Abstract
The atomically thin MnBi2Te4 crystal is a novel magnetic topological insulator, exhibiting exotic quantum physics. Here we report a systematic investigation of ultrafast carrier dynamics and coherent interlayer phonons in few-layer MnBi2Te4 as a function of layer number using time-resolved pump-probe reflectivity spectroscopy. Pronounced coherent phonon oscillations from the interlayer breathing mode are directly observed in the time domain. We find that the coherent oscillation frequency, the photocarrier and coherent phonon decay rates all depend sensitively on the sample thickness. The time-resolved measurements are complemented by ultralow-frequency Raman spectroscopy measurements, which both confirm the interlayer breathing mode and additionally enable observation of the interlayer shear mode. The layer dependence of these modes allows us to extract both the out-of-plane and in-plane interlayer force constants. Our studies not only reveal the interlayer van der Waals coupling strengths, but also shed light on the ultrafast optical properties of this novel two-dimensional material.
Similar content being viewed by others
Introduction
The marriage between topology and magnetism can give birth to many exotic quantum phases and phenomena such as quantum anomalous Hall effect1,2,3,4 and axion electrodynamics5,6,7,8. Recently, few-layer MnBi2Te4 (MBT) crystals have emerged as a new platform for exploring these phases9,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24,25,26,27,28,29,30,31,32,33. MBT is a new class of two-dimensional (2D) topological magnetic material. The crystal structure of MBT is formed by Te-Bi-Te-Mn-Te-Bi-Te septuple layers (SLs) stacked on top of each other along the c direction (Fig. 1a). The topological properties are inherited from the p orbitals of Bi and Te atoms, while the magnetism originates from the d bands of Mn atoms. The adjacent SLs are bonded by van der Waals (vdW) forces and can be cleaved to thin layers. Both electronic and magnetic properties depend sensitively on the sample thickness. Transport studies have revealed rich quantized transport phenomena in few-layer MBT (5–9 SL), suggesting odd- and even- layer MBT samples may host the quantum anomalous Hall and axion insulator states respectively24,25,26,27. Magnetic circular dichroism measurements have revealed the layer-dependent magnetism with an odd-even layer-number effect, verifying the A-type antiferromagnetic structure in few-layer MBT28,29.
In 2D vdW materials, lattice vibrations, especially interlayer phonon modes, have not only provided unique capabilities in determining layer thickness, stacking order, and interface coupling strength34,35,36, but have also played an important role in engineering novel electronic, thermal and magnetic properties in 2D vdW homo/heterostructures37,38,39,40,41,42. For instance, in twisted bilayer graphene interlayer conductance and thermal transport are mediated by the interlayer phonons39,40,41,42. Several Raman studies have been performed recently, primarily on high-frequency intralayer phonons which have demonstrated spin-phonon coupling31,32,33. In the low-frequency regime, magnon modes have been observed43, and a systematic study of interlayer breathing mode phonons showed a very large interfacial coupling which produced somewhat unusual results44. These interlayer phonons provide information about vdW coupling strength and electron-phonon scattering mechanisms, and a good understanding of their properties is useful for future work on MBT, for example in manipulating magnetic and topological states with light at a fast speed23,45,46, in the design and probe of heterostructure devices37,38, or simply as a method for determining sample thicknesses35,36.
Here we report ultrafast optical pump-probe reflectivity measurements in few-layer MBT, accompanied by ultralow-frequency Raman data, of carrier and coherent interlayer phonon dynamics as a function of sample thickness, with the layer number varying from 4 to 25. We observe pronounced oscillatory signals due to coherent interlayer breathing mode phonons in transient reflection measurements and find that physical properties such as the oscillation frequency, its decay time, and the carrier decay rate all depend strongly on the sample thickness. The frequency is particularly consistent and easily measured, which provides a convenient, contact-free and non-destructive tool to characterize sample thickness, especially for ultrafast studies. The increasing decay rates for thinner samples suggest that the surface and interface have a strong impact on the phonon scattering and photocarrier relaxation. The time-domain measurements are complemented by ultralow-frequency (<10 cm−1) Raman studies. In addition to the interlayer breathing modes, polarized Raman measurements enable the observation of the much weaker interlayer shear modes. The measured phonon frequencies all show a typical blue shift with decreasing layer number and can be fit using a linear chain model, from which the out-of-plane and in-plane interlayer force constants are calculated to be (5.7 ± 0.1) \(\ast\) 1019 N m−3 and (2.9 ± 0.1) \(\ast\) 1019 N m−3 respectively. The force constants allow us to calculate other mechanical parameters such as sound velocities, elastic constants and acoustic impedance. These measurements not only uncover the interlayer coupling strengths but also provide crucial information on coherent phonon and carrier lifetimes and relaxation mechanisms.
Results
Atomic force microscopy measurements
Few-layer MBT crystals were prepared by mechanical exfoliation as described previously25. Figure 1b shows an optical image of one of the sample regions used in this work. The layer thickness was determined by atomic force microscopy (AFM) measurements (Fig. 1c–e), where clear step sizes of around 1.4 nm can be observed, consistent with previous studies24,25,26,29.
Time-resolved reflectivity measurements
We measured the transient reflectivity with a standard two-color pump-probe setup, the results of which can be seen in Fig. 2. In the raw data, shown in Fig. 2a, we clearly see the presence of three distinct components. First, there is a large but short-lived change which lasts only 2–3 picoseconds with negligible layer dependence before vanishing, associated with hot electrons which rapidly transfer energy to the surrounding lattice via electron-electron and electron-phonon interactions. Next, we see a simple exponential decay, with a lifetime of around 100 ps depending on the layer thickness, probably reflecting photocarrier scattering and electron-hole recombination processes. The final component is an oscillatory signal which decays over ~30–50 picoseconds, and then briefly reappears at t ≈ 100 ps (see inset) before decaying away once more. Note that the oscillatory signal is very strong, about 20% of the total transient reflection. To show the oscillatory signal more clearly, the data after the first two components are subtracted is plotted again in Fig. 2b, along with the FFT of the data in Fig. 2c, where you can see a clear upward shift in frequency as the sample thickness decreases from ~130 GHz in 9 SL to ~180 GHz in 7 SL. The inset shows the FFT of the echoes, which have frequencies that are identical to the main signals.
In a pump-probe experiment, coherent phonons created by the pump pulse can modulate the optical dielectric function and can therefore be detected via reflectivity changes measured by the synchronized probe pulse. These phonons can be created via rapid expansions or contractions induced by, for example, temperature changes47,48 or carrier excitation49, or through a stimulated Raman scattering process50,51. Because the observed oscillation frequencies are much smaller than the intralayer vibration frequencies measured by Raman spectroscopy31 (also see discussions below), we attribute these results to coherent interlayer phonons, which for ultrathin samples will form standing waves with strongly layer-dependent frequencies. In our measurements, the polarization of the pump beam does not affect the observed signal (see Supplementary Note 3). This suggests that the interlayer vibrations are in the out-of-plane direction (the breathing mode), as in-plane vibrations (the shear mode) would show a phase shift when the pump polarization is changed51,52, a fact which has been utilized to detect very weak coherent interlayer shear mode phonons in graphene52,53. The assignment of the coherent phonon mode is further confirmed by our polarization-resolved ultralow-frequency Raman spectroscopy measurements as discussed below.
This mechanism also explains the echo of the signal at 100 ps, as coupling between the sample and the ~300 nm thick silica layer on the substrate means that acoustic phonons can be generated, travel away from the surface, reflect from the internal silica/Si interface, and return to the surface, where they then re-excite the interlayer phonon in the sample. The timing of the reappearance gives a velocity of about 6 km s−1, which matches well with the speed of longitudinal acoustic phonons in silica. The echo signals indicate that few layer MBT can be used as an optical transducer to launch coherent acoustic phonons in SiO2.
In Fig. 3a, we plot the extracted oscillation frequency at a variety of sample locations for a given layer thickness as a function of the inverse layer number (1/N). The frequency decreases with increasing sample thickness from ~300 GHz in 4 SL to ~50 GHz in 25 SL samples.
We analyze how the frequency of these phonons vary with thickness using a basic freestanding linear chain model34,35,36, in which each SL is moving as a unit and only the nearest layer interaction is considered (see Supplementary Note 9). A similar model has been used to explain the interlayer vibration modes in a variety of other 2D layered materials34,35,36,54,55,56,57,58,59. An N-layer system hosts N-1 breathing/shear modes with frequencies f(N,n) = f0sin (nπ⁄(2N)), where n = 1, 2, ⋯, N−1 is the branch index and \(f_0 = (1/{{{\mathrm{\pi }}}})\sqrt {k/\mu }\), where k = kz (or kx) is the out-of-plane (or in-plane) force constant per unit area between the adjacent layers and μ is the mass per unit area. Fitting our results to f(N, 1) gives a resulting fit parameter f0,B = 760 ± 5 GHz for the breathing mode, which we plot as a dashed gray line in Fig. 3a, showing excellent agreement of this theoretical model with the experimental data. Note that when the number of layers N→∞, these modes correspond to longitudinal acoustic phonons along the out-of-plane direction with velocity \(v = d\sqrt {k/\mu }\), with d the spacing between layers. Therefore, the longitudinal sound velocity is given by vB = πdf0 = 3.25 km s−1. This value is comparable to vB in other 2D layered materials such as MoS2 (see Supplementary Table 1).
One obvious advantage of time-resolved experiments is that we can directly measure the phonon and photocarrier lifetimes. We plot the decay rate of both the oscillatory component and the simple exponential decay in Fig. 3b, c respectively. These decay rates noticeably increase for the thinner regions of the sample. For a given thickness, we performed multiple measurements on different locations. Both the phonon decay and carrier relaxation are very sensitive to the local environment especially for the thinner samples shown as scattered data points for the same thickness in Fig. 3b, c, suggesting that phonon and carrier relaxation is influenced strongly by the surface and interface (e.g., surface roughness, adatoms and charges trapped at the interface, which all act as scatterers). On the other hand, the coherent phonon frequency is measured to be robust against locations (Fig. 3a).
In general, coherent phonon dephasing in solids is governed by scattering at boundaries, lattice defects, carriers or population decaying into lower energy acoustic phonons via anharmonic interactions. As shown in Fig. 3b, for thicker samples (>10 layers) the phonon decay rate is ~50 GHz and is independent of the thickness and sample locations. By contrast, in the thin layer regime (<10 layers) the decay rate grows rapidly with decreasing thickness and depends strongly on the location, indicating that the surface and interface play a dominant role. As demonstrated by the echo of the signal, the interlayer phonons can couple to acoustic phonons in the substrate, which may further increase the interfacial contribution to the decay rate. Furthermore, the layer dependence of phonon decay rate can also result from stronger electron-phonon coupling in thinner samples than in thicker ones31, similar to topological materials such as Bi2Se3 and WP260,61. Additional insight into the anharmonic contribution to the phonon decay rate can be obtained from temperature-dependent data (Supplementary Fig. 5). If the anharmonic contribution were large, the decay rate (linewidth) would increase significantly upon increasing temperature62. Our measurement shows that the decay rate stays roughly constant with temperature from 3 K to room temperature, suggesting that the anharmonic interaction is not important. We have found that the transient reflectivity simply scales linearly with the pump fluence (see Supplementary Note 6), which eliminates scattering with photoinduced carriers as a prominent dephasing factor.
The photoinduced carrier relaxation is determined by carrier scatterings with defects and lattice and electron-hole recombination, etc. The increasing decay rate in thinner samples from ~2 GHz in 20 SL to ~18 GHz in 4 SL shown in Fig. 3c indicates accelerated scattering and recombination rates at the surface and interface compared to the inner layers. The approximate linear scaling of the decay rate with (1/N) can be understood with a simple model, in which the total decay rate is a weighted average between the inner layer decay rate and surface/interface decay rate. Similar behavior has been observed in 2D MoS2 and Bi2Te363,64.
Raman spectroscopy measurements
To confirm our observations, we also performed polarized Raman measurements on our sample, shown in Fig. 4a, b. The six high-frequency peaks (at ~27, 48, 68, 105, 115 and 141 cm−1) have been observed in previous studies31 and are intralayer phonon modes that are Raman active both in bulk and few-layer samples. We assign these modes corresponding to their symmetry class22 based on their polarization dependence (see Supplementary Note 1 for more details). The out-of-plane vibrations (A1g modes) can be observed only in a parallel-polarized geometry, whereas the in-plane vibrations (Eg modes) are detectable in both parallel- and cross-polarized geometries.
At low frequencies, we also observe new peaks which we attribute to the interlayer phonons. In addition to the breathing mode seen in the time-resolved data, (labeled B(1)), Raman measurements also enable observation of the much weaker shear mode (labeled S(1)). Note that unlike the breathing modes, the shear modes are sensitive to applied in-plane strain65, which potentially can be used as a strain probe in MBT and heterostructures when engineering electronic and magnetic properties with strain. The B(1) peak intensity is remarkably strong compared to all other peaks, which is consistent with the pronounced coherent oscillations in the time-resolved measurements as the coherent phonons are likely generated via the stimulated Raman scattering process. The frequencies of the B(1) and S(1) modes are plotted in Fig. 4c alongside the time-resolved data, showing the excellent agreement of the B(1) frequencies with those observed in the transient reflectivity. In addition, we show that the S(1) modes also fit well to the linear chain model, with a slightly lower f0,S = 545 ± 7 GHz. The linewidths of these modes (plotted in Supplementary Fig. 2b) are very noisy, making any layer dependence difficult to observe, but are reasonable compared to the decay rates in the time-resolved data. While some small additional peaks can be observed in the parallel-polarized data (e.g., around ~20 cm−1 in Fig. 4a), they have been left intentionally unlabeled as their precise origin is unclear and is not the focus of this work. Note that only the B(1) mode is seen in the time-resolved measurements, but since Raman scattering intensity is correlated with the amplitude of coherent phonons that can be generated51, these other modes may simply be too weak to be observed.
Since both the B(1) and S(1) modes show a large blue shift from ~120 GHz in 10 SL to ~300 GHz in 4 SL and from ~100 GHz in 9 SL to ~200 GHz in 4 SL, respectively, the frequency dispersions of these interlayer modes could be useful for determining the thickness of few-layer MBT. By contrast, among the high-frequency intralayer modes, only the A1g(1) mode has a noticeable change56, red-shifting from ~47.5 to ~44.5 cm−1 (a difference of ~90 GHz) from 10 SL to 4 SL (see Supplementary Note 2), similar to previously reported observations31. We also point out that while in Raman spectroscopy these interlayer mode frequencies are very low and may be difficult to measure, especially for thick samples (where for our setup, above ~13 SL the frequencies drop below the detection limit), time-resolved measurements can be used to quickly and accurately obtain the breathing mode frequency across a wide thickness range. Acquiring time-resolved data could therefore be a particularly effective tool for non-destructive measurements of MBT sample thickness.
Discussion
As mentioned previously, we have found that for the breathing mode, f0,B = 760 ± 5 GHz from the time-resolved data and for the shear mode, f0,S = 545 ± 7 GHz from the S(1) Raman peaks. Using the B(1) Raman peaks to determine the breathing mode frequency results in a slightly higher and more uncertain \(f_{0,B}^R = 780 \pm 15\) GHz, likely due to the large Rayleigh scattering background in parallel-polarized Raman measurements at such low frequencies. Using a mass per unit area per layer for MBT of μ = 10.0 \(\ast\) 10−6 kg m−2, we find the out-of-plane and in-plane force constants per unit area to be kz = (5.7 ± 0.1) \(\ast\) 1019 N m−3 and kx = (2.9 ± 0.1) \(\ast\) 1019 N m−3. The out-of-plane force constant kz compares well with a recent Raman study, where they indirectly estimated kz = (4.5 ± 0.7) \(\ast\) 1019 N m−3 from the Davydov splitting in bulk MnBi4Te732. Recent first-principles calculations of the interlayer phonon modes in bilayer MBT23 give force constants of kz = 2.85 \(\ast\)1019 N m−3 and kx = 1.66 \(\ast\)1019 N m−3, which like previous studies on Bi2Te358 are much smaller than the experimental values but show a similar ratio between the out-of-plane and in-plane force constants (~1.7 from the theory, compared to ~1.9 from the experiment).
As mentioned in the introduction, a very recent study also measured the interlayer breathing mode phonons using Raman spectroscopy44. They observed somewhat unusual results that were attributed to a strong interfacial coupling, supported by the fact that measuring samples on two different substrates gave different results. This fact necessitated the use of a more complicated linear chain model to include the effects of the substrate coupling, which they found explained their results well. Our measurements, in contrast, agree well with a simpler model where interfacial effects are neglected (see Supplementary Discussion 1 for additional discussion of this model). This is somewhat surprising, considering one of the substrates used in their study was the same as ours (SiO2/Si), and suggests that more work should be done to determine under what circumstances these interfacial effects will vary. However, despite this difference, their result for the out-of-plane force constant kz = (4.3–6.4) \(\ast\) 1019 N m−3 agrees quite well with ours.
A useful number for comparison with other 2D materials is the per bottom atom rather than per unit area force constants, which are kz/atom = (9.3 ± 0.1) N m−1 and kx/atom = (4.7 ± 0.1) N m−1. These per-atom values are smaller than those found in Bi2Te3, but much larger than graphene (see Supplementary Table 1 for details), in line with the relative difficulties of mechanical exfoliation for these different samples. In Supplementary Table 1, we further calculate and compare our results for the interlayer phonon frequencies f0, acoustic velocities, elastic constants C33 and C44, and acoustic impedances of MBT with a few representative vdW materials.
We also investigate the interlayer breathing phonons as a function of temperature and magnetic field (see Supplementary Note 5) in order to determine if there are any strong links between the interlayer phonons and magnetic ordering in few-layer MBT. We find that the breathing mode frequency decreases by ~5% from 3 K to room temperature (Supplementary Fig. 5). This softening results from thermal expansion, which weakens the interlayer coupling with increasing temperature. Note that both magnetic and topological electronic properties are affected by hydrostatic pressure shown by recent theoretical and experimental studies in the MBT family compounds66,67,68; the interlayer phonons provide a sensitive probe of the lattice separation and external strain/pressure. We do not see a noticeable change in the breathing phonon frequency as the temperature crosses the Neel temperature at ~20 K (Supplementary Fig. 5) nor when a magnetic field of up to 6 T is applied to the sample at 3 K (Supplementary Fig. 6). Ref. 31 reports that there is a 0.3% frequency shift of the ~48 cm−1 A1g(1) mode across the phase transition temperature. We note that as the frequency change due to the spin-phonon coupling is proportional to the phonon frequency itself, similar coupling between interlayer breathing phonons and the magnetic order would likely only produce changes that are too small to observe. For example, in a 6-layer sample with ~200 GHz oscillations, a 0.3% change is only 0.6 GHz, which is within the detection uncertainty.
In conclusion, we have directly observed the interlayer breathing mode in few layer MBT both in the time-domain and in the frequency domain. By measuring the vibration frequency as a function of layer number, we have obtained both the out-of-plane and in-plane interlayer force constants. A good understanding of the typical vdW coupling strength and interlayer vibrational properties will set the stage for engineering electronic and magnetic properties69 (e.g., vdW heterostructures) as a device performance may be affected through interlayer electron-phonon interactions37,70,71,72. Because the energies of interlayer phonons in MBT are small (~1 meV), we expect that they play an important role in interlayer conductance even at low temperatures39,41. Our time-resolved measurements have also revealed that the surface and interface have a strong impact on the relaxation of both the coherent phonons and photocarriers, which may also influence carrier mobility. Therefore, a systematic study of transport properties as a function of layer number is desirable. As proposed in ref. 23, topological and magnetic phase transitions in MBT can be manipulated via non-linear phonon dynamics using intense terahertz (THz) light pulses. The light pulses induce lattice distortions leading to the separation of the septuple layers, and thus change the magnetic coupling between layers (from AFM to FM) and topological states. This effect should be largest when driving resonantly at the interlayer breathing phonon frequencies measured in this work. A similar approach has been used to realize a topological phase transition in WTe246, in which intense THz pulses drive the interlayer shear mode and induce a structure phase transition from a non-centrosymmetric to centrosymmetric phase, which resulted in the sample changing from a Weyl semimetal to a topologically trivial metal. Our studies also pave the way for future light-driven topological and magnetic orders in few-layer topological magnetic materials23,45,46, and ultrafast studies of nonequilibrium magnetic dynamics73 and nonequilibrium axion dynamics5,6,7,8,74,75,76,77.
Methods
Sample preparation
MnBi2Te4 single crystals were grown by the direct reaction of Bi2Te3 and MnTe with a ratio of 1:1 in a vacuum-sealed silica ampoule. The mixture was heated to 973 K and then cooled down to 864 K slowly. The growth method and characterization are similar to those used in previous works18,25. The Neel temperature and the critical magnetic field for the spin flop transition of bulk crystals are TN = 25 K and Hc1 = 3.6 T (at 1.5 K) respectively18,25. These values are shown to be correlated with the Mn content and distribution78. MnBi2Te4 flakes were exfoliated onto 285 nm thick SiO2/Si substrates treated by air plasma. The fabrication processes were carried out in an argon-filled glove box. The thickness is determined by the optical contrast and AFM measurement. For optical measurements, we mounted the sample in a vacuum chamber and immediately pumped down to minimize exposure to ambient environment.
Time-resolved reflectivity spectroscopy
Time-resolved measurements were performed using a typical two-color pump-probe setup, where one beam is the direct output of a Ti:Sapphire oscillator (repetition rate: 80 MHz), and the second beam is split off and sent through an OPO to modify the wavelength. After passing through optics and a delay stage, the beams are merged with a dichroic mirror and focused onto the sample using an NA = 0.5 aspheric lens, giving a 1–2 μm spot size for the probe beam and a ~5 μm spot for the pump, which is intentionally defocused slightly to allow better overlap with the probe. The reflected light is passed through a filter to eliminate any pump scattering and measured with a balanced photodiode. We modulate the pump beam at 377 kHz with an electro-optical modulator, which allows sensitive lock-in detection of the differential reflectivity. The data in this work was primarily taken using either a 633 nm probe and an 805 nm pump or an 805 nm probe and a 1050 nm pump (see Supplementary Note 4 for discussion of other combinations). The probe and pump powers were set to ~0.1 and 1 mW (pump fluence ~50 μJ/cm2) average powers respectively to avoid sample damage and laser heating effects. Most measurements were performed at room temperature unless otherwise stated. Temperature and magnetic field dependent measurements were carried out in an optical superconducting magnet system with the magnetic field applied perpendicular to the sample plane.
Raman spectroscopy
The Raman spectroscopy measurements were carried out in backscattering geometry at room temperature using a micro-Raman spectrometer with a charge-coupled device. The laser wavelength was 488 nm and the laser plasma lines were filtered by a reflecting Bragg grating, while the Rayleigh line is suppressed using BragGrate notch filters, achieving a detection limit of ~3 cm−1. The sample was mounted in a vacuum chamber. The laser was focused onto the sample via a 50× microscope objective lens to a spot size of ~2 μm. The backscattered signal was collected through the same objective lens and dispersed by a 2400 g/mm grating with a spectral resolution of ~0.4 cm−1. The laser power was kept below 0.25 mW to avoid sample damage and laser heating.
Data availability
All data needed to evaluate the conclusions in the paper are presented in the paper and the Supplementary Information. Additional data are available from the corresponding author on reasonable request.
References
Haldane, F. D. M. Model for a quantum Hall effect without Landau levels: Condensed- matter realization of the “parity anomaly”. Phys. Rev. Lett. 61, 2015–2018 (1988).
Yu, R., Zhang, W., Zhang, H.-J., Zhang, S.-C., Dai, X. & Fang, Z. Quantized anomalous Hall effect in magnetic topological insulators. Science 329, 61–64 (2010).
Chang, C.-Z. et al. Experimental observation of the quantum anomalous Hall effect in a magnetic topological insulator. Science 340, 167–170 (2013).
Burkov, A. A. & Balents, L. Weyl semimetal in a topological insulator multilayer. Phys. Rev. Lett. 107, 127205 (2011).
Qi, X.-L., Hughes, T. L. & Zhang, S.-C. Topological field theory of time-reversal invariant insulators. Phys. Rev. B 78, 195424 (2008).
Wilczek, F. Two applications of axion electrodynamics. Phys. Rev. Lett. 58, 1799–1802 (1987).
Essin, A. M., Moore, J. E. & Vanderbilt, D. Magnetoelectric polarizability and axion electrodynamics in crystalline insulators. Phys. Rev. Lett. 102, 146805 (2009).
Mong, R. S. K., Essin, A. M. & Moore, J. E. Antiferromagnetic topological insulators. Phys. Rev. B 81, 245209 (2010).
Otrokov, M. M. et al. Highly-ordered wide bandgap materials for quantized anomalous Hall and magnetoelectric effects. 2D Mater. 4, 025082 (2017).
Lee, D. S. et al. Crystal structure, properties and nanostructuring of a new layered chalcogenide semiconductor, Bi2MnTe4. CrystEngComm 15, 5532–5538 (2013).
Gong, Y. et al. Experimental realization of an intrinsic magnetic topological insulator. Chin. Phys. Lett. 36, 076801 (2019).
Li, J. et al. Intrinsic magnetic topological insulators in van der Waals layered MnBi2Te4-family materials. Sci. Adv. 5, eaaw5685 (2019).
Zhang, D. et al. Topological axion states in the magnetic insulator MnBi2Te4 with the quantized magnetoelectric effect. Phys. Rev. Lett. 122, 206401 (2019).
Otrokov, M. M. et al. Unique thickness-dependent properties of the van der waals interlayer antiferromagnet MnBi2Te4 films. Phys. Rev. Lett. 122, 107202 (2019).
Otrokov, M. M. et al. Prediction and observation of an antiferromagnetic topological insulator. Nature 576, 416–422 (2019).
Rienks, E. D. L. et al. Large magnetic gap at the Dirac point in Bi2Te3/MnBi2Te4 heterostructures. Nature 576, 423–428 (2019).
Wu, J. et al. Natural van der Waals heterostructural single crystals with both magnetic and topological properties. Sci. Adv. 5, eaax9989 (2019).
Li, H. et al. Antiferromagnetic topological insulator MnBi2Te4: synthesis and magnetic properties. Phys. Chem. Chem. Phys. 22, 556–563 (2020).
Li, H. et al. Dirac surface states in intrinsic magnetic topological insulators EuSn2As2 and MnBi2nTe3n+1. Phys. Rev. X 9, 041039 (2019).
Chen, Y. et al. Topological Electronic Structure and Its Temperature Evolution in Antiferromagnetic Topological Insulator MnBi2Te4. Phys. Rev. X 9, 041040 (2019).
Hao, Y.-J. et al. Gapless Surface Dirac Cone in Antiferromagnetic Topological Insulator MnBi2Te4. Phys. Rev. X 9, 041038 (2019).
Rodriguez-Vega, M., Leonardo, A. & Fiete, G. A. Group theory study of the vibrational modes and magnetic order in the topological antiferromagnet MnBi2Te4. Phys. Rev. B 102, 104102 (2020).
Rodriguez-Vega, M., Lin, Z.-X., Leonardo, A., Ernst, A., Vergniory, M. G. & Fiete, G. A. Light-driven topological and magnetic phase transitions in thin-layer antiferromagnets. J. Phys. Chem. Lett. 13, 4152–4158 (2022).
Deng, Y. et al. Quantum anomalous Hall effect in intrinsic magnetic topological insulator MnBi2Te4. Science 367, 895–900 (2020).
Liu, C. et al. Robust axion insulator and Chern insulator phases in a two-dimensional antiferromagnetic topological insulator. Nat. Mater. 19, 522–527 (2020).
Ge, J. et al. High-Chern-number and high-temperature quantum Hall effect without Landau levels. Natl Sci. Rev. 7, 1280–1287 (2020).
Liu, C. et al. Magnetic-field-induced robust zero Hall plateau state in MnBi2Te4 Chern insulator. Nat. Commun. 12, 4647 (2021).
Yang, S. et al. Odd-Even Layer-Number Effect and Layer-Dependent Magnetic Phase Diagrams in MnBi2Te4. Phys. Rev. X 11, 011003 (2021).
Ovchinnikov, D. et al. Intertwined Topological and Magnetic Orders in Atomically Thin Chern Insulator MnBi2Te4. Nano Lett. 21, 2544–2550 (2021).
Sass, P. M. et al. Robust A-type order and spin-flop transition on the surface of the antiferromagnetic topological insulator MnBi2Te4. Phys. Rev. Lett. 125, 037201 (2020).
Choe, J. et al. Electron-phonon and spin-lattice coupling in atomically thin layers of MnBi2Te4. Nano Lett. 21, 6139–6145 (2021).
Cho, Y. et al. Phonon modes and Raman signatures of MnBi2nTe3n+1 (n = 1,2,3,4) magnetic topological heterostructures. Phys. Rev. Res. 4, 013108 (2022).
Padmanabhan, H. et al. Interlayer magnetophononic coupling in MnBi2Te4. Nat. Commun. 13, 1929 (2022).
Tan, P.-H. et al. The shear mode of multilayer graphene. Nat. Mater. 11, 294–300 (2012).
Lu, X., Luo, X., Zhang, J., Quek, S. Y. & Xiong, Q. Lattice vibrations and Raman scattering in two-dimensional layered materials beyond graphene. Nano Res. 9, 3559–3597 (2016).
Zhang, X., Tan, Q.-H., Wu, J.-B., Shi, W. & Tan, P.-H. Review on the Raman spectroscopy of different types of layered materials. Nanoscale 8, 6435–6450 (2016).
Jin, C. et al. Interlayer electron-phonon coupling in WSe2/hBN heterostructures. Nat. Phys. 13, 127–131 (2017).
Lui, C. H. et al. Observation of interlayer phonon modes in van der Waals heterostructures. Phys. Rev. B 91, 165403 (2015).
Perebeinos, V. & Tersoff, J. Avouris, Ph. Phonon-mediated interlayer conductance in twisted graphene bilayers. Phys. Rev. Lett. 109, 236604 (2012).
Koren, E., Leven, I., Lörtscher, E., Knoll, A., Hod, O. & Duerig, U. Coherent commensurate electronic states at the interface between misoriented graphene layers. Nat. Nanotechnol. 11, 752–757 (2016).
Kim, Y. et al. Breakdown of the interlayer coherence in twisted bilayer graphene. Phys. Rev. Lett. 110, 096602 (2013).
Mahapatra, P. S., Sarkar, K., Krishnamurthy, H. R., Mukerjee, S. & Ghosh, A. Seebeck Coefficient of a Single van der Waals Junction in Twisted Bilayer Graphene. Nano Lett. 17, 6822–6827 (2017).
Lujan et al. Magnons and magnetic fluctuations in atomically thin MnBi2Te4. Nat. Commun. 13, 2527 (2022).
Li, G. et al. Observation of Ultrastrong Coupling between Substrate and the Magnetic Topological Insulator MnBi2Te4. Nano Lett. 22, 3856–3864 (2022).
de la Torre, A., Kennes, D. M., Claassen, M., Gerber, S., McIver, J. W. & Sentef, M. A. Nonthermal pathways to ultrafast control in quantum materials. Rev. Mod. Phys. 93, 041002 (2021).
Sie, E. J. et al. An ultrafast symmetry switch in a Weyl semimetal. Nature 565, 61–66 (2019).
Thomsen, C., Maris, H. J. & Tauc, J. Picosecond acoustics as a non-destructive tool for the characterization of very thin films. Thin Solid Films 154, 217–223 (1987).
Saito, T., Matsuda, O. & Wright, O. B. Picosecond acoustic phonon pulse generation in nickel and chromium. Phys. Rev. B 67, 205421 (2003).
Wright, O. B. & Gusev, V. E. Acoustic generation in crystalline silicon with femtosecond optical pulses. Appl. Phys. Lett. 66, 1190–1192 (1995).
Merlin, R. Generating coherent THz phonons with light pulses. Solid State Commun. 102, 207–220 (1997).
Garrett, G. A., Albrecht, T. F., Whitaker, J. F. & Merlin, R. Coherent THz phonons driven by light pulses and the Sb problem: what is the mechanism? Phys. Rev. Lett. 77, 3661–3664 (1996).
Mishina, T., Nitta, K. & Masumoto, Y. Coherent lattice vibration of interlayer shearing mode of graphite. Phys. Rev. B 62, 2908–2911 (2000).
Boschetto, D., Malard, L., Lui, C. H., Mak, K. F., Li, Z., Yan, H. & Heinz, T. F. Real-time observation of interlayer vibrations in bilayer and few-layer graphene. Nano Lett. 13, 4620–4623 (2013).
Lui, C.-H. & Heinz, T. F. Measurement of layer breathing mode vibrations in few-layer graphene. Phys. Rev. B 87, 121404(R) (2013).
Miao, X., Zhang, G., Wang, F., Yan, H. & Ji, M. Layer-dependent ultrafast carrier and coherent phonon dynamics in black phosphorus. Nano Lett. 18, 3053–3059 (2018).
Luo, X. et al. Large frequency change with thickness in interlayer breathing mode—significant interlayer interactions in few layer black phosphorus. Nano Lett. 15(6), 3931–3938 (2015).
Zhao, Y. et al. Interlayer breathing and shear modes in few-trilayer MoS2 and WSe2. Nano Lett. 13, 1007–1015 (2013).
Zhao, Y. et al. Interlayer vibrational modes in few-quintuple-layer Bi2Te3 and Bi2Se3 two-dimensional crystals: Raman spectroscopy and first-principles studies. Phys. Rev. B 90, 245428 (2014).
Hu, Z.-X., Kong, X., Qiao, J., Normand, B. & Ji, W. Interlayer electronic hybridization leads to exceptional thickness-dependent vibrational properties in few-layer black phosphorus. Nanoscale 8, 2740–2750 (2016).
Zhang, J. et al. Raman spectroscopy of few-quintuple layer topological insulator Bi2Se3 Nanoplatelets. Nano Lett. 11, 2407–2414 (2011).
Osterhoudt, G. B. et al. Evidence for dominant phonon-electron scattering in Weyl semimetal WP2. Phys. Rev. X 11, 011017 (2021).
Liu, H.-N., Cong, X., Lin, M.-L. & Tan, P.-H. The intrinsic temperature-dependent Raman spectra of graphite in the temperature range from 4K to 1000K. Carbon 152, 451–458 (2019).
Wang, H., Zhang, C. & Rana, F. Surface recombination limited lifetimes of photoexcited carriers in few-layer transition metal dichalcogenide MoS2. Nano Lett. 15, 8204–8210 (2015).
Zhao, J. et al. Thickness-dependent carrier and phonon dynamics of topological insulator Bi2Te3 thin films. Opt. Express 25, 14635 (2017).
Lee, J.-U., Woo, S., Park, J., Park, H. C., Son, Y.-W. & Cheong, H. Strain-shear coupling in bilayer MoS2. Nat. Commun. 8, 1370 (2017).
Chen, K. Y. et al. Suppression of the antiferromagnetic metallic state in the pressurized MnBi2Te4 single crystal. Phys. Rev. Mater. 3, 094201 (2019).
Pei, C. et al. Pressure-induced topological and structural phase transitions in an antiferromagnetic topological insulator. Chin. Phys. Lett. 37, 066401 (2020).
Xu, Z., Ye, M., Li, J., Duan, W. & Xu, Y. Hydrostatic pressure-induced magnetic and topological phase transitions in the MnBi2Te4 family of materials. Phys. Rev. B 105, 085129 (2022).
Huang, B., McGuire, M. A., May, A. F., Xiao, D., Jarillo-Herrero, P. & Xu, X. Emergent phenomena and proximity effects in two-dimensional magnets and heterostructures. Nat. Mater. 19, 1276–1289 (2020).
Lin, M.-L. et al. Cross-dimensional electron-phonon coupling in van der Waals heterostructures. Nat. Commun. 10, 2419 (2019).
Chen, C. et al. Symmetry-controlled electron-phonon interactions in van der Waals heterostructures. ACS Nano 13, 552–559 (2019).
Chow, C. M. et al. Unusual exciton-phonon interactions at van der Waals engineered interfaces. Nano Lett. 17, 1194–1199 (2017).
Kirilyuk, A., Kimel, A. V. & Rasing, T. Ultrafast optical manipulation of magnetic order. Rev. Mod. Phys. 82, 2731 (2010).
Li, R., Wang, J., Qi, X.-L. & Zhang, S.-C. Dynamical axion field in topological magnetic insulators. Nat. Phys. 6, 284–288 (2010).
Zhu, T., Wang, H., Zhang, H. & Xing, D. Tunable dynamical magnetoelectric effect in antiferromagnetic topological insulator MnBi2Te4 films. npj Comput. Mater. 7, 121 (2021).
Ahn, J., Xu, S.-Y. & Ashvin, V. Theory of optical axion electrodynamics. Preprint at https://arxiv.org/abs/2205.06843v1 (2022).
Sekine, A. & Nomura, K. Axion electrodynamics in topological materials. J. Appl. Phys. 129, 141101 (2021).
Yan, J. Q., Huang, Z., Wu, W. & May, A. F. Vapor transport growth of MnBi2Te4 and related compounds. J. Alloy. Compd. 906, 164327 (2022).
Acknowledgements
We thank Qihua Xiong, Bo Sun, Lexian Yang, and Yong Xu for helpful discussions. Sample preparation and ultrafast optical measurements were carried out at Tsinghua University. Raman studies were performed at the Institute of Semiconductors, CAS. The work was supported by the National Key R&D Program of China (Grant Nos. 2020YFA0308800, 2021YFA1400100 and 2018YFA0307100), the National Natural Science Foundation of China (Grant Nos. 12074212, 12004377, 11874350, 51991343 and 21975140), CAS Key Research Program of Frontier Sciences (Grant Nos. ZDBS-LY-SLH004 and XDPB22) and the Beijing Advanced Innovation Center for Future Chip (ICFC).
Author information
Authors and Affiliations
Contributions
L.Y. conceived and supervised the project. F.M.B. built the time-resolved reflectivity experiment and performed the time-resolved measurements with help from L.L. Y.C.L., X.C., M.L.L., and P.H.T. performed the Raman measurements. H.L. and Y.W. grew the samples. Y.W. and J.Z. fabricated the few-layer samples. H.P. and P.Y. performed the AFM measurements. F.M.B. carried out all the data analysis. F.M.B. and L.Y. wrote the paper in consultation with all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Bartram, F.M., Leng, YC., Wang, Y. et al. Ultrafast coherent interlayer phonon dynamics in atomically thin layers of MnBi2Te4. npj Quantum Mater. 7, 84 (2022). https://doi.org/10.1038/s41535-022-00495-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41535-022-00495-x
This article is cited by
-
Fabrication-induced even-odd discrepancy of magnetotransport in few-layer MnBi2Te4
Nature Communications (2024)
-
Full phonon dispersion along the stacking direction in nanoscale van der Waals materials by picosecond acoustics
npj 2D Materials and Applications (2024)