Organic-to-inorganic structural chirality transfer in a 2D hybrid perovskite and impact on Rashba-Dresselhaus spin-orbit coupling

Abstract

Translation of chirality and asymmetry across structural motifs and length scales plays a fundamental role in nature, enabling unique functionalities in contexts ranging from biological systems to synthetic materials. Here, we introduce a structural chirality transfer across the organic–inorganic interface in two-dimensional hybrid perovskites using appropriate chiral organic cations. The preferred molecular configuration of the chiral spacer cations, R-(+)- or S-(−)-1-(1-naphthyl)ethylammonium and their asymmetric hydrogen-bonding interactions with lead bromide-based layers cause symmetry-breaking helical distortions in the inorganic layers, otherwise absent when employing a racemic mixture of organic spacers. First-principles modeling predicts a substantial bulk Rashba-Dresselhaus spin-splitting in the inorganic-derived conduction band with opposite spin textures between R- and S-hybrids due to the broken inversion symmetry and strong spin-orbit coupling. The ability to break symmetry using chirality transfer from one structural unit to another provides a synthetic design paradigm for emergent properties, including Rashba-Dresselhaus spin-polarization for hybrid perovskite spintronics and related applications.

Introduction

Inversion asymmetry is at the heart of various physical properties of inorganic systems. Especially in conjunction with relativistic effects such as spin–orbit coupling (SOC), it engenders rich condensed matter phenomena, such as the quantum spin Hall effect1, topological surface states, and Rashba/Dresselhaus coupling2,3,4 in non-magnetic systems as well as exotic spin topologies including chiral domain walls5 and skyrmions6 in magnetic systems, with promising applications in electronic, magnetic, and spintronic technologies7,8. One potential route for inducing asymmetry relies on chirality, a fundamental design feature based on lack of inversion and mirror symmetries that permeates all hierarchies of molecular organization and assembly9. Transmission of chiral information and asymmetry across structural motifs and length scales has a vital role in biological as well as synthetic systems. The chirality transfer is often expressed as cooperative self-assembly of chiral organic monomers into supramolecular10 and macroscopic chiral aggregates11 or templated chiral helicity in otherwise achiral molecules12 through intra- and inter-molecular interactions. While such chirality transfer phenomena have been mainly established in organic systems, the ability to exploit the influence of chiral organic molecules to structurally modify an extended inorganic lattice and thereby engender emergent properties based on crystal asymmetry remains underexplored.

In this context, two-dimensional (2D) layered hybrid organic–inorganic perovskites (HOIPs) provide ideal platforms to study structural chirality transfer across organic–inorganic interfaces. They exhibit crystallographically well-ordered structures with alternating organic and inorganic layers, coupled with broad flexibility in the choice of organic cations and inherent sensitivity of properties to structural tuning. 2D HOIPs are currently in the spotlight owing to their chemical stability, structural versatility as well as exceptional photophysical properties, including large exciton binding energies, high photoluminescence quantum efficiency, strong exciton–phonon couplings and tailorable optoelectronic properties for light-emitting and energy-related applications13,14,15. Chiral organic cations have been recently employed in 2D HOIPs, resulting in ferroelectricity16 and chiroptical properties such as circular dichroism and circularly polarized luminescence17,18. Notably, the inorganic-related chiroptical activity in these already reported HOIP systems is evidently an optically induced phenomenon caused by dipolar interactions with chiral cations19,20, and thus, the chain of evidence for structural chirality/asymmetry transfer to the inorganic layers remains incomplete if solely based on chiroptical spectroscopies. Indeed, we find (as will be discussed later) that the introduction of a chiral organic cation in 2D HOIPs does not necessarily imply a significant degree of structural chirality within the inorganic framework.

Here, we demonstrate a structural chirality transfer across the organic–inorganic interface in a prototypical 2D HOIP, R-(+)- or S-(−)-1-(1-naphthyl)ethylammonium lead bromide, wherein the enantiopure chiral spacers induce symmetry-breaking helical distortions in the inorganic framework via asymmetric hydrogen-bonding interactions, otherwise absent when employing a racemic mixture of organic spacers. As a result, the P21 chiral symmetry of the organic sublattice “transfers” to the inorganic sublattice. The use of chiral organic spacers imparts added functionalities to the semiconducting inorganic framework including (a) distinct circular dichroism (CD) of excitonic absorption in the [PbBr4]2− layers, induced by net crystallographic handedness and dipolar interactions with polarizable \(\pi\) clouds of chiral organic cations, and (b) Rashba–Dresselhaus (RD) spin-splitting of otherwise two-fold spin-degenerate electronic bands as a consequence of the broken inversion symmetry (resulting from organic-to-inorganic chirality transfer) and strong SOC. While the chiroptical activity enables detection of circularly polarized light in practical applications21, the RD effect (the focus of the current study) is actively pursued in the field of spintronics8,22,23, which relies on the spin degrees of freedom. In the present chiral HOIP, hybrid density-functional theory (DFT) calculations are used to predict a substantial bulk RD splitting of the inorganic-derived conduction band, which is absent in the racemic analog.

Results

Structural chirality transfer in 2D hybrid organic–inorganic perovskites

Single crystals of R/S/racemic-NPB (NPB = 1-(1-naphthyl)ethylammonium lead bromide) were grown by slowly cooling an aqueous HBr solution of stoichiometric amounts of PbBr2 and R/S/racemic-NEA (NEA = 1-(1-naphthyl)ethylamine) (see “Methods” section). All three compounds crystallize as 2D HOIPs, with anionic [PbBr4]2− layers of corner-sharing PbBr6 octahedra separated by bilayers of NEA+ spacer cations (Fig. 1a–c). Racemic-NPB crystallizes in the centrosymmetric P21/c space group, whereas R- and S-NPB adopt the chiral P21 space group (see Supplementary Table 1 for crystallographic data). In all three compounds, any set of four interconnected PbBr6 octahedra forms a puckered square pattern due to the tilting of adjacent octahedra (Fig. 1d–f), causing equatorial Pb–Br–Pb bond angles to deviate significantly from the ideal 180° for an undistorted perovskite sheet. Whereas racemic-NPB features symmetric tilting distortions, resulting in a single Pb–Br–Pb angle of 152° (Fig. 1f), both R- and S-NPB exhibit significant tilting asymmetry with two widely disparate equatorial Pb–Br–Pb angles of 143° and 157°, corresponding to two distinct equatorial Br atoms (denoted with purple and red spheres, respectively, in Fig. 1d, e).

Fig. 1: Structural characteristics of chiral- and racemic-NPB.
figure1

ac Schematic X-ray single-crystal structures of a R-NPB, b S-NPB, and c racemic-NPB. d, e In-plane views of [PbBr4]2− layers in d R-NPB and e S-NPB show two different equatorial Pb–Br–Pb bond angles of 143° and 157° associated with two different Br atoms, denoted as purple and red spheres, respectively. The axial Br atoms are omitted for clarity. Opposite and dissimilar out-of-plane helical distortions (indicated by small and big curved arrows) of red and purple Br atoms can be seen from the spiraling of corresponding Pb–Br–Pb bonds (marked by thicker black and gray lines in d and e) around the 21-screw axes (red and purple arrows). f Racemic-NPB shows a single equatorial Pb–Br–Pb bond angle of 152° with no out-of-plane distortions of Br atoms. Also shown in df are the organic terminal -CH-NH3+ groups, represented as solid and shaded dumbbells for the upper and lower organic layers, respectively. gi, Hydrogen-bonding interactions between the equatorial Br atoms and NEA+ cations in g R-NPB, h S-NPB, and i racemic-NPB. The axial Br atoms and associated interactions are omitted for clarity. The out-of-plane distortions of equatorial Br atoms in d and e are clearly seen in g and h for R-NPB and S-NPB, respectively. Green, red/purple, black, blue, and pink spheres denote Pb, Br, C, N, and H atoms, respectively.

The equatorial bond angle disparity in chiral NPB likely follows from asymmetric hydrogen (H)-bonding associated with the in-plane Br atoms of the inorganic [PbBr4]2− layers (for H-bonding distances and angles, see Supplementary Table 2). As can be seen in Supplementary Fig. 1, each axial (i.e., out-of-plane) Br atom forms the same number of H-bonds in both chiral- and racemic-NPB, i.e., two H-bonds with nearest H-atoms of NH3+ groups in the adjacent organic layer, as commonly found among 2D HOIPs. Thus, in all three compounds (racemic and chiral), H-bonding to axial Br atoms is symmetric for opposite sides of the same inorganic layer. In contrast, for the chiral NPB, when considering the two distinct equatorial (i.e., in-plane) Br atoms within a given inorganic layer (Fig. 1g, h), each purple-labeled Br atom H-bonds with both NH3+ (H2N-H…Br = 2.92 Å) and α-CH3 (H2C-H…Br = 2.83 Å) groups of the NEA+ spacer on one side of the inorganic layer, but with only the NH3+ (H2N-H…Br = 2.87 Å) group of the NEA+ spacer on the opposite side of the inorganic layer. For the red-labeled Br atoms, the corresponding H…Br contacts exceed the van der Waals limit of 3.05 Å, suggesting substantially reduced H-bonding interactions. The equatorial Br atoms thus incur out-of-plane distortions that propagate helically about the 21-screw axis parallel to the b-axis (Fig. 1d, e); the spirals formed by the bonds that connect the two types of Br via adjoining Pb atoms (also indicated in Fig. 1d, e) exhibit opposite yet dissimilar helicities, and the ensuing net crystallographic helicity of Br distortions in R-NPB (Fig. 1d) is opposite to that in S-NPB (Fig. 1e). In the racemic-NPB, this type of helical distortion does not occur. Here, each of the equatorial Br atoms H-bonds to a single NH3+ (H2N-H…Br = 2.59 Å) group on either side of the inorganic layer, with all the equatorial Br atoms being coplanar (Fig. 1f, i). The peculiar H-bonding found for the equatorial Br atoms in chiral NPB derives from the specific organic tethering group configuration. On either side of the inorganic layer, terminal -CH-NH3+ bonds of chiral NEA+ cations are oriented nearly parallel with respect to one another and slightly offset across the inorganic layer (Fig. 1d, e). In racemic-NPB, the -CH-NH3+ bonds orient in a more typical crisscross fashion (Fig. 1f), leading to a hydrogen-bonding pattern frequently observed among 2D HOIPs.

The structural symmetry determined using PLATON’s24 ADDSYM tool yields the same P21 chiral space group for mutually isolated organic and inorganic frameworks in R- and S-NPB (Supplementary Fig. 2). The chiral NEA+ spacers assemble into a P21 sublattice and transfer the P21 chiral symmetry to the inorganic sublattice (Pb and Br atoms in polar C1 point group) by inducing in-plane tilting asymmetry and out-of-plane helical 21 screw distortions, as discussed above. Wilson statistics and cumulative intensity distributions of X-ray reflections both confirm the noncentrosymmetric inorganic layers in chiral NPB (Supplementary Figs. 3 and 4). In contrast, the [PbBr4]2− framework in the racemic-NPB is centrosymmetric (P21/c), with Pb and Br atoms in the Ci point group. Bond length distortions for R-, S-, and racemic-NPB, \({\mathrm{{\Delta} }}d = \left( {\frac{1}{6}} \right){\sum} {\left( {d_i - d} \right)^2} /d^2\) (where \(d_i\) denotes the six Pb–Br bond lengths and \(d\) is the mean Pb–Br bond length), as well as the bond angle variances, \(\sigma ^2 = \mathop {\sum}\nolimits_{i = 1}^{12} {\left( {\theta _i - 90} \right)^2} /11\) (where \(\theta _i\) denotes the individual cis Br–Pb–Br bond angles), quantify the distortions of individual PbBr6 octahedra relative to an undistorted octahedron (Supplementary Table 3). Both \({\mathrm{{\Delta} }}d\) and \(\sigma ^2\) values for chiral R- and S-NPB substantially exceed those for racemic-NPB (Supplementary Table 3) and are among the largest values reported for the <100>-oriented 2D lead bromide HOIP class (Supplementary Fig. 5). Such substantial symmetry-breaking distortions in the inorganic framework, owing to the chirality transfer from the chiral NEA+ spacer cations, are crucial for determining the associated electronic structure and lead to an emergent Rashba–Dresselhaus spin-splitting of electronic bands (discussed below) in chiral R- and S-NPB, otherwise absent when employing a racemic mixture of NEA+ spacers.

Critically, individual symmetries of organic and inorganic sublattices can differ, although the use of chiral spacer cations generally entails a global chiral crystallographic description of the HOIP. We underscore the above point by comparing to the previously reported 2D lead iodide HOIP comprising chiral cations, i.e., R/S-1-methyl benzylammonium lead iodide (MBPI)18,25. Temperature-dependent (298, 200, and 100 K) single-crystal X-ray diffraction for S-MBPI as an example indicates a nominally centrosymmetric Pnma (i.e., P 21/n 21/m 21/a) space group for the inorganic framework despite an overall chiral P212121 description for the hybrid. Note that the inorganic framework scatters X-rays more strongly than the organic component, and the positions of Pb and I atoms, therefore, predominantly dictate the space group determination by crystallographic indexing based on Wilson statistics; a <E2 − 1> value close to 1 is obtained from Wilson statistics, suggesting a centrosymmetric space group (Supplementary Fig. 3). The cumulative intensity distribution plot also points to a centrosymmetric space group (Supplementary Fig. 4). However, structure refinement in the Pnma space group is precluded by the chiral organic cations, thereby requiring an alternative P212121 chiral space group, as inferred from the observed total systematic absences. The global structure of S-MBPI could be successfully refined in the P212121 chiral space group at all three temperatures investigated (Supplementary Table 4), in agreement with an earlier report on its 298 K structure25. However, despite the overall chiral space group, our post-refinement symmetry analysis using PLATON suggests a Pnma space group for the isolated [PbI4]2− framework (i.e., excluding organic cations) (Supplementary Fig. 2). In contrast to S-NPB and R-NPB, the observations for S-MBPI clearly point to a predominantly centrosymmetric inorganic [PbI4]2− framework to within the default positional/angular tolerance criteria used in the PLATON analysis.

Importantly, S-MBPI lacks the asymmetric H-bonding interactions or helical distortions found in chiral NPB and exhibits nearly flat perovskite layers, similar to racemic-NPB (Supplementary Fig. 6). The in-plane tilting distortion is relatively smaller, with equatorial Pb–Br–Pb angles of 151° and 157°, and the computed σ2 value is about half the value found in chiral NPB (Supplementary Table 3). We ascribe the organic-to-inorganic structural chirality transfer in NPB and a lack of detectable transfer in MBPI, at least in part, to the relative strengths of associated H-bonding interactions [e.g., ∆H(H…Br) > ∆H(H…I)] that mainly determine the templating influence of chiral organic spacers. Our attempts to grow single crystals of an iodide analog of NPB led to a 1D hybrid comprising a face-sharing [Pb2I6]2− framework (Supplementary Fig. 7 and Supplementary Table 5). On the other hand, the chiral lead bromide analog of MBPI readily crystallizes into a similar 1D [Pb2Br6]2− hybrid25, although the target 2D phase could be stabilized in thin films17. While we cannot directly compare bromide/iodide analogs for the same chiral organic cation (from a single-crystal structure standpoint), the key point is that detectable organic-to-inorganic structural chirality transfer does not inevitably follow from the use of a chiral cation within the 2D HOIPs, but additionally relies on the detailed H-bonding interactions that couple the organic and inorganic sublattices. Furthermore, as seen below, the degree of structural chirality transfer (and associated structural distortions in the lead halide framework) is found to have a significant impact on the electronic structure of the resulting HOIP.

Circular dichroism and photoluminescence

Thin films of R-, S- and racemic-NPB were deposited by spin-coating DMF solutions of corresponding single crystals (see “Methods” section and Supplementary Fig. 8). The linear absorption spectra for R-, S- and racemic-NPB films all reveal a sharp resonance centered at ~390 nm that corresponds to excitons confined within the 2D lead bromide layers (Fig. 2a). The excitonic bands in R- and S-NPB are blue-shifted by ~30 meV relative to racemic-NPB, due to more pronounced structural distortions in the former26. Circular dichroism (CD) measures differential absorption of left and right circularly polarized light passing through a chiral system and can establish the absolute configuration (i.e., handedness) of chiral enantiomers. Quantum theory relates the CD intensity in a chiral molecule to the imaginary part (Im) of the dot product of electric (\(\vec \mu _{12}\)) and magnetic (\(\vec m_{21}\)) dipole transition moments20:

$${\mathrm{CD}}_{{\mathrm{molecule}}} \propto {\mathrm{Im}}\left[ {\vec \mu _{12}.\vec m_{21}} \right],$$
(1)

where the indices 1 and 2 denote, respectively, the initial and final chiral molecule quantum states. For a non-zero CD signal, \(\vec \mu _{12}\) and \(\vec m_{21}\) cannot be orthogonal, a condition satisfied only by chiral point groups devoid of inversion and mirror symmetries. The CD spectra from R- and S-NPB thin films (Fig. 2b) change signs due to their opposite absolute configurations but are otherwise identical within the experimental error, while racemic-NPB, as expected, shows a negligible CD signal. The distinct CD bands centered at 393 nm for R- and S-NPB correspond to the excitonic absorption in Fig. 2a. The linear absorption spectrum at 50 K for the chiral NPB reveals a 2D-type band-edge absorption onset at 3.54 eV that appears as a step-like feature preceding the exciton band (Supplementary Fig. 9). Consequently, we assign the higher energy CD band centered at 351 nm for chiral NPB as due to transitions into the continuum (i.e., above bandgap) states. It is noteworthy that the CD spectrum reveals these band-edge-like transitions even at room temperature, while they are not resolved in the room-temperature linear absorption spectrum due to the inhomogeneous broadening of the exciton absorption band (Fig. 2a). The exciton binding energy (Eb) of ~0.38 eV, estimated from the energy difference between excitonic and continuum CD bands, matches the value obtained from the 50 K linear absorption (Supplementary Fig. 9).

Fig. 2: Optical properties of chiral- and racemic-NPB.
figure2

a UV–Vis linear absorption spectra and b circular dichroism (CD) spectra recorded at room-temperature for thin films of racemic-, R- and S-NPB. c, d Photoluminescence spectra from single crystals of racemic-, R- and S-NPB obtained at c room-temperature using a 325 nm laser source, and at d 7 K using a 266 nm laser source; FE and STE denote free excitons and self-trapped excitons, respectively.

The opposite CD signals in the inorganic-derived part of the spectra for chiral R- and S-NPB can, in part, arise from the crystallographic handedness induced by structural chirality transfer. However, R- and S-MBPI also exhibit inorganic-derived excitonic and interband CD bands despite their nominally centrosymmetric lead iodide layers, as discussed above18. Indeed, the frontier orbitals at the conduction and valence band edges derive from the inorganic framework for all the 2D HOIPs studied here (Fig. 3f–h), and no significant direct contribution arises from chiral organic cations to the associated band edge or excitonic transitions. The CD bands in chiral NPB can originate from the coupling of dipole transition moments in the inorganic framework and the chiral organic spacer cations (the chiral screening medium surrounding the inorganic framework), as previously observed in inorganic semiconductor nanocrystals capped with chiral surface ligands19. The same dipolar interactions with the chiral, organic screening medium can induce excitonic CD signals in R- and S-MBPI despite their nominally centrosymmetric inorganic layers18,27, thus suggesting that an induced CD does not always imply substantial chirality transfer from organic to inorganic layers.

Fig. 3: RD spin-splitting in chiral NPB.
figure3

a Schematic representation of a two-fold spin-degenerate electronic band in a conventional semiconductor. b, c Spin-polarized sub-bands (red: down spin; blue: up spin) separated in k-space due to the SOC and inversion asymmetry along one dimension of an RD semiconductor. \(E^ +\) and \(E^ -\) denote the inner and outer spin-polarized branches created by the RD spin-splitting. ∆E denotes the energy difference between the two branches at the characteristic momentum (k0), and \(E_{{\mathrm{RD}}}\) is the characteristic RD energy. d A representative unit cell of the relaxed S-NPB structure in real space and e, its Brillouin zone showing the k-path in reciprocal space used for band plotting in fh. For the theoretical structures, cell axes were chosen to be consistent for racemic, R- and S-NPB such that the stacking direction is always along the a-direction, and the inorganic layers are parallel to the b–c plane. fh, The computed DFT+HSE06 electronic band structures of f racemic-NPB, g S-NPB, and h R-NPB shown along selected k-paths. The atomic contributions to the electronic continuum bands are identified for Pb (magenta), Br (green), and organic-derived (black) states. The two-fold spin-degenerate lowest conduction band in f racemic-NPB splits into upper and lower branches in both g S-NPB and h R-NPB mainly along the Γ–Z direction of reciprocal space due to inversion asymmetry in the [PbBr4]2− perovskite layers of S-NPB and R-NPB. Full band structures of R-, S-, and racemic-NPB for all the k-paths are presented in Supplementary Fig. 13.

The room-temperature photoluminescence (PL) spectra measured from single crystals (Fig. 2c) reveal a moderate excitonic emission (centered at 402 nm) for racemic-NPB, which is quenched in the chiral R- and S-NPB. In addition, all three HOIPs exhibit a weak, spectrally shifted broad PL band in the 450–800 nm range, which significantly increases in intensity at 7 K (Fig. 2d). Such a broad PL band may be attributed to exciton self-trapping within excited state transient lattice distortions (i.e., polaron formation), mediated by strong electron-phonon coupling and defects induced during crystal growth28. The PL behavior in chiral- vs. racemic-NPB indeed agrees with a previous empirical correlation—i.e., that the intensity ratio of narrow free-excitonic emission to broad self-trapped excitonic emission in <100>-oriented lead bromide HOIPs decreases with increasing structural distortions in the ground state29. Despite the substantial distortions in chiral NPB (Supplementary Fig. 5), the relatively weak room-temperature broad PL emission suggests competing non-radiative decay channels for the self-trapped excitons30. The lack of free-excitonic emission in chiral NPB is, in part, ascribed to asymmetry-induced changes in the electronic band structures, as discussed below.

Rashba–Dresselhaus spin–orbit coupling and conduction band splitting

Spin–orbit coupling (SOC) describes a relativistic effect, relevant especially for heavy atoms. Pb-based HOIPs are gaining substantial interest in spintronics owing to a strong SOC induced by the heavy Pb constituent and structural flexibility provided by the organic cation31,32. In Pb-containing HOIPs, the SOC-induced energy splitting of the Pb-6p-derived conduction band (CB) is of the order of eV33,34,35. The SOC can be rationalized approximately as the Zeeman-like interaction of electron spin with an effective magnetic field experienced by an electron (in its rest frame) moving in an electric field7. In non-magnetic systems, SOC conserves time-reversal symmetry (TRS), i.e., E↑(k) = E↓(−k), where E is the single-particle (electron or hole) band energy, k represents the crystal momentum (Bloch wavevector), and the arrows correspond to states of s = +1/2 and −1/2 character. TRS, in combination with inversion symmetry [i.e., E↑(k) = E↑(−k)], leads to a two-fold spin degeneracy for the up (↑) and down (↓) spins (Fig. 3a). When the inversion symmetry is broken, a strong SOC lifts this two-fold spin degeneracy. The emergence of the ensuing dispersion relations near the CB minimum along one dimension of an RD system is schematically illustrated in Fig. 3a–c. Without SOC, the CB minimum is located at the Γ-point in this illustration. Upon including SOC, the energy bands about the CB minimum assume the general form2,32:

$$E^ \pm ({\mathrm{k}}) = \frac{{\hbar ^2{\mathbf{k}}^2}}{{2m}} \pm \lambda |{\mathbf{k}}|,$$
(2)

where k is the electron wavevector, and \(\lambda\) is the Rashba (Dresselhaus) coupling parameter for a pure Rashba (Dresselhaus) SOC effect. \(E^ +\) and \(E^ -\) are called the spin-polarized sub-branches (Fig. 3b, c). Owing to the k-space separation of electronic bands (Fig. 3b), forward and backward moving carriers have opposite spins at the band extrema (spin-momentum locking). This effect was first noted by Dresselhaus in strained zinc-blende III–V semiconductors3, then by Rashba in Wurtzite structures4 and later generalized by Bychkov and Rashba for 2D electron gases (2DEG)2. In this paper, we use the combined term, RD splitting, throughout since Rashba and Dresselhaus SOC effects can occur in 2D systems either exclusively or simultaneously with characteristic spin textures for each case32. A detailed discussion of the RD effect for quasi-2D systems was recently given by Even and coworkers32. Opposite spin textures associated with the spin-split sub-bands in opposite momentum directions (Fig. 3b) due to the RD SOC effect lead to circular photogalvanic effects36 and enable interconversion between charge and spin currents (by Edelstein and inverse Edelstein effects)22,23, of interest for spintronic technologies.

To examine the effect of chirality-induced inversion asymmetry on the electronic structures of chiral R- and S-NPB, we have computed the associated electronic band structures using DFT-based first-principles calculations with the all-electron electronic structure code FHI-aims37. The code is a high-precision implementation of current density-functional methods38,39, including an implementation of SOC that has been successfully benchmarked40 and used to calculate band structures of complex HOIPs in previous works35,41,42,43 (see “Methods” section for more details). The input structures for the 2D HOIPs were obtained from our single-crystal X-ray experiments. Geometry optimizations were conducted using dispersion-corrected semilocal DFT (PBE44 generalized-gradient approximation including the Tkatchenko–Scheffler (TS) van der Waals correction45, PBE+TS for short); computationally relaxed lattice parameters fall within 2.5% of the experimental values, while associated bond angles fall within 7° (Supplementary Table 6 and Supplementary Figs. 1012). Figure 3f–h shows the electronic band structures of racemic-, R- and S-NPB calculated with DFT-HSE06+SOC and decomposed into Pb- (purple), Br- (green) and organic-derived (black) states. For all three structures, the frontier orbitals at the band edges derive from the inorganic sublattice so that a type Ib quantum well results35. In agreement with other Pb-based hybrid perovskites46, the conduction band maximum (CBM) and valence band minimum (VBM) consist mainly of Pb- and halogen-derived states, respectively. The calculated bandgaps are the same for R- and S-NPB (2.97 eV) and slightly higher than the predicted bandgap of 2.78 eV for racemic-NPB.

In line with the RD picture, chiral R- and S-NPB exhibit characteristic splitting of an otherwise two-fold degenerate conduction band (CB) away from the Γ-point (Fig. 3g, h), whereas the centrosymmetric racemic-NPB does not show CB splitting (Fig. 3f). Broken inversion symmetry in the chiral lead bromide layers results in CB splitting into upper and lower spin-polarized branches along the Γ–Z path. This k-path coincides with the in-plane [100] crystallographic direction in the 2D [PbBr4]2− layers (see Fig. 1d, e), along which the local geometry fluctuates as the equatorial Pb–Br–Pb bond angles alternate between 143° and 157° (Fig. 1d, e). The lack of band dispersion along the Γ-X path (i.e., coinciding with the out-of-plane [001] layer-stacking direction, which is perpendicular to the 2D inorganic plane in Fig. 1a, b) is in accord with the confinement and localization of inorganic-derived states in the out-of-plane direction. The Γ–Y path coincides with the in-plane [010] crystallographic direction (Fig. 1d, e) along which the same kind of Br atoms— i.e., either purple- or red-type— and hence the associated Pb–Br–Pb bond angles propagate by 21-screw translational symmetry (Fig. 1d, e). So, the C2 rotational axis for chiral NPB (corresponding to P21 space group) points along the Γ–Y path, thereby explaining the minimal spin-splitting along this direction. This configuration contrasts with conventional 2D Rashba systems such as inorganic quantum well (QW) heterostructures32,47 or BiTeI48, which exhibit the CnV symmetry and where the Cn (n = 2, 3) axis coincides with the stacking direction. Therefore, as suggested in earlier work on quasi-2D systems by Even and coworkers32, the situation in chiral NPB corresponds to a 1D problem with dominant SOC contributions only along the [100] crystallographic direction (Fig. 1d, e).

We describe an effective RD coupling parameter, \(\lambda _{{\mathrm{RD}}} = \frac{{{\Delta} E}}{{2{\mathbf{k}}_0}}\), where \({\mathbf{k}}_0\) denotes the momentum-offset from the Γ-point and \({\Delta} E\) is the energy difference between the upper (\(E^ +\)) and lower (\(E^ -\)) conduction band branches at \({\mathbf{k}}_0\). \(E_{{\mathrm{RD}}}\) is the characteristic energy difference between \({\mathbf{k}} = {\mathbf{k}}_0\) (i.e., the bottom of the parabola) and \({\mathbf{k}} = 0\) (i.e., Dirac point where the two parabolas intersect), which for the exact parabolic dispersion, would amount to one-fourth of \({\Delta} E\) (Fig. 3c)32. Based on our DFT-HSE06+SOC band structure calculations, \({\mathrm{{\Delta} }}E^{{\mathrm{{\Gamma} }} - {\mathrm{Y}}} = 0.01\) eV and \({\mathrm{{\Delta} }}E^{{\mathrm{{\Gamma} }} - {\mathrm{Z}}} = 0.22\) eV, with corresponding RD coupling parameters of \(\lambda _{{\mathrm{RD}}}^{{\mathrm{{\Gamma} }} - {\mathrm{Y}}} = 0.28\) eV·Å and \(\lambda _{{\mathrm{RD}}}^{{\mathrm{{\Gamma} }} - {\mathrm{Z}}} = 1.52\) eV·Å for CBs in both R- and S-NPB along the Γ–Y and Γ–Z paths, respectively. The predicted \(\lambda _{{\mathrm{RD}}}^{{\mathrm{{\Gamma} }} - {\mathrm{Z}}}\) of 1.52 eV·Å and estimated \(E_{{\mathrm{RD}}}\) (\(\sim \!{\Delta} E/4\))32,49 of 55 meV in chiral NPB are orders of magnitude higher than those found in QW heterostructures such as InAlAs/InGaAs (\(\lambda \approx 0.07\) eV·Å; \(E_{{\mathrm{RD}}} \approx 1\) meV)50. These values are indeed similar to those recently observed in the 2D phenethylammonium lead iodide HOIP using optical spectroscopies36,49, although the precise origin of the bulk inversion asymmetry is still unclear given its centrosymmetric X-ray crystal structure with a symmetrical disposition of in-plane bond angles and relatively low distortions (in contrast to chiral NPB)26. We speculate that an instantaneous band splitting in phenethylammonium lead iodide can arise from dynamic structural changes induced by temperature and/or photoexcited coherent phonon modes, as recently proposed for methylammonium lead iodide 3D perovskite51,52. Nonetheless, in contrast with the substantially lower RD splitting predicted for noncentrosymmetric lead iodide-based HOIPs (\(E_{{\mathrm{RD}}} \ll 10\,{\mathrm{meV}}\))53, we ascribe the relatively large in-plane RD CB spin-splitting in the chiral NPB compounds to a considerable asymmetry in the in-plane PbBr6 octahedral tilting distortions—i.e., widely disparate Pb–Br–Pb bond angles (Fig. 1d, e)—likely inducing large electric fields and thus large RD SOC, in agreement with our simulations of model structures with distorted vs. undistorted inorganic layers (Supplementary Fig. 14). Furthermore, the opposite chirality in the inorganic layers leads to opposite spin textures for the spin sub-bands between R-NPB and S-NPB, thus enabling a unique control of RD spin polarization using the chiral organic cations (Supplementary Fig. 15).

In R- and S-NPB, the resulting CB minima due to RD splitting are offset in k-space from the VB maxima (indicated by black arrows in Fig. 3g, h), resulting in a momentum-forbidden indirect bandgap close to Γ-point. In contrast, the bandgap in racemic-NPB is direct and momentum-allowed (Fig. 3f). We thus speculate that the quenched free-excitonic PL emission in the chiral NPB compounds may arise in part due to the indirect transition caused by substantial RD CB splitting52,54. The frontier VB in NPB systems is primarily comprised of Br-derived states (Fig. 3f–h) and, owing to the low (compared to Pb) SOC effects associated with the lighter Br, RD VB spin-splitting is expectedly small in chiral NPB (Fig. 3g, h)34. For comparison, we have also computed the DFT-HSE06+SOC electronic band structure of chiral S-MBPI (Supplementary Fig. 16), which, however, shows much lower CB splitting of \({\mathrm{{\Delta} }}E^{{\mathrm{{\Gamma} }} - {\mathrm{Z}}}\) =0.025 eV due to the previously discussed nearly centrosymmetric [PbI4]2− layers, thus reflecting the essential prerequisite of substantial local symmetry-breaking for a large RD spin-splitting.

Discussion

2D HOIPs exhibiting quantum and dielectric confinement of carriers are potential RD candidates49, in analogy with the inorganic 2DEGs, provided the perovskite layers lack inversion symmetry. Most of the known 2D HOIPs, however, adopt centrosymmetric crystal structures, lacking the bulk and/or site inversion asymmetries that are prerequisite to the RD SOC effect (neglecting dynamical effects)32,55. Our present work shows that the use of enantiopure chiral building blocks provides a pathway to induce inversion asymmetry in otherwise centrosymmetric HOIPs, reflecting an additional degree of freedom in HOIP design. Notably, the surrounding chiral cations, the presence of which induces a chiroptical response, need not always entail a significant structural chirality within the inorganic layers; chirality can be structurally transferred to the inorganic layers primarily when mediated by suitably strong hydrogen-bonding interactions with chiral cations, as exemplified by the present chiral NPB systems. Moreover, while specific achiral organic cations might also induce symmetry-breaking distortions in the inorganic layers, the ability to control the associated handedness of these distortions (and associated spin texture in the electronic bands) is made possible by employing chiral organic cations. These structural insights, coupled with theoretical findings in our work, enable the discovery and design of an emerging class of multifunctional hybrid systems with an amalgam of semiconducting, chiroptical, and spin-dependent properties. Indeed, the combination of chiral induced spin selectivity of chiral organic molecules56,57,58,59,60,61,62 and an intrinsic RD spin-splitting in the inorganic framework is a hitherto unexplored aspect unique to 2D chiral HOIPs and might have practical implications in future HOIP-based spintronics. Further, the structural chirality transfer and ensuing lowering of symmetry within the inorganic sublattice opens up a gateway to other emergent properties such as nonlinear light-matter interactions and piezo-/ferroelectricity, not just in 2D HOIPs but also in related diverse low-dimensional metal halide hybrids.

Methods

Materials

(S)-(−)-1-(1-naphthyl)ethylamine (≥99%), (R)-(+)-1-(1-naphthyl)ethylamine (≥99%), 1-(1-naphthyl)ethylamine (98%), (S)-(−)-α-methyl benzylamine (98%), hydrobromic acid (48 wt.% in H2O, ≥ 99.99%), and hydroiodic acid (57 wt. % in H2O, distilled, stabilized, 99.95%) were purchased from Sigma Aldrich and used without further purification.

Synthesis

For growing single crystals of chiral R- or S-NPB, stoichiometric amounts of PbBr2 (45 mg, 0.12 mmol), and R- or S-1-(1-naphthyl)ethylamine (39 µL, 0.24 mmol) were first dissolved in a mixture of 0.5 ml aq. HBr and 1.2 mL deionized water in a sealed vial with an N2 atmosphere at 95 °C. The hot solution was slowly cooled to room temperature over 48 hr. Single crystals of racemic-NPB were grown in a similar way from a solution of racemic 1-(1-naphthyl)ethylamine (39 µL, 0.24 mmol) and PbBr2 (45 mg, 0.12 mmol) in 0.5 mL of aq. HBr and 1.2 mL methanol. The as-obtained colorless plate-like crystals were filtered, washed with diethyl ether, and vacuum-dried. Single crystals of 1D S-NEA2Pb2I6 (S-NPI) were obtained by cooling a hot aq. HI solution of S-1-(1-naphthyl)ethylamine (0.25 mmol) and PbI2 (0.125 mmol) from 90 °C to room-temperature in 48 h. The as-obtained pale-yellow, needle-like crystals were filtered, washed with diethyl ether, and vacuum-dried. Single crystals of S-MBPI were grown by slowly evaporating a solution of (S)-(−)-α-methyl benzylamine (25 µL, 0.2 mmol) and PbI2 (45 mg, 0.1 mmol) in 1 mL aq. HI and 1 mL methanol at room temperature under N2 atmosphere. The as-obtained orange-red, needle-like crystals were filtered, washed with copious amounts of diethyl ether and vacuum-dried. To fabricate thin films, 0.2 M solutions of R/S/racemic-NPB single crystals in DMF were spin-cast on glass substrates (precleaned by ultrasonication in IPA for 10 min followed by Ar-O2 plasma treatment for 10 min) at a spin speed of 3000 rpm for 30 s and annealed at 120 °C for 10 min in an N2 glove box. Similarly, thin films of S-MBPI were spin-coated from 0.2 M DMF solution and annealed at 100 °C for 5 min in an N2 glove box.

Characterization

Single-crystal X-ray diffraction (XRD) was performed at 298 K on a Rigaku XtaLAB Synergy-S diffractometer (Mo-K\(\alpha\) radiation, λ = 0.710 Å; X-ray tube operating at 50 kV and 30 mA) for the chiral R- and S-NPB and S-MBPI single crystals and on a Bruker APEX II CCD diffractometer (Mo-K\(\alpha\) radiation, λ = 0.710 Å; X-ray tube operating at 50 kV and 30 mA) for the racemic-NPB and S-NPI. For S-MBPI, X-ray diffraction data were collected subsequently at 298, 200, and 100 K using an Oxford Cryosystem for temperature control. Structure solutions were obtained by SHELXS direct methods and refined using SHELXL least-squares method within the Olex2 crystallographic package. A post-refinement analysis for missing symmetry has been carried out for both full structures and isolated inorganic frameworks (i.e., after manually deleting the organic component) using the ADDSYM tool implemented in the PLATON program. Powder XRD was carried out for thin films using a PANalytical Empyrean powder X-ray diffractometer (CuKα radiation) operating at 45 kV and 40 mA. Room-temperature circular dichroism (CD) spectra were measured for thin films (on glass substrates) of R/S/racemic-NPB using an AVIV 420 CD spectrophotometer with 1 nm s−1 scan speed. UV–Vis absorption spectra for thin films were obtained at room temperature using a Shimadzu UV-3600 UV–Vis-NIR spectrophotometer. For low-temperature absorption measurements, thin films of R-, S- and racemic-NPB deposited on sapphire substrates were transferred into a He Cryostat and cooled down to low temperatures using a closed-cycle refrigerator. An incandescent light source from a Xenon lamp dispersed through a monochromator was focused on the sample and detected by an ultraviolet-enhanced silicon photodetector. Transmission spectra were measured using a lock-in amplifier, and optical densities were subsequently calculated. The PL emission from single crystals was recorded at room temperature on a Horiba Jobin Yvon LabRam ARAMIS spectrophotometer using a HeCd (325 nm) laser as an excitation source, 1800 gr/min diffraction grating, and an InGaAs detector. For 7 K PL measurements on single crystals, a solid-state laser operating at 266 nm was used as the pump excitation with an oblique incidence angle of 45°, and the PL emission was collected in reflection geometry and measured with a fiber spectrometer (Ocean Optics USB4000). Thin crystals of NPB were cooled down in a cryostat with optical windows (Cryocooler Model SRDK-205).

First-principles calculations

The all-electron electronic structure code FHI-aims37 was employed to perform the first-principles density-functional theory (DFT) calculations. All calculations are based on numeric atom-centered orbital (NAO) basis sets. The massively parallel simulations were assisted by the ELSI infrastructure63,64 and ELPA eigenvalue solver65. Full relaxation of lattice parameters and atomic coordinates for all systems was performed with the semilocal Perdew–Burke–Ernzerhof (PBE) functional44 plus the Tkatchenko–Scheffler (TS) pairwise dispersion scheme for van der Waals (vdW) interactions45. FHI-aims “tight” numerical defaults were used, and the k-point grid was set to \((2 \times 4 \times 4)\). In the experimental structures, the layer-stacking direction is along the c-axis for R- and S-NPB while it is along a-axis for the racemic-NPB (Supplementary Table 1). For the calculations, we chose consistent labeling of crystal axes for all the structures so that the stacking direction is always along a-axis while the b- and c-axes (c > b) span the plane of inorganic layers (see Fig. 3d, e). Hence, the short dimension of the k-space grid corresponds to the long, out-of-plane lattice direction in real space. Regarding energy band structures, it is well-known that DFT-GGA suffers from the electronic delocalization error66 that can lead to too small bandgaps or wrong ordering of electronic levels67. As the lowest-energy crystal structure and electronic structure are different observables, we here used spin–orbit coupled hybrid DFT on top of the PBE+TS relaxed atomic structures for the description of electronic properties, offering a good compromise between affordability in terms of computational cost and known accuracy for HOIPs, as we have shown in past work35,41,42,43,68, compared to more computationally involved GW69. We employed the Heyd–Scuseria–Ernzerhof (HSE06) hybrid density-functional70,71 (with 25% Hartree–Fock exchange and a screening parameter of 0.11 bohr−1) plus second-variation non-self-consistent spin–orbit coupling (SOC)40 within FHI-aims using “intermediate” numerical settings and again a \((2 \times 4 \times 4)\) k-point grid to predict the character of frontier orbitals and band structure properties.

Spin texture implementation and validation

Spin texture based on SOC calculations can help understand the spin-polarization behavior of individual bands. Spin texture can be defined as the expectation value of the vector of Pauli matrices \(\sigma _i\) and this functionality has here been implemented in the FHI-aims code37:

$$\sigma _{i,n{\mathbf{k}}} = \left \langle {{\Psi} _{n{\mathbf{k}}}} \right|\sigma _i\left| {{\Psi} _{n{\mathbf{k}}}} \right \rangle,\,i = x,y,z.$$
(3)

Here, \({\Psi} _{n{\mathbf{k}}}\) is the nth crystal orbital associated with the crystal momentum k. It is a two-component spinor, which can be expanded using N spatial Bloch basis functions \(\varphi _{\mu {\mathbf{k}}}\):

$${\Psi} _{n{\mathbf{k}}} = \mathop {\sum }\limits_{\mu = 1}^N \left( {C_{\mu n}^\alpha \varphi _{\mu {\mathbf{k}}}^\alpha + C_{\mu n}^\beta \varphi _{\mu {\mathbf{k}}}^\beta } \right).$$
(4)

The quantities C are the expansion coefficients and the two spinor components associated with each basis function are denoted as α and β. \(\varphi _{\mu {\mathbf{k}}}^\alpha\) and \(\varphi _{\mu {\mathbf{k}}}^\beta\) are expressed in vector form as follows.

$$\varphi _{\mu {\mathbf{k}}}^\alpha = \left( {\begin{array}{*{20}{c}} {\varphi _{\mu {\mathbf{k}}}} \\ 0 \end{array}} \right),\,\varphi _{\mu {\mathbf{k}}}^\beta = \left( {\begin{array}{*{20}{c}} 0 \\ {\varphi _{\mu {\mathbf{k}}}} \end{array}} \right).$$
(5)

They are Bloch basis functions and, summing over individual unit cells and appropriate phase factors, can be further expressed in terms of localized atom-centered orbital basis functions37,40. The final expression for the expectation values of the three Pauli matrices can be obtained using the overlap matrix between basis functions μ and \(\nu, S_{\mu \nu } = \langle \varphi _{\mu {\mathbf{k}}}{\mathrm{|}}\varphi _{\nu {\mathbf{k}}}\rangle\):

$$\begin{array}{l}\langle \sigma _{x,n{\mathbf{k}}}\rangle = \langle \sigma _{x,n{\mathbf{k}}}\rangle _{\alpha \alpha } + \langle \sigma _{x,n{\mathbf{k}}} \rangle _{\beta \beta } + \langle \sigma _{x,n{\mathbf{k}}}\rangle_{\alpha \beta } + \langle \sigma _{x,n{\mathbf{k}}}\rangle_{\beta \alpha } \\ = \mathop {\sum }\limits_{\mu = 1}^N \mathop {\sum }\limits_{\nu = 1}^N C_{\mu n}^{\alpha \ast }C_{\nu n}^\beta S_{\mu \nu } + \mathop {\sum }\limits_{\mu = 1}^N \mathop {\sum }\limits_{\nu = 1}^N C_{\mu n}^{\beta \ast }C_{\nu n}^\alpha S_{\mu \nu },\end{array}$$
(6a)

in which the \(\langle \sigma _{x,n{\mathbf{k}}}\rangle _{\alpha \alpha }\) and \(\langle \sigma _{x,n{\mathbf{k}}}\rangle _{\beta \beta }\) terms both vanish. Similarly, we have:

$$\langle \sigma _{y,n{\mathbf{k}}} \rangle = - i\mathop {\sum }\limits_{\mu = 1}^N \mathop {\sum }\limits_{\nu = 1}^N C_{\mu n}^{\alpha \ast }C_{\nu n}^\beta S_{\mu \nu } + i\mathop {\sum }\limits_{\mu = 1}^N \mathop {\sum }\limits_{\nu = 1}^N C_{\mu n}^{\beta \ast }C_{\nu n}^\alpha S_{\mu \nu },$$
(6b)
$$\langle \sigma _{z,n{\mathbf{k}}} \rangle = \mathop {\sum }\limits_{\mu = 1}^N \mathop {\sum }\limits_{\nu = 1}^N C_{\mu n}^{\alpha \ast }C_{\nu n}^\alpha S_{\mu \nu } - \mathop {\sum }\limits_{\mu = 1}^N \mathop {\sum }\limits_{\nu = 1}^N C_{\mu n}^{\beta \ast }C_{\nu n}^\beta S_{\mu \nu }.$$
(6c)

We benchmarked the spin texture functionality within our FHI-aims code against results for several reference systems found in the literature, calculated using other codes. The implementation details of SOC vary between different codes, for instance, due to the use of non-self-consistent vs. self-consistent SOC40 or due to the use of a pseudopotential vs. all-electron approach. We thus expect a qualitative, but not necessarily an exactly quantitative match to literature results from different codes. In FHI-aims, SOC calculations are performed non-self-consistently40, based on an all-electron approach that makes no shape approximation to the potential. An underlying atomic zero-order regular approximation (atomic ZORA) treatment is used to include scalar relativistic effects in the kinetic energy expression, following the specific Eqs. (55) and (56) in ref. 37. Three benchmark systems were chosen (Supplementary Figs. 1719).

For the Au (111) surface, we compared with results published using the OpenMX code72,73,74. In Supplementary Fig. 17a, the bands showing Rashba splitting around the Г point are indexed as the 241st and 242nd bands (corresponding to the 55th and 56th bands calculated by OpenMX)74. The calculated spin textures show exactly opposite spin polarizations perpendicular to the momentum k in the kx – ky plane, in qualitative agreement between FHI-aims and OpenMX (Supplementary Fig. 17b, c). The precise locations of the Fermi surfaces in reciprocal space vary somewhat, which we ascribe to differences in SOC and pseudopotential (OpenMX) vs. all-electron (FHI-aims) treatments.

For the 2D hybrid organic–inorganic perovskite (4-BrBzA)2PbI453, the spin textures for the inner and outer branches of the valence and conduction bands were calculated using FHI-aims and compared with results shown in reference53, which were calculated using the VASP code (Supplementary Fig. 18a, b). The spin textures show similar shapes and features.

A third test case, IrBiSe, shows a giant bulk-type Dresselhaus splitting. Along the symmetry line X (0.5, 0, 0) → Г (0, 0, 0), the valence band spin polarization should be parallel to the k-direction75. This is confirmed in Supplementary Fig. 19a, b, in which both \(\sigma _y\) and \(\sigma _z\) vanish, and only \(\sigma _x\) shows non-zero values. In contrast, along X (0.5, 0, 0) → M (0.5, 0.5, 0), the z component of the spin polarization vanishes.

Data availability

Additional data supporting the findings of this work are provided as a Supplementary Information file. Single-crystal structures in this work are available in The Cambridge Crystallographic Data Center (CCDC) database: Racemic-NPB: 2015614 [https://doi.org/10.5517/ccdc.csd.cc25ndt2]; S-NPB: 2015618 [https://doi.org/10.5517/ccdc.csd.cc25ndy6]; R-NPB: 2015620 [https://doi.org/10.5517/ccdc.csd.cc25nf09]; S-MBPI_298 K: 2015617 [https://doi.org/10.5517/ccdc.csd.cc25ndx5]; S-MBPI_200 K: 2015616 [https://doi.org/10.5517/ccdc.csd.cc25ndw4]; S-MBPI_100 K: 2015619 [https://doi.org/10.5517/ccdc.csd.cc25ndz7]; S-NPI: 2015615 [https://doi.org/10.5517/ccdc.csd.cc25ndv3]. Single-crystal data are also available in the HybriD3 material database and can be accessed using the search fields: “racemic-NEA2PbBr4” (Racemic-NPB), “S-NEA2PbBr4” (S-NPB), “R-NEA2PbBr4” (R-NPB), “S-MBA2PbI4” (S-MBPI) and “S-NEA2Pb2I6” (S-NPI). Relaxed geometries and computed band structures can also be accessed from the HybriD3 materials database: “racemic-NEA2PbBr4 [https://materials.hybrid3.duke.edu/materials/dataset/1634]”, “S-NEA2PbBr4 [https://materials.hybrid3.duke.edu/materials/dataset/1630]”, “R-NEA2PbBr4 [https://materials.hybrid3.duke.edu/materials/dataset/1632]”, “S-MBA2PbI4 [https://materials.hybrid3.duke.edu/materials/dataset/1636]”. The whole computational data set is also deposited in the NOMAD repository. Other relevant data can be obtained from the corresponding author or the first author upon reasonable request.

References

  1. 1.

    Bernevig, B. A., Hughes, T. L. & Zhang, S.-C. Quantum spin hall effect and topological phase transition in HgTe quantum wells. Science 314, 1757 (2006).

    ADS  CAS  PubMed  Google Scholar 

  2. 2.

    Bychkov, Y. A. & Rashba, E. I. Properties of a 2D electron gas with lifted spectral degeneracy. JETP Lett. 39, 78–81 (1984).

    ADS  Google Scholar 

  3. 3.

    Dresselhaus, G. Spin-orbit coupling effects in zinc blende structures. Phys. Rev. 100, 580–586 (1955).

    ADS  CAS  MATH  Google Scholar 

  4. 4.

    Rashba, E. I. Properties of semiconductors with an extremum loop. 1. Cyclotron and combinational resonance in a magnetic field perpendicular to the plane of the loop. Sov. Phys. Solid State 2, 1224–1238 (1960).

    Google Scholar 

  5. 5.

    Emori, S., Bauer, U., Ahn, S.-M., Martinez, E. & Beach, G. S. D. Current-driven dynamics of chiral ferromagnetic domain walls. Nat. Mater. 12, 611 (2013).

    ADS  CAS  Google Scholar 

  6. 6.

    Romming, N. et al. Writing and deleting single magnetic skyrmions. Science 341, 636 (2013).

    ADS  CAS  PubMed  Google Scholar 

  7. 7.

    Soumyanarayanan, A., Reyren, N., Fert, A. & Panagopoulos, C. Emergent phenomena induced by spin–orbit coupling at surfaces and interfaces. Nature 539, 509 (2016).

    CAS  PubMed  Google Scholar 

  8. 8.

    Manchon, A., Koo, H. C., Nitta, J., Frolov, S. M. & Duine, R. A. New perspectives for Rashba spin–orbit coupling. Nat. Mater. 14, 871 (2015).

    ADS  CAS  PubMed  Google Scholar 

  9. 9.

    Morrow, S. M., Bissette, A. J. & Fletcher, S. P. Transmission of chirality through space and across length scales. Nat. Nanotechnol. 12, 410 (2017).

    ADS  CAS  PubMed  Google Scholar 

  10. 10.

    Liu, M., Zhang, L. & Wang, T. Supramolecular chirality in self-assembled systems. Chem. Rev. 115, 7304–7397 (2015).

    CAS  PubMed  Google Scholar 

  11. 11.

    Yang, Y. et al. Macroscopic helical chirality and self-motion of hierarchical self-assemblies induced by enantiomeric small molecules. Nat. Commun. 9, 3808 (2018).

    ADS  PubMed  PubMed Central  Google Scholar 

  12. 12.

    Yang, D., Duan, P., Zhang, L. & Liu, M. Chirality and energy transfer amplified circularly polarized luminescence in composite nanohelix. Nat. Commun. 8, 15727 (2017).

    ADS  CAS  PubMed  PubMed Central  Google Scholar 

  13. 13.

    Saparov, B. & Mitzi, D. B. Organic–inorganic perovskites: structural versatility for functional materials design. Chem. Rev. 116, 4558–4596 (2016).

    CAS  PubMed  Google Scholar 

  14. 14.

    Mao, L., Stoumpos, C. C. & Kanatzidis, M. G. Two-dimensional hybrid halide perovskites: principles and promises. J. Am. Chem. Soc. 141, 1171–1190 (2018).

    PubMed  Google Scholar 

  15. 15.

    Smith, M. D., Connor, B. A. & Karunadasa, H. I. Tuning the luminescence of layered halide perovskites. Chem. Rev. 119, 3104–3139 (2019).

    CAS  PubMed  Google Scholar 

  16. 16.

    Yang, C.-K. et al. The first 2D homochiral lead iodide perovskite ferroelectrics: [R- and S-1-(4-chlorophenyl)ethylammonium]2PbI4. Adv. Mater. 31, 1808088 (2019).

  17. 17.

    Long, G. et al. Spin control in reduced-dimensional chiral perovskites. Nat. Photonics 12, 528–533 (2018).

    ADS  CAS  Google Scholar 

  18. 18.

    Ma, J. et al. Chiral 2D perovskites with a high degree of circularly polarized photoluminescence. ACS Nano 13, 3659–3665 (2019).

    CAS  PubMed  Google Scholar 

  19. 19.

    Gao, X., Han, B., Yang, X. & Tang, Z. Perspective of chiral colloidal semiconductor nanocrystals: opportunity and challenge. J. Am. Chem. Soc. 141, 13700–13707 (2019).

    CAS  PubMed  Google Scholar 

  20. 20.

    Govorov, A. O., Fan, Z., Hernandez, P., Slocik, J. M. & Naik, R. R. Theory of circular dichroism of nanomaterials comprising chiral molecules and nanocrystals: plasmon enhancement, dipole interactions, and dielectric effects. Nano Lett. 10, 1374–1382 (2010).

    ADS  CAS  PubMed  Google Scholar 

  21. 21.

    Chen, C. et al. Circularly polarized light detection using chiral hybrid perovskite. Nat. Commun. 10, 1927 (2019).

    ADS  PubMed  PubMed Central  Google Scholar 

  22. 22.

    Nomura, A., Tashiro, T., Nakayama, H. & Ando, K. Temperature dependence of inverse Rashba-Edelstein effect at metallic interface. Appl. Phys. Lett. 106, 212403 (2015).

    ADS  Google Scholar 

  23. 23.

    Sánchez, J. C. R. et al. Spin-to-charge conversion using Rashba coupling at the interface between non-magnetic materials. Nat. Commun. 4, 2944 (2013).

    ADS  PubMed  Google Scholar 

  24. 24.

    Spek, A. L. Structure validation in chemical crystallography. Acta Cryst. D65, 148–155 (2009).

    Google Scholar 

  25. 25.

    Billing, D. G. & Lemmerer, A. Synthesis and crystal structures of inorganic–organic hybrids incorporating an aromatic amine with a chiral functional group. CrystEngComm 8, 686–695 (2006).

    CAS  Google Scholar 

  26. 26.

    Du, K.-Z. et al. Two-dimensional lead(II) halide-based hybrid perovskites templated by acene alkylamines: crystal structures, optical properties, and piezoelectricity. Inorg. Chem. 56, 9291–9302 (2017).

    CAS  PubMed  Google Scholar 

  27. 27.

    Ahn, J. et al. A new class of chiral semiconductors: chiral-organic-molecule-incorporating organic–inorganic hybrid perovskites. Mater. Horiz. 4, 851–856 (2017).

    CAS  Google Scholar 

  28. 28.

    Smith, M. D. & Karunadasa, H. I. White-Light Emission from Layered Halide Perovskites. Acc. Chem. Res. 51, 619–627 (2018).

    CAS  PubMed  Google Scholar 

  29. 29.

    Smith, M. D., Jaffe, A., Dohner, E. R., Lindenberg, A. M. & Karunadasa, H. I. Structural origins of broadband emission from layered Pb–Br hybrid perovskites. Chem. Sci. 8, 4497–4504 (2017).

    CAS  PubMed  PubMed Central  Google Scholar 

  30. 30.

    Wang, X. et al. Atomistic mechanism of broadband emission in metal halide perovskites. J. Phys. Chem. Lett. 10, 501–506 (2019).

    PubMed  Google Scholar 

  31. 31.

    Liao, K. et al. Spintronics of hybrid organic–inorganic perovskites: miraculous basis of integrated optoelectronic devices. Adv. Opt. Mater. 7, 1900350 (2019).

    Google Scholar 

  32. 32.

    Kepenekian, M. et al. Rashba and dresselhaus effects in hybrid organic–inorganic perovskites: from basics to devices. ACS Nano 9, 11557–11567 (2015).

    CAS  PubMed  Google Scholar 

  33. 33.

    Kuneš, J., Novák, P., Schmid, R., Blaha, P. & Schwarz, K. Electronic structure of fcc Th: spin-orbit calculation with 6p1/2 local orbital extension. Phys. Rev. B 64, 153102 (2001).

    ADS  Google Scholar 

  34. 34.

    Even, J., Pedesseau, L., Jancu, J.-M. & Katan, C. Importance of spin–orbit coupling in hybrid organic/inorganic perovskites for photovoltaic applications. J. Phys. Chem. Lett. 4, 2999–3005 (2013).

    CAS  Google Scholar 

  35. 35.

    Liu, C. et al. Tunable semiconductors: control over carrier states and excitations in layered hybrid organic-inorganic perovskites. Phy. Rev. Lett. 121, 146401 (2018).

    ADS  CAS  Google Scholar 

  36. 36.

    Liu, X. et al. Circular photogalvanic spectroscopy of Rashba splitting in 2D hybrid organic–inorganic perovskite multiple quantum wells. Nat. Commun. 11, 323 (2020).

    ADS  CAS  PubMed  PubMed Central  Google Scholar 

  37. 37.

    Blum, V. et al. Ab initio molecular simulations with numeric atom-centered orbitals. Comput. Phys. Commun. 180, 2175–2196 (2009).

    ADS  CAS  MATH  Google Scholar 

  38. 38.

    Jensen, S. R. et al. The elephant in the room of density functional theory calculations. J. Phys. Chem. Lett. 8, 1449–1457 (2017).

    CAS  PubMed  Google Scholar 

  39. 39.

    Lejaeghere, K. et al. Reproducibility in density functional theory calculations of solids. Science 351, aad3000 (2016).

    PubMed  Google Scholar 

  40. 40.

    Huhn, W. P. & Blum, V. One-hundred-three compound band-structure benchmark of post-self-consistent spin-orbit coupling treatments in density functional theory. Phys. Rev. Mater. 1, 033803 (2017).

    Google Scholar 

  41. 41.

    Jana, M. K. et al. A direct-bandgap 2D silver-bismuth iodide double perovskite: the structure-directing influence of an oligothiophene spacer cation. J. Am. Chem. Soc. 141, 7955 (2019).

    CAS  PubMed  Google Scholar 

  42. 42.

    Dunlap-Shohl, W. A. et al. Tunable internal quantum well alignment in rationally designed oligomer-based perovskite films deposited by resonant infrared matrix-assisted pulsed laser evaporation. Mater. Horiz. 6, 1707–1716 (2019).

    CAS  Google Scholar 

  43. 43.

    Jana, M. K. et al. Resolving rotational stacking disorder and electronic level alignment in a 2D oligothiophene-based lead iodide perovskite. Chem. Mater. 31, 8523–8532 (2019).

    CAS  Google Scholar 

  44. 44.

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  CAS  Google Scholar 

  45. 45.

    Tkatchenko, A. & Scheffler, M. Accurate molecular van der waals interactions from ground-state electron density and free-atom reference data. Phys. Rev. Lett. 102, 073005 (2009).

    ADS  PubMed  Google Scholar 

  46. 46.

    Katan, C., Mercier, N. & Even, J. Quantum and dielectric confinement effects in lower-dimensional hybrid perovskite semiconductors. Chem. Rev. 119, 3140–3192 (2019).

    CAS  PubMed  Google Scholar 

  47. 47.

    Lin, W. et al. Interface-based tuning of Rashba spin-orbit interaction in asymmetric oxide heterostructures with 3d electrons. Nat. Commun. 10, 3052 (2019).

    ADS  PubMed  PubMed Central  Google Scholar 

  48. 48.

    Ishizaka, K. et al. Giant Rashba-type spin splitting in bulk BiTeI. Nat. Mater. 10, 521 (2011).

    ADS  CAS  PubMed  Google Scholar 

  49. 49.

    Zhai, Y. et al. Giant Rashba splitting in 2D organic-inorganic halide perovskites measured by transient spectroscopies. Sci. Adv. 3, e1700704 (2017).

    ADS  PubMed  PubMed Central  Google Scholar 

  50. 50.

    Nitta, J., Akazaki, T., Takayanagi, H. & Enoki, T. Gate control of spin–orbit interaction in an inverted In0.53Ga0.47As/In0.52Al0.48As heterostructure. Phys. Rev. Lett. 78, 1335–1338 (1997).

    ADS  CAS  Google Scholar 

  51. 51.

    Schlipf, M. & Giustino, F. Dynamic Rashba-Dresselhaus Effect. Preprint at https://arxiv.org/abs/2004.10477 (2020).

  52. 52.

    Etienne, T., Mosconi, E. & De Angelis, F. Dynamical origin of the rashba effect in organohalide lead perovskites: a key to suppressed carrier recombination in perovskite solar cells? J. Phys. Chem. Lett. 7, 1638–1645 (2016).

    CAS  PubMed  Google Scholar 

  53. 53.

    Schmitt, T. et al. Control of crystal symmetry breaking with halogen substituted benzylammonium in layered hybrid metal-halide perovskites. J. Am. Chem. Soc. 142, 5060–5067 (2020).

    CAS  PubMed  Google Scholar 

  54. 54.

    Zheng, F., Tan, L. Z., Liu, S. & Rappe, A. M. Rashba Spin–Orbit coupling enhanced carrier lifetime in CH3NH3PbI3. Nano Lett. 15, 7794–7800 (2015).

    ADS  CAS  PubMed  Google Scholar 

  55. 55.

    Zhang, X., Liu, Q., Luo, J.-W., Freeman, A. J. & Zunger, A. Hidden spin polarization in inversion-symmetric bulk crystals. Nat. Phys. 10, 387 (2014).

    CAS  Google Scholar 

  56. 56.

    Naaman, R., Paltiel, Y. & Waldeck, D. H. Chiral molecules and the spin selectivity effect. J. Phys. Chem. Lett. 11, 3660–3666 (2020).

    CAS  PubMed  PubMed Central  Google Scholar 

  57. 57.

    Lu, H. et al. Spin-dependent charge transport through 2D chiral hybrid lead-iodide perovskites. Sci. Adv. 5, eaay0571 (2019).

    ADS  CAS  PubMed  PubMed Central  Google Scholar 

  58. 58.

    Long, G. et al. Chiral-perovskite optoelectronics. Nat. Rev. Mater. 5, 423–439 (2020).

    ADS  Google Scholar 

  59. 59.

    Abendroth, J. M. et al. Spin selectivity in photoinduced charge-transfer mediated by chiral molecules. ACS Nano 13, 4928–4946 (2019).

    CAS  PubMed  Google Scholar 

  60. 60.

    Ghosh, K. B. et al. Controlling chemical selectivity in electrocatalysis with chiral CuO-coated electrodes. J. Phys. Chem. C 123, 3024–3031 (2019).

    CAS  Google Scholar 

  61. 61.

    Abendroth, J. M. et al. Spin-dependent ionization of chiral molecular films. J. Am. Chem. Soc. 141, 3863–3874 (2019).

    CAS  PubMed  PubMed Central  Google Scholar 

  62. 62.

    Lu, H. et al. Highly distorted chiral two-dimensional tin iodide perovskites for spin polarized charge transport. J. Am. Chem. Soc. 142, 13030–13040 (2020).

    CAS  PubMed  Google Scholar 

  63. 63.

    Yu, V. W.-z et al. ELSI: a unified software interface for Kohn–Sham electronic structure solvers. Comput. Phys. Commun. 222, 267–285 (2018).

    ADS  CAS  Google Scholar 

  64. 64.

    Yu, V. W.-Z. et al. ELSI—an open infrastructure for electronic structure solvers. Comput. Phys. Commun. 256, 107459 (2020).

    MathSciNet  CAS  Google Scholar 

  65. 65.

    Marek, A. et al. The ELPA library: scalable parallel eigenvalue solutions for electronic structure theory and computational science. J. Phys. Condens. Matter 26, 213201 (2014).

    CAS  PubMed  Google Scholar 

  66. 66.

    Zheng, X., Liu, M., Johnson, E. R., Contreras-García, J. & Yang, W. Delocalization error of density-functional approximations: a distinct manifestation in hydrogen molecular chains. J. Chem. Phys. 137, 214106 (2012).

    ADS  PubMed  Google Scholar 

  67. 67.

    Egger, D. A., Liu, Z.-F., Neaton, J. B. & Kronik, L. Reliable energy level alignment at physisorbed molecule–metal interfaces from density functional theory. Nano Lett. 15, 2448–2455 (2015).

    ADS  CAS  PubMed  PubMed Central  Google Scholar 

  68. 68.

    Gao, Y. et al. Molecular engineering of organic–inorganic hybrid perovskites quantum wells. Nat. Chem. 11, 1151–1157 (2019).

    CAS  PubMed  Google Scholar 

  69. 69.

    Golze, D., Dvorak, M. & Rinke, P. The GW compendium: a practical guide to theoretical photoemission spectroscopy. Front. Chem. 7, 377 (2019).

  70. 70.

    Heyd, J., Scuseria, G. E. & Ernzerhof, M. Hybrid functionals based on a screened Coulomb potential. J. Chem. Phys. 118, 8207–8215 (2003).

    ADS  CAS  Google Scholar 

  71. 71.

    Heyd, J., Scuseria, G. E. & Ernzerhof, M. Erratum: “Hybrid functionals based on a screened Coulomb potential” [J. Chem. Phys. 118, 8207 (2003)]. J. Chem. Phys. 124, 219906 (2006).

    ADS  Google Scholar 

  72. 72.

    Kotaka, H., Ishii, F. & Saito, M. Rashba effect on the structure of the Bi one-bilayer film: fully relativistic first-principles calculation. Jpn. J. Appl. Phys. 52, 035204 (2013).

    ADS  Google Scholar 

  73. 73.

    Ozaki, T. & Kino, H. Efficient projector expansion for the ab initio LCAO method. Phys. Rev. B 72, 045121 (2005).

    ADS  Google Scholar 

  74. 74.

    FermiLoop. Calculation on a constant-energy level. http://www.openmx-square.org/openmx_man3.9/node176.html (2018).

  75. 75.

    Liu, Z. et al. A giant bulk-type dresselhaus splitting with 3D chiral spin texture in IrBiSe. Phys. Status Solidi RRL 14, 1900684 (2020).

    CAS  Google Scholar 

Download references

Acknowledgements

We acknowledge funding from the Center for Hybrid Organic-Inorganic Semiconductors for Energy (CHOISE), an Energy Frontier Research Center funded by the Office of Basic Energy Sciences, Office of Science within the U.S. Department of Energy (DOE) through contract number DE-AC36-08G028308. The views expressed in the article do not necessarily represent the views of the DOE or the U.S. Government. The U.S. Government retains and the publisher, by accepting the article for publication, acknowledges that the U.S. Government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish, or reproduce the published form of this work or allow others to do so, for U.S. Government purposes. C.L. was supported by the National Science Foundation under Award Number DMR-1729297. An award of computer time was provided by the Innovative and Novel Computational Impact on Theory and Experiment (INCITE) program. This research used resources of the Argonne Leadership Computing Facility, which is a DOE Office of Science User Facility supported under Contract DE-AC02-06CH11357. This research also used resources of the National Energy Research Scientific Computing Center (NERSC), a U.S. Department of Energy (DOE) Office of Science User Facility operated under Contract No. DE-AC02-05CH11231. S.M.J. thanks the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) for a postdoctoral fellowship, grant number 393196393. We thank Matthew C. Beard, Evan Lafalce, Sven Lidin, Tianyang Li, and Pete Sercel for useful discussions. We also thank Xinyi Lin for help with the graphical plotting of spin texture output.

Author information

Affiliations

Authors

Contributions

D.B.M. and M.K.J. conceived the idea and designed the experiments. M.K.J. and D.B.M. carried out the synthesis of HOIPs, determined their single-crystal X-ray structures, and performed UV–Vis linear absorption, photoluminescence, and circular dichroism measurements at room temperature. R.S., C.L., R.Z., S.M.J., and V.B. carried out first-principles DFT calculations. Z.V.V., H.L., and D.R. carried out low-temperature absorption and photoluminescence measurements. R.Z. and V.B. developed the spin texture implementation in the FHI-aims code. M.K.J., D.B.M., V.B., R.S., and S.M.J. prepared the manuscript and discussed it with other co-authors.

Corresponding author

Correspondence to David B. Mitzi.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Mikael Kepenekian and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Jana, M.K., Song, R., Liu, H. et al. Organic-to-inorganic structural chirality transfer in a 2D hybrid perovskite and impact on Rashba-Dresselhaus spin-orbit coupling. Nat Commun 11, 4699 (2020). https://doi.org/10.1038/s41467-020-18485-7

Download citation

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing