Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Synthetic control over the binding configuration of luminescent sp3-defects in single-walled carbon nanotubes

Abstract

The controlled functionalization of single-walled carbon nanotubes with luminescent sp3-defects has created the potential to employ them as quantum-light sources in the near-infrared. For that, it is crucial to control their spectral diversity. The emission wavelength is determined by the binding configuration of the defects rather than the molecular structure of the attached groups. However, current functionalization methods produce a variety of binding configurations and thus emission wavelengths. We introduce a simple reaction protocol for the creation of only one type of luminescent defect in polymer-sorted (6,5) nanotubes, which is more red-shifted and exhibits longer photoluminescence lifetimes than the commonly obtained binding configurations. We demonstrate single-photon emission at room temperature and expand this functionalization to other polymer-wrapped nanotubes with emission further in the near-infrared. As the selectivity of the reaction with various aniline derivatives depends on the presence of an organic base we propose nucleophilic addition as the reaction mechanism.

Introduction

Covalent functionalization of single-walled carbon nanotubes (SWNTs) has a long history and many different types of chemistry have been explored1,2,3. However, a major paradigm shift occurred with the discovery of luminescent sp3 defects4,5,6,7,8,9,10. Rather than quenching near-infrared photoluminescence (PL) of semiconducting SWNTs, these sp3 defects with covalently attached functional groups were found to create highly emissive states at lower energies. Mobile excitons, which result in E11 emission if not quenched11, are funneled to these defect states with long PL lifetimes and thus the usually low PL quantum yield (PLQY) of SWNTs increases significantly4,12,13. Luminescent defects (or organic color centers)7 have expanded the emission range of SWNTs further toward the near-infrared and opened up applications in sensing14,15, in vivo imaging within the second biological window16,17, and as quantum-light sources with room-temperature single-photon emission18,19,20,21,22. Various synthetic methods (e.g., radical-based reactions with aryl diazonium salts) allow for different functional groups to be attached to the SWNTs, which lead to additional small energetic shifts18,23,24,25,26. However, defect emission in general occurs over a wide spectral range (e.g., from 1100 to 1350 nm for (6,5) SWNTs). Indeed, the emission wavelength of sp3-functionalized SWNTs is less determined by the nature of the attached functional group than by the precise defect-binding configuration within the sp2-hybridized SWNT lattice20,24. For any functional group that forms a bond with the nanotube, thus creating one sp3 carbon, another carbon atom, either in ortho or para position to the first, must be saturated (e.g., with another substituent, -OH or -H group). For chiral nanotubes, this requirement leads to six possible binding configurations. Each of these is associated with a distinct defect energy and thus emission wavelength as corroborated by density functional theory calculations9,27,28. Most functionalization methods produce a mix of configurations and thus defect emission bands, the most common being the E11* and the even more red-shifted E11* emission with a longer PL lifetime29,30,31. They are considered to originate from the ortho-L90 (ortho++, circumferential direction) and ortho-L30 (ortho+, orientation along the nanotube axis) configurations of the two sp3 carbons, respectively20,24,27. Spectral variation is a problem for practical applications and must be reduced to ideally one single type of defect emission with narrow wavelength and PL lifetime distributions for the entire ensemble of functionalized nanotubes.

The more red-shifted E11* emission is closer to telecommunication wavelengths and is better suited for high-purity single-photon emission at room temperature. However, it is usually found for only a small portion of functionalized nanotubes. Saha et al.20 suggested the use of achiral zigzag-SWNTs whose symmetry leads to degenerate defect configurations and hence single peak emission. However, zigzag nanotubes are a very rare species in typical nanotube raw materials32 and thus difficult to obtain and purify in significant amounts. Another approach is the functionalization of SWNTs with either divalent functional groups (e.g., >CF2)29 or bidentate reactants with short bridging moieties (e.g., bisdiazonium compounds)31, which increase the probability of a specific binding configuration, albeit with limitations. Gaining real synthetic control over the defect-binding configuration and hence emission wavelength in a simple, reproducible, and possibly scalable manner is highly desirable.

Here we demonstrate a synthetic approach for the introduction of luminescent sp3 defects in carbon nanotubes, with which we can either create both types of binding configurations leading to E11* and E11* emission, or exclusively the configuration for E11* emission at longer wavelengths and with longer PL lifetimes. We employ polymer-sorted monochiral (6,5) SWNTs for this functionalization33, as they are easily purified and are available in relatively large amounts. The use of polymer-wrapped SWNTs in organic solvents avoids the limitations of reactions in aqueous dispersions10 and, hence, dramatically expands the available chemical toolbox. The selectivity and reactivity of the functionalization step is controlled by the concentration of potassium tert-butoxide (KOtBu) as a base and, thus, we propose nucleophilic addition as the underlying reaction mechanism as opposed to the commonly applied radical-based functionalization routes that mainly produce defects for E11* emission.

Results

Synthetic control over defect emission from (6,5) SWNTs

Polymer-wrapped (6,5) SWNTs (length 1–2 μm) serve as the model system for the controlled introduction of different luminescent sp3 defects in this study and were selectively dispersed and purified by shear-force mixing in toluene with a polyfluorene copolymer (poly[(9,9-dioctylfluorenyl-2,7-diyl)-alt-(6,6’)-(2,2’-bipyridine)] (PFO-BPy), see Fig. 1a and “Methods”). Excess polymer was removed by vacuum filtration and all reactions were performed with (6,5) nanotubes redispersed in fresh toluene (Supplementary Fig. 1). Functionalization occurred via base-mediated coupling with 2-haloanilines (2-iodoaniline if not specified otherwise) as shown in Fig. 1a, either under ultraviolet (UV)-light irradiation (~365 nm, blue reaction path) or in the dark (red reaction path). As we will see, the key component for controlling the reaction is the organic base KOtBu. Tetrahydrofuran (THF, 8.3 vol%) and dimethyl sulfoxide (DMSO, 8.3 vol%) were added as co-solvents to increase reactivity and selectivity. The functionalization was performed in an open flask at room temperature (10–180 min). Vacuum filtration of the mixture quenched the reaction by separating the reagents from the nanotubes. The collected SWNTs were washed with methanol and redispersed again in toluene for characterization. For a detailed step-by-step description, see Supplementary Methods 1 and Supplementary Table 1.

Fig. 1: Controlling sp3-defect emission from (6,5) SWNTs.
figure1

a Scheme for functionalization of PFO-BPy-wrapped (6,5) SWNTs in toluene/DMSO/THF with aniline derivatives and base KOtBu under UV-light irradiation (blue) and in the dark (red), respectively. Red-shifted defect emission bands are labeled as E11* (~1130 nm) and E11* (~1250 nm). b, c PL spectra of (6,5) SWNTs functionalized with 2-iodoaniline and varying concentrations of KOtBu under UV-light irradiation (b) and in the dark (c); reaction time 30 min. d Evolution of E11* emission normalized to E11 intensity for increasing reaction times with 2 eq. of KOtBu in the dark. The concentration of 2-iodoaniline was kept at 29.30 mmol L−1.

Nanotubes that were functionalized with 2-iodoaniline under UV illumination exhibited PL spectra (Fig. 1b) with the E11 emission of the mobile excitons and two red-shifted emission bands at 1130 nm and 1250 nm, which we assign to E11* and E11*, respectively. The relative intensities of the two defect emission bands could be controlled by the amount of KOtBu (0.5–3 eq.) in the reaction mixture, whereas the concentration of 2-iodoaniline was kept constant. With increasing base concentration, the reactivity increased (i.e., higher ratio of defect to E11 intensity) and the E11* emission became more and more dominant. Evidently, a higher base concentration favors the creation of the defect-binding configuration corresponding to E11*. Nevertheless, the defect configuration for E11*, which is the majority product for reactions with diazonium salts34 as well as photoactivated reactions of 4-iodoaniline in aqueous dispersion23, is still significant at lower base concentrations as long as UV illumination is applied.

Surprisingly, when the same reaction was performed in the dark (i.e., without UV-light activation), only the more red-shifted E11* emission feature (peak width 65 meV) was observed (Fig. 1c). The emission intensity and, thus, the number of defects increased steadily with base concentration and reaction time, and could easily be tuned using these parameters (Fig. 1c, d). Even after very long reaction times, no other defect emission bands appeared. Concentration-dependent functionalization reactions revealed that the highest reactivity and selectivity for defects with E11* emission is achieved when the aniline reagent is used in excess compared to the SWNTs (see Supplementary Note 1 and Supplementary Fig. 2). To the best of our knowledge, this reaction constitutes the first example of sp3 functionalization of chiral carbon nanotubes that exhibits such a high selectivity for this specific type of defect-binding configuration and exclusively leads to strongly red-shifted emission (E11*).

The established reaction scheme was not limited to 2-iodoaniline but was also performed successfully with 2-bromoaniline and 5-fluoro-2-iodoaniline (see Supplementary Fig. 3), although with different reactivities. A high selectivity and yield for E11* defects were achieved with 2-bromoaniline, whereas the additional steric repulsion in 5-fluoro-2-iodoaniline slightly lowered reactivity and selectivity. Overall, the base-mediated functionalization of nanotubes is selective, scalable, and uses inexpensive reagents that are easy and safe to handle. By employing this procedure, we were able to obtain high-quality dispersions of functionalized (6,5) SWNTs with only E11* defects, which previously were only accessible in conjunction with E11* defects. Before investigating the origin of this selectivity, the spectroscopic properties of these functionalized nanotubes and their possible application as single-photon emitters will be discussed and demonstrated.

Spectroscopic properties of functionalized (6,5) SWNTs

As shown above (Fig. 1d), the reaction time represents an excellent tool to precisely tune the E11* defect density of polymer-wrapped (6,5) SWNTs functionalized with 2-iodoaniline in the dark, which is reflected in the linear correlation of the E11*/E11 PL intensity ratio (Fig. 2a). Various additional metrics can be used to quantify the degree of functionalization. These are the integrated E11*/E11 absorption peak ratio and the Raman D/G+-mode ratio. Both are expected to be directly proportional to the number of sp3 defects35. The E11* defect absorption band, located around ~1247 nm (Fig. 2b), is much weaker than the E11 absorption but increases steadily with reaction time. The integrated E11*/E11 absorption ratios for different reaction times also reveal a linear correlation with the E11*/E11 PL intensity ratios (Fig. 2c). Their large difference (approximately a factor of 100) indicates the strong funneling effect of mobile excitons toward the luminescent defect states. The Stokes shift between E11* absorption and emission was rather small with 9–16 meV, similar to values for E11* defects introduced by diazonium chemistry34. The systematic increase of the Raman D-mode signal and thus D/G+ mode ratio with reaction time also showed a linear correlation with the E11*/E11 emission ratio (Supplementary Fig. 4) and can be used as an independent metric for the defect density.

Fig. 2: Spectroscopic characterization of functionalized (6,5) SWNTs.
figure2

ae (6,5) SWNTs functionalized with 2-iodoaniline in the dark. a Integrated E11*/E11 emission ratio vs. reaction time with linear fit. b Absorption spectra of functionalized (6,5) SWNTs normalized to E11 transition, showing phonon sideband (PSB, ~860 nm) and E11* absorption band (~1247 nm) increasing with reaction time. It is noteworthy that a broadening of the E11* defect absorption band may occur due to a scattering background caused by increasing aggregation of SWNTs at very high defect densities. c Integrated E11*/E11 emission vs. E11*/E11 absorbance ratio with linear fit. d Photoluminescence quantum yield (PLQY) of functionalized SWNTs (total and separated into spectral shares of E11* and E11) vs. integrated Raman D/G+ ratios as metric for defect density (lines are guides to the eye). e Normalized intensity of E11* (red) and E11 (black) emission vs. pulse energy density, indicating faster saturation of defect state than band-edge exciton emission. f PL lifetime (τlong, τshort) vs. optical trap depth for E11* and E11* defects created by functionalization of (6,5) SWNTs with 2-iodoaniline (orange), 2-bromoaniline (black), and 5-fluoro-2-iodoaniline (green).

As previously shown for E11* defects4,34, the controlled functionalization of SWNTs can be used to significantly enhance their ensemble PLQYs, albeit only at optimum defect densities. PLQY data (absolute values obtained with an integration sphere, see “Methods”) for (6,5) SWNTs with E11* defects are shown in Fig. 2d. The intensity of the E11 emission and thus also its contribution to the total PLQY decreases steeply with the number of defects (here quantified by the Raman D/G+ ratio), whereas the E11* share rises sharply as mobile excitons are trapped by the emissive defects. At even higher defect densities, the absolute E11 and E11* emission and thus PLQY decreases again as the sp2 lattice is disrupted by too many sp3 carbons, preventing the formation of extended electronic states. Areas with such high sp3 carbon concentrations act as quenching sites, thus decreasing the overall number of excitons for emission. Nevertheless, a strong brightening effect compared to the pristine samples (PLQY ~ 2%) was observed for the total PLQY of functionalized nanotubes, reaching up to 5.1% at optimal defect density. This represents a significant improvement compared to polymer-wrapped (6,5) SWNTs functionalized with diazonium salts (mainly E11* defects) and is consistent with the larger optical trap depth (difference between E11 and defect emission energy) of the E11* defects (241–247 meV)34.

Another characteristic feature of SWNT defect state emission is its nonlinear behavior at high pump power, i.e., the ratio of defect to E11 emission depends strongly on the chosen excitation method (lamp or laser, continuous or pulsed) and power (Fig. 2e and Supplementary Fig. 5), and decreases with excitation density. This power dependence can be explained with filling of the long-lived defect states at higher excitation densities36. It is more pronounced for the E11* defects with their emission already saturating at relatively low laser powers compared to the E11* defects (see Supplementary Fig. 6).

The increase in total PLQY and the power dependence of emission are best understood within the framework of the defect state relaxation dynamics. Hence, the PL decays for (6,5) SWNTs functionalized with 2-iodoaniline, 2-bromoaniline, or 5-fluoro-2-iodoaniline were recorded using time-correlated single-photon counting (TCSPC) and fitted as biexponential decays (see Supplementary Fig. 7) with a short (τshort) and long (τlong) lifetime component. As shown in Fig. 2f, the longer lifetimes increase significantly with optical trap depth from 179 ps for E11* (only for 2-iodoaniline, trap depth 136 meV) to up to 589 ps for E11* (trap depth 241 meV, see also Supplementary Table 2). The values are consistent with previous measurements of E11* defects that were introduced in much smaller numbers by diazonium chemistry18,37. The temperature dependence of the defect emission and thermal detrapping of excitons are presented and discussed in Supplementary Note 2 and Supplementary Figs. 811.

Single-photon emission and individual SWNT spectra

One important application of luminescent sp3 defects in SWNTs is as quantum-light sources in the near-infrared and at room temperature18,38. Defects with large optical trap depths are best suited for single-photon emission at higher temperatures and, ideally, emission should be within one of the standard telecommunication bands (O-band or C-band). The selectively produced E11* defects in polymer-wrapped SNWTs fullfil a good part of these requirements. To confirm their suitability as single-photon emitters, Hanbury–Brown–Twiss experiments were performed on individualized (6,5) SWNTs with a low concentration of E11* defects embedded in a polystyrene matrix at room temperature (see Fig. 3a–c). The probability of two consecutive photon detection events is expressed in the second-order photon-correlation function g(2)(t). Under pulsed excitation, the absence of detection events at zero time delay (here, g(2)(0) = 0.07) indicates photon antibunching with high single-photon purity (93%) for the E11* defects. Furthermore, high count rates (~60 kHz) were observed during the measurement with fluctuations near the shot-noise limit.

Fig. 3: PL characteristics of individual (6,5) SWNTs with E11* defects.
figure3

a PL spectrum of a single (6,5) SWNT functionalized with 2-iodoaniline embedded in a polystyrene matrix at room temperature (298 K) collected under continuous wave excitation at the E11 transition. b Second-order photon-correlation function g(2)(t) of E11* emission at room temperature, confirming high single-photon purity (93%). c PL time trace showing a count rate fluctuation near the shot-noise limit. The deviation of the PL intensity distribution of the emitter (\(\sigma _{\mathrm{QE}}\)) from the Poisson distribution of the detector shot noise (\(\sigma _{\mathrm{SN}}\)) is expressed as \(\sigma _{{\mathrm{QE}}}/\sigma _{{\mathrm{SN}}} = ((\langle {\mathrm{n}}^2\rangle - \langle {\mathrm{n}}\rangle ^2)/\langle n\rangle )^{0.5}\), with n being the number of PL counts within a 0.1 s timeframe. d PL spectra of 12 individual (6,5) SWNTs functionalized with 2-iodoaniline and embedded in a polystyrene matrix recorded at 4 K. The spectral ranges of the E11 (blue) and E11* (red) emission peaks are highlighted.

Comparable values were found by He et al.18 at similar emission wavelengths (1280 nm) for polymer-wrapped (6,5) SWNTs functionalized with a diazonium salt. However, in that case, the defect emission of the whole set of individual (6,5) SWNTs was distributed over a large spectral range (1000–1350 nm) due to the presence of many nanotubes with E11* defects and only few with E11* defects in the ensemble24. It is noteworthy that for the application of SWNTs as single-photon sources, homogeneous emission line broadening also represents a significant challenge. However, cavity enhancement of the radiative emission rate via the Purcell effect was recently shown to improve the photon indistinguishability22. Here, the exclusive introduction of E11* defects via the reaction with 2-iodoaniline in the dark enables a better matching with the limited bandwith of such cavities as the distribution of emission wavelengths is reduced to 1200–1300 nm.

The reduced spectral diversity is also reflected at the single-nanotube level as revealed by PL spectra of individualized (6,5) SWNTs with a low E11* defect density embedded in a polystyrene matrix at 4 K (Fig. 3d). Almost all defect emission peaks appear within an 80 meV window (highlighted in red), with peak widths between 2.9 and 5 meV (limited by a low-resolution grating) and exhibiting the typical asymmetric lineshapes of polymer-wrapped nanotubes. The remaining energetic shifts between emission peaks are likely due to variations in the dielectric environment18. It is noteworthy that the segmentation of the E11 emission (highlighted in blue) at 4 K originates from random localizations of excitons in long polymer-wrapped SWNTs or from other extrinsic defects introduced during initial processing. They are also present in SWNTs that were not specifically functionalized39,40,41. An integrated spectrum of 62 spots closely resembles the ensemble spectrum of a thin film at room temperature (Supplementary Fig. 12).

Luminescent sp 3 defects in larger diameter SWNTs

Although the E11* emission from (6,5) nanotubes (~1250 nm) is already close to relevant telecommunication bands and is well located within the second biological window (1000–1350 nm), further red-shifted PL is desirable. This might be achieved by introducing the same E11* defects in polymer-wrapped semiconducting nanotubes with larger diameters. Two possible candidates are (7,5) SWNTs (diameter 0.83 nm, E11 transition at 1047 nm) and (10,5) SWNTs (diameter 1.05 nm, E11 transition at 1276 nm). They can be selectively dispersed in toluene using suitable polyfluorene derivatives (poly[(9,9-dioctylfluorenyl-2,7-diyl)] (PFO) and poly[(9,9-dioctylfluorenyl-2,7-diyl)-alt-(1,4-benzo[2,1,3]thiadiazole)] (F8BT), see “Methods” and Supplementary Fig. 13). Nearly monochiral dispersions were functionalized with 2-iodoaniline in the dark. The resulting PL spectra are displayed in Fig. 4a, b, respectively. In both cases, almost only the E11* defect emission was observed; however, the achievable concentration of defects remained relatively low in comparison to the (6,5) SWNTs. Very long reaction times were required to reach moderate E11*/E11 PL ratios. The Raman D/G+ ratios for (7,5) nanotubes were also significantly lower than those for (6,5) SWNTs (Supplementary Fig. 14).

Fig. 4: Functionalization of polymer-wrapped SWNTs with larger diameters.
figure4

a PL spectra of PFO-wrapped (7,5) SWNTs functionalized with 2-iodoaniline in the dark after different reaction times with a red-shifted E11* emission band (~1270 nm). b PL spectra of F8BT-wrapped pristine (10,5) SWNTs and functionalized with 2-iodoaniline in the dark for 150 min. Functionalization gives rise to a red-shifted E11* emission band (~1474 nm). The concentration of 2-iodoaniline was kept at 29.30 mmol L−1. c Optical trap depths of E11* defect states as a function of SWNT diameter. d E11* defect fluorescence lifetimes (long and short) depending on optical trap depth.

The E11 and E11* emissions from SWNTs with larger diameters occur at longer wavelengths. However, the defect emission bands for (7,5) and (10,5) SWNTs appear at 1270 nm and 1474 nm, respectively, and thus not as far red-shifted as desired for applications. The optical trap depth of the E11* defects was previously shown to monotonically decrease with increasing nanotube diameter, making even more red-shifted emission increasingly harder to achieve42. This correlation was also found for the E11* defects in (7,5) and (10,5) SWNTs (optical trap depths of 215 meV and 89 meV, respectively) as shown in Fig. 4c. Shallower trap depths also lead to shorter defect PL lifetimes (Fig. 4d) reaching only 128 ps for the long lifetime component of E11* defects in (10,5) nanotubes. Both effects make trapping and radiative recombination at these defect sites less efficient and no increase in PLQY was observed upon functionalization as shown for (7,5) nanotubes with various defect densities (Supplementary Fig. 15).

Functionalization mechanism and origin of selectivity

The selectivity of the reaction of 2-haloanilines with SWNTs for defect-binding configurations with either E11* or E11* emission depends on conditions such as UV-light illumination and KOtBu concentration. The different selectivities suggest divergent reaction pathways that are explored in more detail in the following. Previous functionalization reactions of nanotubes with anilines and haloanilines employed UV activation of the reagent or the nanotubes and produced either only E11* emission or both E11* and E11* emission23,25,30. It is commonly assumed that the halogen is eliminated in the process of activation of haloanilines (dehalogenation). However, under the reaction conditions employed here, i.e., with KOtBu as the base and in the dark, a high reactivity and selectivity was observed not only for reactions with 2-iodoaniline and 2-bromoaniline but also for 2-fluoroaniline (see Fig. 5a). In the latter case, the reaction is not expected to occur via a dehalogenation process, as the C–F bond is one of the strongest known carbon bonds.

Fig. 5: Mechanistic investigation of functionalization.
figure5

a PL spectrum of (6,5) SWNTs functionalized with 2-fluoroaniline in the dark with a strong defect emission band at 1250 nm. b F 1s XPS spectra of (6,5) SWNTs after reaction with 2-fluoroaniline with (red circles including peak fit, red line) and without (black circles; reference) addition of KOtBu as base. The presence of the F 1s signal indicates covalent functionalization with 2-fluoroaniline, whereas the absence of this signal for the reference sample indicates lack of functionalization. c PL spectra of (6,5) SWNTs functionalized with 2-iodoaniline at different reaction temperatures in the dark. The concentrations of 2-fluoroaniline and 2-iodoaniline were kept at 29.30 mmol L1.

To answer the question what chemical group is actually attached to the nanotubes after functionalization, we performed X-ray photoemission spectroscopy (XPS) measurements on thin films of (6,5) SWNTs functionalized with 2-fluoroaniline, using the strong signal of the F 1s core level as a metric (see Fig. 5b). Clearly, the fluorine is present after functionalization, indicating that dehalogenation does not take place. The extracted binding energy (689.5 eV) is in agreement with literature values of alkyl and aryl C–F bonds43,44. Additional experiments were carried out with 5-fluoro-2-iodoaniline (Supplementary Fig. 16), with similar results. It is noteworthy that it was not possible to employ thermogravimetric analysis coupled with mass spectrometry45 to further confirm the nature of attached functional groups due to the necessarily low defect density and limited amount of purified (6,5) SWNTs.

To understand the reaction mechanism of (6,5) SWNTs in the presence of KOtBu and in the dark, we performed a large number of reference and control experiments (see Supplementary Tables 3 and 4). Surprisingly, functionalization of (6,5) nanotubes and strong defect emission bands (E11* and E11*) even occurred without any aniline derivative, thus suggesting side reactions that create the same defect-binding configuration. Control reactions were conducted both in toluene and THF. These experiments revealed a complex influence of reaction parameters and only the key aspects will be discussed here (see Supplementary Note 3 for details). Briefly, E11* emission bands only appear in the presence of KOtBu and a higher selectivity is achieved with the addition of DMSO as a co-solvent. Thus, the introduction of E11* defects can be associated with the basicity of the system, which is greatly increased by DMSO. In contrast to that, E11* emission bands appear only in the absence of DMSO or under UV irradiation. Irradiation of polymer-wrapped (6,5) SWNTs in THF or toluene with UV light without reagents did not result in any functionalization. Functionalization with 2-iodoaniline in the dark showed the typical temperature dependence of thermally activated reactions (see Fig. 5c) without losing its selectivity for E11* defects.

Considering the available data, we propose two possible functionalization mechanisms based on radical and nucleophilic reaction paths that determine the final defect-binding configurations. The E11* emission band is associated with the ortho-L90 (ortho++) configuration20,24,27, which is oriented in circumferential direction for (6,5) SWNTs (see Fig. 6, blue carbon atom). It is usually observed for reactions with diazonium salts and other monovalent functionalization reactions, e.g., with aryl halides, relying on radical formation. In our case, E11* emission mainly appears when the formation of radicals is assisted by UV-light illumination or electron transfer. Consequently, we assign the E11* emission to a reaction path where the carbon bonds in circumferential direction of the SWNT are attacked by radical species (indicated in blue in Fig. 6). Recent studies have shown that functionalization by radicals can also introduce further red-shifted E11* defects, but only when the already existing defects induce a higher π-orbital misalignment in bonds along the tube axis29. In contrast to that, non-radical reactive species exhibit an intrinsic preference for C–C bonds with large π-orbital misalignment and thus preferably attack carbon bonds in the axial direction (highlighted in red). Such reactive species are nucleophilic intermediates.

Fig. 6: Proposed functionalization mechanism for (6,5) SWNTs.
figure6

Aniline derivatives can follow two reaction paths in the presence of KOtBu and DMSO. Under UV-light irradiation, a radical species is formed that attacks the C–C bonds in circumferential direction, leading to the defect configuration for the E11* emission band (blue line). When the reaction is performed in the dark, deprotonation of the amine group and charge delocalization occurs. A nucleophilic attack on bonds with large π-orbital misalignment creates the defect configuration for the E11* emission band (red line). Similar reaction paths are expected for phenols, thiophenols, and indoles with different carbanion intermediates. It is noteworthy that the deprotonated aniline species is in equilibrium with its protonated form.

Nucleophilic intermediates can be formed via deprotonation of aniline derivatives by a base and stabilization of the anion through various possible resonance structures46,47. This initial deprotonation represents an equilibrium reaction, which shifts depending on the concentration of the base in relation to the aniline reagent. The observed increase in E11* emission for higher concentrations of base can therefore be attributed to a shift in favor of the deprotonated aniline species (see Fig. 1b). Nucleophilic attack of the SWNT would then lead to a charged SWNT intermediate that must be saturated quickly, e.g., by a proton from the solvent, yielding the defect configuration for E11* emission (i.e., ortho-L30). Similar nucleophilic reaction mechanisms have been reported for the functionalization of C60-fullerenes via KOtBu-promoted coupling of indoles48 and phenols49. In agreement with the proposed mechanism, strong E11* emission (Supplementary Fig. 17 and Supplementary Table 5) was also observed for the functionalization of (6,5) SWNTs with indole, 2-iodophenol, and thiophenol, although some other emission features were introduced as well. Significant variations of the delocalization of charge can be expected for different anilines, as well as phenols and indoles, thus leading to differences in stabilization and, consequently, reactivity of the carbanion intermediate. Depending on the reactivity of the carbanion intermediate, different selectivities of E11* vs. E11* defects may be achieved (see Supplementary Note 4). Under inert conditions, a strong increase in reactivity is observed (Supplementary Fig. 18), indicating that oxidation of the expected negatively charged intermediates (e.g., SWNT or other carbanionic intermediates, see Supplementary Note 5) and quenching of the base by moisture are inhibiting the functionalization under ambient conditions to some degree. It is also noteworthy that some nucleophilic addition reactions with nanotubes have been known for over a decade2; however, they usually involve very strong organic bases such as sodium hydride50 or organolithium/organomagnesium51,52 compounds. They have never been applied to introduce luminescent sp3 defects at low concentrations and thus their selectivity for certain binding configurations is not known.

Discussion

We have demonstrated a facile method for the functionalization of semiconducting SWNTs that selectively and exclusively creates luminescent sp3 defects with a binding configuration for strongly red-shifted E11* emission instead of the commonly found E11* emission. The reaction can be performed with various 2-haloanilines and other aniline derivatives at room temperature and in air. The final defect density is precisely and easily tuned by the concentration of the base KOtBu and the reaction time. Optimized defect densities enhance the absolute PLQYs to up to 5% for polymer-wrapped (6,5) SWNTs. The deep optical trap depth and long fluorescence lifetimes of the E11* defects in (6,5) SWNTs enable their application as near-infrared single-photon emitters at room temperature with high single-photon purity. Although the defect emission wavelength of 1250 nm lies well within the second biological window and thus might be useful for in vivo imaging, emission even further in the near-infrared was achieved by functionalization of (7,5) and (10,5) nanotubes. The high selectivity of this base-mediated reaction for a specific defect-binding configuration leading to the E11* emission probably relies on a nucleophilic reaction mechanism in contrast to commonly found aryl radical and reductive alkylation reactions. This type of base-mediated nucleophilic functionalization expands and complements the available chemistry for the controlled introduction of luminescent sp3 defects in SWNTs and opens the path to a broader variety of functional groups and thus applications.

Methods

Polymer-sorting of SWNTs

The (6,5) SWNTs were selectively dispersed from CoMoCAT raw material (Chasm SG65i-L63) by shear-force mixing (Silverson L2/Air, 10,230 r.p.m., 20 °C, 72 h) in a solution of PFO-BPy (American Dye Source, Mw = 40 kg mol−1, 0.5 g L−1) in toluene. The (7,5) SWNTs were sorted by dispersion in toluene with PFO (American Dye Source, Mw > 20 kg mol−1, 0.9 g L−1) as the wrapping polymer. For the enrichment of (10,5) SWNTs, HiPco raw material (Unidym, Inc., Batch No. 2172) was dispersed by tip sonication with F8BT (American Dye Source, MW = 59 kg mol−1, 4 g L−1) in toluene. Unexfoliated material was removed by centrifugation at 60,000 × g (Beckman Coulter Avanti J26XP centrifuge) and filtration (polytetrafluoroethylene (PTFE) syringe filter, 5 μm pore size). To remove excess polymer, the SWNTs were collected by vacuum filtration through a PTFE membrane filter (0.1 μm pore size). Filter cakes were washed three times with toluene at 80 °C and redispersed in fresh toluene by bath sonication. Excess F8BT was removed from (10,5) SWNT dispersions by ultracentrifugation (Optima XPN-80 centrifuge, 284,600 × g, 24 h). The polymer-rich supernatant was discarded and the obtained SWNT pellets were washed with THF three times before redispersion in fresh toluene.

Introduction of sp 3 defects

Polymer-wrapped SWNTs were functionalized with a range of commercially available aryl compounds (2-iodoaniline, 2-bromoaniline, 2-fluoroaniline, 5-fluoro-2-iodoaniline, 2-iodophenol, thiophenol, indole; used as received from Sigma Aldrich, ≥97%). For a step-by-step protocol, refer to Supplementary Methods 1. Briefly, an appropriate amount of aryl reagent was dissolved in toluene to achieve a final reaction concentration of 29.30 mmol L−1. DMSO (anhydrous) and KOtBu (Sigma Aldrich, 98%) dissolved in THF (anhydrous) were added to this solution. Finally, an enriched SWNT dispersion in toluene was added to the mixture such that the SWNT concentration in the reaction mixture corresponded to an optical density of 0.3 cm−1 at the E11 transition. The final solvent composition was 83.3 : 8.3 : 8.3 vol-% toluene/DMSO/THF. Functionalization was performed in the dark or under illumination with UV-light (LED SOLIS-365C, Thorlabs, 365 nm, 1.9 mW mm−2) at room temperature. The reaction was stopped after a given time by vacuum filtration of the reaction mixture through a PTFE membrane filter (0.1 μm pore size). The collected SWNTs were washed with methanol and toluene to remove unreacted reagents and side products. The resulting filter cake was redispersed by bath sonication in toluene with fresh wrapping polymer for stabilization.

Spectroscopic characterization

Absorption spectra were acquired with a Cary 6000i UV-VIS-NIR spectrophotometer (Varian, Inc.). PL spectra of dispersions at low excitation power and controlled temperature were recorded using a Fluorolog spectrofluorometer (HORIBA) with a 450 W xenon arc lamp and liquid-nitrogen-cooled InGaAs line camera. For acquisition of room temperature, PL spectra of dispersions, and time-correlated single-photon counting, the wavelength-tunable output of a picosecond-pulsed (~6 ps pulse width) supercontinuum laser (Fianium WhiteLase SC400) was used to excite SWNTs at the E22 transition. PL spectra were collected with an Acton SpectraPro SP2358 spectrograph (grating blaze 1200 nm, 150 lines mm−1) and a liquid-nitrogen-cooled InGaAs line camera (Princeton Instruments, OMA-V:1024). Wavelength-dependent PL lifetimes were measured by focusing the spectrally filtered emission onto a gated InGaAs/InP avalanche photodiode (Micro Photon Devices). The absolute PLQY was determined using an integration sphere (see Supplementary Methods 1 for details).

For low-temperature single-nanotube spectroscopy and temperature-dependent measurements, a dispersion of functionalized SWNTs was diluted with a toluene solution of polystyrene (Polymer Source, Inc., Mw = 230 kg mol−1) and spin-coated onto glass slides coated with 150 nm of gold. Samples were mounted in a closed-cycle liquid helium optical cryostat (Montana Instruments Cryostation s50) and excited with a continuous wave laser diode (OBIS, Coherent, Inc., 640 nm). PL images and spectra were recorded with a thermoelectrically cooled InGaAs camera (NIRvana 640ST) coupled to an IsoPlane SCT-320 spectrograph (Princeton Instruments). A standard Hanbury–Brown and Twiss setup was employed for measurements of second-order photon-correlation function g(2)(t) of individual SWNTs at room temperature. The sample was excited with a supercontinuum laser (NKT Photonics, SuperK EXTREME, 6 ps pulse width, 78 MHz repetition rate, tuned to 995 nm) and the emission detected with a pair of superconducting single-photon detectors (Scontel, TCOPRS-CCR-SW-85). Detection events were recorded and correlated using a TCSPC module (PicoQuant, PicoHarp300).

X-ray photoemission spectroscopy

Samples were prepared by drop casting of highly functionalized (6,5) SWNT dispersions on gold-coated silicon substrates. XPS measurements were performed with a MAX 200 (Leybold–Heraeus) spectrometer equipped with an Mg Kα X-ray source (260 W; ~1.5 cm distance to the samples) and a hemispherical analyzer (EA 200; Leybold–Heraeus). Spectra were acquired in normal emission geometry with an energy resolution of ~0.9 eV. The binding energy scale was calibrated to the Au 4f7/2 line of the substrate at 84.0 eV. Potential damage induced by X-rays was kept as low as possible. The measurements were carried out under ultra-high vacuum conditions at a base pressure of ~3 × 10−9 mbar.

Data availability

The datasets generated and/or analyzed during the current study are available in the heiDATA repository: https://doi.org/10.11588/data/RI2KLV.

References

  1. 1.

    Hirsch, A. Functionalization of single-walled carbon nanotubes. Angew. Chem. Int. Ed. 41, 1853–1859 (2002).

    CAS  Article  Google Scholar 

  2. 2.

    Tasis, D., Tagmatarchis, N., Bianco, A. & Prato, M. Chemistry of carbon nanotubes. Chem. Rev. 106, 1105–1136 (2006).

    CAS  PubMed  Article  Google Scholar 

  3. 3.

    Banerjee, S., Hemraj-Benny, T. & Wong, S. S. Covalent surface chemistry of single-walled carbon nanotubes. Adv. Mater. Lett. 17, 17–29 (2005).

    CAS  Article  Google Scholar 

  4. 4.

    Piao, Y. et al. Brightening of carbon nanotube photoluminescence through the incorporation of sp³ defects. Nat. Chem. 5, 840–845 (2013).

    CAS  PubMed  Article  Google Scholar 

  5. 5.

    Ghosh, S., Bachilo, S. M., Simonette, R. A., Beckingham, K. M. & Weisman, R. B. Oxygen doping modifies near-infrared band gaps in fluorescent single-walled carbon nanotubes. Science 330, 1656–1659 (2010).

    ADS  CAS  PubMed  Article  Google Scholar 

  6. 6.

    Miyauchi, Y. et al. Brightening of excitons in carbon nanotubes on dimensionality modification. Nat. Photonics 7, 715–719 (2013).

    ADS  CAS  Article  Google Scholar 

  7. 7.

    Brozena, A. H., Kim, M., Powell, L. R. & Wang, Y. Controlling the optical properties of carbon nanotubes with organic colour-centre quantum defects. Nat. Rev. Chem. 3, 375–392 (2019).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  8. 8.

    Shiraki, T., Miyauchi, Y., Matsuda, K. & Nakashima, N. Carbon nanotube photoluminescence modulation by local chemical and supramolecular chemical functionalization. Acc. Chem. Res. 53, 1846–1859 (2020).

    CAS  PubMed  Article  Google Scholar 

  9. 9.

    Gifford, B. J., Kilina, S., Htoon, H., Doorn, S. K. & Tretiak, S. Controlling defect-state photophysics in covalently functionalized single-walled carbon nanotubes. Acc. Chem. Res. 53, 1791–1801 (2020).

    CAS  PubMed  Article  Google Scholar 

  10. 10.

    Janas, D. Perfectly imperfect: a review of chemical tools for exciton engineering in single-walled carbon nanotubes. Mater. Horiz. 7, 2860–2881 (2020).

    CAS  Article  Google Scholar 

  11. 11.

    Hertel, T., Himmelein, S., Ackermann, T., Stich, D. & Crochet, J. Diffusion limited photoluminescence quantum yields in 1-D semiconductors: single-wall carbon nanotubes. ACS Nano 4, 7161–7168 (2011).

    Article  CAS  Google Scholar 

  12. 12.

    Kilina, S., Ramirez, J. & Tretiak, S. Brightening of the lowest exciton in carbon nanotubes via chemical functionalization. Nano Lett. 12, 2306–2312 (2012).

    ADS  CAS  PubMed  Article  Google Scholar 

  13. 13.

    Hartmann, N. F. et al. Photoluminescence imaging of solitary dopant sites in covalently doped single-wall carbon nanotubes. Nanoscale 7, 20521–20530 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

  14. 14.

    Kwon, H. et al. Optical probing of local pH and temperature in complex fluids with covalently functionalized, semiconducting carbon nanotubes. J. Phys. Chem. C 119, 3733–3739 (2015).

    CAS  Article  Google Scholar 

  15. 15.

    Hisashi, O., Tsuyohiko, F., Naotoshi, N. & Tomohiro, S. Control of the near infrared photoluminescence of locally functionalized single-walled carbon nanotubes via doping by Azacrown-ether modification. Chem. Eur. J. 24, 9393–9398 (2018).

    Article  CAS  Google Scholar 

  16. 16.

    Mandal, A. K. et al. Fluorescent sp³ defect-tailored carbon nanotubes enable NIR-II single particle imaging in live brain slices at ultra-low excitation doses. Sci. Rep. 10, 5286 (2020).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  17. 17.

    Mann, F. A., Herrmann, N., Opazo, F. & Kruss, S. Quantum defects as a toolbox for the covalent functionalization of carbon nanotubes with peptides and proteins. Angew. Chem. Int. Ed. 59, 17732–17738 (2020).

    CAS  Article  Google Scholar 

  18. 18.

    He, X. et al. Tunable room-temperature single-photon emission at telecom wavelengths from sp³ defects in carbon nanotubes. Nat. Photonics 11, 577–582 (2017).

    CAS  Article  Google Scholar 

  19. 19.

    Ma, X., Hartmann, N. F., Baldwin, J. K. S., Doorn, S. K. & Htoon, H. Room-temperature single-photon generation from solitary dopants of carbon nanotubes. Nat. Nanotechnol. 10, 671–675 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

  20. 20.

    Saha, A. et al. Narrow-band single-photon emission through selective aryl functionalization of zigzag carbon nanotubes. Nat. Chem. 10, 1089–1095 (2018).

    CAS  PubMed  Article  Google Scholar 

  21. 21.

    Nutz, M. et al. Photon correlation spectroscopy of luminescent quantum defects in carbon nanotubes. Nano Lett. 19, 7078–7084 (2019).

  22. 22.

    Luo, Y. et al. Carbon nanotube color centers in plasmonic nanocavities: a path to photon indistinguishability at telecom bands. Nano Lett. 19, 9037–9044 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  23. 23.

    Wu, X., Kim, M., Kwon, H. & Wang, Y. Photochemical creation of fluorescent quantum defects in semiconducting carbon nanotube hosts. Angew. Chem. Int. Ed. 57, 648–653 (2018).

    CAS  Article  Google Scholar 

  24. 24.

    He, X. et al. Low-temperature single carbon nanotube spectroscopy of sp3 quantum defects. ACS Nano 11, 10785–10796 (2017).

    CAS  PubMed  Article  Google Scholar 

  25. 25.

    Kwon, H. et al. Molecularly tunable fluorescent quantum defects. J. Am. Chem. Soc. 138, 6878–6885 (2016).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  26. 26.

    Berger, F. J. et al. Interaction of luminescent defects in carbon nanotubes with covalently attached stable organic radicals. ACS Nano, 15, 5147–5157 (2021).

  27. 27.

    Gifford, B. J., Kilina, S., Htoon, H., Doorn, S. K. & Tretiak, S. Exciton localization and optical emission in aryl-functionalized carbon nanotubes. J. Phys. Chem. C 122, 1828–1838 (2018).

    CAS  Article  Google Scholar 

  28. 28.

    Gifford, B. J. et al. Mod(n-m,3) dependence of defect-state emission bands in aryl-functionalized carbon nanotubes. Nano Lett. 19, 8503–8509 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  29. 29.

    Gifford, B. J. et al. Optical effects of divalent functionalization of carbon nanotubes. Chem. Mater. 31, 6950–6961 (2019).

    CAS  Article  Google Scholar 

  30. 30.

    Zheng, Y., Bachilo, S. M. & Weisman, R. B. Photoexcited aromatic reactants give multicolor carbon nanotube fluorescence from quantum defects. ACS Nano 14, 715–723 (2020).

    CAS  PubMed  Article  Google Scholar 

  31. 31.

    Shiraki, T., Shiraishi, T., Juhász, G. & Nakashima, N. Emergence of new red-shifted carbon nanotube photoluminescence based on proximal doped-site design. Sci. Rep. 6, 28393 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  32. 32.

    Artyukhov, V. I., Penev, E. S. & Yakobson, B. I. Why nanotubes grow chiral. Nat. Commun. 5, 4892 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  33. 33.

    Graf, A. et al. Large scale, selective dispersion of long single-walled carbon nanotubes with high photoluminescence quantum yield by shear force mixing. Carbon 105, 593–599 (2016).

    CAS  Article  Google Scholar 

  34. 34.

    Berger, F. J. et al. Brightening of long, polymer-wrapped carbon nanotubes by sp3 functionalization in organic solvents. ACS Nano 13, 9259–9269 (2019).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  35. 35.

    Dresselhaus, M. S., Jorio, A., Souza Filho, A. G. & Saito, R. Defect characterization in graphene and carbon nanotubes using Raman spectroscopy. Philos. Trans. R. Soc. A 368, 5355–5377 (2010).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Iwamura, M. et al. Nonlinear photoluminescence spectroscopy of carbon nanotubes with localized exciton states. ACS Nano 8, 11254–11260 (2014).

    CAS  PubMed  Article  Google Scholar 

  37. 37.

    He, X. et al. Solvent- and wavelength-dependent photoluminescence relaxation dynamics of carbon nanotube sp3 defect states. ACS Nano 12, 8060–8070 (2018).

    CAS  PubMed  Article  Google Scholar 

  38. 38.

    He, X. et al. Carbon nanotubes as emerging quantum-light sources. Nat. Mater. 17, 663–670 (2018).

    ADS  CAS  PubMed  Article  Google Scholar 

  39. 39.

    Hofmann, M. S., Noé, J., Kneer, A., Crochet, J. J. & Högele, A. Ubiquity of exciton localization in cryogenic carbon nanotubes. Nano Lett. 16, 2958–2962 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  40. 40.

    Raynaud, C. et al. Superlocalization of excitons in carbon nanotubes at cryogenic temperature. Nano Lett. 19, 7210–7216 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  41. 41.

    Kadria-Vili, Y., Bachilo, S. M., Blackburn, J. L. & Weisman, R. B. Photoluminescence side band spectroscopy of individual single-walled carbon nanotubes. J. Phys. Chem. C 120, 23898–23904 (2016).

    CAS  Article  Google Scholar 

  42. 42.

    Kim, M. et al. Mapping structure-property relationships of organic color centers. Chem 4, 2180–2191 (2018).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  43. 43.

    Deimel, P. S., Feulner, P., Barth, J. V. & Allegretti, F. Spatial decoupling of macrocyclic metal–organic complexes from a metal support: a 4-fluorothiophenol self-assembled monolayer as a thermally removable spacer. Phys. Chem. Chem. Phys. 21, 10992–11003 (2019).

    CAS  PubMed  Article  Google Scholar 

  44. 44.

    Lu, H., Kind, M., Terfort, A. & Zharnikov, M. Structure of self-assembled monolayers of partially fluorinated alkanethiols on GaAs(001) substrates. J. Phys. Chem. C 117, 26166–26178 (2013).

    CAS  Article  Google Scholar 

  45. 45.

    Schirowski, M., Hauke, F. & Hirsch, A. Controlling the degree of functionalization: in-depth quantification and side-product analysis of diazonium chemistry on SWCNTs. Chemistry 25, 12761–12768 (2019).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  46. 46.

    Alsharif, M. A., Khan, D., Mukhtar, S., Alahmdi, M. I. & Ahmed, N. KOtBu-mediated Aza-Michael addition of aromatic amines or N-phenylurea to 3-nitro-2-phenyl-2H-chromenes and sequential aerobic dehydrogenation. Eur. J. Org. Chem. 2018, 3454–3463 (2018).

    CAS  Article  Google Scholar 

  47. 47.

    Vakula, N. I., Kuramshina, G. M., Makhmutova, S. F. & Pentin, Y. A. DFT theoretical studies of anions of aniline and its several derivatives. J. Struct. Chem. 22, 345–356 (2010).

    Article  CAS  Google Scholar 

  48. 48.

    Li, F. et al. KOtBu-mediated, three-component coupling reaction of indoles, [60]fullerene, and haloalkanes: one-pot, transition-metal-free synthesis of various 1,4-(3-indole)(organo)[60]fullerenes. Org. Lett. 19, 1192–1195 (2017).

    CAS  PubMed  Article  Google Scholar 

  49. 49.

    Li, F. et al. KOtBu-promoted C4 selective coupling reaction of phenols and [60]fullerene: one-pot synthesis of 4-[60]fullerephenols under transition-metal-free conditions. J. Org. Chem. 83, 5431–5437 (2018).

    CAS  PubMed  Article  Google Scholar 

  50. 50.

    Wu, W. et al. PVK-modified single-walled carbon nanotubes with effective photoinduced electron transfer. Macromolecules 36, 6286–6288 (2003).

    ADS  CAS  Article  Google Scholar 

  51. 51.

    Wunderlich, D., Hauke, F. & Hirsch, A. Preferred functionalization of metallic and small-diameter single-walled carbon nanotubes by nucleophilic addition of organolithium and -magnesium compounds followed by reoxidation. Chem. Eur. J. 14, 1607–1614 (2008).

    CAS  PubMed  Article  Google Scholar 

  52. 52.

    Syrgiannis, Z. et al. Covalent sidewall functionalization of SWNTs by nucleophilic addition of lithium amides. Eur. J. Org. Chem. 2008, 2544–2550 (2008).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation program (Grant agreement number 817494 “TRIFECTs”). S.Z. acknowledges funding from the Alexander von Humboldt Foundation and A.H. from the European Research Council (ERC) under the Grant agreement number 772195 and the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) under Germany’s Excellence Strategy EXC-2111-390814868.

Funding

Open Access funding enabled and organized by Projekt DEAL.

Author information

Affiliations

Authors

Contributions

S.S., F.J.B., and S.L. performed synthesis and characterization. N.F.Z. and A.Y. contributed low-temperature spectroscopy. S.Z. and A.H. performed photon-correlation spectroscopy measurements. A.A. and M.Z. provided photoemission spectroscopy measurements. J.Z. conceived and supervised the project. S.S. and J.Z. wrote the manuscript. All authors discussed the data analysis and commented on the manuscript.

Corresponding author

Correspondence to Jana Zaumseil.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Dawid Janas and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Settele, S., Berger, F.J., Lindenthal, S. et al. Synthetic control over the binding configuration of luminescent sp3-defects in single-walled carbon nanotubes. Nat Commun 12, 2119 (2021). https://doi.org/10.1038/s41467-021-22307-9

Download citation

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing