Electroreduction of carbon dioxide to hydrocarbons and oxygenates on copper involves reduction to a carbon monoxide adsorbate followed by further transformation to hydrocarbons and oxygenates. Simultaneous improvement of these processes over a single reactive site is challenging due to the linear scaling relationship of the binding strength of key intermediates. Herein, we report improved electroreduction of carbon dioxide by exploiting a one-pot tandem catalysis mechanism based on computational and electrochemical investigations. By constructing a well-defined copper-modified silver surface, adsorbed carbon monoxide generated on the silver sites is proposed to migrate to surface copper sites for the subsequent reduction to methane, which is consistent with insights gained from operando attenuated total reflectance surface enhanced infrared absorption spectroscopic investigations. Our results provide a promising approach for designing carbon dioxide electroreduction catalysts to enable one-pot reduction of products beyond carbon monoxide and formate.
The electrochemical reduction of CO2 to energy-dense chemicals is an attractive strategy for storing the intermittent renewable electricity produced by solar and wind sources1,2,3. To ensure sustainability of the entire process, the electrochemical CO2 reduction reaction (CO2RR) is typically conducted in an aqueous electrolyte, in which the protons required are obtained. In this system, tremendous progress has been made in catalyst4,5,6 and reactor design7,8 to drive the two-electron reduction of CO2 to produce CO or formate. However, strategies for direct reduction of CO2 to more valuable fuels and chemicals have been less successful because the catalysts capable of catalyzing this conversion are very limited. Only Cu exhibits appreciable activity and Faradaic efficiency (FE) for reducing CO2 to hydrocarbons and oxygenates9,10,11. The lack of predictive catalyst design principles for CO2RR limits the development of catalysts capable of directly converting CO2 to products beyond CO and formate
To achieve higher efficiencies in the CO2RR toward hydrocarbons and oxygenates, the most common approach involves modifying the Cu surface to produce and/or enrich active sites with a specific structure. These efforts include oxidation and reduction treatment to expose grain boundary-terminated Cu surfaces12,13, plasma treatment14,15, and electro-redeposition16 to introduce stable Cu+ species, morphology control to expose high density low-coordinated surface sites17,18, and alloying with an additional metal to tune the binding strength to the reaction intermediates19,20,21,22. Despite the recent progress, the improvement in the performance as compared to the pure Cu remains unsatisfactory. In particular, the selectivity of alloy catalysts toward products beyond CO and formate do not surpass that of pure Cu10,11. Therefore, novel approaches to design more efficient CO2RR catalysts capable of selectively producing valuable products are highly desirable.
On polycrystalline Cu surfaces, CO2 is first converted to adsorbed CO adsorbate (*CO) followed by its further reduction to hydrocarbons and oxygenates. However, the optimal sites for these two processes could have quite different properties because the formation of *CO requires the optimal binding strength for *COOH23,24,25 while the formation of hydrocarbons and oxygenates requires the optimal binding strength for *CO25,26,27. The simultaneous optimization of the binding strength of *COOH and *CO on one type of reactive site can be challenging due to the linear scaling relationship26. For example, the Au3Cu nanoparticle catalyst exhibited a very high activity for reducing CO2 to CO. However, this catalyst was nearly incapable of producing further reduced products19. An oxide-derived Cu catalyst exhibited a much improved FE for reducing CO to alcohols. However, this catalyst cannot effectively and directly reduce CO2 to products beyond CO and formate12.
Therefore, the conversion of CO2 using tandem catalysis can be a promising strategy to improve the overall efficiencies for further reduced products. By co-locating Cu with a CO-producing surface (e.g., Au and Ag), the Cu may be supplied with abundant CO via spillover. A higher coverage of CO on the Cu surface can not only increase the rates of hydrocarbon and oxygenate production28,29,30 but also suppress the competing hydrogen evolution reaction (HER) by weakening the binding strength of Hads31. Recently, several bimetallic surfaces including Cu-Zn20 and Cu-Au22 were investigated in the CO2RR. The Cu-Zn surface exhibited improved selectivity for ethanol over ethylene, and the Cu-Au surface exhibited an improved partial current density toward reduction products beyond CO from approximately 0.005 to 0.16 mA cm−2 compared to a bare Cu foil at a low overpotential. A tandem catalysis mechanism was proposed to explain these improvements. However, CO spillover was not demonstrated in these systems. Therefore, the origin of the observed synergetic improvements remains unclear. Another recent study demonstrated that a Cu-Ag bimetallic surface can be more selective for C2+ product formation21. However, this improvement was not due to CO spillover but suppression of the HER from the formation of the compressively strained alloy surface. Herein we report a combined computational and experimental study of one-pot tandem catalytic CO2RR. By constructing well-defined model surfaces with isolated thin Cu layers on a CO-producing substrate (i.e., Au and Ag), the CO produced on the CO-producing Au or Ag would migrate to Cu with a low activation energy and be further reduced by Cu. In comparison to pure Cu, our model surface exhibited better CH4 selectivity and activity as well as suppressed HER10,11. Operando attenuated total reflectance surface enhanced infrared absorption spectroscopic (ATR-SEIRAS) investigations yielded the first spectroscopic evidence of CO spillover on a Cu-based bimetallic catalyst. More importantly, our results clearly demonstrate a new paradigm for the design of CO2RR catalysts to achieve further reduced products beyond CO and formate.
Theoretical investigations of carbon monoxide spillover
Ag and Au are known to be the most efficient monometallic surfaces for CO production from the CO2RR4,5. Our computational investigation begins with examination of the possibility for CO spillover from a CO-producing Ag or Au site to a surface Cu site prior to further reduction. The surface is divided into eight regions along the direction from bare Ag (or Au) sites toward surface Cu sites for the discussion of CO spillover, and only the ΔGCO of sites with the strongest binding energy in each region on the Cu-added Ag or Au surface are considered in the CO spillover discussion (Fig. 1a and Supplementary Table 1). As shown in Fig. 1b, *CO adsorption is typically more stable on surface Cu sites than Ag or Au sites. The ΔGCO at bare substrate sites nonadjacent to Cu (i.e., site nos. 1–3) exhibit similar values (i.e., ~0.73 eV for Ag and ~0.34 eV for Au, respectively). As the CO molecule approaches the surface Cu, ΔGCO decreases substantially (stronger adsorption) and reaches a minimum value at site no. 5 on Ag (−0.34 eV) and Au (−0.75 eV) where CO forms a bond with the surface Cu atoms. Significantly better CO adsorption is observed on surface Cu than its substrate for both Ag (1.07 eV) and Au (1.09 eV). Moreover, the free energy barrier for CO spillover on both surfaces is calculated to be very small (no more than 0.16 eV), which can be easily surmounted at room temperature (Supplementary Table 2) and is consistent with previous works32,33. Thus our computational results indicate that CO spillover from the Ag or Au substrate to the surface Cu is thermodynamically and kinetically feasible. The one-pot tandem reduction of CO2 may be viable by converting CO2 to CO on a CO-producing substrate followed by CO spillover and further reduction on a surface Cu site.
Theoretical investigations of carbon monoxide reduction after spillover
The further reduction of CO on surface Cu after spillover is investigated. The conversion of CO to C1 products is chosen as the model reaction process for this investigation because (a) this process is less controversial and the results can be supported by previous work34,35,36,37, and (b) other processes require C-C coupling via mechanisms that are unclear and currently under debate38,39,40. The kinetics and thermodynamics for all possible pathways toward C1 products are calculated (Fig. 2, Supplementary Fig. 1 and Supplementary Table 3). Different from traditional calculations with a fixed electron number, the number of electrons in each calculation is adjusted to maintain a potential of −1.0 VSHE, which is more representative of experimental reaction conditions. The most energetically favored pathway toward CH4 at −1.0 VSHE is determined to be *CO → *CHO → *CHOH → *CH → *CH2 → *CH3 → * + CH4 on both the Ag-Cu and Au-Cu surfaces (Fig. 2 and Supplementary Fig. 1). The surface Cu exhibits the ability to reduce CO to CH4 at −1.0 VSHE. As suggested by the results in Fig. 2 and Supplementary Fig. 1, the hydrogenation of *CO to *CHO, which is the most difficult reaction among all the reaction steps, exhibits the highest free energy barrier (ΔG≠) with a value of 0.57 and 0.50 eV for the Ag-Cu and Au-Cu surfaces, respectively. All reactions along the pathway at a potential bias of −1.0 VSHE are thermodynamically downhill and kinetically feasible with ΔG≠ values being <0.75 eV, a number leading to a turnover frequency of approximately 1 s−1 at room temperature based on the transition state theory34,35. The hydrogenation of *CH, *CH2, and *CH3 exhibits no free energy barrier. Similar results were also reported by Chan et al. in the study of CO2 reduction on stepped copper41,42. This result indicates that CO reduction by the surface Cu on Ag or Au will be kinetically feasible. In contrast, pathways toward other possible C1 product methanol are kinetically unfavorable, although they are thermodynamically feasible. Accordingly, both the thermodynamics and kinetics indicate that the surface Cu on Ag or Au can reduce CO2 to CH4 in a one-pot tandem fashion.
Ag-Cu model surface for electrochemical study
The Ag-Cu surface rather than the Au-Cu surface is chosen as the model catalyst for electrochemical investigations due to the cost-effectiveness of Ag over Au. The Cu-modified Ag surface is prepared at the beginning of CO2 electrolysis by conducting the reaction in a bicarbonate electrolyte containing a predetermined (ppm) level of Cu2+. Owing to the reduction potential of Cu2+ (Cu2+(aq) + 2e− → Cu(s) (+0.16 VSHE for ppm level Cu2+)) being significantly more positive than the electroreduction potential of CO2 (typically <−1.3 VSHE), the ppm-level Cu2+ is instantly electrochemically deposited onto the Ag foil when the electrolysis is initiated, making the deposition process indistinguishable during chronoamperometry. This is supported by the observation that the reduction current of Cu2+ is indistinguishable in current profiles at all potentials (Supplementary Fig. 2). Further, the surface morphologies at the early stage and at the conclusion of the electrolysis are similar (Supplementary Fig. 3). The deposited Cu form islands that are a few tens of nanometers in size on the Ag surface (Fig. 3a–c), which is consistent with previous results using a similar technique43. The coverage of surface Cu can be tuned by controlling the initial Cu2+ concentration in the electrolyte and is characterized using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) (Fig. 3a–c, Table 1, Supplementary Fig. 4). The highly crystalline nature of surface Cu is confirmed by high-resolution transmission electron microscope (HR-TEM) with samples prepared using focused ion beam technique (Supplementary Fig. 5).
The CO2 electrolysis study of these Ag-Cu surfaces is conducted at −1.1 VRHE because Ag foil exhibits the highest FE for CO production at this potential (Fig. 4c)23. The distribution of the major products is shown in Fig. 3d. As the Cu2+ concentration increases from 0 to 1.5 ppm, which corresponds to a Cu coverage increases from 0% to 50.2% (Table 1), the CH4 FE increases substantially from 0% to approximately 60%, and the CO FE decreases concomitantly from >80% to approximately 10% (Fig. 3d). The CH4 FE achieved on this partially Cu-covered Ag-Cu surface (i.e., Cu coverage of 50.2%) is much higher that on a bare polycrystalline Cu foil at the same potential (Supplementary Fig. 6)11. This result indicates that CH4 production on Cu can be efficiently improved via the prior reduction of CO2 to CO on a nearby Ag surface. Because a further increase in the Cu coverage decreases the CH4 FE, the essential role of Ag surface exposure is to provide sufficient CO supply to achieve a high CH4 FE. At a Cu2+ concentration of 2.5 ppm, the Cu coverage reaches 85.3%, and the CH4 FE value decreases to approximately 35%, which is consistent with results obtained on a polycrystalline Cu foil at the same potential (Supplementary Fig. 6)11. The Ag-Cu surfaces are not very selective to C2H4, which is most likely due to the preferential adsorption of those *CO that migrates from the Ag surface on the edge of Cu islands where the reduced dimension may promote the exposure of low-coordinated surface sites. These low-coordinated sites may bind *CO too strongly that prevent the further movement of *CO for dimerization.
Potential dependence study at the silver–copper surface
The Ag-Cu surface with the optimal Cu coverage achieved at a Cu2+ concentration of 1.5 ppm is employed to further investigate the one-pot tandem catalysis in the CO2RR. The potential range for the electrolysis experiment is −0.6 VRHE to −1.3 VRHE (equivalent to −1.0 VSHE to −1.7 VSHE) to drive sufficient but not excessive activities. The Ag-Cu surface at these potentials exhibits nearly identical morphologies (Supplementary Fig. 7). This is most likely due to the large deposition overpotentials (>1.16 V) for only ppm-level Cu2+ in the electrolyte and the deposition processes are limited by the diffusion of Cu2+ rather than the electrode potential. This is supported by the observation in a previous study that the electrodeposition of Cu begins to be diffusion-limited with an overpotential of >300 mV at a Cu2+ concentration of 0.15 M44. When the overpotential is >800 mV, such deposition process is completely diffusion-limited and the deposited Cu exhibits near identical morphologies44,45.
In the −0.6 VRHE to −1.0 VRHE potential range, the Ag-Cu surface exhibits a similar electrocatalytic behavior as that of a bare Ag surface with CO and H2 as the major products (Fig. 4). Both the CO and H2 partial current densities increase as the potential becomes more negative due to the increased overpotential (Fig. 4b, d). The increase in CO production is more significant than that of H2 production, resulting in an increase in CO FE and a decrease in H2 FE (Fig. 4a–c). As the potential becomes more negative than −1.0 VRHE, the Ag-Cu surface exhibits a substantial increase in the CH4 partial current density with a concomitant decrease in the CO partial current density (Fig. 4b). However, for the bare Ag surface, the CO partial current density continuously increases and begins to plateau at −1.1 VRHE, which is most likely due to mass transport limitations (Fig. 4d). This result clearly demonstrates that the exposed Ag surface on Ag-Cu behaves very differently from the bare Ag. If the exposed Ag surface merely converts CO2 to molecular CO that leaves the Ag-Cu surface, as is the case for the bare Ag surface, the CO partial current density should increase as the potential becomes more negative until mass-transport limitation. In contrast, the CO partial current density of Ag-Cu surface actually decreases at more negative potentials where CH4 formation starts to increase (Fig. 4b), indicating that the extra CO produced on exposed Ag sites beyond a potential of −1.0 VRHE is consumed in other processes (i.e., CO spillover). In addition, at −1.0 VRHE, the CO partial current density of Ag-Cu (1.0 mA cm−2) is approximately 46% of that of the bare Ag surface (2.2 mA cm−2). This value is consistent with the 49.8% exposed Ag on the Ag-Cu surface because its CO partial current density is primarily attributed to the exposed Ag due to the very low CO activity of Cu (less than 0.1 mA cm−2 at potentials more negative than −1.0 VRHE)11. As the potential decreases from −1.0 VRHE to −1.1 VRHE, the CO partial current density on the bare Ag increases from 2.23 to 4.82 mA cm−2 representing a factor of 2.16 increase (Fig. 4d). However, the CO partial current density on the Ag-Cu surface decreases slightly from 1.0 to 0.9 mA cm−2 under the same condition (Fig. 4b), assuming that the Ag sites on the Ag-Cu surface would produce more CO with the same factor of 2.16 and the missing portion (i.e., 1.26 mA cm−2) is further converted to CH4 by the surface Cu. The CH4 partial current density can be estimated to be 5.04 mA cm−2 (1.26 mA cm−2 × 4) since CH4 production requires four times as many electrons as CO production. Indeed, this value is consistent with the experimentally measured value (i.e., 4.9 mA cm−2). This result indicates that, at the optimal Cu coverage, nearly 60% of the CO produced on Ag is further reduced to CH4 on the Cu surface via the tandem process. At more negative potentials, significant HER activity is observed on both surfaces, which results in the decreased FE of CO2RR. The drastically increased HER activity on the Ag-Cu surface is most likely due to the rapid HER on surface Cu sites at high potential bias (Supplementary Fig. 6). CO2 electrolysis at extended time (2 h) is also conducted on Ag-Cu and bare Ag surfaces (Supplementary Fig. 8). The CH4 formation is stable in the first hour with an FE of approximately 60%. After that, the CH4 FE gradually increases to 67% at the end of the 2-h electrolysis, which is accompanied by the concomitant decrease of CO and C2H4 FE. The further increase in CH4 FE is likely due to the surface reconstruction of Cu under CO2 electroreduction conditions that favors CH4 formation46,47. Further development of more advanced Ag-Cu catalysts combining Cu and Ag with optimized material structure is a promising approach to achieve better performance in CO2RR.
Operando spectroscopic investigations
To gain further insights into the CO spillover on the Ag-Cu surface, operando ATR-SEIRAS is employed to monitor the adsorbed CO at conditions closely mimicking those in the reactivity studies. Experiments on bare Ag, bare Cu, and Ag-Cu surface (1.5 ppm Cu2+) at −0.4 VRHE are conducted in a custom-designed stirred spectroelectrochemical cell (Supplementary Fig. 9)48. The bare Ag surface in the ATR-SEIRAS study is prepared by electrochemical deposition of Ag film in a silver cyanide plating bath on an Au film that is chemically deposited onto the reflecting plane of a Si prism49,50. The Ag-Cu surface is then prepared in the same fashion as in the reactivity study, i.e., by conducting the experiments in a Cu2+-containing bicarbonate on the Ag film. The bare Cu surface is prepared via the chemical deposition method51. The bare Ag surface exhibits a C≡O stretching band at 2094 cm−1 (Fig. 5), which is typically attributed to CO molecule bound in an atop geometry52. The bare Cu surface shows two stretching bands of atop-bound CO in the 2000–2120 cm−1 range, with the 2088 and 2055 cm−1 bands being attributed to CO adsorption on defect sites and terraces sites, respectively51. This is also consistent with previous studies by Waegele et al. under similar electrolysis conditions53. The 2094 cm−1 band on the Ag-Cu surface is identical to that of bare Ag surface, as the peak position and width are both identical. The deconvoluted C≡O stretching band on surface Cu has a broad feature centered at 2048 cm−1, which is consistent with a previous report54. The difference between the CO adsorption feature on the bare Cu and the Ag-Cu surface shows that the underlying Ag exerts an impact on the properties of Cu. Remarkably, the Ag-Cu surface exhibits a band in the 1800–1900 cm−1 range, typically assigned to bridge CO with stronger binding strength, which is absent on both bare Ag and Cu surfaces55,56. This band is much more intense than the atop CO band, thus is the major CO species on the Ag-Cu surface according to Beer–Lambert law. The spectroscopic observations clearly indicate that the Ag-Cu surface is different from a simple superposition of bare Cu and Ag surfaces. This is consistent with our one-pot tandem catalysis theory that the *CO produced on the exposed Ag sites can migrate to stronger binding sites on the Ag-Cu surface for further reduction. In addition, the exclusive band on the Ag-Cu surface is not due to some new reactive site existing on the Ag-Cu bimetallic interface. If this is the case, the CO produced on the exposed Ag sites on Ag-Cu will not be consumed by further reduction, and the CO production should be promoted at more negatively biased potential until mass-transport limitation, similar as the case of bare Ag foil. This contradicts the experimental results shown in Fig. 4b, d.
Constant and square-wave potential electrolysis of CO on the Ag-Cu surface
To further probe CH4 formation over Ag-Cu surface with respect to local *CO concentration, the electrochemical CO reduction reaction is conducted at −1.1 VRHE using the same bicarbonate electrolyte, and the results are compared to those obtained using a bare Cu foil. At constant potential, the Ag-Cu surface produces fewer hydrocarbons than the bare Cu foil in CO electrolysis (Fig. 6). This result can be rationalized that Ag is not active in CO electroreduction, thus fewer active Cu sites are present on the Ag-Cu surface than on the Cu foil surface. Therefore, the observed enhancement of CH4 formation on the Ag-Cu surface in CO2RR is apparently due to the tandem chemistry between Ag and Cu.
In CO2RR, CO adsorption can be difficult because CO adsorbate is suggested to come from the transformation of radical anion CO2−• instead of direct CO adsorption57,58. In addition, the surface CO adsorption can also be negatively impacted by the near electrode cations that are attracted by electrostatic forces as the electrode potential is negatively biased during the electrolysis50. However, the near electrode cations can be effectively removed at a more positive potential (e.g., 0.4 VRHE), and CO adsorption can be promoted50. Based on these insights, square-wave potential electrolysis (inset of Fig. 6) of CO is employed to probe the catalytic behavior of our Ag-Cu surface with an increased local *CO concentration. The potential is alternated between 0.4 VRHE (U0) for a fixed time interval of 0.01 s, at which the CO adsorption is maximized50, and an electrolysis potential (i.e., −1.1 VRHE, UE) at which the CO reduction is expected to occur. By flipping the electrode potential at a frequency of approximately 1 Hz, the FE toward hydrocarbon formation on the Ag-Cu surface is significantly improved from 5% to 18%, which surpassed that on a bare Cu surface. By increasing the frequency to approximately 2 Hz, the FE toward hydrocarbon formation is further increased to 30%, which is twice as high as that of bare Cu. These results suggest that the increase of electrode *CO concentration can efficiently improve the formation of further reduced products. The one-pot tandem catalysis mechanism that unitizes the complementary surface chemistry between a CO-producing material and Cu can be a very effective strategy for achieving this goal. However, to achieve more valuable products (e.g., C2+ products) requires further development employing more active CO-producing catalysts (e.g., nanoporous Ag4 or oxide-derived Au5) and CO reduction catalysts (e.g., oxide-derived Cu59,60) as well as their combination pattern and structure design for binding *CO to more desired sites after spillover.
Density functional theory (DFT) calculations were carried out to investigate the one-pot tandem catalysis of the CO2RR on Cu-modified Ag and Au surface models. We found that the surface Cu stabilized *CO by 1.07 and 1.09 eV compared to Ag and Au, respectively, indicating that the abundant *CO produced on the Ag or Au surface can migrate to surface Cu for further reduction. We found that all reactions along the possible pathways are downhill under a potential bias of −1.0 VSHE, indicating that the migrated *CO from the Ag surface can be further reduced on the surface Cu with barriers that are not larger than those on a bare Cu surface. Electrochemical studies were conducted using well-defined Ag-Cu surfaces with tunable Cu coverages to confirm our computational predictions. The CO spillover phenomenon was experimentally demonstrated for the first time. At optimum Cu coverage, nearly 70% of the CO produced on Ag can be further reduced on surface Cu, resulting in a high CH4 FE of approximately 60%. This FE is much higher than that on a bare Cu surface, which has intrinsically limited surface *CO. In addition, operando ATR-SEIRAS was employed to investigate the spillover of CO on the Ag-Cu surface. A dominating C≡O stretching band on the Ag-Cu surface with stronger binding strength was found at −0.4 VRHE, which was absent on the bare Ag and Cu surface, suggesting that the major *CO was not from CO2RR on Cu. The stronger adsorption of *CO on Cu as compared to Ag strongly suggest the CO spillover as a viable pathway. Moreover, we conducted square-wave potential electrolysis of CO to assess the role of a higher *CO concentration on hydrocarbon formation over the Ag-Cu surface. By alternating the electrolysis potential between a reductive point and a point that removes the near-surface cations, the FE for hydrocarbon formation was significantly enhanced owing to increased *CO adsorption. These results suggest that the increase of surface *CO could efficiently improve the formation of further reduced products. We conclude that the one-pot tandem catalysis mechanism unitizing the complementary surface chemistry between a CO-producing material and Cu can be a very effective strategy for achieving this goal. Further development employing more active CO-producing catalysts (e.g., nanoporous Ag4 or oxide-derived Au5) and CO reduction catalysts (e.g., oxide-derived Cu59,60) as well as their combination pattern and structure design provides a very promising route to achieve efficient CO2RRs toward more valuable products (e.g., C2+ products).
The total energy of the Cu-modified Ag(111) and Au(111) surfaces with different adsorbates were calculated using DFT with the Perdew-Burke-Ernzerhof exchange-correlation functional61 in plane-wave pseudopotentials62,63, as implemented in the Vienna ab initio Simulation Package (VASP)64,65. The empirical D2 approach as implemented in VASP was employed to describe the van der Waals interactions66. All calculated energy values were extrapolated to kBT = 0. A Monkhorst–Pack k-point net of 3 × 6 × 1 was chosen to sample the reciprocal space for the slab calculations, and only the gamma point was sampled for the molecule calculations. A metal slab (4 × 2) consisting of 3 layers with the bottom layer fixed in its bulk position was employed to simulate the surface of Ag and Au, and a single layer of Cu with a coverage of 1/2 ML (monolayer) was placed on the substrate, as shown in Fig. 1a. A vacuum of 25 Å was introduced to each side to avoid interactions between successive metal slabs. Coordinates of all calculation models are provided (Supplementary Note 1).
The transition state for each reaction was first approached using the nudged elastic band (NEB) method in the neutral state67. Forces on the climbing image were converged to <0.02 eV Å−1. The plane-wave cutoff, smearing parameter and functional, and calculator parameters were the same as those used in slab geometry optimizations. Structures obtained from NEB were employed to generate the input structure and orientation for the dimer calculation68. The force of the dimer calculation was converged to <0.1 eV Å−1 to accurately locate the saddle point, i.e., the transition state. After that, the free energy of transition state was calculated under constant potential. An explicit water molecule was used as the proton source as previous work suggested38.
To establish the electrochemical interface, the approach proposed by Head-Gordon et al., Goddard et al., and Sautet et al. was applied37,38,39. In this model, the Fermi energy is adjusted to a target value by changing the number of electrons in the system during each step of the geometry optimization, which keeps the work function and electrode potential constant in the calculations. Then the linear Poisson–Boltzmann implicit solvation model with a Debye screening length of 3.0 Å was used to neutralize the non-zero charge in the simulation cell and simulate water and the electrolyte, allowing for a more realistic description of the electrochemical double layer. A detailed description of this approach has been provided in our previous work36.
Electrolysis and product quantification
Ag foil (thickness 0.1 mm, 99.998% metal basis), Cu foil (thickness 0.1 mm, 99.9999% metal basis), Ti foil (thickness 0.127 mm, 99.99+% metal basis), and Ni wire (99.9%) were purchased from Alfa Aesar. A 5 mm × 18 mm piece of Ag or Cu foil was used as the working electrode in the CO2 and CO electrolysis experiments. The Ag foil was mechanically polished using sand paper (1200 G, 3 M) and thoroughly cleaned in an ultrasonic bath with deionized water prior to electrolysis. The Cu foil was mechanically polished using sand paper (1200 G, 3 M) followed by electrochemical polishing in phosphoric acid (85 wt.% in H2O, Sigma-Aldrich, 99.99% metal basis) at 2.0 V vs a Ti foil counter electrode and thorough rinsing in fresh 0.1 M NaHCO3 solution to remove phosphoric acid residue prior to each experiment. Ni wires were welded to the edge of these Ag and Cu foil pieces as current collectors.
The 0.1 M NaHCO3 solution was prepared by dissolving Na2CO3 (99.999%, Fluka) in deionized water that was obtained from a Millipore system (18.2 MΩ·cm) and converted to NaHCO3 using CO2 gas (99.99%, Air Liquide). The electrolyte was treated using Chelex® 100 resin (Sigma-Aldrich) prior to electrolysis. The 1 mM Cu2+ solution was prepared by dissolving Cu2SO4·5H2O (99.999%, Sigma-Aldrich) in 0.05 M sulfuric acid (99.999%, Sigma-Aldrich) according to a previously reported protocol43.
The CO2 electrolysis experiments were performed in a gas-tight two-compartment three-electrode electrochemical cell separated by a piece of a proton exchange membrane (Nafion® perfluorinated membrane). A graphite rod (99.999%, Sigma-Aldrich) was used as the counter electrode. The cathodic compartment contained 18.0 mL of electrolyte and approximately 8.2 mL of headspace. Prior to electrolysis, the electrolyte in the cathodic compartment was purged with CO2 (99.99%, Air Liquide) gas for at least 25 min until a pH of 6.8 was reached. Then the Cu2+ solution was added for the Ag-Cu surface investigations. The electrolyte in the cathodic compartment was stirred at a rate of 800 rpm during the electrolysis.
The CO electrolysis experiments were performed under identical conditions as the CO2 electrolysis experiments except for the gas feed. Prior to electrolysis, the electrolyte in the cathodic compartment was purged with CO (99.999%, Air Liquide) gas rather than CO2 for at least 25 min, and the pH was measured to be 8.4.
The square-wave potential electrolysis was performed by alternating the potential between 0.4 VRHE (U0) for a fixed time of 0.01 s and −1.1 VRHE (UE) for 1 and 0.5 s, which is equivalent to a frequency of approximately 1 and 2 Hz, respectively. Only the cathodic charges were counted for the FE calculation. The charges from the capacitive current can be neglected owing to them being <1% of the total cathodic charges.
A Gamry Reference 600+ potentiostat was used for all electrolysis. All potentials were measured against a Ag/AgCl reference electrode (3.0 M KCl, BASi) and converted to the RHE reference scale using E (vs RHE) = E (vs Ag/AgCl) + 0.210 V + 0.05916 V × pH. The IR compensation function of the potentiostat was used to correct the electrode Ru.
The gas products were quantified using a gas chromatograph (Agilent 7890B). The gas chromatograph was equipped with a ShinCarbon ST Micropacked GC Column. Argon (99.999%, Air Liquide) was used as the carrier gas. First, the column effluent was passed through a thermal conductivity detector where the hydrogen was quantified. Then the effluent was passed through a methanizer where CO was converted to methane and subsequently quantified using a flame ionization detector.
The liquid products were quantified using a Bruker AVIII 400 MHz NMR spectrometer. After electrolysis, 0.5 mL of the electrolyte was mixed with 0.1 mL of D2O (99.9%, Sigma-Aldrich), and 1.67 ppm (m/m) dimethyl sulfoxide (≥99.9%, Alfa Aesar) was added as an internal standard. The 1H spectrum was measured with water suppression using a presaturation method.
Al2O3, Na2S2O3 (98%), Na2SO3 (98%), NaOH (99.99%), KOH (99.99%), AgNO3 (99%), KCN (98%), HCHO (37 wt.%), HF (99%), NaAuCl4·2H2O and NH4Cl were purchased from Sigma-Aldrich.
The Au substrate film for the Ag film was deposited directly on the reflecting plane of Si prism using a chemical deposition method50. Before depositing, Si prism was first polished with a slurry of 0.05 μm Al2O3 and sonicated in acetone (Fisher Chemical) and deionized water. After sonicating, the Si prism was dried with air and immersed in NH4F (40%, Sigma-Aldrich) for 120 s to create a hydrogen-terminated surface. Then the reflecting surface was immersed into a mixture of 0.8 mL HF aqueous solution (2 wt.%) and 4.4 mL Au plating solution consisting of 5.75 mM NaAuCl4·2H2O, 0.025 M NH4Cl, 0.025 M Na2S2O3·5H2O, 0.075 M Na2SO3, and 0.026 M NaOH for 10 min. The temperature of the mixed solution was maintained at 55 °C during the deposition. After the deposition, the Au film was rinsed with deionized water and dried with air.
The Ag film was electrodeposited on the Au substrate film potentiostatically in a typical three-electrode system using the Au film as the working electrode, a graphite rod as the counter electrode, and saturated Ag/AgCl (BASi) as the reference electrode49. The electrolytic bath was prepared with deionized water and contained 0.15 M AgNO3, 0.54 M KCN, and 0.38 M Na2CO3. Electrodeposition in the prepared bath was carried out at 50 mVRHE for 200 mC at room temperature. Afterwards, the obtained Ag film was rinsed with deionized water and dried with air. The Ag-Cu surface was then prepared in the same fashion as in reactivity study, i.e., by conducting the experiments in a Cu2+-containing bicarbonate on the Ag film.
The Cu reference film directly deposited on the Si prism was prepared using a similar method as described previously51. Briefly, the polished Si prism was immersed in NH4F for 60 s and then immersed into a copper seeding solution (0.5 wt.% HF and 750 μM CuSO4) for 120 s followed by a plating solution (0.25 M HCHO, 0.02 M CuSO4, 20 mM Na2EDTA (99–101%, ACS Reagent), and 0.3 mM 2,2-bipyridine (99%, Reagent Plus)) for 7 min. The pH of the plating solution was adjusted to 12.2 by KOH and the temperature was maintained at 55 °C during the deposition. Afterwards, the obtained Cu film was rinsed with deionized water and dried with air.
A two-compartment, three-electrode spectroelectrochemical cell, separated by a Nafion® perfluorinated membrane, was designed to accommodate the Si prism and to avoid any possible cross-contamination from the counter electrode (Supplementary Fig. 9)48. NaHCO3 0.1 M was used as the electrolyte. The ATR-SEIRAS experiments were conducted using an Agilent Technologies Cary 660 FTIR spectrometer equipped with a liquid nitrogen-cooled MCT detector. The spectrometer was coupled with a Solartron SI 1260/1287 system for electrochemical measurements. All spectra were collected at a 4 cm−1 spectral resolution and were presented in absorbance units. In a typical process, the obtained films on Si prisms were used as working electrodes with a graphite rod as the counter electrode and saturated Ag/AgCl as the reference electrode.
SEM images were recorded using a HITACHI S-5500 SEM. The accelerating voltage was 5 kV. TEM sample was prepared using Ga+ focused ion on a ZEISS AURIGA® Field Emission-SEM implemented with CrossBeam® Workstations. TEM images were recorded using a JEOL JEM-2010F TEM. The accelerating voltage was 200 kV. XPS measurements were carried out using a PHI Quantera II with Al Kα radiation. The resulting spectra were analyzed using the CasaXPS software package (Casa Software Ltd., U.K.) and peaks were fit using a Gaussian/Lorentzian product line shape with the Shirley-type background.
The data that support the findings of this study are available from the corresponding author upon request.
Centi, G., Quadrelli, E. A. & Perathoner, S. Catalysis for CO2 conversion: a key technology for rapid introduction of renewable energy in the value chain of chemical industries. Energy Environ. Sci. 6, 1711–1731 (2013).
Lu, Q., Rosen, J. & Jiao, F. Nanostructured metallic electrocatalysts for carbon dioxide reduction. ChemCatChem 7, 38–47 (2015).
Lu, Q. & Jiao, F. Electrochemical CO2 reduction: electrocatalyst, reaction mechanism, and process engineering. Nano Energy 29, 439–456 (2016).
Lu, Q. et al. A selective and efficient electrocatalyst for carbon dioxide reduction. Nat. Commun. 5, 3242 (2014).
Chen, Y., Li, C. W. & Kanan, M. W. Aqueous CO2 reduction at very low overpotential on oxide-derived Au nanoparticles. J. Am. Chem. Soc. 134, 19969–19972 (2012).
Chen, Y. & Kanan, M. W. Tin oxide dependence of the CO2 reduction efficiency on tin electrodes and enhanced activity for tin/tin oxide thin-film catalysts. J. Am. Chem. Soc. 134, 1986–1989 (2012).
Verma, S., Lu, X., Ma, S., Masel, R. I. & Kenis, P. J. The effect of electrolyte composition on the electroreduction of CO2 to CO on Ag based gas diffusion electrodes. Phys. Chem. Chem. Phys. 18, 7075–7084 (2016).
Kim, B., Hillman, F., Ariyoshi, M., Fujikawa, S. & Kenis, P. J. A. Effects of composition of the micro porous layer and the substrate on performance in the electrochemical reduction of CO2 to CO. J. Power Sources 312, 192–198 (2016).
Hori, Y., Kikuchi, K. & Suzuki, S. Production of CO and CH4 in electrochemical reduction of CO2 at metal electrodes in aqueous hydrogencarbonate solution. Chem. Lett. 14, 1695–1698 (1985).
Hori, Y., Kikuchi, K., Murata, A. & Suzuki, S. Production of methane and ethylene in electrochemical reduction of carbon dioxide at copper electrode in aqueous hydrogencarbonate solution. Chem. Lett. 15, 897–898 (1986).
Kuhl, K. P., Cave, E. R., Abram, D. N. & Jaramillo, T. F. New insights into the electrochemical reduction of carbon dioxide on metallic copper surfaces. Energy Environ. Sci. 5, 7050–7059 (2012).
Li, C. W. & Kanan, M. W. CO2 reduction at low overpotential on Cu electrodes resulting from the reduction of thick Cu2O films. J. Am. Chem. Soc. 134, 7231–7234 (2012).
Mariano, R. G., McKelvey, K., White, H. S. & Kanan, M. W. Selective increase in CO2 electroreduction activity at grain-boundary surface terminations. Science 358, 1187–1192 (2017).
Mistry, H. et al. Highly selective plasma-activated copper catalysts for carbon dioxide reduction to ethylene. Nat. Commun. 7, 12123 (2016).
Gao, D. et al. Plasma-activated copper nanocube catalysts for efficient carbon dioxide electroreduction to hydrocarbons and alcohols. ACS Nano 11, 4825–4831 (2017).
De Luna, P. et al. Catalyst electro-redeposition controls morphology and oxidation state for selective carbon dioxide reduction. Nat. Catal. 1, 103–110 (2018).
Tang, W. et al. The importance of surface morphology in controlling the selectivity of polycrystalline copper for CO2 electroreduction. Phys. Chem. Chem. Phys. 14, 76–81 (2012).
Roberts, F. S., Kuhl, K. P. & Nilsson, A. Electroreduction of carbon monoxide over a copper nanocube catalyst: surface structure and pH dependence on selectivity. ChemCatChem 8, 1119–1124 (2016).
Kim, D., Resasco, J., Yu, Y., Asiri, A. M. & Yang, P. Synergistic geometric and electronic effects for electrochemical reduction of carbon dioxide using gold-copper bimetallic nanoparticles. Nat. Commun. 5, 4948 (2014).
Ren, D., Ang, B. S.-H. & Yeo, B. S. Tuning the selectivity of carbon dioxide electroreduction toward ethanol on oxide-derived CuxZn catalysts. ACS Catal. 6, 8239–8247 (2016).
Clark, E. L., Hahn, C., Jaramillo, T. F. & Bell, A. T. Electrochemical CO2 reduction over compressively strained CuAg surface alloys with enhanced multi-carbon oxygenate selectivity. J. Am. Chem. Soc. 139, 15848–15857 (2017).
Morales-Guio, C. G. et al. Improved CO2 reduction activity towards C2+ alcohols on a tandem gold on copper electrocatalyst. Nat. Catal. 1, 764–771 (2018).
Hatsukade, T., Kuhl, K. P., Cave, E. R., Abram, D. N. & Jaramillo, T. F. Insights into the electrocatalytic reduction of CO2 on metallic silver surfaces. Phys. Chem. Chem. Phys. 16, 13814–13819 (2014).
Rosen, J. et al. Mechanistic insights into the electrochemical reduction of CO2 to CO on nanostructured Ag surfaces. ACS Catal. 5, 4293–4299 (2015).
Peterson, A. A., Abild-Pedersen, F., Studt, F., Rossmeisl, J. & Nørskov, J. K. How copper catalyzes the electroreduction of carbon dioxide into hydrocarbon fuels. Energy Environ. Sci. 3, 1311–1315 (2010).
Peterson, A. A. & Nørskov, J. K. Activity descriptors for CO2 electroreduction to methane on transition-metal catalysts. J. Phys. Chem. Lett. 3, 251–258 (2012).
Li, J. et al. Effectively increased efficiency for electroreduction of carbon monoxide using supported polycrystalline copper powder electrocatalysts. ACS Catal. 9, 4709–4718 (2019).
Montoya, J. H., Peterson, A. A. & Nørskov, J. K. Insights into C-C coupling in CO2 electroreduction on Copper electrodes. ChemCatChem 5, 737–742 (2013).
Montoya, J. H., Shi, C., Chan, K. & Nørskov, J. K. Theoretical insights into a CO dimerization mechanism in CO2 electroreduction. J. Phys. Chem. Lett. 6, 2032–2037 (2015).
Sandberg, R. B., Montoya, J. H., Chan, K. & Nørskov, J. K. CO-CO coupling on Cu facets: coverage, strain and field effects. Surf. Sci. 654, 56–62 (2016).
Zhang, Y.-J., Sethuraman, V., Michalsky, R. & Peterson, A. A. Competition between CO2 reduction and H2 evolution on transition-metal electrocatalysts. ACS Catal. 4, 3742–3748 (2014).
Poelsema, B., Verheij, L. K. & Comsa, G. He-scattering investigation of CO migration on Pt(111). Phys. Rev. Lett. 49, 1731–1735 (1982).
Klein, R. Adsorption, diffusion, and evaporation of carbon monoxide on tungsten. J. Chem. Phys. 31, 1306–1313 (1959).
Shi, C., Chan, K., Yoo, J. S. & Nørskov, J. K. Barriers of electrochemical CO2 reduction on transition metals. Org. Process Res. Dev. 20, 1424–1430 (2016).
Cheng, T., Xiao, H. & Goddard, W. A. 3rd Full atomistic reaction mechanism with kinetics for CO reduction on Cu(100) from ab initio molecular dynamics free-energy calculations at 298 K. Proc. Natl Acad. Sci. USA 114, 1795–1800 (2017).
Zhang, H., Goddard, W. A. 3rd, Lu, Q. & Cheng, M. J. The importance of grand-canonical quantum mechanical methods to describe the effect of electrode potential on the stability of intermediates involved in both electrochemical CO2 reduction and hydrogen evolution. Phys. Chem. Chem. Phys. 20, 2549–2557 (2018).
Steinmann, S. N., Michel, C., Schwiedernoch, R., Filhol, J. S. & Sautet, P. Modeling the HCOOH/CO2 electrocatalytic reaction: when details are key. ChemPhysChem 16, 2307–2311 (2015).
Xiao, H., Cheng, T., Goddard, W. A. 3rd & Sundararaman, R. Mechanistic explanation of the pH dependence and onset potentials for hydrocarbon products from electrochemical reduction of CO on Cu (111). J. Am. Chem. Soc. 138, 483–486 (2016).
Goodpaster, J. D., Bell, A. T. & Head-Gordon, M. Identification of possible pathways for C-C bond formation during electrochemical reduction of CO2: new theoretical insights from an improved electrochemical model. J. Phys. Chem. Lett. 7, 1471–1477 (2016).
Garza, A., Bell, A. T. & Head-Gordon, M. On the mechanism of CO2 reduction at copper surfaces: pathways to C2 products. ACS Catal. 8, 1490–1499 (2018).
Liu, X. et al. Understanding trends in electrochemical carbon dioxide reduction rates. Nat. Commun. 8, 15438 (2017).
Liu, X. et al. pH effects on the electrochemical reduction of CO(2) towards C2 products on stepped copper. Nat. Commun. 10, 32 (2019).
Dietterle, M., Will, T. & Kolb, D. The initial stages of copper deposition on Ag (111): an STM study. Surf. Sci. 342, 29–37 (1995).
Nikolić, N. D., Pavlović, L. J., Krstić, S. B., Pavlović, M. G. & Popov, K. I. Influence of ionic equilibrium in the CuSO4–H2SO4–H2O system on the formation of irregular electrodeposits of copper. Chem. Eng. Sci. 63, 2824–2828 (2008).
Orhan, G. & Gezgin, G. Effect of electrolysis parameters on the morphologies of copper powder obtained at high current densities. J. Serb. Chem. Soc. 77, 651–665 (2012).
Kim, Y. G., Baricuatro, J. H., Javier, A., Gregoire, J. M. & Soriaga, M. P. The evolution of the polycrystalline copper surface, first to Cu(111) and then to Cu(100), at a fixed CO2RR potential: a study by operando EC-STM. Langmuir 30, 15053–15056 (2014).
Kim, Y.-G. et al. Surface reconstruction of pure-Cu single-crystal electrodes under CO-reduction potentials in alkaline solutions: A study by seriatim ECSTM-DEMS. J. Electroanal. Chem. 780, 290–295 (2016).
Dunwell, M. et al. Examination of near-electrode concentration gradients and kinetic impacts on the electrochemical reduction of CO2 using surface-enhanced infrared spectroscopy. ACS Catal. 8, 3999–4008 (2018).
Wanzenböck, H. D., Mizaikoff, B., Weissenbacher, N. & Kellner, R. Surface enhanced infrared absorption spectroscopy (SEIRA) using external reflection on low-cost substrates. Fresenius J. Anal. Chem. 362, 15–20 (1998).
Dunwell, M. et al. The Central role of bicarbonate in the electrochemical reduction of carbon dioxide on gold. J. Am. Chem. Soc. 139, 3774–3783 (2017).
Malkani, A. S., Dunwell, M. & Xu, B. Operando spectroscopic investigations of copper and oxide-derived copper catalysts for electrochemical CO reduction. ACS Catal. 9, 474–478 (2019).
Ikezawa, Y., Saito, H., Matsubayashi, H. & Toda, G. Comparative study of CO adsorbed on Pt, Pd, Au and Ag electrodes in neutral solution by IR reflection absorption spectroscopy. J. Electroanal. Chem. Inter. 252, 395–402 (1988).
Gunathunge, C. M. et al. Spectroscopic observation of reversible surface reconstruction of copper electrodes under CO2 reduction. J. Phys. Chem. C 121, 12337–12344 (2017).
Heyes, J., Dunwell, M. & Xu, B. CO2 reduction on Cu at low overpotentials with surface-enhanced in situ spectroscopy. J. Phys. Chem. C 120, 17334–17341 (2016).
Gunathunge, C. M., Ovalle, V. J., Li, Y., Janik, M. J. & Waegele, M. M. Existence of an electrochemically inert CO population on Cu electrodes in alkaline pH. ACS Catal. 8, 7507–7516 (2018).
Pérez Gallent, E., Figueiredo, M. C., Calle‐Vallejo, F. & Koper, M. T. M. Spectroscopic observation of a hydrogenated CO dimer intermediate during CO reduction on Cu (100) electrodes. Angew. Chem. Int. Ed. 129, 3675–3678 (2017).
Kortlever, R., Shen, J., Schouten, K. J. P., Calle-Vallejo, F. & Koper, M. T. M. Catalysts and reaction pathways for the electrochemical reduction of carbon dioxide. J. Phys. Chem. Lett. 6, 4073–4082 (2015).
Genovese, C., Ampelli, C., Perathoner, S. & Centi, G. Mechanism of C–C bond formation in the electrocatalytic reduction of CO2 to acetic acid. A challenging reaction to use renewable energy with chemistry. Green. Chem. 19, 2406–2415 (2017).
Li, C. W., Ciston, J. & Kanan, M. W. Electroreduction of carbon monoxide to liquid fuel on oxide-derived nanocrystalline copper. Nature 508, 504–507 (2014).
Wang, Y., Raciti, D. & Wang, C. High-flux CO reduction enabled by three-dimensional nanostructured copper electrodes. ACS Catal. 8, 5657–5663 (2018).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Grimme, S. Semiempirical GGA-type density functional constructed with a long-range dispersion correction. J. Comput. Chem. 27, 1787–1799 (2006).
Henkelman, G. & Jónsson, H. Improved tangent estimate in the nudged elastic band method for finding minimum energy paths and saddle points. J. Chem. Phys. 113, 9978–9985 (2000).
Henkelman, G. & Jónsson, H. A dimer method for finding saddle points on high dimensional potential surfaces using only first derivatives. J. Chem. Phys. 111, 7010–7022 (1999).
This work is supported by the National Key Research and Development Program of China (grant number 2017YFA0208200) and the National Natural Science Foundation of China (grant numbers 21872079, 21606142). W.A.G. is supported by the Joint Center for Artificial Photosynthesis, a DOE Energy Innovation Hub, supported through the Office of Science of the U.S. Department of Energy under Award Number DE-SC0004993. X.C. and B.X. acknowledge the support of the National Science Foundation CAREER Program (Award No. CBET-1651625). M.-J.C. acknowledges financial support from the Ministry of Science and Technology of the Republic of China under grant no. MOST 107–2113-M-006–008-MY2.
The authors declare no competing interests.
Peer review information: Nature Communication would like to thank the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Zhang, H., Chang, X., Chen, J.G. et al. Computational and experimental demonstrations of one-pot tandem catalysis for electrochemical carbon dioxide reduction to methane. Nat Commun 10, 3340 (2019). https://doi.org/10.1038/s41467-019-11292-9
Tandem Electrodes for Carbon Dioxide Reduction into C2+ Products at Simultaneously High Production Efficiency and Rate
Cell Reports Physical Science (2020)
Energy & Environmental Science (2020)
A Robust, Scalable Platform for the Electrochemical Conversion of CO2 to Formate: Identifying Pathways to Higher Energy Efficiencies
ACS Energy Letters (2020)