Abstract
Rechargeable calcium batteries have attracted increasing attention as promising multivalent ion battery systems due to the high abundance of calcium. However, the development has been hampered by the lack of suitable cathodes to accommodate the large and divalent Ca2+ ions at a high redox potential with sufficiently fast ionic conduction. Herein, we report a new intercalation host which presents 500 cycles with a capacity retention of 90% and a remarkable power capability at ~3.2 V (vs. Ca/Ca2+) in a calcium battery. The cathode material derived from Na0.5VPO4.8F0.7 is demonstrated to reversibly accommodate a large amount of Ca2+ ions, forming a series of CaxNa0.5VPO4.8F0.7 (0 < x < 0.5) phases without any noticeable structural degradation. The robust framework enables one of the smallest volume changes (1.4%) and the lowest diffusion barriers for Ca2+ among the cathodes reported to date, offering the basis for the outstanding cycle life and power capability.
Similar content being viewed by others
Introduction
The growing demands for electric vehicles and stationary energy storage systems have motivated exhaustive efforts to explore new types of batteries with a higher energy density, longer life, and lower cost than that offered by the current lithium ion batteries (LIBs)1,2,3. Multivalent ion batteries have been considered as one of the alternative solutions, because multivalent ion insertion/extraction is associated with doubled or tripled electron transfer per ion in the intercalation reaction, potentially leading to higher specific energy densities than that the monovalent ions can carry4. Recently, rechargeable batteries based on magnesium ion5, aluminum ion6, zinc ion7, and calcium ion have thus received much attention and obtained discernible progress in battery performance. Among the multivalent battery systems, calcium ion batteries (CIBs) are capable of offering the highest voltage due to the low reduction potential of Ca/Ca2+ with −2.9 V (vs. standard hydrogen potential, SHE), which is lower than −2.4 V (vs. SHE) for magnesium, −1.7 V (vs. SHE) for aluminum, and −0.76 V (vs. SHE) for zinc8,9, enabling a high energy density with the voltage comparable to that of LIBs. In addition, calcium ion presents the smallest polarization strength of 10.4 (vs. 14.7 for magnesium ion, 16 for zinc ion, and 24 for aluminum ion)10, suggesting comparatively fast mobility of divalent calcium ions in hypothetical insertion host materials. Together with the abundance of calcium in earth crust and its environmental compatibility, these properties appeal CIBs as the next generation post-LIBs.
Recent efforts on the development of negative electrodes could bring the rechargeable calcium chemistries a step closer to a practically feasible battery system11. While a reversible stripping/plating of calcium metal electrode had been regarded extremely challenging due to the formation of ion-blocking layer on the surface of calcium metal, several research groups successfully verified that it can be resolved by employing new electrolyte systems such as Ca(BF4)2 in ethylene carbonate/propylene carbonate (EC/PC)12, Ca(BH4)2 in tetrahydrofuran (THF)13, and Ca[B(hfip)4]2 in dimethoxy ethane (DME), demonstrating elemental calcium metal as an important CIB anode14. Moreover, it was recently reported that a large amount of Ca2+ can be reversibly intercalated to a graphite anode through a co-intercalation reaction over 200 cycles, presenting its promise as a stable anode for CIBs15. In coping with the remarkable advancement of anodes for CIBs, efforts have been also placed on the discovery of cathode over the past years11. Various materials groups have been proposed such as layered materials (i.e., TiS216, V2O517, α-MoO318), Prussian blue analogues (i.e., MnFe(CN)619) and transition metal oxides (i.e., CaxMn2O420), which could exhibit the capability to store calcium ions and the promise for the use as cathode. Nevertheless, the cyclic performance of these proposed cathodes seldom exceeded 100 cycles, and few cathodes could deliver a reasonably high capacity at practically important current rates, incompatible with the advanced CIB anodes16,17,18,19,20. It is likely due to the relatively large ionic radius and divalent nature of Ca2+ compared to monovalent ions (i.e., Li+ and Na+), which make the intercalation kinetics generally sluggish in diffusion channels of intercalation hosts. Moreover, a large calcium ion intercalation in the host is supposed to cause an extended volume change of the host, which triggers a premature degradation of the cathode structure11. The discovery of a reliable calcium cathode material or strategy that can mitigate these issues would expedite the development of the CIBs, and thus has long been awaited.
In our study exploring a new CIB cathode here, we attempted to search for a material chemistry with a rigid open framework that is less sensitive to the volume change arising from the large guest ion insertion/extraction. In this regard, a success-proven polyanion-based cathode for sodium ion battery, Na1.5VPO4.8F0.7 (NVPF)21,22,23, attracted our immediate attention. According to our previous studies, NVPF has shown interesting properties as a host material for sodium ions, exhibiting one of the lowest volume changes with (de-)sodiation (~2.9%) and fast sodium ion diffusion with low activation barriers (30–330 meV) owing to its unique open framework, thus delivering excellent cycle and power performances22. Moreover, the high redox potential (3.9 V vs. Na/Na+) and the latent multi-redox capability of vanadium ion (V3+/V4+/V5+) could contribute to a high energy density in the sodium system, which are also supposed to be beneficial when applied to CIB cathode. Herein, exploiting the structurally robust and open-framework NVPF host, we show that the desodiated NVPF can function as a stable and fast-kinetic calcium ion intercalation host and thus be a strong contender to the currently available cathodes for rechargeable CIBs. It is demonstrated that the NVPF-based host allows reversible Ca2+ ion intercalation and deintercalation at ~3.2 V (vs. Ca/Ca2+) in calcium cells with the capacity fading rate of 0.02% per cycle over 500 cycles, which records one of the lowest values reported to date for CIB electrodes. Equally important is that its power capability outperforms most of the existing cathodes for CIBs. The origin of the outstanding performance is elucidated through comprehensive experimental and theoretical investigations.
Results
Electrochemical properties of NVPF cathode in CIBs
In order to verify the intercalation capability of Ca2+ ion into NVPF framework, we constructed an electrochemical cell as illustrated in Fig. 1a, which consists of desodiated NVPF as the working electrode, activated carbon as a counter electrode, and an electrolyte of 1 M Ca(PF6)2 in EC/PC19. Prior to electrochemical tests in the calcium cell, the desodiated NVPF electrode was prepared by charging the NVPF electrode in a separate sodium electrochemical cell to 4.5 V vs. Na/Na+, resulting in []1.0Na0.5VPO4.8F0.7 ([]: vacancy) compound (see Supplementary Fig. 1 for details), according to our previous work22. The activated carbon was used as the counter electrode to prevent the complexity arising from unwanted side reactions caused by the use of calcium metal, and is known to be electrochemically active in calcium electrolytes via simple (de)adsorption reaction19. The galvanostatic discharging/charging of the calcium cell was first performed at 25 mA g−1 between −1.0 and 1.5 V vs. activated carbon electrode, which corresponds to the voltage range of 1.75 and 4.25 V vs. Ca/Ca2+, as presented in Fig. 1b. (The voltage calibration with respect to the value vs. Ca/Ca2+ is described in the experimental section and Supplementary Figs. 2, 324.) Interestingly, the desodiated NVPF electrode could deliver an appreciable discharge capacity in the calcium electrochemical cell, implying a significant amount of calcium stored in the desodiated NVPF structure. The initial discharge capacity was ~78 mAh g−1, which immediately increased to 88 mAh g−1 in the following discharge cycles. A negligible change in the capacity or the electrochemical profile was observed during the subsequent ten cycles (Fig. 1b), indicating excellent reversibility for Ca2+ insertion and extraction in desodiated NVPF cathodes. As depicted in Supplementary Fig. 3, the electrochemical profile remained almost unchanged even after 50 cycles, delivering a reversible capacity of 87 mAh g−1 at 25 mA g−1. The calcium intercalation into the NVPF host could be directly confirmed from the chemical analysis of the fully discharged electrode. As tabulated in Supplementary Table 1, the electrode composition was determined to be Ca0.38Na0.56VPO4.8F0.7 after the full discharge in the cell from the inductively coupled plasma mass spectrometry (ICP-MS) measurements. It is markedly consistent with the estimated composition of the fully calciated NVPF, i.e., Ca0.35Na0.5VPO4.8F0.7, based on the capacity delivered in Fig. 1b assuming the Ca2+ ion intercalation. After recharging of the electrode, the composition was measured to be Ca0.05Na0.51VPO4.8F0.7, confirming that the capacity in the calcium cell was originated from the reversible calcium intercalation/deintercalation.
The rate capability of the new calcium cathode was further investigated by probing the discharging responses at increasing current densities, as shown in Fig. 1c. When the current density increased to 100 mA g−1 corresponding to ~1 C rate, the discharge capacity only slightly reduced from 87 to 62 mAh g−1. Even with the 50-folds increase in the current density to 500 mA g−1, nearly 50% of the specific capacity could be still retained, indicating a respectable rate capability. While this power performance does not reach that of the conventional LIBs based on the monovalent lithium ion conduction, it outperforms most other intercalation compounds reported in previous CIBs, e.g., 38 mAh g−1 at 400 mA g−1 for VOPO4·2H2O cathode25, and 45 mAh g−1 at 117 mA g−1 for NaV2(PO4)3 cathode26. Moreover, it is noteworthy that the primary particles of our material are a few micrometers in size (Supplementary Fig. 1a), which indicates a further promise in the high power capability by nanostructure engineering. Detailed analysis on the kinetics of the calcium intercalation in NVPF structure will be discussed later in the following section. Figure 1d presents the stability of the NVPF cathode in a calcium electrochemical cell during the extended cycles at a current density of 50 mA g−1. It illustrates that the initial discharge capacity of 75 mAh g−1 is well retained, and the capacity retention is over 90% after 500 cycles, rendering a remarkably low capacity fading rate of 0.02% per cycle. To estimate the standing of current desodiated NVPF cathode among its peers, we summarize the electrochemical performance of the state of the art cathodes in CIBs as listed in Supplementary Table 210,18,19,25,27,28,29. It clearly illustrates that our NVPF cathode delivers the highest cyclic stability and power capability at a high redox voltage (3.2 V in this work in comparison with 2.4 V for Mg0.25V2O5·H2O10, 1.3 V for α-MoO318, and 2.8 V for VOPO4·H2O25) for CIBs.
Calcium storage mechanism of NVPF cathode
In order to elucidate the remarkable performance of the NVPF electrode in calcium electrochemical system, we carefully investigated its charge/discharge mechanism. First, the structural evolution of the electrode was probed in real time by synchrotron in situ XRD measurements. The XRD patterns were periodically collected every 4 min when the cell was galvanostatically cycled at 15 mA g−1. Figure 2a depicts an augmented view of the main XRD peaks of the NVPF electrode during the discharge and charge reactions. (See Supplementary Fig. 4 for the full diffractograms.) It clearly indicates that the electrochemical calciation/decalciation is accompanied by the gradual structural transformation of the NVPF, which is highly reversible, a testament to the excellent reversibility of the CIB cell. A closer examination of the XRD patterns reveals that a continuous shift of peaks occurs during the first half of the calciation, suggesting the solid-solution reaction with the calcium intercalation. On the other hand, during the second half of the calciation into NVPF, a hint of the two-phase coexistence was detected in the region of 28.1–28.4°. As marked with red dash lines in Fig. 2b, the peak at 28.4° gradually disappears, while that at 28.1° emerges from DOD (depth of discharge) 50% to DOD 100%. It implies that a local segregation of two Ca configurations has arisen in the structure (i.e., the occurrence of biphasic domains). This behavior is reminiscent of the Na insertion process in NVPF, where a stable intermediate phase at x = 1 in NaxVPO4.8F0.7 induced the biphasic reaction at a high Na content region22. Analogically, a stable intermediate phase for calciated NVPF or/and short-range ordering of Ca in basic units may be attributable to the two-phase region. More studies are necessary in the future to reveal the origin of the two-phase reaction and to elucidate the detailed structure of the intermediate calcium phase.
In Fig. 2c, lattice parameters a and c are plotted as a function of calciation and decalciation, as determined by the Rietveld refinement of the XRD profiles. It shows that the lattice parameter c, which corresponds to the interlayer distance of the NVPF crystal structure in Fig. 1a, decreases with the calciation, whereas the lattice parameter a corresponding to the basal dimension increases. The reduction of the lattice parameter c is attributed to the decreased electrostatic repulsion between O2− layers, as the Ca2+ layers that screen the electrostatic repulsion between O2− become continuously filled. On the other hand, the increase in the lattice parameter a is attributable to the expansion of vanadium octahedra with the electrochemical reduction of vanadium ions. Upon decalciation, the reverse behavior was observed for the lattice parameters of a and c, manifesting the reversibility of the NVPF structure during calciation and decalciation. Noteworthy is that the variation of c and a lattice parameter is 0.8% by contraction and 1.1% by expansion, respectively, with the full calciation, which leads to an ultra-small volume variation of 1.4%. This value is unusually small considering the large calcium ion intercalation to the crystal, and is even smaller than those of most intercalation compounds for post LIB chemistry. In Fig. 2d, we comparatively displayed the volume expansion of various cathodes for CIB (and for several post LIB systems such as Al, Mg, Zn, and Na ion batteries) upon charging6,17,28,30,31,32,33. For fair comparisons, the volume change was plotted with the amount of charge transfer accompanied with the intercalation. It clearly illustrates that the calcium intercalation in NVPF cathode involves the lowest volume change among peers even with a substantial amount of the charge storage. To our surprise, the volume change of NVPF cathode with calcium (1.4%) is only half of that observed for the sodium intercalation in NVPF, which is known to be 2.9%22. We suspect that, given the similar ionic size of Ca2+ and Na+ (2.0 Å for Ca2+ and 2.04 Å for Na+)10, the divalent Ca2+ only needs to occupy half of the interstitial vacancies in the intercalation host compared with the monovalent Na+ to retain the high specific capacity, thus involves a smaller volume change in the host. It proposes an unexpected merit of the multivalent ion intercalation in batteries, which requires a smaller quantity of guest ion intercalants for a given capacity than the monovalent ion counterpart, leading to a smaller variation in the host structure during the electrochemical reaction. The positive correlation between the small volume variation and the stable cyclic property of electrodes has also been proven in the well-known zero-strain Li4Ti5O12 anodes in LIBs34. We believe that the NVPF framework involving a small volume change with the calcium intercalation has also contributed to the outstanding cyclic stability demonstrated in Fig. 1d.
The detailed structural analysis of the NVPF cathode during calcium insertion/extraction was further carried out using high-resolution powder XRD (HRPD), X-ray absorption near-edge structure (XANES), and 13Na nuclear magnetic resonance (NMR) measurements. The Rietveld refinements of the pristine, desodiated, calciated, and decalciated NVPFs were carried out using HRPD, and their results are provided and tabulated in Supplementary Fig. 5 and Supplementary Tables 3–6, respectively. The Na and Ca stoichiometry derived from the refinement matches the electrochemical and ICP-MS results. Moreover, the a- and c-axis lattice parameters changes as derived from HRPD upon calciation/decalciation are consistent with the in situ XRD results. In Fig. 3a, we comparatively plotted the change in the occupancies of Na1 and Na2 sites in the NVPF, which are known to be the primary sites for the sodium ions in the previous works21,22,23. (Na1 and 2 sites are also schematically shown in Fig. 3e.) The figure indicates that Na1 sites are mainly deintercalated in the desodiation process, which serve as vacant interstitial sites for the following calcium insertion reaction. It was also consistently found that Ca2+ ions mainly occupy vacancies on Na1 sites, presenting a similar crystallographic structure with the pristine NVPF. On the other hand, the Na2 sites were observed to be negligibly occupied by Ca2+ ions, thus do not noticeably contribute to the overall capacity. This preferred contribution of Na1 sites in the capacity is similar to the sodium intercalation/deintercalation behavior of NVPF in the sodium electrochemical system35.
The V K-edge XANES characterization in Fig. 3b discloses that discharging/charging processes were accompanied by the reduction and oxidation of the vanadium ion. Pristine NVPF shows a dominant pre-edge peak at 5469.3 eV, indicating the coexistence of V4+ and V3+, which was also previously confirmed by electron paramagnetic resonance experiment23. After the pre-desodiation, the pre-edge peaks shifted to higher energies at 5469.7 and 5471 eV, signifying the oxidation of the vanadium ion22. When Ca2+ ions were inserted in the desodiated NVPF, the reduction of vanadium ion was identified with a negative shift of the pre-edge peak to that for the pristine NVPF. During the reverse decalciation reaction, the vanadium ion returned to the original oxidation state, implying that the vanadium redox reaction is fully reversible in CIBs. Further probe on the NVPF cathode during discharging/charging was conducted using 23Na NMR, as shown in Fig. 3c. The 23Na NMR spectrum of the pristine NVPF exhibits two major resonances at 84.5 and 127.6 ppm, which are assigned to the Na sites neighboring V4+ and V3+ (Fig. 3d), respectively, as the V4+:V3+ in the structure is 4:1 ratio23. The fully desodiated NVPF presents a low resonance at 23.6 ppm, a sign of high oxidation state of vanadium ion (i.e., V5+) with the reduced number of unpaired electrons35. When Ca2+ ions were inserted in the desodiated NVPF, a major peak was detected at a higher resonance of 96.2 ppm, signifying the reduction of vanadium ion. Considering that Na1 was dominantly extracted for desodiated NVPF from the XRD refinement, we suspect that the broad resonance at 96.2 ppm originates mainly from sodium ions in Na2 sites and some residual Na1 affected by the adjacent Ca2+ ions. The 23Na resonance peak is more broadened than that of pristine NVPF, which is attributable to the weaken interaction between residual Na ions and the paramagnetic vanadium ions in the presence of Ca ions21. After the calcium extraction, the 23Na resonance is still observable and shifts back to 37.8 ppm, close to that for desodiated NVPF. It manifests that a reversible calcium extraction takes place with the remaining structural sodium ions in the NVPF framework, as illustrated in Fig. 3e. The difference between the 23Na peak position of decalciated NVPF and desodiated NVPF (23.6 ppm vs. 37.8 ppm) is possibly arising from partial Na ion migration from Na2 sites to Na1 sites (see the Na occupancies in Supplementary Tables 4 and 6).
The calciation of Na-vacancy layers in desodiated NVPF could be directly confirmed by scanning transmission electron microscopy (STEM) and electron energy loss spectroscopy (EELS) measurements for the calciated NVPF electrode. Figure 3f presents the high-angle annular-dark-field (HAADF, left) and annular-bright-field (ABF, right) STEM images viewed along [110] direction. The Z-contrast of HAADF image illustrates that zigzag stackings of VO5F (or VO4F2) octahedral/PO4 tetrahedra units (bright dots) form the layered structure, where calcium or sodium ions are nearly invisible (dark) between the layers, as schematically illustrated in Supplementary Fig. 6. On the other hand, ABF image on the right panel along with the EELS analysis clearly indicates the presence of calcium ions in the layer. Figure 3g displays the local composition of calciated NVPF determined from the EELS fine structure of V L-edge, Ca L-edge, and O K-edge spectra. Periodical appearance of calcium ions was evidently observed where the intensity for vanadium was low, suggesting calcium ions are located between VO5F (or VO4F2)/PO4 layers. The series of characterization along with the direct observation of calcium approve that the electrochemical reaction in CIB occurs via the reversible Ca2+ intercalation at sodium vacant sites in the desodiated NVPF with vanadium redox reactions (Fig. 3e and Supplementary Fig. 6).
Kinetic behavior of NVPF cathode in CIBs
Having verified the insertion of calcium ions in the structure, we attempted to unveil the kinetic properties of Ca2+ ion migration in the NVPF structure. The diffusion coefficients were measured as a function of the calcium concentration in CaxNa0.5VPO4.8F0.7 using the galvanostatic intermittent titration technique (GITT) in Supplementary Fig. 7. Figure 4a plots the chemical diffusion coefficients of calcium ions measured both at insertion and extraction processes from the GITT. It reveals that the diffusion coefficients range from 8.9 × 10−12 to 4.1 × 10−11 cm2 s−1, which is superior or comparable to the typical values of multivalent ions in the intercalation hosts such as 10−17 cm2 s−1 for Mg2+ diffusion in cation-deficient TiO236, theoretically predicted diffusion coefficient of 5 × 10–11 cm2 s−1 for Mg2+-containing spinel oxides37, 10−18–10−20 cm2 s−1 for Al3+ diffusion in cubic Cu0.31Ti2S438 and 10−17–10−15 cm2 s−1 for Zn2+ in ZnNaV2(PO4)339. It is also worthy of mentioning that the diffusivity is even comparable to those of lithium ion diffusion in conventional LIB cathode materials such as LiCoO2 (10−11–10−13 cm2 s−1)40 and LiFePO4 (10−10–10−16 cm2 s−1)41, highlighting a superior Ca2+ ion diffusion kinetics in the current work. A closer look at the trend in Fig. 4a indicates a concentration-dependent calcium ion diffusion coefficient, which presents higher values at the low calcium concentrations in CaxNa0.5VPO4.8F0.7 (0 ≤ x ≤ 0.175). This result is consistent with the in situ electrochemical impedance spectroscopy (EIS) analysis that the charge transfer resistance is close to the minimum at the vacancy-rich states of charging or discharging (Supplementary Fig. 8). Note that the feature of concentration-dependent diffusion kinetic was widely observed in lithium ion diffusion in other layered compounds such as LixCoO2 and LixTiS242. Compared with these intercalation compounds, the variation of the diffusivities is comparably small with the states of charge, which is speculated to be correlated with the structural aspect involving minimal volume change of the NVPF.
In order to gain more insight into the diffusion behavior in CaxNa0.5VPO4.8F0.7, we conducted density functional theory calculations. As previously reported for lithium and sodium analogues22,23, there are two representative diffusion pathways for the intercalating cation in NVPF structure; one is the intra-unit pathway, and the other is the inter-unit pathway, as illustrated with yellow circle arrows and green arrows in Fig. 4b, respectively. Our calculations revealed that the activation barrier for the Ca2+ ion diffusion is as low as ~243 meV through the intra-unit pathway (Fig. 4c), and ~606 meV through the inter-unit pathway (Fig. 4d). Since calcium ions should migrate through both paths for the overall de/intercalation reaction23, the inter-unit hopping would serve as the rate-determining step with the overall activation barrier of ~606 meV. Noteworthy is that the activation barrier of ~606 meV is significantly lower than 750 meV for CaxCo2O443, ~1.7 eV for α-V2O544, and 2 eV for perovskite CaxMoO345 in CIBs, elucidating the origin of the fast calcium intercalation kinetics in NVPF compared with other reported cathodes11. Additionally, the two-dimensional diffusion nature of the NVPF framework is also beneficial for the fast calcium mobility, while the common one-dimensional diffuser such as LiFePO4 would be sensitively affected by the presence of defects46.
Full CIBs
Finally, in order to verify the practical aspect of NVPF cathode in CIBs, a prototype Ca ion full cell, consisting of calcium metal anode and desodiated NVPF cathode, was constructed and cycled at 75 °C in carbonate electrolyte12. Supplementary Fig. 9 shows that the cell presents the characteristic discharge/charge profile in consistent with those observed in desodiated NVPF//activated carbon cells in Fig. 1b. The NVPF cathode could deliver a specific capacity of 85 mAh g−1 approximately at 3.1 V, yielding an energy density of about 263 Wh kg−1 with the calcium metal. While the capacity degrades rapidly due to the passivation of calcium metal in the carbonate-based electrolyte, it confirms that NVPF cathode is capable of functioning as a cathode. Furthermore, the feasibility of the NVPF cathode was explored in combination with other reported anodes by constructing the all-intercalation-based CIBs for the first time. In Supplementary Fig. 10, we assembled the CIBs using desodiated NVPF cathode, calciated graphite anode in a dual phase liquid electrolyte at room temperature. Since the use of graphite anode in CIB requires the specific choice of electrolyte system for the co-intercalation15, the dual phase electrolyte was designed in regard to immiscibility of two liquid phases47 and chemical compatibility between active material and electrolyte. An all-intercalation-based full cell showed the reversible capacity retention of 63% over 50 cycles, showing the promise of NVPF cathode in diverse cell configurations. Overall, the remarkable cyclic stability, high power capability, and high energy density for the new cathode propose its feasible applications in the future high energy CIBs.
Discussion
We have shown that a new intercalation-type cathode unlocks the electrochemical activity towards multivalent calcium ion batteries. The NVPF-based cathode delivered a reversible capacity of 87 mAh g−1, an unprecedentedly high capacity retention of 90% over 500 cycles and high rate capabilities, which could rival with state of the art cathodes reported for CIBs thus far. Structural analyses coupled with in situ XRD, solid state NMR, XANES, and STEM revealed the reversible insertion and removal of Ca2+ ions in the NVPF framework with an ultra-small volume change, which records one of the smallest values for multivalent ion intercalations. Electrochemical kinetic studies combined with first principles calculations demonstrated the superior diffusion coefficients and low activation barriers for Ca2+ ion diffusion, offering insight into the origins of the high-power calcium intercalation cathodes. This work successfully nudges the reversible Ca2+ intercalations in a polyanion-based cathode, which provides an unexplored pathway toward the realization of stable and high-power cathodes in CIBs.
Methods
Materials synthesis
The Na1.5VPO4.8F0.7 cathode material was synthesized by solid-state reactions22. Specifically, VOPO4 powder was first prepared by mixing a stoichiometric amount of V2O5 (Sigma Aldrich, 95%) and NH4H2PO4 (Sigma Aldrich, 99%) by ball milling and annealing at 750 °C for 4 h in Ar flow. Then, a stoichiometric amount of V2O5 and NH4H2PO4 was blended with 20 wt% super P by ball milling before sending to heat treatment at 850 °C for 2 h in air, to form VPO4. The as-obtained VOPO4, VPO4 powders were later mixed with NaF (Sigma Aldrich, 99%) and Na2CO3 (Sigma Aldrich, 99%) at a molar ratio of 8:2:7:4. The precursors were blended in a high-energy ball milling machine at 300 rpm for 24 h; and the mixture was heat-treated at 750 °C for 1.5 h in a tube furnace with Ar flow. The as-prepared Na1.5VPO4.8F0.7 was grinded into powder and mixed with polyvinylidene fluoride (PVDF) binder and super P conductive additive at a weight ratio of 8:1:1 in N-methyl-2-pyrrolidone (NMP) solvent. The slurry was casted on carbon fiber cloth, because the conventional Cu or Al current collectors were reported unstable in CIBs48. The Na1.5VPO4.8F0.7 electrodes were prepared with diameters of 3/8 inch and active mass loading of 2 mg cm−2. Na ions were extracted from Na1.5VPO4.8F0.7 electrodes by charging sodium ion half cells consisting of Na metal counter electrode and 1 M NaPF6 EC/PC electrolyte up to 4.5 V vs. Na/Na+. The desodiated NVPF electrodes were washed with flooded amount of dimethyl carbonate (DMC) solvent and dried in vacuum before using as working electrodes in CIBs.
The 1 M Ca(PF6)2 electrolyte was prepared by dissolving calcium salt in EC/PC (1/1, v/v) solvent in the glovebox and molecular sieves were also added to further remove H2O in electrolyte. The Ca(PF6)2 slat was synthesized according to the previous work19. A 25 mL acetonitrile suspension of 310 mg CaCl2 was slowly dropped to a 25 mL acetonitrile solution containing 1.26 g AgPF6. The mixture was magnetically stirred in dark for 24 h in the glovebox. After completion of reaction, the solution was centrifuged to obtain clear liquid, which was then dried in vacuum chamber, yielding a pure white powder of Ca(PF6)2.
Materials characterization
High resolution powder diffraction was performed at beamline 9B in the Pohang Accelerator Laboratory (PAL), Korea. The data were collected over 2θ between 10–103° with a step size of 0.01° and the wavelength of λ = 1.5226 Å. The XRD patterns were Rietveld refined using the FullProf program. Vanadium K-edge XANES spectra were obtained at beamline 7D in PAL using a double-crystal monochromator containing two sets of Si (111) crystals. The data were collected in transmission mode and normalized using the Athena program. 23Na MRS NMR spectra for the discharged/charged electrode materials were performed using a Bruker Avance 400 MHz 9.4 T wide-bore spectrometer (4 mm probe). All the shifts were referenced to 0.1 M NaCl aqueous solution. For STEM characterization, cross-sectional (Cs-STEM) TEM specimens of the cycled electrode were prepared using focused ion beam (FIB) milling (FEI, Helio 650). The specimens were utilized for HAADF and ABF imaging under 60 keV using Cs-STEM (JEOL, JEM-ARM200F) with a point-to-point resolution of 0.08 nm.
Electrochemical analysis
CR2032 coin cells were assembled in glovebox using the desodiated NVPF as working electrode, the BP2000 activated carbon as counter electrode and Whatman glass fiber separator socked with 1 M Ca(PF6)2 EC/PC electrolyte. Ca-containing electrolyte served as the Ca resources in the coin cell, thus exceed amount of electrolyte was added, i.e., 400 uL per cell. The activated carbon voltage vs. Ca/Ca2+ was estimated based on the previous literature24 regarding the activated carbon electrode with an Ag/Ag+ reference electrode and Fc/Fc+ as internal reference dissolved in Ca(PF6)2 EC/PC electrolyte (Supplementary Fig. 2). The cells were galvanostatically discharged/charged between −1.0 and 1.5 V vs. activated carbon electrode at various current densities, and the specific capacities were determined based on the mass of active materials. GITT was carried out after a single discharge/charge cycle by applying a constant current density of 10 mA g−1 for 30 min, followed by a relaxation potential measurement for 1 h, which protocol was repeated until the cell potential reached −1 or 1.5 V for discharging or charging, respectively. In situ EIS measurement was carried out on a Bio-Logic VSP-300 analyzer. Specifically, the coin cell was discharged/charged at a constant current density of 10 mA g−1 for 25 min between −1 and 1.5 V and resting for 10 s, when EIS curves were periodically recorded over the frequency range of 10 kHz and 100 mHz at an amplitude of 5 mV.
Synchrotron in situ XRD analysis
In-situ XRD experiment was performed on a 5 A beamline at PAL with a wavelength of λ = 0.6885 Å, and the XRD data were collected approximately every 4 min as a set of circles on a Mar 345-image plate detector in transmission mode. Note that the coin cell was pre-cycled to active electrodes before sending to in situ XRD experiment. The two-dimensional XRD images were converted to one-dimensional XRD curves and were recalculated to corresponding angles for λ = 1.543 Å, the wavelength of general X-ray tube sources with Cu Kα radiation. This process is to make it convenient for comparison of the in situ XRD results with these in literature.
First principle calculations
We used projector-augmented wave pseudopotentials49,50 as implemented in Vienna Ab initio Simulation Package51, and exchange-correlation energies were treated with generalized gradient approximation by Perdew–Burke–Ernzerhof52. In addition, a Hubbard U parameter53 of Ueff = 4.0 eV was introduced to Vanadium in order to deal with the self-interaction error. The calculation of Ca diffusion was conducted in a large supercell containing 16 formula units of CaxNa0.5VPO5F0.5 (x = 0–0.5) to prevent the interaction between migrating Ca ions in periodic unit cells. We note that CaxNa0.5VPO5F0.5 (x = 0–0.5) structure was adapted instead of CaxNa0.5VPO4.8F0.7 (x = 0–0.5) to avoid the modeling of complicated O/F orderings. When x = 0.5, CaxNa0.5VPO4.8F0.7 was fully calciated with full occupation of the capacity induced by Na extraction. For each diffusion path, seven intermediate images were placed to model the Ca diffusion pathway, and Nudged Elastic Band algorithm was used to obtain the activation barrier for Ca diffusion54. All calculations were performed with a cut-off energy of 500 eV and optimized until the remaining force in the unit cell converges within 0.05 eV Å−1.
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author on reasonable request.
References
Armand, M. & Tarascon, J. M. Building better batteries. Nature 451, 652–657 (2008).
Kang, K., Meng, Y. S., Breger, J., Grey, C. P. & Ceder, G. Electrodes with high power and high capacity for rechargeable lithium batteries. Science 311, 977–980 (2006).
Choi, J. W. & Aurbach, D. Promise and reality of post-lithium-ion batteries with high energy densities. Nat. Rev. Mater. 1, 1–16 (2016).
Li, M. et al. Design strategies for nonaqueous multivalent-ion and monovalent-ion battery anodes. Nat. Rev. Mater. 5, 276–294 (2020).
Aurbach, D. et al. Prototype systems for rechargeable magnesium batteries. Nature 407, 724–727 (2000).
Lin, M. C. et al. An ultrafast rechargeable aluminium-ion battery. Nature 520, 325–328 (2015).
Kundu, D., Adams, B. D., Duffort, V., Vajargah, S. H. & Nazar, L. F. A high-capacity and long-life aqueous rechargeable zinc battery using a metal oxide intercalation cathode. Nat. Energy 1, 16119 (2016).
Muldoon, J., Bucur, C. B. & Gregory, T. Quest for nonaqueous multivalent secondary batteries: magnesium and beyond. Chem. Rev. 114, 11683–11720 (2014).
Gummow, R. J., Vamvounis, G., Kannan, M. B. & He, Y. Calcium-ion batteries: current state-of-the-art and future perspectives. Adv. Mater. 30, 1801702 (2018).
Xu, X. et al. Bilayered Mg0.25V2O5·H2O as a stable cathode for rechargeable Ca-ion batteries. ACS Energy Lett. 4, 1328–1335 (2019).
Arroyo-de Dompablo, M. E., Ponrouch, A., Johansson, P. & Palacín, M. R. Achievements, challenges, and prospects of calcium batteries. Chem. Rev. 120, 6331–6357 (2020).
Ponrouch, A., Frontera, C., Bardé, F. & Palacín, M. R. Towards a calcium-based rechargeable battery. Nat. Mater. 15, 169–172 (2016).
Wang, D. et al. Plating and stripping calcium in an organic electrolyte. Nat. Mater. 17, 16–20 (2018).
Li, Z., Fuhr, O., Fichtner, M. & Zhao-Karger, Z. Towards stable and efficient electrolytes for room-temperature rechargeable calcium batteries. Energy Environ. Sci. 12, 3496–3501 (2019).
Park, J. et al. Stable and high‐power calcium‐ion batteries enabled by calcium intercalation into graphite. Adv. Mater. 32, 1904411 (2020).
Lee, C. et al. Electrochemical intercalation of Ca2+ ions into TiS2 in organic electrolytes at room temperature. Electrochem. Commun. 98, 115–118 (2019).
Hayashi, M., Arai, H., Ohtsuka, H. & Sakurai, Y. Electrochemical insertion/extraction of calcium ions using crystalline vanadium oxide. Electrochem. Solid-State Lett. 7, 119–121 (2004).
Cabello, M. et al. Applicability of molybdite as an electrode material in calcium batteries: a structural study of layer-type CaxMoO3. Chem. Mater. 30, 5853–5861 (2018).
Lipson, A. L. et al. Rechargeable Ca-ion batteries: a new energy storage system. Chem. Mater. 27, 8442–8447 (2015).
Dompablo, M. E. A. De et al. A joint computational and experimental evaluation of CaMn2O4 polymorphs as cathode materials for Ca ion batteries. Chem. Mater. 28, 6886–6893 (2016).
Park, Y. U. et al. A family of high-performance cathode materials for na-ion batteries, Na3(VO1−xPO4)2 F1+2x (0 ≤ x ≤ 1): combined first-principles and experimental study. Adv. Funct. Mater. 24, 4603–4614 (2014).
Park, Y. U. et al. A new high-energy cathode for a Na-ion battery with ultrahigh stability. J. Am. Chem. Soc. 135, 13870–13878 (2013).
Park, Y. U. et al. Tailoring a fluorophosphate as a novel 4V cathode for lithium-ion batteries. Sci. Rep. 2, 704 (2012).
Jeon, B. et al. Reversible calcium-ion insertion in NASICON-type NaV2(PO4)3. Chem. Mater. 32, 8772–8780 (2020).
Wang, J. et al. VOPO4·2H2O as a new cathode material for rechargeable Ca-ion batteries. Chem. Commun. 56, 3805–3808 (2020).
Kim, S. et al. High-voltage phosphate cathodes for rechargeable Ca-ion batteries. ACS Energy Lett. 5, 3203–3211 (2020).
Kuperman, N. et al. High performance Prussian Blue cathode for nonaqueous Ca-ion intercalation battery. J. Power Sources 342, 414–418 (2017).
Hyoung, J., Heo, J. W. & Hong, S. T. Investigation of electrochemical calcium-ion energy storage mechanism in potassium birnessite. J. Power Sources 390, 127–133 (2018).
Vo, T. N., Kim, H., Hur, J., Choi, W. & Kim, I. T. Surfactant-assisted ammonium vanadium oxide as a superior cathode for calcium-ion batteries. J. Mater. Chem. A 6, 22645–22654 (2018).
Yabuuchi, N. et al. P2-type Nax[Fe1/2Mn1/2]O2 made from earth-abundant elements for rechargeable Na batteries. Nat. Mater. 11, 512–517 (2012).
Guignard, M. et al. P2-NaxVO2 system as electrodes for batteries and electron-correlated materials. Nat. Mater. 12, 74–80 (2013).
He, P. et al. Layered VS2 nanosheet-based aqueous Zn ion battery cathode. Adv. Energy Mater. 7, 1601920 (2017).
Yoo, H. D. et al. Fast kinetics of magnesium monochloride cations in interlayer-expanded titanium disulfide for magnesium rechargeable batteries. Nat. Commun. 8, 339 (2017).
Ferg, E., Gummow, R. J., de Kock, A. & Thackeray, M. M. Spinel anodes for lithium‐ion batteries. J. Electrochem. Soc. 141, L147–L150 (1994).
Liu, Z. et al. Local structure and dynamics in the Na ion battery positive electrode material Na3V2(PO4)2F3. Chem. Mater. 26, 2513–2521 (2014).
Koketsu, T. et al. Reversible magnesium and aluminium ions insertion in cation-deficient anatase TiO2. Nat. Mater. 16, 1142–1148 (2017).
Bayliss, R. D. et al. Probing Mg migration in spinel oxides. Chem. Mater. 32, 663–670 (2020).
Geng, L. et al. Titanium sulfides as intercalation-type cathode materials for rechargeable aluminum batteries. ACS Appl. Mater. Interfaces 9, 21251–21257 (2017).
Hu, P. et al. Uncovering the potential of M1‐site‐activated NASICON cathodes for Zn‐ion batteries. Adv. Mater. 32, 1907526 (2020).
Xia, H., Lu, L. & Ceder, G. Li diffusion in LiCoO2 thin films prepared by pulsed laser deposition. J. Power Sources 159, 1422–1427 (2006).
Churikov, A. V. et al. Determination of lithium diffusion coefficient in LiFePO4 electrode by galvanostatic and potentiostatic intermittent titration techniques. Electrochim. Acta 55, 2939–2950 (2010).
Van Der Ven, A., Bhattacharya, J. & Belak, A. A. Understanding Li diffusion in Li-intercalation compounds. Acc. Chem. Res. 46, 1216–1225 (2013).
Park, H., Cui, Y., Kim, S., Vaughey, J. T. & Zapol, P. Ca cobaltites as potential cathode materials for rechargeable Ca-ion batteries: theory and experiment. J. Phys. Chem. C. 124, 5902–5909 (2020).
Carrasco, J. Role of van der Waals forces in thermodynamics and kinetics of layered transition metal oxide electrodes: alkali and alkaline-earth ion insertion into V2O5. J. Phys. Chem. C. 118, 19599–19607 (2014).
Arroyo-De Dompablo, M. E., Krich, C., Nava-Avendaño, J., Palacín, M. R. & Bardé, F. In quest of cathode materials for Ca ion batteries: the CaMO3 perovskites (M = Mo, Cr, Mn, Fe, Co, and Ni). Phys. Chem. Chem. Phys. 18, 19966–19972 (2016).
Malik, R., Burch, D., Bazant, M. & Ceder, G. Particle size dependence of the ionic diffusivity. Nano Lett. 10, 4123–4127 (2010).
Cho, S. J. et al. Monolithic heterojunction quasi-solid-state battery electrolytes based on thermodynamically immiscible dual phases. Energy Environ. Sci. 12, 559–565 (2019).
Lipson, A. L. et al. Current collector corrosion in Ca-ion batteries. J. Electrochem. Soc. 162, A1574–A1578 (2015).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B Condens. Matter Mater. Phys. 59, 1758–1775 (1999).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Dudarev, S. & Botton, G. Electron-energy-loss spectra and the structural stability of nickel oxide: An LSDA+U study. Phys. Rev. B Condens. Matter Mater. Phys. 57, 1505–1509 (1998).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. Climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
Acknowledgements
This work was supported by the National Research Foundation of Korea grant (Project No. 2018R1A2A1A05079249); the Supercomputing Center/Korea Institute of Science and Technology Information including technical support (KSC−2016-C3-0069) and code (IBS-R006-A2). This work was partially supported by a grant from the Research Committee of The Hong Kong Polytechnic University under project code 1-BE3M. This work was also supported by Shell International Exploration & Production, Inc.
Author information
Authors and Affiliations
Contributions
K.K. and Z.L.X conceived the original idea. Z.L.X conducted the experiment and analyzed the data. G.Y. carried out the simulation studies. J.W. and J.L. assisted on conducting synchrotron in situ XRD experiment, J.P., H.M., and S.Y.L. worked on fabricating graphite//NVPF CIB full cell, Y.J.K. and S.P.C. performed NMR and Cs-STEM experiments. K.K. revised the manuscript prepared by Z.L.X.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xu, ZL., Park, J., Wang, J. et al. A new high-voltage calcium intercalation host for ultra-stable and high-power calcium rechargeable batteries. Nat Commun 12, 3369 (2021). https://doi.org/10.1038/s41467-021-23703-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-23703-x
This article is cited by
-
Constructing highly safe and long-life calcium ion batteries based on hydratedvanadium oxide cathodes featuring a pillar structure
Rare Metals (2024)
-
Ca2+ Solvation and Electrochemical Solid/Electrolyte Interphase Formation Toward the Multivalent-Ion Batteries
Arabian Journal for Science and Engineering (2023)
-
Organic batteries for a greener rechargeable world
Nature Reviews Materials (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.