Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Perovskite Thin Film Synthesised from Sputtered Lead Sulphide


In the last few years, research on dye-sensitised devices has been focused on the development of solar cells, based on CH3NH3PbX3 (X = I, Br, Cl) composites with perovskite structure. The deposition of perovskite thin films is usually carried out by solution-based processes using spin-coating techniques that result in the production of high quality films. Solar cells made by this method exceed 20% efficiency, with the potential for use in large scale production through ink print or screen printing techniques. As an alternative route, perovskite thin films can be deposited through thermal evaporation. A new method is proposed to produce CH3NH3PbI3, based on a radio-frequency (rf) -sputtering technique that results in a high reproducibility of the films and is compatible with roll-to-roll processes. We deposited thin films of lead-sulphide (PbS) and converted them into perovskite by placing the films in an iodine atmosphere, followed by dipping in a solution of methylammonium iodide (CH3NH3I). The conversions to PbI2 and CH3NH3PbI3 were confirmed by elemental analyses, absorption, and photoluminescence spectroscopy. Structural properties were revealed by X-ray diffraction and infrared and Raman spectroscopy.


Perovskite thin films based on organo-inorganic materials, such as CH3NH3PbX3 (X = I, Br, Cl), have attracted the attention of researchers around the world in recent years due to their impressive optical and electronic properties1,2. These include a direct band-gap (1.4–3.0 eV)3,4, high absorption coefficient5, long charge carrier diffusion length6, and an ambipolar charge transport7,8. In addition, perovskite is a low-cost material that can be prepared on a large scale for mass production. The efficiency of perovskite solar cells increased significantly in a very short period of time, improving from 3.8% in 20099 to 22.1% in 201610, which is comparable with crystalline silicon solar cells11,12,13.

Perovskite thin films have been synthesised by adopting two precursors, e.g., lead iodide (PbI2) and methylammonium iodide (CH3NH3I) (also known as MAI), for CH3NH3PbI3 perovskites. They are deposited in two steps (one precursor at a time), or both precursors are mixed and deposited in a single-step process14,15,16. Several deposition process have been developed, such as spin-coating solution process17,18, doctor-blade19, vapor-assisted solution process, dual source evaporation process, and combinations of these techniques20,21,22. The one-step spin-coating technique was used in the first lead halide perovskite solar cells and consists of deposition of a mixture of PbI2 and CH3NH3I in a polar solvent, such as N,N-dimethyformide (DMF), followed by thermal annealing at 70–150 °C in order to crystallise the perovskite film9,17,23. However, some problems concerning stoichiometry and crystallinity control have arisen due to the uncompleted reaction of precursors in solution, and the annealing process for the one-step solution-processing method24. The two-step sequential solution-processing method provides a more controllable setup than the one-step method for perovskite deposition. The film quality can be improved through controlled crystal growth, which depends on the reaction time between PbI2 and CH3NH3I, and the post annealing duration15,18,25,26. Some approaches to solution engineering and controlled solvent evaporation have been used to improve the film quality and solar cell efficiency in the solution process deposition14,26,27. Nevertheless, the spin-coating technique (in one or two steps) has been associated with poor homogeneity and is incompatible with large-area and large-scale production2,28.

Thermal evaporation is another technique widely used to synthesise perovskite thin films29,30. This method is based on simultaneous thermal evaporation of perovskite precursors (lead-halide salt and CH3NH3I) in an evacuated chamber. The technique has been implemented using single or dual-source evaporation. Film deposited by thermal evaporation are more uniform and have a higher adherence to substrates than films deposited by spin-coating. Besides that, the films are also more compact and pinhole-free, making it compatible with planar solar cells16,20,31.

Some alternative approaches have been implemented to produce more compact and pinhole-free perovskite thin films. Among them, in a work by Sutherland et al.32, an atomic layer deposition (ALD) technique was used to deposit PbS as a seed layer for post-conversion into perovskite thin films, after exposure to iodide (I2 gas) and CH3NH3I vapour, respectively. Conformal deposition and atomic thickness precision are the main advantages of the ALD technique33,34. Even though perovskite thin films based on PbS films deposited by ALD exhibit many interesting qualities, the process involves an expensive apparatus, and it adopts dangerous precursors, i.e., H2S35.

In this work, we propose an alternative approach for producing planar perovskite thin films based on combination of rf-sputtering with the solution process route. PbS thin films with good homogeneity and adherence on bare glass and silicon have been successfully deposited by sputtering36. Thus, a new method is proposed to demonstrate that PbS thin films, deposited by rf-sputtering at room temperature, can be used as precursor films for post-conversion into perovskite (CH3NH3PbI3) thin films with good homogeneity and pinhole-free. This was achieved by converting the PbS thin films into PbI2 through exposure to iodide gas (I2) at room temperature, followed by dipping into a solution of MAI for a few minutes, and subsequently submitting them to annealing at 100 °C for 20 minutes. The procedure can be extended to the production of perovskite alloys (e.g., combinations of Pb, Sn, and Ge), adopting a composite target or the co-sputtering technique. More complex structures, such as those used in the manufacture of highly efficient solar cells37,38, with the inclusion of mixed cations (Cs, MA and FA) and halides (I, Br), seem to be also feasible. Since sputtering is a very well-known technique for thin films deposition39,40,41,42,43, and its application on industrial scale42,44 is already available in the market, this approach has potential to scale-up the perovskite solar cells production.

Results and Discussion

Structural and Morphological properties

A PbS film 250 nm thick was completely converted into PbI2 through its exposure to an iodine atmosphere, generated by sublimation of solid iodine inside a closed petri plate. This step converts PbS into PbI2 by reaction with iodine: PbS + I2 → PbI2 + S(↑) 45. After the conversion the films were rinsed with ethanol to remove excess iodine. The resulting thickness of the PbI2 film was 430 nm (inset of Fig. 1b), approximately twice the thickness of the PbS. After conversion into perovskite, the final thickness was almost doubled again to approximately 800 nm. The increase in film thickness at each step is consistent with variation in the lattice parameters of PbS (a = c = 5.936 Å, JCPDS 02–0699), PbI2 (a = 4.557, c = 6.979 Å, JCPDS 07-0235), and CH3NH3PbI3 (a = 8.78 Å, c = 12.70 Å), since the volume of unit cell increases after each conversion stage, as discussed by Sutherland et. al.32.

Figure 1
figure 1

Elemental composition and structural analyses of films after each conversion step. (a) EDS and (b) XRD of films at each step. Remaining PbI2 are marked with #. The inset shows the thickness of films.

The elemental analysis of the films performed by EDS, Fig. 1a, shows the presence of expected elements for each material, PbS, PbI2, and CH3NH3PbI3. Some small amounts of O were also detected, probably related to post-oxidation of the PbS film deposited at room temperature, and/or to adsorbed water.

XRD of the PbS film, deposited as shown in the Fig. 2a, reveals that it is completely amorphous without any signal from microcrystals (Fig. 1b), due to presence of just a wide band in the spectrum, which is in agreement with previously published results36. After treatment with I2 gas (Fig. 2b), the PbS film was completely converted into PbI2 (blue curve in Fig. 1b), as confirmed by standard PbI2 powder diffraction catalogued JCPDS 07-0235. The as-converted perovskite film (as shown in Fig. 2c) has XRD peaks corresponding to the planes (002), (110), (112), (211), (202), (004), (220), (222), (310), (024), (312), (224), (330) and (314), red curve in Fig. 1b. All these planes agree with previous published results46,47 and confirm the efficiency of our approach. Three peaks with low intensity and marked with # are associated with PbI2 crystals, which were not completely converted into perovskite. It is well known that the conversion of PbI2 into perovskite through post-treatment with MAI leaves a small percentage of unconverted PbI2. This has been attributed to the quick growth of a thick shell of perovskite when using the dipping technique in methylammonium iodide, hindering total conversion48. However, there is some debate in the literature about the detrimental effect of the remaining PbI2 in perovskite film, and some studies have reported even better devices if an appropriate amount of PbI2 is present28,48,49,50.

Figure 2
figure 2

Schematic diagrams for the conversion of PbS into perovskite (CH3NH3PbI3): (a) PbS thin film deposited by sputtering on glass and Si substrates, (b) PbS film exposed to sublimated I2 for its conversion into PbI2, and (c) dipping the PbI2 film into MAI solution for conversion into perovskite.

Figure 3 shown typical SEM and AFM images of films. It can be seen from SEM images, that film morphology undergoes a substantial transformation after each conversion step. The grain size increases significantly, passing from small amorphous grains (~50 nm) on PbS (Fig. 3a) to crystalline pancake-shaped grains on PbI2 (Fig. 3b), and then to cuboid crystals on perovskite (Fig. 3c and inset).

Figure 3
figure 3

Morphological analyses of thin films. (a,b and c) are 20 × 20 µm2 SEM micrographs of PbS, PbI2, and CH3NH3PbI3 perovskite thin films, respectively. (d,e and f) are AFM micrographs in a 10 × 10 µm2 window of the same films. The inset on c) is a detail of the cuboid shape of a CH3NH3PbI3 perovskite crystal, the scale bar represents 2 µm.

Notable morphological variations also were seen through the AFM images, Fig. 3d–f. The increase in grain size was quantified through average roughness (Ra) of the films, which was accessed by AFM measurements. The obtained values for Ra were 2.28 nm, 18.6 nm, and 71.1 nm, for PbS, PbI2, and perovskite films, respectively.

One of the main improvements proposed by this approach concerns to the complete substrate coverage and film homogeneity. To this end, we performed wide-area SEM (40 × 40 µm2) and optical (100 × 70 µm2) images from many points of the films and the Fig. 4 show typical images. It can be seen from the Fig. 4a that films present a homogenous crystal size distribution and connected crystals, which is essential to device production, besides, the films have no evidence of pinholes or cracks. The optical images, Fig. 4b, also confirm the quality of deposited films. In comparation with other popular techniques, like spin-coating, the films here synthesized presented higher surface uniformity and surface coverage.

Figure 4
figure 4

Large-area images of perovskite film. (a) (40 × 40µm2) SEM and (b) (100 × 70 µm2) optical. The scale bars represent 10 µm.

Vibrational and Optical Properties

Figure 5a reveals the FTIR spectral features of films in the wavenumber range 400–4000 cm−1. PbS and PbI2 have presented no IR peaks, since they are transparent in this region of wavelength. Just the asymmetric stretching of CO2 and a peak associated with the silicon substrate (indicated by vertical grey colour bars) are present in the spectra. Characteristic CH3NH3PbI3 IR peaks were detected in the range from 3000–3200 cm−1 (Fig. 5a), which were attributed to symmetric NH3+ and CH3 stretching modes. The absorption features in the 1400–1470 cm−1 range are assigned to symmetric NH3+ bending and asymmetric CH3 bending, and the CH3-NH3+ rocking and C-N stretching modes are in the 900–1250 cm−1 range, as shown in Fig. 5a. All of these peaks agree with results previously reported51,52 and demonstrate that the proposed conversion process is highly efficient.

Figure 5
figure 5

Vibration spectroscopy of films. (a) FTIR spectra in the wavenumber range 400 to 4000 cm−1 and (b) Raman in the 50 to 500 cm−1 wavenumber range.

The Raman spectroscopy for all films, Fig. 5b, was performed at room temperature and ambient conditions using the 532 nm excitation line of an argon laser. Aiming to avoid damage to the samples, a low laser power was applied in the measures (13 µW), which is four orders of magnitude lower than the total laser power.

Since PbS has a weak Raman signal, a precise measure is a challenger task, moreover using a low laser power. The expected Raman peaks for the PbS should be at 154, 205 and 454 cm−153,54. However, due to low scattering efficiency for excitation with 532 nm (2.33 eV), just a broad band centred at 206 cm−1 was detected, which has been assigned to first order longitudinal-optical (LO) phonons53,54. Since the PbS thin film were kept under room conditions and its surface is very sensitive to oxidation, the Raman spectrum of PbS also show bands at 77, 134 cm−1, which were attribute to surface oxidation (PbO and PbSO4)54,55. The wide shoulder in the range of 300–450 cm−1 is accounted to the glass substrate.

The Raman spectrum of the as converted PbI2 shows bands at 72, 94, 109, 165 and 214 cm−1 (blue curve in the Fig. 5b). As discussed elsewhere56,57,58,59 the peaks at 72, 94, 109, 165 cm−1 are assigned to the four allowed LO and traverse optical phonon (TO) modes \({E}_{2}^{1}(TO),{A}_{1}^{1}(TO),{A}_{1}^{2}(LO)\) and \(2{E}_{2}^{1}(TO)\), respectively. The band at 214 cm−1 is attributed to the overtone of the 109 cm−1 band60. These results also indicate that PbS was completely converted into PbI2 after treatment with iodine.

The Raman spectrum of the perovskite film (red curve in the Fig. 5b) shows some features at 75, 90, and 105 cm−1, followed by some structures in the 105–500 cm−1 range which are probably associated with noise since the measurements were performed at a very low power to avoid artifacts. The origin of Raman signals from perovskite films are still under debate, since the few reported studies are contradictory or not well understood. The problem is related to degradation due to laser heating61. Quarti et al.62 and Park et al.63 attributed peaks above to the vibrational modes of inorganic octahedral PbI6, which is part of the perovskite structure, based on comparison between density functional theory (DFT)-simulated Raman spectra and experimental results.

Interesting results were obtained from optical measures for each conversion step, Fig. 6. Aiming to get good optical measurements, the deposition time for PbS thin films was 360 minutes, which produced films of approximately 750 nm. Thus, the thickness of PbI2 and perovskite films after the conversion becomes 1.3 and 2.3 µm, respectively. The band gap of deposited films was determined using the Tauc’s relation, Equation (1)64:

$$\alpha h\nu =C{(h\nu -{E}_{g})}^{n},$$

where α is the absorption coefficient, E g is the band gap, is the incident photon energy and C is a constant.

Figure 6
figure 6

Band-gap calculation for the films at each step. (a) Tauc’s plot (where α = absorption coefficient, h = Plank’s constant and ν = frequency) indicating the band-gap of the film (dashed lines). The insets are pictures of the samples after each conversion step. (b) Absorption and photoluminescence of the perovskite film as a function of wavelength.

In the range of high absorption coefficient (α > 104 cm−1), the band gap of PbS films was 2.66 eV (Fig. 6a). This is a very wide band gap considering that monocrystalline PbS has a band gap of only 0.41 eV60. The reason for this sizeable discrepancy is because our films were deposited at room temperature and are amorphous (black curve in the Fig. 1b), which promote tail states in the band gap onset. However, the obtained results confirm to what has previously been reported in the literature36,65. From our own experience, PbS Films deposited at 300 °C were crystalline with a band gap of 0.72 eV (not shown here).

After the conversion of amorphous PbS into PbI2 is possible to see a huge change in the film colour, which change from semi-transparent to completely yellow (insets in Fig. 6a). The colour change is associated with a decrease in the band gap, which was reduced from 2.66 to 2.36 eV, the expected value for this material66. This reduction in the band gap reinforces the results obtained from XRD measurements about the complete structural transformation from PbS to PbI2.

After the conversion to perovskite, the films experienced another decrease in the band gap, attaining 1.51 eV13,27,67. This optical change can be easily seen by change in the film colour, that now went from yellow to dark brown (insets in Fig. 6a). The photoluminescence spectrum of the perovskite film at room temperature (Fig. 6b) showed a peak centred at 780 nm (~1.58 eV), which is located at the onset of the absorption coefficient attributed to the band gap, also in agreement with previous reports12. Thus, these optical measurements showed that this approach produce perovskite thin films with appropriate optical characteristics for solar cells application, as previously proposed.


In summary, we demonstrated a new method to produce perovskite films using sputtering. At the first step, an amorphous PbS thin film is deposited, which is then converted into PbI2 through treatment with iodine. The PbI2 film was subsequently converted into a CH3NH3PbI3 perovskite film by dipping it into methylammonium iodide. The complete process was performed at a temperature less than 100 °C, allowing its use in a great variety of substrates. The efficiency of the conversion processes from PbS to PbI2 and finally to CH3NH3PbI3 was demonstrated through chemical analyses using EDS, photoluminescence, X-ray diffraction, FTIR, and Raman spectroscopy. The main advantages introduced by this method were the production of perovskite films with high surface uniformity over large areas and films with high optical absorption on visible spectrum. Besides, this route can act as an alternative to the conventional chemical bench approach, since sputtering is an easy, cost-effective, and well-known technique for thin film deposition. Additionally, its implementation in large-area and large-scale production is already consolidated in the electronic market.


Sample preparation

The perovskite films were deposited in three steps, as shown in Fig. 2. Prior to deposition, the substrates were sonicated in a soap solution in water, acetone, and ethanol, for 15 minutes each. The cleaning process was finished with UV-ozone treatment for 30 minutes at 70 °C, to remove any organic contamination. The base pressure for deposition was 4 × 10−6 mbar. Firstly, a PbS target (Stanford Advanced Materials) of 99.9% purity was sputtered in a rf-sputtering system (Leybold-Heraus Z400) at a bias of −1000 V, under argon (99.99999% purity) pressure of 3 × 10−3 mbar (Fig. 2a). All films were deposited on double-side polished crystalline silicon and glass substrates (1.25 × 1.25 cm2) at room temperature. The deposition rate was approximately 2.0 nm/min, and there was no intentional heating during the deposition time, which were 120 and 360 min. However, during the deposition the temperature spontaneously reached approximately 50 °C.

The conversion of the PbS films into perovskites was done in two steps. First, the PbS films were placed inside a sealed enclosure together with approximately 100 mg of solid iodine (I2) (Sigma-Aldrich) with 99.99% purity. Due to the natural sublimation process at room temperature, a vapor pressure of I2 is established inside the container. It reacts with the PbS film (Fig. 2b), converting it into PbI2 after 60 hours, as probed through X-ray diffraction (XRD). This conversion can be catalyzed by temperature, which would reduce the reaction time, but in this report, we will carry out the reaction at room temperature. The last step consisted of dipping the PbI2 thin film into a solution of 10 mg/ml of MAI in isopropyl alcohol heated to 50 °C for 5 minutes, as shown in Fig. 2c. After conversion, the film was annealed at 100 °C, for 30 minutes, in an open furnace. During all synthesis, the relative humidity was in the 50 to 70% range.


Optical properties were extracted from a UV/VIS/NIR Spectrophotometer (Lambda 9, Perkin-Elmer) in the wavelength range 190 to 3200 nm (6.53 to 0.39 eV). Vibrational properties were obtained using Fourier transform infrared spectroscopy (FTIR) in transmittance mode, in the wavenumber range 400 to 4000 cm−1 (Jasco 6100). Raman scattering was carried out in a confocal micro-Raman configuration (XploRA, Horiba), in the wavenumber range 50 to 500 cm−1. XRD was performed using a D8 Advanced system (Bruker) equipped with a Cu (0.15418 nm) X-ray source, operating at 40 kV and 40 mA. The Bragg–Brentano θ–2θ configuration was used, with incidence angle of 1°, an integration time of 10 s, and a step of 0.02°. Atomic force microscopy (AFM) images were obtained for superficial analysis (easyScan 2 Flex, nanoSurf) using a large area (100 × 100 µm2) scanner in tapping mode. The tip radius was smaller than 10 nm. Surface morphology measurements were also performed using Scanning Electron Microscopy (SEM) (Phenon, FEI), with an accelerating voltage of 5 kV in secondary electron scattering mode. For these analyses, the samples were deposited on double-sided polished c-silicon wafers. Energy-dispersive X-ray spectroscopy (EDS) was performed for elemental analyses using a FIB-SEM Nova 200 Nanolab system from FEI, with 10 kV accelerating voltage. The thickness of the films was measured in a DEKTAK 150 Profilometer by Veeco. All measurements were performed immediately after the films were prepared, as they degrade with exposure to moisture, similar to those prepared by solution processes.


  1. Grätzel, M. The light and shade of perovskite solar cells. Nat. Mater. 13, 838–842 (2014).

    Article  PubMed  Google Scholar 

  2. Song, Z., Watthage, S. C., Phillips, A. B. & Heben, M. J. Pathways toward high-performance perovskite solar cells: review of recent advances in organo-metal halide perovskites for photovoltaic applications. J. Photonics Energy 6, 22001 (2016).

    Article  Google Scholar 

  3. Maculan, G. et al. CH3NH3PbCl3 Single Crystals: Inverse Temperature Crystallization and Visible-Blind UV-Photodetector. J. Phys. Chem. Lett. 6, 3781–3786 (2015).

    CAS  Article  PubMed  Google Scholar 

  4. Kumawat, N. K. et al. Band Gap Tuning of CH3NH3Pb(Br1– xCl x)3 Hybrid Perovskite for Blue Electroluminescence. ACS Appl. Mater. Interfaces 7, 13119–13124 (2015).

    Google Scholar 

  5. Brittman, S., Adhyaksa, G. W. P. & Garnett, E. C. The expanding world of hybrid perovskites: materials properties and emerging applications. MRS Commun. 5, 7–26 (2015).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  6. Stranks, S. D. et al. Electron-Hole Diffusion Lengths Exceeding 1 Micrometer in an Organometal Trihalide Perovskite Absorber. Science (80-.). 342, 341–344 (2013).

    CAS  Article  ADS  Google Scholar 

  7. Edri, E. et al. Elucidating the charge carrier separation and working mechanism of CH3NH3PbI3−xClx perovskite solar cells. Nat. Commun. 5, 3461 (2014).

    Article  PubMed  Google Scholar 

  8. Li, F. et al. Ambipolar solution-processed hybrid perovskite phototransistors. Nat. Commun. 6, 1–8 (2015).

    ADS  Google Scholar 

  9. Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal Halide Perovskites as Visible-Light Sensitizers for Photovoltaic Cells. J. Am. Chem. Soc. 131, 6050–6051 (2009).

    CAS  Article  PubMed  Google Scholar 

  10. NREL. Solar cell efficiency chart. National Center for Photovoltaics (2016). Available at: (Accessed: 23rd November 2016).

  11. Green, M. A., Emery, K., Hishikawa, Y., Warta, W. & Dunlop, E. D. Solar cell efficiency tables (version 47). Prog. Photovoltaics Res. Appl. 24, 3–11 (2016).

    Article  Google Scholar 

  12. Tavakoli, M. M. et al. Fabrication of efficient planar perovskite solar cells using a one-step chemical vapor deposition method. Sci. Rep. 5, 14083 (2015).

    Article  PubMed  PubMed Central  ADS  Google Scholar 

  13. Hodes, G. Perovskite-Based Solar Cells. Science (80-.). 342, 317–318 (2013).

    CAS  Article  ADS  Google Scholar 

  14. Zhang, W. et al. Enhanced optoelectronic quality of perovskite thin films with hypophosphorous acid for planar heterojunction solar cells. Nat. Commun. 6, 10030 (2015).

    CAS  Article  PubMed  PubMed Central  ADS  Google Scholar 

  15. Burschka, J. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–320 (2013).

    CAS  Article  PubMed  ADS  Google Scholar 

  16. Fan, P. et al. High-performance perovskite CH3NH3PbI3 thin films for solar cells prepared by single-source physical vapour deposition. Sci. Rep. 6, 29910 (2016).

    CAS  Article  PubMed  PubMed Central  ADS  Google Scholar 

  17. Carnie, M. J. et al. A one-step low temperature processing route for organolead halide perovskite solar cells. Chem. Commun. 49, 7893 (2013).

    CAS  Article  Google Scholar 

  18. Wang, F. et al. Influence of annealing temperature on the crystallization and ferroelectricity of perovskite CH3NH3PbI3 film. Appl. Surf. Sci. 357, 391–396 (2015).

    CAS  Article  ADS  Google Scholar 

  19. Deng, Y. et al. Scalable fabrication of efficient organolead trihalide perovskite solar cells with doctor-bladed active layers. Energy Environ. Sci. 8, 1544–1550 (2015).

    CAS  Article  Google Scholar 

  20. Ono, L. K., Leyden, M. R., Wang, S. & Qi, Y. Organometal Halide Perovskite Thin Films and Solar Cells by Vapor Deposition. J. Mater. Chem. A 4, 6693–6713 (2016).

    CAS  Article  Google Scholar 

  21. Ren, X. et al. Reaction temperature modulating crystal grain size and optoelectronic properties of perovskite film for solar cell application. Nanoscale 8, 3816–3822 (2016).

    CAS  Article  PubMed  ADS  Google Scholar 

  22. Jain, S. M. et al. Vapor phase conversion of PbI2 to CH3NH3PbI3: spectroscopic evidence for formation of an intermediate phase. J. Mater. Chem. A 4, 2630–2642 (2016).

    CAS  Article  Google Scholar 

  23. Lee, M. M., Teuscher, J., Miyasaka, T., Murakami, T. N. & Snaith, H. J. Efficient Hybrid Solar Cells Based on Meso-Superstructured Organometal Halide Perovskites. Science (80-.). 338, 643–647 (2012).

    CAS  Article  ADS  Google Scholar 

  24. Chen, C., Cheng, Y., Dai, Q. & Song, H. Radio Frequency Magnetron Sputtering Deposition of TiO2 Thin Films and Their Perovskite Solar Cell Applications. Sci. Rep. 5, 17684 (2015).

    CAS  Article  PubMed  PubMed Central  ADS  Google Scholar 

  25. Im, J.-H., Jang, I.-H., Pellet, N., Grätzel, M. & Park, N.-G. Growth of CH3NH3PbI3 cuboids with controlled size for high-efficiency perovskite solar cells. Nat. Nanotechnol. 9, 927–932 (2014).

    CAS  Article  PubMed  ADS  Google Scholar 

  26. Cohen, B.-E. & Etgar, L. Parameters that control and influence the organo-metal halide perovskite crystallization and morphology. Front. Optoelectron. 9, 44–52 (2016).

    Article  Google Scholar 

  27. Li, X. et al. A vacuum flash-assisted solution process for high-efficiency large-area perovskite solar cells. Science (80-.). 353, 58–62 (2016).

    CAS  Article  ADS  Google Scholar 

  28. Wu, Y. et al. Retarding the crystallization of PbI2 for highly reproducible planar-structured perovskite solar cells via sequential deposition. Energy Environ. Sci. 7, 2934 (2014).

    CAS  Article  Google Scholar 

  29. Wang, C. et al. Degradation of co-evaporated perovskite thin film in air. Chem. Phys. Lett. 649, 151–155 (2016).

    CAS  Article  ADS  Google Scholar 

  30. Liang, G.-X., Fan, P., Luo, J.-T., Gu, D. & Zheng, Z.-H. A promising unisource thermal evaporation for in situ fabrication of organolead halide perovskite CH3NH3PbI3 thin film. Prog. Photovoltaics Res. Appl. 23, 1901–1907 (2015).

    CAS  Article  Google Scholar 

  31. Liu, M., Johnston, M. B. & Snaith, H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395–398 (2013).

    CAS  Article  PubMed  ADS  Google Scholar 

  32. Sutherland, B. R. et al. Perovskite thin films via atomic layer deposition. Adv. Mater. 27, 53–58 (2015).

    CAS  Article  PubMed  Google Scholar 

  33. Puurunen, R. L. Surface chemistry of atomic layer deposition: A case study for the trimethylaluminum/water process. J. Appl. Phys. 97, 121301 (2005).

    Article  ADS  Google Scholar 

  34. George, S. M. Atomic Layer Deposition: An Overview. Chem. Rev. 110, 111–131 (2010).

    CAS  Article  PubMed  Google Scholar 

  35. Jiang, J. et al. Hydrogen Sulfide—Mechanisms of Toxicity and Development of an Antidote. Sci. Rep. 6, 20831 (2016).

    CAS  Article  PubMed  PubMed Central  ADS  Google Scholar 

  36. Azadi Motlagh, Z. & Azim Araghi, M. E. Effect of annealing temperature on optical and electrical properties of lead sulfide thin films. Mater. Sci. Semicond. Process. 40, 701–707 (2015).

    CAS  Article  Google Scholar 

  37. Saliba, M. et al. Cesium-containing triple cation perovskite solar cells: improved stability, reproducibility and high efficiency. Energy Environ. Sci. 9, 1989–1997 (2016).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  38. Sutton, R. J. et al. Bandgap-Tunable Cesium Lead Halide Perovskites with High Thermal Stability for Efficient Solar Cells. Adv. Energy Mater. 6, 1502458 (2016).

    Article  Google Scholar 

  39. Seeman, J. M. Bias sputtering: its techniques and applications. Vacuum 17, 129–137 (1967).

    CAS  Article  ADS  Google Scholar 

  40. Kelly, P. & Arnell, R. Magnetron sputtering: a review of recent developments and applications. Vacuum 56, 159–172 (2000).

    CAS  Article  ADS  Google Scholar 

  41. Maurya, D., Sardarinejad, A. & Alameh, K. Recent Developments in R.F. Magnetron Sputtered Thin Films for pH Sensing Applications—An Overview. Coatings 4, 756–771 (2014).

    Article  Google Scholar 

  42. Griffith, M. J. et al. Roll-to-Roll Sputter Coating of Aluminum Cathodes for Large-Scale Fabrication of Organic Photovoltaic Devices. Energy Technol. 3, 428–436 (2015).

    CAS  Article  Google Scholar 

  43. Sun, X., Gao, K., Pang, X., Yang, H. & Volinsky, A. A. Annealing temperature effects on optical and photoelectric properties of sputtered indium-doped PbSe thin film. J. Mater. Sci. Mater. Electron. 26, 7873–7881 (2015).

    CAS  Article  Google Scholar 

  44. Pachlhofer, J. M. et al. Industrial-scale sputter deposition of molybdenum oxide thin films: Microstructure evolution and properties. J. Vac. Sci. Technol. A Vacuum, Surfaces, Film. 35, 21504 (2017).

    Article  Google Scholar 

  45. Zhang, H. et al. Tuning of Coupling and Surface Quality of PbS Nanocrystals via a Combined Ammonium Sulfide and Iodine Treatment. J. Phys. Chem. Lett. 7, 642–646 (2016).

    CAS  Article  PubMed  Google Scholar 

  46. Yu, J. et al. A high-performance self-powered broadband photodetector based on a CH3NH3PbI3 perovskite/ZnO nanorod array heterostructure. J. Mater. Chem. C 4, 7302–7308 (2016).

    CAS  Article  Google Scholar 

  47. Qiu, J. et al. All-solid-state hybrid solar cells based on a new organometal halide perovskite sensitizer and one-dimensional TiO2 nanowire arrays. Nanoscale 5, 3245 (2013).

    CAS  Article  PubMed  ADS  Google Scholar 

  48. Zheng, E. et al. PbI2-Based Dipping-Controlled Material Conversion for Compact Layer Free Perovskite Solar Cells. ACS Appl. Mater. Interfaces 7, 18156–18162 (2015).

    Google Scholar 

  49. Yella, A., Heiniger, L., Gao, P., Nazeeruddin, M. K. & Grätzel, M. Nanocrystalline Rutile Electron Extraction Layer Enables Low-Temperature Solution Processed Perovskite Photovoltaics with 13.7% Efficiency. Nano Lett. 14, 2591–2596 (2014).

    CAS  Article  PubMed  ADS  Google Scholar 

  50. Mao, P., Zhou, Q., Jin, Z., Li, H. & Wang, J. Efficiency-Enhanced Planar Perovskite Solar Cells via Isopropanol/Ethanol Mixed Solvent Process. ACS Appl. Mater. Interfaces 8, 23837–23843 (2016).

  51. Glaser, T. et al. Infrared Spectroscopic Study of Vibrational Modes in Methylammonium Lead Halide Perovskites. J. Phys. Chem. Lett. 6, 2913–2918 (2015).

    CAS  Article  PubMed  Google Scholar 

  52. Jeon, N. J. et al. Solvent engineering for high-performance inorganic-organic hybrid perovskite solar cells. Nat. Mater. 13, 1–7 (2014).

    MathSciNet  Article  ADS  Google Scholar 

  53. Smith, G. D., Firth, S., Clark, R. J. H. & Cardona, M. First- and second-order Raman spectra of galena (PbS). J. Appl. Phys. 92, 4375–4380 (2002).

    CAS  Article  ADS  Google Scholar 

  54. Bierman, M. J., Lau, Y. K. A. & Jin, S. Hyperbranched PbS and PbSe nanowires and the effect of hydrogen gas on their synthesis. Nano Lett. 7, 2907–2912 (2007).

    CAS  Article  PubMed  ADS  Google Scholar 

  55. Shapter, J. G., Brooker, M. H. & Skinner, W. M. Observation of the oxidation of galena using Raman spectroscopy. Int. J. Miner. Process. 60, 199–211 (2000).

    CAS  Article  Google Scholar 

  56. Preda, N., Mihut, L., Baibarac, M., Baltog, I. & Lefrant, S. A distinctive signature in the Raman and photoluminescence spectra of intercalated PbI 2. J. Phys. Condens. Matter 18, 8899–8912 (2006).

    CAS  Article  ADS  Google Scholar 

  57. Capozzi, V. et al. Raman scattering in PbI2. Nuovo Cim. B Ser. 11 39, 556–560 (1977).

    Article  Google Scholar 

  58. Khilji, M. Y., Sherman, W. F. & Wilkinson, G. R. Raman study of three polytypes of PbI2. J. Raman Spectrosc. 13, 127–133 (1982).

    CAS  Article  ADS  Google Scholar 

  59. Preda, N., Mihut, L., Baibarac, M. & Baltog, I. Intercalation of layered metal iodides with pyridine evidenced by Raman spectroscopy. Acta Phys. Pol. A 116, 81–83 (2009).

    CAS  Article  ADS  Google Scholar 

  60. Wang, Y., Suna, A., Mahler, W. & Kasowski, R. PbS in polymers. From molecules to bulk solids. J. Chem. Phys. 87, 7315–7322 (1987).

    CAS  Google Scholar 

  61. Zhou, Y., Garces, H. F. & Padture, N. P. Challenges in the ambient Raman spectroscopy characterization of methylammonium lead triiodide perovskite thin films. Front. Optoelectron. 9, 81–86 (2016).

    Article  Google Scholar 

  62. Quarti, C. et al. The Raman Spectrum of the CH3NH3PbI3 Hybrid Perovskite: Interplay of Theory and Experiment. J. Phys. Chem. Lett. 5, 279–284 (2014).

    CAS  Article  PubMed  Google Scholar 

  63. Park, B. et al. Resonance Raman and Excitation Energy Dependent Charge Transfer Mechanism in Halide-Substituted Hybrid Perovskite Solar Cells. ACS Nano 9, 2088–2101 (2015).

    CAS  Article  PubMed  Google Scholar 

  64. Tauc, J. Optical properties and electronic structure of amorphous Ge and Si. Mater. Res. Bull. 3, 37–46 (1968).

    CAS  Article  Google Scholar 

  65. Sun, X., Gao, K., Pang, X., Yang, H. & Volinsky, A. A. Study on the growth mechanism and optical properties of sputtered lead selenide thin films. Appl. Surf. Sci. 356, 978–985 (2015).

    CAS  Article  ADS  Google Scholar 

  66. Roy, A., Sarma, D. D. & Sood, A. K. Spectroscopic studies on quantum dots of PbI2. Spectrochim. Acta Part A Mol. Spectrosc. 48, 1779–1787 (1992).

    Article  ADS  Google Scholar 

  67. Qaid, S. M. H. et al. Band-gap tuning of lead halide perovskite using a single step spin-coating deposition process. Mater. Lett. 164, 498–501 (2016).

    CAS  Article  Google Scholar 

Download references


J. M. C. Silva Filho acknowledges CNPq (grant 165756/2014-4). V. A. Ermakov acknowledges FAPESP (grant 2013/26385-6). F. C. Marques acknowledges CNPq (grants 407887/2013-0 and 554336/2010-3), FAPESP (grant 2012/10127-5) and INES/CNPq (grants 554336/2010-3 and 465423/2014-0).

Author information




J.M.C.S.F. performed the experiments and wrote the manuscript. J.M.C.S.F. and F.C.M. participated in the research design and analysed the data. F.C.M. and V.A.E. participated in writing the manuscript. All authors read and approved the final version of the manuscript.

Corresponding author

Correspondence to José Maria Clemente da Silva Filho.

Ethics declarations

Competing Interests

The authors declare that they have no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Silva Filho, J.M.C., Ermakov, V.A. & Marques, F.C. Perovskite Thin Film Synthesised from Sputtered Lead Sulphide. Sci Rep 8, 1563 (2018).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing