Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

# Visualizing rotation and reversal of the Néel vector through antiferromagnetic trichroism

## Abstract

Conventional magnetic memories rely on bistable magnetic states, such as the up and down magnetization states in ferromagnets. Increasing the number of stable magnetic states in each cell, preferably composed of antiferromagnets without stray fields, promises to achieve higher-capacity memories. Thus far, such multi-stable antiferromagnetic states have been extensively studied in conducting systems. Here, we report on a striking optical response in the magnetoelectric collinear antiferromagnet Bi2CuO4, which is an insulating version of the representative spintronic material, CuMnAs, with four stable Néel vector orientations. We find that, due to a magnetoelectric effect in a visible range, which is enhanced by a peculiar local environment of Cu ions, absorption coefficient takes three discrete values depending on an angle between the propagation vector of light and the Néel vector—a phenomenon that we term antiferromagnetic trichroism. Furthermore, using this antiferromagnetic trichroism, we successfully visualize field-driven reversal and rotation of the Néel vector.

## Introduction

Antiferromagnetism is defined as ordered magnetism in which the net magnetization is canceled out because of microscopic spin arrangements. Its excellent features suitable for spintronics applications include the robustness against perturbations, no stray fields, and ultrafast dynamics1,2. Because of the zero net magnetization, antiferromagnets were originally considered less useful as an active component in spintronic devices. This situation has been drastically changed by recent breakthroughs in the electrical control and detection of the orientation of the Néel vector in metallic collinear antiferromagnets such as CuMnAs and Mn2Au3,4. These materials possess a tetragonal crystal structure, and the in-plane colinear antiferromagnetic (AFM) ordering yields four energetically stable AFM domains, corresponding to in-plane 90° rotations of the Néel vector. In addition, although their crystal structure is centrosymmetric, local inversion symmetry at magnetic Mn-ion sites is broken. Consequently, the AFM ordering breaks both the parity (P) and time-reversal (T) symmetries, thus allowing for a current-induced staggered torque, which is responsible for both 90° and 180° Néel vector switching3,4,5,6,7,8. It has also been shown that the P- and T-symmetry breaking supports a full detection of four Néel vector orientations4,7. Thus, tetragonal in-plane colinear antiferromagnets without local inversion symmetry are promising for the development of multistable magnetic memories.

Besides CuMnAs and Mn2Au, multistable memory functionalities have been extensively explored and demonstrated in various antiferromagnets9,10,11,12. These systems are conductive, and the electrical current accompanying Joule heating is typically used to control the domains. In AFM insulators, by contrast, an electric field without Joule heating is available as an option for direct domain control. A well-known control mechanism is the linear magnetoelectric (ME) effect, which is allowed in a system without P and T symmetries13,14. Furthermore, the ME effect in the optical regime15,16,17,18,19,20,21,22,23,24,25,26,27, often called the optical magnetoelectric (OME) effect, can induce peculiar symmetry-dependent optical responses such as nonreciprocal directional dichroism (NDD), that is, a difference in the absorption coefficient (A) between two counter-propagating light beams. Using the OME effect, AFM domains can be optically identified even in fully compensated AFM materials16,24,26. Moreover, spatially resolved visualization of AFM domains via the OME effects has been experimentally demonstrated very recently27. To date, however, there have been only a few reports on AFM materials exhibiting large OME responses, none of which have multistable (three or more) AFM domains.

Here, we report on large visible-light NDD in the ME AFM material Bi2CuO4 (Fig. 1a, b), which is an insulating version of CuMnAs with four stable Néel vector orientations (Fig. 1c). We demonstrate that the NDD combined with tetragonal symmetry of the crystal structure leads to unconventional magnetically induced trichroism, which we call AFM trichroism (Fig. 1d). Furthermore, using the AFM trichroism, we successfully visualize the field-driven reversal and rotation of the Néel vector.

## Results

### Material and concept of AFM trichroism

Generally, NDD in the (near-)visible range is explained in terms of the interference effect between electric-dipole (E1) and magnetic-dipole (M1) transitions through the spin–orbit interaction18,19,20,23,25,26,27. This indicates that NDD will be most pronounced when E1 and M1 transitions are comparable in magnitude with each other. However, the E1 transition, which arises due to a lack of inversion symmetry, is usually much stronger than the M1 transition. A clue to solving this problem is obtained from a previous observation19,23 of gigantic NDD (more than 100% in a ratio of nonreciprocal-to-reciprocal components in absorption coefficient) in an ME material CuB2O4. The NDD in CuB2O4 is dominated by the intra-atomic dd crystal field excitations at a Cu ion, which is square-coordinated by four oxygens forming a CuO4 plane. Importantly, local inversion symmetry at the Cu site is only slightly broken. This allows a weak E1 transition comparable in magnitude with an M1 transition, thus giving rise to the gigantic NDD19. CuB2O4 is not a fully compensated antiferromagnet but a weak ferromagnet and its NDD appears only in an applied magnetic field. However, as the dd crystal-field excitations are largely dominated by a local ligand environment, large spontaneous (zero-field) NDD can be anticipated even in a simple colinear AFM material if it consists of Cu ions with a local ligand environment similar to that in CuB2O4. To examine this expectation, we explore an AFM material that exhibits linear ME effects and possesses multistable domains, as well as consists of square-planar CuO4 units with weak local inversion breaking.

The target material Bi2CuO4 is an insulating antiferromagnet and has recently attracted attention in terms of possible double Dirac fermions under pressure28 and quantum zero-point fluctuation effects on its magnetic anisotropy29. The crystal structure (Fig. 1a) belongs to the centrosymmetric tetragonal space group P4/ncc (ref. 30). Hereafter, we refer to the [110], $$[\bar{1}10]$$ and [001] axes as X, Y, and Z, respectively. Bi2CuO4 consists of isolated square-planar CuO4 units stacked along the Z axis in a twisted manner. Significantly, local inversion symmetry at the Cu sites is slightly broken by a small off-center displacement of the Cu ions along the Z axis (Fig. 1b). Neutron-scattering experiments29,30,31 have indicated that, below the Néel temperature (TN ≈ 44 K), Cu spins form an in-plane colinear spin structure whose direction is parallel to the CuO4 plane and more specifically along the X (or Y) axis29. The AFM ordering changes its magnetic point group from 4/mmm1ʹ to mmʹm, identical to that in CuMnAs (ref. 7). Consequently, the AFM phase may host four equivalent AFM domains specified by the direction of the Néel vector L (L+X, LX, L+Y, and LY), as shown in Fig. 1c. Here, the direction of L is defined as that parallel to that of Cu1 spins. The linear ME effect was observed in the AFM phase31, in agreement with the broken P and T symmetries of the mmʹm group. Therefore, all the above-mentioned requirements for the enhancement of NDD are fulfilled in Bi2CuO4 with multistable AFM domains.

Furthermore, a combination of the possible NDD and the tetragonal symmetry of the crystal structure can lead to the following characteristic optical phenomenon. As discussed in the literature7,32, an AFM phase with the mmʹm symmetry possesses a finite magnetic toroidal moment T (normal to ) with time-reversal-odd polar symmetry32,33,34. Previous studies15,17,18,19,20,21,22,23,24,26 have established that a system having a finite T exhibits NDD, which is given as a difference in absorption coefficient (A) between light beams parallel and antiparallel to fixed T or, equivalently, a difference in A between +T and −T states for a fixed light-propagation direction:

$${A}_{\rm {NDD}}={A}_{{\bf k}\uparrow \uparrow {\bf T}}-{A}_{{\bf k}\uparrow \downarrow {\bf T}}={A}_{\rm {p}}{\hat{\mathbf k}}\cdot \hat{\mathbf T}$$
(1)

where $$\hat{{{{{{\bf{T}}}}}}}$$ and $$\hat{{{{{{\bf{k}}}}}}}$$ represent unit vectors parallel to T and the light-propagation vector k, respectively. The proportionality constant Ap may depend on angular frequency (ω) and polarization (Eω) of light. In Bi2CuO4, T is orthogonal to L (see Fig. 1c, Supplementary Fig. 1, and Supplementary Note 1). Consequently, when k is parallel to the XY plane, Eq. (1) is rewritten as

$${A}_{\rm NDD}={A}_{{\bf k}\uparrow \to {\bf L}}-{A}_{{\bf k}\uparrow \leftarrow {\bf L}}={A}_{\rm p}{\hat{\bf e}}_{Z}\cdot (\hat{\bf k}\times \hat{\bf L})$$
(2)

where $${\hat{{{{{{\bf{e}}}}}}}}_{Z}$$ and $$\hat{{{{{{\bf{L}}}}}}}$$ denote unit vectors parallel to the +Z axis and L, respectively. Both k↑→L and k$${\leftarrow}$$L represent k normal to L, but the direction of either k or L is opposite between k↑→L and k$${\leftarrow}$$L. Equation (2) predicts that a single-domain sample of L+X, for example, exhibits three different values of ANDD (Ap, −Ap, and 0) when viewed from different principal axes of +Y, −Y, and +X/X, respectively (Supplementary Fig. 2a). Notably, the resulting three-level difference in A upon the 90 × n° rotation of k in the XY plane (n = 1–3) is purely induced by the AFM order, because this rotation never changes A in the paramagnetic phase due to its tetragonal symmetry. Therefore, we term this optical phenomenon AFM trichroism, in analogy with conventional trichroism (or triple absorption) observed in biaxial crystals35,36. Furthermore, because the in-plane 90 ×  rotation of k is equivalent with that of L in terms of symmetry, the AFM trichoism can also be viewed as three different absorptions upon the 90 × rotation of L when k is fixed along the X or Y axis (Supplementary Fig. 2b). For example, when kX > 0 (k||+X), ANDD = Ap and −Ap for L+Y and LY, respectively, whereas ANDD = 0 for both L+X and LX. Thus, the AFM trichroism provides an intriguing possibility that three out of four multi-stable L domains can be spatially resolved using the standard optical microscope technique, as conceptually illustrated in Fig. 1d. Based on the linear optics, this imaging method for the multi-stable L domains is much simpler and can be faster compared with existing methods such as second-harmonic generation microscopy10,11 and X-ray magnetic linear dichroism photoemission electron microscopy37.

### NDD in Bi2CuO4

To demonstrate the possibility of the large NDD and the AFM trichroism, we begin by studying NDD spectra in single crystals of Bi2CuO4 (see “Methods” and Supplementary Fig. 3 for the sample characterization). For k||+X, ANDD is obtained as a difference in A between L+Y and LY states, because the 180° switching of L is equivalent to that of k24,26, as found from Eq. (2). We therefore prepare single-domain states of L+Y and LY by cooling the sample from ~50 K (>TN) while applying magnetic (H) and electric (E) fields. This so-called ME cooling relies on the linear ME coupling term in the free energy, αijHiEj. Here, Hi and Ej represent H and E along the i and j (ij = X, Y, Z) directions, respectively, and αij is the linear ME coefficient13. In Bi2CuO4, the L+Y and LY states have finite αYZ (and αZY) with opposite signs32 and hence will be stabilized by HYEZ > 0 and HYEZ < 0, respectively. (For convenience, we assume αYZ > 0 and αYZ < 0 for L+Y and LY, respectively). Note that the L+X and LX states have αYZ = 0 and thus they are not stabilized by HYEZ (ref. 32).

Figure 2a shows two absorption spectra of an X-plane sample for kX > 0 at 4.2 K after ME cooling with μ0HY = +0.15 T and EZ of opposite signs [+100 kV m−1 (blue) and −100 kV m−1 (red)]. The light polarization is set along the Y axis (Eω||Y). To observe spontaneous effects, the cooling magnetic and electric fields were removed before each measurement. It is seen that both spectra start to increase above 1.6 eV, form a broad band centered at approximately 1.75 eV, and then become more intense above 1.9 eV. At temperatures below TN, fine structures develop at photon energies below ~1.7 eV in both spectra (see the inset in Supplementary Fig. 4), although their physical origins are not yet established. The most significant observation here is that the two spectra exhibit a marked difference between 1.6 and 1.9 eV, which is more evident in the difference spectrum, ΔA = A(+100 kV m−1) − A(−100 kV m−1), as displayed in Fig. 2b (purple curve). This finite ΔA is the first evidence for the presence of the NDD. Moreover, the k and L odd nature of ANDD expected from Eq. (2) is ensured by the fact that the ΔA spectrum is completely reversed upon a reversal of either kX (Fig. 2b) or LY with a negative cooling HY (Supplementary Fig. 5). Furthermore, ΔA emerges only in the AFM phase (below TN) with a finite L (Fig. 2c, d). These results demonstrate that ΔA arises from NDD, that is, ΔA = ANDD [Eq. (2)].

The magnitude of the observed ΔA is very large. In particular, the magnitude at 1.65 eV reaches a value as large as 90 cm1 and a relative difference ΔA/Aave exceeding 40%, where Aave is the average of A(+100 kV m−1) and A(−100 kV m−1) (Supplementary Fig. 6). This relative difference is the largest among the reported OME effects in the (near-)visible light region for antiferromagnets [cf. ~0.02% in Cr2O3 (ref. 16) and ~4% in Pb(TiO)Cu4(PO4)4 (ref. 27)]. Therefore, we have experimentally demonstrated that the material exploration based on the weak inversion asymmetric CuO4 square-planar unit is an efficient way to achieve large visible-light NDD in the in-plane colinear AFM material.

### Possible origin of the NDD

To discuss the possible microscopic origin of the large NDD in Bi2CuO4, it is convenient to begin with electronic energy levels of the square-planar CuO46− unit proposed in ref. 38 (see Supplementary Fig. 7a). The square-planar crystal field splits five 3d orbitals of the Cu2+ ion into $${d}_{{z}^{2}}$$, $${d}_{{x}^{2}-{y}^{2}}$$, $${d}_{xy}$$ and $${d}_{xz}({d}_{yz})$$. Here, x, y, and z represent local coordinate axes at the Cu site, with z being parallel to the crystallographic Z axis. Due to the strong covalency of the Cu(3d)-O(2p) bond in Bi2CuO4, each 3d orbital is hybridized with particular 2p orbitals of the four surrounding oxygens, forming bonding and antibonding molecular orbitals. On the basis of the C4 symmetry at the Cu site, we label bonding orbitals as b(x2y2), b(xy), a(z2) and e(xz) [e(yz)], which belong to the irreducible representations of B, B, A, and E, respectively. Bonding-orbital levels in a hole picture, mainly reproduced from ref. 38, are depicted in Fig. 2e. [a(z2) is omitted for clarity since it is both E1- and M1-forbidden (see Supplementary Fig. 7)]. The ground state is b(x2y2) (formed by $${d}_{{x}^{2}-{y}^{2}}$$), whereas the other four excited levels are located in the energy region from 1.4 to 1.7 eV, which roughly coincides with the region where the broad absorption bands are observed (Fig. 2a). Thus, the observed absorption modes in 1.6–1.9 eV are attributable to the intra-cluster transitions between the 3d–2p hybridized orbitals. The increasing absorption above 1.9 eV is likely ascribed to a charge-transfer excitation to bonding orbitals formed by oxygen 2p orbitals (see Supplementary Fig. 7a). Group theory indicates that a transition from b(x2y2) to b(xy) is E1-allowed with Eω||Z, while that to e(xz) and e(yz) is E1-allowed with Eω||Y. Our measurements show that the absorption for Eω||Z is stronger than that for Eω||Y at around 1.6–1.7 eV, while conversely weaker at around 1.7–1.9 eV (Supplementary Fig. 8). This suggests that the b(xy) state and the e(xz) and e(yz) states are located at around 1.6–1.7 eV and 1.7–1.9 eV, respectively. In the following, we pay our attention to the energy region of 1.6–1.7 eV, where we observe the largest NDD.

As mentioned above, the NDD in the (near-)visible range is explained in terms of the interference between E1 and M1 transitions, which is expressed as19,23,25,26

$${\alpha }_{{{{{\rm{NDD}}}}}} ={\alpha }_{+k}-{\alpha }_{-k}\propto {|\langle e|{H}_{\rm E1}+{H}_{\rm M1}|g\rangle |}^{2}-{|\langle e|{H}_{\rm E1}-{H}_{\rm M1}|g\rangle |}^{2}\\ =4{{{{\mathrm{Re}}}}}[\langle {\it{g}}|{\it{H}}_{\rm E1}|{\it{e}}\rangle \langle {\it{e}}|{\it{H}}_{\rm M1}|{\it{g}}\rangle ]$$
(3)

where g (e) represents the wave function of the ground (excited) state and HE1 (HM1) denotes the electric-dipole (magnetic-dipole) transition operator. This indicates that NDD appears only when the transition g → e is both E1- and M1-allowed. Also, Eq. (3) explicitly indicates that a spin–orbit interaction (SOI), HSO = λ(l·s) = λ(lxsx + lysy + lzsz), plays a critical role for NDD25 because $$\langle g|{H}_{\rm E1}|e\rangle$$ and $$\langle e|{H}_{\rm M1}|g\rangle$$ in the absence of SOI are purely real and imaginary, respectively, yielding $${{{{\mathrm{Re}}}}}[\langle {g}|{H}_{\rm {E1}}|{e}\rangle \langle {e}|{H}_{\rm {M1}}|{g}\rangle ]=0$$. Here, l and s are the orbital and spin angular operators, respectively, and λ is the spin-orbit coupling constant. In our experiments with Eω||Y and an oscillating magnetic field of light parallel to the Z axis (Hω||Z), the transition b(x2y2) → b(xy) is M1-allowed but E1-forbidden in the absence of the SOI. When the SOI is switched on, the E1 allowed e(xz) [e(yz)] state is mixed into b(xy) via the λ(lxsx + lysy) term with E symmetry. (The λlzsz term with A symmetry does not allow such a hybridization.) As a result, the transition from b(x2y2) to the modulated b(xy) state becomes both E1 and M1 allowed through the SOI (Fig. 2e and Supplementary Fig. 7c); hence, NDD can emerge.

The fairly large NDD observed in Bi2CuO4 can be ascribed to, first of all, the weak inversion symmetry breaking at the Cu site (Fig. 1b). This can make the E1 transition small and comparable in magnitude with the M1 transition, which enhances the E1-M1 interference effect. Essentially the same scenario has been proposed for the above-mentioned gigantic NDD in CuB2O4 (ref. 19) (see Supplementary Fig. 9 and Supplementary Note 2 for comparisons of NDD between Bi2CuO4 and CuB2O4 in terms of the magnitude and a light-polarization dependence). In addition, because the SOI energy scale set by λ ~ 0.1 eV for the Cu ion is comparable to the energy difference (0.2 ~ 0.3 eV) between the b(xy) and the e(xz) [e(yz)] state, the hybridization between these states can be significant, which may also contribute to the enhancement of the NDD. Finally, because the spin state of the excited states [b(xy), e(xz), and e(yz)] is identical to that of the ground state (since the E1 and M1 transitions considered here preserve the spin state), the orbital hybridization via the lxsx + lysy term contributes to the optical process only when the ground state has the x-(y-)axis spin component that is preserved upon the operation of lxsx (lysy). Thus, the in-plane (xy-plane) nature of the Cu spins in Bi2CuO4 also contributes to the enhancement of the NDD.

### Imaging of the Néel vector and its electric-field reversal

Taking advantage of the large NDD, we visualize the spatial distribution of L in a crystal with optical microscopy. In the experiments, the spatial distribution of the transmitted light intensity from an X-plane sample (i.e., k||X) is recorded using a CMOS camera. Subtracting I at 50 K (I50K) as a paramagnetic reference, we can obtain an effective absorption coefficient Aʹ (i.e., the variation of A from 50 K), $$A^{\prime} =A-{A}_{\rm 50K}=-[{{{{\mathrm{ln}}}}}({\it{I}}/{\it{I}}_{\rm 50K})]/{\it{d}}$$, where d is the sample thickness. Note that the difference between Aʹ for kXLY > 0 and kXLY < 0 corresponds to ANDD. To obtain the maximum ANDD, we choose Eω||Y and a wavelength of 750 nm (which corresponds to a photon energy of 1.65 eV) (see Fig. 2b–d). Figure 3a displays an Aʹ image of an X-plane sample for kX > 0 at 5 K and 0 T after zero-field cooling, showing the strong contrast between the two discrete levels. Moreover, the contrast is reversed for kX < 0 (Fig. 3b) and, as seen in the profiles of Aʹ taken along the same line (from P1 to P2) shown in Fig. 3c, the reversed component in most of the positions amounts to ~80 cm−1, comparable with ANDD ~90 cm−1 at 1.65 eV (Fig. 2b). This means that the dark and bright regions for kX > 0 correspond to the L+Y and LY domains, respectively, and they are distributed uniformly along the depth direction (otherwise the contrast would be weaker). The same domain pattern, albeit with a weaker contrast, is observed for Eω||Z and unpolarized light (Supplementary Fig. 10). Unexpectedly, the L+X and LX domains seem to be absent. The value of Aʹ (Eω||Y) for these domains is expected to be −60 cm−1, which is the middle of −20 and −100 cm−1 for the L+Y and LY domains (Fig. 3c). However, no region with such an Aʹ value is found in the images.

After identifying the domain states, we examine the electric-field switching of L through the ME coupling. First, we cool the sample to 43.7 K (<TN) at zero field and subsequently apply a small bias field (μ0HY = 0.15 T) to obtain a finite switching force (HYEZ). At this initial state, both the L+Y (dark) and LY (bright) domains are present (Fig. 4a). Then, we investigate the evolution of the domains under the application of an electric field (EZ = 0 → +250 → −250 → +250 kV m−1). Selected images and the extracted population of the L+Y domain are shown in Fig. 4b–g and h, respectively. Figure 4h clearly demonstrates that the application of EZ leads to single-domain states [L+Y (Fig. 4b) and L−Y (Fig. 4e)], evidencing a complete EZ-driven L reversal. It is also observed that nucleation of opposite domains occurs only at the sample edges (Fig. 4c, f), and only the L+Y and LY domains appear throughout the reversal (Fig. 4d, g). Thus, the L reversal in Bi2CuO4 is dominated by 180° AFM domain-wall (AFDW) motion.

### Demonstration of AFM trichroism

A promising strategy to create the L+X and LX domains, which is vital for the demonstration of the AFM trichroism, is an application of HY, because L tends to orient perpendicular to the external H. Indeed, a related anomaly is observed in a magnetization curve at ~0.2 T (Supplementary Fig. 3). Figure 5a–c shows a series of Aʹ images in applied fields of 0, 0.36, and 0.58 T. A complete set of Aʹ images and a real-time video of raw images are provided in Supplementary Movies 1 and 2, respectively. At 0.58 T, the image is almost uniform. The Aʹ value approximately coincides with the expected value (−60 cm−1) for the L+X/LX domains (i.e., L+X or LX or both), indicating the existence of the L+X/LX domains. This is further evidenced by a separate imaging experiment with slightly oblique light (Supplementary Fig. 11 and Supplementary Note 3). Therefore, we experimentally demonstrate three different absorptions upon the in-plane 90 × n° rotation of L, that is, the AFM trichroism.

Furthermore, the AFM trichroism reveals a characteristic field evolution of the L domains. Figure 5e–h shows magnified images of the region surrounded by a yellow box in Fig. 5a at selected HY. In Fig. 5i, we also plot the μ0HY dependence of Aʹ in the representative regions labeled as I–VI (Fig. 5e). It is seen that Aʹ in the majority regions (II and VI) gradually changes above ~0.26 T, and the transformation to the L+X/LX domains is complete at ~0.45 T. By contrast, the domain transformation in stripe-shaped regions (I and V) is complete at a smaller field of 0.3 T, whereas the L+Y and LY domains in the respective regions III and IV survive up to about 0.36 T. Thus, the L+X/LX domains evolve in a highly inhomogeneous manner, yielding the coexistence of L+Y, LY, and L+X/LX domains between 0.31 and 0.36 T.

Finally, we discuss several unusual features of the domain states obtained through the AFM trichroism. The first feature is the absence of the L+X/LX domains at 0 T, which contradicts the energy equivalence of the four domains. In the imaging experiments, the X plane of the crystal is fixed to a copper substrate. Likely, a difference in thermal expansion between the sample and the substrate causes a stress on the sample only within the X plane, and the resulting anisotropic thermal stress breaks the original domain degeneracy. The thermal stress could also explain the discrepancy in the domain-transformation field observed in magnetization (~0.2 T) and imaging experiments (~0.35 T), since it should depend on the way the sample is mounted (see Methods). The second feature is the inhomogeneous field-induced domain transformation; it starts to grow from stripe-shaped regions with a slightly weaker contrast at 0 T (I and V) than other regions (Fig. 5e–h). We speculate that these regions contain a small fraction of the L+X/LX domains along the depth direction, which act as a seed for the full growth of the L+X/LX domains. The weaker contrast regions repeatedly appear at approximately the same positions after heating the sample to room temperature (compare Figs. 3a and 5a) and cannot be eliminated by ME cooling (Supplementary Fig. 12). Thus, they likely originate from internal defects. The third feature is the memory effect: the domain pattern at 0 T remains unchanged after applying μ0HY = 0.58 T (compare Fig. 5a and d), except for the yellow circular regions. This suggests that the domain transformation is dominated by a Néel vector rotation within each domain (see also Supplementary Fig. 11 and Supplementary Note 3). The last feature is the field-induced change in the shape of the boundary separating the L+Y and LY domains, i.e., 180° AFDW (Fig. 5e–g). The 180° AFDWs are curved at 0 T, but they become straight perpendicular to the Z axis upon applying H. Such a field-induced change of the 180° AFDW is unusual, and whether it is intrinsic to antiferromagnets with multistable domain states is an interesting future subject.

In conclusion, through the strategic material exploration based mainly on the square coordinated Cu sites with the weak local inversion breaking, we have successfully achieved the large spontaneous nonreciprocal directional dichroism exceeding 40% at 1.65 eV in the insulating antiferromagnetic material Bi2CuO4, which possesses the four equivalent Néel vector orientations. Moreover, we have demonstrated that the combination of the nonreciprocal directional dichroism and the tetragonal symmetry of the crystal structure in Bi2CuO4 leads to the unconventional antiferromagnetically induced trichroism. Furthermore, we have shown that this antiferromagnetic trichroism enables the visualization of the field-driven reversal and reorientation of the Néel vector. We stress that the concept of antiferromagnetic trichroism is general and extendable to a broad class of magnetoelectric antiferromagnets with high crystal symmetry (trigonal, tetragonal, hexagonal, and cubic). The present work will stimulate further efforts to explore large nonreciprocal optical functionalities in antiferromagnets and understand the complex physics underlying multistable antiferromagnetic domains, which may contribute to the design of electric-field-controllable and optically readable higher-density memories.

## Methods

### Sample preparation and characterization

Single crystals of Bi2CuO4 were grown using a laser-based floating-zone furnace composed of a five laser-head design (Quantum Design LFZ1A)39. A typical growth rate was 2.0 mm h−1 and a counter-rotation speed was 10 rpm both for feed and seed rods. Crystal growth was performed under flowing pure oxygen. At the initial several hours of the crystal growth, a laser current was tuned manually in the range between 26.9 and 27.4 A in order to stabilize a molten zone. Subsequently, an automatic constant-temperature mode was utilized, which allows for a highly stable crystal growth for more than 24 hours without any manual tuning. The obtained single-crystalline rods were very easily cleaved parallel to the Z plane. The cleavage plane is very shiny (see the inset of Supplementary Fig. 3), indicating high crystallinity. No impurity phase was detected in powder X-ray diffraction patterns of crushed crystals. The orientation in the Z plane was determined by the Laue X-ray method. Magnetization (M) as functions of temperature (T) and magnetic field (H) was measured on a plate-like sample whose widest face is parallel to the Z axis by using a commercial SQUID magnetometer (MPMS, Quantum Design). The T dependence of M confirms that the antiferromagnetic transition takes place at TN = 44 K (Supplementary Fig. 3), in agreement with previous studies30,31. The crystal structure displayed in Fig. 1a was drawn by using VESTA software40.

### Optical absorption measurements

Optical absorption spectra in the photon energy range of 1.2 < Eph < 3.1 eV were measured using a homebuilt fiber-based optical system whose design is similar to that reported previously41. Our system can be inserted into a commercial physical property measurement system (PPMS, Quantum Design), which allows for a control of sample temperature and an application of a magnetic field. Light from a tungsten–halogen lamp (AvaLight-HAL-S-MINI, Avantes) was guided using an optical fiber to a sample, and then the light transmitted through the sample was guided using a different optical fiber to a spectrometer (Flame-S, Ocean Insight) with an optical resolution of 1.5 nm. A plate-like sample with the widest face parallel to the (110) plane (X plane) was used for the optical absorption measurements. A pair of the sample surfaces was polished with lapping films. A thickness (d) of the sample was about 100 μm. With this thickness, the absorption spectra at Eph > 2.0 eV cannot be measured due to large absorption. Reducing the sample thickness was unsuccessful due to the above-mentioned cleavage nature. To apply an electric field, a pair of parallel electrodes with a 1 mm gap was made on one side of the sample surfaces using conductive silver paste. The electric field was generated by a voltage source (Keithley 6517). Light polarization was controlled by a wire-grid polarization film (Asahi Kasei WGFTM), which was placed on the optical path in front of the sample. When changing the direction of light polarization and/or switching the light-propagation direction, we took out the optical system from the PPMS cryostat, reoriented the polarization film, and then reinstalled the system.

### Optical domain imaging

Domain-imaging experiments were performed using a homebuilt horizontal polarized microscope in the transmittance geometry27. As an illumination source, we used a monochromatic LED (M730L5, Thorlabs) combined with a band-pass filter of 750 nm (FWHM = 10 nm). Microscopic images were taken by a scientific CMOS camera (Quantalux sCMOS camera, Thorlabs) with an exposure time of 100 milliseconds or less. The spatial resolution of the microscope is better than 4 μm (ref. 27). A plate-like sample (d ≈ 100 μm) whose widest face is parallel to the X plane was used. The sample was glued using a silver paste on an oxygen-free copper plate with a hole for light transmission, which was then mounted on the cold head of a helium-flow cryostat (MicrostatHe, Oxford Instruments). A magnetic field was generated by an electromagnet (3480, GMW Associates). To apply an electric field to the X-plane sample, a voltage source (Keithley 6517) was connected to a pair of parallel electrodes formed on a front surface of the sample. The gap distance of the pair electrodes was about 1 mm.

## Data availability

The source data for one-dimensional plots shown in Figs. 25 and Supplementary Figs. 36,8,9 are provided as a Source Data file. The source numerical data for optical microscopy images are available from the corresponding author upon reasonable request. Source data are provided with this paper.

## References

1. Baltz, V. et al. Antiferromagnetic spintronics. Rev. Mod. Phys. 90, 015005 (2018).

2. Němec, P., Fiebig, M., Kampfrath, T. & Kimel, A. V. Antiferromagnetic opto-spintronics. Nat. Phys. 14, 229–241 (2018).

3. Wadley, P. et al. Electrical switching of an antiferromagnet. Science 351, 587–590 (2016).

4. Godinho, J. et al. Electrically induced and detected Néel vector reversal in a collinear antiferromagnet. Nat. Commun. 9, 4686 (2018).

5. Gomonay, O., Jungwirth, T. & Sinova, J. High antiferromagnetic domain wall velocity induced by Néel spin-orbit torques. Phys. Rev. Lett. 117, 017202 (2016).

6. Shiino, T. et al. Antiferromagnetic domain wall motion driven by spin-orbit torques. Phys. Rev. Lett. 117, 087203 (2016).

7. Watanabe, H. & Yanase, Y. Symmetry analysis of current-induced switching of antiferromagnets. Phys. Rev. B 98, 220412 (2018).

8. Thöle, F., Keliri, A. & Spaldin, N. A. Concepts from the linear magnetoelectric effect that might be useful for antiferromagnetic spintronics. J. Appl. Phys. 127, 213905 (2020).

9. Kriegner, D. et al. Multiple-stable anisotropic magnetoresistance memory in antiferromagnetic MnTe. Nat. Commun. 7, 11623 (2016).

10. Little, A. et al. Three-state nematicity in the triangular lattice antiferromagnet Fe1/3NbS2. Nat. Mater. 19, 1062–1067 (2020).

11. Ni, Z. et al. Imaging the Néel vector switching in the monolayer antiferromagnet MnPSe3 with strain-controlled Ising order. Nat. Nanotechnol. 16, 782–787 (2021).

12. Higo, T. et al. Omnidirectional control of large electrical output in a topological antiferromagnet. Adv. Funct. Mater. 31, 2008971 (2021).

13. Fiebig, M. Revival of the magnetoelectric effect. J. Phys. D. Appl. Phys. 38, R123–R152 (2005).

14. Spaldin, N. A. & Ramesh, R. Advances in magnetoelectric multiferroics. Nat. Mater. 18, 203–212 (2019).

15. Hopfield, J. J. & Thomas, D. G. Photon momentum effects in the magneto-optics of excitons. Phys. Rev. Lett. 4, 357–359 (1960).

16. Krichevtsov, B. B., Pavlov, V. V., Pisarev, R. V. & Gridnev, V. N. Spontaneous non-reciprocal reflection of light from antiferromagnetic Cr2O3. J. Phys. Condens. Matter 5, 8233–8244 (1993).

17. Rikken, G. L. J. A., Strohm, C. & Wyder, P. Observation of magnetoelectric directional anisotropy. Phys. Rev. Lett. 89, 133005 (2002).

18. Jung, J. H. et al. Optical magnetoelectric effect in the polar GaFeO3 ferrimagnet. Phys. Rev. Lett. 93, 037403 (2004).

19. Saito, M., Taniguchi, K. & Arima, T. Gigantic optical magnetoelectric effect in CuB2O4. J. Phys. Soc. Jpn. 77, 013705 (2008).

20. Arima, T. Magneto-electric optics in non-centrosymmetric ferromagnets. J. Phys. Condens. Matter 20, 434211 (2008).

21. Kézsmárki, I. et al. Enhanced directional dichroism of terahertz light in resonance with magnetic excitations of the multiferroic Ba2CoGe2O7 oxide compound. Phys. Rev. Lett. 106, 057403 (2011).

22. Szaller, D., Bordács, S. & Kézsmárki, I. Symmetry conditions for nonreciprocal light propagation in magnetic crystals. Phys. Rev. B 87, 014421 (2013).

23. Toyoda, S. et al. One-way transparency of light in multiferroic CuB2O4. Phys. Rev. Lett. 115, 267207 (2015).

24. Kocsis, V. et al. Identification of antiferromagnetic domains via the optical magnetoelectric effect. Phys. Rev. Lett. 121, 057601 (2018).

25. Yokosuk, M. O. et al. Nonreciprocal directional dichroism of a chiral magnet in the visible range. npj Quantum Mater. 5, 20 (2020).

26. Sato, T., Abe, N., Kimura, S., Tokunaga, Y. & Arima, T. Magnetochiral dichroism in a collinear antiferromagnet with no magnetization. Phys. Rev. Lett. 124, 217402 (2020).

27. Kimura, K., Katsuyoshi, T., Sawada, Y., Kimura, S. & Kimura, T. Imaging switchable magnetoelectric quadrupole domains via nonreciprocal linear dichroism. Commun. Mater. 1, 39 (2020).

28. Di Sante, D. et al. Realizing double Dirac particles in the presence of electronic interactions. Phys. Rev. B 96, 121106(R) (2017).

29. Yuan, B. et al. Neutron scattering study of magnetic anisotropy in the tetragonal antiferromagnet Bi2CuO4. Phys. Rev. B 103, 134436 (2021).

30. Yamada, K. et al. Three-dimensional antiferromagnetic order and anisotropic magnetic properties in Bi2CuO4. J. Phys. Soc. Jpn. 60, 2406–2414 (1991).

31. Zhao, L. et al. Magnetically induced ferroelectricity in Bi2CuO4. Phys. Rev. B 96, 054424 (2017).

32. Schmid, H. Some symmetry aspects of ferroics and single phase multiferroics. J. Phys. Condens. Matter 20, 434201 (2008).

33. Schmid, H. On ferrotoroidics and electrotoroidic, magnetotoroidic and piezotoroidic effects. Ferroelectrics 252, 41–50 (2001).

34. Hlinka, J. Eight types of symmetrically distinct vectorlike physical quantities. Phys. Rev. Lett. 113, 165502 (2014).

35. Okitsu, K. et al. X-ray triple refraction and triple absorption in a cobalt-complex crystal. J. Synchrotron Radiat. 5, 1055–1057 (1998).

36. Majchrowski, A., Borowiec, M. T. & Michalski, E. Top seeded solution growth of KHo(WO4)2 single crystals. J. Cryst. Growth 264, 201–207 (2004).

37. Chmiel, F. P. et al. Observation of magnetic vortex pairs at room temperature in a planar α-Fe2O3/Co heterostructure. Nat. Mater. 17, 581–585 (2018).

38. Pisarev, R. V., Pavlov, V. V., Kalashnikova, A. M. & Moskvin, A. S. Near-band gap electronic structure of the tetragonal rare-earth cuprates R2CuO4 and the bismuth cuprate Bi2CuO4. Phys. Rev. B 82, 224502 (2010).

39. Kaneko, Y. & Tokura, Y. Floating zone furnace equipped with a high power laser of 1 kW composed of five smart beams. J. Cryst. Growth 533, 125435 (2020).

40. Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).

41. Sawada, Y., Kimura, S., Watanabe, K. & Nakano, M. High-field optical spectroscopy of the spin-crossover complex [MnIII(taa)]. J. Low. Temp. Phys. 170, 424–429 (2013).

## Acknowledgements

We thank M. Sato for his contribution in the early stage of this research. We also thank S. Kimura for his help in constructing the fiber-based optical system. K.K. acknowledges support from JSPS KAKENHI Grant Number JP19H01847, from the MEXT Leading Initiative for Excellent Young Researchers (LEADER), and from The Murata Science Foundation. T.K. acknowledges support from JSPS KAKENHI Grant Numbers JP19H05823, JP21H04436, and JP21H04988.

## Author information

Authors

### Contributions

K.K. and T.K. conceived the project. K.K. coordinated experiments. With the help of K.K. and T.K., Y.O. grew single crystals. K.K. measured magnetization and optical absorption spectra and performed domain imaging. The paper was drafted by K.K. and revised by K.K. and T.K.

### Corresponding author

Correspondence to Kenta Kimura.

## Ethics declarations

### Competing interests

The authors declare no competing interests.

## Peer review

### Peer review information

Nature Communications thanks Liang Wu and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Rights and permissions

Reprints and Permissions

Kimura, K., Otake, Y. & Kimura, T. Visualizing rotation and reversal of the Néel vector through antiferromagnetic trichroism. Nat Commun 13, 697 (2022). https://doi.org/10.1038/s41467-022-28215-w

• Accepted:

• Published:

• DOI: https://doi.org/10.1038/s41467-022-28215-w