescent lipid nanocarriers in vitro and in vivo. Colloids Surf B Biointerfaces 156, 414–421 (2017).
Darwich, Z., Klymchenko, A. S., Dujardin, D. & Mely, Y. Imaging lipid order changes in endosome membranes of live cells by using a Nile Red-based membrane probe. Rsc Advances 4, 8481–8488, https://doi.org/10.1039/c3ra47181k (2014).
Machulkin, A. E. et al. Nanohybride Materials Based on Magnetite-Gold Nanoparticles for Diagnostics of Prostate Cancer: Synthesis and In Vitro Testing. Bulletin of Experimental Biology and Medicine 161, 706–710, https://doi.org/10.1007/s10517-016-3490-3 (2016).
Machulkin, A. E. et al. Small-molecule PSMA ligands. Current state, SAR and perspectives. Journal of Drug Targeting 24, 679–693, https://doi.org/10.3109/1061186x.2016.1154564 (2016).
Xu, C. et al. Au-Fe3O4 dumbbell nanoparticles as dual-functional probes. Angewandte Chemie-International Edition 47, 173–176, https://doi.org/10.1002/anie.200704392 (2008).
Smolensky, E. D. et al. Scaling laws at the nanosize: the effect of particle size and shape on the magnetism and relaxivity of iron oxide nanoparticle contrast agents. Journal of Materials Chemistry B 1, 2818–2828, https://doi.org/10.1039/c3tb00369h (2013).
Liu, J. et al. A multifunctional nanoprobe based on Au-Fe3O4 nanoparticles for multimodal and ultrasensitive detection of cancer cells. Chemical Communications 49, 4938–4940, https://doi.org/10.1039/c3cc41984c (2013).
Reguera, J. et al. Janus plasmonic-magnetic gold-iron oxide nanoparticles as contrast agents for multimodal imaging. Nanoscale 9, 9467–9480, https://doi.org/10.1039/c7nr01406f (2017).
Lee, N. et al. Water-Dispersible Ferrimagnetic Iron Oxide Nanocubes with Extremely High r(2) Relaxivity for Highly Sensitive in Vivo MRI of Tumors. Nano Letters 12, 3127–3131, https://doi.org/10.1021/nl3010308 (2012).
Pankhurst, Q. A., Connolly, J., Jones, S. K. & Dobson, J. Applications of magnetic nanoparticles in biomedicine. Journal of Physics D-Applied Physics 36, R167–R181, https://doi.org/10.1088/0022-3727/36/13/201 (2003).
Zhao, Z. H. et al. Octapod iron oxide nanoparticles as high-performance T-2 contrast agents for magnetic resonance imaging. Nature Communications 4, https://doi.org/10.1038/ncomms3266 (2013).
Li, L. et al. Superparamagnetic Iron Oxide Nanoparticles as MRI contrast agents for Non-invasive Stem Cell Labeling and Tracking. Theranostics 3, 595–615, https://doi.org/10.7150/thno.5366 (2013).
Jin, Y. D., Jia, C. X., Huang, S. W., O’Donnell, M. & Gao, X. H. Multifunctional nanoparticles as coupled contrast agents. Nature Communications 1, https://doi.org/10.1038/ncomms1042 (2010).
Heinemann, L. et al. Synergistic effects of oncolytic reovirus and docetaxel chemotherapy in prostate cancer. Bmc Cancer 11, https://doi.org/10.1186/1471-2407-11-221 (2011).
Fornaguera, C. et al. Interactions of PLGA nanoparticles with blood components: protein adsorption, coagulation, activation of the complement system and hemolysis studies. Nanoscale 7, 6045–6058, https://doi.org/10.1039/c5nr00733j (2015).
Naumenko, V., Jenne, C. & Mahoney, D. J. Intravital Microscopy for Imaging the Tumor Microenvironment in Live Mice. Methods in molecular biology (Clifton, N.J.) 1458, 217–230, 10.1007/978-1-4939-3801-8_16 (2016).
We thank Astrid M. Westendorf for fruitful discussions. The authors gratefully acknowledge the financial support of the Ministry of Education and Science of the Russian Federation in the framework of Increase Competitiveness Program of NUST «MISiS» No. K2-2016-069 (synthesis of nanomaterials). U.W. gratefully acknowledges the financial support of the Ministry of Education and Science of the Russian Federation in the framework of Increase Competitiveness Program of NUST «MISiS» № K3-2017-022 (magnetic measurements). V.A.N. gratefully acknowledges the financial support of the Ministry of Education and Science of the Russian Federation in the framework of Increase Competitiveness Program of NUST «MISiS» (№ K4-2017-046), implemented by a governmental decree dated 16th of March 2013, N 211 (intravital microscopy). The reported study was funded by Russian Foundation for Basic Research (RFBR) according to the research project № 18-33-01232 (fluorescent labeling of nanoparticles). The authors also acknowledge financial support of Russian Science Foundation № 17-14-01316 (biological study) and Lomonosov Moscow State University Development Program PNR 5.13 (electron microscopy). MRI measurements were carried out by ClinScan 7 T (Bruker Biospin) located at CKP «Medical Nanobiotechnology». We acknowledge support by the Open Access Publication Fund of the University of Duisburg-Essen.
The authors declare no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Efremova, M.V., Naumenko, V.A., Spasova, M. et al. Magnetite-Gold nanohybrids as ideal all-in-one platforms for theranostics. Sci Rep 8, 11295 (2018). https://doi.org/10.1038/s41598-018-29618-w
This article is cited by
Structure and Magnetic Properties of Nanoparticles of Magnetite Obtained by Mechanochemical Synthesis
Metal Science and Heat Treatment (2021)
Liposomal nanotheranostics for multimode targeted in vivo bioimaging and near‐infrared light mediated cancer therapy
Communications Biology (2020)
Topics in Current Chemistry (2020)
Synthesis, Characterization, and Cytotoxicity of Fe3O4@Ag Hybrid Nanoparticles: Promising Applications in Cancer Treatment
Journal of Cluster Science (2020)
Nano Research (2020)