Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Efficient hybrid colloidal quantum dot/organic solar cells mediated by near-infrared sensitizing small molecules


Solution-processed semiconductors are promising materials to realize optoelectronic devices that combine high performance with inexpensive manufacturing. In particular, the exploitation of colloidal quantum dots (CQDs) capable of harvesting infrared photons, in conjunction with visible-absorbing organic chromophores, has been demonstrated as an interesting route. Unfortunately, CQD/organic hybrid photovoltaics have been limited to power conversion efficiencies (PCEs) below 10% due to chemical mismatch and difficulties in facilitating charge collection. Here we devise a hybrid architecture that overcomes these limitations by introducing small molecules into the CQD/organic stacked structure. The small molecule complements CQD absorption and creates an exciton cascade with the host polymer, thus enabling efficient energy transfer and also promoting exciton dissociation at heterointerfaces. The resulting hybrid solar cells exhibit PCEs of 13.1% and retain over 80% of their initial PCE after 150 h of continuous operation unencapsulated, outperforming present air-processed solution-cast CQD/organic photovoltaics.

Access options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Hybrid CQD/polymer structure design strategy.
Fig. 2: Photo-induced carrier dynamics in CQD–organics hybrid films.
Fig. 3: Structure and spectral response of hybrid solar cells.
Fig. 4: Photovoltaic performance.

Data availability

The authors declare that the main data supporting the findings of this study are available within the article and its Supplementary Information. Extra data are available from the authors upon request.


  1. 1.

    Tan, H. et al. Efficient and stable solution-processed planar perovskite solar cells via contact passivation. Science 355, 722–726 (2017).

    Google Scholar 

  2. 2.

    Hou, J. H., Inganas, O., Friend, R. H. & Gao, F. Organic solar cells based on non-fullerene acceptors. Nat. Mater. 17, 119–128 (2018).

    Google Scholar 

  3. 3.

    Yuan, M. J., Liu, M. X. & Sargent, E. H. Colloidal quantum dot solids for solution-processed solar cells. Nat. Energy 1, 16016 (2016).

    Google Scholar 

  4. 4.

    Kagan, C. R., Lifshitz, E., Sargent, E. H. & Talapin, D. V. Building devices from colloidal quantum dots. Science 353, 5523 (2016).

    Google Scholar 

  5. 5.

    Xu, J. et al. 2D matrix engineering for homogeneous quantum dot coupling in photovoltaic solids. Nat. Nanotechnol. 13, 456–462 (2018).

    Google Scholar 

  6. 6.

    Chuang, C. H. M., Brown, P. R., Bulovic, V. & Bawendi, M. G. Improved performance and stability in quantum dot solar cells through band alignment engineering. Nat. Mater. 13, 796–801 (2014).

    Google Scholar 

  7. 7.

    Huynh, W. U., Dittmer, J. J. & Alivisatos, A. P. Hybrid nanorod-polymer solar cells. Science 295, 2425–2427 (2002).

    Google Scholar 

  8. 8.

    Muller-Buschbaum, P., Thelakkat, M., Fassler, T. F. & Stutzmann, M. Hybrid photovoltaics—from fundamentals towards application. Adv. Energy Mater. 7, 248 (2017).

    Google Scholar 

  9. 9.

    Piliego, C. et al. Charge separation dynamics in a narrow band gap polymer–PbS nanocrystal blend for efficient hybrid solar cells. J. Mater. Chem. 22, 24411–24416 (2012).

    Google Scholar 

  10. 10.

    Seo, J., Cho, M. J., Lee, D., Cartwright, A. N. & Prasad, P. N. Efficient heterojunction photovoltaic cell utilizing nanocomposites of lead sulfide nanocrystals and a low-bandgap polymer. Adv. Mater. 23, 3984–3988 (2011).

    Google Scholar 

  11. 11.

    Seo, J. et al. Enhancement of the photovoltaic performance in PbS nanocrystal: P3HT hybrid composite devices by post-treatment-driven ligand exchange. Nanotechnology 20, 095202 (2009).

    Google Scholar 

  12. 12.

    Speirs, M. J. et al. Hybrid inorganic–organic tandem solar cells for broad absorption of the solar spectrum. Phys. Chem. Chem. Phys. 16, 7672–7676 (2014).

    Google Scholar 

  13. 13.

    Noone, K. M. et al. Broadband absorbing bulk heterojunction photovoltaics using low-bandgap solution-processed quantum dots. Nano. Lett. 10, 2635–2639 (2010).

    Google Scholar 

  14. 14.

    Lu, H., Joy, J., Gaspar, R. L., Bradforth, S. E. & Brutchey, R. L. Iodide-passivated colloidal PbS nanocrystals leading to highly efficient polymer: nanocrystal hybrid solar cells. Chem. Mater. 28, 1897–1906 (2016).

    Google Scholar 

  15. 15.

    Liao, S. H., Jhuo, H. J., Cheng, Y. S. & Chen, S. A. Fullerene derivative-doped zinc oxide nanofilm as the cathode of inverted polymer solar cells with low-bandgap polymer (PTB7-Th) for high performance. Adv. Mater. 25, 4766–4771 (2013).

    Google Scholar 

  16. 16.

    Liang, Y. Y. et al. For the bright future-bulk heterojunction polymer solar cells with power conversion efficiency of 7.4%. Adv. Mater. 22, 135–138 (2010).

    Google Scholar 

  17. 17.

    You, J. B. et al. A polymer tandem solar cell with 10.6% power conversion efficiency. Nat. Commun. 4, 1446 (2013).

    Google Scholar 

  18. 18.

    Martinez, L., Bernechea, M., de Arquer, F. P. G. & Konstantatos, G. Near IR-sensitive, non-toxic, polymer/nanocrystal solar cells employing Bi2S3 as the electron acceptor. Adv. Energy Mater. 1, 1029–1035 (2011).

    Google Scholar 

  19. 19.

    Liu, Z. K. et al. High-efficiency hybrid solar cells based on polymer/PbSxSe1−x nanocrystals benefiting from vertical phase segregation. Adv. Mater. 25, 5772 (2013).

    Google Scholar 

  20. 20.

    Colbert, A. E., Wu, W., Janke, E. M., Ma, F. & Ginger, D. S. Effects of ligands on charge generation and recombination in hybrid polymer/quantum dot solar cells. J. Phys. Chem. C. 119, 24733–24739 (2015).

    Google Scholar 

  21. 21.

    Couderc, E., Greaney, M. J., Brutchey, R. L. & Bradforth, S. E. Direct spectroscopic evidence of ultrafast electron transfer from a low band gap polymer to CdSe quantum dots in hybrid photovoltaic thin films. J. Am. Chem. Soc. 135, 18418–18426 (2013).

    Google Scholar 

  22. 22.

    Jarzab, D. et al. Charge‐separation dynamics in inorganic–organic ternary blends for efficient infrared photodiodes. Adv. Funct. Mater. 21, 1988–1992 (2011).

    Google Scholar 

  23. 23.

    Itskos, G. et al. Optical properties of organic semiconductor blends with near‐infrared quantum‐dot sensitizers for light harvesting applications. Adv. Energy Mater. 1, 802–812 (2011).

    Google Scholar 

  24. 24.

    Kim, G.-H. et al. Synergistic photocurrent addition in hybrid quantum dot: Bulk heterojunction solar cells. Nano Energy 13, 491–499 (2015).

    Google Scholar 

  25. 25.

    Chen, H. Y. et al. A p‐type quantum dot/organic donor: acceptor solar‐cell structure for extended spectral response. Adv. Energy Mater. 1, 528–533 (2011).

    Google Scholar 

  26. 26.

    Yao, H. F. et al. Design and synthesis of a low bandgap small molecule acceptor for efficient polymer solar cells. Adv. Mater. 28, 8283–8287 (2016).

    Google Scholar 

  27. 27.

    Cnops, K. et al. 8.4% efficient fullerene-free organic solar cells exploiting long-range exciton energy transfer. Nat. Commun. 5, 3406 (2014).

    Google Scholar 

  28. 28.

    Huang, J.-S. et al. Polymer bulk heterojunction solar cells employing Förster resonance energy transfer. Nat. Photonics 7, 479 (2013).

    Google Scholar 

  29. 29.

    Gupta, V., Bharti, V., Kumar, M., Chand, S. & Heeger, A. J. Polymer–polymer förster resonance energy transfer significantly boosts the power conversion efficiency of bulk‐heterojunction solar cells. Adv. Mater. 27, 4398–4404 (2015).

    Google Scholar 

  30. 30.

    Penwell, S. B., Ginsberg, L. D. S., Noriega, R. & Ginsberg, N. S. Resolving ultrafast exciton migration in organic solids at the nanoscale. Nat. Mater. 16, 1136–1141 (2017).

    Google Scholar 

  31. 31.

    Knutson, J. R., Beechem, J. M. & Brand, L. Simultaneous analysis of multiple fluorescence decay curves: a global approach. Chem. Phys. Lett. 102, 501–507 (1983).

    Google Scholar 

  32. 32.

    Jakowetz, A. C. et al. What controls the rate of ultrafast charge transfer and charge separation efficiency in organic photovoltaic blends. J. Am. Chem. Soc. 138, 11672–11679 (2016).

    Google Scholar 

  33. 33.

    Cui, Y. et al. Fine-tuned photoactive and interconnection layers for achieving over 13% efficiency in a fullerene-free tandem organic solar cell. J. Am. Chem. Soc. 139, 7302–7309 (2017).

    Google Scholar 

  34. 34.

    Liu, M. et al. Hybrid organic–inorganic inks flatten the energy landscape in colloidal quantum dot solids. Nat. Mater. 16, 258–263 (2017).

    Google Scholar 

  35. 35.

    Fabregat-Santiago, F., Garcia-Belmonte, G., Mora-Seró, I. & Bisquert, J. Characterization of nanostructured hybrid and organic solar cells by impedance spectroscopy. Phys. Chem. Chem. Phys. 13, 9083–9118 (2011).

    Google Scholar 

  36. 36.

    Baran, D. et al. Reducing the efficiency–stability–cost gap of organic photovoltaics with highly efficient and stable small molecule acceptor ternary solar cells. Nat. Mater. 16, 363–369 (2017).

    Google Scholar 

  37. 37.

    Baek, S.-W. et al. A hydro/oxo-phobic top hole-selective layer for efficient and stable colloidal quantum dot solar cells. Energy Environ. Sci. 11, 2078–2084 (2018).

    Google Scholar 

  38. 38.

    Distler, A. et al. The effect of PCBM dimerization on the performance of bulk heterojunction solar cells. Adv. Energy Mater. 4, 1300693 (2014).

    Google Scholar 

  39. 39.

    Holliday, S. et al. High-efficiency and air-stable P3HT-based polymer solar cells with a new non-fullerene acceptor. Nat. Commun. 7, 11585 (2016).

    Google Scholar 

  40. 40.

    Zhang, X. et al. Inorganic CsPbI3 perovskite coating on PbS quantum dot for highly efficient and stable infrared light converting solar cells. Adv. Energy Mater. 8, 1702049 (2018).

    Google Scholar 

  41. 41.

    Cao, Y. M., Stavrinadis, A., Lasanta, T., So, D. & Konstantatos, G. The role of surface passivation for efficient and photostable PbS quantum dot solar cells. Nat. Energy 1, 16035 (2016).

    Google Scholar 

  42. 42.

    Proppe, A. H. et al. Picosecond charge transfer and long carrier diffusion lengths in colloidal quantum dot solids. Nano Lett. 18, 7052–7059 (2018).

    Google Scholar 

  43. 43.

    Pettersson, L. A., Roman, L. S. & Inganäs, O. Modeling photocurrent action spectra of photovoltaic devices based on organic thin films. J. Appl. Phys. 86, 487–496 (1999).

    Google Scholar 

  44. 44.

    Sandeep, C. S. S. et al. High charge-carrier mobility enables exploitation of carrier multiplication in quantum-dot films. Nat. Commun. 4, 2360 (2013).

    Google Scholar 

Download references


This research was supported by Ontario Research Fund–Research Excellence program (ORF7–Ministry of Research and Innovation, Ontario Research Fund–Research Excellence Round 7); and by the Natural Sciences and Engineering Research Council (NSERC) of Canada. This work was supported by National Research Foundation of Korea (NRF) grants (nos. NRF-2015M1A2A2057509 and NRF-2019R1A2C3008035). J.H.S. and S. Jeong were supported by grant no. NRF-2019M3D1A1078296. A.H.P. was supported by an NSERC CGS-D fellowship.

Author information




S.-W.B., F.P.G.A., S.O.K., S.H. and O.V. developed the idea and prepared the manuscript. S. Jun, G.W., A.H.P., H.R.B. and M.S.J. studied and characterized the carrier dynamics. C.K. and B.K. optimized the record device structure. J.K., J.H.S. and S. Jeong synthesized the CQDs dots and characterized the films. O.O. performed the optical calculations. J.-Y. L. and E.H.S. supervised the project. All authors discussed the results and commented on the manuscript.

Corresponding authors

Correspondence to Jung-Yong Lee or Edward H. Sargent.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–23, Tables 1–3, Notes 1–6 and refs. 1–14.

Reporting summary

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Baek, SW., Jun, S., Kim, B. et al. Efficient hybrid colloidal quantum dot/organic solar cells mediated by near-infrared sensitizing small molecules. Nat Energy 4, 969–976 (2019).

Download citation

Further reading

  • Bioinspiration in light harvesting and catalysis

    • Andrew H. Proppe
    • , Yuguang C. Li
    • , Alán Aspuru-Guzik
    • , Curtis P. Berlinguette
    • , Christopher J. Chang
    • , Richard Cogdell
    • , Abigail G. Doyle
    • , Johannes Flick
    • , Nathaniel M. Gabor
    • , Rienk van Grondelle
    • , Sharon Hammes-Schiffer
    • , Shaffiq A. Jaffer
    • , Shana O. Kelley
    • , Mario Leclerc
    • , Karl Leo
    • , Thomas E. Mallouk
    • , Prineha Narang
    • , Gabriela S. Schlau-Cohen
    • , Gregory D. Scholes
    • , Aleksandra Vojvodic
    • , Vivian Wing-Wah Yam
    • , Jenny Y. Yang
    •  & Edward H. Sargent

    Nature Reviews Materials (2020)

  • A bridge for charge carriers

    • Daniele Benetti
    •  & Federico Rosei

    Nature Energy (2019)


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing