A sharp focus of current research on superconducting superhydrides is to raise their critical temperature Tc at moderate pressures. Here, we report a discovery of giant enhancement of Tc in CeH9 obtained via random substitution of half Ce by La, leading to equal-atomic (La,Ce)H9 alloy stabilized by maximum configurational entropy, containing the LaH9 unit that is unstable in pure compound form. The synthesized (La,Ce)H9 alloy exhibits Tc of 148–178 K in the pressure range of 97–172 GPa, representing up to 80% enhancement of Tc compared to pure CeH9 and showcasing the highest Tc at sub-megabar pressure among the known superhydrides. This work demonstrates substitutional alloying as a highly effective enabling tool for substantially enhancing Tc via atypical compositional modulation inside suitably selected host crystal. This optimal substitutional alloying approach opens a promising avenue for synthesis of high-entropy multinary superhydrides that may exhibit further increased Tc at even lower pressures.
Ever since Heike Kamerlingh Onnes made the astonishing discovery1 that the electrical resistance of mercury disappeared as temperature dropped to a few Kelvins via liquid-helium cooling, this exotic quantum phenomenon, known as superconductivity, has attracted tremendous interest in fundamental scientific inquiry and spurred intense efforts for applications ranging from detection of faint magnetic signals to generation of intensive magnetic fields. The long-sought overarching goal is to find materials with sufficiently high superconducting critical temperatures (Tcs) to facilitate experimental exploration and practical implementation, ultimately allowing ambient-environment applications. Over the years, the search for room-temperature superconductors has been among the most luring and challenging topics in condensed matter physics; notable progress includes materials with Tc in liquid-hydrogen and liquid-nitrogen temperature ranges achieved at ambient pressure2,3, making it more easily manageable to utilize superconductors in advanced devices. More recently, superconductivity with Tc approaching or even exceeding the room-temperature has been predicted in a class of hydrogen-rich compounds, termed superhydrides, under extreme compression. Theoretical prediction followed by experimental synthesis led to the discovery of superconductors with Tc of 203 K in covalent SH34,5,6 and 250–260 K in ionic LaH107,8,9,10, obtained at very high pressures between 150–200 GPa. A Tc of 288 K was reportedly achieved at extremely high pressures around 270 GPa in a C-S-H system with unknown composition and structure11, but it has caused intense debate12,13,14 and still awaits confirmation.
Meanwhile, inspired by the prediction of high-temperature superconductive CaH615, extensive ensuing studies have established a large family of clathrate superhydrides, including CaH616,17, YH618, YH919,20, CeH921,22,23, CeH1021, and LaH109,10, which comprise an array of distinct hydrogen cages anchored at the center by a variety of metal atoms. The diverse structural and compositional forms of these binary compounds offer a platform for exploring material parameters to optimize the energetic and superconducting states. Systematic studies indicate that atomic radius, electronegativity, and valence electron of metal atom play important roles in tuning the most concerned properties of superhydrides, i.e., superconductivity and stability24. Among these ionic superhydrides, LaH10 faces an inescapable problem of its harsh synthesis pressure (>150 GPa), despite its very high Tc9,10; whereas CeH9 or CeH10 with relatively low Tc of 95–115 K can be synthesized around megabar pressure21. Improving the superconducting properties of these superhydrides with moderate synthesis and stability pressures presents pressing challenges in this active research field.
Binary superhydrides are highly restricted in their configurational space with limited structural and compositional variations. To expand the material horizon, related research recently shifted focus to ternary systems with much higher degrees of freedom, which offer a larger number and richer variety of structural prototypes for superconducting superhydride screening25. The potential of this approach is demonstrated in a theoretical work26 showing that Li doping introduces an extra electron into the molecular-like hydrogen in MgH16 to generate atomic-like hydrogen, and the formed ternary Li2MgH16 has a Tc of 473 K at 250 GPa. In addition, theoretical studies have also designed a series of ternary superhydrides25,27, such as XYH828,29,30, Ca-Y-H31, and Ca-Mg-H32 that are expected to possess desirable high-Tc features or prospects. A sticking point, however, is to find ternary superhydrides that host high-temperature superconductivity at moderate, near or below megabar, pressures.
Rare-earth (RE) metals have similar electronegativities, electronic configurations, and atomic radii, so their disordered solid solution alloys are easy to form33,34. This offers a viable avenue to use suitably selected binary compounds as the base template to construct ternary alloy superhydrides that share the same crystal structure. It has been shown that LaH6 and YH10 units, which are experimentally unreachable in the binary systems, do appear in La-Y alloy hydrides at pressures of 170–196 GPa35, although superconductivity is not improved. It is of great interest to explore the cubic La-H9,10,36 and hexagonal close packed (hcp) Ce-H21,22,23 systems to find a desirable ternary platform for experimental realization of high-temperature superconductivity in materials that can be stabilized at relatively low pressures.
In this work, we experimentally investigated the crystal structure, superconductivity, and stability pressure range of a La-Ce alloy superhydride. Substitutional (La,Ce)H9 with essentially equal metal-atom occupancy was obtained using the starting materials of equiatomic La-Ce alloy and ammonia borane (NH3BH3) under the synthesis conditions of about 110 GPa and 2100 K. The synthesized ternary alloy was maintained to at least 90 GPa during decompression. Compared with binary CeH9, the Tc is dramatically increased by up to 80 K in ternary (La,Ce)H9, which contains an unprecedented LaH9 unit that is unstable in pure compound form but stabilized in the base binary CeH9 structural framework. This atypical compositional structure unit, together with the reduction of possible Abrikosov-Gor’kov suppression-like effect37 of Ce by replacing with La, have a critical impact on the enhancement of Tc of the ternary (La,Ce)H9 alloy. The present findings demonstrate that substitutional alloying is effective in tuning and improving high-temperature superconductivity in superhydrides by stabilizing new and unusual structural and compositional configurations that are conducive to greatly enhanced Tc, and this approach may be extended to constructing additional ternary and higher multinary alloys to usher in more breakthrough discoveries in the quest of finding optimal clathrate superhydrides through a thoughtful choice of substitutional alloying metal-element combinations.
Synthesis of ternary (La,Ce)H9 alloy superhydride
We took a flake of La-Ce alloy sample from a homogeneous region of the inside part of the specimen and loaded it into a diamond anvil cell (DAC) with NH3BH3 as the pressure transmitting medium and hydrogen source. A total of seven samples were compressed to 110–125 GPa at room-temperature and then heated to 2100–2300 K with pulsed radiation from an yttrium-aluminum-garnet laser (Supplementary Table 1). The color of the sample changed significantly after laser spot irradiation (Fig. 1), indicating that the expected chemical reaction occurred. After keeping the synthesized samples under high pressure while quenching to room-temperature, we performed subsequent structure and superconductivity characterizations.
Crystal structure of synthesized (La,Ce)H9
To determine the crystal structure of synthesized La-Ce superhydride, we conducted in-situ X-ray diffraction (XRD) experiments in synchrotron radiation sources. The representative XRD pattern of the product in Cell-4 at 110 GPa is shown in Fig. 2a. The observed peaks can be indexed by an hcp (P63/mmc) lattice with cell parameters of a = 3.762(6) Å and c = 5.675(5) Å (Supplementary Table 2). The weak peaks marked with asterisks are from the tetragonal tetrahydride reported in previous studies21,22, which is a common occurrence caused by temperature or pressure gradients during high-temperature and high-pressure synthesis. Notably, in this measured hcp lattice, there is only one Wyckoff 2d metal position, but it has to accommodate two different elements of La and Ce, each of which occupies the metal position at a probability of ~50% since the molar ratio of La: Ce is at ~1:1. As a result, there is a formation of a substitutional hcp La/Ce alloy in the metal lattice. Since La and Ce share highly similar X-ray scattering factors, it is impossible to determine the La/Ce ratio through the Rietveld refinement. Instead, we determine the ratio by a true observation. We note that in the XRD data, besides the peaks for the synthesized product, there is absence of any peaks that correspond to those for elemental La and Ce phases. This suggests that the precursor of La-Ce alloy with a molar ratio of La: Ce at ~1:1 (Supplementary Tables 3–5 and Figs. 1–4), fully reacts with hydrogen for the formation of hydrides. As a result, La/Ce ratio in the formed hydride can be concluded as 50% to 50%. A similar hcp structure mixed with tetrahydride was successfully reproduced at 115 GPa in another independent experimental run (Supplementary Figs. 5 and 8), corroborating the reliability of this structure.
Although the occupancy details of the hydrogen atoms cannot be determined experimentally due to the weak X-ray scattering cross section, the measured unit cell volume (Vlattice) can be used to estimate the hydrogen concentration of the superhydride. While the volumes (VLa, VCe, and VH) of La, Ce, and H atoms are not known, they have to be estimated from their elemental phases. Specifically, at 110 GPa, phase structures of distorted-fcc for La38, of bct for Ce39, and of hcp for H240 are adopted where VLa, VCe, and VH are calculated to be ~16.04, ~14.59, and ~2.30 Å3/atom, respectively. As a result, the hydrogen content (n) of the synthesized La-Ce alloy hydrides was determined as ~8.5 using the formula of n = (Vlattice – VLa – VCe)/VH/2, which has a small deviation with the ideal value of 9. Numerical error in this calculation is inevitable, and it comes from the direct use of elemental phases for the evaluation of volumes. It is expected that once a compound is formed the volume of constituted elements will somewhat change compared with their elemental phases. Furthermore, the experimental equation of state (EOS) during decompression is highly consistent with the simulated EOS (Supplementary Fig. 6), where most of the experimental points lie between the lines of hcp CeH9 and hypothetical hcp LaH9. Combined with the composition of the original alloy sample, our diffraction experiments show that ~50% of the Ce atoms in the recently discovered structure of P63/mmc-CeH9 are replaced by La, forming a unique ternary alloy superhydride P63/mmc-(La,Ce)H9 (Fig. 2b).
Superconductivity in (La,Ce)H9
To probe superconductivity in the synthesized alloy superhydride, we performed electrical transport measurements. Representative measured electrical resistance data as a function of temperature are shown in Fig. 3, which clearly shows the superconducting transition, as indicated by the sharp drops in resistance occurring at 158 K, 168 K, and 173 K at about 110 GPa, 125 GPa, and 110 GPa, respectively. In these experiments, zero resistance states were observed in Cell-1 and Cell-4 (Fig. 3 inset). To determine the highest value of Tc, we proceeded to regulate the pressure dependence on Tc, as shown in Fig. 4. With the increase of pressure, Tc increases first and then tends to be flat. The highest Tc of 178 K in this work was observed at 172 GPa (Supplementary Figs. 9–14). Our Rietveld refinement of the synthesized products indicates that the major (~96.2 At%) phase is P63/mmc-(La,Ce)H9 with a tiny amount of impurity (~3.8 At%) being as I4/mmm-(La,Ce)H4 (Fig. 2a). In our four-probe van der Pauw experiment for the superconductivity measurement, the chance is extremely low if the four separate electrodes simultaneously touch the minor phase of the sample. Notably, our experimental superconductivity is quite reproducible at least for six different runs of experiments. This suggests that the experimentally observed superconductivity is unlikely originated from the minor phase. Moreover, it should also be pointed out that the minor phase of I4/mmm-(La,Ce)H4 would not hold such high superconductivity at Tc = 148–178 K observed in this study. For a good comparison, its isostructural phase in a lighter hydride of YH4 shows much lower superconductivity at 76–88 K41,42,43. It is expected that the heavier hydride of (La,Ce)H4 should possess even lower Tc values than that in YH4. Therefore, the measured superconductivity is associated with major (La,Ce)H9 rather than minor (La,Ce)H4. With decreasing pressure, the superconducting transition tends to disappear at about 90 GPa (Supplementary Fig. 11), indicating a probable decomposition of the superconducting phase.
Owing to the rather small size of the samples, it is still a challenging task to measure the weak signals of the magnetic flux expulsion (i.e., Meissner) effect under high pressures10,20. However, due to the Pauli paramagnetic effect of electron spin polarization and the diamagnetic effect of orbital motion, an applied external field can disrupt the Cooper pairs, thereby reducing the value of Tc. As shown in Fig. 5a, the resistance drop gradually shifts to lower temperatures as the magnetic field increases in the range of 0–9 T at 110 GPa. Combined with the observed zero resistance, it can rule out the possibility that the abrupt drop of resistance on cooling arises from structural transitions. The upper critical field as a function of temperature, defined as 90% (10%) of the resistance, is shown in the inset of Fig. 5b, c. At μ0H = 9 T, the application of the magnetic field reduces Tc by about 12 K (14 K). The extrapolated values of the upper critical field μ0Hc2(T) and the coherence lengths towards T = 0 K are 56 T (52 T) and 24 Å (25 Å) and 76 T (70 T) and 21 Å (22 Å), respectively, by Ginzburg-Landau (GL)44 and Werthamer-Helfand-Hohenberg (WHH)45 model fits. The obtained μ0Hc2 data and coherence lengths following the 10% criterion of the metallic state resistance are similar to those derived from the use of 90% resistance. The magnitude of the short coherence lengths and high upper critical fields indicate that ternary (La,Ce)H9 is a typical type-II superconductor. We note that the similar superconductivity of ternary La-Ce-H system was observed by two different groups46,47 during the preparation of our manuscript.
The clathrate REH9 phase with H29 cage was predicted8 to be a high-temperature superconductor in 2017, and this structural prototype has since been experimentally verified by a series of RE metal superhydrides48,49,50,51. Of particular interest among these compounds is CeH9 that was synthesized at easily achievable megabar pressure and exhibited an experimental Tc of ~95 K21. Compared to the higher-Tc LaH109,10,36, the low Tc of CeH9 stems from its low logarithmic average phonon frequency, which may be related to the 4f electron in Ce at high pressure24. Furthermore, no superconductivity or only low-temperature superconductivity was observed in other similar RE metal superhydrides, where strongly correlated interactions of 4f electrons dramatically suppress the superconductivity24,48,49,50,51,52. It has been reported that the superconductivity of LaH10 was dramatically suppressed by doped Nd53 (each atomic percent of Nd causes a decrease in Tc of 10–11 K), which can be reasonably understood by the well-known impure superconductor theory proposed by Abrikosov and Gor’kov37. If half of the weakly magnetic Ce in CeH9 is replaced by non-magnetic La, Abrikosov-Gor’kov suppression-like effect of Ce should be significantly weakened, resulting in the giant lift of Tc in (La,Ce)H9 over that in CeH9. This analysis points to rational improvement of superconductivity in CeH9 via substitution of Ce by La that hosts no 4f electron but otherwise shares most chemical characters.
In addition, the pressure dependence of Tc varies slightly in different experiments, which may originate from subtle differences in molar ratios of the La-Ce alloy polyhydride samples or different degrees of anisotropic stress that leads to variable deformation of the lattice in different experiments54. Moreover, the observed c/a ratio (1.511) of the synthesized hcp (La,Ce)H9 at 110 GPa is smaller than the ideal value of 1.633. This indicates that the structure is not isotropic, which may play somewhat role in regulating superconductivity.
Although hcp LaH9 is calculated to be thermodynamically unstable8 and unlikely to be synthesized among binary system at the corresponding pressure of ~100 GPa, the LaH9 structural unit appears in synthesized ternary La-Ce alloy superhydride via La-substitution modification of the native CeH9 units. This result can be elucidated by the Hume-Rothery rule55, because the ratio of La/Ce atomic radii (~1.032 at 110 GPa)38,39 is well within the rule’s stated 15% range, and La and Ce have similar electronegativity values33, thus satisfying the conditions for the formation of a disordered solid solution compound. Moreover, laser heating helps to overcome the kinetic reaction barrier and stabilize substitutional (La,Ce)H9 via the contribution of the configurational entropy to the total free energy, overcoming the contribution of mixing enthalpy and the energy increment of LaH9 relative to LaH10 at a sufficiently high temperature34. In particular, the configurational entropy reaches the maximum in an equal-atomic distribution and plays a significant role in stabilizing ternary (La,Ce)H9. This effect should be more pronounced in higher multinary superhydrides, such as equiatomic medium- or high-entropy alloy superhydrides. Further theoretical examination and experimental verification are needed.
In conclusion, we discovered a giant Tc enhancement in equal-atomic substitutional ternary alloy (La,Ce)H9 that exhibits high Tc values of 148–178 K in the pressure range of 97–172 GPa examined in this work. These Tc values are significantly higher, by up to 80 K, compared to the results found in binary CeH9, which represents a giant, 80% enhancement. This ternary alloy superhydride integrates the native CeH9 structural units and the atypical LaH9 units that are unstable in pure compound form but stabilized by optimal configurational entropy under the laser-heated DAC compression synthesis conditions. These results show that substitutional alloying is an effective and promising approach to tune and improve superconducting superhydrides, leading to the long-sought scenario of high-temperature superconductivity at relatively lower pressures. The present findings also provide insights for expanding the scope of ongoing studies in search of room-temperature superconductors among diverse compounds via construction of multinary alloys via suitable metal-atom substitution.
La-Ce alloy (commercial product, 1:1 in molar ratio) was prepared by levitation melting technology, where mixed elemental La and Ce with purity of 99.7% were heated to completely melt in an Ar atmosphere at a pressure of 60 KPa for 1–2 min and then were annealed for about 40 min. To ensure the uniformity of the composition, the specimen ingot needed to be turned over and the above process was repeated more than twice. The 1:1 molar ratio and homogeneity of La-Ce alloy were further confirmed by our own experiments using inductively coupled plasma atomic emission spectroscopy (Thermo Fisher iCAP PRO) and scanning electron microscope (JEM-2000FS, Regulus 8100, and ZEISS Gemini 300) equipped for the energy dispersive X-ray spectroscopy.
Synthesis in diamond anvil cell
We synthesized the superhydrides via a reaction of La-Ce alloy and NH3BH3 (Sigma-Aldrich, 97%) in diamond anvil cells (DACs). The diamond anvils with culets of 60–100 µm in diameter were beveled at 8.5° to about 250 µm in diameter. A composite gasket consisting of a rhenium outer annulus and an aluminum oxide (Al2O3) epoxy mixture insert was employed to contain the sample while isolating the electrical leads in the electrical measurements. La-Ce alloy foil with a thickness of 2–3 µm was sandwiched between NH3BH3. Sample preparation and loading were done in an inert Ar atmosphere with residual O2 and H2O contents of <0.01 ppm to guarantee that the sample was properly isolated from the surrounding air atmosphere. The samples were compressed to target pressures at room-temperature. The pressure values in cells were determined from room-temperature first-order diamond Raman edge calibrated by Akahama56,57. One-side laser-heating experiments were performed using a pulsed YAG laser (1064 nm) with spots of ~10 μm in diameter. The temperature was determined using the emission spectrum of the black body radiation within Planck’s radiation law.
X-ray diffraction (XRD) patterns were obtained at BL15U1 (λ = 0.6199 Å) of Shanghai Synchrotron Radiation Facility and BL10XU (λ = 0.4131 Å) of at the SPring-8 facility58 with focused monochromatic X-ray beams (5 × 12 and 3 × 2 µm2). A Mar165 CCD detector and an imaging plate detector (RAXIS-IV; Rigaku) were used to collect the angle-dispersive XRD data. The sample to detector distance and other geometric parameters were calibrated using a CeO2 standard. The software package Dioptas was used to integrate powder diffraction rings and convert the 2-dimensional data to 1-dimensional profiles59. The full profile analysis of the diffraction patterns and the Rietveld refinements were done using GSAS and EXPGUI packages60.
Electrical transport measurement
The resistance was all measured via the four-probe van der Pauw method where four Au electrodes were placed on the NH3BH3 plate with currents of 1–100 µA. The temperature dependence of the electrical resistance was measured upon cooling and warming cycles with a slow temperature ratio (0.2–0.3 K min−1). The data was taken upon warming, as it yielded a more accurate temperature reading. Symmetric Cu-Be alloy DACs were used for electronic transport measurements under external magnetic fields up to 9 T.
The authors declare that the main data supporting the findings of this study are contained within the paper and its associated Supplementary Information. All other relevant data are available from the corresponding author upon reasonable request.
Onnes, H. K. The resistance of pure mercury at helium temperatures. Comm. Phys. Lab. Univ. Leiden 12, 1 (1911).
Nagamatsu, J., Nakagawa, N., Muranaka, T., Zenitani, Y. & Akimitsu, J. Superconductivity at 39 K in magnesium diboride. Nature 410, 63–64 (2001).
Bednorz, J. G. & Müller, K. A. Possible high Tc superconductivity in the Ba-La-Cu-O system. Z. Phys. B 64, 189–193 (1986).
Duan, D. et al. Pressure-induced metallization of dense (H2S)2H2 with high-Tc superconductivity. Sci. Rep. 4, 6968 (2014).
Li, Y., Hao, J., Liu, H., Li, Y. & Ma, Y. The metallization and superconductivity of dense hydrogen sulfide. J. Chem. Phys. 140, 174712 (2014).
Drozdov, A. P., Eremets, M. I., Troyan, I. A., Ksenofontov, V. & Shylin, S. I. Conventional superconductivity at 203 K at high pressures. Nature 525, 73–76 (2015).
Liu, H., Naumov, I. I., Hoffmann, R., Ashcroft, N. W. & Hemley, R. J. Potential high-Tc superconducting lanthanum and yttrium hydrides at high pressure. Proc. Natl Acad. Sci. USA 114, 6990–6995 (2017).
Peng, F. et al. Hydrogen clathrate structures in rare earth hydrides at high pressures: possible route to room-temperature superconductivity. Phys. Rev. Lett. 119, 107001 (2017).
Somayazulu, M. et al. Evidence for superconductivity above 260 K in lanthanum superhydride at megabar pressures. Phys. Rev. Lett. 122, 027001 (2019).
Drozdov, A. P. et al. Superconductivity at 250 K in lanthanum hydride under high pressures. Nature 569, 528–531 (2019).
Snider, E. et al. Room-temperature superconductivity in a carbonaceous sulfur hydride. Nature 586, 373–377 (2020).
Service, R. F. Superconductor finding draws pointed critique. Science 374, 520–521 (2021).
Service, R. F. Criticism of room temperature superconductor ‘temporarily removed’ from journal. N. Sci. https://doi.org/10.1126/science.acx9668 (2021).
Service, R. F. Preprint server removes ‘inflammatory’ papers in superconductor controversy. N. Sci. https://doi.org/10.1126/science.adb2023 (2022).
Wang, H., Tse, J. S., Tanaka, K., Iitaka, T. & Ma, Y. Superconductive sodalite-like clathrate calcium hydride at high pressures. Proc. Natl Acad. Sci. USA 109, 6463–6466 (2012).
Ma, L. et al. High-temperature superconducting phase in clathrate calcium hydride CaH6 up to 215 K at a pressure of 172 GPa. Phys. Rev. Lett. 128, 167001 (2022).
Li, Z. et al. Superconductivity above 200 K discovered in superhydrides of calcium. Nat. Commun. 13, 2863 (2022).
Troyan, I. A. et al. Anomalous high‐temperature superconductivity in YH6. Adv. Mater. 33, 2006832 (2021).
Kong, P. et al. Superconductivity up to 243 K in the yttrium-hydrogen system under high pressure. Nat. Commun. 12, 5075 (2021).
Snider, E. et al. Synthesis of yttrium superhydride superconductor with a transition temperature up to 262 K by catalytic hydrogenation at high pressures. Phys. Rev. Lett. 126, 117003 (2021).
Chen, W. et al. High-temperature superconducting phases in cerium superhydride with a Tc up to 115 K below a pressure of 1 megabar. Phys. Rev. Lett. 127, 117001 (2021).
Li, X. et al. Polyhydride CeH9 with an atomic-like hydrogen clathrate structure. Nat. Commun. 10, 3461 (2019).
Salke, N. P. et al. Synthesis of clathrate cerium superhydride CeH9 at 80-100 GPa with atomic hydrogen sublattice. Nat. Commun. 10, 4453 (2019).
Semenok, D. V., Kruglov, I. A., Savkin, I. A., Kvashnin, A. G. & Oganov, A. R. On distribution of superconductivity in metal hydrides. Curr. Opin. Solid State Mater. Sci. 24, 100808 (2020).
Hilleke, K. P. & Zurek, E. Tuning chemical precompression: theoretical design and crystal chemistry of novel hydrides in the quest for warm and light superconductivity at ambient pressures. J. Appl. Phys. 131, 070901 (2022).
Sun, Y., Lv, J., Xie, Y., Liu, H. & Ma, Y. Route to a superconducting phase above room temperature in electron-doped hydride compounds under high pressure. Phys. Rev. Lett. 123, 097001 (2019).
Zhang, X., Zhao, Y. & Yang, G. Superconducting ternary hydrides under high pressure. WIREs Comput. Mol. Sci. 12, e1582 (2022).
Liang, X. et al. Prediction of high-Tc superconductivity in ternary lanthanum borohydrides. Phys. Rev. B 104, 134501 (2021).
Cataldo, S. D. et al. First-principles search of hot superconductivity in La-X-H ternary hydrides. NPJ Comput. Mater. 8, 2 (2022).
Zhang, Z. et al. Design principles for high-temperature superconductors with a hydrogen-based alloy backbone at moderate pressure. Phys. Rev. Lett. 128, 047001 (2022).
Liang, X. et al. Potential high-Tc superconductivity in CaYH12 under pressure. Phys. Rev. B 99, 100505 (2019).
Sukmas, W., Tsuppayakorn-aek, P., Pinsook, U. & Bovornratanaraks, T. Near-room-temperature superconductivity of Mg/Ca substituted metal hexahydride under pressure. J. Alloy. Compd. 849, 156434 (2020).
Rahm, M., Cammi, R., Ashcroft, N. W. & Hoffmann, R. Squeezing all elements in the periodic table: electron configuration and electronegativity of the atoms under compression. J. Am. Chem. Soc. 141, 10253–10271 (2019).
George, E. P., Raabe, D. & Ritchie, R. O. High-entropy alloys. Nat. Rev. Mater. 4, 515–534 (2019).
Semenok, D. V. et al. Superconductivity at 253 K in lanthanum–yttrium ternary hydrides. Mater. Today 48, 18–28 (2021).
Sun, D. et al. High-temperature superconductivity on the verge of a structural instability in lanthanum superhydride. Nat. Commun. 12, 6863 (2021).
Abrikosov, A. A. & Gor’kov, L. P. Contribution to the theory of superconducting alloys with paramagnetic impurities. Zhur. Eksptl’. i Teor. Fiz. 39, 1782–1796 (1960).
Chen, W. et al. Superconductivity and equation of state of lanthanum at megabar pressures. Phys. Rev. B 102, 134510 (2020).
Vohra, Y. K. & Beaver, S. L. Ultrapressure equation of state of cerium metal to 208 GPa. J. Appl. Phys. 85, 2451–2453 (1999).
Ji, C. et al. Ultrahigh-pressure isostructural electronic transitions in hydrogen. Nature 573, 558–562 (2019).
Li, Y. et al. Pressure-stabilized superconductive yttrium hydrides. Sci. Rep. 5, 9948 (2015).
Shao, M., Chen, W., Zhang, K., Huang, X. & Cui, T. High-pressure synthesis of superconducting clathratelike YH4. Phys. Rev. B 104, 174509 (2021).
Wang, Y. et al. Synthesis and superconductivity in yttrium superhydrides under high pressure. Chinese Phys. B 31, 106201 (2022).
Ginzburg, V. L. & Landau, L. D. On the theory of superconductivity. Zh. Eksp. Teor. Fiz. 20, 1064–1082 (1950).
Helfand, E. & Werthamer, N. R. Temperature and purity dependence of the superconducting critical field, Hc2. Phys. Rev. Lett. 13, 686 (1964).
Chen, W. et al. Enhancement of the superconducting critical temperature realized in the La-Ce-H system at moderate pressures. Preprint at https://doi.org/10.48550/arXiv.2203.14353 (2022).
Huang, G. et al. Synthesis of superconducting phase of La0.5Ce0.5H10 at high pressures. Preprint at https://doi.org/10.48550/arXiv.2208.05199 (2022).
Zhou, D. et al. High-pressure synthesis of magnetic neodymium polyhydrides. J. Am. Chem. Soc. 142, 2803–2811 (2020).
Ma, L. et al. Experimental clathrate superhydrides EuH6 and EuH9 at extreme pressure conditions. Phys. Rev. Res. 3, 043107 (2021).
Zhou, D. et al. Superconducting praseodymium superhydrides. Sci. Adv. 6, eaax6849 (2020).
Semenok, D. V. et al. Novel strongly correlated europium superhydrides. J. Phys. Chem. Lett. 12, 32–40 (2020).
Song, H. et al. High Tc superconductivity in heavy rare earth hydrides. Chin. Phys. Lett. 38, 107401 (2021).
Semenok, D. V. et al. Effect of paramagnetic impurities on superconductivity in polyhydrides: s-wave order parameter in Nd-doped LaH10. Preprint at https://arxiv.org/abs/2203.06500 (2022).
Errea, I. et al. Quantum crystal structure in the 250-kelvin superconducting lanthanum hydride. Nature 578, 66–69 (2020).
Hume-Rothery, W., Mabbott, G. W. & Channel Evans, K. M. The freezing points, melting points, and solid solubility limits of the alloys of sliver and copper with the elements of the b sub-groups. Philos. Trans. R. Soc. Lond. A Contain. Pap. Math. Phys. Character 233, 1–97 (1934).
Baer, B. J., Chang, M. E. & Evans, W. J. Raman shift of stressed diamond anvils: pressure calibration and culet geometry dependence. J. Appl. Phys. 104, 034504 (2008).
Akahama, Y. & Kawamura, H. Pressure calibration of diamond anvil Raman gauge to 310 GPa. J. Appl. Phys. 100, 043516 (2006).
Hirao, N. et al. New developments in high-pressure X-ray diffraction beamline for diamond anvil cell at SPring-8. Matter Radiat. Extrem. 5, 018403 (2020).
Prescher, C. & Prakapenka, V. B. DIOPTAS: a program for reduction of two-dimensional X-ray diffraction data and data exploration. High. Press. Res. 35, 223–230 (2015).
Toby, B. H. EXPGUI, a graphical user interface for GSAS. J. Appl. Crystallogr. 34, 210–213 (2001).
We thank Professor Changfeng Chen for a critical reading and extensive refining of the paper. This research was supported by the National Key Research and Development Program of China (Grant No. 2021YFA1400203), the National Natural Science Foundation of China under Grants No. 12074139, No. 11874175, 12074138, and 52090024; Interdisciplinary Integration and Innovation Project of Jilin University (JLUXKJC2020311), Fundamental Research Funds for the Central Universities (Jilin University, JLU), Program for JLU Science and Technology Innovative Research Team, the Strategic Priority Research Program of Chinese Academy of Sciences (Grant No. XDB33000000). The work was also supported by JSPS KAKENHI Grant Numbers 20H05644. The XRD measurements were performed at the BL15U1 at Shanghai Synchrotron Radiation Facility and the BL10XU of SPring-8 (Proposal No. 2021A1172 and 2021B1407).
The authors declare no competing interests.
Peer review information
Nature Communications thanks Malcolm Guthrie and the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Bi, J., Nakamoto, Y., Zhang, P. et al. Giant enhancement of superconducting critical temperature in substitutional alloy (La,Ce)H9. Nat Commun 13, 5952 (2022). https://doi.org/10.1038/s41467-022-33743-6
This article is cited by
Enhancement of superconducting properties in the La–Ce–H system at moderate pressures
Nature Communications (2023)