Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Combining high-resolution scanning tunnelling microscopy and first-principles simulations to identify halogen bonding


Scanning tunnelling microscopy (STM) is commonly used to identify on-surface molecular self-assembled structures. However, its limited ability to reveal only the overall shape of molecules and their relative positions is not always enough to fully solve a supramolecular structure. Here, we analyse the assembly of a brominated polycyclic aromatic molecule on Au(111) and demonstrate that standard STM measurements cannot conclusively establish the nature of the intermolecular interactions. By performing high-resolution STM with a CO-functionalised tip, we clearly identify the location of rings and halogen atoms, determining that halogen bonding governs the assemblies. This is supported by density functional theory calculations that predict a stronger interaction energy for halogen rather than hydrogen bonding and by an electron density topology analysis that identifies characteristic features of halogen bonding. A similar approach should be able to solve many complex 2D supramolecular structures, and we predict its increasing use in molecular nanoscience at surfaces.


In order to engineer robust functional molecular nanostructures at surfaces, self-assembly via strong, directional intermolecular forces is often required. Both halogen1 and hydrogen bonding2 possess these characteristics to different extents, offering different potential nanofabrication pathways and allowing for a diverse set of molecular moieties that can participate in the formation of supramolecular architectures. There are many examples in the literature of two-dimensional (2D) hydrogen bonded (HB) assemblies on surfaces that have been examined with surface science techniques3,4,5,6. Halogen-bonded (XB) molecular nanostructures1,7,8,9 are considerably less common in on-surface 2D systems but are increasingly being studied and seen as an important addition to the ‘toolbox’ of supramolecular assembly. Typically, iodine10,11,12,13,14 and bromine atoms15,16,17,18,19 are used as halogen bond donors due to their strong polarisability, but examples of chlorine20 and fluorine21,22 based assemblies have also been reported. Halogen bonds can also involve halogen atoms acting simultaneously as both donor and acceptor11,16,17,23,24, with the positive electrostatic potential of the sigma hole oriented towards the central ‘belt’ of negative electrostatic potential found on an adjacent halogen atom. Alternatively, nitrogen10,12,13,19 and oxygen17,25,26,27 atoms act as acceptor sites in heteromolecular assemblies.

2D assemblies are commonly characterised on surfaces with scanning probe microscopy (SPM) techniques such as scanning tunnelling microscopy (STM) and atomic force microscopy (AFM). In recent years, higher resolution forms of SPM have become available28,29,30,31,32 that make use of functionalised tips (such as CO, Xe, D2, H2, Br, and CuO)28,30,31,33,34 to reveal the internal structure of molecules adsorbed on surfaces with astounding clarity29. Non-contact AFM (NC-AFM) and high-resolution STM (HR-STM) have been used to resolve the structures of molecules that are difficult to determine with more traditional analytical methods such as NMR or mass spectrometry35,36,37, as well as to identify intermediates and products of reactions that have taken place on surfaces38,39,40,41. In particular, NC-AFM and HR-STM have been employed for examining the internal structure of graphene nanostructures, as the number and type of molecular rings can easily be resolved42,43,44,45. There are also various examples of the use of these techniques for studying the supramolecular structure of 2D self-assembled layers21,46,47,48,49, although in most of these cases the chemical structure of the molecular components led to an unambiguous assignment of the type of intermolecular bonding.

Here we identify a case—the self-assembly of 3,9-dibromo-peri-xanthenoxanthene (3,9-Br2PXX) molecules on a Au(111) surface—where the potential coexistence of different intermolecular interactions presents a formidable challenge for standard forms of SPM. In particular, while conventional STM measurements cannot determine whether 3,9-Br2PXX assembles via HB or XB, only by means of HR-STM are we able to identify XB interactions as the driving force leading to the formation of supramolecular assemblies of 3,9-Br2PXX on Au(111).


Molecular assembly

3,9-Br2PXX (Fig. 1a) is a dibrominated derivative of PXX, an electron donor molecule50,51,52,53, derivatives of which have previously been employed as p-type semiconductors in organic thin-film transistors due to their efficient carrier injection properties, high mobility, and thermal stability54,55. The Br and O atoms in 3,9-Br2PXX offer the possibility of both HB and XB intermolecular interactions when arranged into supramolecular arrays on a surface. HB can originate from non-classical weak C–H···O interactions, while the possibility of XB stems from the emergence of the so-called σ-hole56 on the Br atom (Fig. 1b). Density functional theory (DFT) calculations (see Methods) show that there is a region of negative electrostatic potential that forms a belt around the C−Br bonds, while a region of positive potential (the σ-hole) develops in the elongation of the same bond, thus providing the opportunity for Br and O atoms to act as halogen bond donors and acceptors, respectively.

Fig. 1: Structure and electrostatic potential of 3,9-Br2PXX.
figure 1

a Molecular structure of 3,9-Br2PXX. b Map of the electrostatic potential (ESP) projected on an isosurface (0.001 a.u.) of the electron density, clearly showing the σ-hole and the corresponding electron-rich belt on the Br atoms. Continuous lines separate ESP regions differing by more than 0.01 a.u.

At low coverages, the majority of the 3,9-Br2PXX molecules self-assemble into kagome-type structures (phase 1) that develop in the face-centred cubic (fcc) regions and elbow sites of the Au(111) herringbone reconstruction (Fig. 2a). At 77 K, the peripheries of the kagome islands are often seen to vary between scans, indicating a significant level of molecular mobility. Combined with the lack of any noticeable herringbone distortion, we attribute this to the 3,9-Br2PXX molecules being weakly bound to the Au(111) surface (typically, strongly bound adsorbates result in a lifting or a significant distortion of the herringbone reconstruction57,58,59,60). Two mirror symmetric orientations of the kagome structures can be found, suggesting that the pro-chiral 3,9-Br2PXX molecules segregate into chiral domains upon adsorption. The kagome structure itself can be thought of as being composed of triangular sub-units that consist of three molecules, each appearing to be bound with the end of one molecule pointing to the side of another (Fig. 2d). While this indicates that the oxygen atoms of 3,9-Br2PXX are involved in intermolecular bonding, the nature of the interaction is not clear, as is discussed below. The triangular sub-units are packed into a hexagonal unit cell with lattice vectors a = b = 2.2 ± 0.1 nm, and an angle of 60 ± 2°. Full unit cells are rarely found due to the confinement of the assembly in the fcc regions of the herringbone reconstruction.

Fig. 2: STM images of self-assembled structures observed by depositing 3,9-Br2PXX onto a Au(111) surface.
figure 2

a, d Majority kagome structure (phase 1) formed at low molecular coverage. Domains of opposite chirality are indicated by red/yellow highlights in a and the parameters of the surface unit cell are shown in d. b, e Minority irregular assembly (phase 2) coexisting with the kagome structure at low molecular coverage. c, f Compact assembly (phase 3) that develops at higher molecular coverage. STM images a and b were acquired at 77 K, cf at 7 K.

Coexisting with the kagome structure, a second minority assembly (phase 2, Fig. 2b) is observed at low molecular coverage. Phase 2 consists of irregular structures that, similar to the kagome assembly, are limited to the fcc regions of the Au(111) herringbone reconstruction. Within these irregular islands, variations in molecular shape are observed, with some of the ends of the molecules appearing differently, and some molecules having an extra feature at the sides (Fig. 2e). Increasing the coverage results in the development of a further, denser assembly (phase 3, Fig. 2c), where the molecules are arranged into parallel rows (Fig. 2f). This structure forms extended and compact islands that span both fcc and bcc regions of the substrate and coexist with few remaining phase 1 and phase 2 regions (Supplementary Fig. 1).

Initial modelling of the kagome assembly by overlaying molecular structures onto the STM images results in two distinct possibilities for the type of intermolecular interaction that governs the assembly. The unit cell dimensions and possible orientations of the molecule are compatible with either halogen bonding between the Br end groups and the O atoms of adjacent molecules (Fig. 3b), or a non-classical O···H–C hydrogen bond and, possibly, a secondary electrostatic Br···H interaction (Fig. 3c). The relatively featureless appearance of the molecules in typical STM tunnelling conditions does not present an obvious solution to this, even when varying the bias voltage. In this case, the position of the molecular groups (and thus the type of assembly) can therefore not be directly inferred by using standard STM techniques.

Fig. 3: Possible intermolecular bonding motifs stabilizing the kagome structure.
figure 3

a High magnification STM image of the kagome structure highlighting one of its composing triangular sub-units. b Possible halogen bonded and c hydrogen-bonded structures for the kagome packing.

High-resolution STM imaging

In order to clarify the structure of the kagome assembly, we harnessed the capabilities of HR-STM, which we performed at 7 K using a CO-functionalised tip. In agreement with previous HR-STM experiments and theoretical studies42,61, intramolecular features could be resolved when approaching the CO tip close to adsorbed molecules (Fig. 4). The rings of the molecule (in particular, the naphthalene aromatic sections) are clearly resolved, as are the positions of the C–Br end groups. This allows us to overlay a molecular model of 3,9-Br2PXX in a single orientation for all molecules in the kagome structures of a given chirality (the flipped orientation of 3,9-Br2PXX matches the HR-STM images of molecules in the kagome structures of the opposite chirality). By doing so, it appears evident that in the triangular sub-units of the kagome packing the Br atoms of one molecule directly face the O atoms of a neighbouring one, as would be expected in XB (Figs. 4d and 3b). Moreover, overlaying scaled molecular models gives an estimated O···Br distance of 3.1 ± 0.1 Å and a C–O···Br angle of 176 ± 2°. The former is smaller than the sum of the van der Waals radii of the two elements (3.37 Å)62 while the latter is very close to 180°, thus satisfying two established criteria63 for identifying halogen bonds. All examples of the kagome packing studied by HR-STM were determined to be governed by halogen-bonding interactions. No examples of hydrogen-bonded assemblies could be found, demonstrating that the 3,9-Br2PXX molecules on Au(111) form only XB at low coverages.

Fig. 4: High-resolution STM images of the 3,9-Br2PXX kagome assembly.
figure 4

a Constant current STM image recorded with typical scanning parameters with a CO tip (V = 0.51 V, I = 160 pA). b Constant height HR-STM image of the same region as a (V = 30 mV) with the CO tip close to the surface. c Smaller scale zoom of the same area seen in b, V = 30 mV. d Molecular model overlay of c, with halogen bonds indicated by green dotted lines. All images were recorded at 7 K.

DFT calculations and image simulations

To get further insight into the nature of the intermolecular bonding, XB and (hypothetical) HB 3,9-Br2PXX assemblies were investigated by means of DFT calculations. As the molecules appeared to be weakly adsorbed on the relatively inert Au(111) surface, and since the commensurability of the molecular adlayer could not be determined from the STM measurements, the calculations were performed on free-standing monolayers, taken as reasonable theoretical approximations of the experimental structure. Similar unit cells to those observed experimentally were obtained upon the optimisation of both cell vectors and atomic positions (Supplementary Table 1). Interestingly, the average O···H distance obtained for the HB assembly is very similar to the O···Br distance expected for the XB assembly, and both are compatible with the experimentally determined value (3.1 ± 0.1 Å). However, the XB appears to be energetically more favourable than the HB assembly by 80–100 meV/unit cell (the precise value depending on the exchange-correlation functional used, see Supplementary Discussion). This energy difference is indicative that, in agreement with the HR-STM result, the DFT calculations predict that 3,9-Br2PXX assemblies are held together preferentially by XB interactions as opposed to HB. We argue that the preference for the XB network is due to the strength of the O···Br halogen bonds between 3,9-Br2PXX molecules: evaluating the “binding” energy of a 3,9-Br2PXX dimer, held together by either XB or HB interactions, results in the former being up to 25 meV stronger than HB (see Supplementary Discussion).

It is however interesting to compare the results for the XB assembly with those of a hypothetical HB assembly: in Fig. 5 we report the simulated HR-STM images of both assemblies, obtained thanks to the PP-AFM/STM framework of Hapala et al.64 and Krejčí et al.61 (see Methods). The agreement between experimental (Fig. 5a) and simulated (Fig. 5b) HR-STM images of the XB assembly is remarkable, further supporting our assignment. On the contrary, the simulated HR-STM image of the (hypothetical) HB assembly (Fig. 5c) not only displays the wrong symmetry with respect to the experimentally observed assembly (Supplementary Fig. 6) but also suggests that the position of the atoms in the HB assembly would produce markedly different features in the HR-STM images. In particular, the bonding region in the XB assembly is characterised by two brighter triangular features crossed by dark streaks (Fig. 5b), while the HB assembly would have an overall darker appearance in (Fig. 5c). We note that the darker streaks observed between the bromine and oxygen atoms of adjacent molecules (Figs. 4c and 5b) should not be interpreted as the ‘imaging’ of the halogen bonds, as it has been demonstrated that such intermolecular features can result from the relaxation of the flexible CO probe61,64.

Fig. 5: Comparison between experimental and simulated HR-STM images of the 3,9-Br2PXX kagome assembly.
figure 5

a Constant height HR-STM image (same region as Fig. 4c). b Simulated HR-STM image (see text) of the XB assembly. c Simulated HR-STM image of the HB assembly. The orange circles highlight the O···Br/H region.

Analysis of the electron density topology

The DFT calculations allows us also to investigate the electron density topology which, in conjunction with the structural features discussed earlier, provides an additional probe to determine the presence of an intermolecular XB. To this aim, we have examined the electron density ρ in the proximity of the O and Br atoms, which is plotted in Fig. 6a as a contour map projected onto the molecular plane. It can be clearly recognised that a gradient path connects O and Br and that a saddle point, corresponding to the bond critical point (BCP), is located in between O and Br. This is another determining feature listed in the IUPAC definition of halogen bond63. Moreover, Fig. 6b shows the computed bonding charge density difference, i.e. the electron density difference Δρ = ρd − ρm1 − ρm2, where ρd and ρm1,2 refer to the electron density of the dimer and the monomers, respectively. One can notice the emergence of some charge transfer from the Br atom to the O atom, with a net accumulation of electron density (red regions) along the direction of the O···Br bond path. Also this is in agreement with the fact that “the forces involved in the formation of the halogen bond are primarily electrostatic, but polarisation, charge transfer, and dispersion contributions all play an important role”63. We finally note that the charge density redistribution is not limited to the close proximity of the O and Br atoms but is characterised by a rather complex pattern as could have been expected from the highly non-uniform molecular electrostatic potential in Fig. 1b. This results in the formation of a sort of binding pocket rather than a single point contact.

Fig. 6: Analysis of the electron density topology.
figure 6

a Contour map of the electron density ρ projected onto the molecular plane xy. The location of the O and Br atoms is explicitly shown, together with that of the bond critical point, BCP. b Electron density difference Δρ, calculated as the difference between the electron density of the dimer and that of the two monomers.

Identification of synthetic impurities

HR-STM also helps to elucidate the nature of the minority phase 2 by revealing the internal structure of the molecules with an “unusual” appearance and demonstrating that these differ in their configuration of C–Br bonds from the expected 3,9-Br2PXX structure. In particular, Supplementary Fig. 2 shows that some of these molecules have one terminal C–Br group shifted by one position (i.e., they are 2,9- and 2,8-dibromo isomers), while others are instead tri-brominated, with an extra Br atom covalently bound to a carbon on the side of the molecule (1,3,9-Br3PXX). The intermolecular interactions controlling the assembly of phase 2 are mostly XB, with some possible contribution from non-classical O···H–C hydrogen bonds and secondary electrostatic Br···H interactions (Supplementary Fig. 2). Although all the analytical spectroscopic characterisations suggested that the 3,9-Br2PXX obtained was pure (Supplementary Figs. 1114), small traces of dibromo isomers and tribromo derivatives might still have been present in the sample due to their low solubility (see experimental procedures in the Supplementary Methods). The fact that these impurities appear in our STM study at a relatively high concentration may be due to a higher rate of sublimation than 3,9-Br2PXX, resulting in an overrepresentation when deposited onto the surface. In any case, the ability of clearly identifying these molecules by HR-STM when other, conventional spectroscopic characterisation techniques fail to do so, is a further demonstration of the potential of sub-molecular resolution scanning probe microscopy as an analytical tool for chemical structure determination35. Interestingly, the minority phase 2 appears to be made exclusively of defective molecules (of various types), while the regular 3,9-Br2PXX molecules all assemble into the kagome phase 1 structures.

Finally, HR-STM also shows that the compact phase 3 that develops at a higher molecular coverage is kept together by synergistic HB and XB (Supplementary Fig. 3). The molecules are arranged into parallel rows and interact with each other via non-classical O···H–C hydrogen bonds as well as type I halogen bonds between terminal C–Br groups. Interestingly, this assembly is identical to that characterising the 3D crystalline phase of 3,9-Br2PXX as determined by X-ray diffraction (Supplementary Fig. 4), with one of the lattice parameters being slightly larger, most probably due to the molecule-surface interaction. Phase 3 is almost exclusively composed of regular 3,9-Br2PXX molecules, although occasional defective molecules (both 2,9-Br2PXX and 2,8-Br2PXX dibromo isomers and 1,3,9-Br3PXX tribromo derivatives) are observed within the compact islands, and partially de-brominated molecules are sometimes found at the edges (Supplementary Fig. 5).

In conclusion, high-resolution STM performed with a CO-functionalised tip is found to be necessary to conclusively identify the arrangement of dibrominated sp2-hybridised molecules within an on-surface self-assembled molecular network. The experimental information provided by HR-STM provides the basis for a theoretical structural, electrostatic, and electron density topology analysis, allowing us to identify with great accuracy the emergence of halogen bonding as the intermolecular interaction that stabilises the observed molecular structures. Whereas standard metallic-tip STM is unable to differentiate between halogen and hydrogen assembly motifs, HR-STM clearly identifies Br···O halogen bonding as the only source of the observed kagome assemblies of 3,9-Br2PXX on Au(111). DFT calculations support this result by predicting a higher stability of halogen versus hydrogen intermolecular binding while simulations of the HR-STM images demonstrate a remarkable agreement with the experimental data only for the halogen bonding interaction. HR-STM also identified the presence of defective molecules that escaped the scrutiny of traditional analytical methods and thereby fully solved the experimentally observed 2D self-assembly. Building upon the cases in which HR-SPM has been shown to be an invaluable tool for identifying the chemical structure of unknown molecules35,36,37 or for determining the intermediates and products of on-surface reactions38,39,40, this work exemplifies the unique analytical insight that HR-SPM can give in establishing the nanoscale arrangement of molecules within a supramolecular structure and the nature of the intermolecular interactions ruling the self-assembly. We believe that this methodology can be effectively used when investigating 2D networks originating from the self-assembly of planar molecules on surfaces and that a significant fraction of difficult or controversial molecular structures that have been discussed in the literature over the last decades could be quickly and clearly solved by using this approach.


Scanning tunnelling microscopy measurements

STM experiments were performed on a low temperature STM under ultra-high vacuum (UHV) conditions. The Au(111) single crystal was cleaned with multiple cycles of Ar+ sputtering and annealing. 3,9-Br2PXX was deposited via sublimation (483 K) onto the Au(111) crystal, held at room temperature. The crystal was then cooled to 77 K or 7 K for STM analysis. Standard STM measurements were carried out with bias voltages (V, applied to the sample) in the range of ±2.0 V and tunnelling currents of 50–200 pA. In order to perform high-resolution STM experiments, CO was leaked into the UHV system, adsorbed onto the Au(111) crystal held at 10 K, and picked up by the STM tip. High-resolution STM images were taken in constant height mode (current channel). STM image analysis was performed with WSxM65, Gwyddion66 and LMAPper67.

Density Functional theory calculations

DFT calculations were performed using the mixed Gaussian and Plane-Waves (GPW) method implemented in the CP2K package68. As the description of both halogen bonding (XB) and hydrogen bonding (HB) interactions is known to be quite sensitive to the choice of the exchange-correlation (XC) functional56, we have used two different fully self-consistent non-local XC functionals, namely vdW-DF69 and optB88-vdW70, to assess the reliability of our results. Goedecker-type pseudopotentials71 with four, one, six and seven valence electrons for C, H, O and Br respectively have been employed. The Kohn-Sham orbitals were expanded in a Double-Zeta Valence plus Polarisation (DZVP) Gaussian-type basis set, while the plane wave cutoff for the finest level of the multi-grid68 has been set to 400 Ry to efficiently solve the Poisson equation within periodic boundary conditions using the Quickstep scheme68. Brillouin zone integration was restricted to the supercell Γ-point. We have found that considering a single unit cell (in-plane dimensions of 20 Å and containing three 3,9-Br2PXX molecules, thus totalling 96 atoms), together with a vacuum region of 20 Å inserted between the periodic replica of the 2D self-assemblies (along the direction normal to the assemblies planes) is sufficient to ensure an accuracy of the resulting total energy of 3 meV/atom.

Image simulations

The simulated HR-STM images have been obtained thanks to the PP-AFM/STM framework of Hapala et al.64 and Krejčí et al.61. The CO-functionalized tip employed experimentally is approximated by a probe particle bonded to the STM tip: this bond is 4 Å long and characterised by a lateral stiffness of 0.5 N/m. The charge of the probe particle is set equal to zero. As the experimental HR-STM images were obtained in constant height using very low bias voltages, all HR-STM simulated images were calculated as constant height dI/dV maps at the energy of the 3,9-Br2PXX highest occupied molecular orbital (HOMO). In order to describe the tunnelling process, we have considered the s and p orbitals of the sample and the px and py orbitals of the functionalized tip. The Lennard-Jones and electrostatic fields characterising the sample have been obtained using simple point-charge electrostatics64 and the equilibrium configuration of the system was used, as obtained via the DFT calculations described above. The electronic density of states and the molecular orbitals of the sample have also been obtained via the CP2K code.

Further details on the STM methods as well as the full synthetic details are given in the Supplementary Methods.

Data availability

All data needed to evaluate the conclusions in the paper are present in the paper and/or the Supplementary Information. Crystallographic data (excluding structure factors) for compound 3,9-Br2PXX reported in this paper have been deposited at the Cambridge Crystallographic Data Centre, under deposition number 1901257. These data can be obtained free of charge from The Cambridge Crystallographic Data Centre via Additional data supporting the findings of this study are available from the corresponding author upon reasonable request.

Code availability

The electronic structure calculations presented in this work have been obtained by the CP2K (version 4.1) package, which is an open source code freely available at The simulated HR-STM images have been computed via the PPSTM framework of Ondřej Krejčí, which is freely available via GitHub at


  1. Gilday, L. C. et al. Halogen bonding in supramolecular chemistry. Chem. Rev. 115, 7118–7195 (2015).

    CAS  PubMed  Article  Google Scholar 

  2. Parthasarathi, R. et al. Hydrogen bonding - new insights (Springer, 2006).

  3. Slater, A. G., Perdigão, L. M. A., Beton, P. H. & Champness, N. R. Surface-based supramolecular chemistry using hydrogen bonds. Acc. Chem. Res. 47, 3417–3427 (2014).

    CAS  PubMed  Article  Google Scholar 

  4. Otero, R., Gallego, J. M., de Parga, A. L. V., Martín, N. & Miranda, R. Molecular self assembly at solid surfaces. Adv. Mater. 23, 5148–5176 (2011).

    CAS  PubMed  Article  Google Scholar 

  5. Barth, J. V. Molecular architectonic on metal surfaces. Annu. Rev. Phys. Chem. 58, 375–407 (2007).

    ADS  CAS  PubMed  Article  Google Scholar 

  6. Bonifazi, D., Mohnani, S. & Llanes-Pallas, A. Supramolecular chemistry at interfaces: molecular recognition on nanopatterned porous surfaces. Chem. Eur. J. 15, 7004–7025 (2009).

    CAS  PubMed  Article  Google Scholar 

  7. Beale, T. M., Chudzinski, M. G., Sarwar, M. G. & Taylor, M. S. Halogen bonding in solution: thermodynamics and applications. Chem. Soc. Rev. 42, 1667–1680 (2013).

    CAS  PubMed  Article  Google Scholar 

  8. Metrangolo, P., Meyer, F., Pilati, T., Resnati, G. & Terraneo, G. Halogen bonding in supramolecular chemistry. Angew. Chem. Int. Ed. 47, 6114–6127 (2008).

    CAS  Article  Google Scholar 

  9. Erdélyi, M. Halogen bonding in solution. Chem. Soc. Rev. 41, 3547–3557 (2012).

    PubMed  Article  CAS  Google Scholar 

  10. Clarke, S. M. et al. Observation of a two-dimensional halogen-bonded cocrystal at sub-monolayer coverage using synchrotron X-ray diffraction. Chem. Commun. 47, 2526–2528 (2011).

    CAS  Article  Google Scholar 

  11. Silly, F. Concentration-dependent two-dimensional halogen-bonded self-assembly of 1,3,5-tris(4-iodophenyl)benzene molecules at the solid-liquid interface. J. Phys. Chem. C 121, 10413–10418 (2017).

    CAS  Article  Google Scholar 

  12. Sacchi, M. et al. Combined diffraction and density functional theory calculations of halogen-bonded cocrystal monolayers. Langmuir 29, 14903–14911 (2013).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  13. Mukherjee, A., Teyssandier, J., Hennrich, G., De Feyter, S. & Mali, K. S. Two-dimensional crystal engineering using halogen and hydrogen bonds: towards structural landscapes. Chem. Sci. 8, 3759–3769 (2017).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  14. Zheng, Q.-N. et al. Formation of halogen bond-based 2D supramolecular assemblies by electric manipulation. J. Am. Chem. Soc. 137, 6128–6131 (2015).

    CAS  PubMed  Article  Google Scholar 

  15. Jeon, U. S. et al. Two-dimensional networks of brominated Y-shaped molecules on Au(111). Appl. Surf. Sci. 432, 332–336 (2018).

    ADS  CAS  Article  Google Scholar 

  16. Jang, W. J. et al. Tetragonal porous networks made by rod-like molecules on Au(1 1 1) with halogen bonds. Appl. Surf. Sci. 309, 74–78 (2014).

    ADS  CAS  Article  Google Scholar 

  17. Yoon, J. K. et al. Visualizing halogen bonds in planar supramolecular systems. J. Phys. Chem. C 115, 2297–2301 (2011).

    CAS  Article  Google Scholar 

  18. Song, W., Martsinovich, N., Heckl, W. M. & Lackinger, M. Thermodynamics of halogen bonded monolayer self-assembly at the liquid–solid interface. Chem. Commun. 50, 13465–13468 (2014).

    CAS  Article  Google Scholar 

  19. Brewer, A. Y. et al. Supramolecular self-assembled network formation containing NBr halogen bonds in physisorbed overlayers. Phys. Chem. Chem. Phys. 16, 19608–19617 (2014).

    CAS  PubMed  Article  Google Scholar 

  20. Noh, S. K. et al. Supramolecular Cl···H and O···H interactions in self-assembled 1,5-dichloroanthraquinone layers on Au(111). ChemPhysChem 14, 1177–1181 (2013).

    CAS  PubMed  Article  Google Scholar 

  21. Kawai, S. et al. Extended halogen bonding between fully fluorinated aromatic molecules. ACS Nano 9, 2574–2583 (2015).

    CAS  PubMed  Article  Google Scholar 

  22. Han, Z. et al. Imaging the halogen bond in self-assembled halogenbenzenes on silver. Science 358, 206–210 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

  23. Huang, H. et al. Competition between hexagonal and tetragonal hexabromobenzene packing on Au(111). ACS Nano 10, 3198–3205 (2016).

    CAS  PubMed  Article  Google Scholar 

  24. Walch, H., Gutzler, R., Sirtl, T., Eder, G. & Lackinger, M. Material- and orientation-dependent reactivity for heterogeneously catalyzed carbon-bromine bond homolysis. J. Phys. Chem. C 114, 12604–12609 (2010).

    CAS  Article  Google Scholar 

  25. Yasuda, S., Furuya, A. & Murakoshi, K. Control of a two-dimensional molecular structure by cooperative halogen and hydrogen bonds. RSC Adv. 4, 58567–58572 (2014).

    CAS  Article  Google Scholar 

  26. Guo, Z. et al. Role of halogenhalogen interactions in the 2D crystallization of n-semiconductors at the liquid–solid interface. Phys. Chem. Chem. Phys. 19, 31540–31544 (2017).

    CAS  PubMed  Article  Google Scholar 

  27. Chen, Q. et al. Two-dimensional OPV4 self-assembly and its coadsorption with alkyl bromide: from helix to lamellar. Chem. Commun., 3765–3767 (2009).

  28. Temirov, R., Soubatch, S., Neucheva, O., Lassise, A. C. & Tautz, F. S. A novel method achieving ultra-high geometrical resolution in scanning tunnelling microscopy. N. J. Phys. 10, 053012 (2008).

    Article  CAS  Google Scholar 

  29. Gross, L. et al. The chemical structure of a molecule resolved by atomic force microscopy. Science 325, 1110–1114 (2009).

    ADS  CAS  PubMed  Article  Google Scholar 

  30. Weiss, C. et al. Imaging pauli repulsion in scanning tunneling microscopy. Phys. Rev. Lett. 105, 2–5 (2010).

    Google Scholar 

  31. Kichin, G., Weiss, C., Wagner, C., Tautz, F. S. & Temirov, R. Single molecule and single atom sensors for atomic resolution imaging of chemically complex surfaces. J. Am. Chem. Soc. 133, 16847–16851 (2011).

    CAS  PubMed  Article  Google Scholar 

  32. Chiang, C. L., Xu, C., Han, Z. & Ho, W. Real-space imaging of molecular structure and chemical bonding by single-molecule inelastic tunneling probe. Science 344, 885–888 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  33. Mohn, F., Schuler, B., Gross, L. & Meyer, G. Different tips for high-resolution atomic force microscopy and scanning tunneling microscopy of single molecules. Appl. Phys. Lett. 102, 073109 (2013).

    ADS  Article  CAS  Google Scholar 

  34. Mönig, H. et al. Quantitative assessment of intermolecular interactions by atomic force microscopy imaging using copper oxide tips. Nat. Nanotechnol. 13, 371–375 (2018).

    ADS  PubMed  Article  CAS  Google Scholar 

  35. Gross, L. et al. Organic structure determination using atomic-resolution scanning probe microscopy. Nat. Chem. 2, 821–825 (2010).

    CAS  PubMed  Article  Google Scholar 

  36. Hanssen, K. O. et al. A combined atomic force microscopy and computational approach for the structural elucidation of breitfussin A and B: Highly modified halogenated dipeptides from thuiaria breitfussi. Angew. Chem. Int. Ed. 51, 12238–12241 (2012).

    CAS  Article  Google Scholar 

  37. Schuler, B., Meyer, G., Peña, D., Mullins, O. C. & Gross, L. Unraveling the molecular structures of asphaltenes by atomic force microscopy. J. Am. Chem. Soc. 137, 9870–9876 (2015).

    CAS  PubMed  Article  Google Scholar 

  38. Riss, A. et al. Imaging single-molecule reaction intermediates stabilized by surface dissipation and entropy. Nat. Chem. 8, 678–683 (2016).

    CAS  PubMed  Article  Google Scholar 

  39. Oteyza, D. G. D. et al. Direct imaging of covalent bond structure in single-molecule chemical reactions. Science 340, 1434–1437 (2013).

    ADS  PubMed  Article  CAS  Google Scholar 

  40. Riss, A. et al. Local electronic and chemical structure of oligo-acetylene derivatives formed through radical cyclizations at a surface. Nano Lett. 14, 2251–2255 (2014).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  41. Hellerstedt, J. et al. Aromatic azide transformation on the Ag(111) surface studied by scanning probe microscopy. Angew. Chem. Int. Ed. 58, 2266–2271 (2019).

    CAS  Article  Google Scholar 

  42. Hieulle, J. et al. On-surface route for producing planar nanographenes with azulene moieties. Nano Lett. 18, 418–423 (2018).

    ADS  CAS  PubMed  Article  Google Scholar 

  43. Nguyen, G. D. et al. Atomically precise graphene nanoribbon heterojunctions from a single molecular precursor. Nat. Nanotechnol. 12, 1077–1082 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

  44. Sánchez-Sánchez, C. et al. Purely armchair or partially chiral: noncontact atomic force microscopy characterization of dibromo-bianthryl-based graphene nanoribbons grown on Cu(111). ACS Nano 10, 8006–8011 (2016).

    PubMed  Article  CAS  Google Scholar 

  45. Liu, M. et al. Graphene-like nanoribbons periodically embedded with four- and eight-membered rings. Nat. Commun. 8, 14924 (2017).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  46. Weiss, C., Wagner, C., Temirov, R. & Tautz, F. S. Direct imaging of intermolecular bonds in scanning tunneling microscopy. J. Am. Chem. Soc. 132, 11864–11865 (2010).

    CAS  PubMed  Article  Google Scholar 

  47. Sweetman, A. M. et al. Mapping the force field of a hydrogen-bonded assembly. Nat. Commun. 5, 1–7 (2014).

    Article  CAS  Google Scholar 

  48. Hämäläinen, S. K. et al. Intermolecular contrast in atomic force microscopy images without intermolecular bonds. Phys. Rev. Lett. 113, 186102 (2014).

    ADS  PubMed  Article  CAS  Google Scholar 

  49. Jarvis, S. P. Resolving intra- and inter-molecular structure with non-contact atomic force microscopy. Int. J. Mol. Sci. 16, 19936–19959 (2015).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  50. Fermi, A. et al. Tailoring colors by O annulation of polycyclic aromatic hydrocarbons. Chem. Eur. J. 23, 2363–2378 (2017).

    PubMed  Article  CAS  Google Scholar 

  51. Stassen, D., Demitri, N. & Bonifazi, D. Extended O-doped polycyclic aromatic hydrocarbons. Angew. Chem. Int. Ed. 55, 5947–5951 (2016).

    CAS  Article  Google Scholar 

  52. Sciutto, A. et al. Customizing photoredox properties of PXX-based dyes through energy level rigid shifts of frontier molecular orbitals. Chem. Eur. J. 24, 4382–4389 (2018).

    CAS  PubMed  Article  Google Scholar 

  53. Berezin, A., Biot, N., Battisti, T. & Bonifazi, D. Oxygen-doped zig-zag molecular ribbons. Angew. Chem. Int. Ed. 57, 8942–8946 (2018).

    CAS  Article  Google Scholar 

  54. Kobayashi, N., Sasaki, M. & Nomoto, K. Stable peri-xanthenoxanthene thin-film transistors with efficient carrier injection. Chem. Mater. 21, 552–556 (2009).

    CAS  Article  Google Scholar 

  55. Wang, L., Duan, G., Ji, Y. & Zhang, H. Electronic and charge transport properties of peri-xanthenoxanthene: the effects of heteroatoms and phenyl substitutions. J. Phys. Chem. C. 116, 22679–22686 (2012).

    CAS  Article  Google Scholar 

  56. Kolář, M. H. & Hobza, P. Computer modeling of halogen bonds and other σ-hole interactions. Chem. Rev. 116, 5155–5187 (2016).

    PubMed  Article  CAS  Google Scholar 

  57. Driver, S. M., Zhang, T. & King, D. A. Massively cooperative adsorbate-induced surface restructuring and nanocluster formation. Angew. Chem. Int. Ed. 46, 700–703 (2007).

    CAS  Article  Google Scholar 

  58. Rossel, F., Brodard, P., Patthey, F., Richardson, N. V. & Schneider, W.-D. Modified herringbone reconstruction on Au(111) induced by self-assembled Azure A islands. Surf. Sci. 602, L115–L117 (2008).

    ADS  CAS  Article  Google Scholar 

  59. Kutsenko, V. Y. et al. Alkylthiol self-assembled monolayers on Au(111) with tailored tail groups for attaching gold nanoparticles. Nanotechnology 28, 235603 (2017).

    ADS  CAS  PubMed  Article  Google Scholar 

  60. Faraggi, M. N. et al. Bonding and charge transfer in metal–organic coordination networks on Au(111) with strong acceptor molecules. J. Phys. Chem. C. 116, 24558–24565 (2012).

    CAS  Article  Google Scholar 

  61. Krejčí, O., Hapala, P., Ondráček, M. & Jelínek, P. Principles and simulations of high-resolution STM imaging with a flexible tip apex. Phys. Rev. B 95, 045407 (2017).

    ADS  Article  Google Scholar 

  62. Bondi, A. Van der waals volumes and radii. J. Phys. Chem. 68, 441–451 (1964).

    CAS  Article  Google Scholar 

  63. Desiraju, G. R. et al. Definition of the halogen bond (IUPAC Recommendations 2013). 85, 1711–1713 (2013).

  64. Hapala, P. et al. Mechanism of high-resolution STM/AFM imaging with functionalized tips. Phys. Rev. B 90, 085421 (2014).

    ADS  Article  CAS  Google Scholar 

  65. Horcas, I. et al. WSXM: a software for scanning probe microscopy and a tool for nanotechnology. Rev. Sci. Instrum. 78, 013705 (2007).

    ADS  CAS  PubMed  Article  Google Scholar 

  66. Nečas, D. & Klapetek, P. Gwyddion: an open-source software for SPM data analysis. Open Phys. 10, 181–188 (2012).

    ADS  Article  Google Scholar 

  67. Perdigão, L. M. A. LMAPper - The SPM and Mol Viewer,

  68. VandeVondele, J. et al. Quickstep: Fast and accurate density functional calculations using a mixed Gaussian and plane waves approach. Comput. Phys. Commun. 167, 103–128 (2005).

    ADS  CAS  Article  Google Scholar 

  69. Dion, M., Rydberg, H., Schroder, E., Langreth, D. C. & Lundqvist, B. I. Van der Waals density functional for general geometries. Phys. Rev. Lett. 92, 246401 (2004).

    ADS  CAS  PubMed  Article  Google Scholar 

  70. Klimes, J., Bowler, D. R. & Michaelides, A. Chemical accuracy for the van der Waals density functional. J. Phys. Condens. Matter 22, 022201 (2010).

    ADS  PubMed  Article  CAS  Google Scholar 

  71. Goedecker, S., Teter, M. & Hutter, J. J. P. R. B. Separable dual-space Gaussian pseudopotentials. Phys. Rev. B 54, 1703 (1996).

    ADS  CAS  Article  Google Scholar 

Download references


G.C. acknowledges financial support from the University of Warwick and from the EU through the ERC Grant “VISUAL-MS” (Project ID: 308115). D.B. gratefully acknowledges the EU through the MSCA-RISE project “INFUSION” (Project ID: 734834), the ERC Grant “COLORLANDS” (Project ID: 280183), and Cardiff University. We thank Dr. Benson Kariuki, Deborah Romito and Nicolas Biot for the X-ray analysis, Dr. Robert L. Jenkins for the help with NMR experiments, Thomas Williams for his support with MALDI-HRMS analysis, and the Analytical Service at the School of Chemistry, Cardiff University. G.C.S. is grateful to the Centre for Scientific Computing at the University of Warwick for providing computational resources. G.C.S. also acknowledges the use of Athena at HPC Midlands+ (funded by the EPSRC on grant EP/P020232/) in this research, as part of the HPC Midlands+ consortium.

Author information

Authors and Affiliations



J.L. performed the surface deposition experiments, the STM and HR-STM experiments, analysed the experimental data, and wrote the first draft of the manuscript. H.P. performed DFT calculations. G.C.S. performed the electronic structure calculations, computed the simulated HR-STM images and analysed the results. L.D. and D.B. designed, synthesised, and characterised the molecular module. G.C. conceived and coordinated the research project. All authors participated in discussing the data and editing the manuscript.

Corresponding authors

Correspondence to Gabriele C. Sosso, Davide Bonifazi or Giovanni Costantini.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Philip Moriarty and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Lawrence, J., Sosso, G.C., Đorđević, L. et al. Combining high-resolution scanning tunnelling microscopy and first-principles simulations to identify halogen bonding. Nat Commun 11, 2103 (2020).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing