Abstract
Sustainable afterglow room temperature phosphorescence (RTP) materials, especially afterglow RTP structural materials, are crucial but remain difficult to achieve. Here, an oxidation strategy is developed to convert lignin to afterglow materials with a lifetime of ~ 408 ms. Specifically, lignin is oxidized to give aromatic chromophores and fatty acids using H2O2. The aromatic chromophores are locked by a fatty acid-based matrix by hydrogen bonds, triggering enhanced spin orbit coupling and long afterglow emission. More interestingly, motivated by this discovery, an auto fabrication line is built to convert wood (natural structural materials) to wood with afterglow RTP emission (RTP wood) via in situ oxidation of naturally-occurring lignin located in the wood cell walls to oxidized lignin (OL). The as-prepared RTP wood exhibits great potential for the construction of sustainable afterglow furniture. With this research we provide a new strategy to promote the sustainability of afterglow RTP materials and structural materials.
Similar content being viewed by others
Introduction
Plant biomass is a potential source of renewable chemicals and materials1,2. Lignin, one of its main components accounting for 15–30% of the total mass, forms via the oxidative polymerization of p-hydroxycinnamyl alcohol monolignols coming from the phenylpropanoid pathway3. Additionally, technical lignin is produced as a byproduct of pulp and paper industry in very large quantities (~60–70 Mt per year)4,5. The need for lignin valorization has become well understood in the scientific community, which has given rise to a large number of studies being published over the last several years6,7. From a chemical perspective, lignin mainly consists of p-hydroxyphenyl (H), guaiacyl (G) and syringyl (S) units, linked primarily by β-O-4 and C-C bonds8,9. This chemical structure endows lignin with great potential as for a core component for functional materials and aromatic compounds10,11,12. Moreover, lignin exhibited interesting bioactivity, facilitating applications in biomedicine, agriculture, and biomass conversion13,14. Attributed to the incorporated aromatic structures, lignin can generate interesting photo physicochemical properties15,16. Recently, our group demonstrated that afterglow RTP emission of lignin can be achieved through encapsulation in a polyacrylic acid matrix17.
Afterglow RTP materials have wide applications in electronic devices, optical sensing, biological imaging and information encryption18,19. To achieve effective RTP, two crucial conditions should be satisfied. First, the triplet excitons could be effectively populated by facilitating ISC from S1 to Tn. Second, the nonradiative deactivation of triplet excitons is suppressed and the radiative transition is promoted from the lowest excited triplet state (T1) to the ground state (S0)20. Until now, small molecules, polymers, supramolecules, carbon dots and MOFs have been reported for the effective afterglow RTP emission21,22. In particular, preparing afterglow RTP materials from natural sources, are particularly sought after since natural sources are abundant, sustainable, flexible and biocompatible23,24. Nevertheless, two main challenges remain: (1) Converting sustainable lignin to afterglow RTP materials requires the use of a petrol-derived matrix (~95 w/w%), which does not meet the requirements for a sustainable system17. (2) Most of afterglow RTP materials, including lignin-derived afterglow RTP materials, exist as powders, crystals, films, liquids or porous materials25,26,27,28,29,30,31,32. However, very few afterglow RTP structural materials have been reported, yet they exhibit high mechanical performance and are crucial in materials science and technology33.
Here, we developed an oxidation method for converting lignin to sustainable afterglow RTP materials without the addition of additional synthetic matrix. Specifically, the G units and S units of lignin were oxidized to give G acids and S acids (chromophores), which are then in situ locked by fatty acids (as matrix, also due to lignin oxidation) via hydrogen bonding (Fig. 1a). As a result, the OL exhibits efficient afterglow emission. More interestingly, motivated by this discovery, an auto fabrication line was built to convert wood, a natural structural material, to RTP wood via in situ oxidation of naturally occurring lignin located in the wood cell walls to OL (Fig. 1b). The as-prepared RTP wood exhibited great potential for constructing afterglow sustainable furniture.
Results
RTP emission of OL
The ultraviolet-visible (UV-Vis) spectra of OL (prepared from lignosulfonates, see the details in the methods) exhibits optical absorbance predominantly in the UV region, over the wavelength range from 200 nm to 400 nm (Supplementary Fig. 1). OL exhibited a decreased absorbance, compared to the raw lignin (Supplementary Fig. 2). Raw lignin and OL also exhibited obvious differences in the FT-IR spectra (Supplementary Fig. 3). The signal intensity of -C = O at 1704 cm−1 and -O-H at 3300 cm−1 increased after lignin oxidation. A decrease in the molecular weight of lignin after oxidation was observed using gel permeation chromatography (GPC) (Supplementary Fig. 4). The weight-average molecular weight of lignin decreased from 11541 to 1588 after oxidation. Thermogravimetric analysis (TGA) and derivative thermogravimetry (DTG) were also investigated before and after lignin oxidation (Supplementary Fig. 5). These results indicated that lignin degraded into small fragments after oxidation. Upon UV irradiation, OL exhibited strong fluorescence emission, centered at ~464 nm (Fig. 2a). Surprisingly, afterglow RTP emission was also observed, with phosphorescence centered at ~525 nm. Time-resolved spectroscopy indicated that the OL displays a long-lasting and stable afterglow emission and retained weak phosphorescence emission at the same emission wavelength for as long as 800 ms (Fig. 2b). The lifetime of OL was ~408 ms (Supplementary Fig. 6). Moreover, excitation-independent RTP emission of OL was observed. The RTP emission wavelength red shifted from 460 nm to 550 nm when the excitation wavelength changed from 275 nm to 400 nm, indicating multiple chromophores in OL (Fig. 2c). Additionally, to illustrate the generality of our strategy, another technical lignin, alkali lignin, was also treated using the same method to obtain OL. As expected, the as-prepared OL from alkali lignin produced efficient afterglow RTP emission with a lifetime of ~215 ms (Supplementary Fig. 7). The afterglow RTP was found to be humidity-sensitive, with reduction of the phosphorescence lifetime when the humidity was gradually increased. In particular, the phosphorescence lifetime dropped rapidly from ~408 ms to ~102 ms when the humidity increased from 10% to 70% (Fig. 2d). To understand the effect of humidity on the lifetime, OL was exposed to different levels of humidity. The results indicated that the lifetime of OL was completely quenched when the humidity reached 100% (Supplementary Fig. 8). More interestingly, this quenched lifetime was recovered again after drying the OL. The “humidity-drying” sensitive RTP lifetime was stable and it could be recycled 7 times (Supplementary Fig. 9). Notably, OL exhibited a decreased lifetime upon exposure to increased temperature (from 100 −175 oC) for an extended time (~90 min) (Supplementary Fig. 10). It was possibly attributed to decomposition of lignin, as determined by TGA and DTG analysis. Additionally, OL displayed mechanoresponsive RTP. The afterglow RTP lifetime decreased from ~408 ms to ~248 ms when the external pressure increased from 0 MPa to 60 MPa (Supplementary Fig. 11). Additionally, the afterglow emission of OL was stable in organic solvents. The lifetimes were 489.34, 516.55 and 519.84 ms in DCM, ETOH and CH3CN, respectively (Supplementary Fig. 12).
Mechanism investigation
To gain a deeper insight into the mechanism of afterglow RTP emission of OL, a set of experiments was conducted. The 2D heteronuclear singular quantum correlation nuclear magnetic resonance (2D HSQC NMR) indicated that lignin mainly consists of G units and S units in the aromatic region and the ratio of G and S units was 10:90 (Fig. 3a). Lignin also displayed abundant signals between 3.0 ppm and 6.0 ppm, which was attributed to the C-O-C and C-C linkers (Supplementary Fig. 13). After oxidation, most of the signals in the aromatic region (6.2–6.8 ppm, 103–115 ppm) disappeared. In response, the signals of G acids and S acids were observed at 6.6 ppm and 134 ppm, which were exactly the oxidated products from G and S units, respectively. While, OL displayed new signals between 3.0 ppm and 6.0 ppm (Supplementary Fig. 13), probably from fatty acids. To further verify the structural evolution of lignin, high-resolution MS (HRMS) analysis was conducted on an OL sample. As expected, G/S acids were observed in the HRMS spectra (Supplementary Fig. 14). Moreover, fatty acids including sulfonic fatty acids and fatty carboxylic acids were detected, confirming that the 2D HSQC NMR signals between 3.0 and 6.0 ppm were due to fatty acids (Supplementary Fig. 14). Pyrolysis gas chromatography-mass spectrometry (Py-GC-MS) analysis was conducted to further understand the structural change. The results indicated that lignin had degraded into smaller fragments after oxidation (Supplementary Fig. 15 vs Supplementary Fig. 16). According to literature34,35,36, and as-obtained HRMS, Py-GC-MS, and GPC results, the proposed pathways for the oxidative depolymerization of lignin into aromatic acids and fatty acids are shown in Supplementary Fig. 17, which went through oxidative Cα-Cβ cleavage and oxidative ring-open reactions, respectively. All the above results indicate that OL contains both aromatic acids and fatty acids. Theoretical simulation further indicated that the aromatic acids (taking vanillic acid as a model compound) could be “locked” by fatty acids (taking succinic acid as a model compound) by hydrogen bonding in OL (Fig. 3b). The simulation results indicated that carbonyl moieties of the aromatic acids formed intermolecular hydrogen bonds, restricting vibration, which enhances spin-orbit coupling and encourages phosphorescence (Fig. 3c)27. Additionally, the results indicated that the average center-center distance between adjacent molecules was ca. ~0.37 nm, facilitating the formation of strong π - π interactions between the aromatic acids (Fig. 3d). The relative orientation of two neighboring model compounds (θ) was populated over a range from ~60o to 100o with an optimal angle of ~95o, indicating H-type dimers formed between them (Fig. 3e)27,37. Such H-type dimers can stabilize the lowest excited triplet states, and prolong the RTP lifetime. Moreover, the calculation result indicated that the spin-orbit coupling ξ (S1, Tn) of the H-type dimers is larger than that of monomer molecule, facilitating phosphorescence (Fig. 3f). Additionally, urea, as a reagent for breaking hydrogen bonding and reducing the interaction between aromatic acids and fatty acids, was added to powdered OL38. Immediately, the lifetime of OL decreased to ~212 ms when the urea fraction increased to 28% (Supplementary Fig. 18). To demonstrate how the urea affected the OL, theoretical calculations were performed. The interaction force between model aromatic acids and fatty acids was 79.9 kJ/mol and the intermolecular interaction between fatty acids was 78.7 kJ/mol. However, the interaction between urea and fatty acids was 83.7 kJ/mol, which was higher than the interactions with OL and as such can break the hydrogen bonding between aromatic acids and fatty acids (Supplementary Fig. 19). Moreover, the hydrogen bond formed between fatty acids and urea was confirmed by a downfield shift of the carboxyl and amino protons in the 1H NMR (Supplementary Fig. 19). According to the literature39, hydrogen bonds can induce a decrease of electron density near the hydroxyl proton and deshield the nuclei, resulting in a downfield shift of the hydrogen-bonded protons. The above 1H NMR results provide direct experimental evidence for the formation of hydrogen bonds between succinic acid and urea. Additionally, humidity-responsive lifetimes could be attributed to decreased hydrogen bonding between the fatty acids and aromatic acids. This was confirmed by theoretical calculations. Water exhibits stronger binding energy with fatty acids (82.6 kJ/mol) than aromatic acid. As a result, the addition of water can break the hydrogen bonding between the fatty acids and aromatic acids, facilitating the free rotation of the carbonyl moieties and decreasing SOC and ISC. As such, the lifetime decreased upon exposure to high humidity. (Supplementary Fig. 19). Based on all the above results, a plausible mechanism was proposed. Firstly, the oxidation of lignin by H2O2 produced aromatic acids and fatty acids. After that, the aromatic acids became “locked” by fatty acid hydrogen bonds. Finally, the “locking” restricted the vibration of the carbonyl moieties and encouraged the formation of H-type dimers, which promoted spin-orbit coupling and afterglow emission.
Activating RTP of natural wood
Inspired by this discovery, naturally-occurring lignin in wood cell walls was oxidized in situ to generate OL to generate RTP wood. In addition, a smart manufacturing line for RTP wood was constructed. In this line, an automatic manipulator was used to control the immersion of the wood in NaOH and H2O2 solution (Supplementary Fig. 20). Specifically, wood was pretreated by NaOH solution to make the lignin in the cell walls more accessible40. After that, H2O2 solution facilitated in situ oxidation. Thanks to the smart manufacturing line, RTP wood was prepared efficiently (Supplementary Movie 1). UV-Vis spectra indicated that the absorbance intensity at 250-350 nm, was due to the absorbance of lignin41, which decreased significantly after in situ oxidation of the natural wood (Fig. 4a). The as-prepared RTP wood from Basswood after drying exhibited long afterglow RTP emission centered at 510 nm with a lifetime of ~431 ms (Figs. 4b-d). As a control, untreated Basswood displayed phosphorescence emission with a lifetime of 28.25 ms, ~15 times lower than that for RTP wood (Fig. 4e and Supplementary Fig. 21)17. Notably, the wood became more hydrophilic after oxidation, as demonstrated by the decrease in contact angle (from 108 to 55 degree) (Supplementary Fig. 22). Such changes led to a sensitive response of RTP wood to water. Immersing the wood in water immediately quenched its emission (Supplementary Fig. 23). However, the problem can be solved by coating RTP wood with hydrophobic wax. Such coated RTP wood exhibited afterglow emission when it was immersed in water (Supplementary Fig. 24). Moreover, the method for producing RTP wood was widely applicable. For example, different types of wood including peach wood, rubber wood, and Schima superba were efficiently converted to RTP woods using the in situ oxidation method (Fig. 4f-i and Supplementary Fig. 25–27). The lifetimes of RTP wood made from peach wood, rubber wood, and Schima superba increased from 19.53, 70.35 and 60.95 to 284.00, 197.31 and 224.91 ms, respectively (Supplementary Fig. 28). Interestingly, a patterned RTP wood could be achieved by the selective oxidation of the wood surface. As such N shape and 2-D code were patterned on natural wood. After switching off the UV light source, afterglow RTP images could be clearly observed (Fig. 4j, k). Moreover, the 2-D code could be recognized using a smartphone (Fig. 4k and Supplementary movie 2). As a practical demonstration, a series of model afterglow furniture were constructed using RTP wood (Fig. 4l). Upon light irradiation, the furniture made from RTP wood exhibited nice fluorescence. In addition, nice afterglow RTP was observed after switching off the light source. Considering the effect and importance of sustainable indoor lighting materials for the physical and psychological well-being of building occupants, our afterglow furniture has great potential for house decorations.
Discussion
In summary, lignin was successfully converted to sustainable afterglow OL with a lifetime of ~408 ms using an oxidation strategy. More interestingly, motivated by this discovery, an auto fabrication line was built to convert natural wood to RTP wood using in situ oxidation of naturally occurring lignin located in the wood cell walls to generate OL. The RTP wood generated was then successfully processed into afterglow furniture. This work not only demonstrates the sustainability of afterglow RTP materials, but also provides new afterglow RTP structural materials. From a wider perspective, considering the sustainability and ease of processibility of natural wood, such RTP wood could have great potential for wood architecture and light management devices.
Methods
Preparation of OL
Sodium lignosulfonate (Alkali lignin) (2 g) was dispersed in H2O2 solution (10%, 120 mL). The mixture was heated in an oil bath at 120 °C for 8 h. The resulting solution was dried to give OL. The OL powder was then ground and dried at 120 °C for 30 min.
Preparation of RTP Wood
Wood was firstly immersed in NaOH (0.15 g/mL) solution for 3 s. Subsequently, the wood was immersed in H2O2 (30%) for 5 s. The treated wood was then dried at 120 °C for 10 min.
Data availability
All relevant data are included in this article and its Supplementary Information files. Source data are provided with this paper.
References
Chen, C., Berglund, L., Burgert, I. & Hu, L. Wood nanomaterials and nanotechnologies. Adv. Mater. 33, 2006207 (2021).
Droguet, B. E. et al. Large-scale fabrication of structurally coloured cellulose nanocrystal films and effect pigments. Nat. Mater. 21, 352–358 (2022).
Neutelings, G. Lignin variability in plant cell walls: Contribution of new models. Plant Sci. 181, 379–386 (2011).
Ragauskas, A. J. et al. Lignin valorization: Improving lignin processing in the biorefinery. Science 344, 1246843 (2014).
Balakshin, M. Y. et al. New opportunities in the valorization of technical lignins. ChemSusChem 14, 1016–1036 (2021).
Schutyser, W. et al. Chemicals from lignin: an interplay of lignocellulose fractionation, depolymerisation, and upgrading. Chem. Soc. Rev. 47, 852–908 (2018).
Sun, R.-C., Samec, J. S. M. & Ragauskas, A. J. Preface to special issue of ChemSusChem on lignin valorization: From theory to practice. ChemSusChem 13, 4175–4180 (2020).
Subbotina, E. et al. Oxidative cleavage of C–C bonds in lignin. Nat. Chem. 13, 1118–1125 (2021).
Sun, R.-C. Lignin source and structural characterization. ChemSusChem 13, 4385–4393 (2020).
Bertella, S. & Luterbacher, J. S. Lignin functionalization for the production of novel materials. Trends Chem. 2, 440–453 (2020).
Figueiredo, P., Lintinen, K., Hirvonen, J. T., Kostiainen, M. A. & Santos, H. A. Properties and chemical modifications of lignin: Towards lignin-based nanomaterials for biomedical applications. Prog. Mater. Sci. 93, 233–269 (2018).
Wu, X. et al. Solar energy-driven lignin-first approach to full utilization of lignocellulosic biomass under mild conditions. Nat. Catal. 1, 772–780 (2018).
Shu, F. et al. Biological activities and emerging roles of lignin and lignin-based products─A review. Biomacromolecules 22, 4905–4918 (2021).
Zhang, B. et al. Transition-metal-free synthesis of pyrimidines from lignin β-O-4 segments via a one-pot multi-component reaction. Nat. Commun. 13, 3365 (2022).
Li, W., Chen, Z., Yu, H., Li, J. & Liu, S. Wood-derived carbon materials and light-emitting materials. Adv. Mater. 33, 2000596 (2021).
Li, J. et al. Lignin: a sustainable photothermal block for smart elastomers. Green. Chem. 24, 823–836 (2022).
Yuan, J. et al. Sustainable afterglow materials from lignin inspired by wood phosphorescence. Cell Rep. Phys. Sci. 2, 100542 (2021).
Miao, Q. et al. Molecular afterglow imaging with bright, biodegradable polymer nanoparticles. Nat. Biotechnol. 35, 1102–1110 (2017).
Li, Y., Gecevicius, M. & Qiu, J. Long persistent phosphors—from fundamentals to applications. Chem. Soc. Rev. 45, 2090–2136 (2016).
Baryshnikov, G., Minaev, B. & Ågren, H. Theory and calculation of the phosphorescence phenomenon. Chem. Rev. 117, 6500–6537 (2017).
Xu, S., Chen, R., Zheng, C. & Huang, W. Excited state modulation for organic afterglow: materials and applications. Adv. Mater. 28, 9920–9940 (2016).
Zhao, W., He, Z. & Tang, B. Z. Room-temperature phosphorescence from organic aggregates. Nat. Rev. Mater. 5, 869–885 (2020).
Wang, H. & Shi, H. Lignin rebirth enables sustainable afterglow emission. Matter 4, 3087–3088 (2021).
Sun, Y. et al. Ultralong lifetime and efficient room temperature phosphorescent carbon dots through multi-confinement structure design. Nat. Commun. 11, 5591 (2020).
Wu, Z., Nitsch, J. & Marder, T. B. Persistent room-temperature phosphorescence from purely organic molecules and multi-component systems. Adv. Opt. Mater. 9, 2100411 (2021).
Sun, S., Wang, J., Ma, L., Ma, X. & Tian, H. A universal strategy for organic fluid phosphorescence materials**. Angew. Chem. Int 60, 18557–18560 (2021).
Gao, R. & Yan, D. Layered host–guest long-afterglow ultrathin nanosheets: high-efficiency phosphorescence energy transfer at 2D confined interface. Chem. Sci. 8, 590–599 (2017).
Hamzehpoor, E. & Perepichka, D. F. Crystal engineering of room temperature phosphorescence in organic solids. Angew. Chem. Int. Ed. 59, 9977–9981 (2020).
Zhang, G., Palmer, G. M., Dewhirst, M. W. & Fraser, C. L. A dual-emissive-materials design concept enables tumour hypoxia imaging. Nat. Mater. 8, 747–751 (2009).
Su, Y. et al. Ultralong room temperature phosphorescence from amorphous organic materials toward confidential information encryption and decryption. Sci. Adv. 4, eaas9732 (2018).
Cai, S. et al. Ultralong organic phosphorescent foams with high mechanical strength. J. Am. Chem. Soc. 143, 16256–16263 (2021).
Jinnai, K., Kabe, R., Lin, Z. & Adachi, C. Organic long-persistent luminescence stimulated by visible light in p-type systems based on organic photoredox catalyst dopants. Nat. Mater. 21, 338–344 (2022).
Chen, C. et al. Structure–property–function relationships of natural and engineered wood. Nat. Rev. Mater. 5, 642–666 (2020).
Ma, R., Guo, M. & Zhang, X. Selective conversion of biorefinery lignin into dicarboxylic acids. ChemSusChem 7, 412–415 (2014).
Cronin, D. J., Zhang, X., Bartley, J. & Doherty, W. O. S. Lignin depolymerization to dicarboxylic acids with sodium percarbonate. ACS Sustain. Chem. Eng. 5, 6253–6260 (2017).
Cai, Z. et al. Selective Production of diethyl maleate via oxidative cleavage of lignin aromatic unit. Chem 5, 2365–2377 (2019).
An, Z. et al. Stabilizing triplet excited states for ultralong organic phosphorescence. Nat. Mater. 14, 685–690 (2015).
Usha, R. & Ramasami, T. Effect of hydrogen-bond-breaking reagent (urea) on the dimensional stability of rat tail tendon (RTT) collagen fiber. J. Appl. Polym. Sci. 84, 975–982 (2002).
Liu, X. et al. Hydrogen-binding-initiated activation of O-H bonds on a nitrogen-doped surface for the catalytic oxidation of biomass hydroxyl compounds. Angew. Chem. Int. Ed. 60, 18103–18110 (2021).
Xia, Q. et al. In situ lignin modification toward photonic wood. Adv. Mater. 33, 2001588 (2021).
Zhang, Y. & Naebe, M. Lignin: A review on structure, properties, and applications as a light-colored UV absorber. ACS Sustain. Chem. Eng. 9, 1427–1442 (2021).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (31890774 (Z. C.) and 21878288 (C. L.)), the National Key R&D Program of China (Grant No. 2020YFA0709900 (Z.A.)), the Natural Science Funding of Heilong Jiang province for Excellent Young Scholar (YQ2020C017 (Z. C.)) and Science and Technology Bureau of Dalian city (2021RT04 (C. L.)), Royal Society for a Wolfson Research Merit Award and the open Research Fund of the School of Chemistry and Chemical Engineering (T. J.), Henan Normal University for support (2020ZD01 (T. J.)).
Author information
Authors and Affiliations
Contributions
Z.C., Z.A. and C.L. conceived the experiments. Z.C., Z.A., C.L., S.Liu., S.Li., J.L., T.J. and K.W. prepared the paper. K.W., B.T., Y.Z., Y.L., H.W., and W.Y. were primarily responsible for the experiments and calculation. All the authors contributed to the data analysis.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Huining Xiao and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wan, K., Tian, B., Zhai, Y. et al. Structural materials with afterglow room temperature phosphorescence activated by lignin oxidation. Nat Commun 13, 5508 (2022). https://doi.org/10.1038/s41467-022-33273-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-33273-1
This article is cited by
-
Photocured room temperature phosphorescent materials from lignosulfonate
Nature Communications (2024)
-
Full-color, time-valve controllable and Janus-type long-persistent luminescence from all-inorganic halide perovskites
Nature Communications (2024)
-
Photoactivated room temperature phosphorescence from lignin
Nature Communications (2024)
-
Biobased and biodegradable films exhibiting circularly polarized room temperature phosphorescence
Nature Communications (2024)
-
Eco-friendly fractionation of natural straws: sustainable ultralong room-temperature phosphorescence and super anti-ultraviolet materials
Science China Chemistry (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.