Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Direct identification of Mott Hubbard band pattern beyond charge density wave superlattice in monolayer 1T-NbSe2

An Author Correction to this article was published on 10 May 2021

This article has been updated


Understanding Mott insulators and charge density waves (CDW) is critical for both fundamental physics and future device applications. However, the relationship between these two phenomena remains unclear, particularly in systems close to two-dimensional (2D) limit. In this study, we utilize scanning tunneling microscopy/spectroscopy to investigate monolayer 1T-NbSe2 to elucidate the energy of the Mott upper Hubbard band (UHB), and reveal that the spin-polarized UHB is spatially distributed away from the dz2 orbital at the center of the CDW unit. Moreover, the UHB shows a √3 × √3 R30° periodicity in addition to the typically observed CDW pattern. Furthermore, a pattern similar to the CDW order is visible deep in the Mott gap, exhibiting CDW without contribution of the Mott Hubbard band. Based on these findings in monolayer 1T-NbSe2, we provide novel insights into the relation between the correlated and collective electronic structures in monolayer 2D systems.


Mott insulators in coexistence with charge density wave (CDW) patterns in layered materials such as 1T-TaS21,2,3,4,5,6,7,8,9,10,11 is a long-term and extremely challenging research topic. They have been investigated for ~40 years owing to their fascinating multiple CDW states2. These types of materials are associated with insulator-to-metal changes and possess promising application potential in future nanodevices, such as ionic field-effect transistors12, voltage oscillators13, and ultrafast switches or memories10,14,15,16,17,18. Mott state and CDW order are believed to be correlated. For example, the CDW order can induce a substantial narrowing of the band width near the Fermi level, and with further on-site Coulomb repulsion, a Mott gap is opened19. Hitherto, significant effort has been expended in manipulating the CDW order to induce the collapse of the Mott insulator, e.g., by pressure application2,20, chemical doping21,22, interfacial structure tuning23,24, interlayer stacking25,26,27,28, and pulse injection of ultrafast laser25,29, current30,31, or voltage5,6,7. The main efforts have focused on bulk TaS2 crystals. Recently, the realization of the two-dimensional (2D) form of TaS2 and similar transition metal dichalcogenides (TMD)8,26,32 has caused the CDW order or Mott insulator to be revisited, with the aim to investigate the underlying mechanism and manipulate the layer-dependent properties of these novel quantum materials.

As a cousin of 1T-TaS2, 1T-NbSe2 has rarely been reported experimentally either in bulk or in a monolayer, because its favorable form is the 2H phase rather than the 1T phase33. Recently, some studies have reported the local induction of a 1T patch using the tip pulse34 or crash35 on the surface of a bulk 2H-NbSe2; furthermore, one study reported the molecular beam epitaxy (MBE) growth of small monolayer islands36. All these studies revealed the Star of David (SOD) pattern, which is a type of CDW superlattice; however, the relation between the upper Hubbard band (UHB) of Mott states with the CDW pattern has not been investigated.

In this study, we used the MBE method to grow high-quality large 1T-NbSe2 islands (a single island can be larger than 140 nm) on bilayer graphene (BLG) supported on a SiC substrate, which provides a good platform for studying the relationship between the Mott UHB and the CDW pattern with a high spatial and energy resolution. In fact, we observed three important features that have not been reported to date in 2D TMDs. First, the Mott UHB was distributed away from the center of the SOD. Second, the UHB exhibited a local √3 × √3 R30° periodicity related to the typically observed CDW pattern. Furthermore, a pattern similar to the CDW superlattice was visible in the Mott gap, showing a separation of the CDW from the Hubbard band. These observations provide some perspectives into the relation between Mott insulator bands and CDW in 2D quantum materials.


SOD CDW pattern of ML 1T-NbSe2

Figure 1a shows a large-scale scanning tunneling microscopy (STM) image with monolayer (ML) NbSe2 islands grown on BLG/SiC(0001). The 1T or 2H islands can be identified from the difference in the CDW superstructures, as the 1T phase has a larger modulation in the CDW pattern than the 2H phase (see Supplementary Fig. 1). Next, we focus on the ML 1T-NbSe2 islands. The center in Fig. 1a shows an ML 1T-island with a truncated triangular shape, with an edge length of ~120 nm. A schematic model of this ML 1T-NbSe2 island is shown in Fig. 1b. The atomic resolution image of the island shows a clear CDW pattern (in Fig. 1c, the inset is the fast Fourier transform (FFT) of this pattern), and a zoomed-in image (Fig. 1d) shows the basis vectors of both the atomic lattice in the topmost layer and the CDW pattern (a1 and a2; b1 and b2, respectively). The CDW order with a superstructure of √13 × √13 R13.9° to the topmost layer can be well distinguished. This type of CDW pattern is often known as the SOD pattern, reminiscent of those in 1T-TaS237,38 and 1T-TaSe28,32.

Fig. 1: Large-scale and high-quality monolayer 1T NbSe2 with “Star of David” (SOD) CDW pattern.
figure 1

a Large-scale STM image of MBE-grown NbSe2 islands on BLG/SiC(0001), showing ML 1T-NbSe2 island with edge length 120 nm at the center. b Side view of schematic atomic model of ML 1T-NbSe2 on BLG/SiC(0001) substrate. c Zoomed-in image of dashed black square in a showing both CDW pattern and atomic resolution of ML 1T-NbSe2 surface. Inset shows FFT image. d Zoomed-in image showing basis vector of CDW unit cell (with unit vectors b1 and b2) and atomic lattice of Top-Se layer (with unit vectors a1 and a2); the SOD (green star) was imaged as six top Se atoms (brown dots). e Top view of atomic model of NbSe2, showing SOD pattern and rhombus unit cell. f SOD model showing 13 Nb atoms at three different equivalent sites with six-fold symmetry. Central Nb atom (Nb1) labeled with schematic \(d_{z^2}\) orbital to indicate spatial distribution. Scanning parameters: a bias voltage VB = −1.5 V, tunneling current It = 20 pA; c and d, VB = −1.5 V, It = 500 pA.

To understand the detailed structure of the observed CDW order with the SOD, we constructed schematic atomic models of an SOD pattern (Fig. 1e) and a single SOD (Fig. 1f). In one single SOD, 13 Nb atoms were categorized as the central atom (Nb1), six at the nearest sites (Nb2), and the other six at the next nearest sites (Nb3). As shown in Fig. 1f, the central Nb atom is superimposed by its \(d_{z^2}\) orbital, whereas the other surrounding Nb atoms contract towards the central Nb1 and give rise to the fluctuation in the top Se plane21. The 12 Se atoms in the SOD unit were categorized into two groups: six Se atoms in the topmost plane (labeled by brown circles), and the other six in the bottom plane (labeled by light brown circles). The six topmost Se atoms contributed more to STM imaging and resulted in triangular protrusions in the SOD unit, as shown in Fig. 1c.

Reversed spatial contrast of UHB

To further study the local electronic structures of different sites in the CDW pattern, we performed constant-height dI/dV scanning tunneling spectroscopy (STS) along line AA′ (as shown in Fig. 2a), which is the long diagonal axis of several CDW rhombus unit cells. The high-quality large ML-1T NbSe2 islands enable us to select an area away from vacancy defects, adsorbates, or step edges; therefore, defect-induced and band-bending effects near the step edge were excluded. A zoomed-in image is shown in Fig. 2b. Owing to the triangular shapes of the top sites, two inequivalent hollow sites appeared and were named Hollow-1 and Hollow-2, as indicated by the blue triangle and green circle, respectively.

Fig. 2: Spatial-dependent electronic structures of monolayer 1T-NbSe2 on BLG/SiC(0001).
figure 2

a Area of 1T-NbSe2; AA′ is the line along which line dI/dV in c is obtained. Line profile (white curve) of AA′ is shown above AA′. b Zoomed-in image of one CDW unit cell showing Top, Hollow-1, and Hollow-2 sites, labeled by black triangle, blue triangle, and green circle, respectively. c Line dI/dV spectra along AA′ shown in color map mode. Spectra in one unit cell is shown in the frame, which contains Top, Hollow-1, and Hollow-2 regions. Four orbitals are labeled as CB, UHB, V1, and V2. d Zoomed-in image of c in 0–0.5 eV range showing spatial dependence of UHB. e Left: calculated band structure of 1T-NbSe2, where blue and red dots represent band projections of spin-down and spin-up dz2 orbitals of the center Nb atom (i.e., Nb1) in SOD, respectively. Right: corresponding partial density of states (PDOS) of Nb1 dz2 orbital. Calculations include spin polarization and GGA + U approximation. Scanning and spectroscopy parameters: a and b −1.5 V, 10 pA; c and d −1.5 V, 1 nA before turning off feedback loop.

The dI/dV spectra along the AA′ direction are shown in Fig. 2c and Supplementary Fig. 2, providing direct evidence of site-dependent change in the local electronic structure; it was observed that the change exhibited the periodicity of the CDW pattern. To provide visual guidance, we denoted four important orbitals (pronounced states at −0.28, −0.75, and +1.0 eV, and a faint state at +0.2 eV) by arrows, and named them as V1, V2, CB, and UHB. ML-1T NbSe2 is generally believed to be a Mott insulator36,38,39, thus the states right above and below the Fermi level probably are the upper and lower Hubbard band (UHB and LHB), respectively. Our GGA + U calculation confirmed the Mott insulator nature and show the LHB is highly mixed with valence band (VB). Whereas energy change was not observed in these orbitals, the intensities of these orbitals changed significantly based on the CDW sites (e.g., along the AA′ direction). For example, at the top sites, the V1 and V2 orbitals were strong, whereas the CB and UHB were weak; meanwhile, this trend was reversed at the hollow sites.

To distinguish the spatial distribution change in UHB state at +0.2 eV, we obtained high-precision line dI/dV spectra, which clearly show orbital feature with a periodicity (see Fig. 2d). Interestingly, the UHB exhibited a contrasting reversal with respect to the CDW topography (as denoted by the dashed-line in Fig. 2b and d). For example, at the bright top sites of the CDW superlattice, where the isolated dz2 orbitals of Nb atoms were located, the UHB was faint. Hence, our observations reveal that the Mott UHB was spatially distributed away from the dz2 orbital at the center of the CDW unit (the SOD).

To further investigate the characteristics of these four states, we conducted first-principles calculations on the band structure of ML-1T NbSe2 under different conditions. At this stage, we considered the freestanding monolayer to obtain the pristine properties. Through a comparison of four different conditions (Supplementary Fig. 3), the following were observed: When both the spin polarization and GGA + U approximation were considered, a Mott gap size of ~0.42 eV was obtained with a Coulomb interaction U of 2.8 eV, as shown in Fig. 2e. The values of the Mott gap and U were similar to those reported in recent literature regarding NbSe236,39,40. Our combination of experimental dI/dV and theoretical study elucidated the characteristics of the faint state at +0.2 eV as the UHB. Furthermore, our calculation highlighted that the opening of the Mott gap was a result of the coupling between the Mott and magnetic effects. Notably, the UHB was isolated from the conduction band with a spin-down state that originated from the contribution of the dz2 orbital of the Nb1 atom, whereas the corresponding LHB was mixed significantly with the VB owing to the hybridization of the spin-up state with other orbitals.

After identifying these four important bands from the line dI/dV spectra, we further performed point spectroscopy and bias-dependent STM imaging (for 2D dI/dV mapping, see Supplementary Fig. 4) to provide a more comprehensive study regarding the spatial distribution of the electronic states. As shown in Fig. 3a, in the three curves obtained from the three typical sites (Top, Hollow-1, and Hollow-2), the main peak positions remained the same, whereas the peak intensities changed. To better describe this change, the top sites were labeled by yellow dots (as shown in Fig. 3b–e) to signify the same or equivalent sites.

Fig. 3: Intriguing spatial dependence of UHB.
figure 3

a dI/dV spectra captured at Top, Hollow-1, and Hollow-2 areas of 1T-NbSe2. b, c STM images of SL 1T-NbSe2 at −0.3 and +0.6 V, respectively. d, e STM images captured with 0.2 V, 0.02 nA, and 0.2 V, 0.1 nA, respectively, showing √3 × √3 R30° superstructure (with unit vectors c1 and c2) with respect to the CDW pattern (with unit vectors b1 and b2). f Corresponding FFT of e. Tunneling parameters: a −1 V, 0.02 nA before turning off feedback loop. Scale bar for be: 2 nm.

Extra superstructure of UHB

The STM image captured at −0.3 eV (as shown in Fig. 3b) shows each triangular protrusion comprising six top Se atoms in each SOD area, resembling the image at −1.5 eV shown in Fig. 1c, and no clear change was visible. However, the STM image at +0.6 eV in Fig. 3c shows a clear change, i.e., the image contrast reversed: each top site marked by the yellow dot shows a clear change from a bright protrusion to a truncated triangular depression. This bias-dependent contrast is consistent with the black dI/dV spectrum shown in Fig. 3a, which shows that at −0.3 and +0.6 eV, the top exhibited the strongest and weakest intensities, respectively. This information is supported by the PDOS in Fig. 2e, which shows a very weak signal above UHB at the Nb1 sites.

Subsequently, we focus on the interesting feature near the Fermi level: the state at +0.2 eV (UHB state). The image captured at a bias voltage of +0.2 eV shows that each top site is also a depression (Fig. 3d). This depression feature is consistent with the line dI/dV spectra shown in Fig. 2d. However, clear differences at +0.2 eV (Fig. 3d) and +0.6 eV (Fig. 3c) were observed. One difference was indicated by the red dashed-line circles in Fig. 3d, where the surrounding orbitals of the top site are not connected, but isolated as “bright petals of a flower”.

Another difference was that a local super-period existed for the UHB states. Using the blue rhombus in Fig. 3e as an example, the two “flowers” centered at the long diagonal axis were brighter, whereas the two centered at the short diagonal axis were dim. Thus, in the hexagonal lattice of the SOD pattern, one bright flower is surrounded by six dim flowers as nearest neighbors. This spatial relationship resulted in a √3 × √3 R30° superstructure (with unit vectors c1 and c2) with respect to the CDW pattern (with unit vectors b1 and b2), as illustrated by the black rhombus in Fig. 3e. Subsequently, we further increased the feedback current from 0.1 to 3 nA to render the tip closer to the sample and resolve the atomic resolution, as shown in Supplementary Fig. 5, in which the atomic lattice in the center of the flower was resolved more effectively. The √3 × √3 R30° superstructure of the flower pattern can be well distinguished in the FFT pattern, as shown in Fig. 3f. Two sets of reciprocal lattices were resolved: the blue basis vectors represent the CDW lattice, and the black ones represent the √3 × √3 R30° with respect to the CDW pattern. Additional data of the √3 × √3 R30° superstructure were observed from a direct comparison of the STM images at −1.5 and +0.2 V, as shown in Supplementary Figs. 6, 7 and 8.

CDW pattern within the Mott gap

After investigating the three pronounced states and the special UHB state of ML-1T NbSe2, we further investigated the state around the Fermi level to identify possible gap states. Figure 4a shows a topographic image with six CDW long axis periods. Along the AA’ direction, the line dI/dV spectra in the range of −0.5 to 1.0 eV were obtained, as shown in Fig. 4b. We further zoomed-in on the energy region of −60 to 60 mV, which was close to the Fermi level but distant from the Hubbard band edge. The corresponding dI/dV spectra are shown in Fig. 4c, in which some residual conductance is visible. The residual conductance (tunneling electrons) was reasonable as the STM tip was brought close to the sample surface and continued tunneling on the 1T-NbSe2 even in the gap. The residual conductance (electronic state) was random and did not exhibit CDW patterns.

Fig. 4: Resolving CDW pattern in Mott insulator gap.
figure 4

a Area of 1T-NbSe2; AA′ is the line along which line dI/dV spectra were obtained. b Line dI/dV spectra captured along six CDW periods (AA′ in a) showing Mott gap between UHB and LHB. c Zoomed-in line dI/dV spectra in b, showing residual conductance within the gap, lacking periodicity. d Bias-dependent images showing CDW pattern clearly in Mott insulator gap. Energy positions are labeled in c, tunneling parameters: a −1.5 V, 10 pA; b −1.5 V, 1 nA; c −0.1 V, 0.5 nA before turning off feedback loop.

Intuitively, no CDW pattern is expected to be resolved in this energy region, and only atomic resolution is expected. However, both atom-resolved imaging and the CDW lattice were resolved clearly and ordered at ±50 meV, and this phenomenon remained at ±30 meV and persisted to ±10 meV, even though the CDW was only partially ordered. The ordered to partially ordered revolution suggested an electronic change among the images captured at different biases. In addition, the buckling of the top-hollow sites changed from 160 pm (at 50 mV) to 107 pm (at 10 mV), also indicating an electronic contribution change within the Mott gap. To the best of our knowledge, this is the first simultaneous observation of the residual conductance state in the Mott gap, bias-dependent CDW pattern, and atomic-resolved topmost lattice 2D TMD material in the same area.


The spatial distribution of the Mott UHB at +0.2 eV is yet to be elucidated. In the literature of density functional theory (DFT) calculations about NbSe238,39,40, the UHB is believed to arise from the central Nb atom in the SOD with an isolated dz2 orbital, which is inconsistent with our observations that the electronic states at the top sites are relatively lower than the hollow sites (Figs. 2d and 3d). We then considered mainly orbitals of the periphery Nb atoms (Nb2 and Nb3 in Fig. 1f), and calculated the local density of states. As seen in Supplementary Fig. 9, the calculated results indicate that the observed electronic states are related to both the central Nb atom and the periphery Nb atoms. Interestingly, our room temperature (RT) and 77 K measurements reveal that STM images at both −0.3 and +0.2 eV show the same spatial distribution without any contrast reversal (Supplementary Fig. 10), in line with the Mottness behavior of TaS221. The unconventional UHB spatial distribution at low temperature is probably associated with a low-temperature condensation process, similar to superconductivity, and paramagnetism. With the high CDW transition temperature above RT, our 1T-NbSe2 facilitates the application of CDW pattern as a template for mono-atomic dispersion41, such as heterogeneous catalysis, nanoscale magnetic quantum dots.

Whereas a Mott insulator with a UHB having a reversed contrast with the SOD top sites is interesting, the √3 × √3 R30° supermodulation at the UHB energy is even more intriguing. In this study, we excluded the substrate geometry effect such as the moiré pattern formed in the substrate. The BLG/SiC(0001) surface was reconstructed at the interface with a period of ~3 nm42, and it did not exhibit a commensurate relationship with the NbSe2 lattice of 1.25 nm. In addition, we studied NbSe2 islands on BLG/SiC(0001) with different rotation angles (0° and 11°), and both showed the same supermodulation with a √3 × √3 R30° pattern (Supplementary Fig. 11). As our GGA + U calculations show that the UHB is spin-polarized, each SOD unit contains one spin at the center Nb atom (numbered as “1” in Fig. 1f), and the SOD lattice forms a triangular lattice. Hence, ML 1T-NbSe2 is very likely to be a platform to host antiferromagnets43 or quantum spin liquid in a 2D triangular lattice44,45,46,47 (Supplementary Fig. 12). Further investigations into this novel supermodulation are necessitated.

We note that there are some limitations with our current STM and DFT methods. The current STM measurements have not characterized the spin properties directly, and a combined measurement with a spin-polarized STM tip and external magnetic field would be very useful to provide direct evidence. For the DFT calculations, the used exchange-correlation functionals have not described the semi-local or long-range ordering precisely. Dynamic mean-field theory and density matrix renormalization group would be employed to give more information on the spin orderings. These limitations would be circumvented in future.

In conclusion, we comprehensively investigated the relationship between the Mott insulator and CDW in ML-1T NbSe2 for the first time. Using STM/S to investigate the spatial and energy dependence of the correlated electronic system, we discovered that ML-1T NbSe2 exhibited the Mott UHB feature away from the SOD center (top sites) in the CDW pattern. Moreover, the Mott UHB state demonstrated a local √3 × √3 R30° superstructure with respect to the typically observed CDW pattern. Furthermore, we observed a CDW pattern in the Mott gap, showing a correlation between the CDW and the Mott Hubbard band state. DFT calculations demonstrated that +0.2 eV was the spin-polarized UHB, whereas the LHB was mixed with the VB. Using this quantum material, our findings provided new insights into the relationship between the correlated Hubbard band and CDW pattern in 2D systems.


Sample preparation and STM measurements

MBE and STM experiments were performed in an interconnected UHV system (base pressure 1 × 10−10 mbar) comprising MBE chambers and a low-temperature STM chamber. Epitaxial graphene was grown by the thermal decomposition of 4H-SiC(0001) at 1200 °C for 40 min. NbSe2 islands were prepared using the MBE method at a deposition rate of ~0.002 ML/min. An elemental Nb rod was used as the metal source in the e-beam evaporators (Focus Ltd.), whereas an elemental Se source in a Knudsen cell was heated to 120 °C. The deposition ratio of Se to Nb was larger than 20:1. During film deposition, the background pressure in the chamber was ~3.0 × 10−9 mbar. The BLG/SiC substrate was stored at ~550 °C during the deposition and post-annealing process to improve the diffusion and desorb excess Se48,49. STM imaging was performed using mechanically cut PtIr tips at a liquid helium temperature (4.2 K). The dI/dV tunneling spectra were acquired using lock-in detection by applying an AC modulation of 20 mV (r.m.s.) at 973 Hz to the bias voltage. A typical dI/dV on BLG is shown in Supplementary Fig. 13.

DFT calculations

First-principles calculations were performed using the Vienna Ab Initio Simulation Package50,51. The projector-augmented wave method and generalized gradient approximation were used to describe the electronics52,53. The 4d and 5s electronics of Nb atoms were considered as valence electrons with a plane wave energy cutoff of 381 eV. A 5 × 5 × 1 Monkhorst–Pack54 k-point mesh was adopted for geometric structure optimization, and a 7 × 7 × 1 k-point mesh was used to perform self-consistent calculations. To simulate the single layer situation, a 20 Å vacuum layer was applied. The relaxation of the atomic structure completed when the force on all atoms was <0.01 eV/Å−1.

Data availability

All data needed to evaluate the conclusions in the paper are present in the paper and in the  Supplementary Materials. Additional data related to this paper are available from the corresponding author upon reasonable request.

Change history


  1. Wu, X. L., Zhou, P. & Lieber, C. M. Determination of the local effect of impurities on the charge-density-wave phase in TaS2 by scanning tunneling microscopy. Phys. Rev. Lett. 61, 2604 (1988).

    ADS  CAS  PubMed  Article  Google Scholar 

  2. Sipos, B. et al. From Mott state to superconductivity in 1T-TaS2. Nat. Mater. 7, 960–965 (2008).

    ADS  CAS  PubMed  Article  Google Scholar 

  3. Wu, X. L., Zhou, P. & Lieber, C. M. Surface electronic properties probed with tunnelling microscopy and chemical doping. Nature 335, 55–57 (1988).

    ADS  CAS  Article  Google Scholar 

  4. Ritschel, T. et al. Orbital textures and charge density waves in transition metal dichalcogenides. Nat. Phys. 11, 328–331 (2015).

    CAS  Article  Google Scholar 

  5. Ma, L. et al. A metallic mosaic phase and the origin of Mott-insulating state in 1T-TaS2. Nat. Commun. 7, 10956 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  6. Cho, D. et al. Correlated electronic states at domain walls of a Mott-charge-density-wave insulator 1T-TaS2. Nat. Commun. 8, 392 (2017).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  7. Cho, D. et al. Nanoscale manipulation of the Mott insulating state coupled to charge order in 1T-TaS2. Nat. Commun. 7, 10453 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  8. Lin, H. et al. Scanning tunneling spectroscopic study of monolayer 1T-TaS2 and 1T-TaSe2. Nano Res. 13, 133–137 (2020).

    CAS  Article  Google Scholar 

  9. Park, J. W., Cho, G. Y., Lee, J. & Yeom, H. W. Emergent honeycomb network of topological excitations in correlated charge density wave. Nat. Commun. 10, 1024 (2019).

    Article  CAS  Google Scholar 

  10. Stojchevska, L. et al. Ultrafast switching to a stable hidden quantum state in an electronic crystal. Science 344, 177–180 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  11. Wu, X. L. & Lieber, C. M. Hexagonal domain-like charge-density wave phase of TaS2 determined by scanning tunneling microscopy. Science 243, 1703–1705 (1989).

    ADS  CAS  PubMed  Article  Google Scholar 

  12. Yu, Y. et al. Gate-tunable phase transitions in thin flakes of 1T-TaS2. Nat. Nano 10, 270–276 (2015).

    CAS  Article  Google Scholar 

  13. Liu, G. et al. A charge-density-wave oscillator based on an integrated tantalum disulfide-boron nitride-graphene device operating at room temperature. Nat. Nanotechnol. 11, 845–850 (2016).

    ADS  CAS  PubMed  Article  Google Scholar 

  14. Vaskivskyi, I. et al. Fast electronic resistance switching involving hidden charge density wave states. Nat. Commun. 7, 11442 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  15. Geremew, A. K. et al. Bias-voltage driven switching of the charge-density-wave and normal metallic phases in 1T-TaS2 thin-film devices. ACS Nano 13, 7231–7240 (2019).

    CAS  PubMed  Article  Google Scholar 

  16. Ligges, M. et al. Ultrafast doublon dynamics in photoexcited 1T-TaS2. Phys. Rev. Lett. 122, 159901 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  17. Laulhe, C. et al. Ultrafast formation of a charge density wave state in 1T-TaS2: observation at nanometer scales using time-resolved X-ray diffraction. Phys. Rev. Lett. 118, 247401 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

  18. Haupt, K. et al. Ultrafast metamorphosis of a complex charge-density wave. Phys. Rev. Lett. 116, 016402 (2016).

    ADS  PubMed  Article  CAS  Google Scholar 

  19. Fazekas, P. & Tosatti, E. Electrical, structural and magnetic properties of pure and doped 1T-TaS2. Philos. Mag. B 39, 229–244 (1979).

    ADS  CAS  Article  Google Scholar 

  20. Martino, E. et al. Preferential out-of-plane conduction and quasi-one-dimensional electronic states in layered 1T-TaS2. NPJ 2D Mater. Appl. 4, 7 (2020).

    CAS  Article  Google Scholar 

  21. Qiao, S. et al. Mottness collapse in 1T-TaS2-xSex transition-metal dichalcogenide: an interplay between localized and itinerant orbitals. Phys. Rev. X 7, 041054 (2017).

    Google Scholar 

  22. Zhu, X.-Y. et al. Realization of a metallic state in 1T-TaS2 with persisting long-range order of a charge density wave. Phys. Rev. Lett. 123, 206405 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  23. Shen, S. et al. Melting of charge density wave and Mott gap collapse on 1T-TaS2 induced by interfacial water. Phys. Rev. Mater. 4, 064007 (2020).

    ADS  CAS  Article  Google Scholar 

  24. Wang, Z. et al. Modulating charge density wave order in a 1T-TaS2/Black phosphorus heterostructure. Nano Lett. 19, 2840–2849 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  25. Stahl, Q. et al. Collapse of layer dimerization in the photo-induced hidden state of 1T-TaS2. Nat. Commun. 11, 1247–1247 (2020).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  26. Zhang, K., Si, C., Lian, C.-S., Zhou, J. & Sun, Z. Mottness collapse in monolayer 1T-TaSe2 with persisting charge density wave order. J. Mater. Chem. C 8, 9742–9747 (2020).

    CAS  Article  Google Scholar 

  27. Ma, Y., Wu, D. & Wang, Z. The evidence of stacking disorder from dielectric response along the c-axis in the commensurate CDW in bulk 1T-TaS2. Solid State Commun. 316, 113946 (2020).

    Article  CAS  Google Scholar 

  28. Butler, C. J., Yoshida, M., Hanaguri, T. & Iwasa, Y. Mottness versus unit-cell doubling as the driver of the insulating state in 1T-TaS2. Nat. Commun. 11, 2477 (2020).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  29. Zhang, J. et al. Photoexcitation induced quantum dynamics of charge density wave and emergence of a collective mode in 1T-TaS2. Nano Lett. 19, 6027–6034 (2019).

    ADS  CAS  PubMed  Article  Google Scholar 

  30. Ma, Y., Wu, D., Lu, C. & Petrovic, C. The electric pulses induced multi-resistance states in the hysteresis temperature range of 1T-TaS2 and 1T-TaS1.6Se0.4. Appl. Phys. Lett. 116, 171906 (2020).

    ADS  Article  CAS  Google Scholar 

  31. Yoshida, M., Sato, T., Kagawa, F. & Iwasa, Y. Charge density wave dynamics in nonvolatile current-induced phase transition in 1T-TaS2. Phys. Rev. B 100, 155125 (2019).

    ADS  CAS  Article  Google Scholar 

  32. Chen, Y. et al. Strong correlations and orbital texture in single-layer 1T-TaSe2. Nat. Phys. 10, 1038 (2020).

    Google Scholar 

  33. Kadijk, F. & Jellinek, F. On the polymorphism of niobium diselenide. J. Less-Common Met. 23, 437–441 (1971).

    CAS  Article  Google Scholar 

  34. Bischoff, F. et al. Nanoscale phase engineering of niobium diselenide. Chem. Mater. 29, 9907–9914 (2017).

    CAS  Article  Google Scholar 

  35. Wang, H., Lee, J., Dreyer, M. & Barker, B. I. A scanning tunneling microscopy study of a new superstructure around defects created by tip–sample interaction on 2H-NbSe2. J. Phys. Condens. Matter 21, 265005 (2009).

    ADS  PubMed  Article  CAS  Google Scholar 

  36. Nakata, Y. et al. Monolayer 1T-NbSe2 as a Mott insulator. NPG Asia Mater. 8, e321 (2016).

    CAS  Article  Google Scholar 

  37. Wilson, J. A., Di Salvo, F. J. & Mahajan, S. Charge-density waves and superlattices in the metallic layered transition metal dichalcogenides. Adv. Phys. 24, 117–201 (1975).

    ADS  CAS  Article  Google Scholar 

  38. Pasquier, D. & Yazyev, O. V. Charge density wave phase, Mottness, and ferromagnetism in monolayer 1T-NbSe2. Phys. Rev. B 98, 045114 (2018).

    ADS  CAS  Article  Google Scholar 

  39. Kamil, E. et al. Electronic structure of single layer 1T-NbSe2: interplay of lattice distortions, non-local exchange, and Mott–Hubbard correlations. J. Phys.: Condens. Matter 30, 325601 (2018).

    CAS  Google Scholar 

  40. Calandra, M. Phonon-assisted magnetic Mott-insulating state in the charge density wave phase of single-layer 1T-NbSe2. Phys. Rev. Lett. 121, 026401 (2018).

    ADS  CAS  PubMed  Article  Google Scholar 

  41. Feng, H. et al. Role of charge density wave in monatomic assembly in transition metal dichalcogenides. Adv. Funct. Mater. 29, 1900367 (2019).

    Article  CAS  Google Scholar 

  42. Hass, J., de Heer, W. A. & Conrad, E. H. The growth and morphology of epitaxial multilayer graphene. J. Phys.: Condens. Matter 20, 323202 (2008).

    Google Scholar 

  43. Huse, D. A. & Elser, V. Simple variational wave-functions for two-dimensional Heisenberg spin-1/2 antiferromagnets. Phys. Rev. Lett. 60, 2531–2534 (1988).

    ADS  CAS  PubMed  Article  Google Scholar 

  44. Law, K. T. & Lee, P. A. 1T-TaS2 as a quantum spin liquid. Proc. Natl Acad. Sci. USA 114, 6996–7000 (2017).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  45. Yu, Y. J. et al. Heat transport study of the spin liquid candidate 1T-TaS2. Phys. Rev. B 96, 081111 (2017).

    ADS  Article  Google Scholar 

  46. Ribak, A. et al. Gapless excitations in the ground state of 1T-TaS2. Phys. Rev. B 96, 195131 (2017).

    ADS  Article  Google Scholar 

  47. Klanjšek, M. et al. A high-temperature quantum spin liquid with polaron spins. Nat. Phys. 13, 1130–1134 (2017).

    Article  CAS  Google Scholar 

  48. Wu, X. et al. Shallowing interfacial carrier trap in transition metal dichalcogenide heterostructures with interlayer hybridization. Nano Res. 14, 1390 (2020).

    ADS  CAS  Article  Google Scholar 

  49. Liu, Z. L. et al. Epitaxially grown monolayer VSe2: an air-stable magnetic two-dimensional material with low work function at edges. Chin. Sci. Bull. 63, 419–425 (2018).

    Google Scholar 

  50. Kresse, G. & Furthmuller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).

    CAS  Article  Google Scholar 

  51. Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

    ADS  CAS  Article  Google Scholar 

  52. Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).

    ADS  CAS  Google Scholar 

  53. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  CAS  PubMed  Article  Google Scholar 

  54. Methfessel, M. & Paxton, A. T. High-precision sampling for brillouin-zone integration in metals. Phys. Rev. B 40, 3616–3621 (1989).

    ADS  CAS  Article  Google Scholar 

Download references


Thanks for the financial supporting from National Key Research and Development Program of China (2019YFA0308000, 2020YFA0308800), National Natural Science Foundation of China (Nos. 61971035, 61725107, 61901038, 61922035, 11874171), Beijing Natural Science Foundation (Nos. Z190006, 4192054), and the Strategic Priority Research Program of Chinese Academy of Sciences (XDB30000000).

Author information

Authors and Affiliations



L.W.L., H.-J.G. and Y.L.W. coordinated the research project. L.W.L. performed the main experimental fabrication and measurements. H.Y., X.S., Q.Z.Z., Z.P.H., Y.H.H., Y.Y.C., Z.Q.X., T.Z., X.W., Y.H. and Y.L.W. partially participated in the sample fabrication and measurements. Y.T.H., J.T.S., X.B.L., F.W.Z. and Y.G.Y. performed the DFT calculations. All authors analyzed the data and discussed the manuscript.

Corresponding author

Correspondence to Liwei Liu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Yi Du and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Liu, L., Yang, H., Huang, Y. et al. Direct identification of Mott Hubbard band pattern beyond charge density wave superlattice in monolayer 1T-NbSe2. Nat Commun 12, 1978 (2021).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing