Abstract
Time reversal symmetric (TRS) invariant topological insulators (TIs) fullfil a paradigmatic role in the field of topological materials, standing at the origin of its development. Apart from TRS protected strong TIs, it was realized early on that more confounding weak topological insulators (WTI) exist. WTIs depend on translational symmetry and exhibit topological surface states only in certain directions making it significantly more difficult to match the experimental success of strong TIs. We here report on the discovery of a WTI state in RhBi_{2} that belongs to the optimal space group P\(\bar{1}\), which is the only space group where symmetry indicated eigenvalues enumerate all possible invariants due to absence of additional constraining crystalline symmetries. Our ARPES, DFT calculations, and effective model reveal topological surface states with saddle points that are located in the vicinity of a Dirac point resulting in a van Hove singularity (VHS) along the (100) direction close to the Fermi energy (E_{F}). Due to the combination of exotic features, this material offers great potential as a material platform for novel quantum effects.
Similar content being viewed by others
Introduction
From the perspective of considering solely TRS, 3D topological insulators are classified by a series of Z_{2} topological invariants, (ν_{0};ν_{1}ν_{2}ν_{3}). The case ν_{0} = 1 is referred to as a strong topological insulator (STI) ^{1,2}. A characteristic feature of a STI is the existence of gapless topological surface state (TSS) on all surfaces, which have been observed experimentally in many materials such as Bi_{1−x}Sb_{x}, Bi_{2}Se_{3}, and Bi_{2}Te_{3} ^{3}. In contrast to 2D TIs, even when ν_{0} = 0 the system can have nontrivial ν_{i}, resulting in a weak topological insulator (WTI). Reported WTI states are rather rare as gapless TSS can be detected only on particular surfaces, which may not be natural cleaving planes in many 3D materials. For instance, Bi_{14}Rh_{3}I_{9} was predicted to be a WTI with Z_{2} = (0;001). However, direct experimental verification of the TSS has remained elusive since the cleaving plane is (001), which is a topologically trivial side ^{4} and hence forces reverting to indirect signals on e.g., step edges^{5}. The recent development of nanoARPES has reinvigorated the search for WTIs. For instance, a first WTI TSS was only recently measured by isolating a ~2 μm size side facet and using nanoARPES in quasionedimensional bismuth iodide βBi_{4}I_{4}^{6}.
As part of an effort to design and discover materials with novel, intrinsically nontrivial, topological properties we identified RhBi_{2} as an exciting candidate material. To minimize potential degeneracies in reciprocal space, we decided to start with the lowest possible symmetry unit cell: triclinic. To maximize spinorbit coupling we chose the heaviest (essentially) stable element, Bi as a majority component. For simplicity we chose to start by limiting our search to binary compounds. As a result of this cascade of physically inspired constraints we rapidly identified RhBi_{2} as a promising candidate material with clear van der Waalslike bonding along the crystallographic aaxis (Fig. 1b). RhBi_{2} grows in triclinic, RhBi_{2} structure (aP12, space group 2). RhBi_{2} is the only known compound to this specific, very low symmetry, structure. Here, we provide theoretical understanding and experimental evidence of the simplest WTI state in triclinic crystal RhBi_{2} with clear TSS at the natural cleaving surface. As we will discuss below, the WTI classification of RhBi_{2} maximally profits from its space group. As \(P\bar{1}\) only features inversion in addition to translations, all topological properties in the presence of TRS can faithfully be determined from the parity eigenvalues of the occupied bands at TRIM points^{7}. Moreover, due to the absence of additional symmetries none of these high symmetry momenta are related and a WTI can exist in every stacking direction^{8}. In fact, this carefully selected, simple structure makes this the only space group in which the symmetry eigenvalues at TRIM points convey all topological invariants onetoone^{9,10,11,12}. Rather surprisingly, we find that this freedom of choosing the stacking direction culminates in an index, (0;001), that is perpendicular to the layering of the material, creating the possibility of a TSS preserving cleavage plane.
The lack of symmetries, especially the absence of rotational symmetry, in triclinic RhBi_{2} allows the system to have a saddle points, where the curvature of a band has opposite sign in two perpendicular direction in momentum space. A saddle point is closely related to a VHS, leading to a divergence in the density of states. Previously, VHSs have been reported in a variety of materials; graphene^{13,14}, cuprate superconductors^{15,16,17}, Pt_{2}HgSe_{3} ^{18}, Pb_{1−x}Sn_{x}Se(Te)^{19}. The proximity of E_{F} to a VHS is expected to significantly enhance the impact of electronic correlations and drive quantum many body instabilities toward superconductivity^{20,21,22} ferromagnetism^{23,24,25,26} or antiferromagnetism^{27}, depending on band structure and manybody interactions. In addition, the subtle interplay of protected and correlated surface states with the bulk is predicted to lead to unusual surface quantum criticality^{28}. As we show, this is expected to result in an order of magnitude enhancement of superconducting T_{c}, and generally increases the tendency toward development of electronic order. Partial substitution of Rh with Ru or electrostatic gating offer a possible path for lowering the E_{F} in RhBi_{2}. Owing to the simplest topological classification and VHS in the vicinity of E_{F}, triclinic crystal RhBi_{2} offers unique advantages for exploring exotic quantum phenomena in a weak topological insulator.
We present a study of triclinic RhBi_{2} by using ARPES, DFT calculations and an effective model. Our result reveals two surface Dirac points, which are protected by timereversal symmetry at the \(\bar{{{\Gamma }}}\) and \(\bar{Z}\) points. We focused experimental attention at the momentum space around the \(\bar{Z}\) point of the surface BZ. The shape of the Dirac cone around \(\bar{Z}\) is significantly modified from typical Dirac dispersion due to the presence of two saddle points associated with a VHS. The saddle points are located at a binding energy of ~ 80 meV. Based on DFT calculations, we identify that surface state of RhBi_{2} along (100) has a WTI phase, which is characterized by Z_{2} = (0;001).
Results
Band structure calculations
Due to the symmetry group hosting only an inversion center, the layered triclinic RhBi_{2} is an interesting case in terms of both band structure and topology. The bulk band structure of RhBi_{2} calculated from density functional theory^{29,30} (DFT) using PBE exchange correlation functional with spinorbit coupling (SOC) is plotted in Fig. 1c. The 3D FS at the E_{F} is shown in Fig. 1e with the eight timereversal invariant momentum (TRIM) points and reciprocal lattice vectors labeled. By virtue of inversion symmetry and TRS, all bands are doubly degenerate in the BZ due to Kramers theorem. The bands of interest arise by hybridization from Rh d and Bi p orbitals. From the small but finite density of states (DOS) at E_{F} in Fig. 1d, we see that RhBi_{2} is a metal exhibiting nonoverlapping pockets. There are no crossings between the top valence and bottom conduction bands anywhere in the BZ. The two bands crossing the E_{F} give multiple electron and hole pockets. The electron and hole pockets are near BZ boundaries, while there is a large band gap around the BZ center Γ point. Notable are the electron pockets around X and near L points and the hole pockets near the Y point. There are also two small hole pockets totally inside the BZ. Although the structure is stacked on the bc plane along the b_{1} direction, a large electron pocket is on the b_{1} = 0.5 plane around the X point. In contrast, there is band gap on the b_{3} = 0.5 plane around the Z point.
Topological analysis. With inversion being the only symmetry in the system besides timereversal symmetry, the topological features are determined by the parity eigenvalues of the occupied bands at TRIM points^{7}. In fact, from the perspective of the recent advancements in classifying band structures using constraints in symmetry eigenvalues^{10} and comparing them to atomic configurations^{11,12}, the space group at hand, number 2 or \(P\bar{1}\), is the only one in which such symmetry indicators unambiguously define all topological invariants^{8,9}, as there are no symmetry constraints between high symmetry momenta^{8}. The topological indices, apart from TRS invariant ν_{0} that we find to be zero, comprise three Z_{2} invariants corresponding to the weak indices and a Z_{4} index^{31} that comes from promoting ν_{0} to the inversion symmetric context. The latter corresponds to the twice the value of the inversion invariant δ_{i}, Z_{4} = 2δ_{i}, here^{9}. The calculated Z_{4} index is 2, indicating that RhBi_{2} is topologically nontrivial, but indeed not a strong topological insulator. The calculated parity eigenvalue products are (+1) at Γ and Z points, and (1) at all the other TRIMs, which gives the FuKane index of (0;001), determining the three Z_{2} invariants. This can also be confirmed by Wannier charge center (WCC) evolution or Wilson loop on k_{3} = 0.0 and 0.5 planes in Fig. 1g and g, showing 2D Z_{2} = 1 on these planes^{32,33,34}. In contrast, 2D Z_{2} = 0 on the other k_{1,2} = 0.0 or 0.5 planes. Interestingly, although the layered structure is stacked along the b_{1} direction, the weak TI can be seen as a stacking of quantum spin Hall (QSH) layers along the b_{3} direction.
In Fig. 1f, the 3D FS is rotated for the view along b_{1} or perpendicular to the bc plane, i.e., (100). On the (100) surface, the Γ and X points are projected to \(\bar{{{\Gamma }}}\) point, Z and N to \(\bar{Z}\) point, and Y and L to \(\bar{Y}\) point, respectively. This shows that for the 2D FS on (100) around the E_{F}, the area near the \(\bar{Z}\) point is gapped without bulk band projection, while the \(\bar{{{\Gamma }}}\) and \(\bar{Y}\) points are surrounded by bulk states. For bulkboundary correspondence of TIs^{35}, parity eigenvalue products can also be projected onto surface as in π_{a} = δ_{a1}δ_{a2}, where TRIM a_{1} and a_{2} projected into a on surface. The result is (−1) for \(\bar{{{\Gamma }}}\) and \(\bar{Z}\) points, while (+1) for the others. Thus, an even number of two surface Dirac points will emerge on (100), one at \(\bar{{{\Gamma }}}\) and the other at \(\bar{Z}\). In summary, RhBi_{2} is a topologically nontrivial 2D material as a layered compensating semimetal hosting the simplest WTI possible as the underlying space group has minimal symmetry.
Electronic structure measured by ARPES
In order to verify the nontrivial topological nature of triclinic RhBi_{2}, we performed ARPES measurements and DFT calculations to identify relevant features in the electronic structure. Fig. 2a shows projection of TRIM points and the FS of triclinic RhBi_{2} measured using laserbased APRES, where dashed lines mark main crystallographic directions in the BZ. The experimental data in Fig. 2a may appear to have twofold symmetry, but upon closer inspection it does not. The left and right surrounding of the \(\bar{Z}\) pocket are quite different, as there is additional FS sheet merging with bulk bands to the right of Z pocket (marked by red circle in Fig 2a), but it is absent on the left side. This is in good agreement with calculations in Fig. 2d, where the sharper surface state is present on the right side of Z pocket, but no on the left. To determine projection of TRIM points on FS, we analyze Momentum distribution curves (MDCs) and Energy distribution curves (EDCs), Dashed lines are marked along two different projection of TRIM points (\(\bar{{{\Gamma }}}\)\(\bar{Y}\) and \(\bar{{{\Gamma }}}\)\(\bar{Z}\)). Since It is well known that surface Dirac points appear at TRIM points, we used location of surface Dirac points to determine TRIM points. We carefully checked MDCs and EDCs to verify the location of \(\bar{Z}\) point. Fig. 2h shows MDC extracted at chemical potential. Fig. 2i shows EDCs at centers of two MDC peaks around \(\bar{{{\Gamma }}}\) and \(\bar{Z}\), respectively. The measured band dispersion along those lines are shown in Fig. 2b and c. Two Dirac points are clearly present in the data: one located at the \(\bar{{{\Gamma }}}\) point with a binding energy of ~ 500 meV and the other at the \(\bar{Z}\) point with a binding energy of ~80 meV. The red arrow marks the Dirac point at the \(\bar{{{\Gamma }}}\) point and the blue arrow marks the Dirac point at the \(\bar{Z}\) point. Fig. 2c shows the band dispersion along the \(\bar{{{\Gamma }}}\)\(\bar{Y}\) direction where the red arrow marks the location of the Dirac point there. Fig. 2d–f shows DFT calculations along the same directions as for the ARPES data. Overall, DFT calculations agree quite well with experimental data. Unlike typical TSS of STIs, which have a single Dirac point, we observe two surface Dirac points at TRIM points. This apparent discrepancy between STIs and WTIs shows that triclinic RhBi_{2} possesses TSS arising from weak topological insulating phase in (100) direction. In addition, we observed twofold rotational symmetry at the FS from the DFT calculations, although the crystal structure is triclinic. This is because threedimensional inversion symmetry reduces to effectively twodimensional rotation symmetry upon projection of all transverse momenta. To understand this phenomenon, we carefully studied different projections of each layer in the unit cell. Supplementary Note 3 shows different projections of k_{1}(k_{x}) values on (100) surface. Red looped curves represent electron pockets. Based on the calculation, only projections from k_{1}= 0 and 0.5 planes show twofold rotational symmetry and the k_{1} = 0 plane shows large electron pocket around the center of the BZ. Therefore, the large electron pocket around \(\bar{{{\Gamma }}}\) is mainly from the k_{1} = 0 plane and addition of all planes in the BZ will give us the effective twofold rotational symmetry on the 2D FS.
To demonstrate surface state origin of the measured band dispersion, we plot data along a \(\bar{{{\Gamma }}}\bar{Z}\) direction that were measured using different photon energy (21.2 eV) in Fig. 2g. The sharp band dispersion measured using 21.2 eV photons is identical to the one measured using 6.7 eV and shown in Fig. 2a, which proves its surface state origin. To demonstrate this better, we plot MDC at the chemical potential in Fig. 2h and EDCs at the two Dirac points in Fig. 2i for the two photon energies.Although there is some variation in overall intensity due to matrix elements, the peaks in solid curves measured using 21.2 eV and dashed curves that were measured using 6.7 eV occur at the same momenta/energies which demonstrates lack of dispersion along direction perpendicular to sample surface and thus surface state origin. We also note that while 6.7 eV data was measured using photons polarized along \(\bar{{{\Gamma }}}\bar{Z}\) direction, the 21.2 eV data was measured with unpolarized beam, thus there are no strong polarization effects.
Saddle points and TSSs around the \(\bar{Z}\) point
Out of the two surface Dirac points present, the Dirac point around the \(\bar{Z}\) point is by far the more interesting. Instead of a typical Dirac like dispersion^{36}, it shows a strong warping effect along the energy axis making saddle points in the lower band. k ⋅ p model band dispersion in Fig. 3a illustrates the Dirac point and two saddle points that exist in proximity of the \(\bar{Z}\) point. The FS in this area of BZ is plotted in Fig. 3b. Fig. 3cf displays calculated DFT band dispersion in the vertical direction(#13) and one horizontal cut(#4) which are marked as dashed lines in Fig. 3b. Interestingly, the vertical cuts (along k_{z}), Fig. 3c and e shows the lower band with negative curvature around k_{z} ~ 0.45 Å^{−1} while the horizontal cut (along k_{y}), Fig. 3f, shows the lower band with positive curvature. Along cut 4, there are actually two upper bands that give rise to two local minimums in energy as marked by black arrows. Those two minimums give rise to two saddle points as demonstrated in Fig. 3a. In cut 1 we can see the upper and lower bands are separated in energy (Fig. 3c). Band dispersion along the \(\bar{Z}\)\(\bar{{{\Gamma }}}\) line is shown in Fig. 3d. Dirac dispersion is clearly visible with Dirac point at the binding energy of ~80 meV and is marked by the black arrow. Figure 3e displays the band dispersion at the cut 3, where the two bands are clearly separated as in cut 1. The separation in Fig. 3c and e is fairly symmetric with respect to the Dirac point. Corresponding ARPES data, measured along the same cuts in the BZ are shown in Fig. 3gj. Based on calculations and the experimental result, we conclude that this is the surface state forms a Dirac point rather than a line of Dirac dispersion along the k_{y} direction. On the other hand, band dispersion in the horizontal direction significantly deviates from the vertical directions as shown in Fig. 3f and j. Both upper and lower bands have a parabolic dispersion instead of the linear dispersion. Naturally, the lower band shows positive curvature. As a result, it looks like the overlap of two parabolic bands with slightly different curvatures.
To qualitatively address the observed saddle points in vicinity of the \(\overline{Z}\) point on the (100) surface we consider a simple effective model. As we have timereversal (\({\mathcal{T}}\)) and inversion symmetry (\({\mathcal{P}}\)) in the bulk, \({\mathcal{A}}={\mathcal{PT}}\) commutes with Hamiltonian, reflecting the Kramers degeneracy by virtue of squaring to −1. The presence of this symmetry will constrain the form of the bulk Hamiltonian affecting the effective model for the surface after projecting. This will be reported elsewhere and we simply note that \({\mathcal{P}}\) is formally broken on the surface. In fact, having the inversion center at the origin ensures that surface states with opposite \({\mathcal{P}}\)value reside on opposite surfaces. Hence, as motivated in Supplementary Note 2, we consider a simple twoband model that is only constrained by TRS to describe the strongly anisotropic anomalous edge states,
In the above d_{0}(k) is even in k and d_{1,2,3}(k) are odd in k. Expanding our energy to second order then gives
where E_{0} is the energy at the crossing points of the surface bands, {A_{i}}, {B_{i}} and {C_{i}} are all real parameters and momenta are measured relative to the \(\overline{Z}\) point. To accommodate strain effects, we could also expand H(k) to third order, giving:
We use simulated annealing to fit this model to our surface band structure around the \(\overline{Z}\) point. This gives the parameters shown in table I and II in Supplementary Note 2. Our parameter space is very high dimensional, so we cannot hope to find the physically relevant parameters. This will be rectified in a future work. As we here are interested only in an effective model to compute the DOS, and as we have the full DFT results available, any model which reproduces the energy dispersion close to the crossing point is sufficient.
van Hove singularity and divergence in the surface state DOS
Extrema of the energy dispersion, ∇ ε_{k} = 0, are called van Hove points and lead to singularities in the density of states (DOS): \(g(E)={g}_{s}\int \frac{{d}^{d1}k}{{(2\pi )}^{d}}\frac{1}{ \nabla {\varepsilon }_{{\bf{k}}}{ }_{{\varepsilon }_{{\bf{k}}} = E}}\) (g_{s} denotes spin degeneracy). In two dimensions, d = 2, saddle points of the dispersion lead to a logarithmically divergent DOS. If this divergence occurs close to the Fermi energy, electronic correlations are strongly amplified, which can drive the system toward various electronically ordered states such as superconductivity, spin or charge density waves. In contrast, nodal points of the dispersion, where the Fermi surface shrinks to a point are characterized by a vanishing DOS.
As described above, our ARPES measurements indicate the presence of both van Hove and nodal points in the surface bands of RhBi_{2} that occur in close proximity to each other. To further underpin this observation, we here study in detail the properties of a lowenergy k ⋅ p model (see Eq. ((2))) that describes the band structure around the \(\bar{\,\text{Z}\,}\) point in the surface BZ (sBZ). As shown in Fig. 3a, the surface band structure exhibits a nodal point at the \(\bar{\,\text{Z}\,}\) point, \(({k}_{\bar{\text{Z}},y},{k}_{\bar{\text{Z}},z})=(0,0.5)\frac{\pi }{a}\). At this point the singly degenerate lower and upper bands touch at an energy E = −82 meV below the Fermi energy E_{F} = 0. Both bands are anisotropic away from the nodal point due to the low symmetry of the material. This is particularly noticeable in the lower band, where the dispersion along the direction \({k}_{y}{k}_{\bar{\text{Z}},y}=4.15({k}_{z}{k}_{\bar{\text{Z}},z})\) is almost flat and quadratic, while it is much steeper in the orthogonal direction (see Fig. S4 in the SI). Importantly, the lower band features two saddle points near \(\bar{\,\text{Z}\,}\) at \(({k}_{y},{k}_{z})\approx (0.042,0.510)\frac{\pi }{a}\) and \((0.042,0.490)\frac{\pi }{a}\). The saddle points reside at energy E = −85 meV, which is only 3 meV below the energy of the nodal point. As shown in Fig. 4a, this gives rise to an intriguing density of states with a logarithmic divergence in close proximity to a zero. Finally, below the logarithmic singularity (E < −85 meV), the DOS is large and almost constant, corresponding to an effective mass of about m^{*} ≈ 0.4m_{e}. This is an average of the almostflat character of the lower band along \({k}_{y}{k}_{\bar{\text{Z}},y}=4.15({k}_{z}{k}_{\bar{\text{Z}},z})\) and the much steeper dispersion in the orthogonal direction.
To explore one of the possible consequences of the logarithmic divergence in the surface DOS, we calculate the enhancement of a hypothetical superconducting transition temperature T_{c} close to the van Hove point. This provides an explicit and quantitative prediction on the expected boost of correlation effects in RhBi_{2} arising from the surface saddle points, stimulating further experimental efforts to tune the Fermi energy close to the saddle points. Such tuning can be accomplished by chemical substitution (e.g., Rh with Ru) or electrostatic gating. For concreteness, we consider a fully gapped swave superconducting state stabilized on the surface of RhBi_{2}. We calculate the ratio T_{c}/T_{c,0} as the system is tuned across the van Hove singularity, where T_{c,0} refers to the transition temperature away from the van Hove point. A discussion of the microscopic origin of superconductivity and possible other pairing channels is left for future work. Note that similar enhancements are expected in other interaction channels such as for density wave states. At weak coupling, T_{c} can be calculated from the standard BCS expression
where g is a momentumindependent superconducting coupling and Λ corresponds to the Debye frequency in case of phononmediated superconductivity. At the saddle points the DOS diverges as \(\rho (\xi )={\rho }_{0}\mathrm{log}\,(D/\left\xi \right)\), with ρ_{0} ≈ 3.2 × 10^{−3} Å^{−2}eV^{−1} and D ≈ 16.5 meV [see Fig. 4(a)]. This implies a large number of states close to \(\bar{\,\text{Z}\,}\) that can pair with their timereversed partners around \(\bar{\,\text{Z}\,}\) favoring a superconducting instability with enhanced transition temperature^{37} (see also Supplementary Note 4)
Here, the quantity λ = gρ_{0}/2 < 1 denotes a dimensionless superconducting coupling. Compared to the standard BCS transition temperature T_{c,0} ≈ 1.13Λe^{−1/λ} for a constant DOS, T_{c} is largely enhanced as follows from the modified dependence on the λ < 1 through \({e}^{1/\sqrt{\lambda }}\) instead of e^{−1/λ}. As shown in Fig. 4(b), this results in dramatic T_{c} enhancement over several orders of magnitude. Note that a second factor that contributes to T_{c} enhancement is the replacement of prefactor Λ by the inverse width of the logarithmic divergence D, where typically D > Λ^{38}.
Our results identify RhBi_{2} as a very promising topological material that has a Dirac surface state with two saddle points close to E_{F}. DFT calculations and symmetry analysis show that triclinic RhBi_{2} is a weak topological insulator having the simplest space group as reflected in its topological characterization. Based on the effective model, we show that the saddle point is related to a VHS. The proximity of the VHS to the Fermi level also provides opportunities to explore quantum many body instabilities to its inherent susceptibility to such instabilities. Our effective model and DFT calculations present guidance for understanding the saddle points and VHS around the Fermi level. Nevertheless the spike of DOS around 80 meV from k ⋅ p model, Experimental observation of DOS needs to be scrutinized in future studies by using different techniques such as Scanning Tunneling Microscope (STM) for several reasons. First, the photon energy and polarization of photon source may influence intensity of ARPES data. Second, the collected data always include signals from both surface and bulk states.
Apart from the discussed implications, RhBi_{2} also hosts potential for other future pursuits. For example, the material could host intriguing new physical phenomena and new topological phase transitions when stress or strain are applied. On a related note, being a WTI in simplest form, RhBi_{2} could also spark interest in making it a material platform to examine the role of defects. Indeed, growing a dislocation in different directions will ensure the binding of topologically protected modes when the weak index vector is parallel to the defect’s Burger vector^{39,40,41,42}. This pursuit is further underpinned by the unusual nature of the stacking vector (001;0) that is perpendicular to layering of the material and thus poses new relative orientations between the two, directly affecting the possibility of growing defects.
Methods
Sample growth. RhBi_{2} crystals were grown using the high temperature solution growth method out of excess Bi^{43}. An initial concentration, Rh_{20}Bi_{80}, of elemental Rh and Bi was placed into a fritted alumina crucible^{44} and sealed in fused silica ampoule under a partial pressure of argon. The ampoule was then heated up to 900 ^{∘}C over 4 h, held there for 3 h and cooled down to 480 ^{∘}C over 200 h. At this temperature the excess solution was separated from the RhBi_{2} crystals using a centrifuge^{43}.The crystal structure is confirmed by Xray diffraction (XRD) measurement.
ARPES experiments. Helium discharge lamp ARPES consists of a helium discharge lamp and a Scienta R8000 analyzer. The Helium discharge lamp ARPES data were collected wtih 21.2 eV photon energy. The laser ARPES system consists of a Scienta DA30 electron analyzer, picosecond Ti:Sapphire oscillator and fourthharmonic generator^{45}. Data from the laser based ARPES were collected with 6.7 eV photon energy. Angular resolution was set at ~0.1^{∘} and 1^{∘}, along and perpendicular to the direction of the analyser slit respectively, and the energy resolution was set at 2 meV. The size of the photon beam on the sample was ~30 μm in the laser system and ~0.5 mm in the helium lamp system. Samples were cleaved insitu at a base pressure lower than 1 × 10^{−10} Torr, 40 K and kept at the cleaving temperature throughout the measurement.
Ab initio Calculations. Band structure with spinorbit coupling (SOC) in density functional theory^{29,30} (DFT) have been calculated with PBE^{46} exchangecorrelation functional, a planewave basis set and projected augmented wave method^{47} as implemented in VAS^{48,49}. The experimental lattice parameters in the triclinic unit cell are used. A MonkhorstPack^{50} (7 × 7 × 7) kpoint mesh with a Gaussian smearing of 0.05 eV including the Γ point and a kinetic energy cutoff of 229 eV have been used. To calculate topological properties, a tightbinding model based on maximally localized Wannier functions^{51,52,53} was constructed to reproduce closely the bulk band structure including SOC in the range of E_{F} ± 1eV with Rh sd and Bi p orbitals. Then the spectral functions and Fermi surface of a semiinfinite RhBi_{2} (100) surface were calculated with the surface Green’s function methods^{54,55,56,57} as implemented in WannierTools^{58}.
Data availability
Raw data for this paper are available at Iowa State University data repository^{59}: https://doi.org/10.25380/iastate.13713589. https://doi.org/10.25380/iastate.13713589.
References
Hasan, M. Z. & Kane, C. L. Colloquium: topological insulators. Rev. Mod. Phys 82, 3045 (2010).
Qi, XiaoLiang & Zhang, ShouCheng Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).
Lv, B., Qian, T. & Ding, H. Angleresolved photoemission spectroscopy and its application to topological materials. Nat. Rev. Phys. 1, 609–626 (2019).
Rasche, B. et al. Stacked topological insulator built from bismuthbased graphene sheet analogues. Nat. Mater. 12, 422–425 (2013).
Pauly, C. et al. Subnanometrewide electron channels protected by topology. Nat. Phys. 11, 338–343 (2015).
Noguchi, R. et al. A weak topological insulator state in quasionedimensional bismuth iodide. Nature 566, 518–522 (2019).
Fu, L., Kane, C. L. & Mele, E. J. Topological insulators in three dimensions. Phys. Rev. Lett. 98, 106803 (2007).
Slager, RobertJan, Mesaros, A., Juričić, V. & Zaanen, J. The space group classification of topological bandinsulators. Nat. Phys. 9, 98–102 (2013).
Song, Z., Zhang, T., Fang, Z. & Fang, C. Quantitative mappings between symmetry and topology in solids. Nat. Comm. 9, 3530 (2018).
Kruthoff, J., de Boer, J., van Wezel, J., Kane, C. L. & Slager, R.J. Topological classification of crystalline insulators through band structure combinatorics. Phys. Rev. X 7, 041069 (2017).
Bradlyn, B. et al. Topological quantum chemistry. Nature 547, 298–305 (2017).
Po, H. C., Vishwanath, A. & Watanabe, H. Symmetrybased indicators of band topology in the 230 space groups. Nat. Commun. 8, 50 (2017).
Li, G. et al. Observation of van hove singularities in twisted graphene layers. Nat. Phys. 6, 109–113 (2010).
McChesney, J. L. et al. Extended van hove singularity and superconducting instability in doped graphene. Phys. Rev. Lett. 104, 136803 (2010).
Tsuei, C. C., Newns, D. M., Chi, C. C. & Pattnaik, P. C. Anomalous isotope effect and van hove singularity in superconducting cu oxides. Phys. Rev. Lett. 65, 2724 (1990).
Gofron, K. et al. Occurrence of van Hove singularities in YBa_{2}Cu_{4}O_{8} and YBa_{2}Cu_{3}O_{6.9}. J. Phys. Chem. Solids 54, 1193–1198 (1993).
Ma, J. et al. Observation of a van Hove singularity in Bi_{2}Sr_{2}CaCu_{2}O_{8+x} with angleresolved photoemission. Phys. Rev. B 51, 3832 (1995).
Ghosh, B. et al. Saddlepoint Van Hove singularity and dual topological state in Pt_{2}HgSe_{3}. Phys. Rev. B 100, 235101 (2019).
Neupane, M. et al. Topological phase diagram and saddle point singularity in a tunable topological crystalline insulator. Phys. Rev. B 92, 075131 (2015).
Hirsch, J. E. & Scalapino, D. J. Enhanced superconductivity in quasi twodimensional systems. Phys. Rev. Lett. 56, 2732 (1986a).
Kohn, W. & Luttinger, J. M. New mechanism for superconductivity. Phys. Rev. Lett. 15, 524 (1965).
Honerkamp, C. & Salmhofer, M. Magnetic and superconducting instabilities of the hubbard model at the van hove filling. Phys. Rev. Lett. 87, 187004 (2001).
González, J., Guinea, F. & Vozmediano, M. A. H. Kinematics of electrons near a van hove singularity. Phys. Rev. Lett. 84, 4930 (2000).
Ziletti, A., Huang, S. M., Coker, D. F. & Lin, H. Van hove singularity and ferromagnetic instability in phosphorene. Phys. Rev. B 92, 085423 (2015).
Fleck, M., Oleś, A. M. & Hedin, L. Magnetic phases near the van hove singularity in sand dband hubbard models. Phys. Rev. B 56, 3159 (1997).
Hlubina, R., Sorella, S. & Guinea, F. Ferromagnetism in the two dimensional tt’ hubbard model at the van hove density. Phys. Rev. Lett. 78, 1343 (1997).
Lederer, P., Montambaux, G. & Poilblanc, D. Antiferromagnetism and superconductivity in a quasi twodimensional electron gas. scaling theory of a generic hubbard model. Journal de Physique 48, 1613–1618 (1987).
Liu, J. & Balents, L. Correlation effects and quantum oscillations in topological nodalloop semimetals. Phys. Rev. B 95, 075426 (2017).
Hohenberg, P. & Kohn, W. Inhomogeneous electron gas. Phys. Rev. B 136, B864 (1964).
Kohn, W. & Sham, L. J. Selfconsistent equations including exchange and correlation effects. Phys. Rev. B 140, A1133 (1965).
Khalaf, E., Po, H. C., Vishwanath, A. & Watanabe, H. Symmetry indicators and anomalous surface states of topological crystalline insulators. Phys. Rev. X 8, 031070 (2018).
Yu, R., Qi, XiaoLiang, Bernevig, A., Fang, Z. & Dai, X. Equivalent expression of \({{\mathbb{z}}}_{2}\) topological invariant for band insulators using the nonabelian berry connection. Phys. Rev. B 84, 075119 (2011).
Alexandradinata, A., Dai, X. & Bernevig, B. A. Wilsonloop characterization of inversionsymmetric topological insulators. Phys. Rev. B 89, 155114 (2014).
Bouhon, A., BlackSchaffer, A. M. & Slager, R.J. Wilson loop approach to fragile topology of split elementary band representations and topological crystalline insulators with timereversal symmetry. Phys. Rev. B 100, 195135 (2019).
Slager, R.J., Rademaker, L., Zaanen, J. & Balents, L. Impuritybound states and green’s function zeros as local signatures of topology. Phys. Rev. B 92, 085126 (2015).
Xia, Y. et al. Observation of a largegap topologicalinsulator class with a single dirac cone on the surface. Nat. Phys. 5, 398–402 (2009).
Hirsch, J. E. & Scalapino, D. J. Enhanced superconductivity in quasi twodimensional systems. Phys. Rev. Lett. 56, 2732 (1986b).
Labbe, J. & Bok, J. Superconductivity in alcalineearthsubstituted La_{2}CuO_{4}: a theoretical model. EPL (Europhys. Lett.) 3, 1225 (1987).
Ran, Y., Zhang, Y. & Vishwanath, A. Onedimensional topologically protected modes in topological insulators with lattice dislocations. Nat. Phys. 5, 298–303 (2009).
Slager, RobertJan The translational side of topological band insulators. J. Phys. Chem. Solids 128, 24–38 (2019).
Slager, RobertJan, Mesaros, A., Juričić, V. & Zaanen, J. Interplay between electronic topology and crystal symmetry: dislocationline modes in topological band insulators. Phys. Rev. B 90, 241403 (2014).
Teo, JeffreyC. Y. & Kane, C. L. Topological defects and gapless modes in insulators and superconductors. Phys. Rev. B 82, 115120 (2010).
Canfield, P. C. New materials physics. Rep. Progr. Phys. 83, 016501 (2019).
Canfield, P. C., Kong, T., Kaluarachchi, U. S. & Jo, Na. Hyun Use of fritdisc crucibles for routine and exploratory solution growth of single crystalline samples. Philos. Mag. 96, 84–92 (2016).
Jiang, R. et al. Tunable vacuum ultraviolet laser based spectrometer for angle resolved photoemission spectroscopy. Rev. Sci. Instrum. 85, 033902 (2014).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Blöchl, P. E. Projector augmentedwave method. Phys. Rev. B 50, 17953 (1994).
Kresse, G. & Furthmüller, J. ürgen Efficient iterative schemes for ab initio totalenergy calculations using a planewave basis set. Phys. Rev. B 54, 11169 (1996a).
Kresse, G. & Furthmüller, J. ürgen Efficiency of abinitio total energy calculations for metals and semiconductors using a planewave basis set. Comput. Mater. Sci. 6, 15–50 (1996b).
Monkhorst, H. J. & Pack, J. D. Special points for brillouinzone integrations. Phys. Rev. B 13, 5188 (1976).
Marzari, N. & Vanderbilt, D. Maximally localized generalized wannier functions for composite energy bands. Phys. Rev. B 56, 12847 (1997).
Souza, I., Marzari, N. & Vanderbilt, D. Maximally localized wannier functions for entangled energy bands. Phys. Rev. B 65, 035109 (2001).
Marzari, N., Mostofi, A. A., Yates, J. R., Souza, I. & Vanderbilt, D. Maximally localized wannier functions: theory and applications. Rev. Mod. Phys. 84, 1419 (2012).
Lee, D. H. & Joannopoulos, J. D. Simple scheme for surfaceband calculations. i. Phys. Rev. B 23, 4988 (1981a).
Lee, D. H. & Joannopoulos, J. D. Simple scheme for surfaceband calculations. ii. the green’s function. Phys. Rev. B 23, 4997 (1981b).
Sancho, M. P. Lopez, Sancho, J. M. Lopez & Rubio, J. Quick iterative scheme for the calculation of transfer matrices: application to mo (100). J. Phys. F: Metal Phys. 14, 1205 (1984).
Sancho, M. P. Lopez, Sancho, J. M. Lopez, Sancho, J. M. Lopez & Rubio, J. Highly convergent schemes for the calculation of bulk and surface green functions. J. Phys. F: Metal Phys. 15, 851 (1985).
Wu, QuanSheng, Zhang, ShengNan, Song, HaiFeng, Troyer, M. & Soluyanov, A. A. Wanniertools: an opensource software package for novel topological materials. Comput. Phys. Commun. 224, 405–416 (2018).
Lee, Kyungchan, et al. “Discovery of a weak topological insulating state and van hove singularity in triclinic RhBi_{2}”, Iowa State University data repository: https://doi.org/10.25380/iastate.13713589.
Acknowledgements
We are grateful to Thomas Iadecola for useful discussions and Sergey L. Bud’ko for help with transport measurements. This work was supported by the U.S. Department of Energy, Office of Basic Energy Sciences, Division of Materials Sciences and Engineering. R.J.S. acknowledges funding from Trinity college, the Marie Curie programme under EC Grant agreement No. 842901 and the Winton programme at the University of Cambridge. G.F.L. acknowledges funding from the Aker Scholarship. The research (K.L., L.L.W., B.K., T.V.T., N.H.J., P.P.O., P.C.C., and A.K.) was performed at Ames Laboratory. Ames Laboratory is operated for the U.S. Department of Energy by the Iowa State University under Contract No. DEAC0207CH11358. This work was also supported by the Center for Advancement of Topological Semimetals (B.K., T.V.T., N.H.J., P.P.O.), an Energy Frontier Research Center funded by the U.S. Department of Energy Office of Science, Office of Basic Energy Sciences, through the Ames Laboratory under its Contract No. DEAC0207CH11358.
Author information
Authors and Affiliations
Contributions
G.F.L, T.V.T., P.P.O, and R.J.S provided theoretical modeling and interpretation. B.K. and P.C.C. designed, grew and characterized the samples. L.L.W. performed DFT calculations. K.L., N.H.J., B.S., and A.K. performed ARPES measurements and support. The manuscript was drafted by K.L., G.F.L., L.L.W., B.K., T.V.T., N.H.J., P.P.O., R.J.S., P.C.C., and A.K. All authors discussed and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Lee, K., Lange, G.F., Wang, LL. et al. Discovery of a weak topological insulating state and van Hove singularity in triclinic RhBi_{2}. Nat Commun 12, 1855 (2021). https://doi.org/10.1038/s4146702122136w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s4146702122136w
This article is cited by

Critical topology and pressureinduced superconductivity in the van der Waals compound AuTe2Br
npj Quantum Materials (2022)

Angleresolved photoemission spectroscopy
Nature Reviews Methods Primers (2022)

Unsupervised clustering for identifying spatial inhomogeneity on local electronic structures
npj Quantum Materials (2022)

Observation and control of the weak topological insulator state in ZrTe5
Nature Communications (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.