Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Intermolecular channels direct crystal orientation in mineralized collagen

Abstract

The mineralized collagen fibril is the basic building block of bone, and is commonly pictured as a parallel array of ultrathin carbonated hydroxyapatite (HAp) platelets distributed throughout the collagen. This orientation is often attributed to an epitaxial relationship between the HAp and collagen molecules inside 2D voids within the fibril. Although recent studies have questioned this model, the structural relationship between the collagen matrix and HAp, and the mechanisms by which collagen directs mineralization remain unclear. Here, we use XRD to reveal that the voids in the collagen are in fact cylindrical pores with diameters of ~2 nm, while electron microscopy shows that the HAp crystals in bone are only uniaxially oriented with respect to the collagen. From in vitro mineralization studies with HAp, CaCO3 and γ-FeOOH we conclude that confinement within these pores, together with the anisotropic growth of HAp, dictates the orientation of HAp crystals within the collagen fibril.

Introduction

Bone possesses exceptional mechanical properties, where these derive from its complex composition and structure. Principally comprising plate-like carbonated hydroxyapatite (HAp) crystals and collagen fibrils, bone is organized over up to nine hierarchical levels1,2,3, where the HAp crystals efficiently bear the stress applied to the collagen, increasing its stiffness, fracture strength and robustness4,5,6,7. The HAp crystals are located both within (intrafibrillar) and around (extrafibrillar) the fibrils2,3,8, where the intrafibrillar crystals have received the lion’s share of attention. The organization of these crystals is usually depicted according to the traditional model of a 3-dimensional deck-of-cards structure in which the platelets lie morphologically and crystallographically parallel throughout a fibril (Fig. 1)1,9,10,11,12,13,14. However, recent studies have questioned the validity of this model, providing evidence that the mineral platelets only form small stacks of 2–4 platelets2, and that they exhibit uniaxial orientation with respect to the collagen long axis15,16.

Fig. 1: Schematic representation of the deck-of-cards model of mineralized collagen.
figure1

The model considers the collagen fibril to comprise staggered molecular layers and the gap regions to contain rectangular shaped channels (a)1,11,13. In that model the HAp crystals nucleate in the gap regions (b), where they are epitaxially templated by charged functional groups (inset in b)9,18. They subsequently develop into platelets that are embedded between the collagen layers as shown in c. A 3D array of oriented parallel platelets eventually forms, as shown in d.

The mechanism by which collagen directs the orientation of these intrafibrillar HAp crystals is also a topic of debate15,17,18,19. HAp forms within specific gap regions inside the collagen fibrils (also called the hole zone) which contain rectangular (2D) channels1,12,13,20 that have long been thought to both induce nucleation9,21,22,23 and provide an organized organic matrix that guides epitaxial growth (Fig. 1)9,13,18,21. This mechanism has been recently called into question, however, by the demonstration that the HAp platelets in bone are covered by a hydrated amorphous layer that would preclude such molecular recognition24. As an alternative, Gower and coworkers suggested that the orientation of the crystals may be governed by their confinement within the collagen fibrils15, which was supported by the demonstration that cylindrical nanopores can direct the oriented growth of the HAp crystals in vitro25. However, this suggestion could not be considered further without a detailed model of the ultrastructure of the gap region in collagen. Existing models also do not explain the longstanding observation that the HAp nanoplates start as needle-like crystals2,12, and only later develop their 2D shape.

To resolve the mechanism by which collagen directs the oriented growth of HAp crystals, we first revisit the orientation of these crystals within the collagen fibrils in bone, as well as the shape of the gap zone in the unmineralized collagen. Detailed electron microscopic analysis shows unequivocally that mineralized single collagen fibrils in human bone indeed contain small stacks of a few crystals, and that the mineral platelets only exhibit uniaxial orientation. Using X-ray diffraction (XRD) we then visualize the 3D structure of the gap regions of the unmineralized collagen fibril and demonstrate the presence of elongated cylindrical nanopores which we propose direct HAp growth, as previously demonstrated for in vitro model systems. Finally, in vitro mineralization of the fibrils with alternative, non-native minerals shows that this orientation mechanism is only possible thanks to the strongly anisotropic structure of HAp. This provides compelling evidence that the orientation of HAp within collagen fibrils arises due to confinement effects only.

Results

Electron tomographic analysis of mineralized collagen in bone

To resolve the actual orientation of the apatite crystals in human bone, we performed a high-resolution electron tomography (ET) study (Fig. 2, see also Supplementary Movie 1) on waste material from a surgical procedure on a fractured tibia from a 10-year-old healthy female. Energy-filtered TEM tomography was used to visualize both the collagen fibrils and the HAp platelets. Using focused ion beam (FIB) milling, a 100 nm-thick lamella was cut parallel to the long axes of the mineralized collagen fibrils, and analyzed by low dose ET (total dose = 65 e Å−2, see also Supplementary Fig. 1. Computer generated lateral tomography reconstruction slices viewed perpendicular to the long axes of the collagen fibrils are defined as y-slices, while the longitudinal reconstructed slices viewed along the fibril long axes are defined as z-slices)26.

Fig. 2: Electron tomography of in vitro and in vivo mineralized collagen fibrils.
figure2

ah Electron tomography of a human bone lamella. a 2D projection of 70 tomographic reconstruction y-slices showing two adjacent mineralized collagen fibrils. b Tomographic reconstruction y-slice of one single fibril averaged from five adjacent slices. c TEM image of two parallel fibrils. d LDSAED pattern of the circled area in c. e 2D projection of 400 cross-section tomographic reconstruction z-slices showing two adjacent fibrils, as highlighted in yellow and red, respectively. f Tomographic reconstruction z-slice of one single fibril averaged from 10 adjacent slices. g, h Longitudinal and lateral angular distributions (α and γ, as indicated in b and f, respectively) of HAp platelets in the fibril. ip Cryogenic electron tomography of a type I collagen fibril mineralized with HAp in the presence of pAsp and stained with uranyl acetate38. i 2D projection of 50 tomographic reconstruction y-slices showing one mineralized collagen fibril. j Tomographic reconstruction y-slice of one single fibril averaged from five adjacent slices. k CryoTEM image of one single fibril. l LDSAED pattern of the circled area in k. m 2D projection of 300 tomographic reconstruction z-slices of one single fibril. n Tomographic reconstruction z-slice of one single fibril averaged from 10 adjacent slices. o, p Longitudinal and lateral angular distributions of the platelets, respectively. The gap/overlap regions are highlighted in a and i by white/yellow brackets, respectively. Gap regions in a are darker than overlap regions due to heavy metal staining (see Supplementary Fig. 1). Long axis of the fibrils are indicated by white arrows in d and l. The orientations of some HAp platelets are highlighted in b, f, j, and n by yellow arrows. Stacks of HAp platelets are highlighted in f and n by yellow circles, while a stack of ~10 HAp platelets is highlighted in n by an array of yellow arrows. ~150 crystals were measured that were at least 20 nm apart for b and j, and 100 nm apart for f and n. Scale bars: all panels 50 nm, except d and i 2 nm−1.

To optimize contrast for the visualization of the mineralized collagen fibrils, 70 y-slices (slice thickness 0.75 nm) of the tomographic reconstruction were averaged to generate a 2D projected volume with a thickness of 52.5 nm (Fig. 2). The resulting 2D projection showed collagen fibrils with diameters of ~100 nm (Fig. 2a) that displayed the characteristic ~67 nm banding pattern. The collagen fibrils are closely packed and heavily mineralized with HAp crystals, where the discontinuity in the banding pattern in the lateral direction allowed the individual fibrils to be recognized. The precise boundaries of the fibrils were identified by viewing the reconstructed tomogram along the fibril axis (Fig. 2e). To optimize the contrast for visualization of the organic fibrils, 400 z-slices (slice thickness 0.75 nm) of the tomogram were added, generating a 2D projected volume with a thickness of 300 nm.

Low dose selected area electron diffraction (LDSAED, Fig. 2d) of an area containing two parallel fibrils (Fig. 2c) shows the characteristic pair of (002) diffraction arcs, which indicates that the HAp platelets are oriented with their c-axes along the fibrils. In line with previous reports of bone and in vitro mineralized collagen15,27, an additional diffraction ring was observed at ~2.8 Å, which can be attributed to the unresolved (112), (211), and (300) diffractions. These reflections arise from multiple lattice planes, and can only co-exist when the planes of the HAp platelets are misoriented by >60°. This implies that the platelets are only uniaxially oriented15. No other calcium phosphate phase was detected, although it is possible that the sample still contains small amounts of amorphous calcium phosphate (ACP) and octacalcium phosphate (OCP). These have been suggested to be precursors to bone mineralization28,29,30 and can still exist in mature bone24,31, but are difficult to identify by LDSAED.

Most crystals were intrafibrillar with dimensions of ~65 × 20 × 3 nm (Fig. 2b and f, see also Supplementary Fig. 2), and sometimes displayed a curved, propeller-like morphology as previously reported (Supplementary Fig. 3)2. A smaller number of extrafibrillar crystals were also observed near the boundaries of the fibrils, where these had the same size and shape as the intrafibrillar crystals, and usually propagated into the fibrils (Supplementary Fig. 3). Analysis of the orientations of the intrafibrillar crystals confirmed that they were aligned along the long axis of the collagen fibril, with an angular distribution of ~±20° (Fig. 2g, see also Supplementary Fig. 2 and Supplementary Movie 2). The ± values here and in later discussions all correspond to the maximum misalignment angles, based on the analysis of ~150 crystals.

Definitive proof for the uniaxial orientation of these crystals then came from viewing the tomographic reconstruction along the collagen fibril axis. 2D projections of 10 added adjacent tomographic z-slices (total slice thickness 7.5 nm) showed that the platelets are indeed not organized in an ordered deck of cards structure (Fig. 2f, see also Supplementary Movie 3). Instead, in most regions of the fibril the z-slices showed that the crystals had random orientations (Fig. 2h) forming small stacks of just 2–4 platelets. In areas with higher mineral density, larger stacks of ~8 platelets were occasionally observed, (see Supplementary Fig. 4) but these were still randomly oriented within the diameter of the collagen fibril (~100 nm). Significantly, as the investigated volumes only had a thickness of 7.5 nm along the fibril axis, the observed different crystal orientations are independent of the twisted structure of the embedding collagen fibrils27. Needles (~2 nm in width and ~10 nm in length, Supplementary Figs. 4 and 5) were observed at the tip of some platelets, which confirms previous observations2,12 and supports the hypothesis that the HAp platelets evolve from needle-like crystals.

The observed uniaxial orientation of the HAp crystals seems to contrast with the pioneering tomography work of Landis et al. in the 1990s on mineralized turkey tendon13 and chick bone1, where that data is consistent with the deck-of-cards model. We note, however, that this difference may derive from their use of thicker samples (250 and 500 nm, respectively) and of a less sensitive camera system. Both of these limit the detection of HAp platelets that are not oriented parallel to the electron beam, as platelets oriented edge-on will have significantly higher contrast in TEM imaging. This was confirmed by analysis of a model system starting from different image qualities (see Supplementary Figs. 6 and 7 for details).

X-ray analysis of the structure of unmineralized collagen fibrils

To understand the role of collagen in directing the oriented growth of the HAp crystals, we examined the structure of the collagen gap zone by analyzing the 3D electron density map created from existing X-ray data of hydrated type-I collagen fibrils32. The data show that the collagen molecules are organized in a triclinic superstructure, with only a modest degree of lateral organization, and without real long-range order. This superstructure consists of unit cells called microfibrils, which each comprise five 1D-staggered, twisted collagen triple helix molecules. In the overlap region of this structure, the collagen molecules are tightly packed in a quasi-hexagonal manner with a tilt relative to the c-axis of the unit cell and an intermolecular spacing of <1 nm (Fig. 3a and b). The widths of the collagen triple helix molecules vary between ~1.1 and ~1.5 nm, in line with previous reports30,33,34. In the gap region, however, the collagen molecules are oriented approximately parallel to the unit cell c-axis (slightly tilted in the opposite direction to that of the overlap tilt). Importantly, one of the five collagen molecules is missing in each unit cell due to the 1D-staggering and the non-integer dividend of the collagen molecules length and D. As a consequence, each collagen unit cell contains a straight channel which runs parallel to the long axis of the fibril (Fig. 3a, and Supplementary Movie 4). Each of the channels is 2–3 nm in width and its cross section varies in shape along the channel (as shown by Fig. 3c–e, and Supplementary Movie 4). The channels span the gap zone and have a discontinuity between the so-called e2 and e1 bands (Fig. 3a)35, which separates them into discrete sections of 15–20 nm in length. In lateral directions, these channels are mostly separated from each other, with only ~0.3 nm wide small connections (Fig. 3c, magenta arrow). These channel geometries are consistent with recent computational data36, and are markedly different from the traditional picture which depicts rectangular 2D channels in the gap region (Fig. 1)1,13,19,37.

Fig. 3: Analysis of the 3D electron density map of the structure of collagen.
figure3

The electron density map is created from X-ray diffraction data32. a Intermolecular voids within the collagen structure, with the gap/overlap zones and the banding structure labeled. The white structures correspond to the collagen molecules, and the channels between them are labeled with different colors based on their connectivity. be Cross-section slices viewed along the collagen fibril cut at position i (0.075 D), ii (0.505 D), iii (0.773 D) and iv (0.872 D) as highlighted by white arrows in a, respectively. b Shows the typical structures of overlap region, while ce show the 2–3 nm wide channels in gap region with varying cross section shapes. The unit cell is highlighted by the yellow parallelogram. A ~0.3 nm wide small connection is highlighted by magenta arrow in c. Scale bars: a 2 nm, be 10 nm.

Cryo-TEM analysis of collagen fibrils in vitro mineralized with HAp

To understand how these cylindrical channels can direct the crystal orientation of HAp in bone, we revisited our minimal in vitro model system. There, self-assembled type I collagen fibrils from horse tendon were mineralized by immersing them in a solution containing CaCl2, K2HPO4 and poly(aspartic acid) (pAsp) for 72 h (see “Methods” section for details)38, where the pAsp was used as a crystallization control agent following the method developed by Gower et al. 15,16. The fidelity of this model system was certified using cryo-ET39 to carry out a detailed comparison of the size, shape, and orientation of the intrafibrillar crystals with those observed in bone.

Analysis of existing cryo-electron tomograms38 revealed intrafibrillar platelets with dimensions of 60 × 15 × 4 nm (Figs. 2i–p, see also Supplementary Fig. 2), where these are comparable to the dimensions previously reported for HAp crystals in human bone (thickness 2–8 nm, width 20–30 nm, length 50–100 nm)2,40,41,42, and to those derived from our own data (Fig. 2a–h). The orientation of the crystallites was also similar to those in the human bone sample. The 3D reconstruction of the cryo-electron tomogram showed that the intrafibrillar platelets were aligned with the fibril axis (Fig. 2j and o, see also Supplementary Movie 5), while the HAp (002) reflections appeared as a pair of narrow arcs with an angular spread of ±15° (Fig. 2k and l). The reflections corresponding to the (112), (211), and (300) planes were also observed as three arcs with comparable d-values (~2.8 Å) at angles of 36°, 66°, and 90° with respect to the (002) diffraction signal15,27, again pointing to uniaxial orientation of the crystals. The tomogram further showed that adjacent HAp platelets form small stacks of up to 10 platelets (Fig. 2n and Supplementary Movie 6), and that these had no preferred lateral orientation (Fig. 2p). The structure is therefore comparable to that observed in the human bone sample (Fig. 2f and h)2,19. Notably, we also obtained similar crystal sizes and orientations for the in vitro mineralization of type I collagen fibrils separated from bovine Achilles tendon (Supplementary Fig. 8)15, demonstrating that these results are not specific to the source of the collagen.

The above detailed comparison between the in vivo and in vitro results shows that our minimal model system provides a reliable means of studying the intrafibrillar mineralization in bone. Further, as pAsp was the only non-collagenous component present, it additionally indicates that the uniaxial orientation of intrafibrillar HAp crystals does not require extensive biological control, but can be attributed to the initial confinement within the intermolecular channels inside the collagen fibril. It is also important to point out that HAp crystals precipitated in bulk solution have similar thicknesses to those formed within the collagen fibril, but are about twice as wide and long (Supplementary Fig. 9). These crystals express the same crystallographic faces as the biogenic crystals, indicating that their morphology is related to the surface energies of the expressed crystal planes under the solution conditions used, rather than to specific interactions with biological macromolecules.

Mineralization of collagen with non-native minerals

To confirm whether the orientation of intrafibrillar minerals derives from specific interactions between the mineral and the amino acid residues within the gap region—as previously proposed9,13,18,21—or whether it is just due to confinement of the mineral in the intermolecular channels, we mineralized collagen with lepidocrocite (γ-FeOOH) and calcium carbonate. These two mineral systems offer different structures and compositions and have no relevance to the mineralization of collagen in biological systems.

Type I collagen fibrils (bovine Achilles) were mineralized with γ-FeOOH by immersing them in a solution of FeCl2, FeCl3, and pAsp, and increasing the pH by exposure to ammonia (Supplementary Fig. 10)43. Analysis of fibrils isolated after 3 weeks revealed the presence of γ-FeOOH platelets with average dimensions of ~25 × 13 × 2.5 nm adjacent to the fibril surface only (Fig. 4a and d), where shallow infiltration is attributed to the low solubility of Fe2+/Fe3+ ions in alkaline solutions44. In contrast, γ-FeOOH crystals with average dimensions of ~77 × 25 × 3 nm formed outside the fibrils under the same conditions. These were longer and wider than the intrafibrillar crystals, but in common with HAp had comparable thicknesses and were elongated along the c-axis (Supplementary Fig. 11)45. No intrafibrillar mineralization occurred in the absence of pAsp, but instead the fibrils became coated with 5–10 nm ferrihydrite particles (Supplementary Fig. 12).

Fig. 4: Type I collagen fibril mineralized with γ-FeOOH in the presence of pAsp.
figure4

a TEM image of a collagen fibril containing γ-FeOOH platelets. b LDSAED of a showing wide arcs of γ-FeOOH (002) diffraction along the collagen fibril axis. The pattern is obtained after radial alignment and averaging of 9 individual patterns (see Supplementary Figs. 13 and 14, and Supplementary Table 1). The direction of the collagen fibril long axis is highlighted by the white arrow. c, d Tomographic reconstruction y- and z-slices, respectively. d Is averaged from 10 adjacent slices to enhance the contrast. The orientations of some γ-FeOOH platelets are highlighted by yellow arrows in c, d. e, f Longitudinal and lateral angular distribution (α and γ, as indicated in c and d) of the platelets, respectively. ~150 crystals were measured that were at least 10 nm apart for e and 50 nm apart for f. Scale bars: a 100 nm, b 2 nm−1, c, d 50 nm.

LDSAED patterns of a single mineralized fibril exhibited a pair of broad arcs with angular spreads of ~80°, corresponding to the (002) planes of γ-FeOOH (Fig. 4b, see details in Supplementary Figs. 13 and 14 and Supplementary Table 1). The centers of the arcs, and therefore the c-axes of these platelets, were aligned with the long axis of the fibrils. ET also showed that the long axes of the platelets were generally oriented with the fibril axis (Fig. 4c and Supplementary Movie 7), but with a wider angular distribution (~±40°, Fig. 4e). In common with HAp, the γ-FeOOH platelets showed no preferred lateral orientation (Fig. 4d and f and Supplementary Movie 8).

The fibrils were also mineralized with calcium carbonate, which under ambient conditions can form three different polymorphs (vaterite, calcite, and aragonite)46, that all exhibit crystal morphologies distinct from those of HAp and lepidocrocite. Mineralization was conducted by immersing type I collagen fibrils (bovine Achilles) in a solution of CaCl2 and poly(allylamine hydrochloride) (pAH) and exposing them to ammonium carbonate vapor47, where the pAH is a crystallization control agent48, facilitating infiltration (Supplementary Fig. 15). The collagen fibrils became heavily mineralized within 48 h. The image contrast was insufficient for cryoTEM, so TEM was performed after freeze-drying vitrified samples on TEM grids.

Two types of crystals developed within the collagen fibrils. The first were ellipsoidal nanoparticles of dimensions 10 × 20 nm that were elongated along the fibril axis (Fig. 5a and b). Higher densities of these crystals were present in the gap regions than in the overlap regions, resulting in a banding pattern (Fig. 5b). These were identified as vaterite using LDSAED, where the (002) reflections were present as a pair of arcs oriented along the fibril axis, while all other lattice planes appeared as rings (Fig. 5c). The second were ~100 × 600 nm calcite disks comprising ~10 nm nanoparticles. In common with previous observations49 these were present in discrete regions in the collagen (Fig. 5d and e), and were neither elongated nor oriented in the collagen matrix (inset of Fig. 5e and f). Control experiments performed in the absence of collagen as expected17, yielded micron-sized calcite and vaterite crystals with morphologies including thin films and fibers.

Fig. 5: Type I collagen fibril mineralized with CaCO3 in the presence of pAH.
figure5

a, b SEM and TEM images of collagen fibrils mineralized by vaterite after 48 h, respectively. Inset: higher magnification image showing the elongated morphology of the vaterite particles. c LDSAED of b showing arcs of vaterite (002) diffraction along the collagen fibril axis. d, e SEM and TEM images of collagen fibrils mineralized by calcite after 48 h, respectively. Zoom-in image in the inset of e shows the nanoparticle subunits. f LDSAED pattern of e. The direction of the collagen fibril long axes are highlighted by white arrows in c and f. g, h In situ WAXS and SAXS spectra of collagen fibrils during mineralization, respectively. * In g indicate the background signals from the X-ray or the mica windows. The 3rd and 5th order peaks corresponding to the 67 nm axial organization of collagen are highlighted in h. After long mineralization times, the signal from the CaCO3 dominates, obscuring the signals of collagen. i Zoom-in of the square in h. The two vertical dash lines indicate the SAXS peaks related to the original lateral intermolecular distance of d = 2π/4.08 nm−1 (~1.5 nm) and the compressed d = 2π/5.68 nm−1 (~1.1 nm). Scale bars: a, d 500 nm, b, e 200 nm, Inset of b, e: 20 nm c, f: 1 nm−1.

Scanning electron microscopy (SEM) demonstrated that CaCO3 mineralization induced significant distortion of the fibrils (Fig. 5d). To understand the molecular basis of this distortion, we conducted in-situ analysis of the mineralization process using small-angle/wide-angle X-ray scattering (SAXS/WAXS) (Supplementary Fig. 16). No changes in the SAXS and WAXS spectra were observed during the first 80 min of the reaction, while an increase in the scattering intensity was detected after 90 min (Fig. 5g). This can be attributed to the formation of amorphous calcium carbonate (ACC) within the fibrils, where this causes a small decrease of the lateral packing distance of the collagen molecules. This is demonstrated by broadening of the SAXS peak at q = 4.08 nm−1 (~1.5 nm), which corresponds to a reduction in the separation of the collagen molecules (Fig. 5h and i).

WAXS confirmed the development of both vaterite and calcite at incubation times >95 min (Fig. 5g), while SAXS revealed that crystallization of the ACC is accompanied by a significant reduction in the intermolecular distances of the collagen molecules from ~1.5 to 1.1 nm, as shown by the replacement of the q = 4.08 nm−1 peak with one at q = 5.68 nm−1 (Fig. 5h and i). The axial ~67 nm d-band organization remains unchanged during this process. The amount of crystalline material in the sample then continued to develop with time and significant amounts of calcite and vaterite were observed after 440 min (Fig. 5g). Similar observations have been made for bovine50, fish bone51, and turkey tendon mineralized with HAp52, demonstrating that the collagen molecules are pushed apart and compressed by initial infiltration of the ACC, and more significantly by its subsequent crystallization.

Discussion

Historically, the first ideas about the structure of mineralized collagen came from the early TEM study of Weiner and Traub, who suggested that HAp platelets in mineralized collagen are co-aligned along all three crystallographic axes throughout a collagen fibril forming a deck-of-cards organization (Fig. 1d)11. This was later supported by the ET studies of Landis et al. 1,13. A highly ordered gap region structure was proposed to explain such an organization, in which the collagen molecules are 3D organized and form parallel 2D channels (Fig. 1a). In this well-defined scaffold, the amino acid residues and the distribution of charge in these channels are believed to induce HAp nucleation9,21,22,23 and to epitaxially template the crystal orientation (Fig. 1b)9,13,18,21. While this scenario has never been confirmed experimentally, it has been widely accepted and is frequently described in textbooks and review papers (see Supplementary Note 1 for a list of influential papers presenting this model)3,4,14. Over the last decade, however, experimental and computational studies have questioned this model, both with respect to the orientation of the crystals in the collagen matrix, and to the way in which crystal orientation is achieved.

Burger et al. concluded from an X-ray scattering study of fish bone that although the HAp platelets were aligned with their c-axes along the collagen axis, the stacks of platelets had irregular intercrystalline spacings, and varied in their lateral orientations19. From STEM tomography Reznikov et al. proposed that the HAp platelets in human bone had random lateral orientations and only formed short stacks2. Both of these studies therefore support the conclusion of Olszta et al. that the platelets only exhibit uniaxial alignment15.

Nevertheless, these studies do not provide a comprehensive picture for the structure of collagen and the way it is mineralized. Reznikov et al. did not discuss the origin of crystal orientation with respect to the collagen fibrils while Burger et al. proposed that parallel 2D channels exist within a collagen fibril (cf. Fig. 1a), which could template the formation of HAp platelet stacks. Deformation of the matrix during this process would also lead to distortion of the parallel alignment of the crystals19. Olstza et al. proposed that the HAp platelets form by transformation of the ACP confined in the space between collagen molecules, but did not yet have the details of how this intermolecular space was distributed throughout the collagen structure15.

While the community had considered the collagen structure to consist of a quasi-hexagonally packed array of staggered, straight collagen molecules, in 2006 the XRD study of Orgel et al. revealed a more complex triclinic superstructure, in which the tropocollagen molecules are organized in a twisted and tilted arrangement32. One collagen microfibril comprises five 1D-staggered, twisted collagen triple helix molecules, where the staggering leads to the characteristic periodical band structure that contains a dense overlap region and a more loosely packed gap region32. Under this structural model, which was confirmed by a recent computational study of Xu et al.36, a hole zone with 2D channels as depicted in Fig. 1a does not exist.

Looking then from the perspective of the mineral phase, Wang et al. used solid-state nuclear magnetic resonance (ssNMR) to reveal that the HAp platelets—even in mature bone—are covered by a hydrated amorphous layer24,31, which prevents any direct molecular recognition between collagen and HAp. Nevertheless, some recent studies have suggested that the charged amino acids in collagen are able to nucleate calcium phosphate minerals22,23,30, and that an epitaxial match (cf. Fig. 1b) exist with calcium-deficient apatite18. More consistent with our new insights on collagen-directed mineralization is the proposal that the orientation of HAp crystals is simply induced by confinement within the gap region15,19. Indeed, precipitation of HAp in various in vitro systems including nanotubes25, peptide amphiphile nanofibers53, polymerized liquid crystals54, and cellulose fibers55 results in crystals whose c-axes are aligned with the long axis of the confining media.

The work we present here comprehensively addresses all three key aspects of the mineralization of collagen: (1) the organization of intrafibrillar HAp crystals, (2) the structure of the collagen gap region, and (3) the interaction between the mineral and the organic collagenous matrix. Our high resolution/high contrast TEM study visualized both the mineral and the collagen fibrils in bone and unequivocally confirms that the intrafibrillar HAp platelets are only uniaxially aligned with respect to the collagen long axis15, and that they sometimes form small stacks of platelets2. Notably, these data were obtained from the analysis of single collagen fibrils rather than bulk bone2, or bundles of collagen fibrils19, such that the structural information is unambiguously related to intrafibrillar crystals only.

We then demonstrate that the gap regions—where the HAp crystals nucleate12—contain discrete, elongated channels that start in the a-band region. Based on our previous observations of an in vitro model system, which show that mineral infiltration in the form of ACP begins in these sites38, we propose that the first crystals form by the transformation of the ACP in the channels, resulting in the formation of needle-like crystals whose sizes and shapes are defined by the geometry of the channels. Our observations therefore necessitate that the traditional model based on 2D gap zones is revised, and provide the foundation for a model of collagen mineralization based on confinement (Fig. 6) rather than on specific interactions between the mineral and organic matrix components. This model is further supported by our demonstration that collagen also induces the crystallographic and morphological alignment of γ-FeOOH and vaterite, in a manner comparable to that of HAp.

Fig. 6: Schematic representation of the proposed confinement model for collagen mineralization.
figure6

The model is based on the X-ray crystal structure of the collagen fibril in Fig. 3, a where the overlap regions consist of tilted molecules which are densely packed in a quasi-hexagonal pattern (highlighted by yellow lines), and the gap regions contain straight channels (highlighted by yellows lines) allowing HAp nucleation. The channels are initially filled with ACP phase (purple particles in b), which through an amorphous-to-crystalline transformation form HAp nuclei (red particles in c). Nuclei with their fast growing c-axes parallel to the channels out-compete those with other orientations (d), and develop into platelets by pushing aside the collagen molecules, as shown in e. Needle-like tips are left on some platelets (highlighted by yellow arrow). Misoriented nuclei and ACP are either consumed by Ostwald ripening (highlighted by the orange arrow), or fuse with other platelets by adjusting the ionic arrangement58 (highlighted by blue arrows). The platelets further grow and start to twist around their long axes probably due to the locally changing collagen organization (f). This results in the twisted HAp platelets being roughly uniaxially oriented with their c-axis parallel to the long axis of the fibril (g).

In line with our model, Traub et al. have shown that the intrafibrillar HAp crystallization starts in the gap regions within the collagen fibrils12. Additionally, it has been shown both in vivo28 and in vitro38 that collagen mineralization proceeds through an ACP precursor that subsequently transforms into crystalline HAp. We therefore propose that ACP readily fills the channels in the gap regions (Fig. 6b), and that smaller amounts of ACP will infiltrate into the tightly packed overlap regions where intermolecular spacings are <1 nm (Fig. 6a). This is likely to be a synergistic process where the collagen defines the shape of the ACP, and the ACP infiltration induces some distortion of the collagen structure, as is also observed for CaCO3 (Fig. 5g–i). A population of randomly oriented HAp nuclei will then form in the channels, either via dissolution-recrystallization, or pseudomorphic transformation of the ACP precursor (Fig. 6c)56.

Based on previous in vitro experiments using cylindrical nanopores25 we expect that only those crystals oriented with their fast growing c-axes aligned with the channel (and thus the fibril) axis are able to grow unrestricted into needle-shaped crystals (Fig. 6d). Crystals that are oriented in other directions can only grow by pushing apart the collagen molecules, which is energetically less favorable. Those misoriented smaller crystals and remaining ACP will subsequently be consumed by the growth of the needles, either by a dissolution-reprecipitation process (Ostwald ripening)57, or by adjusting the ionic arrangement and fusing with the growing HAp crystal58. The lateral growth of the needles will then generate platelets by pushing aside neighboring collagen molecules (Fig. 6e).

This mechanism is possible due to the unique structure of collagen, where the gap region is more compliant and compressible than the overlap region59. Continued growth of the crystals along the c-axis will cause them to extend into the overlap region, causing a rearrangement of the collagen molecules, and a concomitant displacement of the included ACP. This is supported by our SAXS/WAXS data on CaCO3 (Fig. 5g–i) that show the rearrangement of the collagen during the amorphous to crystalline transition. During this process, the platelets also start to twist along their long axes in agreement with previous reports (Fig. 6f)2, which we tentatively attribute to the locally changing collagen organization within the microfibril. This eventually leads to twisted HAp platelets that are uniaxially oriented along their c-axes, where adjacent platelets may direct each other and form small stacks, depending on the degree of mineralization (Fig. 6g, see also Fig. 2f and n).

This scenario is in excellent agreement with studies of fish bones19 and human bones2, which showed that HAp nanoplatelets2,12 only form short or irregular stacks, that may become intergrown in time2. Furthermore, the recent study of Reznikov et al. also observed needle-like tips on HAp platelets in human bone that resemble fingers of a hand as well as individual needle-like crystals2, and proposed that the HAp nanoplatelets develop from these needle-like crystals. We note that a similar scenario was suggested as far back as 1992 by Traub et al. based on the observation of needle-like crystals in the early stages of turkey tendon mineralization12. We emphasize that the final intrafibrillar mineral principally comprises crystalline HAp nanoplatelets, rather than needle-like crystals60 or ACP61 as suggested by some dark-field TEM (DFTEM) studies. These discrepancies may be related to the fact that only a small fraction of the total diffraction signals were used to form DFTEM images. As the intrafibrillar HAp nanoplatelets have an imperfect uniaxial orientation and can also be twisted, most will have no contrast or only be partly visible in the DFTEM images, making it difficult to deduce their crystallinity and morphology with this technique.

γ-FeOOH and vaterite also have anisotropic crystal structures and grow fastest along their c-axes45,62, resulting in a preferred alignment of this axis with the collagen fibril. Calcite, in contrast, has a rhombohedral crystal structure and no preferential growth direction63, such that no orientation was observed within the collagen fibrils. That the degrees of orientation of γ-FeOOH and vaterite are less pronounced than for HAp can be attributed to the smaller aspect ratios of the intrafibrillar γ-FeOOH and vaterite crystals (1.9 and 2.0, respectively) as compared with HAp (4.1). The gap zone channels therefore have a weaker influence on their crystallographic orientation.

Although collagen can effectively direct crystal orientation, it has a relatively small effect on crystal morphologies. The HAp and γ-FeOOH crystals formed within the collagen have nanoplatelet morphologies comparable to those formed in bulk solution, and are just 2–3 times smaller in length and width. The intrafibrillar vaterite nanoparticles also closely resemble the subunits from which polycrystalline vaterite particles are usually constructed. In all of these cases, the width of the final crystals exceeds the original width of the channel in which they form. This shows that the collagen matrix is flexible enough for a crystal to push the collagen molecules aside, accessing a neighboring pore to develop into its preferred morphology (Fig. 6c). In contrast, calcite—which invariably appears as micron-sized, rhombohedral crystals in bulk solutions—grows to large sizes, vastly distorting the fibrils. These observations suggest that the final morphologies of the intrafibrillar crystals are largely determined by their crystallographic structure rather than by the collagen matrix.

While the oriented growth of intrafibrillar HAp in bone can be explained based on principles of physical chemistry alone, we also emphasize the importance of biological control mechanisms in the formation of this complex hierarchical tissue. While our model shows that the uniaxial orientation of HAp in collagen fibrils can be induced by confinement only, it does not exclude the involvement of organic matrix components in the nucleation process22,23,64, such as the amino acid groups lining the channels, carbohydrate modifications of collagen, or osteocalcin entrapped in the gap region. In particular, one could envision a role for charged groups in creating a Ca2+ sponge to increase the local supersaturation, promoting nucleation in the gap region. This has been proposed, not only for calcium phosphate12, but also for the nucleation of CaCO3 in the nacre of mussel65,66.

It is also recognized that additional soluble molecules including citrate67 and many non-collagenous proteins are involved in collagen mineralization68. Here, we emphasize that in contrast to most other reports, the data from our study can be unequivocally attributed to intrafibrillar mineralization. Therefore, these non-collagenous molecules are unlikely to be involved in the orientational control of intrafibrillar crystal formation. However, they most certainly play a role in intrafibrillar mineralization by facilitating mineral infiltration69, as has been demonstrated for polyelectrolytes (e.g., pAsp) in in vitro model systems15,38. These molecules may also be involved in the control of extrafibrillar mineralization, which accounts for a significant fraction of the mineral content in bone70.

Finally, our model does not address the higher levels of hierarchical organization of the mineral platelets2,3,69 that are responsible for the 3D mechanical anisotropy of bone70,71, nor does it describe the rotated-plywood organization of the crystals due to the twisting of collagen fibrils70, or the formation of extrafibrillar minerals2,8. Again, multiple bio-molecules are inevitably involved in these complex processes.

The exceptional properties of bone are intimately linked to its unique hierarchical structure, of which the mineralized collagen fibril is the basic building block. Identification of the structure of the mineralized collagen fibril, and the mechanisms that underlie its formation, therefore underpins the development of new strategies for promoting bone regeneration and creating biomaterials with properties comparable to those of bone54,55. The long-standing deck-of-cards model of intrafibrillar HAp, and the belief that orientation is achieved via an epitaxial chemical interaction between the organic matrix and nascent crystals, have made it extremely difficult to replicate this structure. We demonstrate here that the reality is actually considerably less complex: the HAp platelets are only uniaxially oriented, and that this is achieved via generic confinement effects. This minimalistic approach to the formation of highly ordered assemblies by crystallization from solution is also known to operate in other biological systems, where biomolecules are only organized to create the boundaries for physical chemistry to do its work72,73. We anticipate that application of similar simple strategies will facilitate the design of synthetic systems that mimic bone or promote its regeneration54,55.

Methods

Materials

Analytical grade CaCl2, K2HPO4, FeCl2, FeCl3, (NH4)OH aqueous solution (28%), (NH4)2CO3, 4-(2-hydroxyethyl)piperazine-1-ethanesulfonic acid (HEPES), uranyl acetate, poly-(α, β)-dl-aspartic acid sodium salt (pAsp, molecular weight = 2000–11,000 g mol−1) and poly(allylamine hydrochloride) (pAH, mw = 15,000 g mol−1) were purchased from Sigma-Aldrich and used without further purification. Type-I collagen extracted from horse tendon was kindly provided by Prof. Giuseppe Falini (Department of Chemistry, University of Bologna, Italy) and was originally purchased from OPOCRIN Spa38. Type-I collagen sponge tapes derived from bovine Achilles tendon was purchased from ACE Surgical.

Preparation of TEM lamella of bone sample

The present study was carried out on a sample of healthy cortical bone from the left tibia of a 10-year-old female. According to the Central Committee on Research involving Human Subjects (CCMO), this type of study does not require approval from an ethics committee in the Netherlands (see https://english.ccmo.nl/investigators/legal-framework-for-medical-scientific-research/your-research-is-it-subject-to-the-wmo-or-not). A section of ~2 cm × 2 cm × 2 cm, containing cortical bone was cut and pre-fixed in a solution of 2% paraformaldehyde (PFA) in cacodylate buffer at pH = 7 for 2 days. After pre-fixation the samples were washed using ultrapure water on a rocking table (for two periods of 6 h and subsequently overnight) which were fixed again with 4% glutaraldehyde in cacodylate buffer at pH = 7 and washed with double-distilled water in steps as above mentioned74.

Later, fixed samples were stained with the OTOTO procedure (also known as conductive staining)75, involving the sequential exposure to osmium tetroxide (O) and thiocarbohydrazide (T) providing contrast as well as conductive properties2,3. After the staining procedure, bone pieces were washed with double-distilled water for 2 min and embedded in Epon epoxy resin dissolved in acetone (Embed 812, EMS, USA). The Epon embedding was carried out in five steps, each for 2 h: 25%, 50%, 75%, 100% repeated twice, which was followed by 100% resin overnight and final embedding in a mold for 48 h at 60 °C. After 48 h, Epon-embedded bone pieces were trimmed using a glass knife on a microtome order to expose the embedded tissue. The trimmed blocks were mounted on a house made sample holder using silver paste and sputter-coated with gold. The TEM lamella preparation was performed in a dual-beam FIB/SEM (FEI Quanta FEG 600, Thermo Fisher Scientific), equipped with a gallium ion source operating with an accelerating voltage range of 0.5–30 kV and an Omniprobe™ micromanipulator. We prepared a 100 nm-thick section from the bone sample for transmission electron microscopy studies using the FIB lift-out technique. The region of interest for TEM lamella was determined after visualizing the surface of bone pieces by SEM. A thin section was cut parallel to the orientation of the long axis of the bone meaning that collagen fibrils would have in-plane view upon visualizing the thin section by TEM. The thin section (10 × 10 × 0.1 µm) was transferred to a three post lift-out TEM half-grid (Agar Scientific AGJ420) in order to use it for further ET characterization.

Analysis of collagen structure

The electron density map of 8 × 8 × 1 collagen unit cells was built using the UCSF Chimera package76, based on the structure obtained by a previous X-ray study32. The map was generated with a resolution of 0.3 nm and voxel size of 0.1 nm. From this electron density map we segmented the intermolecular channels within the collagen structure by applying in-house Matlab scripts. The edges of the channels were defined by considering the diameter of each collagen triple-helix molecule as 1.5 nm77. Channels with diameters <8 pixels (0.8 nm) were removed from the segmentation by eroding and then dilating the segmented channels for 4 pixels for an enhanced separation of the main channels. The channels on the model surface were also removed for improved visualization of the channels inside the collagen structure. The remaining channels were then labeled with different colors according to their connectivity, and visualized in 3D using Amira-Avizo software (Thermo ScientificTM).

Mineralization with HAp

Horse tendon collagen fibrils (purchased from OPOCRIN Spa) were prepared and mineralized with HAp38. These collagen fibrils were self-assembled on cryoTEM grids and incubated in HEPES buffer (10 mM, pH 7.4) containing CaCl2 (2.7 mM), K2HPO4 (1.35 mM) and pAsp (10 µg mL−1) at 37 °C for 72 h. After mineralization, the grids were removed from the mineralization solution and subsequently washed with MilliQ water, incubated in 0.5% uranyl acetate in MilliQ water for 15 s. After that the grids were washed with MilliQ water for 1 min, manually blotted and vitrified using an automated vitrification robot. For the experiments using bovine Achilles collagen fibrils, the fibrils were separated from collagen sponges (purchased from ACE Surgical) by thoroughly grinding the sponges into a fine powder in liquid nitrogen and drying at 37 °C. The powder was then dispersed at a concentration of 5 g L−1 into Hepes buffer (10 mM, pH 7.4) containing CaCl2 (4.5 mM), K2HPO4 (2.1 mM), and pAsp (75 µg mL−1) and heated at 37 °C for 4 days15. After mineralization, 3 µL of solution was applied to a cryoTEM grid and vitrified.

Mineralization with lepidocrocite

Mineralization of collagen fibrils with lepidocrocite was performed by incubating 0.125 cm3 of collagen sponge (bovine Achilles, ACE Surgical) in a solution of FeCl3 (1 mM), FeCl2 (0.5 mM), and pAsp (0.69 mg mL−1, Asp residue:Fe ions = 4:1) overnight. The solution was subsequently placed in a glove box under N2 saturated with 8% NH4OH for 24 h. The increase in pH was constantly monitored using a TIAMO Titrando Set-up (Metrohm). Control experiments were performed with different concentrations of pAsp. After the reaction, the sponge was washed thoroughly with ethanol, and ground in liquid nitrogen for TEM analysis.

Mineralization with calcium carbonate

To mineralize collagen fibrils with calcium carbonate, collagen sponge (bovine Achilles, ACE Surgical) was ground in liquid nitrogen as described above, and dispersed in solutions of 10 mM CaCl2 at a concentration of 5 g L−1, in the absence of further additives or in the presence of 1 mg mL−1 pAH. The solutions were then transferred to a desiccator in which they were exposed to the CO2/NH3 gaseous mixture released on the decomposition of solid (NH4)2CO3. 3 µL of the reaction solutions were collected at different time points and vitrified. For SEM studies, the samples were added to ethanol, centrifuged (4715 × g) and dried at room temperature. The in situ X-ray studies were performed at the DUBBLE beamline at the European Synchrotron Research Facility (ESRF), Grenoble, France, by incubating 0.125 cm3 of collagen sponge (bovine Achilles) in a flow cell between two mica windows (Supplementary Fig. 16)78.

Electron microscopy analysis

SEM and energy-dispersive X-ray spectroscopy (EDX) studies were performed using an FEI Quanta 3D field emission SEM equipped with an EDAX EDX detector. Au quantifoil grids were used for cryoTEM sample preparations, and the vitrification was performed using an automated vitrification robot (FEI Vitrobot™ Mark III). (Cryo)TEM imaging was typically performed under ~5 μm defocus on a FEI-Titan TEM equipped with a field emission gun and operating at 300 kV. Images were recorded using a 2k × 2k Gatan CCD camera equipped with a post-column Gatan energy filter (GIF), with an electron dose of lower than 10 e Å−2 per image. For bone samples and collagen fibrils mineralized with lepidocrocite, the tomography tilt series were taken by tilting the specimen from approximately −65° to 65°, 2° per step. For collagen fibril mineralized in vitro with HAp, the tomography tilt series was taken by tilting the specimen from approximately −60° to 60°, with a low-angle tilting step of 2° (from −45° to 45°) and a high-angle tilting step of 1° (<−45° or >45°). The electron dose of all the tomography tilt series is 1.0 e Å−2 per frame. The alignment and 3-dimensional reconstructions of the data sets were performed in IMOD. Image analysis was carried out using Gatan Digital Micrograph and Matlab.

Data availability

All of the data that support the findings of this study are available online at: Supporting Data for “Intermolecular Channels Direct Crystal Orientation in Mineralized Collagen”, Figshare, https://doi.org/10.6084/m9.figshare.12845990.

References

  1. 1.

    Landis, W. J., Hodgens, K. J., Arena, J., Song, M. J. & McEwen, B. F. Structural relations between collagen and mineral in bone as determined by high voltage electron microscopic tomography. Microsc. Res. Tech. 33, 192–202 (1996).

    CAS  PubMed  Article  Google Scholar 

  2. 2.

    Reznikov, N., Bilton, M., Lari, L., Stevens, M. M. & Kröger, R. Fractal-like hierarchical organization of bone begins at the nanoscale. Science 360, eaao2189 (2018).

    PubMed  PubMed Central  Article  CAS  Google Scholar 

  3. 3.

    Reznikov, N., Shahar, R. & Weiner, S. Bone hierarchical structure in three dimensions. Acta Biomater. 10, 3815–3826 (2014).

    PubMed  Article  Google Scholar 

  4. 4.

    Fratzl, P., Gupta, H. S., Paschalis, E. P. & Roschger, P. Structure and mechanical quality of the collagen–mineral nano-composite in bone. J. Mater. Chem. 14, 2115–2123 (2004).

    CAS  Article  Google Scholar 

  5. 5.

    Gao, H. J., Ji, B. H., Jager, I. L., Arzt, E. & Fratzl, P. Materials become insensitive to flaws at nanoscale: lessons from nature. Proc. Natl Acad. Sci. USA 100, 5597–5600 (2003).

    ADS  CAS  PubMed  Article  Google Scholar 

  6. 6.

    Nair, A. K., Gautieri, A., Chang, S.-W. & Buehler, M. J. Molecular mechanics of mineralized collagen fibrils in bone. Nat. Commun. 4, 1724 (2013).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  7. 7.

    Currey, J. D. Bones: Structure and Mechanics (Princeton University Press, New Jersey, 2006).

  8. 8.

    McNally, E. A., Schwarcz, H. P., Botton, G. A. & Arsenault, A. L. A model for the ultrastructure of bone based on electron microscopy of ion-milled sections. PLoS ONE 7, e29258 (2012).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  9. 9.

    Mann, S. Molecular recognition in biomineralization. Nature 332, 119 (1988).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Lowenstam, H. A. & Weiner, S. On Biomineralization (Oxford University Press, Oxford, 1989).

  11. 11.

    Weiner, S. & Traub, W. Organization of hydroxyapatite crystals within collagen fibrils. FEBS Lett. 206, 262–266 (1986).

    CAS  PubMed  Article  Google Scholar 

  12. 12.

    Traub, W., Arad, T. & Weiner, S. Origin of mineral crystal-growth in collagen fibrils. Matrix 12, 251–255 (1992).

    CAS  PubMed  Article  Google Scholar 

  13. 13.

    Landis, W. J., Song, M. J., Leith, A., Mcewen, L. & Mcewen, B. F. Mineral and organic matrix interaction in normally calcifying tendon visualized in 3 dimensions by high-voltage electron-microscopic tomography and graphic image-reconstruction. J. Struct. Biol. 110, 39–54 (1993).

    CAS  PubMed  Article  Google Scholar 

  14. 14.

    Mann, S. Biomineralization: Principles and Concepts in Bioinorganic Materials Chemistry Vol. 5 (Oxford University Press, Oxford, 2001).

  15. 15.

    Olszta, M. J. et al. Bone structure and formation: a new perspective. Mater. Sci. Eng. R. Rep. 58, 77–116 (2007).

    Article  CAS  Google Scholar 

  16. 16.

    Jee, S. S., Kasinath, R. K., DiMasi, E., Kim, Y.-Y. & Gower, L. Oriented hydroxyapatite in turkey tendon mineralized via the polymer-induced liquid-precursor (PILP) process. CrystEngComm 13, 2077–2083 (2011).

    CAS  Article  Google Scholar 

  17. 17.

    Cantaert, B. et al. Formation and structure of calcium carbonate thin films and nanofibers precipitated in the presence of poly (allylamine hydrochloride) and magnesium ions. Chem. Mater. 25, 4994–5003 (2013).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  18. 18.

    Tao, J. et al. Energetic basis for the molecular-scale organization of bone. Proc. Natl Acad. Sci. USA 112, 326–331 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

  19. 19.

    Burger, C. et al. Lateral packing of mineral crystals in bone collagen fibrils. Biophys. J. 95, 1985–1992 (2008).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  20. 20.

    Jackson, S. F. & Randall, J. The fine structure of bone. Nature 178, 798–798 (1956).

    ADS  CAS  PubMed  Article  Google Scholar 

  21. 21.

    Christoffersen, J. & Landis, W. A contribution with review to the description of mineralization of bone and other calcified tissues in vivo. Anat. Rec. 230, 435–450 (1991).

    CAS  PubMed  Article  Google Scholar 

  22. 22.

    Silver, F. H. & Landis, W. J. Deposition of apatite in mineralizing vertebrate extracellular matrices: a model of possible nucleation sites on type I collagen. Connect. Tissue Res. 52, 242–254 (2011).

    CAS  PubMed  Article  Google Scholar 

  23. 23.

    Xu, Z. et al. Molecular mechanisms for intrafibrillar collagen mineralization in skeletal tissues. Biomaterials 39, 59–66 (2015).

    CAS  PubMed  Article  Google Scholar 

  24. 24.

    Wang, Y. et al. Water-mediated structuring of bone apatite. Nat. Mater. 12, 1144–1153 (2013).

    ADS  CAS  PubMed  Article  Google Scholar 

  25. 25.

    Cantaert, B., Beniash, E. & Meldrum, F. C. Nanoscale confinement controls the crystallization of calcium phosphate: relevance to bone formation. Chem. Eur. J. 19, 14918–14924 (2013).

    CAS  PubMed  Article  Google Scholar 

  26. 26.

    Friedrich, H., Frederik, P. M., de With, G. & Sommerdijk, N. A. Imaging of self‐assembled structures: interpretation of TEM and cryo-TEM images. Angew. Chem. Int. Ed. 49, 7850–7858 (2010).

    CAS  Article  Google Scholar 

  27. 27.

    Traub, W., Arad, T. & Weiner, S. Three-dimensional ordered distribution of crystals in Turkey tendon collagen fibers. Proc. Natl Acad. Sci. USA 86, 9822–9826 (1989).

    ADS  CAS  PubMed  Article  Google Scholar 

  28. 28.

    Mahamid, J. et al. Mapping amorphous calcium phosphate transformation into crystalline mineral from the cell to the bone in zebrafish fin rays. Proc. Natl Acad. Sci. USA 107, 6316–6321 (2010).

    ADS  CAS  PubMed  Article  Google Scholar 

  29. 29.

    Vyalikh, A., Elschner, C., Schulz, M. C., Mai, R. & Scheler, U. Early stages of biomineral formation—a solid-state NMR investigation of the mandibles of minipigs. Magnetochemistry 3, 39 (2017).

    Article  CAS  Google Scholar 

  30. 30.

    Simon, P. et al. First evidence of octacalcium phosphate@ osteocalcin nanocomplex as skeletal bone component directing collagen triple-helix nanofibril mineralization. Sci. Rep. 8, 1–17 (2018).

    ADS  Article  CAS  Google Scholar 

  31. 31.

    Von Euw, S. et al. Bone mineral: new insights into its chemical composition. Sci. Rep. 9, 1–11 (2019).

    Article  CAS  Google Scholar 

  32. 32.

    Orgel, J. P. R. O., Irving, T. C., Miller, A. & Wess, T. J. Microfibrillar structure of type I collagen in situ. Proc. Natl Acad. Sci. USA 103, 9001–9005 (2006).

    ADS  CAS  PubMed  Article  Google Scholar 

  33. 33.

    Baranauskas, V., Vidal, B. & Parizotto, N. Observation of geometric structure of collagen molecules by atomic force microscopy. Appl. Biochem. Biotechnol. 69, 91–97 (1998).

    CAS  PubMed  Article  Google Scholar 

  34. 34.

    Orgel, J. P., Persikov, A. V. & Antipova, O. Variation in the helical structure of native collagen. PLoS ONE 9, e89519 (2014).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  35. 35.

    Sweeney, S. M. et al. Candidate cell and matrix interaction domains on the collagen fibril, the predominant protein of vertebrates. J. Biol. Chem. 283, 21187–21197 (2008).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  36. 36.

    Xu, Z., Zhao, W., Wang, Z., Yang, Y. & Sahai, N. Structure analysis of collagen fibril at atomic-level resolution and its implications for intra-fibrillar transport in bone biomineralization. Phys. Chem. Chem. Phys. 20, 1513–1523 (2018).

    CAS  PubMed  Article  Google Scholar 

  37. 37.

    Kim, D., Lee, B., Thomopoulos, S. & Jun, Y.-S. The role of confined collagen geometry in decreasing nucleation energy barriers to intrafibrillar mineralization. Nat. Commun. 9, 962 (2018).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  38. 38.

    Nudelman, F. et al. The role of collagen in bone apatite formation in the presence of hydroxyapatite nucleation inhibitors. Nat. Mater. 9, 1004–1009 (2010).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  39. 39.

    Nudelman, F., de With, G. & Sommerdijk, N. A. J. M. Cryo-electron tomography: 3-dimensional imaging of soft matter. Soft Matter 7, 17–24 (2011).

    ADS  CAS  Article  Google Scholar 

  40. 40.

    Rubin, M. A. et al. TEM analysis of the nanostructure of normal and osteoporotic human trabecular bone. Bone 33, 270–282 (2003).

    PubMed  Article  Google Scholar 

  41. 41.

    Weiner, S. & Price, P. A. Disaggregation of bone into crystals. Calcif. Tissue Int. 39, 365–375 (1986).

    CAS  PubMed  Article  Google Scholar 

  42. 42.

    Rinnerthaler, S. et al. Scanning small angle X-ray scattering analysis of human bone sections. Calcif. Tissue Int. 64, 422–429 (1999).

    CAS  PubMed  Article  Google Scholar 

  43. 43.

    Lenders, J. J. M. et al. A bioinspired coprecipitation method for the controlled synthesis of magnetite nanoparticles. Cryst. Growth Des. 14, 5561–5568 (2014).

    CAS  Article  Google Scholar 

  44. 44.

    Schwertmann, U. Solubility and dissolution of iron oxides. Plant Soil 130, 1–25 (1991).

    CAS  Article  Google Scholar 

  45. 45.

    Taylor, R. Influence of chloride on the formation of iron oxides from Fe (II) chloride. II. Effect of [Cl] on the formation of lepidocrocite and its crystallinity. Clays Clay Min. 32, 175–180 (1984).

    ADS  CAS  Article  Google Scholar 

  46. 46.

    Meldrum, F. C. & Cölfen, H. Controlling mineral morphologies and structures in biological and synthetic systems. Chem. Rev. 108, 4332–4432 (2008).

    CAS  PubMed  Article  Google Scholar 

  47. 47.

    Ihli, J., Bots, P., Kulak, A., Benning, L. G. & Meldrum, F. C. Elucidating mechanisms of diffusion-based calcium carbonate synthesis leads to controlled mesocrystal formation. Adv. Funct. Mater. 23, 1965–1973 (2013).

    CAS  Article  Google Scholar 

  48. 48.

    Cantaert, B. et al. Think positive: phase separation enables a positively charged additive to induce dramatic changes in calcium carbonate morphology. Adv. Funct. Mater. 22, 907–915 (2012).

    CAS  Article  Google Scholar 

  49. 49.

    Olszta, M., Douglas, E. & Gower, L. Scanning electron microscopic analysis of the mineralization of type I collagen via a polymer-induced liquid-precursor (PILP) process. Calcif. Tissue Int. 72, 583–591 (2003).

    CAS  PubMed  Article  Google Scholar 

  50. 50.

    Bonar, L. C., Lees, S. & Mook, H. Neutron diffraction studies of collagen in fully mineralized bone. J. Mol. Biol. 181, 265–270 (1985).

    CAS  PubMed  Article  Google Scholar 

  51. 51.

    Lee, D. & Glimcher, M. Three-dimensional spatial relationship between the collagen fibrils and the inorganic calcium phosphate crystals of pickerel (Americanus americanus) and herring (Clupea harengus) bone. J. Mol. Biol. 217, 487–501 (1991).

    CAS  PubMed  Article  Google Scholar 

  52. 52.

    Fratzl, P., Fratzl-Zelman, N. & Klaushofer, K. Collagen packing and mineralization—an X-ray-scattering investigation of Turkey leg tendon. Biophys. J. 64, 260–266 (1993).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  53. 53.

    Hartgerink, J. D., Beniash, E. & Stupp, S. I. Self-assembly and mineralization of peptide-amphiphile nanofibers. Science 294, 1684–1688 (2001).

    ADS  CAS  PubMed  Article  Google Scholar 

  54. 54.

    He, W.-X., Rajasekharan, A. K., Tehrani-Bagha, A. R. & Andersson, M. Mesoscopically ordered bone–mimetic nanocomposites. Adv. Mater. 27, 2260–2264 (2015).

    CAS  PubMed  Article  Google Scholar 

  55. 55.

    Qi, Y., Cheng, Z., Ye, Z., Zhu, H. & Aparicio, C. Bioinspired mineralization with hydroxyapatite and hierarchical naturally aligned nanofibrillar cellulose. ACS Appl. Mater. Interfaces 11, 27598–27604 (2019).

    CAS  PubMed  Article  Google Scholar 

  56. 56.

    Li, Y. & Aparicio, C. Discerning the subfibrillar structure of mineralized collagen fibrils: a model for the ultrastructure of bone. PLoS ONE 8, e76782 (2013).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  57. 57.

    Ostwald, W. Studien über die Bildung und Umwandlung fester Körper. Z. Phys. Chem. 22, 289–330 (1897).

    CAS  Google Scholar 

  58. 58.

    Von Euw, S. et al. Solid-state phase transformation and self-assembly of amorphous nanoparticles into higher-order mineral structures. J. Am. Chem. Soc. 142, 12811–12825 (2020).

    Article  CAS  Google Scholar 

  59. 59.

    Orgel, J. P. & Madhurapantula, R. S. A structural prospective for collagen receptors such as DDR and their binding of the collagen fibril. Biochim. Biophys. Acta Mol. Cell Res. 1866, 118478 (2019).

    CAS  PubMed  Article  Google Scholar 

  60. 60.

    Arsenault, A. L. Crystal-collagen relationships in calcified turkey leg tendons visualized by selected-area dark field electron microscopy. Calcif. Tissue Int. 43, 202–212 (1988).

    CAS  PubMed  Article  Google Scholar 

  61. 61.

    Schwarcz, H., Binkley, D., Luo, L. & Grandfield, K. A search for apatite crystals in the gap zone of collagen fibrils in bone using dark-field illumination. Bone 135, 115304 (2020).

    CAS  PubMed  Article  Google Scholar 

  62. 62.

    Greer, H. F., Liu, M.-H., Mou, C.-Y. & Zhou, W. Dipole field driven morphology evolution in biomimetic vaterite. CrystEngComm 18, 1585–1599 (2016).

    CAS  Article  Google Scholar 

  63. 63.

    de Leeuw, N. H. & Parker, S. C. Surface structure and morphology of calcium carbonate polymorphs calcite, aragonite, and vaterite: an atomistic approach. J. Phys. Chem. B 102, 2914–2922 (1998).

    Article  Google Scholar 

  64. 64.

    Chen, L., Jacquet, R., Lowder, E. & Landis, W. J. Refinement of collagen–mineral interaction: a possible role for osteocalcin in apatite crystal nucleation, growth and development. Bone 71, 7–16 (2015).

    CAS  PubMed  Article  Google Scholar 

  65. 65.

    Addadi, L., Moradian, J., Shay, E., Maroudas, N. & Weiner, S. A chemical model for the cooperation of sulfates and carboxylates in calcite crystal nucleation: relevance to biomineralization. Proc. Natl Acad. Sci. USA 84, 2732–2736 (1987).

    ADS  CAS  PubMed  Article  Google Scholar 

  66. 66.

    Smeets, P. J., Cho, K. R., Kempen, R. G., Sommerdijk, N. A. & De Yoreo, J. Calcium carbonate nucleation driven by ion binding in a biomimetic matrix revealed by in situ electron microscopy. Nat. Mater. 14, 394 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

  67. 67.

    Davies, E. et al. Citrate bridges between mineral platelets in bone. Proc. Natl Acad. Sci. USA 111, E1354–E1363 (2014).

    CAS  PubMed  Article  Google Scholar 

  68. 68.

    Gorski, J. P. Biomineralization of bone: a fresh view of the roles of non-collagenous proteins. Front. Biosci. 16, 2598 (2011).

    CAS  Article  Google Scholar 

  69. 69.

    Liu, Y. et al. Hierarchical and non-hierarchical mineralisation of collagen. Biomaterials 32, 1291–1300 (2011).

    ADS  PubMed  Article  CAS  Google Scholar 

  70. 70.

    Ziv, V., Wagner, H. & Weiner, S. Microstructure–microhardness relations in parallel-fibered and lamellar bone. Bone 18, 417–428 (1996).

    CAS  PubMed  Article  Google Scholar 

  71. 71.

    Liu, Y. et al. Hierarchical intrafibrillar nanocarbonated apatite assembly improves the nanomechanics and cytocompatibility of mineralized collagen. Adv. Funct. Mater. 23, 1404–1411 (2013).

    CAS  Article  Google Scholar 

  72. 72.

    Bayerlein, B. et al. Self-similar mesostructure evolution of the growing mollusc shell reminiscent of thermodynamically driven grain growth. Nat. Mater. 13, 1102–1107 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  73. 73.

    Sommerdijk, N. A. & Cusack, M. Biomineralization: crystals competing for space. Nat. Mater. 13, 1078 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  74. 74.

    Reznikov, N., Shahar, R. & Weiner, S. Three-dimensional structure of human lamellar bone: the presence of two different materials and new insights into the hierarchical organization. Bone 59, 93–104 (2014).

    CAS  PubMed  Article  Google Scholar 

  75. 75.

    Seligman, A. M., Wasserkrug, H. L. & Hanker, J. S. A new staining method (OTO) for enhancing contrast of lipid-containing membranes and droplets in osmium tetroxide-fixed tissue with osmiophilic thiocarbohydrazide (TCH). J. Cell. Biol. 30, 424 (1966).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  76. 76.

    Pettersen, E. F. et al. UCSF Chimera—a visualization system for exploratory research and analysis. J. Comput. Chem. 25, 1605–1612 (2004).

    CAS  PubMed  Article  Google Scholar 

  77. 77.

    Traub, W. & Piez, K. A. The chemistry and structure of collagen. Adv. Protein Chem. 25, 243–352 (1971).

    CAS  PubMed  Article  Google Scholar 

  78. 78.

    Bras, W. et al. Recent experiments on a small-angle/wide-angle X-ray scattering beam line at the ESRF. J. Appl. Crystallogr. 36, 791–794 (2003).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

We thank Dr. Koen Pieterse (Institute for Complex Molecular Systems, Eindhoven University of Technology, the Netherlands (TU/e)) for his help with data analysis, Zaf Khalil (Department of Chemical Engineering and Chemistry, TU/e) for his help with bone sample preparation and Andreas J. Fijneman (Department of Chemical Engineering and Chemistry, TU/e) for helpful discussions. We thank Dr. Elena Macias (Radboud Institute for Molecular Life Sciences) for her critical review of the manuscript. This work was supported by the Netherlands Organization for Scientific Research (NWO) through VICI (F.N., M.J.M.W.) and Toppunt (Y.X.) grants to N.S. E.D.E. and N.S. were supported by the European Research Council (ERC) Advanced Investigator grant (H2020-ERC-2017-ADV-788982-COLMIN). Y.X. was supported by the Marie Curie Individual Fellowship (H2020-MSAC-IF-2019- 885795-PolyTEM), and A.A. was supported by the Marie Curie Individual Fellowship (H2020-MSCA-IF-2017-794296-SUPERMIN). E.D.E. and A.A. were also partially supported by an NWO Echo Grant. W.B.’s contribution is partially based upon work supported by Oak Ridge National Laboratory, managed by UT-Battelle, LLC, for the U.S. Department of Energy. The work was further supported by an Engineering and Physical Sciences (EPSRC) Platform Grant to F.C.M. (EP/N002423/1), an EPSRC Program Grant (EP/R018820/1) which funds the Crystallization in the Real World Consortium (F.C.M.), and a Leverhulme research project grant (F.C.M., N.S., and Y.X.). NWO is also gratefully acknowledged for making access to the DUBBLE ESRF beamline possible. This project was also supported by grant 9 P41 GM103622 from the National Institute of General Medical Sciences of the National Institutes of Health. We also thank the University of Edinburgh for financial support.

Author information

Affiliations

Authors

Contributions

F.C.M. and N.S. originated and co-supervised this project. W.H.N., E.D.E., A.A., and Y.X. prepared and analyzed the bone sample. Y.X., C.O., and H.F. performed the analysis of collagen structure. Y.X. and F.N. performed the collagen mineralization experiments and TEM study. E.D.E., M.J.M.W., F.N., and Y.X. performed analysis of TEM data. B.C. helped with CaCO3 mineralization experiments and together with F.N., D.H.-M., G.P., and W.B. performed the in situ X-ray study. P.H.H.B. provided support on TEM studies. H.F. supervised TEM data analysis. J.P.R.O.O. supervised the analysis of collagen structure. A.A. supervised bone sample preparation. Y.X., F.C.M., and N.S. co-wrote the manuscript. All the authors have read and commented on the manuscript.

Corresponding authors

Correspondence to Joseph P. R. O. Orgel or Fiona C. Meldrum or Nico Sommerdijk.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Elia Beniash, Laurie Gower and Paul Simon for their contribution to the peer review of this work. Peer reviewer reports are available

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Xu, Y., Nudelman, F., Eren, E.D. et al. Intermolecular channels direct crystal orientation in mineralized collagen. Nat Commun 11, 5068 (2020). https://doi.org/10.1038/s41467-020-18846-2

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing