# Room-temperature direct synthesis of semi-conductive PbS nanocrystal inks for optoelectronic applications

## Abstract

Lead sulphide (PbS) nanocrystals (NCs) are promising materials for low-cost, high-performance optoelectronic devices. So far, PbS NCs have to be first synthesized with long-alkyl chain organic surface ligands and then be ligand-exchanged with shorter ligands (two-steps) to enable charge transport. However, the initial synthesis of insulated PbS NCs show no necessity and the ligand-exchange process is tedious and extravagant. Herein, we have developed a direct one-step, scalable synthetic method for iodide capped PbS (PbS-I) NC inks. The estimated cost for PbS-I NC inks is decreased to less than 6 $·g−1, compared with 16$·g−1 for conventional methods. Furthermore, based on these PbS-I NCs, photodetector devices show a high detectivity of 1.4 × 1011 Jones and solar cells show an air-stable power conversion efficiency (PCE) up to 10%. This scalable and low-cost direct preparation of high-quality PbS-I NC inks may pave a path for the future commercialization of NC based optoelectronics.

## Introduction

Lead chalcogenide nanocrystals (NCs) are promising materials with high bandgap-tunability for flexible and lightweight infrared optoelectronics1,2. Devices based on lead chalcogenide NCs can be processed using industrially friendly solvents under room temperature, which is compatible with low-cost, large-scale manufacturing on plastic substrates3,4,5,6.

Lead sulfide (PbS) NCs can be synthesized using a variety of reported methods7,8,9,10. Although many different methods have led to high-efficiency devices, the most common approach is the lead oxide (PbO) and hexamethyldisilathiane (TMS-S) hot injection route pioneered by Hines and Scholes9. The NCs synthesized in these routes are generally accomplished by the use of precursors with long-alkyl chains surfactants, which served as surface ligands for the NCs. Although excellent control over the optical properties and morphologies of these NCs can be achieved through the organic surfactants11, these long chain ligands hamper the electronic transport between NCs, leading to poor device performance12,13. One sophisticated approach for solving this issue has been through post-synthetic ligand exchange method whereby these long organic ligands can be replaced by shorter organic molecules or single atoms/ions14,15,16.

A range of ligand exchange strategies have been explored to reduce the inter-particle spacing for enhanced carrier transport and, at the same time, achieve excellent surface passivation to reduce trap induced recombination losses17,18,19. Conventionally, ligand exchange is carried out in solid-state using time-consuming layer-by-layer (LbL) process to build up thick device-level films15,20,21. Recently reported solution-phase ligand exchange can provide NCs inks that can be deposited in a single step16,22,23. Efficient PbS NCs devices have been achieved using this method with lead halides or organic molecules as the exchange ligands23,24. However, the initial synthesis of long organic-ligands capped PbS NCs show no necessity for the final film deposition and the ligand exchange process is still tedious and extravagant25. The cost of present PbS NC inks is still estimated higher than 16 $g−1, which hinders the commercial possibility of PbS NC solar cells25. Furthermore, large-scale NC inks preparation is also critical for high-throughput manufacturing of NCs based optoelectronics26. Herein, we have developed a new method to direct synthesize halide capped semi-conducting metal chalcogenide NC inks for optoelectronic applications. Metal halide and N, N-Diphenyl thiourea (DPhTA) are employed as precursors. Based on this method, in situ halide capped PbS, silver sulfide (Ag2S) and cadmium sulfide (CdS) NC inks are directly synthesized at room temperature, showing excellent scalability and versatility. We have also demonstrated a lab scale-up synthesis to increase the reaction volume to 2 L and obtained more than 88 g PbS NC ink solids in one pot, with the cost of PbS NC inks lower than 6$ g−1. Furthermore, Obtained PbS NC inks show good size tunability and state-of-the-art performance for optoelectronic applications. Based on these PbS NC inks, photodetectors show a high detectivity up to 1.4 × 1011 Jones at 635 nm with a fast response time less than 4 ms and photovoltaic devices show a power conversion efficiency (PCE) up to 10% with superior device air stability, which outperform the control devices based on solution-phase ligand exchanged NCs.

## Results

### Direct synthesis and characterization of iodide capped PbS NC inks

Conventionally, in order to obtain semi-conductive films, oleic acid capped PbS (PbS-OA) NCs have to be first synthesized by hot injection method and then ligand exchanged with shorter organic ligands or inorganic halide ligands to improve conductivity by either LbL solid-state ligand exchange or solution-phase ligand exchange method, which is tedious and time-& cost-consuming25, as shown in Fig. 1a. Here, we have developed a direct and low-cost synthetic method for iodide capped PbS (PbS-I) NC inks. The synthesis of the PbS-I NC inks, as depicted in Fig. 1b, is carried out by a simple and fast one-step injection at room temperature under nitrogen. We use dimethyl formamide (DMF) to dissolve lead iodide (PbI2) and diphenyl thiourea (DPhTA) with no degassing process that is usually required for conventional PbS synthesis. After butyl amine (BA) was injected into the aforementioned solution, the solution turned from light yellow to black immediately, indicating the formation of PbS NCs. Since PbI2 and DPhTA cannot react in the absence of BA, we speculate that the SH converted from DPhTA under alkaline condition works as the real sulfur precursor (Supplementary Fig. 1)27,28. We also tried to replace DPhTA with TMS-S, which can react with PbI2 directly. The reaction could indeed be triggered without BA and, however, resulted in large size PbS precipitates (Supplementary Fig. 2). If BA was introduced, the obtained PbS NCs showed almost similar size and dispersibility with our PbI2 + DPhTA + BA recipe, which indicates BA also function as temporal surface ligands to control the nucleation and growth in addition to promote the release of SH from DPhTA. The detailed discussion of reaction mechanism was presented in the Supplementary Note 1.

The PbS-I NCs can be separated by anti-solvent centrifugation for one time and the solids can be re-dispersed in DMF with concentration up to 800 mg mL−1, after which the inks can be used directly for device preparation. The size of the PbS-I NCs can be easily controlled by varying the PbI2 to DPhTA ratio (Pb/S ratio). With the decrease of Pb/S ratio, larger NCs can be obtained, which is evidenced from the redshift of both absorption and photoluminescence (PL) peaks as shown in Fig. 2a, b. Since the synthesis process was performed at room temperature (Supplementary Figs. 3, 4 and 5), it could be easily scaled-up to a litre-sized synthesis (2000 mL, Supplementary Fig. 6, 7). It is worth noting that DMF is not an optimal solvent for commercialization. Thus, we chose a more environmentally benign solvent γ-butyrolactone (GBL)29 for the synthesis of PbS-I NCs. As shown in Supplementary Figs. 8 and 9, we have successfully synthesized PbS-I NCs using non-toxic GBL as the reaction solvent. In addition, devices based on GBL synthesized PbS-I NCs show comparably high performance as well (Supplementary Fig. 10).

Important difference between our one-step reaction scheme and the previous reported “synthesis to ligand-exchange” (two-step) methods is that we use scalable room temperature reactions, and NCs are in situ passivated during synthesis by halide ions. As solution phase exchanged PbS NC inks, these NCs can be directly deposited to form thick and uniform films in only one single step. In addition, the sulfur precursor used here is diphenylthiourea (DPhTA), which is more environment friendly and cheaper than conventionally used TMS-S9,30. Therefore, our method is more amenable to be scaled-up in industrial processes by saving the cost of both processing and materials (Supplementary Note 2, Supplementary Tables 1 and 2).

As shown in Fig. 2c, d, based on the images of transmission electron microscope (TEM), the crystalline PbS-I NCs have an average size of 3.46 ± 0.58 nm. The lattice of the NCs matches well with cubic phase PbS structure, as shown in Fig. 2e. According to X-ray photoelectron spectroscopy (XPS) analysis, as shown in Fig. 3a, b, the iodide to lead (I/Pb) ratio is 0.84 in a spin-coated film of PbS-I NCs, which is comparable to the highest reported halide/lead ratio((I + Br)/Pb = 0.86) in solution-phase ligand exchange method16, indicating an exceptional passivated surface (Supplementary Fig. 11). Pb-OH groups bound on the facet of PbS NCs are considered as one of the main sources for sub-bandgap states31. From the O 1s XPS spectrum shown in Fig. 3c, there is a small amount of oxidized butyl amine on the surface of NCs (Supplementary Fig. 12) and the Pb-OH/Pb ratio is only 0.04, which indicates a low trap states density in these PbS-I NCs31.

Furthermore, considering Ag2S and CdS are also commonly used materials in photovoltaic devices32,33, we further explored the synthesis of halide capped Ag2S and CdS NCs. With some modifications (See the “Methods” section), Accanthite phase Ag2S NCs and Hawleyite phase CdS NCs were successfully synthesized (Supplementary Figs. 13 and 14) with I and Cl ions as the capping ligands, respectively. These results indicate the versatility of this synthetic method and its potential to become a general synthetic routine for obtaining other metal chalcogenide NCs inks.

### Optoelectronic characterization and device performance

For exploring the basic electronic properties of PbS-I NC films, carrier density is calculated to be 8.77 × 1016 cm−3 by capacitance-voltage test (Supplementary Note 3, Supplementary Fig. 15), which is also similar with that of ligand exchanged PbS NCs34,35. In order to further explore the surface passivation and trap states of PbS-I NCs, time-resolved PL has been tested. As shown in Fig. 3d, PbS-I NCs in DMF solution show a very long average PL lifetime of 1.90 µs, which is even close to that of oleic acid capped PbS QDs36, indicating a good surface passivation of these PbS-I NCs. The trap density of PbS-I NCs film is then measured by the space charge limited current (SCLC) method35. As shown in Fig. 3e, the trap density can be calculated as 7 × 1015 cm−3 for PbS-I NCs film (Supplementary Note 4), which is even lower than the reported 1.6 × 1016 cm−3 for solution-phase ligand exchanged PbS NCs films37. Furthermore, field-effect transistors (FETs) measurements were carried out to study the mobility of PbS-I NCs films. The FETs were fabricated on a highly doped silicon substrate covered with a 230 nm thick SiO2 as gate dielectric layer and photo-lithographically patterned gold electrodes as source and drain. Figure 3f shows the transfer characteristics at a drain voltage of 15 V. The carrier mobility is calculated from the slope of the IDS versus VGS plot in the linear regime according to the equation38,

$$\mu = \frac{L}{{WV_{{\mathrm{DS}}}C_{\mathrm{i}}}} \cdot \frac{{\partial I_{{\mathrm{DS}}}}}{{\partial V_{{\mathrm{GS}}}}}$$
(1)

Where µ is the carrier mobility, IDS is the drain current, VGS is the gate voltage, L and W are the channel length (10 µm) and channel width (10 mm), respectively; Ci is the gate capacitance per unit area. The electron mobility of PbS-I NC film is calculated as 0.0267 cm2 V−1 s−1, which is close to the reported mobility of solution-phase ligand exchanged PbS NCs37,39.

For further practical demonstration of the synthesized PbS-I NC inks, broadband photodetectors were fabricated and characterized. Figure 4a shows the schematic structure of the photodetector with a channel length and width of 20 µm and 1 mm, respectively. For a photodetector, responsivity (R) and specific detectivity (D*) are two key figures-of-merit40. R is defined as $$R = \frac{{I_{{\mathrm{ph}}}}}{{P_{{\mathrm{in}}}}}$$, representing the ratio of photocurrent generated in the detector over the incident optical power in units of A·W−1, where Iph is the photocurrent and Pin is the incident light power on the effective area41. Figure 4b shows the photocurrent and responsivity of the PbS-I NCs based photodetectors as a function of light power density, exhibiting a high R of 1.5 A W−1 at low irradiance, which is evidently higher than solution-phase ligand exchanged devices (0.56 A W−1, Supplementary Fig. 16). D* is commonly used to characterize the sensitivity of a detector, which can enable the comparison of detectors with different geometries. The unit is cm·Hz1/2·W−1 or Jones. The specific D* can be defined as following equation:42

$$D^ \ast = \frac{{\sqrt {AB} }}{{{\mathrm{NEP}}}} = \frac{{R\sqrt A }}{{S_{\mathrm{n}}}}$$
(2)

where NEP is the noise equivalent power in W, R is the responsivity in A·W−1, A is the active area of the detector in cm2, B is the noise bandwidth in Hz, and Sn is the noise current spectral density of the detector in A·Hz−1/2. For the NEP of detectors, the time-resolved dark current is measured with applying a constant drain bias. By taking the Fourier transform of dark current traces, the noise power densities are obtained as shown in Supplementary Fig. 17, and then the noise spectral densities Sn are extracted at frequency of 1 Hz, under the same conditions as the optical measurements were performed, resulting in noise values of 0.15 pA Hz−1/2. The spectral D* and R for PbS-I NCs based devices has been plotted in Fig. 4c, which shows a broad spectral response up to 1.1 µm and is consistent with the absorption spectral of PbS-I NCs. The D* at 635 nm light is 1.4 × 1011 Jones, which is an order of magnitude higher than solution-phase ligand exchanged devices (Supplementary Table 3). Furthermore, if only shot noise is taken into account, the shot noise estimated detectivity can be calculated to be 1.78 × 1013 Jones, which is, based on the same calculation method, superior than the performance of recently reported PbS QDs based bilayer structure41,43. In addition to the excellent R and D*, our detectors also exhibit a high light-to-dark current ratio up to around 5 × 103 and fast response speed (Fig. 4d). From the time traces of photocurrent with light irradiation on/off in Fig. 4d, the devices show a well photocurrent on/off repeatability and fast speed with rise and decay time of less than 4 ms, which is limited by the measurement system resolution. These excellent photodetection performances are benefited from the high optical and electronic quality of the PbS-I ink, which may be due to the low density of electronic defects and reasonably high mobility in the NCs array film.

In addition to photodetectors, iodide-passivated PbS NCs are also promising absorbers in high-performance photovoltaics. In order to investigate these NCs inks in solar-cell devices, we have selected a widely used architecture:15,16 indium doped tin oxide coated glass as the substrate, a layer of solution processed zinc oxide (ZnO) nanoparticles as the electron-extracting layer, one layer of spin-coated PbS-I NCs as the photoactive layer, two layers of ethanedithiol (EDT) treated PbS-OA NCs as the hole-transporting layer and evaporated gold (Au) as the top contact. In Fig. 5a we scheme the device architecture and in Fig. 5b we present the energy levels of each layer. For the electrodes and the charge-extracting layers, we have used values reported in the literature15,44, while for the PbS-I NCs layer, the energy level of the conduction and valence band edges have been extracted by adding the optical bandgap to the position of the valence band maximum as determined by ultraviolet photoelectron spectroscopy (UPS) measurements (Supplementary Fig. 18).

With a single spin-coating of the suspended PbS-I NC inks onto the ZnO substrate, a device-level thick film could be obtained. After 5 days’ air storage, photovoltaic devices based on PbS-I NCs show an average PCE of 9.48% and the champion device exhibits a short-circuit current density (Jsc) of 25.1 mA cm−2, an open-circuit voltage (Voc) of 0.63 V, and a fill factor (FF) of 0.64, leading to a power-conversion efficiency (PCE) of 10.14%, as shown in Fig.5c, which is slightly higher than that for solution-phase ligand exchanged devices in our lab (Table 1, Supplementary Figs. 19 and 20). The high Voc and FF confirm the excellent passivation of the as-synthesized PbS-I NCs. Meanwhile, as shown in Supplementary Fig. 21, the Jsc is also calculated from the external quantum efficiency (EQE) integration, which is in good agreement with the results from the J-V measurement. Furthermore, photovoltaic devices fabricated with PbS-I NC inks synthesized in large-scale show a decent PCE up to 9% (Supplementary Fig. 22), which indicates the good scalability of this room temperature direct synthesis method. Considering the device stability is closely related with the surface passivation of employed NCs31,45, air stability of PbS-I NCs based solar cells has been tested. After storage in ambient air under an average humidity of 30% for one month without encapsulation, the solar cells can still maintain more than 98% of the original efficiency (Fig. 5d), which further confirms the high quality of in situ passivation of PbS-I inks. In addition, PbS-I NCs synthesized from concentrate solution showed higher performance, as shown in Supplementary Fig. 23. With purer lead iodide and more concentrate precursor solution, devices may provide even higher performance.

## Discussion

In summary, we have developed a direct one-step and scalable synthetic method for halide capped semi-conducting metal chalcogenide (PbS, Ag2S, and CdS) NC inks. This method enables the in situ iodide passivation of PbS NCs and the fabrication of thick films without ligand exchange. Due to the reduced processing-steps, and the use of cheaper precursors, the estimated cost is reduced from more than 16 $g−1 for previously reported PbS inks to lower than 6$ g−1 for our directly synthesized PbS-I inks. We have also easily demonstrated a lab scale-up synthesis, benefiting from the room temperature reaction. In addition, the obtained PbS NC inks show state-of-the-art performance for optoelectronic applications. Based on these PbS-I NCs, photodetector devices show a high detectivity of 1.4 × 1011 Jones with a fast response time less than 4 ms and solar cells show an air-stable PCE more than 10%, which indicates the excellent in situ passivation of the NCs ink during synthesis. Furthermore, this simple, scalable and low-cost preparation of high-quality PbS NCs may pave a path for the future commercialization of NC based optoelectronics.

## Methods

### Chemicals

Lead iodide (PbI2, 99+ %), silver iodide (AgI, 99.9%), cadmium chloride (CdCl2, 99.99%), N,N′-diphenyl thiourea (DPhTA, 98%), lead acetate trihydrate (PbAc2·3H2O, 99%), hexamethyldisilathiane (TMS-S, 98%), ammonium acetate (AA, >98%), ammonium chloride (NH4Cl, 98%), oleic acid (OA, 90%), 1-octadecene (ODE, 90%), hexane (95%), isopropanol (IPA, 95%), acetone (95%), toluene (95%), N,N′-dimethylformamide (DMF, 99.8% anhydrous), N-methylfomamide (NMF, 99.8%), butyl amine (BA, >99%), 1,2-ethanedithiol (EDT, 98%), acetonitrile (ACN, 99%).

### Synthesis and purification of PbS NCs ink

For oleate capped PbS NCs, the synthesis is the same as reported in our previous work36. For the synthesis of PbS-I NCs, 8 mmol PbI2 and 2 mmol DPhTA was dissolved in 9 mL DMF with stirring at room temperature in a nitrogen filled glovebox, after solids all dissolved in DMF, 1 mL butylamine was injected. The solution immediately turned black. After adding toluene as anti-solvent, the PbS NCs were centrifuged for 5 min at 8000 rpm. The solids were stored in glovebox. The solubility of resulted PbS-I NCs could be improved if the synthesis process is proceeded inside nitrogen atmosphere. PbS-I NCs solution was prepared by re-dispering NC solids in DMF with a concentration of 500 mg mL−1 for further devices fabrication. For the PbS-I NCs synthesized with GBL as solvent, 4 mmol PbI2, 4 mmol MAI and 1 mmol DPhTA was dissolved in 9 mL GBL with stirring at room temperature in a nitrogen filled glovebox, after solids all dissolved, 2 mL butylamine was injected. After 5 min reaction at room temperature, toluene was added as anti-solvent and after centrifugation, supernatant was discarded. Solid is dissolved in GBL for further use.

For solution-phase ligand exchanged PbS NCs, 5 mmol PbI2 and 2 mmol NH4Ac (AA) are dissolved in 50 mL DMF. Then, 50 ml 10 mg mL−1 PbS-OA NCs in hexane was dropwise added into PbI2/AA/DMF solution. After the PbS NCs completely transferred to the DMF phase, the DMF solution was washed four times with 50 mL hexane. After ligand exchange, NCs were precipitated by adding toluene as anti-solvent and centrifuged at 8000 rpm for 5 min. The PbS NCs were vacuumized for 30 min to yield NCs powder. The dried iodide-passivated PbS NCs powder was then redispersed in butylamine (200 mg mL−1) for device fabrication.

### Synthesis of Ag2S-I NCs and CdS-Cl NCs ink

For the synthesis of Ag2S-I NCs, 19 mg DPhTA was dissolved in 1 mL DMF and 78 mg AgI was dissolved in 400 μL BA. AgI/BA precursor was swiftly injected into DPhTA/DMF precursor under stirring at room temperature. After 10 min reaction, 4 mL toluene was added and solution was centrifuged for 5 min at 6000 rpm. Supernatant was discarded and solid is dissolved in DMF for further characterization.

For the synthesized of CdS-Cl NCs, 10.7 mg NH4Cl and 36.6 mg CdCl2 were dissolved in 2 mL NMF. 91.2 mg DPhTA (or 12.8 mg sulfur powder) was dissolved into 400 uL BA. Sulfur/BA precursor was rapidly injected into CdCl2/NMF precursor under stirring at room temperature. After 10 min reaction, crude solution was centrifuged directly for 5 min at 6000 rpm. Solid is dissolved in pyridine for further characterization.

### Synthesis of ZnO nanoparticles

ZnO nanoparticles were synthesized according to the literature with some modification46. Zinc acetate dehydrate (2.95 g) was dissolved in 125 mL of methanol at 60 °C. Potassium hydroxide (1.48 g) was dissolved in 65 mL methanol. The potassium hydroxide solution was slowly added to the zinc acetate solution and the solution was kept stirring at 63 °C for 3 h. ZnO nanocrystals were extracted by centrifugation and then washed twice by methanol followed by centrifugation. Finally, 10 mL of chloroform and 10 mL of methanol were added to the precipitates and the solution was filtered with a 0.45 µm filter.

### Solar cell fabrication

ITO-coated glass substrates were sonicated in sequence with acetone, detergent water, acetone, 2-propanol and acetone again for 15 min, respectively. The substrates were treated with oxygen plasma for 10 min to remove the last traces of organic residues before spin coating. The ZnO NP layers were fabricated by spin-coating the nanoparticle solution onto the ITO substrates. The PbS-I NCs solution was spin coated at 2000 rpm for 45 s, followed by 10 min annealing at 70 °C. The PbS-I NCs layer was proceeded in inert atmosphere to achieve high-performance devices. For the EDT treated PbS NCs layers, 20 mg mL−1 oleate capped PbS NCs were spin-coated at 2500 rpm for 20 s, followed with EDT/acetonitrile solution treatment for 30 s and acetonitrile rinsing for twice. Two layers of PbS-EDT were deposited. After 12 h of exposure to dry air, a 100 nm thick gold film was thermally evaporated through a shadow mask to prepare devices with a total active area of about 0.0725 cm2. Devices are stored in ambient air (humidity around 30%) for the air stability test.

### Photodetector fabrication

Before the device fabrication, the silicon substrate was cleaned by acetone and isopropanol. Metal contacts were then fabricated by the laser writing lithography, and Au (50 nm) electrodes were evaporated by thermal evaporation. Then the PbS-I NCs were spin-coated and annealed the same as solar cell devices.

### Measurement and characterization

Current-voltage characteristics were recorded using a Keithley 2400 (I-V) digital source meter under a simulated AM 1.5 G solar irradiation at 100 mW cm−2 (Newport, Class AAA solar simulator, 94023A-U). The light intensity is calibrated by a certified Oriel Reference Cell (91150 V) and verified with a National Renewable Energy Laboratory calibrated Hamamatsu S1787-04 diode. Voltage swept from −1 to 0.1 V (revrese sweep) and 0.1 to −1 V (forward sweep) with the speed of 0.01 V per point and a dwell time of 10 ms. Devices were tested in ambient air. The electrical and photocurrent measurements were performed in ambient conditions using an Agilent B1500A semiconducting device analyzer. For spectral photo-response measurements, the devices were illuminated with fiber-coupled light from a supercontinuum light source (SuperKExtreme EXW-4, NKT Photonics). Responsivity and temporal response times were measured under short-pulsed light at a wavelength of 635 nm from a four-channel laser controlled with an Agilent A33220A waveform generator. UV-vis-NIR spectra were recorded on a Perkin Elmer model Lambda 750. PL measurements were performed on samples dissolved in DMF. The second harmonic (400 nm) of a Ti:sapphire laser (Coherent, Mira 900, repetition rate 76 MHz) was used to excite the samples. The optical emission was recorded by a cooled array detector (Andor, iDus 1.7 µm). Time-resolved PL spectra were detected using a Hamamatsu streak camera with a cathode sensitive to near-IR radiation. The PbS-I NC films for UPS/XPS test were made by spin-coating 50–100 nm thick film onto glass/ITO substrate.

### Reporting summary

Further information on research design is available in the Nature Research Reporting Summary linked to this article.

## Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.

## References

1. 1.

Kagan, C. R., Lifshitz, E., Sargent, E. H. & Talapin, D. V. Building devices from colloidal quantum dots. Science 353, 885–895 (2016).

2. 2.

Yuan, M., Liu, M. & Sargent, E. H. Colloidal quantum dot solids for solution-processed solar cells. Nat. Energy 1, 16016 (2016).

3. 3.

Kovalenko, M. V. Opportunities and challenges for quantum dot photovoltaics. Nat. Nanotechnol. 10, 994–997 (2015).

4. 4.

Carey, G. H. et al. Colloidal quantum dot solar cells. Chem. Rev. 115, 12732–12763 (2015).

5. 5.

Kamat, P. V. Quantum dot solar cells.The next big thing in photovoltaics. J. Phys. Chem. Lett. 4, 908–918 (2013).

6. 6.

Zhang, X. et al. Highly photostable and efficient semitransparent quantum dot solar cells by using solution-phase ligand exchange. Nano Energy 53, 373–382 (2018).

7. 7.

Hendricks, M. P., Campos, M. P., Cleveland, G. T., Jen-La Plante, I. & Owen, J. S. A tunable library of substituted thiourea precursors to metal sulfide nanocrystals. Science 348, 1226–1230 (2015).

8. 8.

Zhang, J., Gao, J., Miller, E. M., Luther, J. M. & Beard, M. C. Diffusion-controlled synthesis of PbS and PbSe quantum dots with in situ halide passivation for quantum dot solar cells. ACS Nano 8, 614–622 (2014).

9. 9.

Hines, M. A. & Scholes, G. D. Colloidal PbS nanocrystals with size-tunable near-infrared emission: observation of post-synthesis self-narrowing of the particle size distribution. Adv. Mater. 15, 1844–1849 (2003).

10. 10.

Wang, X., Zhuang, J., Peng, Q. & Li, Y. A general strategy for nanocrystal synthesis. Nature 437, 121–124 (2005).

11. 11.

Weidman, M. C., Beck, M. E., Hoffman, R. S., Prins, F. & Tisdale, W. A. Monodisperse, air-stable PbS nanocrystals via precursor stoichiometry control. ACS Nano 8, 6363–6371 (2014).

12. 12.

Boles, M. A., Ling, D., Hyeon, T. & Talapin, D. V. The surface science of nanocrystals. Nat. Mater. 15, 141–153 (2016).

13. 13.

Wang, R. et al. Colloidal quantum dot ligand engineering for high performance solar cells. Energy Environ. Sci. 9, 1130–1143 (2016).

14. 14.

Tang, J. et al. Colloidal-quantum-dot photovoltaics using atomic-ligand passivation. Nat. Mater. 10, 765–771 (2011).

15. 15.

Chuang, C. H., Brown, P. R., Bulovic, V. & Bawendi, M. G. Improved performance and stability in quantum dot solar cells through band alignment engineering. Nat. Mater. 13, 796–801 (2014).

16. 16.

Liu, M. et al. Hybrid organic-inorganic inks flatten the energy landscape in colloidal quantum dot solids. Nat. Mater. 16, 258–263 (2017).

17. 17.

Ning, Z. et al. Air-stable n-type colloidal quantum dot solids. Nat. Mater. 13, 822–828 (2014).

18. 18.

Ip, A. H. et al. Hybrid passivated colloidal quantum dot solids. Nat. Nanotechnol. 7, 577–582 (2012).

19. 19.

Carey, G. H., Levina, L., Comin, R., Voznyy, O. & Sargent, E. H. Record charge carrier diffusion length in colloidal quantum dot solids via mutual dot-to-dot surface passivation. Adv. Mater. 27, 3325–3330 (2015).

20. 20.

Lu, K. et al. High-efficiency PbS quantum-dot solar cells with greatly simplified fabrication processing via “solvent-curing”. Adv. Mater. 30, 1707572 (2018).

21. 21.

McDonald, S. A. et al. Solution-processed PbS quantum dot infrared photodetectors and photovoltaics. Nat. Mater. 4, 138–142 (2005).

22. 22.

Ning, Z., Dong, H., Zhang, Q., Voznyy, O. & Sargent, E. H. Solar cells based on inks of n-type colloidal quantum dots. ACS Nano 8, 10321–10327 (2014).

23. 23.

Xu, J. et al. 2D matrix engineering for homogeneous quantum dot coupling in photovoltaic solids. Nat. Nanotechnol. 13, 456–462 (2018).

24. 24.

Aqoma, H. & Jang, S.-Y. Solid-state-ligand-exchange free quantum dot ink-based solar cells with an efficiency of 10.9%. Energy Environ. Sci. 11, 1603–1609 (2018).

25. 25.

Jean, J. et al. Synthesis cost dictates the commercial viability of lead sulfide and perovskite quantum dot photovoltaics. Energy Environ. Sci. 11, 2295–2305 (2018).

26. 26.

Pan, J. et al. Automated synthesis of photovoltaic-quality colloidal quantum dots using separate nucleation and growth stages. ACS Nano 7, 10158–10166 (2013).

27. 27.

García-Rodríguez, R., Hendricks, M. P., Cossairt, B. M., Liu, H. & Owen, J. S. Conversion reactions of cadmium chalcogenide nanocrystal precursors. Chem. Mater. 25, 1233–1249 (2013).

28. 28.

Walter, J. L. et al. A study of thiourea and substituted thiourea analogs by the Bjerrum titration method. J. Am. Chem. Soc. 78, 5560–5562 (1956).

29. 29.

Schep, L. J. et al. The clinical toxicology of gamma-hydroxybutyrate, gamma-butyrolactone and 1, 4-butanediol. Clin. Toxicol. 50, 458–470 (2012).

30. 30.

Yuan, M. et al. High-performance quantum-dot solids via elemental sulfur synthesis. Adv. Mater. 26, 3513–3519 (2014).

31. 31.

Cao, Y., Stavrinadis, A., Lasanta, T., So, D. & Konstantatos, G. The role of surface passivation for efficient and photostable PbS quantum dot solar cells. Nat. Energy 1, 16035 (2016).

32. 32.

Ren, S. et al. Inorganic–organic hybrid solar cell: bridging quantum dots to conjugated polymer nanowires. Nano. Lett. 11, 3998 (2011).

33. 33.

Öberg, V. A. et al. Hot-injection synthesized Ag2S quantum dots with broad light absorption and high stability for solar cell applications. ChemNanoMat 4, 1223 (2018).

34. 34.

Wang, R. et al. Highly efficient inverted structural quantum dot solar cells. Adv. Mater. 30, 1704882 (2018).

35. 35.

Speirs, M. J. et al. Temperature dependent behaviour of lead sulfide quantum dot solar cells and films. Energy Environ. Sci. 9, 2916–2924 (2016).

36. 36.

Wang, Y. et al. In situ passivation for efficient PbS quantum dot solar cells by precursor engineering. Adv. Mater. 30, 1704871 (2018).

37. 37.

Sun, B. et al. Pseudohalide-exchanged quantum dot solids achieve record quantum efficiency in infrared photovoltaics. Adv. Mater. 29, 1700749 (2017).

38. 38.

Han, L. et al. PbSe nanorod field-effect transistors: room- and low-temperature performance. Adv. Electron. Mater. 4, 1700580 (2018).

39. 39.

Sun, B. et al. Multibandgap quantum dot ensembles for solar-matched infrared energy harvesting. Nat. Commun. 9, 4003 (2018).

40. 40.

Huo, N. & Konstantatos, G. Recent progress and future prospects of 2D-based photodetectors. Adv. Mater. 30, 1801164 (2018).

41. 41.

Wei, Y. et al. Hybrid organic/PbS quantum dot bilayer photodetector with low dark current and high detectivity. Adv. Funct. Mater. 28, 1706690 (2018).

42. 42.

Saran, R. & Curry, R. J. Lead sulphide nanocrystal photodetector technologies. Nat. Photonics 10, 81–92 (2016).

43. 43.

Ren, Z. et al. Bilayer PbS quantum dots for high-performance photodetectors. Adv. Mater. 29, 1702055 (2017).

44. 44.

Yang, F. et al. Synthesis of cesium-doped ZnO nanoparticles as an electron extraction layer for efficient PbS colloidal quantum dot solar cells. J. Mater. Chem. A 6, 17688–17697 (2018).

45. 45.

Tan, L., Li, P., Sun, B., Chaker, M. & Ma, D. Stabilities related to near-infrared quantum dot-based solar cells: the role of surface engineering. ACS Energy Lett. 2, 1573–1585 (2017).

46. 46.

Shi, G. et al. Stable and highly efficient PbS quantum dot tandem solar cells employing a rationally designed recombination layer. Adv. Energy Mater. 7, 1602667 (2017).

## Acknowledgements

This work was supported by the National Key Research Projects (Grant No. 2016YFA0202402), the Natural Science Foundation of Jiangsu Province of China (BK20170337), the National Natural Science Foundation of China (Grant No. 61674111), and “111” projects. The author thanks the Collaborative Innovation Center of Suzhou Nano Science and Technology, Soochow University. We also acknowledge the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD). G.K. acknowledges financial support from Fundacio Privada Cellex, the program CERCA and from the Spanish Ministry of Economy and Competitiveness, through the “Severo Ochoa” Programme for Centres of Excellence in R&D (SEV-2015-0522). This project has received funding from the European Union’s Horizon 2020 research and innovation programme under the Marie Skłodowska-Curie grant agreement No. 754558.

## Author information

Authors

### Contributions

W.M. supervised the study. Y.W. conceived the idea and carried out the synthesis, characterizations of PbS NCs. Y.W., K.L., and Z.L. carried out the TEM test. Y.W. and F.L. fabricated and characterized the solar cell devices. Y.W., N.H., and G.K. fabricated and characterized the photodetector devices. M.A.L., H.F., and A.G.S. carried out the FET fabrication and characterization. Y.W., X.L., Y.Z., carried out the UPS and XPS test. Y.X., M.G., S.Z., F.Y., X.T., L.H., and J.Z. synthesized the ZnO NPs and prepared the solution. The manuscript was mainly written by Y.W. and revised by W.M. All authors discussed the results and provided input to the manuscript.

### Corresponding author

Correspondence to Wanli Ma.

## Ethics declarations

### Competing interests

The authors declare no competing interests.

Peer review information Nature Communications thanks Qing Shen and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Rights and permissions

Reprints and Permissions

Wang, Y., Liu, Z., Huo, N. et al. Room-temperature direct synthesis of semi-conductive PbS nanocrystal inks for optoelectronic applications. Nat Commun 10, 5136 (2019). https://doi.org/10.1038/s41467-019-13158-6

• Accepted:

• Published:

• ### A Chemically Orthogonal Hole Transport Layer for Efficient Colloidal Quantum Dot Solar Cells

• Margherita Biondi
• , Min‐Jae Choi
• , Olivier Ouellette
• , Se‐Woong Baek
• , Petar Todorović
• , Bin Sun
• , Seungjin Lee
• , Mingyang Wei
• , Peicheng Li
• , Laxmi K. Sagar
• , Lee J. Richter
• , Sjoerd Hoogland
• , Zheng‐Hong Lu
• , F. Pelayo García de Arquer
•  & Edward H. Sargent

• ### Facet Control for Trap‐State Suppression in Colloidal Quantum Dot Solids

• Yong Xia
• , Wei Chen
• , Peng Zhang
• , Sisi Liu
• , Kang Wang
• , Xiaokun Yang
• , Haodong Tang
• , Linyuan Lian
• , Jungang He
• , Xinxing Liu
• , Guijie Liang
• , Manlin Tan
• , Liang Gao
• , Huan Liu
• , Haisheng Song
• , Daoli Zhang
• , Jianbo Gao
• , Kai Wang
• , Xinzheng Lan
• , Xiuwen Zhang
• , Peter Müller‐Buschbaum
• , Jiang Tang
•  & Jianbing Zhang

• ### Low-Cost, Air-Processed Quantum Dot Solar Cells via Diffusion-Controlled Synthesis

• Emek G. Durmusoglu
• , Gurpreet Singh Selopal
• , Hui Zhang
• , Pinar Dagtepe
• , David Barba
• , Shuhui Sun
• , Haiguang Zhao
• , Havva Yagci Acar
• , Zhiming Wang
•  & Federico Rosei

ACS Applied Materials & Interfaces (2020)

• ### Ligand-Assisted Reconstruction of Colloidal Quantum Dots Decreases Trap State Density

• Bin Sun
• , Maral Vafaie
• , Larissa Levina
• , Mingyang Wei
• , Yitong Dong
• , Yajun Gao
• , Hao Ting Kung
• , Margherita Biondi
• , Andrew H. Proppe
• , Bin Chen
• , Min-Jae Choi
• , Laxmi Kishore Sagar
• , Oleksandr Voznyy
• , Shana O. Kelley
• , Frédéric Laquai
• , Zheng-Hong Lu
• , Sjoerd Hoogland
• , F. Pelayo García de Arquer
•  & Edward H. Sargent

Nano Letters (2020)

• ### Cubic AgBiS2 Colloidal Nanocrystals for Solar Cells

• Viktor A. Öberg
• , Malin B. Johansson
• , Xiaoliang Zhang
•  & Erik M. J. Johansson

ACS Applied Nano Materials (2020)