Abstract
Chiral optical materials based on circularly polarized luminescence (CPL) have emerged rapidly due to their feasible applications in diverse fields of research. However, limited to the small luminescence dissymmetry factor (glum), real application examples have rarely been reported. Here, we present a complex system, which show intense circularly polarized ultraviolet luminescence (CPUVL) with large glum value, enabling a chiral UV light triggered enantioselective polymerization. By integrating sensitized triplet-triplet annihilation upconversion and CPL, both visible-to-UV upconversion emission and upconverted circularly polarized ultraviolet luminescence (UC-CPUVL) were obtained in the systems, built of chiral annihilator R(S)-4,12-biphenyl[2,2]paracyclophane (R-/S-TP), and a thermally activated delayed fluorescence (TADF) sensitizer. After dispersing this upconversion system into room-temperature nematic liquid crystal, induced chiral nematic liquid crystal could significantly amplify the glum value (0.19) of UC-CPUVL. Further, the UC-CPUVL emission has been used to trigger the enantioselective photopolymerization of diacetylene. This work paves the way for the further development of functional application of CPL active materials.
Similar content being viewed by others
Introduction
Circularly polarized luminescence (CPL) has gained considerable interest1,2,3,4,5,6,7,8,9,10,11,12 in recent years thanks to their widely potential applications in optical displays1,13,14,15, disease detection16 and even as catalysts for asymmetric photochemical synthesis17,18,19. However, real applications have rarely been reported due to the small luminescence dissymmetry factor (glum). In terms of circularly polarized luminescent materials, the luminescence dissymmetry factor is defined as glum = 2 × (IL − IR)/(IL + IR), where IL and IR signifies respectively the left- and right-handed CPL intensity, are applied to quantify the level of CPL performance. Therefore, the glum can vary from −2 to +2, which corresponds to a total emission of right- and left-handed circularly polarized light20. Searching large glum value of CPL-active materials is a critical issue for real application in this field. Nevertheless, in organic systems, particularly chiral small organic molecules, the glum value was not satisfying for practical application despite their good performance in other aspects. In this sense, over the past few years, various strategies for amplifying glum value have been developed, including supramolecular self-assembly21,22,23,24, aggregation-induced emission11,25,26,27,28, energy transfer involved circularly polarized excitation29,30,31,32, incorporating into chiral liquid crystals33,34,35, and so forth. Nevertheless, the reported CPL-active systems with high glum value were almost located in the visible light region, whose relatively low energy limited their practical applications. Accordingly, the development of circularly polarized ultraviolet luminescence (CPUVL) with high glum value and further expanding its application remain a big challenge.
Recently, we have reported one kind of upconverted CPL (UC-CPL), which was constructed by integrating triplet–triplet annihilation upconversion (TTA-UC) and CPL36. The triplet–triplet energy transfer involved TTA-UC process could significantly amplify the circular polarization of the UC-CPL. Considering that TTA-UC can easily realize upconverted UV emission by flexible selecting appropriate sensitizer/annihilator combination, and the remarkable glum value amplification effect of UC-CPL process, a well-designed sensitizer/annihilator pair of TTA-UC, which possess excellent performance in the upconverted CPUVL (UC-CPUVL), is required.
Photon upconversion affords the possibility to convert low energy photons into high energy photons. The TTA-UC has an expansion to a wider range of scientific fields in terms of applications, such as photovoltaics37,38,39, biomolecular systems40, and photocatalysis41,42 primarily due to its high efficiency, low-power excitation37,38,39,40,41,42,43,44,45,46,47. Undoubtedly, visible-to-UV upconversion is particularly important because many applications of upconversion deal with the presence of high energy. However, few examples of visible-to-UV TTA-UC can be found in the literatures and their upconversion efficiency is unsatisfactory because of the unsuitable energy levels between sensitizers and annihilators45,48,49,50,51. More importantly, the UC-CPUVL with high glum value, to the best of our knowledge, remains unexploited.
Although the amplification of CPL emission through TTA-UC has been demonstrated to be an efficient approach, the amplified glum values are still very small in a range from 10−4 to 10−3, which is pretty far from the requirement of real application. On the other hand, chiral nematic liquid crystal (N*LC) has been regarded as one kind of smart materials to realize CPL and UC-CPL with larger glum value, attributing to its unique optical properties, such as optical rotation and circular dichroism (CD)35,52,53,54,55. Thus, by incorporating the CPL-active TTA-UC pairs into N*LC, the glum value of UC-CPL should be remarkably boosted.
Here, we report an example of visible-to-UV UC-CPUVL, which is composed of chiral annihilator R(S)-4,12-biphenyl[2,2]paracyclophane (R-/S-TP) and achiral sensitizer thermally activated delayed fluorescence (TADF) molecule 4CzIPN56. It should be noted that, thanks to the excellent performance of TADF molecule in small S1–T1 gap (ΔEST) and less energy loss during the intersystem crossing process57, the combination shows a reasonably high photon upconversion efficiency (ΦUC = 7.9%). Due to the essential planar chirality, the annihilator R-/S-TP shows good CPL performance in dilute solution (|glum| = 3.1 × 10−3, Fig. 1). TTA-UC process can further amplify the circular polarization of UC-CPUVL to a larger value (|glum| = 9.2 × 10−3). In addition, after embedding this upconversion pairs into a room-temperature nematic liquid crystal, induced N*LC and high performance UC-CPUVL can be easily obtained. It’s worth mentioning that the glum value reaches to 0.19, which is almost three times larger than the prompt CPL in N*LC (7.5 × 10−2). This larger glum value of upconverted UV light motivates us to put it into practical application. Here, taking a step forward, the UC-CPUVL emission generated from N*LC, has been successfully used to trigger the enantioselective polymerization of diacetylen with great stereoselectivity.
Results
Prompt CPUVL behavior in solution
It is acknowledged that the combination of chiral group with organic emitter was one of the most direct and efficient routes to construct CPL-active materials. Thus, following this strategy, the employed chiral annihilator R(S)-TP, was synthesized directly R(S)-4,12-dibromo[2,2]paracyclophane and 1,4-biphenylboronic acid by Suzuki coupling reactions (Supplementary Methods and Supplementary Fig. 1). Subsequently, R-TP was chosen as an example for exploring the photophysical properties, and its absorption and emission spectra were shown in Fig. 2a, with a concentration of 0.01 mM in THF solution. It could be clearly observed that R-TP showed a characteristic vibrational structure of p-terphenyl. The absorption spectrum showed intense absorption band at 255 and 290 nm, and its maximum emission located at 380 nm under the excitation of 290 nm. Notably, compared with the p-terphenyl, both absorption and emission spectra of R-TP showed obvious red shift due to the increased π-conjugation length.
Subsequently, we explored the chiroptical properties of R(S)-TP through testing the CD and CPL spectra. As shown in Fig. 2b, R-TP and S-TP showed a mirror-image CD signals. R-TP possessed a positive Cotton effect at 330 nm and a negative Cotton effect at 271 nm. In addition, both enantiomers showed clear CPUVL emission at 380 nm, and its corresponding glum value was about 3.1 × 10−3. It should be noted that positive signal represented the R-TP exhibited left-handed CPL emission while negative signal corresponding to the opposite one, which demonstrated the achiral π-conjugated chromophores were endowed chiral emission after tethering the planar chirality58.
TTA-UC and UC-CPUVL behavior in solution
To our knowledge, visible-to-UV TTA-UC, where p-terphenyl and 4CzIPN were utilized as annihilator and sensitizer, respectively, has been explored. However, in this work, better TTA-UC efficiency was obtained by replacing the p-terphenyl with chiral annihilator R(S)-TP. The solubility of R(S)-TP in toluene is better than in THF solution, which was beneficial to the TTET process in TTA-UC. Thus, we have thoroughly investigated the TTA-UC behavior in toluene solution (the experimental setup is presented in Supplementary Fig. 3). The photophysical properties of annihilators, as well as the TADF sensitizer in toluene solution have been examined (Supplementary Fig. 2). We have carefully tested the solubility of the annihilators in toluene, and the concentration of 3 mM was found to be the maximum concentration. To get high efficient TTA-UC, a larger concentration of annihilator is required. We then thoroughly tested the TTA-UC behavior by fixing the R-TP concentration at 3 mM, blending with various amount of sensitizer 4CzIPN. It has been confirmed that, when the mixing molar ratio of R-TP/4CzIPN at 3 mM/0.1 mM, we could observe the best TTA-UC emission in toluene solution. As shown in Fig. 3a, after fixing the concentration of R-TP and 4CzIPN in toluene solution at 3 and 0.1 mM, respectively, upconverted UV emission spectra with different incident power densities were obtained with the excitation of 445 nm continuous wave laser. The location of the upconversion emission is similar to the normal fluorescence (λex = 290 nm). In order to deeply understand the TTA-UC mechanism, the algebraic relationship between the upconversion emission intensity and the excitation power density was measured. Figure 3b presented the double-logarithmic plots of the upconverted UV emission intensity as a function of incident light power density. The blue and red lines (slopes = 2.0 and 1.0, respectively) showed the perfect fitting results in the range of low and high excitation intensity, which was the vitally important experimental evidence for typical TTA-UC system59. In addition, the threshold excitation intensity (Ith) was 75 mW cm−2, where TTA became the main deactivation channel for the annihilator triplet and the upconversion quantum yield reached saturation. Figure 3c showed the dependence of the TTA-UC quantum efficiency ΦUC on the excitation power intensity for the mixed solution of R-TP/4CzIPN, a saturation quantum yield of about 7.9% was obtained by using Coumarin 6 in DMF as a standard when the maximum efficiency is standardized to be 100% (Supplementary Methods)60. This value is relatively large compared with previous reports45,48,50. The TTA-UC mechanism could also be confirmed by the lifetime measurement. As shown in Fig. 3d, the upconverted UV emission lifetime at 385 nm was 84 μs, which could be ascribed to the mechanism based on long-lived triplet species. In addition, after comparing the lifetime of 4CzIPN in the TTA-UC process with its normal luminescence lifetime in solution, the emission decays of 4CzIPN decrease dramatically from 149 to 34 μs when the addition of annihilators (Supplementary Fig. 4), indicating a sensitizer-to-annihilator fast and efficient TTET process. The corresponding TTA-UC measurements of S-TP/4CzIPN pair were collected in Supplementary Fig. 5. Accordingly, in the excitation of 445 nm CW laser, CPUVL based on the TTA-UC process, named UC-CPUVL, was successfully realized, whose emission was consistent with the prompt CPUVL of R(S)-TP (Fig. 3e). The corresponding glum value of UC-CPUVL presented three times larger than the prompt CPUVL, from 3.1 × 10−3 to 9.2 × 10−3, which could be attributed to the chirality-induced spin polarization of singlet excitons resulting from the TTA-UC process (Fig. 3f)61.
CPUVL and UC-CPUVL behavior in N*LC
Currently, doping the chiral emitters into the achiral nematic liquid crystal was considered as a preferred method to realize CPL-active N*LC. In this work, we showed the example of enhanced UC-CPUVL emission in N*LC, which could be easily achieved by blending a chiral TTA-UC pair with an achiral room-temperature nematic liquid crystal (5CB). Firstly, before exploring the upconverted emission properties in the N*LC, we separately tested the luminescence spectra of annihilator R-TP and sensitizer 4CzIPN in 5CB. As shown in Supplementary Fig. 6, compared to the monodisperse state, both the emission of R-TP and 4CzIPN in 5CB showed a 20 nm red shift. Normally, in a certain range, increasing the weight ratio of chiral molecule is favorable to the induction of chiral nematic liquid crystal. However, the properties of host liquid crystal (room-temperature nematic liquid crystal 5CB is used in this work) will perform significant changes, such as viscosity increase or clear point decrease, after adding an excess of chiral dopants. Thus, it is essential to thoroughly explore the CPL activity of various mixing weight ratios of chiral dopant. As shown in Fig. 4a, the highest glum value is obtained when the mixing weight ratio of R-TP/5CB was 10 wt%, indicating that the chiral nematic liquid crystal possessed the most favorable configuration in this case. Since the CPL signal direction can be determined by the handedness of N*LC, it can be clearly clarified that R-TP will induce the 5CB to a right-handed N*LC, while the addition of S-TP to 5CB will result in a left-handed N*LC. Subsequently, we had also checked the polarizing optical microscope images of R-TP in 5CB (Fig. 4c). The typical fingerprint texture proved that the N*LC has been induced perfectly by the chiral annihilator. After embedding with 4CzIPN, the fingerprint texture could still be preserved (Supplementary Fig. 7). Additionally, after fixing the mixing weight ratio of R(S)-TP/5CB at 10 wt%, 4CzIPN could also exhibit the intense CPL emission in the N*LC, whose direction followed the regulation of N*LC (Supplementary Fig. 8). These results explicitly demonstrated that the CPL signal direction of emitters was determined by the handedness of N*LC.
Rather surprisingly, after blending with 4CzIPN, the UC-CPUVL with a larger glum value (|glum| = 1.9 × 10−1) was achieved through the TTA-UC process in the N*LC. Similarly, the upconverted glum exhibited the same tendency compared to the prompt CPUVL in 5CB. After fixing the mixing molar ratio of 4CzIPN/R-TP around 3 mol%, the glum value came up to the highest point when the weight ratio of R-TP/5CB reached 10 wt% (Supplementary Fig. 9). As expected, a mirror-image UC-CPUVL signal could be observed under excitation by the 445 nm CW laser, whose glum value was around 0.2 (Fig. 5a). It was in agreement with the prompt CPUVL in the N*LC. However, in this study, the intensity of TTA-UC emission in N*LC was relatively weak (ΦUC ~2.3%), even the excitation of 445 nm CW laser was in a high incident power density (Supplementary Fig. 10), which should be ascribed to the bad dispersion state of sensitizer/annihilator pair in N*LC. We have thoroughly compared the glum values of all the tested CPL behavior (Fig. 5b). Obviously, in chiral liquid crystal, the glum value of UC-CPUVL was almost three times magnitude of the prompt CPUVL. Impressively, comparing with the values in dilute solution, after incorporating into chiral liquid crystal, glum value of CPUVL was magnified 60 times, while glum value of UC-CPUVL was magnified 20 times.
UC-CPUVL triggered enantioselective photopolymerization
For the development of practical applications of the UC-CPUVL with higher glum value (0.19) generated from the TTA-UC system, enantioselective photopolymerization would be a desirable application direction. Since the chiral UV light possesses high energy, it has been widely used for initiating the enantioselective photopolymerization of diacetylene62,63,64,65. In our previous work, we have reported one typical example about the enantioselective photopolymerization of diacetylene, which could be triggered by applying the upconverted circularly polarized light generated from a co-gel composed of upconversion nanoparticles (UCNPs) and chiral gelator66. However, since the obtained glum value of CPL from the UCNPs-doped co-gel was small (~10−3), the chiral direction of predominant helical polydiacetylene (PDA) chain could not be controlled very well. Thus, whether the TTA-UC process based UC-CPUVL with high glum value could trigger the enantioselective polymerization of diacetylene with great stereoselectivity? In order to advance this idea, we have constructed a simple irradiation platform, as shown in Fig. 6a. We selected 445 nm CW semiconductor laser as light source. According to the above demonstration, by fixing the mixing molar ratio of R-TP/4CzIPN at 30/1, an optimized mixing mass ratio of R-TP/5CB at 10 wt% was used for generating UC-CPUVL emission. Encapsulating the complexes R-TP/4CzIPN/5CB into a quartz cell (0.1 cm optical length) refilled with argon, intense UC-CPUVL was generated under shining with 445 nm CW laser. The quartz plate covered with 2, 4-nonadecanediynoic acid (NA) spin-coating film was placed behind the sample, with a 445 nm short-pass filter placing between them. After exposing to the UC-CPUVL for a few minutes, the NA film turned blue, indicating the formation of PDA. It was pleasant that the obtained PDA film showed a mirror-image Cotton effect in the CD spectra after irradiated by the UC-CPUVL with different handedness (Fig. 6b).The PDA film exhibited negative CD signal after exposing to the UC-CPUVL generated from the S-TP/4CzIPN/5CB complexes, while the positive CD signal could be achieved in the other combination. The reliability of CD spectra acquired from PDA films must be identified by testing the linear dichroism (LD), which excluded the possible effect of LD (Supplementary Fig. 11). It should be emphasized that the CD signals of PDA were in agreement with the molecular chirality of the annihilator R(S)-TP. To examine the reliability of the enantioselectivity, we have repeated the photopolymerization of NA with ten different batches. Statistical analysis of the CD signals at 640 nm showed that the chirality of the obtained PDA always follow the molecular chirality of the annihilator (Fig. 6c). These results indicated that, after exposing to UC-CPUVL, PDA could be effectively fabricated by the enantioselective polymerization. More importantly, the chirality of PDA could be regulated by the handedness of UC-CPUVL and performed good stability and repeatability.
Discussion
It is a very significant attempt to apply the UC-CPUVL to enantioselective photopolymerization reaction. By integrating visible-to-UV TTA-UC, chiral liquid crystal and circularly polarized UV emission, here, we proposed an effective approach for achieving UC-CPUVL with larger circular polarization. Two synthesized chiral UV emitters were used as the TTA-UC annihilators to construct the TTA-UC system, sensitized by a TADF compound 4CzIPN. Both visible-to-UV photon upconversion with a relatively high upconversion quantum efficiency (ΦUC = 7.9%) and UC-CPUVL were realized. When chiral annihilators were embedded into nematic liquid crystal, the induced N*LC has endowed the upconversion system with bright UC-CPUVL activity, enabling a large glum value up to 0.19. More importantly, the UC-CPUVL emission, generated from the TTA-UC process in N*LC, can trigger the enantioselective polymerization of diacetylene and perform good stability and repeatability. This work will not only provide the proof-of-concept for the usage of TTA-UC for challenging chiral polymerization employing UC-CPUVL and paves the way for the further development of functional application of CPL-active materials.
Methods
Materials
All reagents and solvents were used as received otherwise indicated. R(S)-4,12-dibromine[2.2]paracyclophane was purchased from Daicel Chiral Technologies (China) Co., Ltd. and used as received. 1,4-biphenylboronic acid was purchased from TCI and used as received. The R(S)-4,12-biphenyl[2,2]paracyclophane (R-/S-TP) are synthesized according to literature and purified by column chromatography and confirmed the molecular structures by proton nuclear magnetic resonance (1H NMR), matrix-assisted laser desorption–ionization-time of flight–mass spectrometry. The commercial room-temperature nematic liquid crystal, 5CB, was bought from the Chengzhi Yonghua Display Material Co., Ltd. 2,4-Nonadecadiynoic Acid was purchased from TCI and purified by dissolution in toluene and subsequent filtration to remove polymer before use.
Characterization
The 1H NMR spectra were recorded on a Bruker Avance III 400 HD spectrometer. Mass spectral data were obtained by using a SolariX maldi-FTMS instrument. UV–vis spectra were recorded on Hitachi U-3900 spectrophotometer. Fluorescence spectra were measured were obtained using and F-4500 fluorescence spectrophotometer. CD and CPL spectra were measured on JASCO J-1500 and JASCO CPL-200 spectrophotometers, respectively. The fluorescence lifetime measurements were recorded on the Edinburg FLS-980 fluorescence spectrometer using time-correlated single photon counting, phosphorescence decays and upconverted emission decays were recorded on Edinburg FLS-980 using Multi-Channel Scaling. Upconverted emission spectra were recorded on a Zolix Omin-λ500i monochromator with photomultiplier tube PMTH-R 928 using an external excitation source, 445 nm semiconductor laser (Changchun New Industries Optoelectronics Tech Co., Ltd., MDL-III-445-1W), 445 nm short-pass filter (Changchun New Industries Optoelectronics Tech Co., Ltd.). POM images were recorded on a Leica DM2700M upright materials microscope. UC-CPUVL were recorded on JASCO CPL-200 spectrophotometer with an external excitation source of linearly polarized 445 nm semiconductor laser (Changchun New Industries Optoelectronics Tech Co., Ltd., MDL-III-445-1W).
Data availability
Data supporting the findings of this study are available within the paper and its Supplementary Information files. The source data underlying Figs. 2a–c, 3a, d–f, 4a, b, 5b, and 6b are provided as a Source Data file. The data that support the findings of this study are available from the corresponding author on request. Source data are provided with this paper.
References
Zhang, D.-W., Li, M. & Chen, C.-F. Recent advances in circularly polarized electroluminescence based on organic light-emitting diodes. Chem. Soc. Rev. 49, 1331–1343 (2020).
Sang, Y., Han, J., Zhao, T., Duan, P. & Liu, M. Circularly polarized luminescence in nanoassemblies: generation, amplification, and application. Adv. Mater. 32, 1900110 (2020).
Roose, J., Tang, B. Z. & Wong, K. S. Circularly-polarized luminescence (CPL) from chiral AIE molecules and macrostructures. Small 12, 6495–6512 (2016).
Sanchez-Carnerero, E. M. et al. Circularly polarized luminescence from simple organic molecules. Chemistry 21, 13488–13500 (2015).
Carr, R., Evans, N. H. & Parker, D. Lanthanide complexes as chiral probes exploiting circularly polarized luminescence. Chem. Soc. Rev. 41, 7673–7686 (2012).
Song, F. Y. et al. Chiral sensing for induced circularly polarized luminescence using an Eu(III)-containing polymer and D- or L-proline. Chem. Commun. 49, 5772–5774 (2013).
Sugimoto, M. et al. Circularly polarized luminescence from inorganic materials: encapsulating guest lanthanide oxides in chiral silica hosts. Chemistry 24, 6519–6524 (2018).
Xu, M. C. et al. Assembling semiconductor quantum dots in hierarchical photonic cellulose nanocrystal films: circularly polarized luminescent nanomaterials as optical coding labels. J. Mater. Chem. C 7, 13794–13802 (2019).
David, A. H. G., Casares, R., Cuerva, J. M., Campana, A. G. & Blanco, V. A 2 rotaxane-based circularly polarized luminescence switch. J. Am. Chem. Soc. 141, 18064–18074 (2019).
Shen, C. S. et al. Helicene-derived aggregation-induced emission conjugates with highly tunable circularly polarized luminescence. Mater. Chem. Front. 4, 837–844 (2020).
Shi, Y. et al. Aggregation Induced emissive and circularly polarized homogeneous sulfono-gamma-AApeptide foldamers. Adv. Opt. Mater. 8, 1902122 (2020).
Zinna, F. & Di Bari, L. Lanthanide circularly polarized luminescence: bases and applications. Chirality 27, 1–13 (2015).
Li, M. et al. Stable enantiomers displaying thermally activated delayed fluorescence: efficient OLEDs with circularly polarized electroluminescence. Angew. Chem. Int. Ed. 57, 2889–2893 (2018).
Han, J. M. et al. Recent progress on circularly polarized luminescent materials for organic optoelectronic devices. Adv. Opt. Mater. 6, 1800538 (2018).
Yan, Z. P. et al. Configurationally stable platinahelicene enantiomers for efficient circularly polarized phosphorescent organic light-emitting diodes. Chemistry 25, 5672–5676 (2019).
Kunnen, B. et al. Application of circularly polarized light for non-invasive diagnosis of cancerous tissues and turbid tissue-like scattering media. J. Biomed. Opt. 8, 317–323 (2015).
Richardson, R. D. et al. Dual wavelength asymmetric photochemical synthesis with circularly polarized light. Chem. Sci. 6, 3853–3862 (2015).
Kawasaki, T. et al. Enantioselective synthesis of near enantiopure compound by asymmetric autocatalysis triggered by asymmetric photolysis with circularly polarized light. J. Am. Chem. Soc. 127, 3274–3275 (2005).
Yeom, J. et al. Chiral templating of self-assembling nanostructures by circularly polarized light. Nat. Mater. 14, 66–72 (2015).
Richardson, F. S. & Riehl, J. P. Circularly polarized luminescence spectroscopy. Chem. Rev. 77, 773–792 (1977).
Bobrovsky, A., Shibaev, V. & Stumpe, J. Cholesteric polymer guest-host mixture with circularly polarized fluorescence: Two ways for phototuning of polarization and its intensity. J. Phys. Chem. A 110, 2331–2336 (2006).
Li, X. J., Hu, W. R., Wang, Y. X., Quan, Y. W. & Cheng, Y. X. Strong CPL of achiral AIE-active dyes induced by supramolecular self-assembly in chiral nematic liquid crystals (AIE-N*-LCs). Chem. Commun. 55, 5179–5182 (2019).
Yang, D., Duan, P. F., Zhang, L. & Liu, M. H. Chirality and energy transfer amplified circularly polarized luminescence in composite nanohelix. Nat. Commun. 8, 15727 (2017).
Kumar, J., Nakashima, T. & Kawai, T. Circularly polarized luminescence in chiral molecules and supramolecular assemblies. J. Phys. Chem. Lett. 6, 3445–3452 (2015).
Mei, J., Leung, N. L. C., Kwok, R. T. K., Lam, J. W. Y. & Tang, B. Z. Aggregation-induced emission: together we shine, united we soar! Chem. Rev. 115, 11718–11940 (2015).
Xiong, J. B. et al. The fixed propeller-like conformation of tetraphenylethylene that reveals aggregation-induced emission effect, chiral recognition, and enhanced chiroptical property. J. Am. Chem. Soc. 138, 11469–11472 (2016).
Liu, X. H. et al. A tetraphenylethene-based chiral polymer: an AIE luminogen with high and tunable CPL dissymmetry factor. J. Mater. Chem. C 1, 4713–4719 (2013).
Li, H. K. et al. L-Valine methyl ester-containing tetraphenylethene: aggregation-induced emission, aggregation-induced circular dichroism, circularly polarized luminescence, and helical self-assembly. Mater. Horiz. 1, 518–521 (2014).
Han, B. New APproaches to Enhance Circularly Polarized Luminescence: Interfacial Self-assembly of Chiral Emitters and Emissive Charge-transfer Complexes. Acta Phys. Chim. Sin. 35, 1177–1178 (2019).
Zhang, J. et al. Real-time monitoring of hierarchical self-assembly and induction of circularly polarized luminescence from achiral luminogens. ACS Nano 13, 3618–3628 (2019).
Yang, D., Han, J., Liu, M. & Duan, P. Photon upconverted circularly polarized luminescence via triplet-triplet annihilation. Adv. Mater. 31, 1805683 (2019).
Zhang, S. W. et al. Circularly polarized luminescence of AIE-active chiral O-BODIPYs induced via intramolecular energy transfer. Chem. Commun. 51, 9014–9017 (2015).
Yoshida, J., Tamura, S., Yuge, H. & Watanabe, G. Left- and right-circularly polarized light-sensing based on colored and mechano-responsive chiral nematic liquid crystals. Soft Matter 14, 27–30 (2018).
Yan, J. L., Ota, F., San Jose, B. A. & Akagi, K. Chiroptical resolution and thermal switching of chirality in conjugated polymer luminescence via selective reflection using a double-layered cell of chiral nematic liquid crystal. Adv. Funct. Mater. 27, 1604529 (2017).
Jose, B. A. S., Matsushita, S. & Akagi, K. Lyotropic chiral nematic liquid crystalline aliphatic conjugated polymers based on disubstituted polyacetylene derivatives that exhibit high dissymmetry factors in circularly polarized luminescence. J. Am. Chem. Soc. 134, 19795–19807 (2012).
Han, J., Duan, P., Li, X. & Liu, M. Amplification of circularly polarized luminescence through triplet triplet annihilation-based photon upconversion. J. Am. Chem. Soc. 139, 9783–9786 (2017).
Goldschmidt, J. C. & Fischer, S. Upconversion for photovoltaics—a review of materials, devices and concepts for performance enhancement. Adv. Opt. Mater. 3, 510–535 (2015).
Cheng, Y. Y. et al. Improving the light-harvesting of amorphous silicon solar cells with photochemical upconversion. Energy Environ. Sci. 5, 6953–6959 (2012).
Cheng, Y. Y. et al. Kinetic analysis of photochemical upconversion by triplet-triplet annihilation: beyond any spin statistical limit. J. Phys. Chem. Lett. 1, 1795–1799 (2010).
Tian, B., Wang, Q. H., Su, Q. Q., Feng, W. & Li, F. Y. In vivo biodistribution and toxicity assessment of triplet-triplet annihilation-based upconversion nanocapsules. Biomaterials 112, 10–19 (2017).
Kim, J. H. & Kim, J. H. Encapsulated triplet-triplet annihilation-based upconversion in the aqueous phase for sub-band-gap semiconductor photocatalysis. J. Am. Chem. Soc. 134, 17478–17481 (2012).
Ravetz, B. D. et al. Photoredox catalysis using infrared light via triplet fusion upconversion. Nature 565, 343–346 (2019).
Mahammed, A., Chen, K. P., Vestfrid, J., Zhao, J. Z. & Gross, Z. Phosphorus corrole complexes: from property tuning to applications in photocatalysis and triplet-triplet annihilation upconversion. Chem. Sci. 10, 7091–7103 (2019).
Kimizuka, N., Yanai, N. & Morikawat, M.-A. Photon upconversion and molecular solar energy storage by maximizing the potential of molecular self-assembly. Langmuir 32, 12304–12322 (2016).
Chen, Q. et al. Energy transfer dynamics in triplet-triplet annihilation upconversion using a bichromophoric heavy-atom-free sensitizer. J. Phys. Chem. A 122, 6673–6682 (2018).
Fan, C. Y. et al. Efficient triplet-triplet annihilation upconversion with an anti-stokes shift of 1.08 eV achieved by chemically tuning sensitizers. J. Am. Chem. Soc. 141, 15070–15077 (2019).
Peng, J., Guo, X., Jiang, X., Zhao, D. & Ma, Y. Developing efficient heavy-atom-free photosensitizers applicable to TTA upconversion in polymer films. Chem. Sci. 7, 1233–1237 (2016).
Duan, P., Yanai, N. & Kimizuka, N. A bis-cyclometalated iridium complex as a benchmark sensitizer for efficient visible-to-UV photon upconversion. Chem. Commun. 50, 13111–13113 (2014).
Deng, F., Blumhoff, J. & Castellano, F. N. Annihilation limit of a visible-to-UV photon upconversion composition ascertained from transient absorption kinetics. J. Phy. Chem. A 117, 4412–4419 (2013).
Gray, V. et al. Photophysical characterization of the 9,10-disubstituted anthracene chromophore and its applications in triplet-triplet annihilation photon upconversion. J. Mater. Chem. C 3, 11111–11121 (2015).
Singh-Rachford, T. N. & Castellano, F. N. Low power visible-to-UV upconversion. J. Phys. Chem. A 113, 5912–5917 (2009).
Hu, W. et al. Electrically controllable selective reflection of chiral nematic liquid crystal/chiral ionic liquid composites. Adv. Mater. 22, 468–472 (2010).
San Jose, B. A., Yan, J. & Akagi, K. Dynamic switching of the circularly polarized luminescence of disubstituted polyacetylene by selective transmission through a thermotropic chiral nematic liquid crystal. Angew. Chem. Int. Ed. 53, 10641–10644 (2014).
Wang, H. et al. Photochemically and thermally driven full-color reflection in a self-organized helical superstructure enabled by a halogen-bonded chiral molecular switch. Angew. Chem. Int. Ed. 57, 1627–1631 (2018).
Gutierrez-Cuevas, K. G. et al. Frequency-driven self-organized helical superstructures loaded with mesogen-grafted silica nanoparticles. Angew. Chem. Int. Ed. 55, 13090–13094 (2016).
Yanai, N. et al. Increased vis-to-UV upconversion performance by energy level matching between a TADF donor and high triplet energy acceptors. J. Mater. Chem. C 4, 6447–6451 (2016).
Uoyama, H., Goushi, K., Shizu, K., Nomura, H. & Adachi, C. Highly efficient organic light-emitting diodes from delayed fluorescence. Nature 492, 234–238 (2012).
Tanaka, H., Inoue, Y. & Mori, T. Circularly polarized luminescence and circular dichroisms in small organic molecules: correlation between excitation and emission dissymmetry factors. ChemPhotoChem 2, 386–402 (2018).
Haefele, A., Blumhoff, J., Khnayzer, R. S. & Castellano, F. N. Getting to the (Square) root of the problem: how to make noncoherent pumped upconversion linear. J. Phys. Chem. Lett. 3, 299–303 (2012).
Monguzzi, A., Mezyk, J., Scotognella, F., Tubino, R. & Meinardi, F. Upconversion-induced fluorescence in multicomponent systems: steady-state excitation power threshold. Phys. Rev. B 78, 195112 (2008).
Zhao, T., Han, J., Qin, X., Zhou, M. & Duan, P. Amplifying dissymmetry factor of upconverted circularly polarized luminescence through chirality-induced spin polarization in the photon upconversion process. J. Phys. Chem. Lett. 11, 311–317 (2020).
Kim, J. et al. Induction and control of supramolecular chirality by light in self-assembled helical nanostructures. Nat. Commun. 6, 6959 (2015).
Xu, Y. et al. Enantioselective synthesis of helical polydiacetylene by application of linearly polarized light and magnetic field. Nat. Commun. 5, 5050 (2014).
He, C. et al. Highly enantioselective photo-polymerization enhanced by chiral nanoparticles and in situ photopatterning of chirality. Nat. Commun. 11, 1188–1188 (2020).
Yang, G. et al. Near-infrared circularly polarized light triggered enantioselective photopolymerization by using upconversion nanophosphors. Chemistry 23, 8032–8038 (2017).
Jin, X. et al. Optically active upconverting nanoparticles with induced circularly polarized luminescence and enantioselectively triggered photopolymerization. ACS Nano 13, 2804–2811 (2019).
Acknowledgements
This work was supported by the Strategic Priority Research Program of Chinese Academy of Sciences (No. XDB36000000); the Ministry of Science and Technology of China (2016YFA0203400 and 2017YFA0206600), National Natural Science Foundation of China (51673050 and 91856115).
Author information
Authors and Affiliations
Contributions
D.H. and X.Y. synthesized the samples and carried out all the characterizations. T.J. and P.D. supervised the work. J.H. and J.Z. helped the characterization of the nanostructure and spectral measurements. P.D. analyzed the data and wrote the paper. D.H., X.Y., and P.D. carried out the additional experiments and revised the paper. All the authors participated in the discussion and commented on the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Jeanne Crassous, Gang Zou and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Han, D., Yang, X., Han, J. et al. Sequentially amplified circularly polarized ultraviolet luminescence for enantioselective photopolymerization. Nat Commun 11, 5659 (2020). https://doi.org/10.1038/s41467-020-19479-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-19479-1
This article is cited by
-
Helical-caging enables single-emitted large asymmetric full-color circularly polarized luminescence
Nature Communications (2024)
-
Responsive circularly polarized ultralong room temperature phosphorescence materials with easy-to-scale and chiral-sensing performance
Nature Communications (2024)
-
Light-triggered fluorochromic cholesteric liquid crystal elastomer with hydrogen-bonded fluorescent switch: dualmodal-switchable circularly polarized luminescence
Science China Chemistry (2024)
-
The first chiral cerium halide towards circularly-polarized luminescence in the UV region
Science China Chemistry (2024)
-
Upconverting and downshifting circularly polarized luminescence in a superstructural helix
Science China Chemistry (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.