Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Ion buffering and interface charge enable high performance electronics with organic electrochemical transistors


Organic electrochemical transistors rely on ionic-electronic volumetric interaction to provide a seamless interface between biology and electronics with outstanding signal amplification. Despite their huge potential, further progress is limited owing to the lack of understanding of the device fundamentals. Here, we investigate organic electrochemical transistors in a wide range of experimental conditions by combining electrical analyses and device modeling. We show that the measurements can be quantitatively explained by nanoscale ionic-electronic charge interaction, giving rise to ion buffering and interface charge compensation. The investigation systematically explains and unifies a wide range of experiments, providing the rationale for the development of high-performance electronics. Unipolar inverters — universal building blocks for electronics — with gain larger than 100 are demonstrated. This is the highest gain ever reported, enabling the design of devices and circuits with enhanced performance and opening opportunities for the next-generation integrated bioelectronics and neuromorphic computing.


Organic electrochemical transistors (OECTs) are iontronic devices where ions penetrate the semiconductor and dramatically modulate the electrical properties of the transistor channel. Owing to this bulk ionic-electronic interaction, OECTs provide a seamless interface between biology and electronics combining the benefits typical of organic material technologies—such as large-area deposition with simple and low-cost techniques, chemically-tunable properties, mechanical flexibility, softness, and biological compatibility1,2,3,4,5—with high signal amplification, ultra-low voltage operation, and stability in aqueous environment6,7,8. Fueled by this unique benefits combination, OECTs are gaining significant interest in numerous bioelectronic applications, including neural interfacing, electrophysiology, cell monitoring, enhanced ionic and biological sensing, neuromorphic devices, and neuron stimulation9,10,11,12,13,14,15,16,17. Despite the huge potential, the lack of understanding of the fundamental processes governing the device operation hinder further progress in the rational design of engineered and optimized devices for new and improved applications.

The operation of OECTs has been described for the first time by Bernards and Malliaras18 in 2007. Their pioneering work depicted OECTs as the combination of an electronic circuit that accounts for electronic transport in the organic semiconductor, and an ionic circuit that accounts for ionic transport in the electrolyte. Importantly, the model captured the key characteristic of OECTs, i.e., the volumetric response due to the ion penetration into the transistor channel. This point has been recently investigated by several experimental works19,20,21,22, showing that ions uptake from an electrolyte into a polymeric film results in a purely volumetric capacitance19. The linear dependence of the capacitance on the volume of the polymeric channel and the zero offset led to the conclusion that the ionic charges are uniformly distributed in the polymer and no significant ion accumulation at the polymer/electrolyte interface takes place23. On one hand, studies24 based on the modeling of cyclic voltammograms of the prototypical conducting polymer poly(3,4-ethylenedioxythiophene) doped with the polyelectrolyte poly(styrene sulfonate) (PEDOT:PSS) suggest that the capacitance originates from an electrical double layer (EDL) at the interface between the PEDOT phase and the PSS phase. In this direction, Tybrandt and coworkers25 show a modified drift diffusion model for the description of PEDOT:PSS based OECTs. On the other hand, several reports show that in conductive polymers the characteristic shape of the supercapacitive voltammograms is due to pseudo-capacitive processes involving faradaic reactions26,27,28,29. These findings are further corroborated by specific studies on OECTs, where the dedoping process is commonly explained as a faradaic reaction30,31,32,33. The redox model is usually invoked to explain the ion concentration dependent OECT transfer characteristics31 but a limited range of ion concentrations has been assessed. In this complex scenario, a comprehensive experimental and theoretical analysis identifying the key physical effects and providing a consistent picture of the OECT operation is highly desirable.

Here we investigate the ionic-electronic interaction in OECTs accounting for a very wide range of ion concentrations, channel thicknesses, and polymer charge densities. OECTs are systematically analyzed by combining electrochemical impedance spectroscopy, current-voltage characteristics, and device modeling. First, the analysis considers the widely studied PEDOT:PSS OECTs, enabling us to compare our results with the state of the art. Then, to prove the generality of our results, we modify the polymer formulation by changing the amount of fixed charges in the polyelectrolyte by about two orders of magnitude. Finally, the analysis is extended to a widely used accumulation mode material, namely poly(3-hexylthiophene-2,5-diyl) (P3HT). We show that the measurements can be quantitatively explained by an electrostatic bulk uptake of ions that compensate both fixed and mobile electronic charges. The key OECT characteristics can be quantitatively explained by ion buffering and interface charge compensation. The analysis unifies a wide range of experiments, explaining the ion concentration-dependent threshold voltage and the ion concentration-independent volumetric capacitance in OECTs. On the basis of this understanding, we demonstrate OECT unipolar inverters, ubiquitous building blocks for electronics, with gain and noise margin up to 107 and 82% of the theoretical limit, respectively. These are the best performances ever reported for the fundamental figures of merit of inverters and, importantly, are achieved basing on a device-aware circuit design approach.


Device structure and electrical characteristics

A schematic representation of the OECT structure is depicted in Fig. 1a. A thin film of PEDOT:PSS is deposited by inkjet printing on a plastic polyethylene foil. Gold is used for source and drain electrodes. The transistor channel width and length are W = 1000 μm and L = 500 μm, respectively. The printing technique allows to easily vary the channel thickness (t) by printing multiple stacked polymer layers, ranging from 230 to 2300 nm. It is worth to note that the channel thickness is a key design parameter because it enables the tuning of the transistor capacitance and, in turn, of the transconductance19. As electrolyte, we used an aqueous solution of sodium-chloride (NaCl) at concentrations ranging from c = 1 10−3 M to c = 5 M. A PDMS well is used to spatially confine the electrolyte. The wide range of ion concentrations and polymer thicknesses here investigated is extremely relevant for OECT-based biological applications, sensing, and circuits19,34,35,36. The gate electrode is an Ag/AgCl pellet immersed into the electrolyte. Further details on the OECTs fabrication are provided in the Methods section.

Fig. 1

OECTs structure and electrical characteristics. a Schematic representation of an OECT. b Typical transfer characteristics in linear scale of an OECT. c Typical output characteristics of an OECT. The NaCl concentration is 100 mM. d Measured transconductance gm = dID/dVG, with a maximum gm of about 10 mS at VG = 0 V and VD = −0.4 V. The transconductance normalized to the device geometry and drain voltage amounts to 60 S cm−1 V−1. e, f Typical transfer characteristics (semi-log scale and linear scale) measured at several NaCl concentrations and at VD = −0.4 V. The device thickness is 2095 nm

Typical transfer and output characteristics of the fabricated devices are shown in Fig. 1b, c, respectively. By applying a positive gate voltage (VG) cations drift into the polymer, reduce the hole concentration and lower the drain current (ID). Analogously, when a negative VG is applied previously injected cations drift out of the polymer while anions drift into the polymer, the hole concentration increases and this results in a larger ID. As shown in Fig. 1d the maximum transconductance normalized to the OECT geometries and drain voltage is larger than 60 S cm−1 V−1 at VG = 0 V and VD = −0.4 V, in agreement with state-of-the-art OECTs6. The extremely large transconductance, resulting from the ionic-electronic interaction through the bulk of the polymeric channel, is a hallmark of OECTs.

Analysis of the main OECT parameters

To investigate the ionic-electronic interaction in OECTs, we measured the transfer characteristics (IDVG) by varying the ion concentration c. Figure 1e, f shows that the IDVG characteristics systematically shift to more negative voltages with increasing ion concentrations. To gain insight on the physical mechanisms underlying the device operation, we reproduced the electrical characteristics of the OECTs with the drain current model proposed by Bernards and Malliaras18, that in the case of linear operation reads18,37:

$$I_{\mathrm{D}} = \Gamma \left[ {\left( {V_{\mathrm{T}} - V_{\mathrm{G}}} \right)V_{\mathrm{D}} + \frac{{V_{\mathrm{D}}^2}}{2}} \right]$$


$$\Gamma = \frac{{Wt}}{L}\mu C_{\mathrm{v}}$$

The drain current depends on the geometrical and physical device parameters, namely polymer width (W), length (L), thickness (t), hole mobility (μ), volumetric capacitance (Cv), and threshold voltage (VT), which is defined as:

$$V_{\mathrm{T}} = V_{\mathrm{P}} - V_{{\mathrm{SH}}}$$

where VP=q p0 Cv−1 is the pinch-off voltage, q is the elementary charge, p0 is the intrinsic doping of the semiconductor, and VSH accounts for the voltage shift as a function of the ion concentration c. It is worth noting that VSH can be attributed to both the gate/electrolyte and electrolyte/semiconductor interfaces.

According to Eq. (1), the drain current depends on the applied voltages (VG and VD) and on the device parameters Γ and VT. Γ and VT can be obtained by fitting the transfer characteristics in the linear regime. The modeling is systematically performed on OECTs with various channel thicknesses and the transfer characteristics are reproduced. Supplementary Figure 1 shows the modeling of the ID-VG as a function of c. It is worth to note that we focus on a narrow range of the transfer characteristics since this enables a reliable extraction of the model parameters and ensures excellent stability of the OECT characteristics38,39 (Supplementary Fig. 2). The slope of the linear least square approximation of the ID–VG provides Γ. Figure 2a shows Γ normalized to the channel geometries (viz. Γn = Γ L W−1 t−1) as a function of c. For each c the mean value and standard deviation of Γn are calculated by modeling OECTs with several thicknesses. We found that Γn is independent of c and, according to Eq. (2), it follows that Cv is independent of c. The analysis is further corroborated by reproducing the OECT transfer characteristics with the drain current model recently proposed by Friedlein and co-workers40 (Supplementary Note 1), which accounts for a non-uniform mobility in OECTs and provides superior fitting performance of the saturation region of operation (Supplementary Fig. 2a). Supplementary Figure 2d shows Γn extracted by fitting the OECT characteristics with the Friedlein model, confirming that Cv is independent of c.

Fig. 2

OECT parameters as a function of the ion concentration. a Normalized conductivity Γn = ΓLW−1t−1 as a function of the ion concentration. b Threshold voltage VT as a function of the ion concentration. Circles are the mean value and error bars are the standard deviation calculated by modeling ten OECTs with various thicknesses

A c-independent Cv is crucially important because in the case of an EDL a capacitance affected by the counterion concentration is expected41,42. To investigate this point, we perform electrochemical impedance spectroscopy (EIS) measurements by systematically varying the counterion concentration. The OECT impedance spectra as a function of c are shown in Supplementary Fig. 3. In order to obtain Cv, for each c and t we modeled the measured impedance as a function of the frequency with the Randles equivalent circuit that, in the case of an OECT, is composed of a resistor Rs in series with the parallel of a resistor Rp and a capacitor C 19. In this model, Rs is the electrolyte resistance, Rp depends on the reactions at the working electrode, and C accounts for the ion accumulation at the working electrode43. The OECT volumetric capacitance is calculated as Cv=C v−1 where v=W L t is the total volume of the OECT channel. Cv and Rs as a function of c are shown in Supplementary Fig. 4. In all cases we found that Cv is independent of the ion concentration and results Cv = 44 ± 2 F cm−3. This value is in agreement with the state-of-the-art19,25.

To further investigate the origin of the ion-dependent drain current displayed in Fig. 1e, f, we analyzed VT as a function of c. The mean value and standard deviation are extracted from OECTs with several thicknesses at each ion concentration. Figure 2b shows that VT decreases with increasing ion concentration. According to the previous analysis, the pinch-off voltage is independent of the ion concentration (VP = q p0 Cv−1) provided that p0 is independent of c. To this aim, we monitored the polymer conductivity as a function c by measuring the drain current of an OECT when the gate electrode is not immersed into the electrolyte. We found that ID is independent of c (Supplementary Fig. 5) and therefore the variation of VT as a function of c can be ascribed to VSH. Figure 3a (symbols) shows the extracted VSH as a function of c. VSH accounts for the voltage drop at both the gate/electrolyte (VG/E) and the electrolyte/polymer (VE/P) interfaces, and reads:

$$V_{{\mathrm{SH}}} = V_{{\mathrm{G}}/{\mathrm{E}}} + V_{{\mathrm{E}}/{\mathrm{P}}}$$

Focusing on the gate-electrolyte interface, it is worth to note that we used an Ag/AgCl pellet as gate electrode, which is a non-polarizable quasi-reference electrode. According to the Nernst equation, the potential drop at the gate-electrolyte interface results44:

$$V_{{\mathrm{G}}/{\mathrm{E}}} = \frac{{k_{\mathrm{B}}T}}{q}\log c$$

where kB is the Boltzmann constant and T is the temperature. Figure 3a (full line) shows the voltage drop at the gate/electrolyte interface calculated with Eq. (5). At large ion concentrations VG/E (full line) is close to VSH (symbols), while at small ion concentrations VG/E is significantly larger than VSH. This indicates that the contribution of the electrolyte/polymer interface cannot be neglected and it can be calculated with Eq. (4), viz. VE/P=VSH − VG/E.

Fig. 3

Potential at the interfaces as a function of the ion concentration. a Measured threshold voltage shift VSH as a function of the ion concentration (symbols) and Nernst potential at the gate/electrolyte interface VG/E (vs. SHE) calculated with Eq. (5) (solid line). b Potential at the electrolyte/polymer interface VE/P as a function of the ion concentration. Symbols are the measurements and solid line is calculated with Eq. (6). Circles are the mean value and error bars are the standard deviation calculated by modeling ten OECTs with various thicknesses

The role of the bulk charge interaction

Figure 3b (symbols) shows the voltage drop at the electrolyte/polymer interface (VE/P) as a function of c. Supplementary Figure 6 shows that VE/P extracted with the Friedlein et al. model fully agrees. VE/P is large and negative (VE/P ≈ −0.2 V) at the minimum ion concentration c = 10−3 M, it increases with a Nernstian slope of 59 mV dec−1 up to c = 5 10−1 M, and at larger concentrations VE/P is close to zero. This can be explained as follows. In OECTs, ions dissolved in the electrolyte can flow into the bulk of the polymeric channel. In the case of PEDOT:PSS OECTs, the channel is made of a polymer blending composed of a PSS-rich matrix hosting nanometric sized PEDOT-rich grains20,24,25, as schematically depicted in Fig. 4. The electronic (hole) conduction takes place in the PEDOT (blue islands in Fig. 4) while ionic conduction is provided by the PSS polyelectrolyte (light-gray regions in Fig. 4). Indeed, when in contact with an electrolyte, the PSS matrix swells and allows the hydrated ions to penetrate the polymeric blend20,45. The polyelectrolyte/electrolyte interface acts as a semi-permeable membrane, which can be penetrated by the mobile ions provided by the electrolyte solution (red spheres in Fig. 4) but cannot be crossed by the SO3 fixed anions of the PSS (blue cubes in Fig. 4). As a consequence, the fixed charges in the bulk of the polyelectrolyte (Nfix) are electrostatically compensated by cations provided by the electrolyte. More in detail, at low electrolyte concentrations (c « Nfix) cations drift into the polymer and compensate the fixed negative charges. At the equilibrium, the cation concentration in the polymer (cPSS+) is equal to Nfix independently of c and a negative potential rises at the polyelectrolyte/electrolyte interface (VE/P  < 0 V). On the other hand, when c » Nfix, the fixed charges in the polyelectrolyte are negligible, cPSS+ ≈ c and VE/P ≈ 0 V.

Fig. 4

Schematic material-view of a PEDOT:PSS OECT. The polymeric channel is depicted by PEDOT-rich grains (dark blue) hosted by a PSS-rich matrix (gray). The zoom shows the ionic–electronic interaction in the PEDOT:PSS channel. Fixed anions in the PSS polyelectrolyte (blue cubes) are electrostatically compensated both by holes in the PEDOT semiconductor (red h+) at the PEDOT/PSS interface and by mobile cations (red spheres) in the bulk of the PSS

This behavior resembles the Donnan equilibrium in semi-permeable membranes and the potential at the polyelectrolyte/electrolyte interface can be calculated as (see Supplementary Note 2)25,46:

$$V_{{\mathrm{E}}/{\mathrm{P}}} = - \frac{{k_{\mathrm{B}}T}}{q}{\mathrm{asinh}}\left( {\frac{{z_{{\mathrm{fix}}}N_{{\mathrm{fix}}}}}{{2zc}}} \right)$$

where z and zfix are the number of charges of the ions dissolved into the electrolyte and fixed charge into the polyelectrolyte, respectively. Interestingly the model predicts that VE/P shows a Nernstian behavior when c « Nfix, while VE/P ≈ 0 when c » Nfix. Figure 3b (line) shows that VE/P calculated with Eq. (6) accurately reproduces the measurements in the whole range of ion concentrations. By reproducing the measurements with the model we estimated a SO3 concentration Nfix = 3.16 M (viz. about 1.9 1021 cm−3). The wide range of ion concentrations here assessed proves that the Nernst equation fails to describe VE/P and hence the faradaic redox reactions can be disregarded. In addition, Supplementary Fig. 7 shows that Eq. (6) is able to explain the threshold voltage shift measured in OECTs exploiting electrolytes with different chemical nature, such as KCl, Ca(NO3)2, and Al2(SO4)3. This provides further insight on the strong dependence of the transistor performance on the chemical nature of the counterion used, as reported in refs. 47,48.

Interestingly, Eqs. (4)–(6) show that the actual gating voltage (viz. VG + VSH) depends on the electrolyte concentration (VSH = VG/E + VE/P). Combining this model with the approach proposed by Friedlein et al.40, the normalized hole concentration (p/p0) as a function of c results:

$$\frac{p}{{p_0}} = \frac{{V_{\mathrm{P}} - V_{\mathrm{G}} + V_{{\mathrm{ch}}}}}{{V_{\mathrm{P}}}} - \frac{{k_{\mathrm{B}}T}}{{qV_{\mathrm{P}}}}\left[ {\log \left( c \right) - {\mathrm{asinh}}\left( {\frac{{z_{{\mathrm{fix}}}N_{{\mathrm{fix}}}}}{{2zc}}} \right)} \right]$$

where Vch is the potential along the polymeric channel. Figure 5a shows p as a function of c and VG. p/p0 linearly decreases with the logarithm of c with a slope equal to 147 10−3 dec−1 in the low range of c (10−3 M < c < 1 M) where c affects both VE/P and VG/E, and 74 10−3 dec−1 in the high range of c (1 M < c < 5 M) where VE/P vanishes and only VG/E depends on c. Figure 5a also shows the dependence on VGVch. In the whole range of c, p/p0 linearly decreases by increasing VG since Cv is constant.

Fig. 5

Hole and ion concentration in the OECT channel. a Hole concentration in the PEDOT:PSS channel normalized to the intrinsic hole concentration as a function of c and VG − Vch. The hole concentration is calculated according to Eq. (7) at a channel coordinate x = L/2 when the OECT is biased at VD = −0.1 V. b Mobile ion concentration in the electrolyte (black dashed line), and mobile cation (blue line) and anion (red line) concentration in the PSS polyelectrolyte normalized to the fixed charge concentration into the polymer Nfix. The concentrations are calculated with Supplementary Equations (19), (20), (21) (see Supplementary Note 2)

Figure 5b shows the mobile cation and anion concentrations in the PSS bulk (cPSS+ and cPSS-, respectively) as a function of the electrolyte ion concentration c. For the sake of generality, cPSS+, cPSS-, and c are normalized with respect to Nfix. When c / Nfix « 1, cPSS+ is buffered to a constant value cPSS+ = Nfix, while cPSS quadratically increases with c. In this case a concentration-dependent potential rises across the electrolyte/polymer interface. On the other hand, when c / Nfix » 1, the effect of the electrostatic interaction between the fixed charges and the mobile ions is negligible. It follows that the concentration of both anions and cations in the PSS phase is equal to c and a vanishing potential at the interface is obtained.

As a further confirmation, we fabricate OECTs including a positively charged polyelectrolyte in the channel. Poly-L-lysine (PLL) is added to the PEDOT:PSS dispersion by varying the ratio between PLL and PEDOT:PSS (details are provided in the Methods section). The electrical analyses (EIS and transfer characteristics) of the PEDOT:PSS:PLL OECTs are performed and the device parameters are extracted. Figure 6a shows the electrolyte/polymer potential VE/P as a function of c when the PEDOT:PSS/PLL ratio is equal to 1/3, 5/1 and 1/0 (no PLL) v/v. The minimum c where VE/P ≈ 0 V systematically lowers with increasing PLL concentration. In all cases the model (Eq. (6)) accurately reproduces the measurements in the whole range of ion concentrations and we found that the net negative fixed charge concentration in the PEDOT:PSS:PLL amounts to Nfix(5/1)= 1.8 1020 cm−3 (0.3 M) and Nfix(1/3)= 4 1019 cm−3 (66 10−3 M) when the PEDOT:PSS/PLL ratio is equal to 5/1 and 1/3 v/v, respectively. These results show that the potential at the electrolyte/polymer interface can be controlled by tuning the fixed charge concentration in the polymer. To investigate the generality of the model we extend the analysis to other materials, namely P3HT and Crystalized PEDOT:PSS (Crys-P)49, which are widely used for the fabrication of high performance OECTs21,47,50. Figure 6a shows that in the case of P3HT OECTs VE/P is equal to 0 V in the whole concentration range explored, resulting in NfixP3HT < 1017 cm−3 (10−4 M). This small fixed charge concentration is expected in the case of undoped P3HT51,52,53. Moreover, Fig. 6a shows that in the case of Crys-P the minimum c where VE/P vanishes is shifted to lower c with respect to pristine PEDOT:PSS and we found NfixCrys−P = 6 1019 cm−3. This provides quantitative evidence that in Crys-P the excess PSS (viz. bulk PSS) is chemically removed by sulfuric acid treatment. Interestingly, we found that NfixCrys−P is almost equal to that obtained in PEDOT:PSS:PLL when the PEDOT:PSS/PLL ratio is 1/3 v/v, suggesting that in the case of PEDOT:PSS/PLL = 1/3 the bulk fixed charge is completely compensated.

Fig. 6

The effect of bulk and interface charge. a Measured (symbols) and calculated (solid lines, Eq. (6)) VE/P as a function of c in OECTs with various polymeric channels. b PEDOT concentration (red symbols, left axis) and volumetric capacitance Cv (blue symbols, right axis) of PEDOT:PSS:PLL OECTs as a function of the PEDOT:PSS/PLL ratio. The Cv is normalized to the Cv of pristine PEDOT:PSS. Analogously, the PEDOT concentration is normalized to the PEDOT concentration of PEDOT:PSS OECTs. The dashed lines are guide for the eye. c Measured Cv as a function of c for OECTs with various PEDOT:PSS/PLL ratio (symbols). The dashed lines are the mean values

The role of the interface charge interaction

To further assess the effect of the polyelectrolyte charges on the OECTs characteristics, we fabricate PEDOT:PSS:PLL OECTs with PEDOT:PSS/PLL ratio equal to 5/1, 1/3, 1/5, 1/10 and 1/50. Supplementary Figure 8a shows that at small PLL contents (viz. PEDOT:PSS/PLL larger than 1/3 v/v) the PEDOT is well dispersed and no visible polymer separation is obtained. By increasing the PLL content a clear separation of PEDOT from the dispersion shows up. This is confirmed by Supplementary Fig. 8b where, after the syringe withdrawal of the dispersion, no significant PEDOT residue is obtained at PEDOT:PSS/PLL ratios equal to 5/1 and 1/3 v/v, while PEDOT aggregates can be clearly seen at larger PLL concentrations. The formation of undispersed PEDOT is not surprising, considering that PEDOT is a water-insoluble polymer and the negative charges of the PSS are used as charge-balancing dopants to yield a water-soluble PEDOT:PSS complex54. It follows that the compensation of the negative fixed charges of the PSS located at the PEDOT/PSS interface by the positive charges of the PLL yields water-insoluble PEDOT aggregates. To quantitatively assess the PEDOT concentration in PEDOT:PSS:PLL OECTs we electro-optically investigate the composition of the deposited films. Figure 7a shows the experimental setup. We measure the optical transmittance at 620 nm55 and VG ranging from 0 V to 0.5 V of devices with various amount of PLL. Figure 7b shows the images acquired in the case of an OECT with PEDOT:PSS/PLL = 5/1 and Fig. 7c shows the corresponding histogram of the red channel intensity at various VG. By applying the Beer-Lambert law, the measured optical intensity provides the ratio between the PEDOT concentration in PEDOT:PSS:PLL and pristine PEDOT:PSS. Figure 6b shows the PEDOT concentration in the PEDOT:PSS:PLL films as a function of the PEDOT:PSS/PLL ratio. When PEDOT:PSS/PLL ≥ 1/3 the PEDOT concentration into the PEDOT:PSS:PLL film is independent of the PLL content and equals to that of pristine PEDOT:PSS (without PLL), whereas further increasing the PLL content results in a reduction of the PEDOT content. Importantly, the electro-optical measurements show that the PEDOT doping state is not affected by PLL (Supplementary Note 3, Supplementary Fig. 9). We can conclude that small contents of PLL (PEDOT:PSS/PLL ≥ 1/3 v/v) result in a compensation of the fixed charges in the bulk of the polyelectrolyte with negligible effect on the fixed charges at the PEDOT/PSS interface. Besides, large amounts of PLL (PEDOT:PSS/PLL ≤ 1/5 v/v) result in a separation of PEDOT from the dispersion due to the compensation of the interfacial charges.

Fig. 7

Electro-optical characterization of OECTs. a Schematic of the measurement setup. b 2D intensity maps measured on an OECT with PEDOT:PSS/PLL = 5/1 at VG = [0, 0.1, 0.2, 0.3, 0.4, 0.5] V and VD = VS = 0 V. The scale bar is 50 µm. c Probability density function (PDF) of the 2D intensity maps measured on an OECT with PEDOT:PSS/PLL = 5/1 at various VG

Taking advantage of this charge compensation effect, we investigate the volumetric capacitance as a function of the polyelectrolyte charge by performing EIS on PEDOT:PSS:PLL OECTs with various PEDOT:PSS/PLL ratios. Figure 6b shows that Cv of OECTs with small PLL contents (PEDOT:PSS/PLL > 1/5 v/v) is almost equal to the one of pristine PEDOT:PSS OECTs, Cv slightly decreases for devices with PEDOT:PSS/PLL ratio equal to 1/5, while it dramatically decreases at larger PLL contents. In the light of the previous analysis, small PLL contents affect only the bulk of the polymer without affecting the PEDOT:PSS interface. Therefore, we can conclude that Cv depends on the amount of PEDOT in the deposited film demonstrating that Cv is related to an electrostatic interaction at the semiconductor/(poly)electrolyte (PEDOT/PSS) interface. Figure 6c shows that the measured Cv is independent of the ion concentration. This behavior can be explained by considering the large concentration of fixed charge (about 1 M) at the PEDOT/PSS interface, which yields a negligible diffuse layer42.

OECT based electronics

The understanding and quantification of the key mechanisms in OECTs, provide the rationale for the development of high-performance electronics. Here, as a relevant example, we demonstrate unipolar inverters. The inverter is a fundamental building block of any electronic circuit enabling the development of OECT-based integrated electronics and bioelectronics. Inverters are used both in digital circuits as logic gates and in analogue circuits as voltage amplifiers. Figure 8a shows the circuit schematic, which comprises two p-type OECTs connected in series. The input voltage VI is applied to the gate of the Driver OECT while the Load OECT is operated as a zero-VGS topology56. The OECT model (Supplementary Note 4, Supplementary Fig. 10) is implemented in a circuit simulator in order to predict the circuit operation.

Fig. 8

Unipolar OECT based inverter. a Schematic of the designed circuit. The driver geometries are W = 1000 µm, L = 500 µm, t = 210 nm, the load geometries are W = 1000 µm, L = 500 µm, t = 280 nm. Crys-P is used for the OECT channel, and details are provided in Supplementary Note 4. b Measured (solid line) and simulated (dashed lines) voltage transfer characteristics of the inverter. c Measured (solid line) and simulated (dashed lines) gain of the inverter

The ion concentration of the Load OECT is exploited as a design parameter to maximize the key circuit figures of merit, namely the gain and noise margin, while the Driver ion concentration is 5 M. Figure 8b shows that the simulated (dashed lines) and measured (full lines) transfer characteristics are in agreement in the whole range of voltages and ion concentrations. When the input is low (e.g., VI = GND) the source-gate voltage VSG applied to the Driver OECT is large (VSG = VDD − VI) and, as a result, the output voltage VOUT is close to VDD. By increasing VI, the pull-up becomes progressively weaker and a sharp transition of VO from VDD to GND is displayed when VI reaches the trip-point voltage VTP. Further increasing VI (VI > VTP) reduces VSG and VO is close to GND. Figure 8b shows that the transfer characteristics are strongly affected by the ion concentration. More in detail, when c increases from 5 10−3 to 3 M VTP shifts from VI = 0.3 V to VI = 0.54 V and the gain increases from 12 up to 107 (Fig. 8c), with a maximum noise margin equal to 0.33 V, i.e., 82% of the theoretical limit. This can be explained as follows. By increasing c, ion buffering yields a more negative threshold voltage of the Load transistor while, due to the interface charge, its capacitance is unaffected. As a result, VTP increases since a larger VI is required to switch VO from the high to the low state. In addition, the reduced drain current of the Load transistor yields a larger gain, which is inversely proportional to the current flowing through the inverter. It is worth to note that for the sake of simplicity we varied only the Load electrolyte concentration, but similar considerations hold in the case that both the Load and the Driver concentrations are taken as design variables.

The proposed approach is compared with several inverters based on electrolyte-gated technologies in Table 1. The gain and noise margin of the designed inverter outperform those obtained by state-of-art electrolyte-gated inverters based on metal-oxides, carbon nanotubes, two-dimensional and organic materials33,57,58,59,60,61,62,63,64,65,66.

Table 1 Performance comparison


In summary, we provide experimental evidence of the electrostatic nature of the ionic-electronic interaction in OECTs. We perform both electrical ID-VG characteristics and electrochemical impedance spectroscopies on OECTs by exploring a wide range of channel thicknesses, polymer formulations and electrolyte ion concentrations. We show that to understand the OECT operation it is crucial to consider the bulk and interface electrostatic charge compensation taking place in the transistor channel. More in detail, the fixed charges in the bulk of the polyelectrolyte are electrostatically compensated by the mobile ions provided by the electrolyte. This results in an ion buffering in the polymeric channel and, in turn, in a concentration-dependent voltage drop at the polyelectrolyte/electrolyte interface. The fixed charges close to the semiconductor are electrostatically compensated by the electronic charges accumulated at the semiconductor/polyelectrolyte interface. This bulk uptake of ions results in a capacitance distributed in the volume of the polymer and independent of the electrolyte ion concentration. The ion concentration dependent transfer characteristics are quantitatively explained. The analysis is extended to OECTs with different polymers, proving its generality. We show that a large set of measurements in a wide range of experimental conditions can be consistently explained without invoking faradaic reactions. The impact of our analysis on the design of OECT based circuits is demonstrated by the design of unipolar inverters with tunable performances, showing the highest gain and noise margin ever reported for this class of circuits.

Prospectively, our study opens opportunities for several applications and research directions. Our work provides both fundamental knowledge and experimental demonstration of OECTs with tailored ionic response. This finds application for future development of integrated bioelectronics67, electronic circuits, ion sensors16,17 and neuromorphic circuits. For example, in neuromorphic applications a wide range of ion concentration can be exploited as a global regulation parameter to emulate the homeoplasticity phenomena of neural environments12,68. Our work enables the design of neuromorphic circuits with synapse-specific response, typical of biological neural networks69. Finally, the demonstration of an ion concentration-independent volumetric capacitance is crucial for in vivo applications, as the ionic concentration of the body fluid may vary from person to person and between the different body fluids34, thus requiring OECTs with a transconductance independent of the ionic environment. Our findings provide important design rules for the rational design of devices with enhanced performance and application-specific functionalities, opening opportunities for the next generation OECT-based electronic, bioelectronics and neuromorphic computing.



100 nm thick Au source/drain contacts are sputtered through a shadow mask on a polyethylene substrate. An adhesion layer of 15 nm of Ti-W is previously deposited to enhance Au adhesion. Polyethylene substrates are cleaned with DI water, dried with N2 and treated with oxygen plasma to promote PEDOT:PSS adhesion. An Epson XP-215 is used for the printing process, filling a cartridge with either PEDOT:PSS or PEDOT:PSS:PLL. PEDOT:PSS (PH-500 from Heraeus Clevios GmbH) is mixed with 5 vol% ethylene glycol, 1 vol% 3-glycidoxypropyl-trimethoxysilane, 0.25 vol% dodecyl benzene sulfonic acid as conductivity enhancer, crosslinker and wetting agent, respectively. PEDOT:PSS:PLL is obtained by adding to PEDOT:PSS a PLL solution (0.1 % w/v in H2O) at various volume ratios. All the reagents were purchased from Sigma-Aldrich. The dispersion is filtered through a syringe filter (regenerated cellulose, pore size 0.2 µm) prior to deposition. The tuning of the film thickness is obtained by printing multiple stacked layers. A minimum of 4 layers is necessary to obtain a continuous conductive film. The thickness of the polymeric film obtained by varying the number of printed layers is measured with a stylus profilometer Bruker Dektak XT. A soft bake (1 min at 50 °C) is performed between the printing of each layer to avoid the spread of the printed polymer. The films are baked at 100 °C for 1 h and immersed in deionized water to remove any excess low molecular weight compounds.

Crys-P OECT fabrication

We fabricate Crys-P OECTs following the fabrication process reported in ref. 50. In brief, PEDOT:PSS (PH-500 from Heraeus Clevios GmbH) is filtered (regenerated cellulose, pore size 0.2 µm) and spin coated on quartz-coated substrates with sputtered gold source and drain electrodes (W = 1000 µm, L = 100 µm). The deposited films are annealed at 120 °C for 15 min and then immersed in a bath of concentrated H2SO4 (>95%, Sigma Aldrich) for 15 min, thoroughly rinsed with deionized water, and dried at 120 °C for 15 min.

P3HT OECT fabrication

We fabricate P3HT OECTs following the fabrication process reported in ref. 21. Briefly, 25 mg ml−1 of regioregular P3HT (Ossila M105) are dissolved overnight at 80 °C in dichlorobenzene. The solution is filtered through a 0.45 µm PTFE filter and spin coated (3 s at 500 r.p.m., 60 s at 1000 r.p.m., 10 s at 5000 r.p.m. from 45 °C solution) on Si-SiO2 substrates with gold interdigitated source and drain electrodes (W = 1500 µm, L = 5 µm).

Electrical characterization

Transfer and output characteristics are measured with a Keithley 2636 A SourceMeter Unit. A solution of NaCl in DI water at several concentrations is used as electrolyte and an Ag/AgCl pellet (Warner Instruments) is used as gate electrode. Transfer characteristics are measured by sweeping the gate voltage, with the source electrode grounded and the drain electrode polarized at a constant potential. Output characteristics are measured by sweeping the drain voltage, with the source electrode grounded and the gate electrode polarized at a constant potential. The electrical characteristics of the devices are measured with a constant sweep rate of 18 mV/s, which allows the device to reach the steady state operation regime. Electrochemical Impedance Spectroscopy measurements are performed using a National Instruments PXI-1042 system, equipped with a PXI-5112 oscilloscope, a PXI-5421 arbitrary wave-function generator and custom Labview software for the control of the system. A three-electrode configuration is adopted. The drain and source electrodes are shortened together and the OECT channel acted as the working electrode. Two Ag/AgCl pellets serve as reference and counter electrodes. The inverter characteristics are measured with a Keithley 2636 A Source Meter Unit. The input voltage is swept from 0 V to 0.8 V with a voltage step of 0.3 mV and at supply voltage of 0.8 V.

Electrical and optical characterization

The OECT is placed on an opaque sample holder with the channel in correspondence of a slit. A droplet of 10−1 M NaCl solution is placed on top of the transistor and an Ag/AgCl gate is dipped into the solution. The source and drain electrodes are shortened and VD = VS = 0 V, while the gate voltage is biased in the range 0 to 0.5 V. The light from a red light emitting diode (Superlight, LED emission peak at wavelength 620 nm) placed below the sample holder is conveyed at the transistor channel through the holder slit and the transmitted light is captured by a camera (Dino-Lite AM4023CT, raw acquisition) on the opposite side of the sample. The measurements are performed in a dark room. The 2D transmitted intensity map was acquired on a scale from 0 to 255 taking care that no pixel saturated at 0 or 255.

Data availability

The data that support the findings of this study are available from the corresponding author on reasonable request.


  1. 1.

    Li, M. et al. Integrated circuits based on conjugated polymer monolayer. Nat. Commun. 9, 451 (2018).

    ADS  Article  Google Scholar 

  2. 2.

    Fukuda, K. et al. Fully-printed high-performance organic thin-film transistors and circuitry on one-micron-thick polymer films. Nat. Commun. 5, 4147 (2014).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Rivnay, J., Owens, R. M. & Malliaras, G. G. The rise of organic bioelectronics. Chem. Mater. 26, 679–685 (2014).

    CAS  Article  Google Scholar 

  4. 4.

    Kaltenbrunner, M. et al. An ultra-lightweight design for imperceptible plastic electronics. Nature 499, 458–463 (2013).

    ADS  CAS  Article  Google Scholar 

  5. 5.

    Arias, A. C., MacKenzie, J. D., McCulloch, I., Rivnay, J. & Salleo, A. Materials and applications for large area electronics: solution-based approaches. Chem. Rev. 110, 2–24 (2010).

    Article  Google Scholar 

  6. 6.

    Khodagholy, D. et al. High transconductance organic electrochemical transistors. Nat. Commun. 4, 2133 (2013).

    ADS  Article  Google Scholar 

  7. 7.

    Giovannitti, A. et al. N-type organic electrochemical transistors with stability in water. Nat. Commun. 7, 13066 (2016).

    ADS  CAS  Article  Google Scholar 

  8. 8.

    Rivnay, J. et al. Organic electrochemical transistors. Nat. Rev. Mater. 3, 17086 (2018).

    ADS  CAS  Article  Google Scholar 

  9. 9.

    Lee, W. et al. Transparent, conformable, active multielectrode array using organic electrochemical transistors. Proc. Natl. Acad. Sci. USA 114, 10554–10559 (2017).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    van de Burgt, Y. et al. A non-volatile organic electrochemical device as a low-voltage artificial synapse for neuromorphic computing. Nat. Mater. 16, 414 (2017).

    ADS  Article  Google Scholar 

  11. 11.

    Braendlein, M. et al. Lactate detection in tumor cell cultures using organic transistor circuits. Adv. Mater. 29, 1605744 (2017).

    Article  Google Scholar 

  12. 12.

    Gkoupidenis, P., Koutsouras, D. A. & Malliaras, G. G. Neuromorphic device architectures with global connectivity through electrolyte gating. Nat. Commun. 8, 15448 (2017).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Lee, W. et al. Integration of organic electrochemical and field-effect transistors for ultraflexible, high temporal resolution electrophysiology arrays. Adv. Mater. 28, 9722–9728 (2016).

    CAS  Article  Google Scholar 

  14. 14.

    Williamson, A. et al. Localized neuron stimulation with organic electrochemical transistors on delaminating depth probes. Adv. Mater. 27, 4405–4410 (2015).

    CAS  Article  Google Scholar 

  15. 15.

    Khodagholy, D. et al. In vivo recordings of brain activity using organic transistors. Nat. Commun. 4, 1575 (2013).

    ADS  Article  Google Scholar 

  16. 16.

    Ghittorelli, M. et al. High-sensitivity ion detection at low voltages with current-driven organic electrochemical transistors. Nat. Commun. 9, 1441 (2018).

    ADS  Article  Google Scholar 

  17. 17.

    Macchia, E. et al. Ultra-sensitive protein detection with organic electrochemical transistors printed on plastic substrates. Flex. Print. Electron. 3, 034002 (2018).

    Article  Google Scholar 

  18. 18.

    Bernards, D. A. & Malliaras, G. G. Steady-state and transient behavior of organic electrochemical transistors. Adv. Funct. Mater. 17, 3538–3544 (2007).

    CAS  Article  Google Scholar 

  19. 19.

    Rivnay, J. et al. High-performance transistors for bioelectronics through tuning of channel thickness. Sci. Adv. 1, e1400251 (2015).

    ADS  Article  Google Scholar 

  20. 20.

    Rivnay, J. et al. Structural control of mixed ionic and electronic transport in conducting polymers. Nat. Commun. 7, 11287 (2016).

    ADS  Article  Google Scholar 

  21. 21.

    Giridharagopal, R. et al. Electrochemical strain microscopy probes morphology-induced variations in ion uptake and performance in organic electrochemical transistors. Nat. Mater. 16, 737–742 (2017).

    ADS  CAS  Article  Google Scholar 

  22. 22.

    Inal, S., Malliaras, G. G. & Rivnay, J. Benchmarking organic mixed conductors for transistors. Nat. Commun. 8, 1767 (2017).

    ADS  Article  Google Scholar 

  23. 23.

    Proctor, C. M., Rivnay, J. & Malliaras, G. G. Understanding volumetric capacitance in conducting polymers. J. Polym. Sci. B Polym. Phys. 54, 1433–1436 (2016).

    ADS  CAS  Article  Google Scholar 

  24. 24.

    Volkov, A. V. et al. Understanding the capacitance of PEDOT:PSS. Adv. Funct. Mater. 27, 1700329 (2017).

    Article  Google Scholar 

  25. 25.

    Tybrandt, K., Zozoulenko, I. V. & Berggren, M. Chemical potential–electric double layer coupling in conjugated polymer–polyelectrolyte blends. Sci. Adv. 3, eaao3659 (2017).

    Article  Google Scholar 

  26. 26.

    Simon, P. & Gogotsi, Y. Materials for electrochemical capacitors. Nat. Mater. 7, 845–854 (2008).

    ADS  CAS  Article  Google Scholar 

  27. 27.

    Bryan, A. M., Santino, L. M., Lu, Y., Acharya, S. & D’Arcy, J. M. Conducting polymers for pseudocapacitive energy storage. Chem. Mater. 28, 5989–5998 (2016).

    CAS  Article  Google Scholar 

  28. 28.

    Heinze, J., Frontana-Uribe, B. A. & Ludwigs, S. Electrochemistry of conducting polymers-persistent models and new concepts. Chem. Rev. 110, 4724–4771 (2010).

    CAS  Article  Google Scholar 

  29. 29.

    Yeu, T., Yin, K.-M., Carbajal, J. & White, R. E. Electrochemical characterization of electronically conductive polypyrrole on cyclic voltammograms. J. Electrochem. Soc. 138, 2869–2877 (1991).

    CAS  Article  Google Scholar 

  30. 30.

    Hutter, P. C., Fian, A., Gatterer, K. & Stadlober, B. Efficiency of the switching process in organic electrochemical transistors. ACS Appl. Mater. Interfaces 8, 14071–14076 (2016).

    Article  Google Scholar 

  31. 31.

    Lin, P., Yan, F. & Chan, H. L. W. Ion-sensitive properties of organic electrochemical transistors. ACS Appl. Mater. Interfaces 2, 1637–1641 (2010).

    CAS  Article  Google Scholar 

  32. 32.

    Zeglio, E. & Inganäs, O. Active materials for organic electrochemical transistors. Adv. Mater. 30, 1800941 (2018).

    Article  Google Scholar 

  33. 33.

    Doris, S. E., Pierre, A. & Street, R. A. Dynamic and tunable threshold voltage in organic electrochemical transistors. Adv. Mater. 30, 1706757 (2018).

    Article  Google Scholar 

  34. 34.

    Leleux, P. et al. Organic electrochemical transistors for clinical applications. Adv. Healthc. Mater. 4, 142 (2014).

    Article  Google Scholar 

  35. 35.

    Vander, A., Sherman, J. & Luciano, D. Human Physiology: The Mechanisms of Body Function 8th edn (McGraw-Hill, New York, 2001).

    Google Scholar 

  36. 36.

    Strakosas, X., Bongo, M. & Owens, R. M. The organic electrochemical transistor for biological applications. J. Appl. Polym. Sci. 132, 41735 (2015).

    Article  Google Scholar 

  37. 37.

    Bernards, D. A. et al. Enzymatic sensing with organic electrochemical transistors. J. Mater. Chem. 18, 116–120 (2008).

    CAS  Article  Google Scholar 

  38. 38.

    Giovannitti, A. et al. Controlling the mode of operation of organic transistors through side-chain engineering. Proc. Natl. Acad. Sci. USA 113, 12017–12022 (2016).

    ADS  CAS  Article  Google Scholar 

  39. 39.

    Nielsen, C. B. et al. Molecular design of semiconducting polymers for high-performance organic electrochemical transistors. J. Am. Chem. Soc. 138, 10252–10259 (2016).

    CAS  Article  Google Scholar 

  40. 40.

    Friedlein, J. T., Shaheen, S. E., Malliaras, G. G. & McLeod, R. R. Optical measurements revealing nonuniform hole mobility in organic electrochemical transistors. Adv. Electron. Mater. 1, 1500189 (2015).

    Article  Google Scholar 

  41. 41.

    Wang, H. & Pilon, L. Accurate simulations of electric double layer capacitance of ultramicroelectrodes. J. Phys. Chem. C 115, 16711–16719 (2011).

    CAS  Article  Google Scholar 

  42. 42.

    Srinivasan, S. in Fuel Cells Ch. 2 (Springer, Boston, 2006).

  43. 43.

    Randles, J. E. B. Kinetics of rapid electrode reactions. Discuss. Faraday Soc. 1, 11–19 (1947).

    Article  Google Scholar 

  44. 44.

    Bard, A. J. & Faulkner, L. R. Electrochemical Methods 2nd edn (John Wiley & Sons, New York, 2001).

  45. 45.

    Duc, C., Vlandas, A., Malliaras, G. G. & Senez, V. Wettability of PEDOT:PSS films. Soft Matter 12, 5146–5153 (2016).

    ADS  CAS  Article  Google Scholar 

  46. 46.

    Sperelakis, N. Cell Physiology. Source Book (Academic Press, San Diego, 1995).

  47. 47.

    Flagg, L. Q., Giridharagopal, R., Guo, J. & Ginger, D. S. Anion-dependent doping and charge transport in organic electrochemical transistors. Chem. Mater. 30, 5380–5389 (2018).

    CAS  Article  Google Scholar 

  48. 48.

    Pecqueur, S., Guérin, D., Vuillaume, D. & Alibart, F. Cation discrimination in organic electrochemical transistors by dual frequency sensing. Org. Electron. 57, 232–238 (2018).

    CAS  Article  Google Scholar 

  49. 49.

    Kim, N. et al. Highly conductive PEDOT:PSS nanofibrils induced by solution-processed crystallization. Adv. Mater. 26, 2268–2272 (2014).

    CAS  Article  Google Scholar 

  50. 50.

    Kim, S. et al. Influence of PEDOT:PSS crystallinity and composition on electrochemical transistor performance and long-term stability. Nat. Commun. 9, 3858 (2018).

    ADS  Article  Google Scholar 

  51. 51.

    Brondijk, J. J. et al. Formation of inversion layers in organic field-effect transistors. Phys. Rev. B Condens. Matter 85, 165310 (2012).

    ADS  Article  Google Scholar 

  52. 52.

    Kao, C. et al. Doping of conjugated polythiophenes with alkyl silanes. Adv. Funct. Mater. 19, 1906–1911 (2009).

    CAS  Article  Google Scholar 

  53. 53.

    Maddalena, F., Meijer, E. J., Asadi, K., de Leeuw, D. M. & Blom, P. W. M. Doping kinetics of organic semiconductors investigated by field-effect transistors. Appl. Phys. Lett. 97, 043302 (2010).

    ADS  Article  Google Scholar 

  54. 54.

    Groenendaal, L., Jonas, F., Freitag, D., Pielartzik, H. & Reynolds, J. R. Poly(3,4-ethylenedioxythiophene) and its derivatives: past, present, and future. Adv. Mater. 12, 481–494 (2000).

    CAS  Article  Google Scholar 

  55. 55.

    Marks, Z. D. et al. Switchable diffractive optics using patterned PEDOT:PSS based electrochromic thin-films. Org. Electron. 37, 271–279 (2016).

    CAS  Article  Google Scholar 

  56. 56.

    Cantatore, E. et al. A 13.56-MHz RFID system based on organic transponders. IEEE J. Solid State Circuits 42, 84–92 (2007).

    ADS  Article  Google Scholar 

  57. 57.

    Hong, K., Kim, S. H., Lee, K. H. & Daniel Frisbie, C. D. Printed, sub-2 V ZnO electrolyte gated transistors and inverters on plastic. Adv. Mater. 25, 3413–3418 (2013).

    CAS  Article  Google Scholar 

  58. 58.

    Park, S. et al. Sub-0.5 V highly stable aqueous salt gated metal oxide electronics. Sci. Rep. 5, 13088 (2015).

    ADS  CAS  Article  Google Scholar 

  59. 59.

    Cho, K. G. et al. Sub-2 V, transfer-stamped organic/inorganic complementary inverters based on electrolyte-gated transistors. ACS Appl. Mater. Interfaces 10, 40672–40680 (2018).

    CAS  Article  Google Scholar 

  60. 60.

    Joshi, S. et al. Ambient processed, water-stable, aqueous-gated sub 1 V n-type carbon nanotube field effect transistor. Sci. Rep. 8, 11386 (2018).

    ADS  Article  Google Scholar 

  61. 61.

    Ha, M. et al. Aerosol jet printed, low voltage, electrolyte gated carbon nanotube ring oscillators with sub-5 μs stage delays. Nano Lett. 13, 954–960 (2013).

    ADS  CAS  Article  Google Scholar 

  62. 62.

    Gao, G. et al. Triboiontronic transistor of MoS2. Adv. Mater. 31, 1806905 (2019).

    Article  Google Scholar 

  63. 63.

    Xia, Y. et al. Printed sub-2 V gel-electrolyte-gated polymer transistors and circuits. Adv. Funct. Mater. 20, 587–594 (2010).

    CAS  Article  Google Scholar 

  64. 64.

    Herlogsson, L., Crispin, X., Tierney, S. & Berggren, M. Polyelectrolyte-gated organic complementary circuits operating at low power and voltage. Adv. Mater. 23, 4684–4689 (2011).

    CAS  Article  Google Scholar 

  65. 65.

    Porrazzo, R. et al. Water-gated n-type organic field-effect transistors for complementary integrated circuits operating in an aqueous environment. ACS Omega 2, 1–10 (2017).

    CAS  Article  Google Scholar 

  66. 66.

    Sun, H. et al. Complementary logic circuits based on high-performance n-type organic electrochemical transistors. Adv. Mater. 30, 1704916 (2018).

    Article  Google Scholar 

  67. 67.

    Spyropoulos, G. D., Gelinas, J. N. & Khodagholy, D. Internal ion-gated organic electrochemical transistor: a building block for integrated bioelectronics. Sci. Adv. 5, eaau7378 (2019).

    ADS  Article  Google Scholar 

  68. 68.

    Koutsouras, D. A., Malliaras, G. G. & Gkoupidenis, P. Emulating homeoplasticity phenomena with organic electrochemical devices. MRS Commun. 8, 493–497 (2018).

    CAS  Article  Google Scholar 

  69. 69.

    Kim, J. & Tsien, R. W. Synapse-specific adaptations to inactivity in hippocampal circuits achieve homeostatic gain control while dampening network reverberation. Neuron 58, 925–937 (2008).

    CAS  Article  Google Scholar 

Download references


The authors acknowledge the financial support of the European Commission for the project SiMBiT (Horizon 2020 ICT, contract number 824946).

Author information




P.R. and F.T. conceived the idea and designed the experiments. P.R. fabricated and measured the devices and circuits. P.R., M.G., and F.T. developed the physical analysis. Z.M.K.-V. supervised the project. P.R. and F.T. wrote the paper. All the authors revised and commented on the paper.

Corresponding author

Correspondence to Fabrizio Torricelli.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information: Nature Communications thanks Magnus Berggren and other anonymous reviewer(s) for their contribution to the peer review of this work.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Romele, P., Ghittorelli, M., Kovács-Vajna, Z.M. et al. Ion buffering and interface charge enable high performance electronics with organic electrochemical transistors. Nat Commun 10, 3044 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing