Abstract
Weyl semimetals exhibit unusual surface states and anomalous transport phenomena. It is hard to manipulate the band structure topology of specific Weyl materials. Topological transport phenomena usually appear at very low temperatures, which sets challenges for applications. In this work, we demonstrate the band topology modification via a weak magnetic field in a ferromagnetic Weyl semimetal candidate, Co_{2}MnAl, at room temperature. We observe a tunable, giant anomalous Hall effect (AHE) induced by the transition involving Weyl points and nodal rings. The AHE conductivity is as large as that of a 3D quantum AHE, with the Hall angle (Θ^{H}) reaching a record value (\(\tan {\Theta }^{H}=0.21\)) at the room temperature among magnetic conductors. Furthermore, we propose a material recipe to generate large AHE by gaping nodal rings without requiring Weyl points. Our work reveals an intrinsically magnetic platform to explore the interplay between magnetic dynamics and topological physics for developing spintronic devices.
Similar content being viewed by others
Introduction
The Weyl semimetal (WSM)^{1,2,3,4,5,6,7} is characterized by the linear bandcrossing points, called Weyl points, which exhibits monopoletype structure of the Berry curvature^{8,9}, leading to many exotic properties, such as the Fermi arc surface states^{1}, the chiral anomaly effect^{10,11}, and the anomalous Hall effect (AHE)^{12,13}. This topological phase has been discovered in materials such as TaAs^{14,15,16,17,18} and MoTe_{2}^{19,20,21,22} recently. In these materials, once the crystal is formed, their positions and energies of Weyl points are usually predetermined by material parameters, including the crystal structure and spin–orbit coupling (SOC), and can hardly be manipulated freely.
A Weyl point is robust in the sense it does not require any symmetry protection except the lattice translation. Inside a mirror plane that prohibits the Berrycurvature monopole, the Weyl point disappears, while 1D nodal lines may emerge due to the mirror symmetry^{23,24,25}. The nodal line displays a π Zak–Berry phase accumulated along a loop circling the nodal line, which induces Shockleylike^{26,27} surface states (called drumhead surface states^{28}). However, the nodal line exhibits zero Berry curvature in its vicinity and thus does not generate an AHE. If the mirror symmetry is broken, the nodal line gets gapped out and evolves into a pair of Weyl points (e.g., ref. ^{29}). The topology change can be directly probed by the AHE or observed in other topologyinduced phenomena. Therefore, the rotation of the magnetization orientation, which sensitively switches the mirror symmetry in a ferromagnet, provides a powerful tool to tune the topological band structure.
Although there have been several reported/predicted magnetic WSMs, few of them are appropriate for tuning the band structure topology via magnetic field. For the antiferromagnetic WSMs Mn_{3}Sn and its sister compound Mn_{3}Ge^{30,31,32,33,34}, in spite of their AHE varying with the rotation of spins within the spin easy plane, it remains unclear how their Weyl points and nodal lines (if they exist) evolve because of the complexity in the band structure. Co_{3}Sn_{2}S_{2} was reported to be a layered ferromagnetic (FM) WSM^{35,36,37,38,39}, which presents only Weyl points near the Fermi energy. Since its magnetization favors only the outofplane direction with the Curie temperature at 177 K, the band tuning by magnetization is challenging, which is similar to the case of a recently reported FM nodal line semimetal Fe_{3}GeTe_{2}^{40}. Recently, Cobased Heusler alloy compounds Co_{2}XZ (X=V, Zr, Nb, Ti, Mn, Hf; Z=Si, Ge, Sn, Ga and Al), previously known as half metallic ferromagnets, were predicted to host FM WSM phases^{41,42,43,44,45,46,47}. Since many of these materials are soft ferromagnets with their Curie temperatures far above room temperature, a weak external magnetic field can easily drive their magnetization to rotate in a wide temperature range. Hence, these materials provide ideal platforms to tune the band structure topology.
Although Co_{2}XZ allows for many different element combinations, experimental studies on their possible exotic properties induced by the expected WSM states are sparse, which is possibly due to the difficulty of the single crystal growth of this family of materials. Uptodate, Co_{2}MnGa is the only member that was reported to have distinct properties associated with the FM WSM state, that is, a giant AHE and anomalous Nernst effect^{48,49}. The band structure calculations show that Co_{2}MnGa as well as other Co_{2}XZ members have both Weyl points and nodal rings, and the giant AHE in these materials is generally believed to originate from Weyl points^{42,43,46,48,50}, with the anomalous Hall conductivity (AHC) being proportional to the separation of Weyl points. In theory, the largest possible Weyl point separation is the Brillouin size, which should induce the quantized AHC, that is, a 3D quantum AHE (QAHE). How can a magnetic WSM reach the 3D QAHE or giant AHE? What is the recipe to find such materials? Answers to these questions are not only of fundamental importance, but also likely leads to technological applications.
In this study, we give clues to these questions through the study of AHE of a Heusler alloy Co_{2}MnAl. This compound has attracted much attention due to its potential applications in spintronics^{51} and Hall sensors^{52,53}, as well as its recent prediction of FM WSM^{42}. Co_{2}MnAl possesses several structural phases with different disorder types, including L2_{1} (Mn, Al ordered), B2 (Mn, Al disordered), DO_{3} (Co, Mn disordered), A2 (Co, Mn, Al disordered)^{52}, and only the L2_{1} phase with the cubic space group of \(Fm\overline{3}m\) was predicted to host the FM WSM phase. However, synthesis of the L2_{1} phase has been challenging. All previous studies on this material were based on either polycrystalline or thin film samples with the B2 phase. Our recent success in growing Co_{2}MnAl single crystals with the L2_{1} phase has enabled us to observe its fascinating properties originating from the band topology. We found that this material exhibits very large AHC, up to 1300 Ω^{−1} cm^{−1} at room temperature; more noticeably, its room temperature anomalous Hall angle (AHA) Θ^{H} reaches a new record value among all magnetic conductors, with \(\tan\,{\Theta }^{\mathrm{H}}=0.21\). Furthermore, its AHE can be tuned by rotation of the magnetization axis as expected. From the comparison between our experimental results and theoretical calculations, we found that the gapped nodal rings induce large Berry curvature, which is responsible for the observed giant AHE. The consistency between our experiments and theory suggests a new mechanism of creating a large AHE by nodal ring’s gap opening; through this mechanism, an AHC as large as that of a 3D QAHE can be reached. This mechanism is distinct from the previous understanding of the AHE originating from Weyl points for Co_{2}MnGa and similar materials.
Results
Characterization of single crystals
The Co_{2}MnAl single crystals used in this study were grown using floatingzone (FZ) technique (see the “Methods” section). Figure 1b shows an optical image of typical crystals. As shown in Fig. 1a, in the L2_{1} phase, Mn and Al are ordered, which is manifested by the (111) diffraction spot/peak in an electron/Xray diffraction pattern according to previous studies^{54}. From our electron diffraction analyses, we have indeed observed the (111) diffraction spot in the electron diffraction pattern taken along the [110] zone axis (Fig. 1d), indicating that our Co_{2}MnAl crystals surely have the L2_{1} structure phase. This is further corroborated by scanning transmission electron microscopy (STEM) imaging shown in Fig. 1c, where the periodic, alternating distribution of Mn and Al (left inset to Fig. 1b) can be seen clearly from the atomic intensity line due to Zcontrast. Furthermore, we have also used the highangle annular darkfield (HAADF) STEM technology to check the sample homogeneity, which confirmed that uniform L2_{1} phase is formed throughout the entire sample.
The magnetic properties of Co_{2}MnAl single crystals were characterized through magnetization M measurements. Figure 1e shows the isothermal magnetization data at 2 and 400 , measured with the magnetic field applied parallel and perpendicular to the (001)/(111) plane, respectively. Field sweep measurements of M reveal small magnetic hysteresis, and the remnant magnetization is ~0.1 and 0.2μ_{B} per formula unit, respectively, for B ⊥ (001) and B ∥ (111) at 2 and 400 K (see the insets to Fig. 2e). These data are consistent with the previous report that Co_{2}MnAl is a soft ferromagnet, with the saturation moment M_{s} of ~4.2 ± 0.2μ_{B} per formula^{54}. The small decrease of M_{s} from 2 to 400 K suggests that its Curie temperature is far above room temperature, which cannot be probed in our superconducting quantum interference device (SQUID) magnetometer. The previously reported T_{c} for this material is 726 K^{54}. Moreover, our magnetization data also reveal its FM properties are anisotropic and the (111) plane is the easy spin plane.
AHE measurement
We have performed Hall resistivity ρ_{xy} measurements on the Co_{2}MnAl samples with the electric current applied to the (001), (010), and (111) planes, respectively. Figure 2a presents the field dependence of ρ_{xy} in the 10–300 K temperature ranges for two typical samples with I ∥ (001) and I ∥ (111). In general, ρ_{xy} of an FM conductor can be expressed as ρ_{xy} = R_{H}B + 4πR_{s}M, where R_{H}B represents normal Hall contribution due to Lorentz effect (R_{H}, Hall coefficient) and 4πR_{s}M is anomalous Hall contribution \({\rho }_{{xy}}^{A}\). As seen in Fig. 2a, ρ_{xy} shows a similar magnetic field dependence as the isothermal magnetization shown in Fig. 1e, indicating that the anomalous Hall contribution (proportional to M) is dominant and the normal contribution is very small and estimated to be 0.3–3% of ρ_{xy} in the 2–9 T field range, where M is saturated. \({\rho }_{{xy}}^{A}\) at room temperature shows large values, ~17.9 μΩcm for I ∥ (001) and 36.9 μΩcm for I ∥ (111). We have also measured field dependence of longitudinal resistivity ρ_{xx} at various temperatures for these samples; the representative data from these measurements are presented in Supplementary Fig. 5. From the \({\rho }_{{xy}}^{A}\) obtained after subtracting normal Hall contribution and the ρ_{xx} data, we have derived the AHC \({\sigma }_{{yx}}^{A}\) as a function of temperature at 2 T for the I ∥ (001) and I ∥ (111) samples (Fig. 2b) via tensor conversion, that is, \({\sigma }_{{yx}}^{A}={\rho }_{{xy}}^{A}/({\rho }_{{xy}}^{A\ 2}+{\rho }_{{xx}}^{2})\). Both samples are found to show exceptionally large AHC. At 2 K, \({\sigma }_{{yx}}^{A}\) reaches ~1600 Ω^{−1} cm^{−1} for the I ∥ (001) sample. Upon increasing temperature, the AHC decreases slightly and remains up to ~1300 Ω^{−1} cm^{−1} at room temperature. For the I ∥ (111) sample, the AHC is almost temperature independent and just decreases from ~1250 Ω^{−1} cm^{−1} at 2 K to ~1190 Ω^{−1} cm^{−1} at room temperature. Such a large AHC at room temperature in Co_{2}MnAl has never been reported due to the lack of bulk single crystals. The previously reported Hall effect measurements on Co_{2}MnAl were performed on thin film samples with the B2 phase^{52,53}. The giant room temperature AHC revealed in our experiment, as well as its tunability by a weak magnetic field as discussed below, suggests that Co_{2}MnAl is a promising material for device applications such as Hall sensor.
Besides large AHC, Co_{2}MnAl also shows a large AHA, Θ^{H} (\(\tan\,{\Theta }^{\mathrm{H}}={\sigma }_{{yx}}^{A}/{\sigma }_{{xx}}\)), as shown in Fig. 2c. For the I ∥ (111) sample, its \(\tan\,{\Theta }^{\mathrm{H}}\) value is as large as 21% even at room temperature, which is a record value among either trivial or topological magnetic conductors, as far as we know. This can be seen in Fig. 2d, where we have compared AHC and AHA between our Co_{2}MnAl samples and those magnetic materials known as having large \({\sigma }_{{yx}}^{A}\) and Θ^{H}. Magnetic WSMs are generally expected to have large AHC and AHA due to the Berry curvature induced by nontrivial band topology. Among reported magnetic WSMs, while some of them indeed exhibit large AHC and AHA, they occur mostly at low temperatures. For instance, the \(\tan\,{\Theta }^{\mathrm{H}}\) of the FM WSM Co_{3}Sn_{2}S_{2} can also reach 20%, but it can be observed only below 120 K^{35}. The magnetic field induced WSM GdPtBi was also reported to have large AHA, with the largest \(\tan\,{\Theta }^{\mathrm{H}}\) value of ~10% being probed only below 10 K^{55}. As noted above, Heusler compound Co_{2}MnGa has also been reported to have very large AHE^{48}; its AHC reaches ~2000 Ω^{−1} cm^{−1} at 2 K, but decreases down to 1000 Ω^{−1} cm^{−1} at room temperature. Its room temperature \(\tan\;{\Theta }^{\mathrm{H}}\) is 12%, about half of the largest value we observed in Co_{2}MnAl. Compared to Co_{2}MnGa, Co_{2}MnAl shows a much weaker temperature dependence in AHC and AHA for I ∥ (111) (Fig. 2b, c), which is important for device applications.
In general, an AHE may either originate from extrinsic mechanism (i.e., skew scattering and side jump), or arises from intrinsic Berrycurvature contribution^{9}, or combined extrinsic and intrinsic contributions^{8}. From the comparison of the temperature dependence of longitudinal resistivity ρ_{xx}(T) and AHC \({\sigma }_{{yx}}^{A}(T)\) (Fig. 2c), we find large AHC revealed in our experiments for Co_{2}MnAl is of intrinsic origin. In Supplementary Fig. 6, we show the ρ_{xx}(T) data for both I ∥ (001) and I ∥ (111), from which we observe clear temperature dependence as well as localization behavior below 40 K, indicating the scattering rate varies with temperature. In contrast, \({\sigma }_{{yx}}^{A}\) remains nearly unchanged from several K to 300 K for I ∥ (111) despite the scattering rate variation, which is a proof of the intrinsic nature of the AHE according to the theory of AHE in ferromagnets^{8,9}. Furthermore, our theoretical studies presented below also show the intrinsic origin of AHE in Co_{2}MnAl. The \({\sigma }_{{yx}}^{A}\) calculated based on Berry curvature (Supplementary Fig. 1) is close to the experimental value noted above. Additionally, our theory not only explains why \({\sigma }_{{yx}}^{A}(T)\) for I ∥ (001) has a slightly negative slope as compared to the I ∥ (111) case as shown in Fig. 2c, but also predicts \({\sigma }_{{yx}}^{A}\) can be tuned by the rotation of magnetization, which is also consistent with our experiments, as to be discussed below.
Discussion
To understand the intrinsic AHE of Co_{2}MnAl, we have preformed theoretical calculations on the band structure and AHC of Co_{2}MnAl. The intrinsic AHE originates from the band structure and is robust against disorders and defects. The magnetization direction can modify the AHE, because it determines the symmetry and consequently the band structure of the system. We show the calculated AHC (\({\sigma }_{{yx}}^{A}\)) in Supplementary Fig. 1. It is not surprising to find that the magnetization along [001] and [111] leads to slightly different amplitude in \({\sigma }_{{yx}}^{A}\). Near the charge neutral point, the [111] value is slightly lower than the [001] value and the [111] AHC shows weaker temperature dependence than the [001] case, which is semiquantitatively consistent with our experiment and is attributed to the band structure anisotropy. \({\sigma }_{{yx}}^{A}\) exhibits different dependence on the chemical potential between the [001] and [111] cases, leading to different temperature dependence of \({\sigma }_{{yx}}^{A}\) as shown in the calculation (Supplementary Fig. 1b) and experiment (Fig. 2b).
We examine the origin of the strong AHE in the band structure by taking the [001] magnetization for example. In an energy window of −0.2 to +0.1 eV with respect to the charge neutral point (μ = 0), we find four nodal rings centered at the Z point of the FCC Brillouin zone (see more information in the Supplementary information). We note that these nodal rings are protected by the mirror symmetry of the k_{z} = 0 (k_{z} = 0 and π planes are equivalent in the FCC Brillouin zone), as shown in Fig. 3c and Supplementary Fig. 4b. However, corresponding nodal rings at the k_{x} = 0 and k_{y} = 0 planes are gapped out because of the mirror symmetry breaking caused by the [001] magnetic moment (as shown in Supplementary Fig. 2c). These four nodal rings, which are denoted by #1–4 in the following discussions, are induced by band crossing between the highest two valence bands and lowest two conduction bands (see Fig. 3c). In a previous study (ref. ^{44}), only nodal rings #2 and #3 were investigated in a similar compound Co_{2}MnGa without considering the SOC. Without SOC, the magnetization axis does not pick up a specific direction. Thus, these nodal rings appear in all mirror planes, that is, k_{x,y,z} = 0. As shown in Fig. 3b, four nodal rings in different planes interconnect each other to form topological Hopf nodal links^{44,56}. The SOC leads the magnetic moment to couple to the lattice, thus reducing the symmetry. The preserved nodal rings in the mirror plane do not contribute any Berry curvature (see Supplementary Fig. 2), which is characterized by a π Berry phase accumulated along a loop interlocking the nodal ring. Thus, these four nodal rings do not contribute to the AHE. In contrast, the gapped nodal rings generate large Berry curvature and thus give rise to the huge AHC (see Supplementary Fig. 2) as observed in our experiments. Four peaks of \({\sigma }_{{yx}}^{A}\) in this energy window are dominantly contributed by these four gapped nodal rings (see Supplementary Fig. 3). Near the charge neutral point, AHC exhibits a large value because of the existing peak at μ = 25 meV, which is mainly induced by the gapped nodal ring #3 (see Supplementary Fig. 3), rather than Weyl points. It should be clarified that although Co_{2}MnAl also hosts normal carriers (see Supplementary Fig. 4) besides topological bands, the large AHE is predominantly contributed by the topological carriers.
We can control the AHE response by rotating the magnetization axis, when fixing the current and Hall voltage probes on the (001) plane (see the right inset of Fig. 2a). In the experiment, we observed a \(\cos (\theta )\)like oscillation of \({\sigma }_{{yx}}^{A}\) with respect to the magnetization angle, θ. As shown in Fig. 3a, the experiment is consistent with our theoretical calculations. As the magnetization changes from [001] to [010], nodal rings appear in the the k_{y} = 0 plane, while they disappear in k_{x,z} = 0 planes. In between [001] and [010], #3 nodal rings are fully gapped in all three planes, although some other nodal rings (e.g., #1 and #4) evolve into Weyl points (Fig. 3e). As a consequence, the induced Berry curvature Ω_{yx} evolves dramatically from [001] to [010], as shown in Fig. 3d, f, leading to the oscillating \({\sigma }_{{yx}}^{A}\) as seen in experiments. The nearly cosinelike profile is consistent with the fact that Co_{2}MnAl exhibits weak anisotropy in the magnetization orientation in experiment. We should point out that the present \(\cos (\theta )\)type AHE is different from the known planar Hall effect, which has a sin(2θ) dependence^{57}. The planar Hall effect appears in an FM metal where the magnetization remains unchanged as rotating an inplane magnetic field, or a nonmagnetic WSM where the chiral anomaly plays a role^{58,59}. The gap opening of the various nodal lines and the associated band structure reconstruction driven by the rotation of magnetization is manifested by the angular dependence of Hall coefficient R_{H}. In Supplementary Fig. 7, we present the ρ_{xy} data collected under various magnetization orientations between [001] and [010]; R_{H} can be extracted from the linear fit in the field range where magnetization is saturated for each orientation. We found that R_{H} varies remarkably as the magnetization is rotated from [001] to [011], with a sign change near 20°, as shown in the right inset of Fig. 2a. Moreover, R_{H} for M ∥ [111] is almost four times of that for M ∥ [001], see the left inset of Fig. 2a. These observations, together with the angular dependence of \({\sigma }_{{yx}}^{A}\) shown in Fig. 3a, is consistent with the theoretical picture of the band structure and topology tuning by the rotation of magnetization in Co_{2}MnAl discussed above.
In principle, a simple nodal ring can evolve into a pair of Weyl points when the magnetization breaks the corresponding mirror symmetry, as illustrated in Fig. 4a. The induced AHC is proportional to the Weyl point separation^{12,13}. This scenario is seemingly consistent with our observation on nodal rings #1 and #4. However, we do not observe the existence of Weyl points for nodal ring #3, which is the main source of the AHE observed in the experiment, when rotating the magnetization axis.
Actually the missing of Weyl points for nodal ring #3 can explain the large magnitude of the AHC observed in Co_{2}MnAl. Take the [001] magnetization as an example. The theoretical value of \({\sigma }_{{yx}}^{A} \sim 1400\,{\Omega }^{1}\,{\mathrm{cm}}^{1}\) is as large as the AHC of a 3D QAHE^{60}, \(\frac{2{e}^{2}}{h}\frac{1}{a}=1347\,{\Omega }^{1}\,{\mathrm{cm}}^{1}\), where a takes the experimental value 5.75 Å. We note that this is not coincidence. Although this nodal ring is centered at the Z point, it emerges from a large nodal ring that is centered at Γ. Because it even crosses the Brillouin zone boundary, the Γcentered ring gets reconstructed to smaller rings at the zone boundary (see Fig. 3g). Although smaller nodal rings generate Weyl points, a reconstructed nodal ring does not generate Weyl points (illustrated in Fig. 4c). This is because a Weyl point, if it exists, must annihilate with another one from the neighboring Brillouin zone. As a consequence, the band structure has a gap and the induced AHC has a quantized value \(\frac{{e}^{2}}{h}\frac{1}{a}\). In our material, there are two groups of gapped nodal rings on the k_{x,y} = 0 planes. Therefore, the ideal AHC is \(\frac{2{e}^{2}}{h}\frac{1}{a}\). Because the nodal ring cannot be fully gapped out in the Fermi energy and there are also contribution for other bands, we do not expect a true 3D QAHE here. We note that the same scenario can also be applied to Co_{2}MnGa. In addition, if the Γcentered ring was smaller than the Brillouin zone size in Co_{2}MnAl, it could generate Weyl points but smaller AHC than the quantized value. This is actually the case of Heusler compounds Fe_{2}MnX (X = P, As, Sb)^{46}, Co_{2}VGa^{45}, and Co_{2}TiX (X = Si, Ge, Sn)^{43}. We can rationalize these full Heusler magnets in the same framework here.
Conclusions
Based on the understanding of Co_{2}MnAl, we can obtain useful insights to design magnetic materials with strong AHE. To generate large AHC, we need multiple large nodal rings that are larger than the Brillouin zone size. To host multiple nodal rings (in the absence of SOC), we prefer to have multiple mirror planes in the crystal structure, which usually indicates highindex space groups. In general, highly symmetric magnetic materials with strong SOC are an optimal choice, not only for the AHE, but also for other Berrycurvatureinduced phenomena like the anomalous thermal Hall effect and anomalous Nernst effect. Similarly, nonmagnetic materials with many mirror planes and strong SOC are ideal for the spin Hall effect, as pointed out in ref. ^{61}.
Our theory and experiment together also demonstrate that the form of the gapless nodes (Weyl points or nodal rings), as well as their locations and velocities, all strongly rely on the magnetization axis. Therefore, the magnetization can potentially be utilized to engineer an artificial gauge field^{62,63} and spacetime geometric structure^{64,65} of Weyl fermions. On the other hand, Weyl fermions can also mediate a strong coupling between magnetization dynamics and electromagnetic fields^{63}, thus allowing for the electric control of magnetic dynamics in this system. Thus, Co_{2}MnAl provides an ideal intrinsically magnetic platform to explore the interplay between magnetic dynamics and topological physics for the development of a new generation of spintronic devices.
Methods
Experimental
Co_{2}MnAl single crystals were grown using FZ technique. The material rods used for the FZ growth were made using an induction furnace. The crystals were annealed at 1550 K for 1 week, followed by annealing at 873 K for another week. The powder Xray diffraction measurements confirmed that the Co_{2}MnAl single crystals grown using the above method possesses a cubic structure. Since Co_{2}MnAl has multiple structural phases with different types of disorders as mentioned in the main text and only the L2_{1} phase is predicted to host an FM WSM phase, we performed detailed TEM analyses to identify its structure phase. The TEM sample was prepared using a Thermo Fisher Helios NanoLab DualBeam focused ion beam system. The HAADFSTEM images are taken with the Thermo Fisher Titan S/TEM equipped with a spherical aberration corrector, and it was operating at 300 kV accelerating voltage with a probe convergence angle of 30 mrad. Magnetization properties were measured using a SQUID (VSM, Quantum Design). The electrical transport properties were measured using a standard four probe method in a physical property measurement system (Quantum Design).
Ab initio calculation
We have performed densityfunctional theory (DFT) calculations with a fullpotential localorbital minimumbasis (FPLO)^{66} code to calculate electronic structure. The exchange and correlation energies are considered in the generalized gradient approximation by Perdew–Burke–Enzerhof scheme^{67}. SOC is included. From the DFT electronic structure, we have projected the Bloch wave function into Wannier functions (Co3d, Mn3d, and Al3p orbitals), to construct an effective Hamiltonian (\(\hat{H}\)) for the bulk material.
We have evaluated the AHC (\({\sigma }_{{yx}}^{A}\)) and Berry curvature (Ω_{yx}) by the Kuboformula approach in the linear response scheme^{9},
Here ϵ_{n} is the eigenvalue of the \(\leftn\right\rangle\) eigenstate, and \({\hat{v}}_{i}=\frac{{\mathrm{d}}\hat{H}}{\hslash {\mathrm{d}}{k}_{i}}\) (i = x, y, z) is the velocity operator, μ is Fermi level of the system, and f(ξ − μ) is the Fermi–Dirac distribution. A kpoint of grid of 300 × 300 × 300 is used for the numerical integration in Eq. (1).
Data availability
All relevant data are available from the corresponding authors upon request.
Change history
16 September 2020
An amendment to this paper has been published and can be accessed via a link at the top of the paper.
References
Wan, X., Turner, A. M., Vishwanath, A. & Savrasov, S. Y. Topological semimetal and fermiarc surface states in the electronic structure of pyrochlore iridates. Phys. Rev. B 83, 205101 (2011).
Volovik, G. E. The Universe in a Helium Droplet. (Clarendon Press, Oxford, 2003).
Murakami, S. Phase transition between the quantum spin hall and insulator phases in 3d: emergence of a topological gapless phase. N. J. Phys. 9, 356 (2007).
Burkov, A. A., Hook, M. D. & Balents, L. Topological nodal semimetals. Phys. Rev. B 84, 235126 (2011).
Hosur, P. & Qi, X. L. Recent developments in transport phenomena in Weyl semimetals. C. R. Phys. 14, 857–870 (2013).
Yan, B. & Felser, C. Topological materials: Weyl semimetals. Annu. Rev. Condens. Matter Phys. 8, 337–354 (2017).
Armitage, N. P., Mele, E. J. & Vishwanath, A. Weyl and dirac semimetals in threedimensional solids. Rev. Mod. Phys. 90, 015001 (2018).
Nagaosa, N., Sinova, J., Onoda, S., MacDonald, A. H. & Ong, N. P. Anomalous Hall effect. Rev. Mod. Phys. 82, 1539 (2010).
Xiao, D., Chang, M.C. & Niu, Q. Berry phase effects on electronic properties. Rev. Mod. Phys. 82, 1959–2007 (2010).
Nielsen, H. B. & Ninomiya, M. Absence of neutrinos on a lattice: (I). Proof by homotopy theory. Nucl. Phys. B 185, 20–40 (1981).
Nielsen, H. B. & Ninomiya, M. The Adler–Bell–Jackiw anomaly and Weyl fermions in a crystal. Phys. Lett. B 130, 389–396 (1983).
Yang, K.Y., Lu, Y.M. & Ran, Y. Quantum Hall effects in a Weyl semimetal: possible application in pyrochlore iridates. Phys. Rev. B 84, 075129 (2011).
Burkov, A. A. Anomalous Hall effect in Weyl metals. Phys. Rev. Lett. 113, 187202 (2014).
Weng, H., Fang, C., Fang, Z., Bernevig, B. A. & Dai, X. Weyl semimetal phase in noncentrosymmetric transitionmetal monophosphides. Phys. Rev. X 5, 011029 (2015).
Huang, S.M., Xu, S.Y., Belopolski, I., Lee, C.C. & Chang, G. A Weyl Fermion semimetal with surface Fermi arcs in the transition metal monopnictide TaAs class. Nat. Commun. 6, 8373 (2015).
Lv, B. Q., Weng, H. M., Fu, B. B., Wang, X. P. & Miao, H. Experimental discovery of Weyl semimetal TaAs. Phys. Rev. X 5, 031013 (2015).
Xu, S.Y., Belopolski, I., Alidoust, N., Neupane, M. & Bian, G. Discovery of a Weyl fermion semimetal and topological Fermi arcs. Science 349, 613 (2015).
Yang, L. X., Liu, Z. K., Sun, Y., Peng, H. & Yang, H. F. Weyl semimetal phase in noncentrosymmetric compound TaAs. Nat. Phys. 11, 728–732 (2015).
Soluyanov, A. A., Gresch, D., Wang, Z., Wu, Q. S. & Troyer, M. Typeii Weyl semimetals. Nature 527, 495 (2015).
Sun, Y., Wu, S. C., Ali, M. N., Felser, C. & Yan, B. Prediction of Weyl semimetal in orthorhombic MoTe 2. Phys. Rev. B 92, 161107(R) (2015).
Jiang, J., Liu, Z. K., Sun, Y., Yang, H. F. & Rajamathi, C. R. Signature of typeII Weyl semimetal phase in MoTe_{2}. Nat. Commun. 8, 13973 (2017).
Deng, K., Wan, G., Deng, P., Zhang, K. & Ding, S. Experimental observation of topological Fermi arcs in typeII Weyl semimetal MoTe2. Nat. Phys. 12, 1105–1110 (2016).
Chiu, C.K. & Schnyder, A. P. Classification of reflectionsymmetryprotected topological semimetals and nodal superconductors. Phys. Rev. B 90, 205136 (2014).
Fang, C., Chen, Y., Kee, H.Y. & Fu, L. Topological nodal line semimetals with and without spin–orbital coupling. Phys. Rev. B 92, 081201(R) (2015).
Fang, C., Weng, H., Dai, X. & Fang, Z. Topological nodal line semimetals*. Chin. Phys. B 25, 117106 (2016).
Shockley, W. On the surface states associated with a periodic potential. Phys. Rev. 56, 317–323 (1939).
Yan, B., Stadtmüller, B., Haag, N., Jakobs, S. & Seidel, J. Topological states on the gold surface. Nat. Commun. 6, 10167 (2015).
Bian, G., Chang, T.R., Zheng, H., Velury, S. & Xu, S.Y. Drumhead surface states and topological nodalline fermions in tltase 2. Phys. Rev. B 93, 121113 (2016).
Ominato, Y., Yamakage, A. & Nomura, K. Phase diagram of a magnetic topological nodal semimetal: stable nodal line in an easyplane ferromagnet. J. Phys. Soc. Jpn. 88, 114701 (2019).
Yang, H., Sun, Y., Zhang, Y., Shi, W.J., Parkin, S. S. P. & Yan, B. Topological weyl semimetals in the chiral antiferromagnetic materials mn3ge and mn3sn. N. J. Phys. 19, 015008 (2017).
Nayak, A. K., Fischer, J. E., Sun, Y., Yan, B. & Karel, J. Large anomalous Hall effect driven by a nonvanishing Berry curvature in the noncolinear antiferromagnet Mn3Ge. Sci. Adv. 2, e1501870–e1501870 (2016).
Nakatsuji, S., Kiyohara, N. & Higo, T. Large anomalous Hall effect in a noncollinear antiferromagnet at room temperature. Nature 527, 212–215 (2015).
Kuroda, K., Tomita, T., Suzuki, M. T., Bareille, C. & Nugroho, A. A. Evidence for magnetic Weyl fermions in a correlated metal. Nat. Mater. 16, 1090–1095 (2017).
Li, X., Xu, L., Zuo, H., Subedi, A. & Zhu, Z. Momentumspace and realspace Berry curvatures in Mn3Sn. SciPost Phys. 5, 063 (2018).
Liu, E., Sun, Y., Kumar, N., Muechler, L. & Sun, A. Giant anomalous Hall effect in a ferromagnetic Kagomelattice semimetal. Nat. Phys. 14, 1125–1131 (2018).
Wang, Q., Xu, Y., Lou, R., Liu, Z. & Li, M. Large intrinsic anomalous Hall effect in halfmetallic ferromagnet Co 3 Sn 2 S 2 with magnetic Weyl fermions. Nat. Commun. 9, 3681 (2018).
Guin, S. N., Vir, P., Zhang, Y., Kumar, N. & Watzman, S. J. Zerofield Nernst effect in a ferromagnetic Kagomelattice Weylsemimetal Co3Sn2S2. Adv. Mater. 357, 1806622 (2019).
Ding, L., Koo, J., Xu, L., Li, X. & Lu, X. Intrinsic anomalous Nernst effect amplified by disorder in a halfmetallic semimetal. Phys. Rev. X 9, 041061 (2019).
Morali, N., Batabyal, R., Nag, P. K., Liu, E. & Xu, Q. Fermiarc diversity on surface terminations of the magnetic weyl semimetal co3sn2s2. Science 365, 1286–1291 (2019).
Kim, K., Seo, J., Lee, E., Ko, K.T. & Kim, B. S. Large anomalous Hall current induced by topological nodal lines in a ferromagnetic van der Waals semimetal. Nat. Mater. 17, 794 (2018).
Kuebler, J. & Felser, C. Berry curvature and the anomalous Hall effect in Heusler compounds. Phys. Rev. B 85, 012405 (2012).
Kuebler, J. & Felser, C. Weyl points in the ferromagnetic Heusler compound Co2MnAl. EPL 114, 47005 (2016).
Chang, G., Xu, S.Y., Zheng, H., Singh, B. & Hsu, C.H. Roomtemperature magnetic topological Weyl fermion and nodal line semimetal states in halfmetallic Heusler Co2TiX (X=Si, Ge, or Sn). Sci. Rep. 6, 38839 (2016).
Chang, G., Xu, S.Y., Zhou, X., Huang, S.M. & Singh, B. Topological Hopf and chain link semimetal states and their application to Co_{2}MnGa. Phys. Rev. Lett. 119, 156401 (2017).
Manna, K., Muechler, L., Kao, T.H., Stinshoff, R. & Zhang, Y. From colossal to zero: controlling the anomalous Hall effect in magnetic Heusler compounds via Berry curvature design. Phys. Rev. X 8, 041045 (2018).
Noky, J., Xu, Q., Felser, C. & Sun, Y. Large anomalous Hall and Nernst effects from nodal line symmetry breaking in Fe2MnX (X = P, As, Sb). Phys. Rev. B 99, 165117 (2019).
Belopolski, I., Manna, K., Sanchez, D. S., Chang, G. & Ernst, B. Discovery of topological weyl fermion lines and drumhead surface states in a room temperature magnet. Science 365, 1278–1281 (2019).
Sakai, A., Mizuta, Y. P., Nugroho, A. A., Sihombing, R. & Koretsune, T. Giant anomalous Nernst effect and quantumcritical scaling in a ferromagnetic semimetal. Nat. Phys. 14, 1119–1124 (2018).
Guin, S. N., Manna, K., Noky, J., Watzman, S. J. & Fu, C. Anomalous Nernst effect beyond the magnetization scaling relation in the ferromagnetic Heusler compound co 2 mnga. NPG Asia Mater. 11, 16 (2019).
Manna, K., Sun, Y., Muechler, L., Kübler, J. & Felser, C. Heusler, Weyl and Berry. Nat. Rev. Mater. 3, 244–256 (2018).
Oogane, M., Sakuraba, Y., Nakata, J., Kubota, H. & Ando, Y. Large tunnel magnetoresistance in magnetic tunnel junctions using co2mnx (x= al, si) heusler alloys. J. Phys. D 39, 834 (2006).
Vidal, E. V., Stryganyuk, G., Schneider, H., Felser, C. & Jakob, G. Exploring co2mnal Heusler compound for anomalous hall effect sensors. Appl. Phys. Lett. 99, 132509 (2011).
Chen, Y. J., Basiaga, D., O’Brien, J. R. & Heiman, D. Anomalous magnetic properties and Hall effect in ferromagnetic co 2 mnal epilayers. Appl. Phys. Lett. 84, 4301–4303 (2004).
Umetsu, R. Y., Kobayashi, K., Fujita, A., Kainuma, R. & Ishida, K. Magnetic properties and stability of l 2 1 and b 2 phases in the co 2 mn al heusler alloy. J. Appl. Phys. 103, 07D718 (2008).
Suzuki, T., Chisnell, R., Devarakonda, A., Liu, Y. T. & Feng, W. Large anomalous Hall effect in a halfHeusler antiferromagnet. Nat. Phys. 12, 1119 – 1123 (2016).
Yan, Z., Bi, R., Shen, H., Lu, L., Zhang, S.C. & Wang, Z. Nodallink semimetals. Phys. Rev. B 96, 041103 (2017).
Ky, V. D. Planar Hall effect in ferromagnetic films. Phys. Stat. Sol. B 26, 565–569 (1968).
Burkov, A. A. Giant planar hall effect in topological metals. Phys. Rev. B 96, 041110 (2017).
Nandy, S., Sharma, G., Taraphder, A. & Tewari, S. Chiral anomaly as the origin of the planar hall effect in weyl semimetals. Phys. Rev. Lett. 119, 176804 (2017).
Rhim, J.W. & Kim, Y. B. Landau level quantization and almost flat modes in threedimensional semimetals with nodal ring spectra. Phys. Rev. B 92, 045126 (2015).
Sun, Y., Zhang, Y., Felser, C. & Yan, B. Strong intrinsic spin Hall effect in the TaAs family of Weyl semimetals. Phys. Rev. Lett. 117, 146403 (2016).
Liu, C.X., Ye, P. & Qi, X.L. Chiral gauge field and axial anomaly in a weyl semimetal. Phys. Rev. B 87, 235306 (2013).
Hutasoit, J. A., Zang, J., Roiban, R. & Liu, C.X. Weyl fermions induced magnon electrodynamics in a weyl semimetal. Phys. Rev. B 90, 134409 (2014).
Weststrom, A. & Ojanen, T. Designer curvedspace geometry for relativistic fermions in Weyl metamaterials. Phys. Rev. X 7, 041026 (2017).
Liang, L. & Ojanen, T. Curved spacetime theory of inhomogeneous weyl materials. Phys. Rev. Res. 1, 032006(R) (2019).
Koepernik, K. & Eschrig, H. Fullpotential nonorthogonal localorbital minimumbasis bandstructure scheme. Phys. Rev. B 59, 1743 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Acknowledgements
The experimental work at Tulane and Penn State is supported by the US National Science Foundation under Grant DMR1917579. L.Miao, L.Min, and N.A.’s work is supported by the Penn State Center for Nanoscale Science, an NSF MRSEC under the Grant number DMR1420620. B.Y. acknowledges the financial support by the Willner Family Leadership Institute for the Weizmann Institute of Science, the Benoziyo Endowment Fund for the Advancement of Science, Ruth and Herman Albert Scholars Program for New Scientists, and the European Research Council (ERC Grant no. 815869). C.X.L. acknowledges the support of the Office of Naval Research (Grant No. N000141812793), the US Department of Energy (Grant no. DESC0019064), and Kaufman New Initiative research grant KA201898553 of the Pittsburgh Foundation. Y.Z. and Y.W. acknowledge financial support from the National Science Foundation through the Penn State 2D Crystal ConsortiumMaterials Innovation Platform (2DCCMIP) under NSF cooperative agreement DMR1539916.
Author information
Authors and Affiliations
Contributions
Z.M. and B.Y. conceived the project. P.L., Y.W., and Y.Z. synthesized the single crystals. J.L. made the feed rods for single crystal growth. P.L. and W.N. performed the transport and magnetization measurements. L.Min oriented crystals using Laue pattern. L.Miao and N.A. carried out TEM analyses. J.K. performed theoretical calculations. C.X.L. discussed the gauge field and magnetic dynamics. P.L., J.K., Z.M., and B.Y. wrote the manuscript. All authors examined results. The experimental and theoretical parts of this work are supervised by Z.M. and B.Y., respectively.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, P., Koo, J., Ning, W. et al. Giant room temperature anomalous Hall effect and tunable topology in a ferromagnetic topological semimetal Co_{2}MnAl. Nat Commun 11, 3476 (2020). https://doi.org/10.1038/s41467020171749
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467020171749
This article is cited by

The discovery of threedimensional Van Hove singularity
Nature Communications (2024)

Hightemperature concomitant metalinsulator and spinreorientation transitions in a compressed nodalline ferrimagnet Mn3Si2Te6
Nature Communications (2024)

Breakdown of the scaling relation of anomalous Hall effect in Kondo lattice ferromagnet USbTe
Nature Communications (2023)

Weyl nodal ring states and Landau quantization with very large magnetoresistance in squarenet magnet EuGa4
Nature Communications (2023)

Emergent topological quantum orbits in the charge density wave phase of kagome metal CsV3Sb5
npj Quantum Materials (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.