The breaking of symmetry across an oxide heterostructure causes the electronic orbitals to be reconstructed at the interface into energy states that are different from their bulk counterparts1. The detailed nature of the orbital reconstruction critically affects the spatial confinement and the physical properties of the electrons occupying the interfacial orbitals2,3,4. Using an example of two-dimensional electron liquids forming at LaAlO3/SrTiO3 interfaces5,6 with different crystal symmetry, we show that the selective orbital occupation and spatial quantum confinement of electrons can be resolved with subnanometre resolution using inline electron holography. For the standard (001) interface, the charge density map obtained by inline electron holography shows that the two-dimensional electron liquid is confined to the interface with narrow spatial extension (~1.0 ± 0.3 nm in the half width). On the other hand, the two-dimensional electron liquid formed at the (111) interface shows a much broader spatial extension (~3.3 ± 0.3 nm) with the maximum density located ~2.4 nm away from the interface, in excellent agreement with density functional theory calculations.
Subscribe to Journal
Get full journal access for 1 year
only $14.08 per issue
All prices are NET prices.
VAT will be added later in the checkout.
Rent or Buy article
Get time limited or full article access on ReadCube.
All prices are NET prices.
Chakhalian, J. et al. Orbital reconstruction and covalent bonding at an oxide interface. Science 318, 1114–1117 (2007).
Okamoto, S. & Millis, A. J. Electronic reconstruction at an interface between a Mott insulator and a band insulator. Nature 428, 630–633 (2004).
Mannhart, J. & Schlom, D. G. Oxide interfaces—An opportunity for electronics. Science 327, 1607–1611 (2010).
Zubko, P. et al. Interface physics in complex oxide heterostructures. Annu. Rev. Condens. Matter Phys. 2, 141–165 (2011).
Ohtomo, A. & Hwang, H. A high-mobility electron gas at the LaAlO3/SrTiO3 heterointerface. Nature 427, 423–426 (2004).
Jang, H. W. et al. Metallic and insulating oxide interfaces controlled by electronic correlations. Science 331, 886–889 (2011).
Hwang, H. Y. et al. Emergent phenomena at oxide interfaces. Nat. Mater. 11, 103–113 (2012).
Breitschaft, M. et al. Two-dimensional electron liquid state at LaAlO3–SrTiO3 interfaces. Phys. Rev. B 81, 153414 (2010).
Salluzzo, M. et al. Orbital reconstruction and the two-dimensional electron gas at the LaAlO3/SrTiO3 interface. Phys. Rev. Lett. 102, 166804 (2009).
Delugas, P. et al. Spontaneous 2-dimensional carrier confinement at the n-type SrTiO3/LaAlO3 interface. Phys. Rev. Lett. 106, 166807 (2011).
Doennig, D., Pickett, W. E. & Pentcheva, R. Massive symmetry breaking in LaAlO3/SrTiO3 (111) quantum wells: A three-orbital strongly correlated generalization of graphene. Phys. Rev. Lett. 111, 126804 (2013).
Reyren, N. et al. Superconducting interfaces between insulating oxides. Science 317, 1196–1199 (2007).
Caviglia, A. et al. Tunable Rashba spin–orbit interaction at oxide interfaces. Phys. Rev. Lett. 104, 126803 (2010).
Brinkman, A. et al. Magnetic effects at the interface between non-magnetic oxides. Nat. Mater. 6, 493–496 (2007).
Pesquera, D. et al. Two-dimensional electron gases at LaAlO3/SrTiO3 interfaces: Orbital symmetry and hierarchy engineered by crystal orientation. Phys. Rev. Lett. 113, 156802 (2014).
McKeown Walker, S. et al. Control of a two-dimensional electron gas on SrTiO3(111) by atomic oxygen. Phys. Rev. Lett. 113, 177601 (2014).
Herranz, G. et al. Engineering two-dimensional superconductivity and Rashba spin–orbit coupling in LaAlO3/SrTiO3 quantum wells by selective orbital occupancy. Nat. Commun. 6, 6028 (2015).
Berner, G. et al. Direct k-space mapping of the electronic structure in an oxide–oxide interface. Phy. Rev. Lett. 110, 247601 (2013).
Basletic, M. et al. Mapping the spatial distribution of charge carriers in LaAlO3/SrTiO3 heterostructures. Nat. Mater. 7, 621–625 (2008).
Huang, B.-C. et al. Mapping band alignment across complex oxide heterointerfaces. Phys. Rev. Lett. 109, 246807 (2012).
Koch, C. T. & Lubk, A. Off-axis and inline electron holography: A quantitative comparison. Ultramicroscopy 110, 460–471 (2010).
Midgley, Pa & Dunin-Borkowski, R. E. Electron tomography and holography in materials science. Nat. Mater. 8, 271–280 (2009).
Pentcheva, R. & Pickett, W. E. Avoiding the polarization catastrophe in LaAlO3 overlayers on SrTiO3 (001) through polar distortion. Phys. Rev. Lett. 102, 107602 (2009).
Pauli, S. A. et al. Evolution of the interfacial structure of LaAlO3 on SrTiO3. Phys. Rev. Lett. 106, 036101 (2011).
Cantoni, C. et al. Electron transfer and ionic displacements at the origin of the 2D electron gas at the LAO/STO interface: Direct measurements with atomic-column spatial resolution. Adv. Mater. 24, 3952–3957 (2012).
Cancellieri, C. et al. Electrostriction at the LaAlO3/SrTiO3 interface. Phys. Rev. Lett. 107, 056102 (2011).
Yu, L. & Zunger, A. A polarity induced defect mechanism for conductivity and magnetism at polar–nonpolar oxide interfaces. Nat. Commun. 5, 5118 (2015).
Hernandez, T. et al. Localization of two-dimensional electron gas in LaAlO3/SrTiO3 heterostructures. Phys. Rev. B 85, 161407(R) (2012).
Popovic, Z. S. et al. Origin of the two-dimensional electron gas carrier density at the LaAlO3 on SrTiO3 interface. Phys. Rev. Lett. 101, 256801 (2008).
This work was supported by AFOSR Asian Office of Aerospace Research and Development (AOARD) under grant number FA2386-15-1-4046 (S.H.O. and C.B.E.) and AFOSR under grant number FA9550-15-1-0334 (C.B.E.). Research at SKKU was supported by the Creative Materials Discovery Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Science, the ICT and Future Planning (NRF-2015M3D1A1070672) (S.H.O.), an NRF grant funded by the Korean government (NRF-2015R1A2A2A01007904) (S.H.O.) and by the Ministryof Trade, Industry & Energy (MOTIE, Korea) under Industrial Technology Innovation Program (10080654) (S.H.O.). K.S. and S.-Y.C. acknowledge the support of the Fundamental Research of the Korean Institute of Materials Science (KIMS-PNK5260) and the Global Frontier Hybrid Interface Materials of the NRF funded by Korea Government (2013M3A6B1078872). Research at the University of Nebraska was supported by NSF MRSEC (grant no. DMR-420645). C.T.K. acknowledges support by the German Research Foundation (DFG grant KO 2911/12-1).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Song, K., Ryu, S., Lee, H. et al. Direct imaging of the electron liquid at oxide interfaces. Nature Nanotech 13, 198–203 (2018). https://doi.org/10.1038/s41565-017-0040-8
Physica E: Low-dimensional Systems and Nanostructures (2020)
Nano Select (2020)
Prediction of orientation relationships and interface structures between α-, β-, γ-FeSi2 and Si phases
Acta Crystallographica Section B Structural Science, Crystal Engineering and Materials (2020)
Probing Charge Accumulation at SrMnO3/SrTiO3 Heterointerfaces via Advanced Electron Microscopy and Spectroscopy
ACS Nano (2020)
Interfacial enhancement for hydrogen radical transfer on hollow Cu2O/rGO nanohybrid with efficient catalytic reduction activity
Applied Catalysis A: General (2020)