Abstract
Transition metal dichalcogenides, by virtue of their two-dimensional structures, could provide the largest active surface for reactions with minimal materials consumed, which has long been pursued in the design of ideal catalysts. Nevertheless, their structurally perfect basal planes are typically inert; their surface defects, such as under-coordinated atoms at the surfaces or edges, can instead serve as catalytically active centers. Here we show a reaction probability > 90 % for adsorbed methanol (CH3OH) on under-coordinated Pt sites at surface Te vacancies, produced with Ar+ bombardment, on layered PtTe2 — approximately 60 % of the methanol decompose to surface intermediates CHxO (x = 2, 3) and 35 % to CHx (x = 1, 2), and an ultimate production of gaseous molecular hydrogen, methane, water and formaldehyde. The characteristic reactivity is attributed to both the triangular positioning and varied degrees of oxidation of the under-coordinated Pt at Te vacancies.
Similar content being viewed by others
Introduction
Two-dimensional transition metal dichalcogenides (TMDs) have attracted considerable interest, owing to their distinctive electronic properties1,2,3,4,5,6,7,8 and highly tunable surface reactivity9,10,11,12,13,14,15,16. TMDs, by virtue of their two-dimensional structures, could provide the largest active surface for reactions with minimal materials consumed, which has long been a goal in the design of ideal catalysts. Structurally perfect basal planes of TMDs are typically inert whereas their surface defects, such as unsaturated coordinative atoms at the surfaces or edges, become catalytically active centers. Many studies on MoS2, one of the most developed TMDs, have demonstrated that by controlling the density of sulfur vacancies (active centers) at MoS2 surface, its reactivity toward varied reactions can be manipulated13,14,15,16,17,18,19,20,21. For instance, the sulfur vacancies at MoS2 surface, in spite of varied generation approaches (plasma10, ion bombardment13 or chemical etching14), facilitated hydrogen evolution reaction, through the mechanism involved with altered surface electronic structures and boosted electric conductivity10,13,14. Pt-based catalysts, including single crystals, nanoclusters, alloys, and electrodes, have been extensively investigated in both heterogeneous catalysis and electrocatalysis, because of their superior catalytic properties22,23,24,25,26,27,28,29,30,31,32,33,34,35,36,37,38,39,40,41,42. Nevertheless, the catalytic properties of Pt-based TMDs have been little explored11,43,44,45, even though they could possess better chemical and structural stability than commercial Pt-based catalysts such as supported Pt nanoclusters. The present study aims to shed light on the catalytic properties of Pt-based TMDs and their potential as catalysts.
We studied the decomposition of methanol (methanol-d4) on layered PtTe2 with various surface-probe techniques under both ultrahigh-vacuum (UHV) and near-ambient-pressure (NAP) conditions. Methanol (CH3OH) decomposition serves as the principal reaction in direct methanol fuel cells (DMFCs), a promising device that converts methanol efficiently to electricity46,47,48,49,50,51,52, and the liberation of hydrogen from the decomposition leads to viable generation of hydrogen, another clean source of energy53,54. PtTe2, as a group-10 TMD material, draws much attention for its tunable bandgap, high charge mobility, and ultrahigh air stability1,3,5,6,7,11,43,44, but its surface reactivity is little understood. We generated the surface defects on PtTe2 and controlled their concentration with Ar ion (Ar+) bombardment. The surface structures of PtTe2 were characterized using scanning tunneling microscopy (STM) and synchrotron-based photoelectron spectroscopy (PES), while the reactions, intermediates, and products, were monitored using PES, near-ambient-pressure photoelectron spectroscopy (NAP-PES) and near-ambient-pressure mass spectroscopy (NAP-MS). We also performed calculations based on density functional theory (DFT) to explore the mechanisms in detail.
The results showed that under-coordinated Pt (denoted as Ptuc) at the PtTe2 surface served as active sites for the reaction. Both dehydrogenation and C-O bond scission occurred for adsorbed methanol on the Ptuc sites, leading to the formation of CHxO* (x = 2 and 3; * denotes adsorbates) and CHx* (x = 1 and 2) as major intermediates and finally production of gaseous molecular hydrogen, methane, water, and formaldehyde via various processes. Gaseous formaldehyde (CH2O(g)) was rarely observed from methanol decomposition on either Pt single crystals or supported Pt nanoclusters; meanwhile, CO* (or CO(g)), a common product from Pt-based catalysts22,23,24,25,26,30,33,34,35,36,42, was not produced in the present reaction; the pathway of C-O bond scission in the present reaction accounted for a significant proportion (reflected on a considerable quantity of produced CHx*), which also contrasts with its minor role on supported Pt clusters34. The catalytic nature of Ptuc sites on PtTe2 thus differs from that of typical Pt-based catalysts. Moreover, the reactivity depended notably on the Ptuc concentration. At a small Ptuc concentration (≤ 10 %), methanol on the Ptuc at surface Te vacancies, the dominating surface defects, decomposed at a great probability (> 90 %). With increased Ptuc concentration (10 − 20 %), the probability decreased as the probability of decomposition to CHxO* was selectively decreased, attributed to structurally different Ptuc generated by extended Ar+ bombardment. Nevertheless, in either case, the reaction probability (≥ 80 %) exceeds those on Pt single crystals22,25 and supported Pt clusters34. We propose, with the support of DFT modeling, that both structural and electronic effects play essential roles in determining the observed catalytic properties. These results suggest that a PtTe2 surface with the Ptuc at surface Te vacancies can serve as a superior catalyst for methanol decomposition; its catalytic selectivity can be controlled with the surface structures manipulated by varied Ar+ bombardment.
Results
Structural characterization with STM and PES
We utilized STM to characterize the surface structures of layered PtTe2 before and after the treatment of Ar+ bombardment. The as-cleaved surface was generally very flat and had few defects, as illustrated in Fig. 1a; the hexagonally arranged white spots were topmost Te atoms imaged, and several types of intrinsic defects observed previously with STM55, such as Te and Pt vacancies, were also observed in the present sample (Fig. S1). After controlled Ar+ bombardment, the surface Te vacancies were evidently increased, together with few small clusters on the surface; the size of the vacancies varied from single- to multiple-Te vacancies (Fig. 1b) and the proportion of larger vacancies increased with the bombardment time (Fig. S1). Continuing to increase either the bombardment time or the Ar+ kinetic energy generated more not only the surface Te vacancies but also structural variations, such as island edges and re-deposited atoms (Fig. 1c, d). With the aim of correlating structures with reactivity, we chose a kinetic energy of 0.5 keV for incident Ar+ and a reduced Ar+ dosage (the sample current multiplied by bombardment time) to control structural complexity for reaction experiments — the Te vacancies were produced as the main surface defects while the surface crystallinity (monitored with the RHEED measurements, Fig. S2) was largely sustained.
Fig. 1e–h exemplify a high-resolution image for two single-Te vacancies and the corresponding line profile across one of the vacancies. The vacancy depth about 0.1 nm (Fig. 1f), similar to that of an intrinsic Te vacancy at the surface (Fig. S1), and the well overlap of the top Te atoms and vacancies in the model with the imaged ones (Fig. 1g) suggest that the vacancies were formed by the removal of the topmost Te atoms, i.e., the surface Te vacancies. As the positions of the surface Te atoms neighboring the vacancies remained nearly unchanged (Fig. 1g) and as they were mainly bonded to the underlying Pt, the generation of these Te vacancies altered little the positions of underlying Pt atoms. The well match of the STM image with the DFT-simulated one (Fig. 1h), produced based on the vacancy model in Fig. 1g, corroborates the vacancy structure. Small Ar+ dosages removed mainly the surface Te while left the underlying Pt atoms unaltered. Our DFT modeling for the reactions discussed below also adds weight to the argument. The small clusters in Fig. 1b likely correspond to re-deposited atoms (0.15 nm, one-atom high) after Ar+ bombardment. As they were much fewer than the surface Te vacancies at small Ar+ dosages, for which the reaction experiments were primarily performed, their contribution to the observed reactions was considered limited even though they could initiate or assist (as adsorption sites) reactions.
Our PES spectra further characterized these surface defects observed with STM. Fig. 2a exemplifies the comparison of the PES spectra of Pt 4 f core level for the layered PtTe2 as cleaved and bombarded by Ar+. The spectrum from as-cleaved PtTe2 (upper panel of Fig. 2a) shows a doublet, Pt 4f5/2 and Pt 4f7/2, centered at the binding energies (BE) 75.9 and 72.6 eV respectively, which corresponds to intact Pt-Te chemical bonds in PtTe2. Meanwhile, the PES spectrum from Ar+-bombarded PtTe2 shows an additional feature at a BE slightly smaller than that of the main Pt feature, i.e., at 71.8 eV for Pt 4f7/2 and 75.1 eV for Pt 4 f5/2 (indicated by red fitted curves in the bottom panel). The smaller BE for Pt 4 f implies less oxidized Pt, corresponding to under-coordinated Pt (Ptuc), at the PtTe2 surface and therefore the removal of Te atoms by Ar+ bombardment. In contrast, the Te 4d signals were insensitive to the removal of neighboring Te atoms ― the line shape of Te 4d doublet altered little after Ar+ bombardment (Fig. 2b), since the surface Te is mainly bonded to the underlying Pt. Both the Pt 4f and Te 4d lines from Ar+-bombarded PtTe2 shifted negatively (approximately 0.1 eV as shown in Fig. 2a, b), likely because the bombardment induced a band-bending effect. As the spectral features for varied Ar+ dosages are similar despite varied intensities of the Ptuc features (Fig. S3), the Ptuc signals correspond to the Ptuc at surface Te vacancies (denoted as Ptuc-Vac) and also to those at other surface defects (denoted as Ptuc-Ex) generated by greater Ar+ dosages. Our experiments show that the number or concentration of Ptuc can be controlled with Ar+ dosage and Ar+ kinetic energy. Fig. 2c plots the ratio of the Ptuc and total Pt signals (denoted as Ptuc/Pt), measured by the integrated intensities of the red and black fitted curves (Fig. 2a), as a function of the Ar+ dosage. The Ptuc/Pt ratio increased almost in a linear fashion with the Ar+ dosage, despite varied Ar+ kinetic energies. As about 90 % of the Pt signals came from the top two PtTe2 bilayers (according to the escape depth of the Pt 4 f photoelectrons) and as Ar+ bombardment at a small dosage removed primarily the surface Te (Fig. 1), each Ptuc/Pt ratio corresponds to a derivable concentration of surface Ptuc. Notably, the rate of increase of the Ptuc/Pt ratio depended on the Ar+ kinetic energy, since the cross-section of removing surface Te varied with the Ar+ kinetic energy. The Ar+ at 0.5 keV was chosen to prepare the sample, as it exhibited the best controllability in producing small Ptuc concentrations (small Ptuc/Pt ratios), warranting the surface Te vacancies as the dominating surface defects for catalytic studies (Fig. S1). Our reaction experiments were primarily performed on the PtTe2 with Ptuc/Pt ratios ≤ 0.13 (Ar+ dosage ≤ 4.5, Fig. 2c), corresponding to the Ptuc concentration ≤ 20 %; the Ar+ dosages (0.5 keV) at 1 and 6 in Fig. 2c produced the surfaces resembling those shown in Fig. 1b, c respectively.
Methanol decomposition monitored with PES, NAP-PES and NAP-MS
The methanol reactions were characterized primarily by PES spectra; with the spectra, we monitored the evolution of surface species with temperature and Ptuc concentrations. Fig. 3a, b compare the C 1 s spectra for methanol adsorbed on as-cleaved and Ar+-bombarded PtTe2 (Ptuc/Pt ratio = 0.07) at 145 K and annealed stepwise to selected temperatures. The dominant feature at 145 K on either surface, centered about 286.5 eV, is assigned to the C 1 s line of monolayer methanol adsorbed on PtTe2 (top in Fig. 3a, b), since multilayer methanol desorbed near 130 K34,56,57. On the as-cleaved PtTe2 surface, the methanol signals decreased with increased temperature and vanished at 200 K, reflecting the desorption of methanol (Fig. 3a). In contrast, on the PtTe2 with a number of surface Ptuc produced by Ar+ bombardment, new features grew at 283.8 – 285.1 eV above 160 K, at the expense of attenuating methanol feature at 286.5 eV (Fig. 3b). The results suggest that with increased temperature, a fraction of methanol desorbed whereas the other fraction decomposed and produced new carbon species. As the as-cleaved PtTe2 has very limited surface defects, the contrasting results indicate that the structurally perfect basal plane of layered PtTe2 is catalytically inert but the surface Ptuc, mostly at the Te vacancies (Fig. 1b, e), i.e. Ptuc-Vac, are reactive toward methanol decomposition. The products at elevated temperature consisted of three carbon species: CHxO* (x = 1-3), CHx* (x = 1-3) and atomic carbon (C*), corresponding to the C 1 s lines centered at 285.158,59,60,61,62,63,64, 283.865,66,67 and 284.2 eV (Fig. S4a), respectively. CO* was not expected because our adsorption experiments showed no CO adsorbed on such a defective PtTe2 surface even at 145 K. Fig. 3c, d exemplify the fits to the C 1 s lines (at 180 and 260 K) with characteristic fitted curves representing C 1 s signals from adsorbed monolayer methanol and the proposed products. CHxO* (red curve in Fig. 3c, d) and CHx* (blue) were the primary products at 160 – 260 K but C* became notable above 260 K, implying that further decomposition of CHxO* and/or CHx* occurred at elevated temperature. Fig. 3e plots the integrated intensities of these fitted C 1 s curves, used to measure the quantities of produced CHxO*, CHx*, and C*, as a function of temperature. The produced CHxO* (red circles) and CHx* (blue) increased to maxima near 180 K and decreased at even higher temperatures, whereas C* (purple) began to emerge above 200 K and became the major species at and above 300 K. The formation of CHxO* and CHx* indicates that dehydrogenation and C-O bond scission, the two competing processes of methanol decomposition30,34,35,68, were both catalytically activated at such low temperature on the surface Ptuc sites. A fraction of CHxO* and CHx* must have desorbed at elevated temperature, since the quantity of the remaining C* was not comparable to that of the produced CHxO* and CHx* (Fig. 3e). Our NAP experiments presented below indicate that the desorbing carbon species consisted largely of CH2O(g) and CH4(g).
To reveal how the catalytic properties of PtTe2 surface vary with the concentration of surface Ptuc, we plot the probabilities of conversion of adsorbed monolayer methanol to CHxO* (red circles) and CHx* (blue) as a function of the concentration of surface Ptuc, shown in Fig. 4a. The conversion probability was derived from the ratio of the C 1 s intensities of CHxO* (or CHx*) to monolayer methanol (145 K); the former was measured at 180 K because the maximum quantity of CHxO* (or CHx*) was produced around 180 K; only monolayer methanol was considered because it was directly in contact with the PtTe2 surface. The concentration of surface Ptuc was estimated according to the measured Ptuc/Pt ratios (Fig. 2), as mentioned above; the percentage corresponds to the fraction of Ptuc in the total amount of Pt in the top PtTe2 bilayer. For CHx* (blue circles), the conversion probability of monolayer methanol increased almost in linear proportion to the Ptuc concentration, corroborating that Ptuc served as reactive sites for the C-O bond scission. Nevertheless, the trend becomes complicated for CHxO* (red). The conversion probability increased linearly at a Ptuc concentration ≤ 10 %, while became saturated (10 - 20 %) or even decreased at a greater Ptuc concentration (> 20 %). At greater Ptuc concentrations (> 10 %) the Ptuc structurally different from Ptuc-Vac had grown and accounted for a fraction of total Ptuc, although they were not resolved in the Pt 4 f spectra. Such Ptuc corresponded to Ptuc-Ex; they possessed different catalytic properties so initiated a separate reaction pathway, for which the C-O bond scission was more facilitated so CHxO* became instable and decreased.
The conversion probability of methanol adsorbed on the Ptuc sites (denoted as methanol/Ptuc) as a function of the Ptuc concentration shows clearly the evolving catalytic selectivity (Fig. 4b). The fraction of methanol/Ptuc in total monolayer methanol was estimated to be that of Ptuc in total amount of Pt in the top PtTe2 bilayer (the Ptuc concentration), by assuming that monolayer methanol adsorbed uniformly on the PtTe2 surface. As shown in Fig. 4b, the conversion probability of methanol/Ptuc to CHx* varied little with the Ptuc concentration, remaining near 35 %; in contrast, that to CHxO* was approximately 60 % at a Ptuc concentration ≤ 10 % but decreased continuously at a Ptuc concentration > 10 %. The observation does not simply suggest that the formation of CHxO* (dehydrogenation) was structure-sensitive whereas that of CHx* (C-O bond scission) was not69,70,71 because the productions of these two intermediates were not necessarily separate — CHx* could be produced largely via the C-O bond scission of CHxO*. Besides, both the dehydrogenation and C-O bond scission were considered sensitive to structures69,70,71. The present result is likely due to enhanced C-O bond scission, which decreases CHxO* but increases CHx*, and obstructed dehydrogenation, which decreases both CHxO* and CHx*, on the Ptuc-Ex sites mentioned above. Our STM measurements show that at a greater Ar+ dosage (Ptuc concentration > 10 %), the generated surface defects include not only the Te vacancies (Fig. 1b) but also other defects, such as edges of PtTe2 patches (islands) and Pt-Te nanoclusters formed by nucleation of redeposited Pt and Te (exemplified in Fig. 1c and Fig. S4b). We thus associated the Ptuc-Ex with the Ptuc at these two surface defects. Nevertheless, we note that the total reaction probability was remarkably great — about 95 % at a Ptuc concentration ≤ 10 % and remaining greater than 80 % even at a concentration near 20 %. In either case, the reaction probability exceeded that for methanol on either Pt single-crystal surfaces (10 %)22,25 or supported Pt clusters (60 - 70 %)34. Additionally, the probability of conversion to CHx* (35 %) was also evidently greater than that on Pt clusters (<10 %)34; the C-O bond scission pathway apparently played an important role in the present reaction.
The above experiments demonstrate that the catalytic reactivity of layered PtTe2 is controllable by the surface Ptuc under UHV conditions. To unveil their catalytic performance under “real-world” conditions72, we investigated methanol reactions on layered PtTe2 near ambient pressure. Fig. 5a exemplifies the NAP-PES spectra of C 1 s core level from PtTe2 bombarded by Ar+ (Ptuc/Pt ratio = 0.10) and subsequently exposed stepwise to selected pressures of methanol at 300 K; 300 K was used because the desorption and further decomposition of products (intermediates) already occurred (Fig. 3). The as-bombarded PtTe2 surface was free of carbon contamination, indicated by the absence of C 1 s signals (the bottom of Fig. 5a); increasing methanol pressure to \({10}^{-4}\) mbar, a small C 1 s line arose around 284.2 eV and continued to grow with increased pressure; at \({10}^{-3}\) mbar and above, a shoulder centered about 283.0 eV (Fig. 5a,b) also grew. The former is assigned to C*, while the latter to CHx*, both of which resulted from decomposed methanol on PtTe2. The reactions must have occurred on the surface Ptuc sites (largely Ptuc-Vac sites at this small Ptuc concentration) as the experiments on as-cleaved PtTe2 (with scarce surface Ptuc), as a comparison, showed negligible C 1 s signals. This observation agrees with that on the Ar+-bombarded PtTe2 surface under UHV conditions, in which C* and CHx* were primary remaining species on the surface at 300 K (Fig. 3e). These C 1 s signals increased with methanol pressure, since more methanol decomposed on the PtTe2 surface at greater methanol pressures. They decreased at 0.1 mbar (second from the top in Fig. 5a) as the photoelectrons were attenuated by the increased pressure; at such a great pressure, the C 1 s feature resulting from gaseous methanol also appeared at 288.5 eV35,73. Notably, the ratio of CHx* to C* signals increased with methanol pressure but altered little with the decreasing pressure from 0.1 to \({10}^{-7}\) mbar. The ratio was affected little by the pressure-induced signal attenuation but determined by the composition of carbon species on the surface. The fraction of CHx* in total surface carbon species became greater at a greater pressure or C* concentration. We speculate that a greater C* concentration at the Ptuc sites suppressed the dehydrogenation of CHx* by altering the electronic properties of Ptuc and/or adsorption configurations of CHx*.
The corresponding gaseous products from the methanol reactions near ambient pressure were monitored with NAP-MS. Fig. 5c exemplifies the observed main products, including D2(g), D2O(g)/CD4(g) and CD2O(g), from Ar+-bombarded PtTe2 (Ptuc/Pt ratio = 0.10) at 300 K exposed to methanol-d4 (CD3OD) at varied pressures. Instead of methanol, methanol-d4 was used because these isotopic variants have similar chemical properties, such as the activation for desorption and decomposition (determined from their electronic structures), but methanol-d4 gave clearer signals of molecular deuterium (D2), an essential product to reveal the reaction mechanisms, in desorption experiments. These three desorbing species increased generally with methanol-d4 pressure, consistent with the above NAP-PES experiments, as more methanol-d4 interacted with the Ptuc at a higher methanol-d4 pressure. D2(g) came from recombinative desorption of D*, while D* was produced from dehydrogenated CD3OD*, CDxO*, and CDx*; therefore, its formation as the major desorbing species reflects the essential role of dehydrogenation at different stages of methanol-d4 decomposition. Both D2O(g) and CD4(g) were possible products, reflecting the process of C-O bond scission, but they could not be resolved by our mass spectra. CD4(g) was formed through CDx* combining with D*, and D2O(g) through either O* or OD* combining with D*. The observed CD2O(g) suggests that CHxO* decreased above 180 K (Fig. 3e) through not only C-O bond scission but also desorption as CH2O(g). The formation of CD2O(g) and D2O(g) also rationalizes scarce O* remaining on the surface, as evidenced by vanishing O 1 s signals above 200 K in the UHV PES experiments as well as absent O 1 s signals in the NAP-PES spectra (300 K). The absence of CO(g) and CO* indicates that the dehydrogenation of methanol-d4 (or methanol) to CO, a process typically observed on Pt clusters or single crystals22,23,24,26,30,33,34,35,36,42, did not occur on the Ptuc sites of PtTe2. The observed C* accordingly originated from dehydrogenated CHx*.
The gaseous products also confirm that the reactivity and selectivity of Ptuc sites depend on the Ptuc concentration. Fig. 5d shows the gaseous products (at methanol pressure 10-2 mbar) as a function of the Ptuc concentration. For a Ptuc concentration <20 %, the products increased generally with the Ptuc concentration, which is consistent with the trend shown in Fig. 4a. The production of CD2O(g) dropped dramatically when the Ptuc concentration increased above 20 %, in agreement with the decrease of CHxO* (Fig. 4a). The produced D2(g) also decreased, indicating the selectively suppressed dehydrogenation to CHxO*. In contrast, CD4(g)/D2O(g) decreased only slightly at a Ptuc concentration > 20 %, as CDx* increased at 180 K (Fig. 4a); the proportion of CDx* desorbing as CD4(g) could vary with the Ptuc concentration. The dependence is associated, as discussed above, with the composition of Ptuc-Vac and Ptuc-Ex evolving with the Ptuc concentration.
DFT modeling
Our first-principles DFT modeling aimed to elucidate the key mechanisms behind the observed reactions. We established a Te-divacancy model by removing two adjacent Te atoms at the topmost layer in order to mimic a PtTe2 surface at which the reactive sites consist primarily of the Te vacancies (Fig. 1b,e). The model is applicable to the cases of Ptuc concentration ≤ 20 % because the Te vacancies remained as the main surface defects despite the growth of the Ptuc-Ex at a Ptuc concentration > 10 %. Although the Te vacancies of various sizes were observed, the divacancy model suffices to represent the key features of the reactions on the Ptuc-Vac sites. A divacancy site has five Ptuc-Vac: one loses two Te-Pt bonds in the bilayer structure (denoted as Ptuc2-Vac), corresponding to the coordination to four Te, and the other four lose one Te-Pt bond (Ptuc1-Vac), illustrated in Fig. 6a. The structural modeling confirms that the underlying Pt atoms remain nearly at the same positions after the removal of surface Te. We considered three main reaction processes in the methanol decomposition: dehydrogenation from either oxygen (red arrows) or carbon (green arrow), and C-O bond scission (deoxygenation and dihydroxylation; black arrows), presented in Fig. 6b. The adsorption configurations and energies of methanol and its decomposition fragments are presented in Fig. S5. The modeling shows that a methanol molecule adsorbs on a Ptuc-Vac site with an O-Pt binding configuration and adsorption energy −1.02 eV, which is evidently stronger than that (−0.41 eV) on pristine PtTe2 basal plane (Fig. S5). The Ptuc-Vac, therefore, has the potential to serve as a reactive center on PtTe2. The three main decomposition processes at varied stages at the divacancy sites were calculated and compared. For the first step of decomposition, the barrier for dehydrogenation from oxygen (0.66 eV) of CH3OH* was significantly smaller than those for dehydrogenation from carbon (1.42 eV) and dehydroxylation (1.82 eV). The comparison suggests the preferential formation of methoxy (CH3O*), agreeing well with the observed selectivity that methanol decomposed via a pathway to produce more CHxO* than CHx* at a small Ptuc concentration (Fig. 4a). The great difference between the energy barriers for desorption and dehydrogenation to CH3O* (1.02 vs. 0.66 eV) also explains the great conversion probability for methanol adsorbed on the Ptuc-Vac site (Fig. 4b). CH3O* is expected to undergo further dehydrogenation (with a barrier 1.08 eV) to formaldehyde (CH2O*), because of the considerably greater activation energies for the two competing processes, namely desorption (2.58 eV) and deoxygenation (2.29 eV). CH2O*, due to its planar structure with sp2 hybridized carbons, has an adsorption energy (−1.52 eV) smaller than those of the other intermediates, that impedes subsequent decomposition. Compared to the greater barriers for its C-O bond cleavage (3.33 eV) or further dehydrogenation (to CHO*, 1.56 eV), CH2O* would prefer desorption (as CH2O(g)) to decomposition at elevated temperature, as observed in our NAP-MS experiments (Fig. 5c, d). Alternatively, if H* from the dehydrogenation is nearby (not yet desorbed as H2(g)), then CH2O* could also combine with H* to form CH2OH* (with a small barrier 0.12 eV), which provides a feasible pathway for further reactions. CH2OH* would decompose via dehydroxylation to CH2* and OH*, instead of dehydrogenation to CHOH* and H*; the latter process does not occur because the inverse process (CHOH* + H* → CH2OH*) has a negligible barrier (<0.01 eV) and CH2OH* has a lower total energy. As the barrier for the dehydroxylation (1.27 eV) of CH2OH* is evidently smaller than those for the C-O bond scission of CH3O* and CH2O* (2.29 and 3.33 eV), the observed CHx species resulted from decomposed CH2OH*. As a result, the observed CHxO* species in our PES spectra correspond to CH3O* and CH2O* and the CHx species mainly to CH2* and CH1*. The CH2* species may undergo either further dehydrogenation to yield C* or combination with H* to produce CH4(g), as observed in NAP-PES spectra (Fig. 5a) and NAP-MS spectra (Fig. 5c, d) respectively. Details of the calculated energy barriers are provided in our Supplementary Information (Figs. S5 – S18).
After the C-O bond scission of CH2OH*, the produced OH* either diffuses away from the active sites or combines with H* to desorb as H2O(g) (Fig. 5c, d), so its “poisoning effect” is insignificant. The calculated activation energy for OH* to migrate to an intermediate adsorption site on Te at the edge of divacancy amounts to 0.95 eV; their diffusion barrier on the basal plane is even smaller (0.36 eV), as shown in Fig. S19. These diffusion barriers are smaller than that for the C-O bond scission of CH2OH*, so with the progress of methanol decomposition, the produced OH* can diffuse readily to other sites to prevent the active sites from obstruction.
The above modeling shows that Ptuc-Vac in the divacancy model activates the decomposition in a coordinative manner; the adsorbates (CH3OH*, its decomposition intermediates and fragments) are bonded mostly to two or three Ptuc-Vac in varied decomposition processes (Figs. S5 – S18). Fig. 7a shows the simulated dehydrogenation of CH3OH* to CH3O* as an example. CH3OH* first adsorbs on the Ptuc2-Vac through its O and then undergoes the scission of O-H bond. At the final stage, H* is bonded to one of Ptuc1-Vac and CH3O* to both Ptuc1-Vac and Ptuc2-Vac. It is noted that neither CH3O* nor H* is bonded to Te near the vacancy in the process, since they adsorb weakly on these Te sites, like CH3OH* and its other decomposition intermediates or fragments (Fig. S5). As Te atoms at PtTe2 surface are mainly bonded to the underlying Pt6,11,55, instead of their neighboring Te atoms, the removal of surface Te atoms altered little the electronic properties of Te atoms surrounding the vacancies ― the bonding of these surface Te atoms remains saturated. As a result, they were not heavily involved in the methanol decomposition. In the divacancy model, Ptuc2-Vac appears to be more active than Ptuc1-Vac, indicating that the processes are mostly centered around Ptuc2-Vac in spite of varied reaction pathways (Figs. S5 –S18). The Ptuc-Vac are like separated Pt single atoms, triangularly positioned and oxidized to different extents dependent on their bonding to Te. The number of coordination (to Te) or missing Te-Pt bonds of Ptuc-Vac determines its electronic properties and hence catalytic properties. To illuminate the effect of the coordination number of Ptuc-Vac on the activity, a tri-vacancy model with a Ptuc3-Vac in the middle of the tri-vacancy site, which was also likely formed on the Ar+-bombarded PtTe2 surface, was introduced to simulate the reactions. The results show that the adsorption energies of CH3OH*, CH3O* and CH2O* on the tri-vacancy site were slightly increased by 0.05 ~ 0.10 eV, and the energy barrier for dehydrogenation of CH3OH* to CH3O* remained similar, whereas that of CH3O* to CH2O* was reduced by 0.12 eV (Figs. S20–S22). Consequently, the formation of CH2O* on this tri-vacancy became more probable. Reducing the coordination to Te enhances the activity of Ptuc-Vac.
The corresponding electronic structures reflect the same trend. The measured and calculated local densities of states (LDOS) near the Fermi level of Ptuc0-3-Vac (Fig. 7b) show consistently that with decreased coordination number, the Ptuc0-3-Vac at PtTe2 surface become more metallic, reflected on the enhanced LDOS near the Fermi level; meanwhile, their d-band centers shift toward higher energies (Fig. 7c). Both results are indicative of enhanced catalytic reactivity74,75. The LDOS of Ptuc1-3-Vac at PtTe2 surface and Pt at Pt(111) surface are evidently different (Fig. S23), accounting for their different catalytic behaviors. Previous studies indicate that the spatial distribution and orientation of frontier orbitals of single-atom catalysts are well correlated with adsorption and catalytic activities76. We note that the spatial distributions of frontier orbitals (in the energy ranging from -0.25 eV to the Fermi level) of Ptuc-Vac at PtTe2 surface expanded with decreased coordination number, as plotted in the insets of Fig. 7c. The expansion reflects a promoted probability of wave-function overlap, which is required for adsorption and catalytic activities76, so agrees with the enhanced reactivity indicated above. Thus, the characteristic reactivity of the Ptuc-Vac arises from not only the peculiar structural (geometric) effect — triangularly positioned Ptuc-Vac, but also the electronic effect — differently oxidized Ptuc-Vac.
The above modeling also indicates that enlarging the Te vacancies (increasing the number of more active Ptuc3-Vac) promotes the main reaction processes shown in Fig. 6b, instead of altering the reaction pathway. It accordingly supports the argument that a separated reaction pathway reflected on either the decreased conversion probability to CHxO on Ptuc sites (Fig. 4b) or the decreased production of CD2O(g) and D2(g) (Fig. 5d) at a greater Ptuc concentration was initiated by the Ptuc-Ex. The Ptuc-Ex consists largely of Ptuc at the edges of PtTe2 patches (Fig. 1c and S4b) or in redeposited Pt-Te nanoclusters (Fig. 1c). The Ptuc-Ex at the edges of PtTe2 patches (islands) are primarily the Ptuc with one missing Te-Pt bond (Ptuc1-Ex), as illustrated in Fig. S24. Our DFT modeling for methanol on the edges of PtTe2 patches (Figs. S24–S27) show that CH3OH* on the edge Ptuc1-Ex sites prefers desorption to decomposition, in the light of evidently greater activation energies for the dehydrogenation to CH3O* (1.64 eV) and the C-O bond scission (2.07 eV) than that for desorption (0.57 eV). Notably, the activation energies are greater and the adsorption is weaker than those (Fig. 6b and Fig. S20) on the Ptuc2-Vac (or Ptuc3-Vac) in the divacancies (trivacancies). The result implies that increasing the edge Ptuc1-Ex sites decreases the average conversion probability (to both CHxO* and CHx*) on Ptuc sites, which explains the observed behavior of CHxO* (Fig. 4b). As a result, the Ptuc-Ex on the redeposited Pt-Te nanoclusters should be responsible for the production of CHx*, to match the nearly constant probability of conversion to CHx* (Fig. 4b). Earlier studies showed that the C-O bond scission of methanol and subsequent production of CH4 were promoted on supported nanoscale Pt clusters34; meanwhile, the dehydrogenation to CO also occurred, which contrasts with the present observation. Therefore, the Pt-Te nanoclusters, instead of pure Pt clusters, are more likely the structures to yield CHx*. These Pt-Te nanoclusters had no long-range structural ordering since our RHEED measurements showed no additional diffraction patterns. As they were formed by nucleation of redeposited Pt and Te, the Pt atoms in the clusters were not bonded exclusively to Te so not separated as far as those in PtTe2. The Ptuc-Ex at the cluster’s surface thus differs structurally from the Ptuc-Vac and the Ptuc-Ex at edges of PtTe2 patches discussed above. Small Pt aggregates likely formed in the Pt-Te clusters so their surface Ptuc-Ex exhibited reactivity partially resembling that of supported Pt nanoclusters34.
Discussion
With STM, PES, NAP-PES, NAP-MS, and DFT calculations, we studied methanol reactions on layered PtTe2 under both UHV and NAP (up to 0.1 mbar) conditions. A structurally perfect PtTe2 surface was inactive whereas the surface with Ptuc sites, which was formed primarily by removing surface Te using controlled Ar+ bombardment, became able to activate methanol decomposition. Adsorbed methanol on the Ptuc-Vac sites, the dominating reactive sites at small Ptuc concentrations, began to decompose at approximately 160 K and yielded CHxO* (x = 2 and 3) as the main intermediates; CHxO* either desorbed as CH2O(g) or decomposed further, via the transient formation and subsequent C-O bond scission of CH2OH*, to produce CHx* (x = 1 and 2). The reaction probability on the Ptuc-Vac sites exceeded 90 % ― approximately 60 % of the methanol decomposed to CHxO* and 35 % to CHx* at 180 K, and the reaction ultimately produced gaseous hydrogen, methane, water, and formaldehyde at elevated temperature. We argue that the Ptuc-Vac activated the reaction processes like single-atom catalysts and in a coordinative manner; their triangular positioning and varied degrees of oxidation accounted for the observed characteristic reactivity. Increased Ar+ dosage (Ptuc concentration increased to 10 – 20 %) generated structurally different Ptuc-Ex, associated with the edges of PtTe2 patches and re-deposited Pt-Te nanoclusters, even though the Te vacancies remained major at the surface; on such Ptuc-Ex sites the probability of decomposition to CHxO* was selectively decreased. A consistent trend was reflected in the gaseous products from the reaction under NAP conditions. The results suggest that the PtTe2 surface can serve as a superior catalyst toward methanol decomposition, with advantages of great catalytic reactivity and tunable selectivity.
Methods
Sample preparation
Single-crystal PtTe2 was synthesized by the self‐flux method. High‐purity Pt (99.99%, 0.35 g, 1.79 mmol) foils and a Te ingot (99.9999%, 4.35 g, 34.09 mmol), obtained from Ultimate Materials Technology Co., Ltd, were mixed in a ratio of 1:17 and sealed in a quartz tube under vacuum at ~ 5 × 10-5 Torr. The tube was heated to 1000 °C in 12 hours, held there for 24 hours, and then slowly cooled to 500 °C at a rate of −3 to −5 °C. The excess Te was subsequently separated by centrifugation. To improve the crystal quality and remove any residual Te, the crystal was sealed in an evacuated quartz tube again and heated at 450 °C for 100 hours. The average yield of PtTe2 with this method was 90 - 95% (based on Pt). The grown bulk crystal has a diameter near 8.0 mm; it was cleaved in situ before each experiment.
Characterization
The UHV experiments were conducted in UHV chambers with a base pressure in the regime of 10−10 Torr. Ar+ bombardment was performed with an acceleration energy of 0.5 −2.0 keV and under a pressure of 5 × 10-6 Torr; 0.5 keV was chosen for the sample preparation in catalytic studies. The sample was maintained at 300 K for exposure to CH3OH and methanol-d4 (CD3OD) at selected pressures. The highly pure CH3OH and CD3OD (Merck, 99.8%) were additionally purified by repeated freeze–pump–thaw cycles before being introduced into the experimental chambers. The gas exposure in the present work is reported in Langmuir units (1.0 L = 1 × 10−6 Torr s). STM images were acquired at sample temperature 77 K (samples cooled from 300 K in an hour) in constant-current mode using an electrochemically etched tungsten tip, with a sample bias voltage (Vs) of −150 mV − −500 mV and a tunneling current (It) of 1.0 − 3.0 nA. The PES and NAP-PES experiments were conducted at the TLS BL09A2 and BL24A beamlines, respectively, at the National Synchrotron Radiation Research Center (NSRRC) in Taiwan77,78. For the former, the incident photon beam (with a fixed energy 410 eV) was normal to the surface and photoelectrons were collected (Scienta R3000) at an angle of 58° from the surface normal; for the latter, the beam (with a fixed energy 380 eV) was incident 56° from the surface normal and the analyzer (SPECS NAP 150), equipped with a 4-stages differential pumping system, was placed normal to the surface. The energy resolution was estimated to be near 0.1 eV and the BE was referred to the Au 4 f core level at 84.0 eV of an Au substrate placed beside the investigated PtTe2 sample. All spectra presented here were normalized to the photon flux. The gaseous reaction products were measured with NAP-MS, comprised of a quadrupole mass spectrometer (Hiden HAL201RC) and a doubly-differentially pumping system with a stainless steel tubing inlet terminated with an aperture (a diameter 0.75 mm) 3 mm from the sample. We used a full-range gauge mounted on the reaction chamber to calibrate the ion current at a selected m/z ratio to the partial pressure of the corresponding product. The presented partial pressures of the gaseous products were derived by subtracting the background, which was collected from as-cleaved PtTe2 surface (inert toward methanol decomposition), under the corresponding methanol pressure.
DFT calculations
First-principles calculations were performed by using Vienna ab initio simulation package (VASP)79,80, in the framework of DFT with the projector-augmented wave (PAW) method81 and the Perdew–Burke–Ernzerhof functional82 type generalized gradient approximation exchange-correlation functional. For the 1T-PtTe2 calculations, the energy cutoff was 330 eV and the energy convergence criterion was 10-4 eV. A 12 × 12 × 1 Γ-centered k-point sampling was performed for the Brillouin zone integration until the relative energies converged to a few meV. The optimized lattice constant was 3.91 Å, in good agreement with a previous report of 3.9 Å83. We included weak van der Waals (vdW) interaction between adjacent two bilayers using the recently developed SCAN+rVV1084 correction method that yielded excellent geometric and energetic results at a reasonable computational cost. The 1T-PtTe2 layered structure was then modeled by a 6 × 6 supercell with three bilayers of 1T-PtTe2. The bottom bilayer was fixed and the remaining two bilayers were allowed to relax. The adsorption energy (Eads) for each adsorbate was evaluated by the following standard formula: Eads = EA+S – ES – EA, where EA+S, ES, and EA denote the total energies of the adsorbed system, the clean PtTe2 layered system, and the chemical potentials of the corresponding adsorbed species in a gas phase, respectively. The energy barriers were determined using the climbing image nudged elastic band (CINEB) method85.
Data availability
Data that support the findings of this study are presented in the main article and Supplementary Information files. Source data are provided with this paper.
References
Yan, M. et al. Lorentz-violating type-II Dirac fermions in transition metal dichalcogenide PtTe2. Nat. Commun. 8, 257 (2017).
Oyedele, A. D. et al. PdSe2: pentagonal two-dimensional layers with high air stability for electronics. J. Am. Chem. Soc. 139, 14090–14097 (2017).
Ma, H. et al. Thickness-tunable synthesis of ultrathin type-ii dirac semimetal ptte2 single crystals and their thickness-dependent electronic properties. Nano Lett. 18, 3523–3529 (2018).
Bahramy, M. S. et al. Ubiquitous formation of bulk Dirac cones and topological surface states from a single orbital manifold in transition-metal dichalcogenides. Nat. Mater. 17, 21–28 (2018).
Ghosh, B. et al. Broadband excitation spectrum of bulk crystals and thin layers of PtTe2. Phys. Rev. B 99, 045414 (2019).
Politano, A. et al. 3D dirac plasmons in the type-ii dirac semimetal PtTe2. Phys. Rev. Lett. 121, 086804 (2018).
Lin, M.-K. et al. Dimensionality-mediated semimetal-semiconductor transition in ultrathin PtTe2 films. Phys. Rev. Lett. 124, 036402 (2020).
D’Olimpio, G. et al. PdTe2 transition-metal dichalcogenide: chemical reactivity, thermal stability, and device implementation. Adv. Funct. Mater. 30, 1906556 (2020).
Xie, J. et al. Controllable disorder engineering in oxygen-incorporated mos2 ultrathin nanosheets for efficient hydrogen evolution. J. Am. Chem. Soc. 135, 17881–17888 (2013).
Li, H. et al. Corrigendum: activating and optimizing MoS2 basal planes for hydrogen evolution through the formation of strained sulphur vacancies. Nat. Mater. 15, 364 (2016).
Politano, A. et al. Tailoring the Surface Chemical Reactivity of Transition-Metal Dichalcogenide PtTe2 Crystals. Adv. Funct. Mater. 28, 1706504 (2018).
Chen, Y. et al. Tuning electronic structure of single layer mos2 through defect and interface engineering. ACS Nano 12, 2569–2579 (2018).
Yang, J. et al. Single atomic vacancy catalysis. ACS Nano 13, 9958–9964 (2019).
Wang, X. et al. Single-atom vacancy defect to trigger high-efficiency hydrogen evolution of MoS2. J. Am. Chem. Soc. 142, 4298–4308 (2020).
Hu, J. et al. Sulfur vacancy-rich MoS2 as a catalyst for the hydrogenation of CO2 to methanol. Nat. Catal. 4, 242–250 (2021).
Xu, J. et al. Frenkel-defected monolayer MoS2 catalysts for efficient hydrogen evolution. Nat. Commun. 13, 2193 (2022).
Xie, J. et al. Defect-rich MoS2 ultrathin nanosheets with additional active edge sites for enhanced electrocatalytic hydrogen evolution. Adv. Mater. 25, 5807–5813 (2013).
Nan, H. et al. Strong photoluminescence enhancement of mos2 through defect engineering and oxygen bonding. ACS Nano 8, 5738–5745 (2014).
He, Z. et al. Defect engineering in single-layer MoS2 using heavy ion irradiation. ACS Appl. Mater. Interfaces 10, 42524–42533 (2018).
Du, H.-Y. et al. Nanoscale redox mapping at the MoS2-liquid interface. Nat. Commun. 12, 1321 (2021).
Huang, Y.-F. et al. Thickness-dependent photocatalysis of ultra-thin mos2 film for visible-light-driven Co2 reduction. Catalysts 11, 1295 (2021).
Sexton, B. A. Methanol decomposition on platinum (111). Surf. Sci. 102, 271–281 (1981).
Sexton, B. A., Rendulic, K. D. & Huges, A. E. Decomposition pathways of C1 C4 alcohols adsorbed on platinum (111). Surf. Sci. 121, 181–198 (1982).
Akhter, S. & White, J. M. A static SIMS/TPD study of the kinetics of methoxy formation and decomposition on O/Pt(111). Surf. Sci. 167, 101–126 (1986).
Attard, G. A., Chibane, K., Ebert, H. D. & Parsons, R. The adsorption and decomposition of methanol on Pt(110). Surf. Sci. 224, 311–326 (1989).
Gibson, K. D. & Dubois, L. H. Step effects in the thermal decomposition of methanol on Pt(111). Surf. Sci. 233, 59–64 (1990).
Wang, J. & Masel, R. I. Carbon-oxygen bond scission during methanol decomposition on (1 × 1)platinum(110). J. Am. Chem. Soc. 113, 5850–5856 (1991).
Franaszczuk, K. et al. A comparison of electrochemical and gas-phase decomposition of methanol on platinum surfaces. J. Phys. Chem. 96, 8509–8516 (1992).
Kizhakevariam, N. & Stuve, E. M. Promotion and poisoning of the reaction of methanol on clean and modified platinum (100). Surf. Sci. 286, 246–260 (1993).
Greeley, J. & Mavrikakis, M. Competitive paths for methanol decomposition on Pt(111). J. Am. Chem. Soc. 126, 3910–3919 (2004).
Antolini, E., Salgado, J. R. C. & Gonzalez, E. R. The methanol oxidation reaction on platinum alloys with the first row transition metals: The case of Pt–Co and –Ni alloy electrocatalysts for DMFCs: a short review. Appl. Catal. B: Environ. 63, 137–149 (2006).
Peng, T. L. & Bernasek, S. L. The internal energy of CO2 produced by the catalytic oxidation of CH3OH by O2 on polycrystalline platinum. J. Chem. Phys. 131, 154701 (2009).
Matolínová, I. et al. CO and methanol adsorption on (2 × 1)Pt(110) and ion-eroded Pt(111) model catalysts. Surf. Interface Anal. 43, 1325–1331 (2011).
Chao, C.-S. et al. Two-channel decomposition of methanol on Pt nanoclusters supported on a thin film of Al2O3/NiAl(100). J. Phys. Chem. C. 117, 5667–5677 (2013).
Miller, A. V., Kaichev, V. V., Prosvirin, I. P. & Bukhtiyarov, V. I. Mechanistic study of methanol decomposition and oxidation on Pt(111). J. Phys. Chem. C. 117, 8189–8197 (2013).
Wang, H. et al. In situ XANES study of methanol decomposition and partial oxidation to syn-gas over supported Pt catalyst on SrTiO3 nanocubes. Catal. Today 237, 71–79 (2014).
Kemppainen, E. et al. Scalability and feasibility of photoelectrochemical H2 evolution: the ultimate limit of Pt nanoparticle as an HER catalyst. Energy Environ. Sci. 8, 2991–2999 (2015).
Kattel, S., Yan, B., Chen, J. G. & Liu, P. CO2 hydrogenation on Pt, Pt/SiO2 and Pt/TiO2: importance of synergy between Pt and oxide support. J. Catal. 343, 115–126 (2016).
Lin, L. et al. Low-temperature hydrogen production from water and methanol using Pt/α-MoC catalysts. Nature 544, 80–83 (2017).
Li, H. et al. Synergetic interaction between neighbouring platinum monomers in CO2 hydrogenation. Nat. Nanotechnol. 13, 411–417 (2018).
Damte, J. Y., Lyu, S.-l, Leggesse, E. G. & Jiang, J. C. Methanol decomposition reactions over a boron-doped graphene supported Ru–Pt catalyst. Phys. Chem. Chem. Phys. 20, 9355–9363 (2018).
Liao, T.-W. et al. Composition-tuned Pt-skinned ptni bimetallic clusters as highly efficient methanol dehydrogenation catalysts. Chem. Mater. 31, 10040–10048 (2019).
Chia, X. et al. Layered platinum dichalcogenides (PtS2, PtSe2, and PtTe2) electrocatalysis: monotonic dependence on the chalcogen size. Adv. Funct. Mater. 26, 4306–4318 (2016).
Chia, X., Sofer, Z., Luxa, J. & Pumera, M. Layered noble metal dichalcogenides: tailoring electrochemical and catalytic properties. ACS Appl. Mater. Interfaces 9, 25587–25599 (2017).
Li, X. et al. Ordered clustering of single atomic Te vacancies in atomically thin PtTe2 promotes hydrogen evolution catalysis. Nat. Commun. 12, 2351 (2021).
Burstein, G. T., Barnett, C. J., Kucernak, A. R. & Williams, K. R. Aspects of the anodic oxidation of methanol. Catal. Today 38, 425–437 (1997).
Hamnett, A. Mechanism and electrocatalysis in the direct methanol fuel cell. Catal. Today 38, 445–457 (1997).
Williams, K. R. & Burstein, G. T. Low temperature fuel cells: Interactions between catalysts and engineering design. Catal. Today 38, 401–410 (1997).
Aricò, A. S., Srinivasan, S. & Antonucci, V. DMFCs: from fundamental aspects to technology development. Fuel Cells 1, 133–161 (2001).
Rostrup‐Nielsen, J. R. Fuels and energy for the future: the role of catalysis. Catal. Rev. 46, 247–270 (2004).
Li, X. & Faghri, A. Review and advances of direct methanol fuel cells (DMFCs) part I: Design, fabrication, and testing with high concentration methanol solutions. J. Power Sources 226, 223–240 (2013).
Bahrami, H. & Faghri, A. Review and advances of direct methanol fuel cells: Part II: Modeling and numerical simulation. J. Power Sources 230, 303–320 (2013).
Peraldo Bicelli, L. Hydrogen: a clean energy source. Int. J. Hydrog. Energy 11, 555–562 (1986).
Hung, Y.-H. et al. Manipulation of heteroatom substitution on nitrogen and phosphorus co-doped graphene as a high active catalyst for hydrogen evolution reaction. J. Phys. Chem. C. 123, 22202–22211 (2019).
Zhussupbekov, K. et al. Imaging and identification of point defects in PtTe2. npj 2D Mater. Appl. 5, 14 (2021).
Hu, G.-R. et al. Low-temperature decomposition of methanol on Au nanoclusters supported on a thin film of Al2O3/NiAl(100). Phys. Chem. Chem. Phys. 13, 3281–3290 (2011).
Hung, T.-C. et al. Dependence on size of supported rh nanoclusters in the decomposition of methanol. ACS Catal. 5, 4276–4287 (2015).
Cox, D. F. & Schulz, K. H. Methanol decomposition on single crystal Cu2O. J. Vac. Sci. Technol. A 8, 2599–2604 (1990).
Bukhtiyarov, V. I. et al. In situ study of selective oxidation of methanol to formaldehyde over copper. React. Kinet. Catal. Lett. 79, 181–188 (2003).
Pöllmann, S., Bayer, A., Ammon, C. & Steinrück, H.-P. Adsorption and reaction of methanol on clean and oxygen precovered Cu(111). Z. f.ür. Physikalische Chem. 218, 957–971 (2004).
Koitaya, T. et al. Systematic study of adsorption and the reaction of methanol on three model catalysts: Cu(111), Zn–Cu(111), and Oxidized Zn–Cu(111). J. Phys. Chem. C. 121, 25402–25410 (2017).
Besharat, Z. et al. Dehydrogenation of methanol on Cu2O(100) and (111). J. Chem. Phys. 146, 244702 (2017).
Setvin, M. et al. Methanol on anatase TiO2 (101): mechanistic insights into photocatalysis. ACS Catal. 7, 7081–7091 (2017).
Evans, P. E. et al. Methoxy formation induced defects on MoS2. J. Phys. Chem. C. 122, 10042–10049 (2018).
Larciprete, R., Goldoni, A., Groŝo, A., Lizzit, S. & Paolucci, G. The photochemistry of CH4 adsorbed on Pt(111) studied by high resolution fast XPS. Surf. Sci. 482-485, 134–140 (2001).
Fuhrmann, T. et al. Activated adsorption of methane on Pt(1 1 1) —an in situ XPS study. N. J. Phys. 7, 107–107 (2005).
Hsia, Y.-Y. et al. Effects of O2 and H2O in the oxidative steam-reforming reaction of ethanol on Rh catalysts. J. Phys. Chem. C. 123, 11649–11661 (2019).
Wu, Y.-C. et al. Catalyzed decomposition of methanol-d4 on vanadium nanoclusters supported on an ultrathin film of Al2O3/NiAl(100). J. Phys. Chem. C. 126, 3903–3914 (2022).
Liu, Z.-P. & Hu, P. General rules for predicting where a catalytic reaction should occur on metal surfaces: a density functional theory study of C−H and C−O bond breaking/making on flat, stepped, and kinked metal surfaces. J. Am. Chem. Soc. 125, 1958–1967 (2003).
Van Santen, R. A. Complementary structure sensitive and insensitive catalytic relationships. Acc. Chem. Res. 42, 57–66 (2009).
van den Berg, R. et al. Structure sensitivity of Cu and CuZn catalysts relevant to industrial methanol synthesis. Nat. Commun. 7, 13057 (2016).
Freund, H. J. et al. Bridging the pressure and materials gaps between catalysis and surface science: clean and modified oxide surfaces. Top. Catal. 15, 201–209 (2001).
Liao, G.-J. et al. Decomposition of methanol-d4 on a thin film of Al2O3/NiAl(100) under near-ambient-pressure conditions. J. Chem. Phys. 158, 174707 (2023).
Hammer, B. & Nørskov, J. K. Theoretical surface science and catalysis—calculations and concepts. In: Advances in Catalysis). Academic Press (2000).
Wang, J.-H., Lee, C. S. & Lin, M. C. Mechanism of ethanol reforming: theoretical foundations. J. Phys. Chem. C. 113, 6681–6688 (2009).
Fu, Z., Yang, B. & Wu, R. Understanding the activity of single-atom catalysis from frontier orbitals. Phys. Rev. Lett. 125, 156001 (2020).
Hong, I. H. et al. Performance of the SRRC scanning photoelectron microscope. Nucl. Instrum. Methods Phys. Res. Sect. A: Accelerators, Spectrometers, Detect. Associated Equip. 467-468, 905–908 (2001).
Wang, C.-H., Chang, S.-T., Chen, S.-Y. & Yang, Y.-W. New ambient pressure X-ray photoelectron spectroscopy endstation at Taiwan light source. AIP Conf. Proc. 2054, 040012 (2019).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Computational Mater. Sci. 6, 15–50 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Hao, S. et al. Low-temperature eutectic synthesis of ptte2 with weak antilocalization and controlled layer thinning. Adv. Funct. Mater. 28, 1803746 (2018).
Peng, H., Yang, Z.-H., Perdew, J. P. & Sun, J. Versatile van der waals density functional based on a meta-generalized gradient approximation. Phys. Rev. X 6, 041005 (2016).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
Acknowledgements
The National Science and Technology Council in Taiwan provided support with Grants No. NSTC 109-2112-M-018-008-MY3 (P.-H. C. and C.-P. C.), MOST 109-2112-M-008-030-MY2 (J.-W. H., L.-H. K. and M.-F. L.), NSTC 110-2112-M-213-010 (Y.-L. L. and Y.-J. H.), NSTC 110-2112-M-A49-013-MY3 (W.-H. Chen, C.-Y. C. and C.-L. L.), NSTC 110-2112-M-A49-022-MY2 (W.-H. Chen, C.-Y. C. and C.-L. L.), NSTC 111-2634-F-A49-008 (W.-H. Chen, C.-Y. C. and C.-L. L.), NSTC 112-2112-M-213-017 (C.-H. W.) and NSTC 112-2124-M-006-009 (C.-N. K. and C.-S. L.) for this work. This work is also partially supported by the “Center for the Semiconductor Technology Research” from The Featured Areas Research Center Program within the framework of the Higher Education Sprout Project by the Ministry of Education in Taiwan. CPU time at Taiwan’s National Center for High-performance Computing (NCHC) is greatly appreciated. We also thank Drs. Hung-Wei Shiu and An-Cheng Yang for their technical support.
Author information
Authors and Affiliations
Contributions
M.-F. L., C.-L. L., and J.-P. C. conceived and supervised the project. J.-W. H. and L.-H. K. performed measurements of PES, NAP-PES, NAP-MS, and RHEED, and analyzed the data. Y.-L. L., B.-H. L., C.-H. W. and Y.-J. H. assisted the synchrotron-based experiments. C.-N. K. and C.-S. L. prepared the TMDs samples. W.-H. C. and Q.-Y. Z. performed STM characterization. P.-H. C. and J.-P. C. performed DFT calculations. The text was initially composed by J.-W. H. and M.-F. L., with input from all co-authors. All authors further contributed to the discussion of the experimental work and the final version of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hsueh, JW., Kuo, LH., Chen, PH. et al. Investigating the role of undercoordinated Pt sites at the surface of layered PtTe2 for methanol decomposition. Nat Commun 15, 653 (2024). https://doi.org/10.1038/s41467-024-44840-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-44840-z