Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Spin–orbit torque driven by a planar Hall current

Abstract

Spin–orbit torques (SOTs) in multilayers of ferromagnetic (FM) and non-magnetic (NM) metals can manipulate the magnetization of the FM layer efficiently. This is employed, for example, in non-volatile magnetic memories for energy-efficient mobile electronics1,2 and spin torque nano-oscillators3,4,5,6,7 for neuromorphic computing8. Recently, spin torque nano-oscillators also found use in microwave-assisted magnetic recording, which enables ultrahigh-capacity hard disk drives9. Most SOT devices employ spin Hall10,11 and Rashba12 effects, which originate from spin–orbit coupling within the NM layer and at the FM/NM interfaces, respectively. Recently, SOTs generated by the anomalous Hall effect in FM/NM/FM multilayers were predicted13 and experimentally realized14. The control of SOTs through crystal symmetry was demonstrated as well15. Understanding all the types of SOTs that can arise in magnetic multilayers is needed for a formulation of a comprehensive SOT theory and for engineering practical SOT devices. Here we show that a spin-polarized electric current known to give rise to anisotropic magnetoresistance (AMR) and the planar Hall effect (PHE) in a FM16 can additionally generate large antidamping SOTs with an unusual angular symmetry in NM1/FM/NM2 multilayers. This effect can be described by a recently proposed magnonic mechanism17. Our measurements reveal that this torque can be large in multilayers in which both spin Hall and Rashba torques are negligible. Furthermore, we demonstrate the operation of a spin torque nano-oscillator driven by this SOT. These findings significantly expand the class of materials that exhibit giant SOTs.

This is a preview of subscription content

Access options

Rent or Buy article

Get time limited or full article access on ReadCube.

from$8.99

All prices are NET prices.

Fig. 1: Sample geometry and ST-FMR measurements.
Fig. 2: Microwave generation.
Fig. 3: Angular symmetry and material dependence of SOTs.

Data availability

All data supporting the findings of this study are available within the article and the Supplementary Information and are available at the University of California Data Repository at https://doi.org/10.15146/R3H09M. All the data are available from the authors on request.

References

  1. 1.

    Miron, I. M. et al. Perpendicular switching of a single ferromagnetic layer induced by in-plane current injection. Nature 476, 189–193 (2011).

    CAS  Article  Google Scholar 

  2. 2.

    Liu, L. et al. Spin-torque switching with the giant spin Hall effect of tantalum. Science 336, 555–558 (2012).

    CAS  Article  Google Scholar 

  3. 3.

    Slavin, A. & Tiberkevich, V. Nonlinear auto-oscillator theory of microwave generation by spin-polarized current. IEEE Trans. Magn. 45, 1875–1918 (2009).

    CAS  Article  Google Scholar 

  4. 4.

    Demidov, V. E. et al. Magnetic nano-oscillator driven by pure spin current. Nat. Mater. 11, 1028–1031 (2012).

    CAS  Article  Google Scholar 

  5. 5.

    Duan, Z. et al. Nanowire spin torque oscillator driven by spin orbit torques. Nat. Commun. 5, 5616 (2014).

    CAS  Article  Google Scholar 

  6. 6.

    Collet, M. et al. Generation of coherent spin-wave modes in yttrium iron garnet microdiscs by spin–orbit torque. Nat. Commun. 7, 10377 (2016).

    CAS  Article  Google Scholar 

  7. 7.

    Awad, A. A. et al. Long-range mutual synchronization of spin Hall nano-oscillators. Nat. Phys. 13, 292–299 (2016).

    Article  Google Scholar 

  8. 8.

    Torrejon, J. et al. Neuromorphic computing with nanoscale spintronic oscillators. Nature 547, 428–431 (2017).

    CAS  Article  Google Scholar 

  9. 9.

    Western Digital unveils next-generation technology to preserve and access the next decade of big data (Western Digital, 2017); https://www.wdc.com/about-wd/newsroom/press-room/2017-10-11-western-digital-unveils-next-generation-technology-to-preserve-and-access-the-next-decade-of-big-data.html

  10. 10.

    Ando, K. et al. Electric manipulation of spin relaxation using the spin Hall effect. Phys. Rev. Lett. 101, 036601 (2008).

    CAS  Article  Google Scholar 

  11. 11.

    Sinova, J., Valenzuela, S. O., Wunderlich, J., Back, C. H. & Jungwirth, T. Spin Hall effects. Rev. Mod. Phys. 87, 1213–1260 (2015).

    Article  Google Scholar 

  12. 12.

    Manchon, A., Koo, H. C., Nitta, J., Frolov, S. M. & Duine, R. A. New perspectives for Rashba spin–orbit coupling. Nat. Mater. 14, 871–882 (2015).

    CAS  Article  Google Scholar 

  13. 13.

    Taniguchi, T., Grollier, J. & Stiles, M. D. Spin-transfer torques generated by the anomalous Hall effect and anisotropic magnetoresistance. Phys. Rev. Appl. 3, 044001 (2015).

    Article  Google Scholar 

  14. 14.

    Gibbons, J. D., MacNeill, D., Buhrman, R. A. & Ralph, D. C. Reorientable spin direction for spin current produced by the anomalous Hall effect. Phys. Rev. Appl. 9, 064033 (2018).

    Article  Google Scholar 

  15. 15.

    MacNeill, D. et al. Control of spin–orbit torques through crystal symmetry in WTe2/ferromagnet bilayers. Nat. Phys. 13, 300–305 (2016).

    Article  Google Scholar 

  16. 16.

    Kokado, S., Tsunoda, M., Harigaya, K. & Sakuma, A. Anisotropic magnetoresistance effects in Fe, Co, Ni, Fe4N, and half-metallic ferromagnet: a systematic analysis. J. Phys. Soc. Jpn 81, 024705 (2012).

    Article  Google Scholar 

  17. 17.

    Bender, S. A. & Tserkovnyak, Y. Thermally driven spin torques in layered magnetic insulators. Phys. Rev. B 93, 064418 (2016).

    Article  Google Scholar 

  18. 18.

    Mangin, S. et al. Current-induced magnetization reversal in nanopillars with perpendicular anisotropy. Nat. Mater. 5, 210–215 (2006).

    CAS  Article  Google Scholar 

  19. 19.

    Arora, M., Hübner, R., Suess, D., Heinrich, B. & Girt, E. Origin of perpendicular magnetic anisotropy in Co/Ni multilayers. Phys. Rev. B 96, 024401 (2017).

    Article  Google Scholar 

  20. 20.

    Gonçalves, A. M. et al. Spin torque ferromagnetic resonance with magnetic field modulation. Appl. Phys. Lett. 103, 172406 (2013).

    Article  Google Scholar 

  21. 21.

    Mosendz, O. et al. Detection and quantification of inverse spin Hall effect from spin pumping in permalloy/normal metal bilayers. Phys. Rev. B 82, 214403 (2010).

    Article  Google Scholar 

  22. 22.

    Garello, K. et al. Symmetry and magnitude of spin–orbit torques in ferromagnetic heterostructures. Nat. Nanotech. 8, 587–593 (2013).

    CAS  Article  Google Scholar 

  23. 23.

    Safranski, C. et al. Spin caloritronic nano-oscillator. Nat. Commun. 8, 117 (2017).

    CAS  Article  Google Scholar 

  24. 24.

    Demidov, V. E. et al. Chemical potential of quasi-equilibrium magnon gas driven by pure spin current. Nat. Commun. 8, 1579 (2017).

    CAS  Article  Google Scholar 

  25. 25.

    Du, C. et al. Control and local measurement of the spin chemical potential in a magnetic insulator. Science 357, 195–198 (2017).

    CAS  Article  Google Scholar 

  26. 26.

    Humphries, A. M. et al. Observation of spin–orbit effects with spin rotation symmetry. Nat. Commun. 8, 911 (2017).

    Article  Google Scholar 

  27. 27.

    Baek, S.-C. Spin currents and spin-orbit torques in ferromagnetic trilayers. Nat. Mater. 17, 509–513 (2018).

    CAS  Article  Google Scholar 

  28. 28.

    Mann, M. & Beach, G. S. D. Reduction of in-plane field required for spin–orbit torque magnetization reversal by insertion of Au spacer in Pt/Au/Co/Ni/Co/Ta. APL Mater. 5, 106104 (2017).

    Article  Google Scholar 

  29. 29.

    Ryu, K.-S., Thomas, L., Yang, S.-H. & Parkin, S. Chiral spin torque at magnetic domain walls. Nat. Nanotech. 8, 527–533 (2013).

    CAS  Article  Google Scholar 

  30. 30.

    Legrand, W. et al. Room-temperature current-induced generation and motion of sub-100 nm skyrmions. Nano Lett. 17, 2703–2712 (2017).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

We thank M. Arora and E. Girt for discussion on the Co/Ni multilayer growth. Work on the deposition of the magnetic multilayers was supported as part of the Spins and Heat in Nanoscale Electronic Systems (SHINES), an Energy Frontier Research Centre funded by the US Department of Energy, Office of Basic Energy Sciences under Award no. DE-SC0012670. Nanowire device fabrication was supported by the US Department of Energy, Office of Basic Energy Sciences under Award no. DE-SC0014467. Spin torque oscillator development was supported by the National Science Foundation under Award no. DMR-1610146. Work on the variable-angle ST-FMR set-up development was supported by the National Science Foundation under Award no. EFMA-1641989. ST-FMR characterization was supported by the Army Research Office under Award no. W911NF-16-1-0472. Work on the absorptive FMR and spin pumping measurements was supported by the Defence Threat Reduction Agency under Award no. HDTRA1-16-1-0025. Work on experiment design and SOT analysis was supported by the National Science Foundation under Award no. ECCS-1708885.

Author information

Affiliations

Authors

Contributions

E.A.M. deposited the magnetic multilayers, and performed the resistivity, absorptive FMR and spin pumping measurements. C.S. and E.A.M. fabricated the nanowire devices, and performed the ST-FMR and spin torque oscillator measurements. I.N.K. designed the experiment and performed the SOT analysis. All the authors analysed the data and co-wrote the paper.

Corresponding author

Correspondence to Ilya N. Krivorotov.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figures 1–7, Supplementary Notes 1–9

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Safranski, C., Montoya, E.A. & Krivorotov, I.N. Spin–orbit torque driven by a planar Hall current. Nature Nanotech 14, 27–30 (2019). https://doi.org/10.1038/s41565-018-0282-0

Download citation

Further reading

Search

Quick links

Find nanotechnology articles, nanomaterial data and patents all in one place. Visit Nano by Nature Research