Abstract
Defect-free monolayers of graphene and hexagonal boron nitride are surprisingly permeable to thermal protons, despite being completely impenetrable to all gases. It remains untested whether small ions can permeate through the two-dimensional crystals. Here we show that mechanically exfoliated graphene and hexagonal boron nitride exhibit perfect Nernst selectivity such that only protons can permeate through, with no detectable flow of counterions. In the experiments, we use suspended monolayers that have few, if any, atomic-scale defects, as shown by gas permeation tests, and place them to separate reservoirs filled with hydrochloric acid solutions. Protons account for all the electrical current and chloride ions are blocked. This result corroborates the previous conclusion that thermal protons can pierce defect-free two-dimensional crystals. Besides the importance for theoretical developments, our results are also of interest for research on various separation technologies based on two-dimensional materials.
Similar content being viewed by others
Introduction
Proton transport through two-dimensional (2D) crystals has recently been studied, both experimentally and theoretically1,2,3,4,5,6,7,8,9. As for the experiment, it was found that proton permeation through mechanically exfoliated crystals is thermally activated with energy barriers of ≈0.8 eV for graphene and ≈0.3 eV for monolayer hexagonal boron nitride (hBN)1. Further measurements using deuterons, nuclei of the hydrogen isotope deuterium, show that quantum oscillations raise the energy of incoming protons by 0.2 eV2. This correction yielded the total barriers of ≈0.5 eV for monolayer hBN and ≈1 eV for graphene. From a theoretical perspective, the latter value is notably lower (by at least 30% but typically a factor of 2) than that found in density-functional calculations for graphene3,4,5,6,7. To account for the difference, a recent theory suggests that graphene can be partially hydrogenated during the measurements, which makes its lattice slightly sparser; thus, making it more permeable to protons8,9. An alternative explanation put forward attributes the observed proton currents to atomic-scale lattice defects, including vacancies10,11. This was argued on the basis of ion-selectivity measurements using chemical-vapor-deposited (CVD) graphene11. Indeed, CVD graphene is known to possess a large density of atomic-scale defects that appear during growth12,13,14. Such defects are generally absent in mechanically exfoliated 2D crystals, which was proven conclusively in gas-leak experiments using the so-called nanoballoons15,16,17. Even a single angstrom-sized vacancy per micrometer-size area could be detected in those experiments16,17. Whereas it is plausible that vacancies and similar defects played a dominant role in experiments using CVD graphene10,11, extrapolation of those results to mechanically exfoliated 2D crystals is unjustifiable. To resolve the controversy, it is crucial to carry out similar ion-selectivity studies using mechanically exfoliated crystals with little or no defects1,2,15.
Here we report ion-selectivity measurements using mechanically exfoliated graphene and hBN monolayers. The crystals are found to be perfectly selective with respect to protons. The latter can permeate through the 2D membranes, whereas even such small ions as chlorine are blocked. The results support the previous conclusion1 that transport of thermal protons through high-quality graphene and hBN occurs through their bulk and does not involve vacancies and other atomic-scale defects.
Results
Device fabrication and characterization
The investigated devices were fabricated using monolayer graphene and mono- and bi-layer hBN crystals that were isolated by micromechanical cleavage18 (see Methods and Supplementary Fig. 1). The crystals were suspended over microfabricated apertures (2 μm in diameter) etched in free-standing silicon-nitride (SiN) membranes1 (Supplementary Fig. 2). A prefabricated polymer washer with a 10 μm-diameter hole was then transferred on top of the crystal so that the hole was aligned with the aperture in the SiN membrane (Supplementary Fig. 2). The assembly was baked at ∼150 °C, to ensure that the washer firmly clamped the 2D crystal to SiN and sealed the crystal edges, to prevent any possible leak along the substrate. In a series of control experiments, we checked that there were no microscopic defects in our exfoliated 2D crystals by employing the approach described in refs. 15,16 and previously also used in our experiments1. To this end, we made hBN and graphene membranes to cover micrometer-sized cavities etched in an oxidized Si wafer and tested the enclosures for possible gas leaks (see inset Fig. 1b and Supplementary Section ‘Leak tests using nanoballoons’). Even a single vacancy would be detectable in these measurements16,17, but neither of the dozens of tested 2D crystals showed such leakage (Supplementary Fig. 3). In contrast, similar devices made from CVD graphene normally exhibited notable gas permeation.
Ion conductivity measurements
The chips containing the individual 2D membranes (Supplementary Fig. 2) were then used to separate two compartments filled with hydrochloric acid (HCl) at chosen concentrations19. Electrical conductance through the membranes was probed using Ag/AgCl electrodes placed inside the compartments. Figure 1a shows the current density I as a function of applied voltage V for representative devices made from graphene and hBN. The I–V response was linear, which allowed us to determine the areal conductivity σ = I/V. We found monolayer hBN to be the most conductive of the studied crystals, followed by bilayer hBN and monolayer graphene. For example, using 1 M HCl we found σ ≈ 1,000 mS cm−2 for monolayer hBN, ≈ 40 mS cm−2 for bilayer hBN and ≈ 12 mS cm−2 for monolayer graphene. The relative conductivities agree well with those found in the previous studies using Nafion (rather than HCl) as the proton-conducting medium1. Thicker crystals (e.g., bilayer graphene) exhibited no discernable conductance, again in agreement with the previous report1.
As monolayer hBN exhibited the highest conductivity, we focus our discussion below on this particular 2D material, as it allowed the most accurate ion-selectivity measurements (results for graphene are presented in Supplementary Information). Figure 1b shows σ found for hBN at various HCl concentrations (the same concentration was used in both compartments). For concentrations above 1 mM, σ increased linearly with HCl concentration. At lower concentrations, the measured current was below our detection limit. The latter was determined by electrical leakage along surfaces of the liquid cell and was of the order of 1 pA as found using control devices with no holes in the SiN membranes19. In another control experiment, we used devices with the same SiN aperture but without a 2D crystal. They exhibited conductance at least ~1000 times larger than that for the devices with graphene or hBN crystals covering the aperture (Supplementary Fig. 4). This demonstrates that the reported values of σ were limited by the relatively low ion permeation through 2D crystals and the series resistance due to the electrolyte itself could be neglected.
Proton selectivity
The measured conductivity could be due to either H+ or Cl−, or both ions permeating through 2D crystals. For the purpose described in the introduction, it is necessary to determine the fraction of I carried by each of these species. Such fractions are usually referred to as transport numbers20 (tH and tCl for protons and chloride, respectively) and, by definition, they satisfy tH + tCl ≡ 1 and the inequality: 0 ≤ both tH and tCl ≤ 1. To find their values for our 2D membranes, we used the same setup as in the measurements discussed in Fig. 1 but with different HCl concentrations in the two compartments (inset of Fig. 2b). The concentration gradient drives both H+ and Cl− ions towards equilibrium, from the high concentration (Ch) compartment to the low concentration (Cl) one. Therefore, the sign of the total ionic current at zero V indicates whether the majority carriers are protons (positive I) or chloride ions (negative). Figure 2a shows typical I–V characteristics for monolayer hBN devices and concentration ratio ΔC ≡ Ch/Cl = 10. Independently of the absolute values of HCl concentrations, the zero V current was always positive, proving that the protons dominate ion transport through our membranes. The same behavior was found for graphene devices (Supplementary Fig. 5).
The force pushing ions across the membrane, due to the concentration gradient, can be counteracted by applying voltage V. The value V0 at which the current becomes zero is known as the membrane or reversal potential and is given by the Nernst equation21
where kB is the Boltzmann constant, T is the temperature and e is the elementary charge. If one of the transport numbers is unity, the other must be zero and, then, it is said that a membrane displays perfect Nernst selectivity. Figure 2a shows that for ΔC = 10, the I–V curves intersected the x -axis at the same V, which means that our membranes exhibited V0 ≈ − 58 mV, regardless of the absolute values of the HCl concentrations. This value is equal to −(kBT/e)ln(ΔC = 10) ≈ − 58 meV at our measurement temperature of ∼20 °C and, therefore, the observation implies tH ≈ 1 or, equivalently, that all the ionic current through the membrane is due to proton transport. Within our experimental accuracy, the same perfect selectivity was also found for graphene (Supplementary Fig. 5).
To corroborate the above result and obtain better statistics for the ion selectivity, we carried out similar measurements using different devices and several concentration ratios ranging from ΔC = 1 to 30 (Fig. 2b). For all of them, we found membrane potentials consistent with the perfect proton selectivity in Eq. (1). The best fit to the data in Fig. 2b yields tH = 0.99 ± 0.02, or tH ≈ 1. In control experiments, we verified our experimental approach using porous glass membranes. They allow large concentration gradients but provide no ion selectivity because of large pore sizes. The latter experiments yielded tH = 0.81 ± 0.04 (Supplementary Fig. 6), in agreement with the transport numbers known for bulk hydrochloric acid (tH ≈ 0.83, tCl ≈ 0.17)20.
Discussion
Finally, it is instructive to compare our results with those obtained previously in conceptually similar experiments but using CVD graphene11. The latter was reported to have σ ≈ 4 S cm−2 at 1 M HCl, in clear disagreement with our experiments for mechanically exfoliated graphene, where σ was nearly three orders of magnitude smaller. Furthermore, no current could be detected for 1 mM HCl concentration in our experiments; however, large current densities of ~10 mA cm−2 were reported in ref. 11 for CVD graphene membranes of the same area. The membrane potential reported for CVD graphene was also different, reaching only ∼8 mV for ΔC = 10, or ~7 times smaller than what we found for our devices. All this shows that the ion transport properties of exfoliated 2D crystals are radically different from those of CVD films where atomic-scale defects and, possibly, even macroscopic ones11 dominate ion transport. This conclusion is consistent with all the other evidence for intrinsic proton transport through 2D crystals, which was reported previously1,2.
In conclusion, our experiments clearly demonstrate that mechanically exfoliated, defect-free 2D crystals allow only proton transport and block even small ions such as chlorine that has one of the smallest hydrated diameters19. This provides further support to the view that the activation barriers found for proton transport through high-quality graphene and hBN do not involve vacancies and other atomic-scale defects1, a conclusion important for further theory developments (e.g., for the hydrogenation model proposed in refs. 8,9). Our results also have implications for the widely discussed use of atomically thin crystals as a novel platform for various separation technologies. In such technologies, selectivity is typically achieved by either perforating nanopores22,23,24,25 or exploiting those naturally occurring in CVD films26,27. The fast permeation of H+ through the 2D bulk is usually ignored but can be important for designing and optimizing the membranes’ properties.
Methods
Fabrication of 2D membranes
Device fabrication started by isolating atomically thin layers of graphene and hBN from bulk crystals. We used hBN crystals commercially supplied by HQ Graphene. The flake was first identified optically and then characterized using atomic force microscopy and Raman spectroscopy. Supplementary Fig. 1 shows typical characterization data for one of the used hBN crystals. Similar characterization procedures were performed for graphene.
Supplementary Fig. 2 illustrates the device fabrication process. Several lithography, reactive ion etching, and wet-etching steps were performed to obtain a fully suspended SiN membrane with a 2 μm-diameter aperture in the center. The exfoliated 2D crystals were then suspended over the apertures. The crystals were also clamped down to the SiN substrate with a polymer washer. To this end, an SU-8 photo-curable epoxy washer was prefabricated with a 10 μm-diameter hole in the middle and transferred over the devices with the hole and aperture aligned (Supplementary Fig. 2). After the transfer, the seal was hard baked at 150 °C to ensure good adhesion to the SiN substrate.
Electrical measurements
Devices were clamped with O-rings to separate two reservoirs filled with HCl solutions and Ag/AgCl electrodes were placed inside each reservoir. The I–V characteristics were measured, applying voltages between typically ±200 mV at sweep rates < 0.1 V min−1.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
References
Hu, S. et al. Proton transport through one-atom-thick crystals. Nature 516, 227–230 (2014).
Lozada-Hidalgo, M. et al. Sieving hydrogen isotopes through two-dimensional crystals. Science 351, 68–70 (2016).
Miao, M., Nardelli, M. B., Wang, Q. & Liu, Y. First principles study of the permeability of graphene to hydrogen atoms. Phys. Chem. Chem. Phys. 15, 16132–16137 (2013).
Wang, W. L. & Kaxiras, E. Graphene hydrate: theoretical prediction of a new insulating form of graphene. New J. Phys. 12, 125012 (2010).
Poltavsky, I., Zheng, L., Mortazavi, M. & Tkatchenko, A. Quantum tunneling of thermal protons through pristine graphene. J. Chem. Phys. 148, 204707 (2018).
Zhang, Q., Ju, M., Chen, L. & Zeng, X. C. Differential permeability of proton isotopes through graphene and graphene analogue monolayer. J. Phys. Chem. Lett. 7, 3395–3400 (2016).
Kroes, J., Fasolino, a & Katsnelson, M. Density functional based simulations of proton permeation of graphene and hexagonal boron nitride. Phys. Chem. Chem. Phys. 19, 5813–5817 (2017).
Feng, Y. et al. Hydrogenation facilitates proton transfer through two-dimensional honeycomb crystals. J. Phys. Chem. Lett. 8, 6009–6014 (2017).
Bartolomei, M., Hernández, M. I., Campos-Martínez, J. & Hernández-Lamoneda, R. Graphene multi-protonation: a cooperative mechanism for proton permeation. Carbon 144, 724–730 (2019).
Achtyl, J. L. et al. Aqueous proton transfer across single-layer graphene. Nat. Commun. 6, 6539 (2015).
Walker, M. I., Braeuninger-Weimer, P., Weatherup, R. S., Hofmann, S. & Keyser, U. F. Measuring the proton selectivity of graphene membranes. Appl. Phys. Lett. 107, 213104 (2015).
Gao, L. et al. Repeated growth and bubbling transfer of graphene with millimetre-size single-crystal grains using platinum. Nat. Commun. 3, 699 (2012).
Huang, P. Y. et al. Grains and grain boundaries in single-layer graphene atomic patchwork quilts. Nature 469, 389–392 (2011).
Lee, G. H. et al. High-strength chemical-vapor-deposited graphene and grain boundaries. Science 31, 1073–1076 (2013).
Bunch, J. S. et al. Impermeable atomic membranes from graphene sheets. Nano Lett. 8, 2458–2462 (2008).
Koenig, S. P., Wang, L., Pellegrino, J. & Bunch, J. S. Selective molecular sieving through porous graphene. Nat. Nanotechnol. 7, 728–732 (2012).
Wang, L. et al. Molecular valves for controlling gas phase transport made from discrete ångström-sized pores in graphene. Nat. Nanotechnol. 10, 785–790 (2015).
Kretinin, A. V. et al. Electronic properties of graphene encapsulated with different two-dimensional atomic crystals. Nano Lett. 14, 3270–3276 (2014).
Gopinadhan, K. et al. Complete steric exclusion of ions and proton transport through confined monolayer water. Science 11, 145–148 (2019).
Bard, A. J. & Faulkner, L. R. Electrochemical Methods (Wiley, 2001).
Helfferich, F. Ion Exchange (McGraw Hill, 1962).
Wang, L. et al. Fundamental transport mechanisms, fabrication and potential applications of nanoporous atomically thin membranes. Nat. Nanotechnol. 12, 509–522 (2017).
Surwade, S. P. et al. Water desalination using nanoporous single-layer graphene. Nat. Nanotechnol. 10, 459–464 (2015).
Garaj, S. et al. Graphene as a subnanometre trans-electrode membrane. Nature 467, 190–193 (2010).
Feng, J. et al. Single-layer MoS2 nanopores as nanopower generators. Nature 536, 197–200 (2016).
O’Hern, S. C. et al. Selective molecular transport through intrinsic defects in a single layer of CVD graphene. ACS Nano 6, 10130–10138 (2012).
Prozorovska, L. & Kidambi, P. R. State-of-the-art and future prospects for atomically thin membranes from 2D materials. Adv. Mater. 30, 1801179 (2018).
Acknowledgements
We acknowledge support from EPSRC–EP/N010345/1, the Lloyd’s Register Foundation, the European Research Council and from Graphene Flagship. M.L.-H. acknowledges a Leverhulme Early Career Fellowship. G.-P.H. acknowledges a Marie Curie International Incoming Fellowship. L.M. acknowledges the EPSRC NowNANO program.
Author information
Authors and Affiliations
Contributions
M.L.-H. and A.K.G. designed and directed the project. L.M. fabricated devices, performed measurements, and carried out data analysis with help from S.Z., K.G., G.-P. H., and D.B. B.L.L. and H.M.C. helped with interpretation. L.M., A.K.G., and M.L.-H. wrote the manuscript. All authors contributed to discussions.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications would like to thank Xinzheng Li and other, anonymous, reviewers for their contributions to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mogg, L., Zhang, S., Hao, GP. et al. Perfect proton selectivity in ion transport through two-dimensional crystals. Nat Commun 10, 4243 (2019). https://doi.org/10.1038/s41467-019-12314-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-12314-2
This article is cited by
-
Control of proton transport and hydrogenation in double-gated graphene
Nature (2024)
-
Proton-selective coating enables fast-kinetics high-mass-loading cathodes for sustainable zinc batteries
Nature Communications (2024)
-
Gate-controlled suppression of light-driven proton transport through graphene electrodes
Nature Communications (2023)
-
Proton transport through nanoscale corrugations in two-dimensional crystals
Nature (2023)
-
Proton and molecular permeation through the basal plane of monolayer graphene oxide
Nature Communications (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.