Abstract
We report on synthesis and investigation of nanocrystalline cobaltironpyrites with an emphasis on nanocrystal structure, morphology and magnetic behavior. The nanocrystals (NCs) were 5–25 nm in diameter as characterized using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). With an increase in Fe fraction, Xray diffraction and smallangleXray scattering (SAXS) showed a systematic decrease in lattice constant, primary grain/NC size (15 to 7 nm), and nanoparticle (NP) size (70 to 20 nm), respectively. The temperature dependence of the DC magnetization and AC susceptibility versus frequency revealed a number of magnetic phases in Co_{ x }Fe_{1−x}S_{2}. Samples with x = 1 and x = 0.875–0.625 showed evidence of superspin glass (SSG) behavior with embedded ferromagnetic (FM) clusters of NPs. For x = 0.5, samples retained their mixed phases, but showed superparamagnetic (SPM) behavior with antiferromagnetic clusters suppressing magnetic dipolar interactions. Below x = 0.5, the pyrites show increasing paramagnetic character. We construct a phase diagram, which can be understood in terms of competition between the various dipolar, exchange, inter and intracluster interactions. Our results suggest that NC size and shape can be tuned to engineer spinpolarized ferromagnetism of ndoped iron pyrite.
Introduction
3d transition metal chalcogenides, in particular metal disulfides such as the pyrites (cubic MS_{2}, with M = Mn, Fe, Co, Ni, Cu, Zn, Ru), are of great interest due to their multiple functional electronic and magnetic properties. Iron pyrite (FeS_{2}) is a diamagnetic semiconductor (with a band gap of 0.95 eV) of interest for photovoltaics^{1}. CoS_{2} is a metallic itinerant ferromagnet with a transition temperature T_{ C } = 120 K^{2,3}.
The solid solution Co_{ x }Fe_{1−x}S_{2} forms a solid solution over the entire compositional range (0 ≤ x ≤ 1). In the dilute limit (x < 0.01), Co is reported to be a very shallow donor that gives ntype FeS _{2} and metallic electrical behavior at low doping levels. This is due to the shift in Fermi level into the conducting band. Co_{ x }Fe_{1−x}S_{2} is also believed to be paramagnetic at room temperature for all values of x > 0^{4}. Undoped CoS_{2} and doped alloyed samples for x > 0.7 show a ferromagnetic to paramagnetic phase transition at T_{ C } ≈ 120 K^{5}. We therefore expected Co_{ x }Fe_{1−x} S_{2} nanocrystals (NCs) to exhibit a range of magnetic behavior, from pure diamagnetism (x = 0) to fully spinpolarized ferromagnetism (half metallic ferromagnetism) at low temperatures for x > 0.5.
The preparation of Co_{ x }Fe_{1−x}S_{2} NCs offers the possibility of tunable magnetic properties by changing particle size, shape, and surface chemistry via synthesis conditions^{6} or postsynthesis surface treatments^{3}. NCs are expected to show strongly enhanced magnetic moments due to their high surface area to volume ratio and the reduced coordination of atoms at the surface. The magnetic properties of Co_{ x }Fe_{1−x}S_{2} NC powders have not yet been reported.
In order to harmonize the terminologies used in describing different structural entities in the paper we define them at the onset. A crystallite or a grain is defined as a single crystalline domain which we call nanocrystal; a nanoparticle (NP) is defined as an object that may consist of one or more crystallites/grains and lastly, a cluster is a collection of nanoparticles. The polydispersity index of a particle ensemble, which is given by the standard deviation of the particle sizes divided by the mean of their sizes, defines monodispersity. If the index parameter is smaller than 0.25, then the particles are monodispersed^{7}.
One may note that different magnetic interactions take place on different length scales, e.g. exchange interaction between NCs and dipole interaction between NPs. In general, nanocrystallites can have random orientation of the anisotropy axes varying locally (random magnetic anisotropy). Due to exchange interactions, however, the particles can be magnetic. Also due to the finite size of the particles one can have stray fields/dipolar fields and, finally, due to the aggregation one can have dipolar interactions between the particles. The transition from ferromagnetism to superparamagnetism (SPM) or superspin glass (SSG) behavior is generally expected for discrete small clusters where the individual magnetic moments within such clusters are thermally unstable. The SSG state is believed to result from the frustration generated by dipoledipole interactions among superspins (magnetic moments of nanoparticles) and from disorders in the system (e.g., the random distributions of particles, positions, sizes and anisotropyaxis orientations). A further increase of interparticle interactions may lead to a kind of ferromagnetic domain state or superferromagnetism (SFM)^{8}.
Here, we report the synthesis of Co_{ x }Fe_{1−x}S_{2} NCs and their structure, morphology and magnetic properties. We measured the lattice constant, NC size and NP size as a function of composition x using Xray diffraction (XRD), small angle Xray scattering (SAXS)^{9} and scanning electron microscope (SEM)/transmission electron microscope (TEM). DC magnetization and AC susceptibility measurements were performed as a function of temperature and frequency. At low temperatures, samples with x = 0.625–1.0 appear to consist of ferromagnetic (FM) nanoclusters embedded in a superspin glass matrix. Samples with x = 0.5 behave as antiferromagnetic (AF) clusters embedded in a superparamagnetic matrix. Below x = 0.5, the samples are predominantly paramagnetic. Thus, the overarching trend in magnetic properties can be seen as a gradual transition between these extremes, going from ferromagnetism in the Co end, via antiferromagnetism to an increasingly paramagnetic behavior for high Fe content. All these have lead to a fairly complex magnetic phase diagram which is explained in terms of competition between the various dipolar, exchange, inter and intracluster interactions.
Results and Discussions
SEM and TEM
SEM and TEM provide real space images of the NCs. Figure 1(a–c) shows the SEM images of typical samples with nominal composition x = 1.0, 0.5 and 0.0. The NCs are irregular in shape, fairly polydisperse, and somewhat aggregated. From the TEM images in Fig. 1(d–f), we estimate that the NCs have an average diameter of 24 ± 5 nm (x = 1), 6.0 ± 1.5 nm (x = 0.5) and 9.0 ± 2.5 nm (x = 0). Highresolution TEM (HRTEM) images in Fig. 1(g–i) show the lattice planes of the samples. The observed latticefringes correspond to the {100}, {111}, {200}, {210} and {220} planes of pyrite Co_{ x }Fe_{1−x}S_{2}. Size histograms compiled from the SEM data are shown in Fig. 1(j–l). Analysis of the Gaussian fits gave an estimate of the mean NC size. The average polydispersity index in our samples is around 0.35. Statistical processing of the raw TEM data were exported and plotted using Origin 9.0 software.
XRD
XRD and SAXS are indirect methods, but they provide statistical information as opposed to local information from SEM or TEM. Figure 2(a) shows the typical XRD data for the Co_{ x }Fe_{1−x} S_{2} NC powders. The samples are apparently phase pure within the limit of detection of this technique. A gradual shift in the peak positions towards lower 2θ values with increasing x, indicates a systematic increase in the lattice constant, as expected for Co_{ x }Fe_{1−x}S_{2} solid solutions. The dotted vertical lines show the reference peak positions for pure FeS _{2} (x = 0) and pure CoS _{2} (x = 1). The diffraction peaks at the two ends are consistent with the values given in the standard PDF cards for FeS_{2} (PDF 000421340), CoS_{2} (PDF 000411471).
The patterns were analyzed by Rietveld refinement^{10} using the Highscore Plus software (v4.1, PANalytical B.V., Almelo, Netherlands)^{11}. The extracted lattice constants have been plotted in Fig. 2(b) along with the predicted lattice constant (a), following Vegard’s law^{6}. Note that we have included the binary end members 5.417 Å for FeS _{2} and 5.528 Å for CoS_{2}. The estimated accuracy in composition is ±6%. We have used the lattice constants to estimate the NC composition, which is in good agreement with the nominal one.
We also directly measured the Co:Fe ratio of each sample using energy dispersive spectroscopy (EDS) mapping in a TEM. The measured (expected) values of x averaged over thousands of NCs across several areas of each sample were 0.0 (0.0), 0.140 ± 0.014 (0.125), 0.270 ± 0.027 (0.250), 0.340 ± 0.013 (0.375), 0.380 ± 0.015 (0.500), 0.600 ± 0.087 (0.625), 0.740 ± 0.032 (0.750), 0.880 ± 0.017 (0.875), and 1.0 (1.0). These values agree quite well with the XRD results and demonstrate that the average composition of the Co_{ x }Fe_{1−x}S_{2} NCs is close to the intended composition. Highresolution EDS mapping revealed significant compositional variation from NC to NC in some of the samples, but poor sample stability under the focused electron beam made accurate quantification of the degree of particletoparticle inhomogeneity very difficult, so it was not pursued further.
Figure 2(c) shows the crystallite size as obtained from the Rietveld refinements corresponding to the 200, 220 and 311 reflections. The crystallite size decreases from 14 ± 2 nm at x = 1.0 to 7 ± 1 nm for x = 0.125 to 0.625, then increases gradually to 15 ± 1 nm for x = 0.0. A similar trend was observed following the evolution of all main peaks. Alternatively, strainfree crystallite size was determined from individual peak widths using the Scherrer formula which give similar values. The size of the crystallites is fairly similar to that observed by TEM. However, their size is smaller than the size of the NPs observed by SAXS, showing that some of the NPs are composed of a few NCs.
SAXS
The basic theory of SAXS applied in this work involves the determination of a set of parameters related to several average values of the radii of the NPs. For polydisperse systems the local monodisperse approximation (LMA) is commonly used^{12,13}. In the present work, we have considered scattering from spheres of two different sizes of radii R and R′, with ΔR and ΔR′ representing the mean of the particle radii and their respective distributions, as this provides the most accurate description of the form factor for the present data. The corresponding interparticle distances (ξ and ξ^{′} and their respective standard deviations σ and σ′) are related to the pair correlation function embedded within the scattering crosssection^{14,15}.
In Fig. 3(a), the scattered intensity is plotted as a function of the total scattering vector q. From the 1D data, one can see that all samples show a prominent scattering feature in the form of a hump that shifts from 0.12 nm^{−1} to 0.02 nm^{−1} as composition changes from x = 0.125 to x = 1. This feature appears at 0.05 nm^{−1} for FeS_{2}. The shift of the hump with x can also be interpreted as a change in NP assemblies with different interparticle correlations. An additional smaller humplike feature is seen at 0.1 nm^{−1} for all compositions. Below q = 0.01 nm^{−1}, the instrument resolution limits us to make a proper estimate of NP size.
Figure 3(b) shows the two parameters (NP radius R and interparticle distance ξ) as a function of x. R is 40 nm for x = 0. R decreases to 20 nm and then increases to 70 nm with increasing x, while R′ always remains around 30 nm. It may be noted that the trend in NP size (particle diameter 2 R) is similar to that of the NC size extracted from the XRD/TEM data. This signifies that the ratio of the NC size and NP size is constant at around six to eight. This indicates that each NP contains a similar number of NCs, regardless of its composition. The interparticle distances ξ maintain a small variation from 80 ± 20 nm to 150 ± 33 nm within the LMA. One may note that the SEM/TEM data cannot be directly correlated to the SAXS data where the accessible length scale depends upon the scattering geometry. The former is a local probe whereas the latter has more sampling statistics, giving information on the statistically averaged value of sample morphology (object geometry, size, size distribution and spatial correlations) over a much larger sample volume. Notably, from TEM one gets a numberweighted mean of the NC/NP size but with XRD it is volumeweighted and with SAXS it is intensityweighted.
Magnetization
FC and ZFC
To characterize the magnetic properties of the NCs, the magnetization (M) was measured as a function of temperature (T). We used five different applied fields H of 50, 100, 500, 1000 and 2000 Oe during measurements with increasing temperature. The samples were initially cooled down to 5 K either in the presence of H = 70 kOe (FC) or with no magnetic field (ZFC). The M(T) curves are shown in Fig. 4(a–e).
For x = 1, 0.875, and 0.75, the ZFC curves show a broad maximum (particularly at lower fields) which can be referred to as blocking/freezing temperature (T_{F}) of the polydisperse NCs, while the FC curves do not show a temperature independent platformlike behavior at low temperatures. The appearance of the maximum in the ZFC curve suggests that the assembly of magnetic nanoparticles passes from the blocked/frozen state to the superparamagnetic regime as the temperature rises. The broadness of the peak is due to the distribution of blocking temperatures, which is expected from a system with particle size distribution. The FC curves continue to increase gently with decreasing temperature for x ≥ 0.75, and steeply for x ≤ 0.625. This strong history dependence is a generic feature of several commonly known magnetic systems like superspin glasses and superparamagnets^{16}. In Fig. 4(f), we show a gradual decrease of T_{F} with field for x = 1, which suggests that the frozen state is suppressed by the field.
We find a eightfold decrease in magnetization from x = 1 to x = 0.875 which can be plausibly due to an initial disorder in the system^{17}. This is followed by an increase in magnetization for x = 0.75 which is not understood at present. On further increase in Fe content, a monotonous decrease in magnetization can be seen at least up to x = 0.5. With increase in Fe below x = 0.5, the system becomes increasingly paramagnetic as the M(H) hysteresis curve at x = 0.5 still displays a positive slope.
We also observe a maximum in M(T) at around \({T}_{{\rm{\max }}}^{F}\) = 20 K for x = 0.875 to 0.5, also known as spin freezing temperature, which is a typical feature of systems with antiferromagnetic or ferrimagnetic ordering and thus indicates that a small proportion of Co oxide is present in every sample. These ordering temperatures have often been seen to decrease with nanocluster size^{18}. Since the magnetization of CoS _{2} is higher than other compositions, the \({T}_{{\rm{\max }}}^{F}\) peak remains in the background. The origin of \({T}_{{\rm{\max }}}^{F}\) was further verified by fully oxidizing the CoS_{2} sample in air, after which a single sharp peak was identified at 20 K in the susceptibility plot.
A welldefined irreversibility temperature (T_{irr}), i.e. the temperature where the FC and ZFC curves diverge, could be identified. The irreversibility temperature corresponds to the supermagnetic transition of the biggest nanoparticles in the assembly. We plot T_{F} and T_{irr} versus x in Fig. 5. Both, T_{F}, T_{irr}, are found to increase with x or in other words they scale with particle radius and interparticle distance. Linear scaling of T_{F} signifies an increase in the anisotropy energy barrier^{19}. T_{irr} shows a gradual saturation behavior with x, which signifies a progressive blocking/freezing of bigger nanoparticles^{20}.
We plot T_{irr} versus field only for samples with x = 1, 0.875, 0.75 and 0.625 as shown in Fig. 6(a,d,g,j). For sample with x = 0.5, a field dependence could not be ascertained. The observed shift of T_{irr} to lower temperatures with increasing field can follow the AlmeidaThouless (AT) line that indicates superspinglass (SSG) behavior, as shown in Fig. 6(b,e,h,k). The AT line expression is
where T_{irr(0)} is the zero field freezing temperature and ΔJ is the width of the distribution of exchange interactions. Figure 6(c,f,i,l) shows the evolution of T_{irr} which can be mapped on the H−T plane in order to distinguish the SSG phase from the SPM phase.
Hysteresis loop
Inplane MH curves of samples with x = 1.0, 0.875, 0.75, 0.625 and 0.5 measured at 10–150 K are shown in Fig. 7(a–e). For all temperatures, we find that the magnetization increases with increasing x, except for x = 0.875, where we find a decrease. This decrease is consistent with the decrease in the FCZFC curves discussed in the previous section. The magnetization decreases from x = 0.75 onwards and finally disappears below x = 0.5. Similar behavior was reported for Co_{ x }Fe_{1−x}S_{2} single crystals by Leighton et al.^{5}. Samples with x < 0.5 show increasing paramagnetic response. The magnetization of all samples is unsaturated at even the highest fields explored here (10 kOe). We observe ferromagnetic hysteresis loops with coercive fields as large as 0.6 kOe (x = 1, T = 10 K). The hysteresis diminishes with increasing temperature and decreasing x; for x = 0.5, the magnetization exhibits barely any hysteresis even at 10 K. The absence of saturation combined with pronounced hysteresis loops for x > 0.5 is characteristic of ferromagnetic grains embedded in SSGlike matrices^{8,21}.
We define H_{ c } = (\({H}_{c}^{+\alpha }\) − \({H}_{c}^{\alpha }\))/2 and H_{ eb } = (\({H}_{c}^{+\alpha }\) + \({H}_{c}^{\alpha }\))/2, where \({H}_{c}^{+\alpha /\alpha }\) are the coercive fields for the positive and negative field axes. We plot the coercivity (H_{c}) and exchange bias field (H_{eb}) at 10 K as a function of x in Fig. 7(f)). The existence of H_{eb} (=−0.12 kOe for x = 1) confirms the presence of a small proportion of antiferromagnetic Co oxide. The magnitude of both parameters gradually increases with increasing x because the spinspin coupling is proportional to the concentration of cobalt centers in the lattice which affects the exchange coupling of Co with cobalt oxide. Plots of H_{ c } versus T^{1/2} in Fig. 8(a–d)) for x = 1, 0.875, 0.75 and 0.625 do not intercept the T axis as expected for the SPM type of noninteracting nanoparticle ensemble, thus indicating a SSG type of behavior in these samples. A linear slope would have indicated a SPM type of behavior.
AC susceptibilities
AC magnetic susceptibility (χ′(T) = dM/dH) measurements are utilized in supermagnetic systems due to their ability to probe different values of the relaxation time that categorize paramagnetic or glassy behaviors. To distinguish between SPM and SSG behavior, we measured the temperature dependence of the AC magnetic susceptibility since the frequency response of the peak in the χ′(T) curve is different for the SPM phase from the SSG phase. Data were taken over a frequency range of 10 to 10,000 Hz in the presence of a small AC field of 5 Oe and without any DC field. We categorize the data analysis section into three separate ones viz. (i) with x = 1.0, (ii) x = 0.875, 0.75, 0.625 and (iii) x = 0.5.

(i)
Co_{ x }Fe_{1−x}S_{2} with x = 1.0:
The frequency dependence of the real part of the susceptibility (χ′(T)) of a sample with x = 1.0 shows two different temperature regimes demarcated by the two paramagnetic Curie temperatures T_{p1} = 233 K and T_{p2} = 110 K in Fig. 9(a). In each regime, two broad peaks centered at \({T}_{{\rm{\max }}}^{AC}\)\(\simeq \) 75 K and 225 K are visible. Multiple peaks in χ′(T) often indicate the presence of several magnetic phases in a sample. We believe that the two phases, primary and secondary, correspond to the two different magnetic nanoparticle correlations observed in the SAXS measurements described above. One may recall the two humps in the SAXS spectra (Fig. 3(a)), one that shifts with x (particularly for x > 0.625) and the other one that remains unchanged. The difference in the χ′(T) signals, corresponding to T_{p1} and T_{p2}, defines their respective proportionality within the system for a particular composition.
Inverse χ′(T) plot is a good marker for the critical temperature to show the differences between, e.g., ferromagnetism and antiferromagnetism below the respective ordering temperature. Above the ordering temperature, its linearity represents a typical Curie behavior. The first part of the magnetic phases in Fig. 9(b) follow a linear behavior according to the CurieWeiss law. Accordingly, we find two CurieWeiss temperatures (T_{CW1} = 175 K and T_{CW2} = 28 K) from linear fits to the inverse χ′(T) plot. We have used the increasing portion of 1/χ′(T) following T_{N2} in determining the average T_{CW2} value before it flattens out. For T_{CW1}, a linear fit to the increasing proportion of the same following T_{N1} is more obvious. The positive T_{CW} values indicate ferromagnetic interactions between embedded magnetic nanoparticles in a SPM or SSG matrix. In the second part of the magnetic phases, the data depart progressively away from linearity. The points where the hyperbola intersects the temperature axis are the estimated values of T_{p1} and T_{p2}. The deviations from linearity give the corresponding Néel temperatures T_{N1} = 260 K and T_{N2} = 122 K. Above these temperatures, the magnetic nanoparticles behave according to the CurieWeiss law, while below where the experimental data deviate from the fit, SPM/SSGlike interactions may determine the response of the system. We have used T_{N} to mark the ferromagnetic Curie temperature following its familiarity with the localizedmoment picture proposed by Néel in his theory of antiferromagnetism.
Our focus will mainly be on the \({T}_{{\rm{\max }}}^{AC}\) at lower temperature because the higher temperature maxima can be neglected. Note the difference in the \({T}_{{\rm{\max }}}^{AC}\) signals at the two temperatures. This difference signifies a lower proportionality of the secondary phase as compared to the primary phase. The \({T}_{{\rm{\max }}}^{AC}\) peaks decrease in magnitude and shift to higher temperature with higher driving frequency. The shift gives the activation energy and is characteristic of SPMtype or SSGtype behavior. Since a shift in χ′(T) peak with frequency is expected for both superparamagnets and superspin glasses, further analysis is need to identify. One may note that noninteracting SPM clusters should show larger frequency dependence than SSG clusters since the distribution of relaxation times is characteristic for the spinglass phase. We performed several cross checks to qualitatively analyze the dynamical behavior. Three common models of superparamagnetic dynamics are embodied in the (a) NéelArrhenius law, (b) VogelFulcher law and (c) power law in addition to the (d) empirical equation, which are all employed in discerning the two magnetic phases^{22,23,24,25,26}.

(a)
Noninteracting SPM clusters generally follow the NéelArrhenius law.
$${\tau }_{m}={\tau }_{0}\exp \frac{{\rm{\Delta }}E}{{k}_{B}T}$$(2)where τ_{0} = (2πf_{0})^{−1} is the relaxation time or the inverse of the attempt frequency (f_{0}) and τ_{m} = (2πf_{m})^{−1} is the measuring time (~10^{2}s for the DC magnetization measurement) or the inverse of the measuring frequency (f_{m}). ΔE( = K_{A}V) is the anisotropy energy or activation energy for cluster formation. Here K _{A} is the anisotropy constant, k_{B} ( = 1.38 × 10^{−16} erg/K) is the Boltzmann constant and V the average cluster volume critical for SPM or SSG state at T_{F}. τ_{0} has a typical value of 10^{−9}–10^{−13} s for SPM behavior.
We plot the dependence of (\({T}_{{\rm{\max }}}^{AC}\))^{−1} on the natural logarithm of the measurement frequency in Fig. 9(c). A linear fit yields a slope of ΔE/k_{B} = 22,193 K and this value derives an unreasonably small value of τ_{0}~10^{−129} s. Based on the unphysical value of τ_{0}, we conclude that the NéelArrhenius expression fails to describe the system, suggesting that magnetic dipoledipole interactions between the magnetic nanoparticles are important and cannot be ignored.

(b)
The VogelFulcher law phenomenologically describes the frequency response of the relaxation time by taking into account the weak interactions among spin clusters and is expressed by
$${\tau }_{{\rm{m}}}={\tau }_{{\rm{0}}}\exp [\frac{{\rm{\Delta }}E}{{k}_{{\rm{B}}}({T}_{{\rm{\max }}}^{AC}{T}_{{\rm{0}}})}]$$(3)where T_{0} is the characteristic temperature that accounts for the static interaction field of the surrounding clusters. We show a plot of ln(τ_{ m }) versus \({T}_{{\rm{\max }}}^{AC}\) in Fig. 9(d). The values obtained from a fit to the equation 3 are ΔE/k_{ B } ~130 K, T_{0} ~71 K and τ_{0} ~3 × 10^{−13} s. These values are physically reasonable and comply with the SSG behavior for which the typical value of τ_{0} ~10^{−10}–10^{−13} s^{23}. Thus we believe that the maxima observed in χ′(T) correspond to the freezing of weakly interacting NC moments.

(c)
The power law or the scaling hypothesis supposes the existence of an equilibrium phase transition. It relies on the relation of critical slowing down of the relaxation time near the transition temperature. The relaxation behavior is expressed by
$${\tau }_{{\rm{m}}}={\tau }_{\ast }{[\frac{{T}_{{\rm{\max }}}^{AC}{T}_{SSG}}{{T}_{SSG}}]}^{z\nu }$$(4)Here, τ_{*} is a relaxation time for each nanocluster, zν is the dynamical scaling–critical exponent constant^{25} related to the correlation length ξ, which is a measure of the size of the lateral coarsening (ν describes the divergence while z is involved in the dynamical scaling hypothesis τ_{ m } ~ ξ^{z}). In Fig. 9(e) we plot the variation of τ_{ m } (in log scale) versus \({T}_{{\rm{\max }}}^{AC}\). The fit to the equation 4 yields a value of zν ~ 9 and τ_{*} ~ 10^{−10} s, which are comparable with the typical values reported for SSG systems^{26}.

(d)
Beyond the three models described above, another simple, useful and sensitive criterion to distinguish between the freezing and the blocking processes is to determine the relative shift of the χ′(T) peak with frequency using the empirical equation
where \(\overline{{T}_{{\rm{\max }}}^{AC}}\) is the mean value of the frequency dependent maximum in χ′(T), while \({\rm{\Delta }}{T}_{{\rm{\max }}}^{AC}\) is the difference in \({T}_{{\rm{\max }}}^{AC}\) over the frequency interval Δlog_{10}(f_{ m }^{)23,26}. Typically, the parameter p assumes values of 0.0045–0.06 (for SSG phases) and 0.10–0.13 (for SPM phases). In our case, p = 0.014, which again indicates an interacting SSGtype of behavior^{22}.

(ii)
Co_{ x }Fe_{1−x}S_{2} with x = 0.875, 0.75 and 0.625:
Figures 10(a), 11(a) and 12(a) plot χ′(T) at different frequencies for samples with x = 0.875, 0.75 and 0.625. All samples show a broad peak \({T}_{{\rm{\max }}}^{AC}\) in χ′(T). Two Weiss temperatures T_{CW1} and T_{CW2} can be extracted from the linear fits of each inverse χ′(T) plot and two deviations from linearity for the inverse χ′(T) with two corresponding ordering temperatures T_{N1} and T_{N2} for x = 0.875 and 0.75 as shown in Figs 10(b), 11(b), respectively. For x = 0.625, in Fig. 12(b), we find only one T_{CW2} and the corresponding T_{N2}. One may note that the net magnetization in our system largely shows a decreasing trend with decreasing x. For x = 1, for example, the magnetization is highest and we can see the two peaks in the AC spectra. The secondary peak being much weaker as compared to the primary one shows a systematic decrease with decreasing x. Beyond x = 0.625, it simply goes into the background. All CurieWeiss temperatures are positive. Their frequency dependence is typical of SSG behavior as demonstrated using the three models described above and shown in Figs 10(c–e), 11(c–e) and 12(c–e). These are typical signatures of a mixedphase situation with embedded FM clusters in SSG matrices^{27}.

(iii)
Co_{ x }Fe_{1−x}S_{2} with x = 0.5:
The frequency dependence of χ′(T) for samples with x = 0.5 is shown in Fig. 13(a). A peak (\({T}_{{\rm{\max }}}^{AC}\)) is observed at ~5 K for all frequencies. The peak shifts to higher temperature and lower height with driving frequency. Plots of inverse χ′(T) versus temperature yield a negative CurieWeiss temperature T_{CW2} = −30 K, indicating predominant AF ordering and a deviation from linearity gives T_{N2} = 121 K as shown in Fig. 13(b). We performed a similar qualitative analysis for the dynamical behavior. We plot the natural logarithm of the measurement frequency versus (\({T}_{{\rm{\max }}}^{AC}\))^{−1} in Fig. 13(c). A linear fit to the data gave a slope of 74 K, which equates to a value of τ_{0} ~ 10^{−9} s. Thus, this sample is well described by the NéelArrhenius law indicating no magnetic dipolar interactions which is relevant for a typical SPMtype of behavior. In light of the negative CurieWeiss temperature, we believe that this system consists of AF clusters embedded within a SPMlike matrix.
Magnetic nanoparticles within random magnetic anisotropy (RMA) model
In order to understand such complex systems, we refer to the model suggested for disordered magnetic nanoparticle systems within the random magnetic anisotropy (RMA) model^{28} with competing dipolar interactions and exchange couplings by Mao et al.^{29}. The total energy of the system reduced by the anisotropy energy K_{ A }V is written as
Here, magnetic moment of cluster i is assumed to be \({M}_{s}V{\hat{s}}_{i}\), where M_{ s } is the saturation magnetization and \({\hat{s}}_{i}\) is the orientation while \({\hat{e}}_{i}\) is the direction of the easy axis with the anisotropy constant K_{ A }. The reduced energies, g, J and h are the dipolar, exchange and Zeeman energies. The distance between the clusters i and j is given by r_{i,j} in units of ξ (\({\hat{r}}_{i,j}\) indicates the direction of r_{i,j}). The average distance between two nearestneighbor of clusters is ξ for nanospheres of volume V = R^{3}.
Under the mean field approximation, due to random anisotropy^{28} the mean anisotropy of the system is zero, which leads to the Curie–Weiss temperature T_{CW} = 0. For a ferromagnetic exchange system, the mean field of ferromagnetic exchange coupling is positive, yielding T_{CW} > 0. For a disorder (random anisotropy axes) system with dipolar interaction^{30}, such as in the present case with x = 0.5, a negative mean field is expected from the first part of the dipolar energy \((g\frac{{\hat{s}}_{i}\cdot {\hat{s}}_{j}}{{r}_{i,j}^{3}})\) while the average over the random field \((g\frac{\mathrm{3(}{\hat{s}}_{i}\cdot {\hat{r}}_{i,j})({\hat{s}}_{j}\cdot {\hat{r}}_{i,j})}{{r}_{i,j}^{3}})\) of the second part of the dipolar energy would give zero, yielding T_{CW} < 0. In a competing interaction system, with x ≥ 0.5, T_{CW} can increase from negative to positive as J increases for a fixed value of g. When T_{CW} < 0, dipolar interactions are dominant where SSGtype phase may appear or dipolar interactions are suppressed and SPMtype phase may appear. With increase in J, T_{CW} > 0, exchange coupling may dominate and ferromagnetic order can prevail.
It was reported earlier that by changing the volume density over a wide range, one can monitor the effect of dipolar interactions^{31}. In Fig. 14 we sketch the complex magnetic phase diagram deduced from our susceptibility results as function of temperature and Co fraction (x) and explain it in terms of competition between the various dipolar, exchange, inter and intracluster interactions. We plot the change in average \({T}_{{\rm{\max }}}^{AC}\) and T_{N1,N2} as a function of cobalt fraction showing the different regimes. One clearly observes an obvious paramagnetic phase at high temperature for all x. Below x = 0.5, the system is increasingly paramagnetic at all temperatures. Competitive and diluted interactions are induced by the presence of Fe and Co atoms. Thus, large Fe content stabilizes the AF phase while low Fe content (high Co) stabilizes the FM phase.
For x = 0.5 (dilute system), the NCs exhibit a twostage magnetic transition, i.e., an antiferromagnetic phase (T_{CW} < 0) at ~121 K and a SPMlike phase with embedded AF clusters at ~6.5 K. The microscopic origin of antiferromagnetism can be due to the presence of small proportions of exchangecoupled antiferromagnetic Co oxide aggregates while the NCs remain isolated. Oxides may include CoO, Co_{3}O_{4}, etc., with different Neél temperatures of 290 K and 40 K. However, we do not observe any exchange bias even below 40 K. This indicates the presence of randomly associated (decoupled) isolated nanocrystals. Random agglomeration of magnetic domains leads to demagnetizing effects that decreases coercivity. This scenario is consistent with the obtained NC sizes. The NC system is evolving here from a randomly coupled isolated system (x < 0.5) to an exchange coupled antiferromagnetic NP system embedded in a SPM matrix (x = 0.5). The NPs can acquire a a finite moments due to a canted spin state. Thus, in such a scenario, a competition between the exchange coupling within the antiferromagnetic clusters and the dipolar forces between the clusters is plausible. Once an antiferromagnetic coupling is established, dipolar interactions are no longer possible. Consequently, the dipolar interaction is not sufficiently strong here and a SPMlike phase is established^{32}.
For x ≥ 0.625, the magnetic dynamics change the twostage magnetic transitions due to increasing dipolar interaction. The magnetic behavior changes from ferromagnetism (T_{CW} < 0) at ~136 K to that resembling SSGlike phases with embedded FM clusters at ~28 K. The basic physical picture is provided by the RMA model encapsulated in equation (6). It describes that as the volume fraction of Co increases, the effects of both dipolar and exchange interactions are evident. The aggregates evolve from isolated NCs to exchangecoupled magnetic nanoparticles. The SSGlike behavior comes from the competition between a mixture of ferromagnetic and antiferromagnetic clusters interacting with each other via dipolar forces.
Conclusions
We have synthesized cobalt iron pyrite (Co_{ x }Fe_{1−x}S_{2}) nanocrystals and investigated their structure, morphology, and magnetic properties. Using XRD, SAXS, SEM and TEM, we show that there is a systematic variation in the lattice constant, primary grain size, and aggregate size with increasing cobalt content. We find a reasonable agreement of lattice constant a with Vegard’s law which is evidence for alloying with x close to the nominal ones. TEMbased EDS confirmed these compositions. Each nanoparticle is a collection of a few NCs whose number remain similar over a wide range of x.
Magnetically, the cobalt iron pyrites show interesting regimes of competing exchange and dipolar interactions with increasing Fe content, which is investigated using DC magnetization and AC susceptibility at various temperatures and frequencies. Below x = 0.5, the system remains mostly paramagnetic. With an increase in x, for x = 0.5, the nanocrystals remain largely isolated as they show noninteracting SPMlike behavior, i.e. absence of magnetic dipole interactions between the embedded AF nanoclusters. Here, the exchange interaction is not strong enough to suppress the SPM behavior. However, dipolar interactions result in a collective state at larger x. For x ≥ 0.625, the collective state possesses SSGlike behavior along with embedded FM characteristics. In samples of magnetic nanoparticles, exchange interactions are often important and can be sufficiently strong to suppress the SPM relaxation. We have constructed a phase diagram as function of temperature and Co fraction and explained the terms of competition between the various dipolar, exchange, inter and intracluster interactions.
Functional ndoped iron pyrite with tuning possibilities of NC size and shape has opened up new prospects in the field of spin polarized ferromagnetism. In the future, improvements in the NC quality, detailed structural analysis, and analysis of functional properties will be addressed.
Methods
Sample preparation
Chemicals
Anhydrous iron (II) chloride (98%, Aldrich), anhydrous cobalt (II) chloride (99.7%, Alfa Aesar), sulfur powder (99.998%, Aldrich), chloroform (99.5%, Aldrich), anhydrous ethanol (99.5%, Aldrich), octadecylamine (90%, Acros), phenyl ether (99%, Acros) and argon gas (99.999%, Praxair) were used as received.
Nanocrystal Synthesis
Co_{ x }Fe_{1−x}S_{2} nanocrystals were synthesized using a modified version of a literature recipe^{3}. All steps were performed using standard airfree techniques. A total of 3 mmol of MCl _{2} (M = Co + Fe, with the ratio of the two metals determined by the desired Co_{ x }Fe_{1−x}S_{2} NC compositions of x = 0.0, 0.125, 0.25, 0.375, 0.5, 0.625, 0.75, 0.875, and 1.0) was dissolved in 25 g of octadecylamine at 80 °C, then degassed under vacuum for one hour. Separately, 1 mmol of sulfur was dissolved in 10 mL phenyl ether at 90 °C, then vacuum degassed for one hour. After degassing, the MCl_{2} solution was heated to 215 °C, whereupon the sulfur solution was quickly injected into the MCl_{2} solution to initiate nanocrystal nucleation. The reaction was held at 218 °C for 3 hours, then quenched in a water bath and diluted with 20 mL of ethanol once the temperature fell to 95 °C. The raw product was collected by centrifuging the reaction mixture for 3 min, removing the supernatant, and resuspending the solid in 30 mL of chloroform. Two additional rounds of centrifugation and reprecipitation were used to clean the nanocrystals. The purified nanocrystals were dried and stored as a loose powder.
SEM and TEM
The local morphology of the NCs were imaged using a FEI Magellan 400 XHR scanning electron microscope (SEM) operating at 10 kV (50 pA) and an FEIPhilips CM20 transmission electron microscope (TEM) operating at 200 kV.
Co:Fe ratios were measured by energy dispersive Xray spectroscopy (EDS) in a JEOL JEMARM300F GrandARM (S)TEM equipped with dual silicon drift detectors (0.98 sr collection solid angle) and operating at 300 kV. Co_{ x }Fe_{1−x}S_{2} NCs were dispersed in chloroform (10 mg/mL) with 5 minutes of sonication. Copper TEM grids with carbon film coatings (400 mesh, Ted Pella) were dipped into the NC solution for 3 s, rinsed with chloroform and anhydrous ethanol to remove unreacted precursors, and dried. EDS maps of four large particle clusters (>500 particles each) were collected for each sample after a 20 minute electron beam shower. Quantitative EDS analysis utilized the CliffLorimer model as implemented in the Gatan Microscopy Suite software package.
Xray characterization: XRD
Powder Xray diffraction (XRD) measurements were performed on a Rigaku SmartLab Xray diffractometer in BraggBrentano reflection geometry with a 2θ angular range of 20 to 90 degrees.
Xray characterization: SAXS
In order to get a statistical information about the morphology of the NCs powders, we carried out smallangle Xray scattering (SAXS) measurements. SAXS was performed on a Ganesha 300XL instrument (SAXSLAB ApS, Copenhagen/Denmark) equipped with a GENIX 3D microfocus Cu Xray source operating at 50 kV/0.6 mA (wavelength λ = 1.542 Å). The samples were mounted in between adhesive tapes. A twodimensional Pilatus 300 K detector was used, which can be moved to the desired sampletodetector distance for WAXS or SAXS resulting in a qrange of 0.01–0.25 nm^{−1} where q is the momentum transfer corresponding to the scattering angle 2θ via q = 4 πsin(θ)/λ. A pin–diode detector was used to record the beam intensity and transmission of each sample and of the sample holder. All images were corrected for cosmic background and parasitic scattering. The obtained 2D images were azimuthally integrated to get 1D data, and the background from the adhesive tapes was subtracted prior to data analysis.
For analysis, the raw data was converted to intensity versus momentum transfer q with the software DPDAK (v.0.2.9) using a sample to detector distance of 1056 mm and a detector pixel size of 172 micron^{9}. The SAXS data were fit with the software Genplot (v.2.11 by Computer Graphic Service Ltd.).
SAXS data are modelled using the crude approximation for dense system known as LMA which is often used to describe a polydispersed system by separating the form factor from the interference function. The LMA hypothesis assumes that the system is comprised of locally monodispersed domains that interfere incoherently. The particleparticle pair correlation function can vary from domain to domain. The surrounding of each particle is supposed to be made of particles of same size and shape in such a way that the particle kind varies slowly across the sample but with a spatial wavelength lower than the coherence length of the beam. The total scattering intensity is obtained by an incoherent sum of the intensities from each domain of monodisperse subsystems weighted according to the sizeshape distribution and is given by
where * denotes the convolution product and 〈...〉_{ D } is the average over coherent domain D enclosing the form factor F(q, R)^{2} in which the local interference function S(q, R) can depend on the particle size^{15}.
Features in scattering data at low q values arise from instrumental resolution effects. To fit the full scattering curve, these contributions from the instrumental resolution are modelled by considering a Lorentzian function. The intensity maximum provide a good estimate of the particle size. The smeared intensity minima of the SAXS data indicate a modest polydispersity in size distribution. Two form factors of the form
with spherical geometry distributed over a 1D paracrystalline^{14} lattice were considered. These form factors correspond to radii R and R′ of the scattering objects. The proportion of spherical particles with radius R′ was very small in comparison to the spherical particles with radius R. A Gaussian distribution function is used to describe the polydispersity of the scattering objects and is given by
where 〈R〉 and ΔR represent the mean and the distribution of the particle radii. Notably, the size distribution of the NPs are often difficult to determine precisely, and are typically assumed to be spherical with lognormal size distributions.
The distribution of particles is given by the interparticle correlation or local interference function S(q,R). The structure factor S(q,R), on omitting the homogeneous part, is expressed with the pair correlation function g(R) by
where n_{ P } is the number density of particles. According to paracrystal theory, the scattering function is affected by the shape of the aggregation and expressed as a convolution product of S(q)*γ(q) where γ(q) is the structure factor of the aggregation by which finite size effects are introduced. The respective correlation functions of γ(q) (or the Debye–Bueche equation) and S(q) are known and are given by
and
where σ and ξ are respectively the squareroot of the variance and the mean value of the the distance probability or the correlation length^{15}. S(q)*γ(q) is obtained by taking the Fourier transform of the products of the correlation functions. Thus the average centertocenter distances (ξ and ξ′) of the scattering objects (R and R′) were associated with the structure factors and were also obtained from the fits. The distributions of radii (ΔR) and standard deviations of correlation lengths (σ) were also used as fit parameters. The SAXS signal from the whole sample volume revealed an isotropic scattering pattern from the pyrites which means there was no azimuthal dependence of the signal on the 2D detector.
Magnetometry
Conventional inplane magnetization measurements were performed as a function of temperature and field using a superconducting quantum interference device (SQUID) from Quantum Design (MPMSXL). Conventional AC field susceptibility measurements were acquired at various temperatures and frequencies using a physical property measurement system (PPMS).
References
Ennaoui, A. et al. Iron disulfide for solar energy conversion. Sol. Energy Mater. Sol. Cells 29, 289–370 (1993).
Ennaoui, A. & Tributsch, H. Iron Sulphide Solar Cells. Sol. Energy Mater. Sol. Cells 13, 197–200 (1984).
Puthussery, J., Seefeld, S., Berry, N., Gibbs, M. & Law, M. Colloidal iron pyrite (FeS2) nanocrystal inks for thinfilm photovoltaics. J. Am. Chem. Soc. 133, 716 (2011).
Guo, S. et al. Charge transport in cobaltdoped iron pyrite. Phys. Rev. B 81, 144424 (2010).
Leighton, C. et al. Composition controlled spin polarization in Co_{1−x}FexS_{2} alloys. J. Phys.: Condens. Matter 19, 315219 (2007).
Kinner, T. et al. Majority Carrier Type Control of Cobalt Iron Sulfide (Co_{ x }FeS_{1x}) Pyrite Nanocrystals. J. Phys. Chem. C 120, 5706 (2016).
Wells, J. et al. Standardisation of magnetic nanoparticles in liquid suspension. J. Phys. D: Appl. Phys. 50, 383003 (2017).
Bedanta, S. et al. Superferromagnetic domain state of a discontinuous metal insulator multilayer. Phys. Rev. B. 72, 24419 (2005).
Benecke, G. et al. A customizable software for fast reduction and analysis of large Xray scattering data sets: applications of the new DPDAK package to smallangle Xray scattering and grazingincidence smallangle Xray scattering. J. Appl. Cryst. 47, 1797–1803 (2014).
Rietveld, H. M. A Profile Refinement Method for Nuclear and Magnetic Structures. J. Appl. Cryst. 2, 65–71 (1969).
Degen, T., Sadki, M., Bron, E., König, U. & Nénert, G. The HighScore suite. Powder Diffraction 29(S2), 13–18 (2014).
Pedersen, J. S. Determination of size distributions from smallangle scattering data for systems with effective hardsphere interactions. J. Appl. Cryst. 27, 595–608 (1994).
Daillant, J. and Gibaud, A. (Eds), Xray and Neutron Reflectivity: Principle and Applications, Lect. Notes Phys. 770 (Springer, Berlin Heidelberg 2009) https://doi.org/10.1007/9783540885887.
Hosemann, R., & Bagchi, S. N., Direct Analysis of Diffraction by Matter (NorthHolland Pub. 1962).
Renaud, G., In situ GISAXS studies of growing nanoparticles, Habilitation Thesis, Université de Grenoble (2011).
Mukadam, M. D., Yusuf, S. M., Sharma, P., Kulshreshtha, S. K. & Dey, G. K. Dynamics of spin clusters in amorphous Fe_{2}O_{3}. Phys. Rev. B 72, 174408 (2005).
Nedelkoski, Z. et al. Origin of reduced magnetization and domain formation in small magnetite nanoparticles. Sci. Rep. 7, 45997, https://doi.org/10.1038/srep45997 (2017).
Resnick, D. A. et al. Magnetic properties of Co_{3}O_{4} nanoparticles mineralized in Listeria innocua Dps. J. Appl. Phys. 99, 08501 (2006).
Pacakova, B., Mantlikova, A., Niznansky, D., Kubickova, S. & Vejpravova, J. Understanding particle size and distance driven competition of interparticle interactions and effective singleparticle anisotropy. J. Phys.: Condens. Matter 28, 206004 (2016).
Dai, J. et al. Magnetic coupling induced increase in the blocking temperature of γFe_{2}O_{3} nanoparticles. Journ. Appl. Phys. 87, 7397 (2000).
Knobel, M., Nunes, W. C., Socolovsky, L. M., De Biasi, E., Vargas, J. M. and Denardin, J. C., J. Nanosci. Nanotechnol. 8, 2836 (2008).
Mukherjee, S. et al. Exchangebiaslike coupling in a CudilutedFe/Tb multilayer. Phys. Rev. B 91, 104419 (2015).
Mydosh, J. A. Spin Glasses: An Experimental Introduction. Taylor & Francis, London (1993).
Djurberg, C., Svedlindh, P., Nordblad, P., Hansen, M. F., Bødker, F. & Mørup, S. Dynamics of an Interacting Particle System: Evidence of Critical Slowing Down. Phys. Rev. Lett. 79, 5154 (1997).
Hiroi, K., Komatsu, K. & Sato, T. Superspin glass originating from dipolar interaction with controlled interparticle distance among γFe_{2}O_{3} nanoparticles with silica shells. Phys. Rev. B 83, 224423 (2011).
Zelenáková, A., Zelenák, V., Michalík, Ŝ., Kovác, J. & Meisel, M. W. Structural and magnetic properties of CoOPt coreshell nanoparticles. Phys. Rev. B 89, 104417 (2014).
Khurshid, H. et al. Spinglasslike freezing of inner and outer surface layers in hollow γFe_{2}O_{3} nanoparticles. Sci. Rep. 5, 15054, https://doi.org/10.1038/srep15054 (2015).
Herzer, G. Nanocrystalline soft magnetic alloys, in Buschow, K. H. J. (Ed.), Handbook of Magnetic Materials Vol. 10, Elsevier Science, pp. 415–462 (1997).
Mao, Z. & Chen, X. Magnetic phase diagram of interacting nanoparticle systems under the meanfield model. J. Phys.: Condens. Matter 23, 226005 (2011).
Klughertz, G., Manfredi, G., Hervieux, P.A., Pichon, B. P. & BeginColin, S. Effect of Disorder and Dipolar Interactions in TwoDimensional Assemblies of IronOxide Magnetic Nanoparticles. J. Phys. Chem. C 120(13), 7381 (2016).
Hiroi, K., Kura, H., Ogawa, T., Takahashi, M. & Sato, T. Magnetic ordered states induced by interparticle magnetostatic interaction in aFe/Au mixed nanoparticle assembly. J. Phys.: Condens. Matter 26, 176001 (2014).
González, C., Alcázar, G. A. P., Zamora, L. E., Tabares, J. A. & Greneche, J.M. Magnetic properties of the Fe_{ x }Mn_{0.600−x}Al_{0.400}, 0.200 = x = 0.600, disordered alloy series. J. Phys.: Condens. Matter 14, 653 (2002).
Acknowledgements
This work was partially funded by Bavaria California Technology Center (BaCaTeC), project No.: 4 [20142] during 2015–2016. A. Paul acknowledges the BaCaTeC funding. P. MüllerBuschbaum acknowledges Nanosystems Initiative Munich (NIM) for funding. M. Law and Z. Luan were supported by the U.S. Department of Energy under Contract No. DEEE0005324, funded by the SunShot Next Generation Photovoltaics II (NextGen PVII) program. SEM, TEM, EDS, and XRD experiments were performed in the user facilities of the UC Irvine Materials Research Institute (IMRI). This work was supported by the German Research Foundation (DFG) and the Technische Universität München within the Open Access Publishing Funding Programme.
Author information
Authors and Affiliations
Contributions
H.G. and Z.L. prepared the samples and did the XRD, SEM and TEM measurements with guidance from M.L. N.P. did the SAXS measurements and the data analysis along with A.P. using the software developed by P.M.B. H.G. and M.O. did the magnetization measurements. M.L. suggested improvements in the manuscript. P.M.B. read and commented on the manuscript. A.P. conceived and designed the work, analyzed the data, coordinated the work, and wrote the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gabold, H., Luan, Z., Paul, N. et al. Structural and magnetic properties of cobalt iron disulfide (Co_{x}Fe_{1−x}S_{2}) nanocrystals. Sci Rep 8, 4835 (2018). https://doi.org/10.1038/s41598018229961
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598018229961
Further reading

Surface distortion of Fe dotdecorated TiO2 nanotubular templates using timeofflight grazing incidence small angle scattering
Scientific Reports (2020)

Topologically stable helices in exchange coupled rareearth/rareearth multilayer with superspinglass like ordering
Communications Physics (2019)